CN106625297A - Cbn砂轮 - Google Patents

Cbn砂轮 Download PDF

Info

Publication number
CN106625297A
CN106625297A CN201611071584.7A CN201611071584A CN106625297A CN 106625297 A CN106625297 A CN 106625297A CN 201611071584 A CN201611071584 A CN 201611071584A CN 106625297 A CN106625297 A CN 106625297A
Authority
CN
China
Prior art keywords
cbn
powder
abrasive
grinding
grinding wheel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611071584.7A
Other languages
English (en)
Other versions
CN106625297B (zh
Inventor
胡成洋
其他发明人请求不公开姓名
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pan Dimensional Technology (qingdao) Co Ltd
Original Assignee
Pan Dimensional Technology (qingdao) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pan Dimensional Technology (qingdao) Co Ltd filed Critical Pan Dimensional Technology (qingdao) Co Ltd
Priority to CN201611071584.7A priority Critical patent/CN106625297B/zh
Publication of CN106625297A publication Critical patent/CN106625297A/zh
Application granted granted Critical
Publication of CN106625297B publication Critical patent/CN106625297B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及超硬材料领域,具体地说,涉及一种CBN砂轮,本发明提出一种具有良好的抗冲击性和形状保持性,能承受高速磨削过程中的较大载荷的CBN砂轮,其包括钢芯、磨料圈,钢芯和磨料圈通过结合剂结合在一起,其特征在于:磨料圈由以下质量百分比的原料制成:CBN磨料30~70%,金属结合剂20~60%,辅助粘结剂2~10%,本发明的CBN砂轮具有良好的热导率有利于降低磨削温度,从而降低功率损耗,提高磨削速度;配方中的辅助粘结剂有利于孔隙的形成,结合金属结合剂把持力强的特点,可以有效增大容屑空间,磨料的利用更加充分;砂轮具有磨削效率高、磨削温度低、功率损耗低、加工精度好、使用寿命长等特点。

