CN102329135A - 一种一次烧成抛晶砖的生产方法 - Google Patents

一种一次烧成抛晶砖的生产方法 Download PDF

Info

Publication number
CN102329135A
CN102329135A CN201110292509A CN201110292509A CN102329135A CN 102329135 A CN102329135 A CN 102329135A CN 201110292509 A CN201110292509 A CN 201110292509A CN 201110292509 A CN201110292509 A CN 201110292509A CN 102329135 A CN102329135 A CN 102329135A
Authority
CN
China
Prior art keywords
firing
layer
transparent
polished
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201110292509A
Other languages
English (en)
Other versions
CN102329135B (zh
Inventor
曾权
邝志均
管霞菲
曾立华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Dongpeng Ceramic Co Ltd
Guangdong Dongpeng Holdings Co Ltd
Qingyuan Nafuna Ceramics Co Ltd
Original Assignee
Guangdong Dongpeng Ceramic Co Ltd
Qingyuan Nafuna Ceramics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Dongpeng Ceramic Co Ltd, Qingyuan Nafuna Ceramics Co Ltd filed Critical Guangdong Dongpeng Ceramic Co Ltd
Priority to CN 201110292509 priority Critical patent/CN102329135B/zh
Publication of CN102329135A publication Critical patent/CN102329135A/zh
Application granted granted Critical
Publication of CN102329135B publication Critical patent/CN102329135B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种一次烧成抛晶砖的生产方法，其特征在于：它是采用现行的抛光砖布料技术将各种不同颜色、质感的粉料按照设计要求布料并压制成型干燥后进行表面抛坯处理，再喷淋或印刷一层透明釉，然后再利用进行印花装饰，完成后再铺一层透明微晶熔块粉并喷一层甲基水或固定剂进行固定最后入窑烧成抛光。本发明布料纹理多层复合，三维立体感强，在对产品进行加工时仍能呈现产品丰富自然犹如天然石材切割后的三维立体花纹，而且硬度高、耐磨性好，装饰应用范围广，能耗水平低，生产周期短，具有良好的推广价值。

