CN102728782A - 一种以粘土为粘结剂的型砂 - Google Patents
一种以粘土为粘结剂的型砂 Download PDFInfo
- Publication number
- CN102728782A CN102728782A CN2012101870154A CN201210187015A CN102728782A CN 102728782 A CN102728782 A CN 102728782A CN 2012101870154 A CN2012101870154 A CN 2012101870154A CN 201210187015 A CN201210187015 A CN 201210187015A CN 102728782 A CN102728782 A CN 102728782A
- Authority
- CN
- China
- Prior art keywords
- parts
- clay
- sand
- cement
- molding sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种以粘土为粘结剂的型砂及其制作方法，其主要是将组成原料硅灰石粉30-40、回用砂20-30、煤粉5-10、水滑石粉5-10、糠4-8、石膏3-5、水泥2-4、粘土3-8，先干混均匀，再加水混合，混好后放砂、造型、浇铸冷却分离得到成品。本发明制作方法简单，配方合理、成本低廉、生产效率高，利用香菇栽培袋料出菇后废料，烘干后粉碎，作为型砂原料，可以变废为宝，同时水泥、石膏、粘土作为粘结剂，强度高，透气性好。
Description
技术领域
本发明涉及一种以粘土为粘结剂的型砂及其制作方法，属于铸造工业领域。
背景技术
型砂是在砂型铸造中用来造型的材料，型砂一般由铸造砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成，也可用天然含粘土的硅砂，通常的铸铝用的型砂配方中型砂粒径太大或太小，型砂料径太大，虽然透气性较好，但是铝砂件表面比较粗糙，光洁度不好，型砂料径太小，导致砂型透气性不好，铝铸件有气孔好产生。型砂按所用粘结剂不同，可分为粘土砂、水玻璃砂、水泥砂、硅灰石粉等，以粘土砂、水玻璃砂及硅灰石粉用的最多。
发明内容
为了缓解现有技术的不足和缺陷，本发明的目的在于提供一种以粘土为粘结剂的型砂及其制作方法。
为了实现上述目的本发明采用如下技术方案：
以粘土为粘结剂的型砂，其组成原料的重量份为：硅灰石粉30-40、回用砂20-30、煤粉5-10、水滑石粉5-10、糠4-8、石膏3-5、水泥2-4、粘土3-8和水适量。
以粘土为粘结剂的型砂，其组成原料的重量份为：硅灰石粉35、回用砂25、煤粉8、水滑石粉8、糠6、石膏4、水泥3、粘土5和水适量。
本发明的有益效果：
本发明制作方法简单，配方合理、成本低廉、生产效率高，利用香菇栽培袋料出菇后废料，烘干后粉碎，作为型砂原料，可以变废为宝，同时水泥、石膏、粘土作为粘结剂，强度高，透气性好。
具体实施方式
实施例1：以粘土为粘结剂的型砂，其组成原料的重量份为：硅灰石粉30、回用砂20、煤粉5、水滑石粉5、糠4、石膏3、水泥2、粘土3和水适量。
以粘土为粘结剂的型砂的制作方法，包括以下步骤：
（1）按组成原料的重量份混合硅灰石粉、回用砂、煤粉、水滑石粉、糠、石膏、水泥和粘土，先干混10-20秒，再加水混合3-5分钟，混好后放砂；
（2）将步骤（1）得到的混合物放入储砂斗中，造型，分离得到成品。
实施例2：以粘土为粘结剂的型砂，其组成原料的重量份为：硅灰石粉35、回用砂25、煤粉8、水滑石粉8、糠6、石膏4、水泥3、粘土5和水适量。
以粘土为粘结剂的型砂的制作方法，包括以下步骤：
（1）按组成原料的重量份混合硅灰石粉、回用砂、煤粉、水滑石粉、糠、石膏、水泥和粘土，先干混10-20秒，再加水混合3-5分钟，混好后放砂；
（2）将步骤（1）得到的混合物放入储砂斗中，造型，分离得到成品。
实施例3：以粘土为粘结剂的型砂，其组成原料的重量份为：硅灰石粉40、回用砂30、煤粉10、水滑石粉10、糠8、石膏5、水泥4、粘土8和水适量。
以粘土为粘结剂的型砂的制作方法，包括以下步骤：
（1）按组成原料的重量份混合硅灰石粉、回用砂、煤粉、水滑石粉、糠、石膏、水泥和粘土，先干混10-20秒，再加水混合3-5分钟，混好后放砂；
（2）将步骤（1）得到的混合物放入储砂斗中，造型，分离得到成品。
本发明制得的铸造型砂的工艺性能：
湿压强度：0.095MPa，透气率：79.5%，热湿拉强度：320kPa，破碎指数：80%。
Claims (2)
1.一种以粘土为粘结剂的型砂，其特征在于其组成原料的重量份为：硅灰石粉30-40、回用砂20-30、煤粉5-10、水滑石粉5-10、糠4-8、石膏3-5、水泥2-4、粘土3-8和水适量。
2.根据权利要求1所述的以粘土为粘结剂的型砂，其特征在于其组成原料的重量份为：硅灰石粉35、回用砂25、煤粉8、水滑石粉8、糠6、石膏4、水泥3、粘土5和水适量。