CN107252874A - 一种提高铸件密实度的铁模型砂 - Google Patents

一种提高铸件密实度的铁模型砂 Download PDF

Info

Publication number
CN107252874A
CN107252874A CN201710521136.0A CN201710521136A CN107252874A CN 107252874 A CN107252874 A CN 107252874A CN 201710521136 A CN201710521136 A CN 201710521136A CN 107252874 A CN107252874 A CN 107252874A
Authority
CN
China
Prior art keywords
weight
parts
molding sand
swage
glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710521136.0A
Other languages
English (en)
Inventor
胡宗道
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HUIHUANG MACHINERY MANUFACTURING CO LTD
Original Assignee
ANHUI HUIHUANG MACHINERY MANUFACTURING CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HUIHUANG MACHINERY MANUFACTURING CO LTD filed Critical ANHUI HUIHUANG MACHINERY MANUFACTURING CO LTD
Priority to CN201710521136.0A priority Critical patent/CN107252874A/zh
Publication of CN107252874A publication Critical patent/CN107252874A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种提高铸件密实度的铁模型砂，它是由以下重量份的组分组成：型砂98‑112重量份、石子32‑36重量份、硫铝酸盐水泥15‑19重量份、硼酸1‑5重量份、氟硅酸钠4‑6重量份、铸石粉8‑12重量份、纳米二氧化钛2‑4重量份、纳米二氧化锑1‑3重量份、玻璃纤维1‑3重量份、水120‑140重量份。本发明提供一种提高铸件密实度的铁模型砂，组分配制科学合理，颗粒分布更加均匀，颗粒结合更加牢固，能够有效提高制得的铸件的密实度，耐热性更强，抗压强度更高，耐酸碱腐蚀性更强等。

Description

一种提高铸件密实度的铁模型砂
技术领域
本发明涉及机械制造技术领域，特别涉及一种提高铸件密实度的铁模型砂。
背景技术
铸造是生产零件毛坯的主要方法之一，其成型方法主要是将铁件加热熔化，使其成为具有流动性的铁液，然后浇铸到具有一定形状的铸型型腔内，在重力的作用下注满型腔，冷却并凝固成铸件或零件。传统的铸造工艺包括以下步骤 ：A、根据产品的形状制出造型制芯用的模具，B、将模具放入砂箱的上、下砂箱进行填砂、紧实、起模后合箱，C、将熔化后的铁液浇注入砂箱中的型腔内，最后脱砂清理铸件，得铸件。目前，这种工艺制造的铸件硬度差，且铸砂型结构稳定性差、结构不标准从而导致铸件后的铸件结构不符合标准，影响铸件的合格率。
型砂在铸造中用来造型的材料。型砂一般由铸造用原砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成。型砂按所用粘结剂不同，可分为粘土砂、水玻璃砂、水泥砂、树脂砂等。以粘土砂、水玻璃砂及树脂砂用的最多。
型砂在铸造生产中的作用极为重要，因型砂的质量不好而造成的铸件废品约占铸件总废品的30~50%。通常对型砂的要求是:①具有较高的强度和热稳定性，以承受各种外力和高温的作用。②良好的流动性，即型砂在外力或本身重力作用下砂粒间相互移动的能力。③一定的可塑性，即型砂在外力作用下变形，当外力去除后能保持所给予的形状的能力。④较好的透气性，即型砂孔隙透过气体的能力。⑤高的溃散性，又称出砂性，即在铸件凝固后型砂是否容易破坏，是否容易从铸件上清除的性能。
本发明提供了一种提高铸件密实度的铁模型砂。
发明内容
本发明所要解决的技术问题在于：提供了一种提高铸件密实度的铁模型砂。
为解决上述技术问题，本发明提供了一种提高铸件密实度的铁模型砂，它是由以下重量份的组分组成：型砂98-112重量份、石子32-36重量份、硫铝酸盐水泥15-19重量份、硼酸1-5重量份、氟硅酸钠4-6重量份、铸石粉8-12重量份、纳米二氧化钛2-4重量份、纳米二氧化锑1-3重量份、玻璃纤维1-3重量份、水120-140重量份。
进一步地，它是由以下重量份的组分组成：型砂98重量份、石子36重量份、硫铝酸盐水泥15重量份、硼酸5重量份、氟硅酸钠4重量份、铸石粉12重量份、纳米二氧化钛2重量份、纳米二氧化锑3重量份、玻璃纤维1重量份、水140重量份。
进一步地，它是由以下重量份的组分组成：型砂105重量份、石子34重量份、硫铝酸盐水泥17重量份、硼酸3重量份、氟硅酸钠5重量份、铸石粉10重量份、纳米二氧化钛3重量份、纳米二氧化锑2重量份、玻璃纤维2重量份、水130重量份。
进一步地，它是由以下重量份的组分组成：型砂112重量份、石子32重量份、硫铝酸盐水泥19重量份、硼酸1重量份、氟硅酸钠6重量份、铸石粉8重量份、纳米二氧化钛4重量份、纳米二氧化锑1重量份、玻璃纤维3重量份、水140重量份。
本发明有益的技术效果在于：本发明提供一种提高铸件密实度的铁模型砂，组分配制科学合理，颗粒分布更加均匀，颗粒结合更加牢固，能够有效提高制得的铸件的密实度，耐热性更强，抗压强度更高，耐酸碱腐蚀性更强等。
具体实施方式
以下将结合实施例来详细说明本发明的实施方式，借此对本发明如何应用技术手段来解决技术问题，并达成技术效果的实现过程能充分理解并据以实施。
需要说明的是，为节省说明书撰写篇幅，避免不必要的重复和浪费，在不冲突的情况下，本申请中的实施例及实施例中的特征可以相互组合。
实施例1一种提高铸件密实度的铁模型砂
一种提高铸件密实度的铁模型砂，它是由以下重量份的组分组成：型砂98重量份、石子36重量份、硫铝酸盐水泥15重量份、硼酸5重量份、氟硅酸钠4重量份、铸石粉12重量份、纳米二氧化钛2重量份、纳米二氧化锑3重量份、玻璃纤维1重量份、水140重量份。
实施例2一种提高铸件密实度的铁模型砂
一种提高铸件密实度的铁模型砂，它是由以下重量份的组分组成：型砂105重量份、石子34重量份、硫铝酸盐水泥17重量份、硼酸3重量份、氟硅酸钠5重量份、铸石粉10重量份、纳米二氧化钛3重量份、纳米二氧化锑2重量份、玻璃纤维2重量份、水130重量份。
实施例3一种提高铸件密实度的铁模型砂
一种提高铸件密实度的铁模型砂，它是由以下重量份的组分组成：型砂112重量份、石子32重量份、硫铝酸盐水泥19重量份、硼酸1重量份、氟硅酸钠6重量份、铸石粉8重量份、纳米二氧化钛4重量份、纳米二氧化锑1重量份、玻璃纤维3重量份、水140重量份。
所有上述的首要实施这一知识产权，并没有设定限制其他形式的实施这种新产品和/或新方法。本领域技术人员将利用这一重要信息，上述内容修改，以实现类似的执行情况。但是，所有修改或改造基于本发明新产品属于保留的权利。