Description

CBN砂轮
技术领域
[0001] 本发明涉及超硬材料领域,具体地说,涉及一种CBN砂轮。
背景技术
[0002] 现代机械加工朝着高精度、高速度、硬加工、干加工(无冷却液)及降低成本等方向发展,对超硬磨具的性能提出了相当高的要求。目前常用的超硬磨削材料包括立方氮化硼(CBN)和金刚石磨料两种。CBN磨料虽然硬度次于金刚石,但其热稳定性和化学稳定性强,尤其是不会与铁及铁合金发生反应,因而在铁基合金材料如淬硬钢、高速工具钢、轴承钢、不镑钢、t旲具钢、耐热钢、先进尚强钢和尚络铸铁,以及钦合金与银基尚温合金等诸多尚强韦刃性难加工材料的磨削中得到了广泛应用。CBN超硬磨具(砂轮)的磨削效率、加工精度和耐磨性等性能是高速精密磨削加工中的关键问题。
[0003] 在超硬磨具中用于固结磨粒的结合剂是影响超硬磨具性能的关键因素。传统的超硬磨具(砂轮)的结合剂多采用树脂、陶瓷、金属等三种材料。树脂结合剂易加工修整,然而其使用温度低,结合强度和对磨料的把持力较低,磨料易脱落,磨削精度差;陶瓷结合剂具有较好的结合强度,把持力高,使用温度高,然而其脆性大,导热性差,抗冲击和疲劳性能较差,难适用于高速加工。而现有的金属结合剂虽然具有良好的强韧性配合和耐热性,但是通常存在结合剂与磨粒之间不能产生化学冶金结合的问题,因而磨粒仅仅被机械包埋镶嵌在结合剂中,把持力有限;容易因磨料呈颗粒脱落而导致砂轮的失效,在难加工材料的高效磨削时尤其明显;另外,磨料出露高度低,容肩空间小,磨削时很容易因切肩的粘附堵塞而失效。
发明内容
[0004] 为了解决上述问题,本发明提出一种具有良好的抗冲击性和形状保持性,能承受高速磨削过程中的较大载荷的CBN砂轮,其具体的技术方案如下:
一种CBN砂轮,其包括钢芯、磨料圈,钢芯和磨料圈通过结合剂结合在一起,磨料圈由以下质量百分比的原料制成:CBN磨料30~70%,金属结合剂20~60%,辅助粘结剂2〜10%。
[0005] 优化地,金属结合剂由以下材料组成:Cu粉40〜60%,Sn粉20_40%,TiH2粉2-20%;各组分质量分数之和为100%。
[0006] 优化地,Cu粉、Sn粉和TiH2粉的粒径范围均为10-150μπι。
[0007] 优化地,具有以下组成与体积百分比:CBN磨料12.5〜50%,金属结合剂5〜45%,孔隙I5-45%ο
[0008] 优化地,辅助粘结剂设置为丙烯酸乳液。
[0009] —种CBN砂轮的生产方法,其特征在于:其包括下列步骤:
Α、混料:按权利要求1、2的配方取CBN磨料,Cu粉,Sn粉和TiH2粉混合,加入辅助粘结剂混合2〜Sh,得到混合料;
B、烘干:将步骤A混合均匀的原料加热至100~ 150 ° C,保温3〜4小时; C、成型:将步骤B烘干后的原料过筛,均匀投入模具内,于液压机冷压成型,压力为50~120 MPa,保压30~60分钟;
D、烧结:将步骤C砂轮磨料圈生坯在氩气保护气氛下烧结,其烧结温度为800~1050 °C,升温速率3〜10 °C/分钟,保温时间30~120分钟,之后冷却,低于50 °C出炉;
E、粘结:使用树脂胶粘剂将烧结后的砂轮磨料圈坯体与钢芯粘合,去除毛边,修整成型。
[0010] 优化地,Cu粉、Sn粉和T iH2粉的粒径范围设置为I O-150μπι。
[0011] 优化地,步骤A用混合机混料,步骤B中用烘干机烘干,步骤D中用烧结炉烧结。
[0012] 本发明的CBN砂轮具有良好的热导率有利于降低磨削温度,从而降低功率损耗,提高磨削速度;配方中的辅助粘结剂有利于孔隙的形成,结合金属结合剂把持力强的特点,可以有效增大容肩空间,磨料的利用更加充分;砂轮具有磨削效率高、磨削温度低、功率损耗低、加工精度好、使用寿命长等特点。
[0013] 本发明提供的制备方法,烧结时间短,有利于保持磨料特性,金属结合剂、孔隙率和烧结温度、时间的控制,使砂轮在工作过程中具有良好的热导率和较大的容肩空间,在高速磨削过程中也不易堵塞,磨削锋利,磨削精度高,且具有自锐性。
具体实施方式
[0014]下面结合具体实施案例对本发明作进一步说明,但本发明并不局限于这些实施例。
[0015] 实施例1:
本实施例的金属结合剂,由以下质量百分比的原料组分组成:Cu 52%, Sn 32%,TiH216%;各组分质量分数之和为100%;上述原料为Cu粉、Sn粉和TiH2粉;上述原料粉粒径均为 30μηι。
[0016] 本实施例的CBN砂轮,由以下质量百分比的原料制成:CBN磨料48%,金属结合剂粉45%,辅助粘结剂7%。上述CBN磨料的粒径为20μπι。
[0017] 上述CBN砂轮的制备方法如下:
(1)混料:按配方取CBN磨料,Cu粉,Sn粉和TiH2粉放入混合机中,加入辅助粘结剂混合4h,得到混合料;
(2)烘干:将步骤I混合均匀的原料放入烘干机中加热至120°C,保温3h;
(3)成型:将步骤2烘干后的原料过筛,均匀投入模具内,于液压机冷压成型,压力为70MPa,保压 40min;
(4)烧结:将砂轮磨料圈生坯置入烧结炉内,在氩气保护气氛下烧结,其烧结温度为950°C,升温速率5°C/min,保温时间30min,之后随炉冷却,低于50°C出炉;
