CN102677261A - 一种防断裂铜氨面料及其生产方法 - Google Patents
一种防断裂铜氨面料及其生产方法 Download PDFInfo
- Publication number
- CN102677261A CN102677261A CN2012101658141A CN201210165814A CN102677261A CN 102677261 A CN102677261 A CN 102677261A CN 2012101658141 A CN2012101658141 A CN 2012101658141A CN 201210165814 A CN201210165814 A CN 201210165814A CN 102677261 A CN102677261 A CN 102677261A
- Authority
- CN
- China
- Prior art keywords
- cuprammonium
- breakage
- fabric
- warping
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种防断裂铜氨面料,由经纱和纬纱织造而成,所述经纱和所述纬纱均具有75D至150D铜氨长丝;在所述面料的两侧均设置有数量相同的若干涤纶丝。本发明同时还公开了一种防断裂铜氨面料的生产方法,包括以下步骤:1)选取铜氨长丝为原料;2)整经,整经完成后整经轴上各处卷绕的铜氨丝的厚度之差不大于5mm,并且在整经两边放置对应的涤纶丝;3)浆丝,浆丝过程中浆丝机的引纱辊的速度要小于上浆辊的速度;4)并轴,幷轴时将两边8-12根涤纶丝分成相等两组放置在最上边;5)穿综丝、插筘;6)上机织造。与现有技术相比,本发明的面料具有柔软滑顺的触感,成本低廉,符合绿色环保要求,而且断头率低,整体强度高于同类型产品,而且面料整体不易断裂。该方法操作简单,有效解决了在生产过程中铜氨纤维易断裂的问题,降低了纯铜氨面料的生产难度。
Description
技术领域
本发明涉及一种纺织面料,尤其涉及一种防断裂铜氨面料,本发明同时还涉及该面料的生产方法。
背景技术
铜氨纤维是一种再生纤维素纤维,它是将棉短绒等天然纤维素原料溶解在氢氧化铜或碱性铜盐的浓氨溶液内,配成纺丝液,在凝固浴中铜氨纤维素分子化学物分解再生出纤维素,生成的水合纤维素经后加工即得到铜氨纤维。铜氨纤维的截面呈圆形,无皮芯结构,制得的单丝较细,所以铜氨纤维面料的手感柔软,光泽柔和,具有真丝感,吸湿性能好。但其湿强力低、湿延伸率大,因此导致铜氨面料的加工难度大,在织造过程中铜氨纤维易断裂,而且在织造完成后,纯铜氨面料的整体强度偏低,吸湿后面料容易破裂
因此,目前,铜氨纤维用于面料织造时通常是与其他纤维进行混纺,如申请号为200910145158.7的中国发明专利,公开了 羊毛/铜氨纤维混纺面料的染色方法;如另一申请号为200910049036.8的中国发明专利,公开了 一种桑蚕丝和铜氨丝交织面料及其织造方法。
当然也有专利公开了纯铜氨面料的生产方法,这一方面的资料可以参考如申请号为200910186478.7的中国发明专利,其公开了 一种铜氨面料的制造方法。但是在该专利中其主要改进的地方在于纯铜氨面料的染整部分,但事实上,当铜氨纤维织造成坯布后,由于其整体性,纯铜氨面料的强度受其特性的影响已经较小。由于铜氨纤维湿强力低、湿延伸率大的特性,纯铜氨面料生产工艺的难点在于其织造过程,该专利申请在这一方面没有提及。
发明内容
本发明针对现有技术中的不足,提供了一种成本低廉,强度高,不易破裂,生产过程中断头率低的防断裂铜氨面料。