Claims (4)

1.一种提高铸件密实度的铁模型砂，其特征在于，它是由以下重量份的组分组成：型砂98-112重量份、石子32-36重量份、硫铝酸盐水泥15-19重量份、硼酸1-5重量份、氟硅酸钠4-6重量份、铸石粉8-12重量份、纳米二氧化钛2-4重量份、纳米二氧化锑1-3重量份、玻璃纤维1-3重量份、水120-140重量份。
2.根据权利1所述的一种提高铸件密实度的铁模型砂，其特征在于，它是由以下重量份的组分组成：型砂98重量份、石子36重量份、硫铝酸盐水泥15重量份、硼酸5重量份、氟硅酸钠4重量份、铸石粉12重量份、纳米二氧化钛2重量份、纳米二氧化锑3重量份、玻璃纤维1重量份、水140重量份。
3.根据权利1所述的一种提高铸件密实度的铁模型砂，其特征在于，它是由以下重量份的组分组成：型砂105重量份、石子34重量份、硫铝酸盐水泥17重量份、硼酸3重量份、氟硅酸钠5重量份、铸石粉10重量份、纳米二氧化钛3重量份、纳米二氧化锑2重量份、玻璃纤维2重量份、水130重量份。
4.根据权利1所述的一种提高铸件密实度的铁模型砂，其特征在于，它是由以下重量份的组分组成：型砂112重量份、石子32重量份、硫铝酸盐水泥19重量份、硼酸1重量份、氟硅酸钠6重量份、铸石粉8重量份、纳米二氧化钛4重量份、纳米二氧化锑1重量份、玻璃纤维3重量份、水140重量份。
CN201710521136.0A 2017-06-30 2017-06-30 一种提高铸件密实度的铁模型砂 Pending CN107252874A (zh)