(5)粘结:使用树脂胶粘剂将烧结后的砂轮磨料圈坯体与钢芯粘合,在砂轮修整磨床上去除毛边,修整成型。
[0018] 本实施例的辅助粘结剂设置为丙烯酸乳液。
[0019] 实施例2:
本实施例的金属结合剂,由以下质量百分比的原料组分组成:Cu粉52%,Sn粉32%,TiH2粉16%;各组分质量分数之和为100%;上述原料粉粒径均为60μπι。
[0020] 本实施例的CBN砂轮,由以下质量百分比的原料制成:CBN磨料45%,金属结合剂粉48%,辅助粘结剂7%。上述CBN磨料的粒径为45μπι。
[0021] CBN砂轮的制备过程如下:
(1)混料:按配方取CBN磨料,Cu粉,Sn粉和TiH2粉,加入辅助粘结剂人工混合4h,得到混合料;
(2)烘干:将步骤I混合均匀的原料放入到加热器中,加热至120°C,保温3h;
(3)成型:将步骤2烘干后的原料过筛,均匀投入模具内,于液压机冷压成型,压力为70MPa,保压 40min;
(4)烧结:将砂轮磨料圈生坯在氩气保护气氛下烧结,其烧结温度为950°C,升温速率5°C /min,保温时间30min,之后冷却,低于50°C出炉;
(5)粘结:使用树脂胶粘剂将烧结后的砂轮磨料圈坯体与钢芯粘合,在砂轮修整磨床上去除毛边,修整成型。
[0022] 实施例3:
本实施例的金属结合剂,由以下质量百分比的原料组分组成:Cu粉60%,Sn粉20%,TiH2粉20%;各组分质量分数之和为100%;上述原料粉粒径均为80μπι。
[0023] 本实施例的CBN砂轮,由以下质量百分比的原料制成:CBN磨料45%,金属结合剂粉48%,辅助粘结剂7%。上述CBN磨料的粒径为80μπι。
[0024] CBN砂轮的制备过程如下:
(1)混料:按配方取CBN磨料,Cu粉,Sn粉和TiH2粉放入混合机中,加入辅助粘结剂混合4h,得到混合料;
(2)烘干:将步骤I混合均匀的原料放入烘干机中加热至120°C,保温3h;
(3)成型:将步骤2烘干后的原料过筛,均匀投入模具内,于液压机冷压成型,压力为70MPa,保压 40min;
(4)烧结:将砂轮磨料圈生坯置入烧结炉内,在氩气保护气氛下烧结,其烧结温度为950°C,升温速率5 °C /min,保温时间30min,之后随炉冷却,低于50°C出炉;
(5)粘结:使用树脂胶粘剂将烧结后的砂轮磨料圈坯体与钢芯粘合,在砂轮修整磨床上去除毛边,修整成型。
[0025] 实施例4:
本实施例的金属结合剂,由以下质量百分比的原料组分组成:Cu粉50%,Sn粉48%,TiH2粉2%;各组分质量分数之和为100%;上述原料粉粒径均为ΙΟΟμπι。
[0026] 本实施例的CBN砂轮,由以下质量百分比的原料制成:CBN磨料45%,金属结合剂粉48%,辅助粘结剂7%。上述CBN磨料的粒径为80μπι。
[0027] CBN砂轮的制备过程如下:
(1)混料:按配方取CBN磨料,Cu粉,Sn粉和TiH2粉放入混合机中,加入辅助粘结剂混合4h,得到混合料;
(2)烘干:将步骤I混合均匀的原料放入烘干机中加热至120°C,保温3h;
(3)成型:将步骤2烘干后的原料过筛,均匀投入模具内,于液压机冷压成型,压力为70MPa,保压 40min;
(4)烧结:将砂轮磨料圈生坯置入烧结炉内,在氩气保护气氛下烧结,其烧结温度为950°C,升温速率5 °C /min,保温时间30min,之后随炉冷却,低于50°C出炉;
(5)粘结:使用树脂胶粘剂将烧结后的砂轮磨料圈坯体与钢芯粘合,在砂轮修整磨床上去除毛边,修整成型。
[0028] 实施例5:
本实施例的金属结合剂,由以下质量百分比的原料组分组成:Cu 52%, Sn 32%,TiH216%;各组分质量分数之和为100%;上述原料为Cu粉、Sn粉和TiH2粉;上述原料粉粒径均为150ymo
[0029] 本实施例的CBN砂轮,由以下质量百分比的原料制成:CBN磨料45%,金属结合剂粉48%,辅助粘结剂7%。上述CBN磨料的粒径为80μπι。
[0030] CBN砂轮的制备过程如下:
(1)混料:按配方取CBN磨料,Cu粉,Sn粉和TiH2粉放入混合机中,加入辅助粘结剂混合4h,得到混合料;
(2)烘干:将步骤I混合均匀的原料放入烘干机中加热至120°C,保温3h;
(3)成型:将步骤2烘干后的原料过筛,均匀投入模具内,于液压机冷压成型,压力为70MPa,保压 40min;
(4)烧结:将砂轮磨料圈生坯置入烧结炉内,在氩气保护气氛下烧结,其烧结温度为950°C,升温速率5 °C /min,保温时间30min,之后随炉冷却,低于50°C出炉;
(5)粘结:使用树脂胶粘剂将烧结后的砂轮磨料圈坯体与钢芯粘合,在砂轮修整磨床上去除毛边,修整成型。
[0031]以上所述的具体实施例,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所应理解的是,以上所述仅为本发明的具体实施例而已,并不用于限制本发明,凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。

