CN102649156A - 硬质合金混合料石蜡成型剂的一种加入方法 - Google Patents

硬质合金混合料石蜡成型剂的一种加入方法 Download PDF

Info

Publication number
CN102649156A
CN102649156A CN2012100607852A CN201210060785A CN102649156A CN 102649156 A CN102649156 A CN 102649156A CN 2012100607852 A CN2012100607852 A CN 2012100607852A CN 201210060785 A CN201210060785 A CN 201210060785A CN 102649156 A CN102649156 A CN 102649156A
Authority
CN
China
Prior art keywords
hard alloy
paraffin wax
carbide alloy
alloy mixture
slurry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100607852A
Other languages
English (en)
Inventor
江绍平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHENGDU BANGPU ALLOY MATERIALS Co Ltd
Original Assignee
CHENGDU BANGPU ALLOY MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHENGDU BANGPU ALLOY MATERIALS Co Ltd filed Critical CHENGDU BANGPU ALLOY MATERIALS Co Ltd
Priority to CN2012100607852A priority Critical patent/CN102649156A/zh
Publication of CN102649156A publication Critical patent/CN102649156A/zh
Pending legal-status Critical Current

Abstract

硬质合金混合料石蜡成型剂的一种加入方法，它涉及粉末冶金技术、硬质合金材料生产技术领域。它的加入方法为：经400目以上的筛网过滤的硬质合金料浆(不含石蜡)，在沉淀后、干燥制粒前，将酒精料浆加热至45-100℃后，再加入过滤的含5-30％酒精的石蜡粉，并用螺旋双叶片以30-100转/分钟的速度进行搅拌加热10-60分钟，待料浆与石蜡混合均匀后，再干燥制粒，从而制成硬质合金混合料；本发明提高了球磨生产效率；同时提高了硬质合金混合料料浆的过滤网目，解决了球磨机桶内不易清洗、易残留粉末形成混料的难题。

Description

硬质合金混合料石蜡成型剂的一种加入方法
技术领域：
本发明涉及粉末冶金技术、硬质合金材料生产技术领域，具体涉及硬质合金混合料石蜡成型剂的一种加入方法。
背景技术：
现有的硬质合金混合料石蜡成型剂的加入方法是：将酒精石蜡粉直接加入装有硬质合金各种粉末原料的酒精球磨机中，一起滚动球磨混合均匀后，再将用180-320目筛网过滤的硬质合金料浆沉淀、干燥、制粒，从而制成硬质合金混合料。该方法的缺点有：1、球磨生产效率低；2、料浆过滤困难，Co片、WC等粗大颗粒未过滤出去而形成组织组织结构不均匀等缺陷，从而致使硬质合金的韧性等力学性能下降；3、球磨机桶内不易清洗，易残留粉末形成混料，从而导致硬质合金的组织结构不均匀。
发明内容：
本发明的目的是提供硬质合金混合料石蜡成型剂的一种加入方法，它提高了球磨生产效率；同时提高了硬质合金混合料料浆的过滤网目，由180-300目提高到400目以上，使Co片、WC等粗大颗粒过滤出去，形成均匀的硬质合金组织结构，从而提高硬质合金韧性等力学性能；解决了球磨机桶内不易清洗、易残留粉末形成混料的难题。
为了解决背景技术所存在的问题，本发明是采用以下技术方案：经400目以上的筛网过滤的硬质合金料浆(不含石蜡)，在沉淀后、干燥制粒前，将酒精料浆加热至45-100℃后，再加入过滤的含5-30％酒精的石蜡粉，并用螺旋双叶片以30-100转/分钟的速度进行搅拌加热10-60分钟，待料浆与石蜡混合均匀后，再干燥制粒，从而制成硬质合金混合料。
本发明具有以下有益效果：
1、提高了球磨生产效率。
2、提高了硬质合金混合料料浆的过滤网目，由180-300目提高到400目以上，使Co片、WC等粗大颗粒过滤出去，形成均匀的硬质合金组织结构，从而提高硬质合金韧性等力学性能。
3、解决了球磨机桶内不易清洗、易残留粉末形成混料的难题。
具体实施方式：
本具体实施方式采用以下技术方案：经400目以上的筛网过滤的硬质合金料浆(不含石蜡)，在沉淀后、干燥制粒前，将酒精料浆加热至45-100℃后，再加入过滤的含5-30％酒精的石蜡粉，并用螺旋双叶片以30-100转/分钟的速度进行搅拌加热10-60分钟，待料浆与石蜡混合均匀后，再干燥制粒，从而制成硬质合金混合料。
本发明通过改变硬质合金混合料石蜡成型剂的加入时机，由现有的将酒精石蜡粉直接加入装有硬质合金各种粉末原料的酒精球磨机中一起滚动球磨混合改成在硬质合金各种粉末原料的酒精球磨机中一起滚动球磨混合形成的硬质合金料浆过滤后、干燥制粒前再加入，从而制成硬质合金混合料。
本具体实施方式具有以下有益效果：
1、提高了球磨生产效率。
2、提高了硬质合金混合料料浆的过滤网目，由180-300目提高到400目以上，使Co片、WC等粗大颗粒过滤出去，形成均匀的硬质合金组织结构，从而提高硬质合金韧性等力学性能。
3、解决了球磨机桶内不易清洗、易残留粉末形成混料的难题。

Claims (1)

1.硬质合金混合料石蜡成型剂的一种加入方法，其特征在于加入方法为：经400目以上的筛网过滤的硬质合金料浆(不含石蜡)，在沉淀后、干燥制粒前，将酒精料浆加热至45-100℃后，再加入过滤的含5-30％酒精的石蜡粉，并用螺旋双叶片以30-100转/分钟的速度进行搅拌加热10-60分钟，待料浆与石蜡混合均匀后，再干燥制粒，从而制成硬质合金混合料。
CN2012100607852A 2012-03-09 2012-03-09 硬质合金混合料石蜡成型剂的一种加入方法 Pending CN102649156A (zh)