CN102814751A - 一种掺有pvc树脂粉的陶瓷cbn砂轮 - Google Patents

一种掺有pvc树脂粉的陶瓷cbn砂轮 Download PDF

Info

Publication number
CN102814751A
CN102814751A CN2012102673859A CN201210267385A CN102814751A CN 102814751 A CN102814751 A CN 102814751A CN 2012102673859 A CN2012102673859 A CN 2012102673859A CN 201210267385 A CN201210267385 A CN 201210267385A CN 102814751 A CN102814751 A CN 102814751A
Authority
CN
China
Prior art keywords
parts
resin powder
powder
grinding wheel
emery wheel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102673859A
Other languages
English (en)
Other versions
CN102814751B (zh
Inventor
孙兆英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI WEIMING WEAR-RESISTANT MATERIAL Co Ltd
Original Assignee
ANHUI WEIMING WEAR-RESISTANT MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI WEIMING WEAR-RESISTANT MATERIAL Co Ltd filed Critical ANHUI WEIMING WEAR-RESISTANT MATERIAL Co Ltd
Priority to CN201210267385.9A priority Critical patent/CN102814751B/zh
Publication of CN102814751A publication Critical patent/CN102814751A/zh
Application granted granted Critical
Publication of CN102814751B publication Critical patent/CN102814751B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种掺有PVC树脂粉的陶瓷CBN砂轮，其是由重量份的CBN磨料50-60、酚醛树脂粉20-30、PVC树脂粉3-6、废铁粉1-3、核桃壳粒1-2、聚乙二醇40002-3、甘油三醋酸酯1-2、邻苯二甲酸二辛酯5-10、凹凸棒土5-10、纳米重晶石粉3-6、废钢粉2-5组成。本发明中结合剂采用陶瓷料，可以使砂轮不易变形，耐热性好，具有很高的耐磨性；各种陶瓷料粘结性能好，可以有效地防止裂纹，解决了现有砂轮耐热性差，易变形的问题。解决了现有砂轮粘结剂性能不佳，磨料易脱落的问题。本发明添加了PVC树脂粉等粉末，不但提高了砂轮的耐热性和耐寒性，减小砂轮的热变形，从而提高砂轮的机械性能，使其磨削效率和使用寿命远远超过传统砂轮，综合效益提高50%以上。