Claims (8)

1.一种CBN砂轮,其包括钢芯、磨料圈,钢芯和磨料圈通过结合剂结合在一起,其特征在于:磨料圈由以下质量百分比的原料制成:CBN磨料30~70%,金属结合剂20~60%,辅助粘结剂2-10%ο
2.根据权利要求1所述的CBN砂轮,其特征在于:金属结合剂由以下材料组成:Cu粉40〜60%,Sn粉20-40%,TiH2粉2-20%;各组分质量分数之和为100%。
3.根据权利要求1所述的CBN砂轮,其特征在于:Cu粉、Sn粉和TiH2粉的粒径范围均为10-150μπιο
4.根据权利要求1所述的CBN砂轮,其特征在于:磨料圈具有以下组成与体积百分比:CBN磨料12.5〜50%,金属结合剂5〜45%,孔隙15〜45%。
5.根据权利要求1所述的CBN砂轮,其特征在于:辅助粘结剂设置为丙烯酸乳液。
6.一种CBN砂轮的生产方法,其特征在于:其包括下列步骤: Α、混料:按权利要求1、2的配方取CBN磨料,Cu粉,Sn粉和TiH2粉混合,加入辅助粘结剂混合2〜8h,得到混合料; B、烘干:将步骤A混合均匀的原料加热至100~150 ◦ C,保温3〜4小时; C、成型:将步骤B烘干后的原料过筛,均匀投入模具内,于液压机冷压成型,压力为50~120 MPa,保压30~60分钟; D、烧结:将步骤C砂轮磨料圈生坯在氩气保护气氛下烧结,其烧结温度为800~1050 °C,升温速率3〜10 °C/分钟,保温时间30~120分钟,之后冷却,低于50 °C出炉; E、粘结:使用树脂胶粘剂将烧结后的砂轮磨料圈坯体与钢芯粘合,去除毛边,修整成型。
7.根据权利要求书6所述的CBN砂轮,其特征在于:步骤A用混合机混料,步骤B中用烘干机烘干,步骤D中用烧结炉烧结。
8.根据权利要求书6所述的CBN砂轮,其特征在于:Cu粉、Sn粉和TiH2粉的粒径范围均为10-150μπιο
CN201611071584.7A 2016-11-29 2016-11-29 一种金属结合剂立方氮化硼磨轮 Active CN106625297B (zh)