CN102814459A - 一种环保型铸造型砂 - Google Patents
一种环保型铸造型砂 Download PDFInfo
- Publication number
- CN102814459A CN102814459A CN2012103011973A CN201210301197A CN102814459A CN 102814459 A CN102814459 A CN 102814459A CN 2012103011973 A CN2012103011973 A CN 2012103011973A CN 201210301197 A CN201210301197 A CN 201210301197A CN 102814459 A CN102814459 A CN 102814459A
- Authority
- CN
- China
- Prior art keywords
- sand
- parts
- molding sand
- casting molding
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种以水泥为粘结剂的型砂及其制作方法,其主要是将组成原料回用砂80-90、石膏3-8、铬铁矿砂20-30、锯末80-90、凹凸棒土2-5、面粉2-4、水泥5-10和水适量,先干混,再加水混合,混好后放砂、造型、浇铸和冷却分离得到成品。本发明制作方法简单,配方合理、成本低廉、增加了湿压强度,而且透气性也很好。
Description
技术领域
本发明涉及铸造领域,具体的说是一种环保型铸造型砂。
背景技术
型砂是在砂型铸造中用来造型的材料,型砂一般由铸造砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成,也可用天然含粘土的硅砂,通常的铸铁用的型砂配方中型砂粒径太大或太小,型砂料径太大,虽然透气性较好,但是铝砂件表面比较粗糙,光洁度不好,型砂料径太小,导致砂型透气性不好,铝铸件有气孔好产生。型砂按所用粘结剂不同,可分为粘土砂、水玻璃砂、水泥砂、树脂砂等,以粘土砂、水玻璃砂及树脂砂用的最多。
发明内容
为了缓解现有技术的不足和缺陷,本发明的目的在于提供一种环保型铸造型砂。
为了实现上述目的本发明采用如下技术方案:
一种环保型铸造型砂,按其组成原料的重量份为:硅灰石粉30-40、回用砂20-30、石膏粉5-7、膨润土15-20、碳渣粉5-8、凹凸棒土1-3、面粉2-4、树脂5-7和水适量,以上原料按重量份称取搅拌均匀即可。
本发明的有益效果:
本发明制作方法简单,配方合理、成本低廉、增加了湿压强度,而且透气性也很好。
具体实施方式
实施例1:一种环保型铸造型砂,其特征在于其组成原料的重量份为:硅灰石粉30-40、回用砂20-30、石膏粉5-7、膨润土15-20、碳渣粉5-8、凹凸棒土1-3、面粉2-4、树脂5-7和水适量,以上原料按重量份称取搅拌均匀即可。
实施例2:一种环保型铸造型砂,按其组成原料的重量份为:硅灰石粉30、回用砂20、石膏粉5、膨润土15、碳渣粉5、凹凸棒土1、面粉2、树脂5和水适量,以上原料按重量份称取搅拌均匀即可。
Claims (1)
1.一种环保型铸造型砂,其特征在于其组成原料的重量份为:硅灰石粉30-40、回用砂20-30、石膏粉5-7、膨润土15-20、碳渣粉5-8、凹凸棒土1-3、面粉2-4、树脂5-7和水适量,以上原料按重量份称取搅拌均匀即可。