为解决上述技术问题,本发明通过下述技术方案得以解决:一种防断裂铜氨面料,由经纱和纬纱织造而成,其特征在于:所述经纱和所述纬纱均具有75D至150D铜氨长丝;在所述面料的两侧均设置有数量相同的若干涤纶丝,所述涤纶丝的规格与所述铜氨长丝的规格相匹配。本产品除两边设置的数根涤纶丝外,其余为纯铜氨面料,在整体触感上与纯铜氨面料相同,具有柔软滑顺的触感,成本低廉,符合绿色环保要求,而且断头率低,整体强度高于同类型产品,而且由于两边涤纶丝的存在使其不易断裂。
作为优选,上述面料两侧的涤纶丝的数量为8-12根,分成相等的两组,其设置方式为:距边3-5mm内为铜氨,然后设置4-6根涤纶丝,在接下来的3-5mm内为铜氨,再设置4-6根涤纶丝。
本发明同时还提供了一种操作方便的生产上述纯铜氨提花面料的方法,按照该方法,生产过程中铜氨纤维不易断裂,保证了织造完成的纯铜氨面料的整体强度及质量,而且在织造成型后面料不易断裂。为解决上述技术问题,本发明通过下述技术方案得以解决:一种防断裂铜氨面料的生产方法,其特征在于包括以下步骤:1)选取75D至150D铜氨长丝为原料;2)整经,采用分批整经机进行整经,整经时的退绕张力大于卷绕张力,整经完成后整经轴上各处卷绕的铜氨丝的厚度之差不大于5mm,并且在整经两边分别放置1-2根对应的涤纶丝;3)浆丝,浆丝过程中浆丝机的引纱辊的速度要小于上浆辊的速度,所述引纱辊的速度为90-110m/min;4)并轴,幷轴时将两边8-12根涤纶丝分成相等两组放置在最上边,其设置方式为:距边3-5mm内为铜氨,然后设置4-6根涤纶丝,在接下来的3-5mm内为铜氨,再设置4-6根涤纶丝;5)穿综丝、插筘;6)上机织造。
本发明主要通过调节整经环节中的退绕张力和卷绕张力以及浆丝环节中引纱辊和上浆辊的速度达到减少铜氨长丝断裂的目的。事实上,铜氨长丝的断裂主要集中在浆丝工艺过程中,其原因就在于铜氨长丝吸湿后其湿强力低、湿延伸率大,特别是如果在浆丝时各个位置的丝线如果长度不一导致各个丝线所受张力不一致而造成铜氨长丝断裂。如果在整经时卷绕张力大于退绕张力,一旦出现偏差,会导致整经轴上丝线在不同位置上的厚度不同,由于卷绕张力较大,铜氨长丝崩的较紧,那么在厚度大的位置,铜氨长丝缠绕的数量会越来越多,厚度越来越大,则在浆丝时,该处位置的铜氨长丝释放的长度较其他地方长,造成浆丝时各个位置的铜氨长丝的长度不一导致各个铜氨长丝所受张力不一致而造成铜氨长丝断裂。在本发明中,整经时退绕张力大于卷绕张力可以使铜氨长丝缠绕到整经轴上时具有自我调节的能力,不会出现整经轴上各个位置铜氨长丝缠绕的厚度不一致的现象,保证整经完成后整经轴上各处卷绕的铜氨丝的厚度之差不大于5mm,从而避免在浆丝时由于长度不一导致铜氨长丝断裂的现象。另一方面,在浆丝时由于铜氨长丝吸湿后延长,如果引纱辊的速度要大于或等于上浆辊的速度,会导致停留在浆料中的铜氨长丝越来越多,也容易造成铜氨长丝的断裂。因此,本发明将引纱辊的速度设置的小于上浆辊的速度,使经过浆料的铜氨长丝能及时离开浆料,避免铜氨长丝的断裂,在实际操作过程中,引纱辊的速度需要根据上浆辊的速度以及铜氨长丝的吸湿延伸率来进行确定。再次,本发明通过在面料两边设置涤纶丝来增强面料的抗撕裂能力,使其织造成型后亦不易断裂。
作为优选,上述步骤3中浆丝所用的浆料的配方为:按重量百分比计,主料为98%-99%的PVA205MB,辅料为2%-1%的抗静电剂。
作为优选,上述步骤6中织造所用的织布机为电子多臂无梭织机,该无梭织机的门幅为55-57英寸。
作为优选,上述无梭织机的转速为500-650转/分钟。
与现有技术相比,本发明的有益效果是:面料具有柔软滑顺的触感,成本低廉,符合绿色环保要求,而且断头率低,整体强度高于同类型产品,而且面料整体不易断裂。该方法操作简单,有效解决了在生产过程中铜氨纤维易断裂的问题,降低了纯铜氨面料的生产难度。