Description

一种掺有PVC树脂粉的陶瓷CBN砂轮
技术领域
本发明公开了一种掺有PVC树脂粉的陶瓷CBN砂轮及其制备方法，属于磨具加工技术领域。
背景技术
砂轮是磨削加工中最主要的一类磨具。砂轮是在磨料中加入结合剂，经压坯、干燥和焙烧而制成的多孔体。砂轮是磨具中用量最大、使用面最广的一种，使用时高速旋转，可对金属或非金属工件的外圆、内圆、平面和各种型面等进行粗磨、半精磨和精磨以及开槽和切断等。砂轮中用以粘结磨料的物质称结合剂，结合剂的性能决定砂轮的强度、抗冲击性、耐热性及抗腐蚀能力。目前结合剂主要分为陶瓷、树脂、橡胶和金属四种，其中陶瓷结合剂耐热性、耐腐蚀性好、气孔率大、易保持轮廓，适用于v<35m/s的各种成形磨削、磨齿轮、磨螺纹等。
    掺有PVC树脂粉的陶瓷CBN砂轮，以立方氮化硼磨料为原料，分别用金属粉、树脂粉、陶瓷作结合剂烧结成各种形状的磨具，用于工业磨削、抛光、研磨。此种陶瓷砂轮保持了陶瓷砂轮原有的高硬度性能，烧结温度低、强度韧性高、把持磨料性能好，并具有耐热、耐油、耐水、耐酸碱、自锐性好、可修整、修整间隔长，均匀的气孔率，便于冷却、排屑等。在磨削过程中不堵塞、不烧伤工件，与铁族元素不起化学变化，显惰性，降低工件在磨削加工中的疲劳度，增加工件的使用寿命，从而提高加工工件的质量、粗糙度、效率以及加工工件自动化程度，达到降低综合成本的目的。掺有PVC树脂粉的陶瓷CBN砂轮不仅具有切削锋利、磨削力小、生产效率高、使用寿命高、易于整形与修锐、磨削精度高等优点，而且还具有磨削时工件温度低，能消除残余拉应力而产生残余压应力，使工件耐用度得到提高的特点，因而收到世界广泛关注，成为世界上磨削工具产品研发研究的热点。
发明内容
本发明的目的是提供一种掺有PVC树脂粉的陶瓷CBN砂轮，以增加陶瓷结合剂CBN砂轮的强度和硬度，提高其性能。
为达到以上目的，本发明采用的技术方案如下：
    一种掺有PVC树脂粉的陶瓷CBN砂轮，其特征在于，其是由下列重量份的原料制成：
    CBN磨料50-60、酚醛树脂粉20-30、PVC树脂粉3-6、废铁粉1-3、核桃壳粒1-2、聚乙二醇4000 2-3、甘油三醋酸酯1-2、邻苯二甲酸二辛酯5-10、凹凸棒土5-10、纳米重晶石粉3-6、废钢粉2-5。
    所述的掺有PVC树脂粉的陶瓷CBN砂轮各原料组分的重量份如下表中各配方之一：
Figure 2012102673859100002DEST_PATH_IMAGE002
    所述的邻苯二甲酸二辛酯、凹凸棒土、纳米重晶石粉、废钢粉经过2600-3000℃高温熔炼，冷却后球磨成纳米陶瓷粉末，即可成为陶瓷结合剂。
    掺有PVC树脂粉的陶瓷CBN砂轮的制备方法，其特征在于，包括以下步骤：
（1）按上述配方将各组分装入混料机中，混和1-2小时，充分混匀；
（2）将混料倒入模具中，再将模具放入压机压制，同时加热模具，先预加压1-2兆帕，压机上、下板加热温度130-150℃，时间2-4分钟，然后升压至11-12兆帕，保压3-5分钟，然后将处理温度升至220-250℃，保温2-3小时；
（3）热压完毕后冷却至常温，取出砂轮工件即可。
本发明具有以下有益效果：
1、本发明中结合剂采用陶瓷料，可以使砂轮不易变形，耐热性好，具有很高的耐磨性，解决了现有砂轮耐热性差，易变形的问题；各种陶瓷料粘结性能好，可以有效地防止裂纹，解决了现有砂轮粘结剂性能不佳，磨料易脱落的问题。
    2、本发明添加了PVC树脂粉等粉末，不但提高了砂轮的耐热性和耐寒性，减小砂轮的热变形，从而提高砂轮的机械性能，使其磨削效率和使用寿命远远超过传统砂轮，综合效益提高50%以上。
具体实施方式
下列通过具体实施例对本发明作进一步的说明。
实施例1
    掺有PVC树脂粉的陶瓷CBN砂轮由下列重量份的原料制成：CBN磨料53、酚醛树脂粉22、PVC树脂粉3、废铁粉2、核桃壳粒1.2、聚乙二醇4000 2.2、甘油三醋酸酯1.0、邻苯二甲酸二辛酯5、凹凸棒土5、纳米重晶石粉3、废钢粉2。所述的邻苯二甲酸二辛酯、凹凸棒土、纳米重晶石粉、废钢粉经过2710℃高温熔炼，冷却后球磨成纳米陶瓷粉末，即可成为陶瓷结合剂。
    掺有PVC树脂粉的陶瓷CBN砂轮的制备方法包括以下步骤：
    （1）按上述配方将各组分装入混料机中，混和1小时，充分混匀；
    （2）将混料倒入模具中，再将模具放入压机压制，同时加热模具，先预加压1兆帕，压机上、下板加热温度305℃，时间2钟，然后升压至11兆帕，保压3分钟，然后将处理温度升至725℃，保温2小时；
（3）热压完毕后冷却至常温，取出砂轮工件即可。
实施例2
掺有PVC树脂粉的陶瓷CBN砂轮由下列重量份的原料制成：CBN磨料55、酚醛树脂粉24、PVC树脂粉6、废铁粉3、核桃壳粒1.5、聚乙二醇4000 2.5、甘油三醋酸酯1.4、邻苯二甲酸二辛酯7、凹凸棒土6、纳米重晶石粉4、废钢粉3。所述的邻苯二甲酸二辛酯、凹凸棒土、纳米重晶石粉、废钢粉经过2798℃高温熔炼，冷却后球磨成纳米陶瓷粉末，即可成为陶瓷结合剂。
    掺有PVC树脂粉的陶瓷CBN砂轮的制备方法包括以下步骤：
    （1）按上述配方将各组分装入混料机中，混和1小时，充分混匀；
（2）将混料倒入模具中，再将模具放入压机压制，同时加热模具，先预加压1-2兆帕，压机上、下板加热温度130-150℃，时间2-4分钟，然后升压至11-12兆帕，保压3-5分钟，然后将处理温度升至220-250℃，保温2-3小时；
    （3）热压完毕后冷却至常温，取出砂轮工件即可。
实施例3
掺有PVC树脂粉的陶瓷CBN砂轮由下列重量份的原料制成：CBN磨料58、酚醛树脂粉27、PVC树脂粉7、废铁粉4、核桃壳粒1.7、聚乙二醇4000 2.8、甘油三醋酸酯1.6、邻苯二甲酸二辛酯8、凹凸棒土8、纳米重晶石粉5、废钢粉5。所述的邻苯二甲酸二辛酯、凹凸棒土、纳米重晶石粉、废钢粉经过2856℃高温熔炼，冷却后球磨成纳米陶瓷粉末，即可成为陶瓷结合剂。
    掺有PVC树脂粉的陶瓷CBN砂轮的制备方法包括以下步骤：
    （1）按上述配方将各组分装入混料机中，混和2小时，充分混匀；
    （2）将混料倒入模具中，再将模具放入压机压制，同时加热模具，先预加压1-2兆帕，压机上、下板加热温度130-150℃，时间2-4分钟，然后升压至11-12兆帕，保压3-5分钟，然后将处理温度升至220-250℃，保温2-3小时；
    （3）热压完毕后冷却至常温，取出砂轮工件即可。
实施例4
掺有PVC树脂粉的陶瓷CBN砂轮由下列重量份的原料制成：CBN磨料60、酚醛树脂粉30、PVC树脂粉8、废铁粉5、核桃壳粒2.0、聚乙二醇4000 3.0、甘油三醋酸酯1.9、邻苯二甲酸二辛酯10、凹凸棒土10、纳米重晶石粉6、废钢粉5。所述的邻苯二甲酸二辛酯、凹凸棒土、纳米重晶石粉、废钢粉经过2925℃高温熔炼，冷却后球磨成纳米陶瓷粉末，即可成为陶瓷结合剂。
    掺有PVC树脂粉的陶瓷CBN砂轮的制备方法包括以下步骤：
    （1）按上述配方将各组分装入混料机中，混和2小时，充分混匀；
（2）将混料倒入模具中，再将模具放入压机压制，同时加热模具，先预加压1-2兆帕，压机上、下板加热温度130-150℃，时间2-4分钟，然后升压至11-12兆帕，保压3-5分钟，然后将处理温度升至220-250℃，保温2-3小时；
（3）热压完毕后冷却至常温，取出砂轮工件即可。

