CN103521693A - 一种高效激冷型砂及其制备方法 - Google Patents

一种高效激冷型砂及其制备方法 Download PDF

Info

Publication number
CN103521693A
CN103521693A CN201310481144.9A CN201310481144A CN103521693A CN 103521693 A CN103521693 A CN 103521693A CN 201310481144 A CN201310481144 A CN 201310481144A CN 103521693 A CN103521693 A CN 103521693A
Authority
CN
China
Prior art keywords
parts
molding sand
efficiency
sand
chilling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310481144.9A
Other languages
English (en)
Inventor
孙爱琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Tenver Precision Casting Co Ltd
Original Assignee
Hefei Tenver Precision Casting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Tenver Precision Casting Co Ltd filed Critical Hefei Tenver Precision Casting Co Ltd
Priority to CN201310481144.9A priority Critical patent/CN103521693A/zh
Publication of CN103521693A publication Critical patent/CN103521693A/zh
Pending legal-status Critical Current

Abstract

一种高效激冷型砂,其特征在于由下列重量份的原料制成:铬铁矿砂240-260、矾土100-120、棕刚玉20-30、纳米碳粉1-2、铝酸钙水泥1-2、α-Al2O3微粉3-4、钢纤维10-12、三聚磷酸钠2-3、二甲基硅油1-2、二茂铁1-2、呋喃树脂4-5、苯磺酸2-3、水适量。本发明使用了铬铁矿砂、矾土,经煅烧,结合加三聚磷酸钠、呋喃树脂等研磨,再高温煅烧使得型砂具有优异的粘结性、可塑性、热稳定性、透气性、分散性;通过使用α-Al2O3微粉,更增加了分散性,使型砂均匀;通过使用纳米碳粉增加了导热性能,增强了激冷铸件效果,本发明易于造型、制芯,解决铸件缩孔、缩松效果达90%以上,提高铸件成品率。