具体实施方式
下面结合具体实施方式对本发明作进一步详细描述:实施例1 。
一种防断裂铜氨面料,由经纱和纬纱织造而成,其特征在于:所述经纱和所述纬纱均具有75D至150D铜氨长丝;在所述面料的两侧均设置有数量相同的若干涤纶丝,所述涤纶丝的规格与所述铜氨长丝的规格相匹配。通常来说,70D铜氨丝应配75DDTY涤纶网格丝,120D铜氨丝应配100DDTY涤纶网格丝,150D铜氨丝应配150DDTY涤纶网格丝。
在本实施例中,上述面料两侧的涤纶丝的数量为8根,分成相等的两组,其设置方式为:距边3-5mm内为铜氨,然后设置4根涤纶丝,在接下来的3-5mm内为铜氨,再设置4根涤纶丝。
除本实施例外,上述面料两侧的涤纶丝的数量也可为12根,分成相等的两组,其设置方式为:距边3-5mm内为铜氨,然后设置,6根涤纶丝,在接下来的3-5mm内为铜氨,再设置6根涤纶丝。
实施例2。
一种防断裂铜氨面料的生产方法,包括以下步骤:1)选取75D至150D铜氨长丝为原料;2)整经,采用分批整经机进行整经,整经时的退绕张力大于卷绕张力,整经完成后整经轴上各处卷绕的铜氨丝的厚度之差不大于5mm,并且在整经两边分别放置1-2根对应的涤纶丝;3)浆丝,浆丝过程中浆丝机的引纱辊的速度要小于上浆辊的速度,所述引纱辊的速度为90-110m/min;4)并轴,幷轴时将两边8根涤纶丝分成相等两组放置在最上边,其设置方式为:距边3-5mm内为铜氨,然后设置4根涤纶丝,在接下来的3-5mm内为铜氨,再设置4根涤纶丝;5)穿综丝、插筘;6)上机织造,织造所用的织布机为电子多臂无梭织机,该无梭织机的门幅为55-57英寸,织机的转速为500-650转/分钟。
在本实施例中,上述步骤3中浆丝所用的浆料的配方为:按重量百分比计,主料为98%-99%的PVA205MB,辅料为2%-1%的抗静电剂。
Claims (6)
1.一种防断裂铜氨面料,由经纱和纬纱织造而成,其特征在于:所述经纱和所述纬纱均具有75D至150D铜氨长丝;在所述面料的两侧均设置有数量相同的若干涤纶丝,所述涤纶丝的规格与所述铜氨长丝的规格相匹配。
2.根据权利要求1所述的一种防断裂铜氨面料,其特征在于:所述面料两侧的涤纶丝的数量为8-12根,分成相等的两组,其设置方式为:距边3-5mm内为铜氨,然后设置4-6根涤纶丝,在接下来的3-5mm内为铜氨,再设置4-6根涤纶丝。
3.一种如权利要求1或2所述的防断裂铜氨面料的生产方法,其特征在于包括以下步骤:1)选取75D至150D铜氨长丝为原料;2)整经,采用分批整经机进行整经,整经时的退绕张力大于卷绕张力,整经完成后整经轴上各处卷绕的铜氨丝的厚度之差不大于5mm,并且在整经两边分别放置1-2根对应的涤纶丝;3)浆丝,浆丝过程中浆丝机的引纱辊的速度要小于上浆辊的速度,所述引纱辊的速度为90-110m/min;4)并轴,幷轴时将两边8-12根涤纶丝分成相等两组放置在最上边,其设置方式为:距边3-5mm内为铜氨,然后设置4-6根涤纶丝,在接下来的3-5mm内为铜氨,再设置4-6根涤纶丝;5)穿综丝、插筘;6)上机织造。
4.根据权利要求2所述的一种纯铜氨提花面料的生产方法,其特征在于:所述步骤3中浆丝所用的浆料的配方为:按重量百分比计,主料为98%-99%的PVA205MB,辅料为2%-1%的抗静电剂。
5.根据权利要求2或3或4所述的一种纯铜氨提花面料的生产方法,其特征在于:所述步骤6中织造所用的织布机为电子多臂无梭织机,该无梭织机的门幅为55-57英寸。
6.根据权利要求5所述的一种纯铜氨提花面料的生产方法,其特征在于:所述无梭织机的转速为500-650转/分钟。