Description

一种一次烧成抛晶砖的生产方法
技术领域
本发明涉及陶瓷技术领域，更具体的说是涉及一种抛晶砖的生产方法。
背景技术
抛晶砖因其表面光泽晶莹剔透、似水晶若玛瑙，越来越受到人们的喜爱，但其与抛光砖相比莫氏硬度低、耐磨性差，使得使用范围受到限制。现有的抛晶砖制备工艺一般是在经高温烧制好的印花砖面上堆积低温熔块和高温熔块的混合物，然后经低温二次烧成、抛光得到产品。通过该工艺制得的抛晶砖三维立体感不强，特别是在近距离观察和产品进行倒角等加工处理后坯体表现更为明显。另外，采用两次烧成工艺存在能耗高、产量低等劣势。
发明内容
本发明的目的就是为了解决现有技术之不足而提供的一种不仅布料纹理清晰可见、层次分明、三维立体感强，在对产品进行加工时仍能呈现产品丰富自然犹如天然石材切割后的三维立体花纹，而且硬度高耐磨、生产周期缩短、能耗降低的一次烧成抛晶砖的生产方法。
本发明是采用如下技术解决方案来实现上述目的： 一种一次烧成抛晶砖的生产方法，其特征在于，它包括如下步骤：
a、配料、成型，将不同颜色、不同质感的粉料按设计要求配料成花纹料并布料后压制成型； 
b、干燥、抛坯，将砖坯干燥后进行表面抛坯处理，得到表面具有清晰纹理的砖坯；
c、施釉、印花装饰，在抛坯处理后的砖坯表面喷淋或印刷一层透明釉后再进行印花装饰；
d、施透明熔块粉，在印花装饰好的砖坯上再铺撒一层透明微晶熔块粉并喷一层甲基水或固定剂进行固定； 
e、烧成、抛光，将固定后的砖坯入窑烧成并抛光，烧成时间为1.5-3小时，烧成温度为1200－1280℃。
在所述工艺步骤c过程中，喷淋或印刷的透明釉的比重为1.2-1.3/cm3，施釉量200-500g/m2。
在所述工艺步骤d过程中，所述透明微晶熔块粉的铺撒量为2-5kg/m2。
本发明采用上述技术解决方案所能达到的有益效果是：
1、本发明是在干燥抛坯处理后的砖坯表面喷淋或印刷一层透明釉后，再在透明釉层表面进行纹理装饰后再增加一层透明微晶熔块层，使产品形成布料纹理层、装饰纹理层并通过两层透明层呈现出多层复合的三维立体装饰效果，并且在近距离观察或对产品进行加工时仍能呈现产品丰富自然犹如天然石材切割后的三维立体花纹； 
2、本发明采用一次烧成工艺，得到的产品硬度>6，可用于地面装饰扩展了抛晶砖的应用范围；并且节约时间、节省能耗，根据试验统计得到一次烧成的能耗仅占二次烧成能耗的20-50%，有效解决两次烧成工艺存在生产周期长、能耗高、产量低等劣势。
具体实施方式
本实施例中， 一种一次烧成抛晶砖的生产方法，它包括如下步骤：
1、首先采用现行的抛光砖布料技术将各种不同颜色、质感的粉料按照设计要求合理安排到砖坯表面，通过压机压制成型并干燥后进行表面抛坯处理，其中，在所述抛坯处理工序前，需要对其进行干燥处理，使坯体的含水率低于1.5%，然后再利用抛光设备对其进行抛光，抛光深度为0.1-5mm，得到表面具有清晰纹理的砖坯后再喷淋一层透明釉（比重为1.25/cm3，施釉量360g/m2），再利用滚筒印花进行印刷补充装饰纹理，完成后再进行丝网印花装饰增加带色熔块和乳浊熔块三维立体效果，所有装饰完成后再铺一层透明微晶熔块粉（铺撒量为3.5kg/m2），然后再喷一层甲基水进行固定；
2、入窑一次烧成，烧成时间为2小时，烧成温度为1260℃； 
3、将烧好后的砖坯采用弹性模块进行抛光处理，抛光后可得到莫氏硬度6.5，多层复合布料纹理清晰可见、三维立体感强烈、生产过程能耗降低的抛晶砖产品。
其中，抛晶砖的配方按重量百分比算包括：高岭土5-10%，黑泥10-20%，钠长石10-20%，钾长石30-50%，中温砂20-50%，滑石1-3%。本实施例中，抛晶砖的原料配方按重量百分比算优选高岭土8%，黑泥15%，钠长石15%，钾长石32%，中温砂28%，滑石2%。
以上所述的仅是本发明的优选实施方式，应当指出，对于本领域的普通技术人员来说，在不脱离本发明创造构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。

Claims (3)

1.一种一次烧成抛晶砖的生产方法，其特征在于，它包括如下步骤：
a、配料、成型，将不同颜色、不同质感的粉料按设计要求配料成花纹料并布料后压制成型；
b、干燥、抛坯，将砖坯干燥后进行表面抛坯处理，得到表面具有清晰纹理的砖坯；
c、施釉、印花装饰，在抛坯处理后的砖坯表面喷淋或印刷一层透明釉后再进行印花装饰；
d、施透明熔块粉，在印花装饰好的砖坯上再铺撒一层透明微晶熔块粉并喷一层甲基水或固定剂进行固定； 
e、烧成、抛光，将固定后的砖坯入窑烧成并抛光，烧成时间为1.5-3小时，烧成温度为1200－1280℃。
2.根据权利要求1所述的一次烧成抛晶砖的生产方法，其特征在于，在所述工艺步骤c过程中，喷淋或印刷的薄层透明釉的比重为1.2-1.3/cm3，施釉量200-500g/m2。
3.根据权利要求1所述的一次烧成抛晶砖的生产方法，其特征在于，在所述工艺步骤d过程中，所述透明微晶熔块粉的铺撒量为2-5kg/m2。
CN 201110292509 2011-09-30 2011-09-30 一种一次烧成抛晶砖的生产方法 Active CN102329135B (zh)