Description

一种高效激冷型砂及其制备方法
技术领域
[0001] 本发明涉及一种铸造领域,尤其涉及一种高效激冷型砂及其制备方法。
背景技术
[0002] 型砂是在铸造中用来造型的材料。型砂一般由铸造用原砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成,也可用天然含粘土的硅砂,通常的铸铝用的型砂配方中型砂粒径太大或太小,型砂料径太大,虽然透气性较好,但是铝砂件表面比较粗糙,光洁度不好,型砂料径太小,导致砂型透气性不好,铝铸件有气孔产生。国内外广泛使用的煤粉粘土湿型砂,一般由原砂、粘结剂、煤粉添加物等与水混制而成,具有一定的防粘砂效果和材料成本低、生产效率高的优点,但其消耗量大、排放严重、在铸造过程煤粉燃烧分解产生有毒气体污染。
[0003] 型砂按所用粘结剂不同,可分为粘土砂、水玻璃砂、水泥砂、石英砂等,以粘土砂、水玻璃砂及石英砂用的最多。型砂在铸造生产中的作用极为重要,因型砂的质量不好而造成的铸件废品约占铸件总废品的30〜50%。通常对型砂的要求是:1、具有较高的强度和热稳定性,以承受各种外力和高温的作用。2、良好的流动性,即型砂在外力或本身重力作用下砂粒间相互移动的能力。3、一定的可塑性,即型砂在外力作用下变形,当外力去除后能保持所给予的形状的能力。4、较好的透气性,即型砂孔隙透过气体的能力。5、高的溃散性,又称出砂性,即在铸件凝固后型砂是否容易破坏,是否容易从铸件上清除的性能。
[0004] 目前的铸造领域发展迅速,对于铸钢件和铸铁件的性能要求更高,从而要求进一步提升型砂的性能。
发明内容
[0005] 本发明的目的在于提供一种高效激冷型砂及其制备方法,该型砂具有高的导热性、可塑性好、透气性好、粘结性好的特点。
[0006] 本发明的技术方案如下:
一种高效激冷型砂,其特征在于由下列重量份的原料制成:铬铁矿砂240-260、矾土100-120、棕刚玉20-30、纳米碳粉1-2、铝酸钙水泥1-2、a -Al203微粉3-4、钢纤维10-12、三聚磷酸钠2-3、二甲基硅油1-2、二茂铁1-2、呋喃树脂4-5、苯磺酸2-3、水适量;
所述高效激冷型砂的制备方法,其特征在于包括以下步骤:将铬铁矿砂、矾土放入520-540°C煅烧炉中煅烧4-5小时,然后,取出,粉碎成250-350目粉末,然后加入三聚磷酸钠、二茂铁、适量水,搅拌分散,练泥,送入1420-1450°C煅烧炉中煅烧3-5小时,取出粉碎至50-100目,得到煅烧料;将铝酸钙水泥、a-A1203微粉、钢纤维、三聚磷酸钠、二甲基硅油混合,研磨30-40分钟,与煅烧料、其它剩余成分混合15-20分钟,即得。
[0007] 本发明的有益效果
本发明使用了铬铁矿砂、矾土,经煅烧,结合加三聚磷酸钠、呋喃树脂等研磨,再高温煅烧使得型砂具有优异的粘结性、可塑性、热稳定性、透气性、分散性;通过使用a-A1203微粉,更增加了分散性,使型砂均匀;通过使用纳米碳粉增加了导热性能,增强了激冷铸件效果,本发明易于造型、制芯,解决铸件缩孔、缩松效果达90%以上,提高铸件成品率。
具体实施方式
[0008] 一种高效激冷型砂,由下列重量份(公斤)的原料制成:铬铁矿砂250、矾土 110、棕刚玉25、纳米碳粉1.5、铝酸钙水泥1.5、α -Al203微粉3.4、钢纤维11、三聚磷酸钠2、二甲基硅油1.4、二茂铁1.5、呋喃树脂4、苯磺酸2.5、水适量;
所述高效激冷型砂的制备方法,包括以下步骤:将铬铁矿砂、矾土放入530°C煅烧炉中煅烧4小时,然后,取出,粉碎成300目粉末,然后加入三聚磷酸钠、二茂铁、适量水,搅拌分散,练泥,送入1440°C煅烧炉中煅烧4小时,取出粉碎至70目,得到煅烧料;将铝酸钙水泥、α -Α1203微粉、钢纤维、三聚磷酸钠、二甲基硅油混合,研磨34分钟,与煅烧料、其它剩余成分混合18分钟,即得。
[0009] 本发明制得的型砂的工艺性能:
湿压强度:0.105Mpa,透气率:101%,热湿拉强度:421Kpa,破碎指数:87%。

Claims (2)

1.一种高效激冷型砂,其特征在于由下列重量份的原料制成:铬铁矿砂240-260、矾土100-120、棕刚玉20-30、纳米碳粉1-2、铝酸钙水泥1-2、α -Al203微粉3-4、钢纤维10-12、三聚磷酸钠2-3、二甲基硅油1-2、二茂铁1-2、呋喃树脂4-5、苯磺酸2_3、水适量。
2.根据权利要求1所述高效激冷型砂的制备方法,其特征在于包括以下步骤:将铬铁矿砂、矾土放入520-540°C煅烧炉中煅烧4-5小时,然后,取出,粉碎成250-350目粉末,然后加入三聚磷酸钠、二茂铁、适量水,搅拌分散,练泥,送入1420-145(TC煅烧炉中煅烧3-5小时,取出粉碎至50-100目,得到煅烧料;将铝酸钙水泥、α-Α1203微粉、钢纤维、三聚磷酸钠、二甲基硅油混合,研磨30-40分钟,与煅烧料、其它剩余成分混合15-20分钟,即得。
CN201310481144.9A 2013-10-16 2013-10-16 一种高效激冷型砂及其制备方法 Pending CN103521693A (zh)