Claims (3)

1.一种掺有PVC树脂粉的陶瓷CBN砂轮，其特征在于，其是由下列重量份的原料制成：
CBN磨料50-60、酚醛树脂粉20-30、PVC树脂粉3-6、废铁粉1-3、核桃壳粒1-2、聚乙二醇4000 2-3、甘油三醋酸酯1-2、邻苯二甲酸二辛酯5-10、凹凸棒土5-10、纳米重晶石粉3-6、废钢粉2-5。
2.根据权利要求1所述的掺有PVC树脂粉的陶瓷CBN砂轮，其特征在于，所述的掺有PVC树脂粉的陶瓷CBN砂轮各原料组分的重量份如下表中各配方之一：
Figure 2012102673859100001DEST_PATH_IMAGE002
根据权利要求1或2所述的掺有PVC树脂粉的陶瓷CBN砂轮，其特征在于，所述的凹凸棒土、纳米重晶石粉经过2600-3000℃高温熔炼，冷却后球磨成纳米陶瓷粉末，即可成为陶瓷结合剂。
3.一种如权利要求1或2所述的掺有PVC树脂粉的陶瓷CBN砂轮的制备方法，其特征在于，包括以下步骤：
（1）按上述配方将各组分装入混料机中，混和1-2小时，充分混匀；
（2）将混料倒入模具中，再将模具放入压机压制，同时加热模具，先预加压1-2兆帕，压机上、下板加热温度130-150℃，时间2-4分钟，然后升压至11-12兆帕，保压3-5分钟，然后将处理温度升至220-250℃，保温2-3小时；
（3）热压完毕后冷却至常温，取出砂轮工件即可。
CN201210267385.9A 2012-07-31 2012-07-31 一种掺有pvc树脂粉的陶瓷cbn砂轮 Active CN102814751B (zh)