CN102234352A - D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法 - Google Patents

D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法 Download PDF

Info

Publication number
CN102234352A
CN102234352A CN2011100997187A CN201110099718A CN102234352A CN 102234352 A CN102234352 A CN 102234352A CN 2011100997187 A CN2011100997187 A CN 2011100997187A CN 201110099718 A CN201110099718 A CN 201110099718A CN 102234352 A CN102234352 A CN 102234352A
Authority
CN
China
Prior art keywords
warming
incubated
hours
exchange resin
cation exchange
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011100997187A
Other languages
English (en)
Other versions
CN102234352B (zh
Inventor
王方银
王峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI MEIJIA NEW MATERIAL Co Ltd
Original Assignee
ANHUI MEIJIA NEW MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI MEIJIA NEW MATERIAL Co Ltd filed Critical ANHUI MEIJIA NEW MATERIAL Co Ltd
Priority to CN 201110099718 priority Critical patent/CN102234352B/zh
Publication of CN102234352A publication Critical patent/CN102234352A/zh
Application granted granted Critical
Publication of CN102234352B publication Critical patent/CN102234352B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法，主要是以丙烯酸甲酯、二乙烯苯、TAIC、异丁醇、偶氮、丙二胺、乙二醇等为主要原料，经过聚合和胺化的工艺步骤制备出D213大孔强碱性丙烯酸系阳离子交换树脂。

Description

D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法
技术领域
本发明涉及离子交换树脂的制备工艺，具体地说，是一种D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法。
背景技术
交换树脂主要用于纯水、高纯水制备、废水处理、生化制品提取、稀有金属提取、湿法冶金中钨、钼、钒等的提取，具有机械强度好、耐热性高等特点。
发明内容
本发明目的在于提供一种D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法。
本发明目的是通过如下技术手段实现的：
一种D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法，包括如下步骤：
一、聚合：
1、投料量：丙烯酸甲酯370.2kg，二乙烯苯21.8kg，TAIC8kg，异丁醇120kg，偶氮4kg。
2、操作步骤：
(1)按规定配好水相，搅拌均匀；
(2)停止搅拌，将混合好的单体加入开机搅拌，视粒度情况调好转速；
(3)缓慢升温至69℃，观察球体粒度及定型情况；
(4)定型时放热比较强烈，注意降温，放热后保持温度在70℃，保温2小时；
(5)用半小时升温至82℃，保温3小时；
(6)用1小时升温至96℃，保温5小时；
(7)用热水洗球数遍至水清澈为止；
(8)抽干水，烘干，分筛备用。
二、胺化：
1、投料量：白球400kg，丙二胺800kg，乙二醇900kg。
2、操作步骤：
(1)在干净的反应釜中加入白球，再加入胺、醇开动搅拌；
(2)升温至140℃，保温5小时，升温至160℃，保温6小时，升温至170℃，保温4小时，升温至175℃，保温4小时；
(3)取样测中控，交换大于4.2mmol/g合格；
(4)抽母液，水洗，出料。
具体实施方式
下面结合实施例对本发明进一步描述，但并非用以限定本发明。
实施例1：
按照如下方法制备D213大孔强碱性丙烯酸系阳离子交换树脂：
一、聚合：
1、投料量：丙烯酸甲酯370.2kg，二乙烯苯21.8kg，TAIC8kg，异丁醇120kg，偶氮4kg。
2、操作步骤：
(1)按规定配好水相，搅拌均匀；
(2)停止搅拌，将混合好的单体加入开机搅拌，视粒度情况调好转速；
(3)缓慢升温至69℃，观察球体粒度及定型情况；
(4)定型时放热比较强烈，注意降温，放热后保持温度在70℃，保温2小时；
(5)用半小时升温至82℃，保温3小时；
(6)用1小时升温至96℃，保温5小时；
(7)用热水洗球数遍至水清澈为止；
(8)抽干水，烘干，分筛备用。
二、胺化：
1、投料量：白球400kg，丙二胺800kg，乙二醇900kg。
2、操作步骤：
(1)在干净的反应釜中加入白球，再加入胺、醇开动搅拌；
(2)升温至140℃，保温5小时，升温至160℃，保温6小时，升温至170℃，保温4小时，升温至175℃，保温4小时；
(3)取样测中控，交换大于4.2mmol/g合格；
(4)抽母液，水洗，出料。

Claims (1)

1.一种D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法，其特征在于，包括如下步骤：
(一)聚合：
(1)投料量：丙烯酸甲酯370.2kg，二乙烯苯21.8kg，TAIC8kg，异丁醇120kg，偶氮4kg。
(2)操作步骤：
①按规定配好水相，搅拌均匀；
②停止搅拌，将混合好的单体加入开机搅拌，视粒度情况调好转速；
③缓慢升温至69℃，观察球体粒度及定型情况；
④定型时放热比较强烈，注意降温，放热后保持温度在70℃，保温2小时；
⑤用半小时升温至82℃，保温3小时；
⑥用1小时升温至96℃，保温5小时；
⑦用热水洗球数遍至水清澈为止；
⑧抽干水，烘干，分筛备用。
(二)胺化：
(1)投料量：白球400kg，丙二胺800kg，乙二醇900kg。
(2)操作步骤：
①在干净的反应釜中加入白球，再加入胺、醇开动搅拌；
②升温至140℃，保温5小时，升温至160℃，保温6小时，升温至170℃，保温4小时，升温至175℃，保温4小时；
③取样测中控，交换大于4.2mmol/g合格；
④抽母液，水洗，出料。
CN 201110099718 2011-04-20 2011-04-20 D213大孔强碱性丙烯酸系阳离子交换树脂的制备方法 Expired - Fee Related CN102234352B (zh)