CN102234186A - Natural color sand decorative mortar - Google Patents
Natural color sand decorative mortar Download PDFInfo
- Publication number
- CN102234186A CN102234186A CN 201010160419 CN201010160419A CN102234186A CN 102234186 A CN102234186 A CN 102234186A CN 201010160419 CN201010160419 CN 201010160419 CN 201010160419 A CN201010160419 A CN 201010160419A CN 102234186 A CN102234186 A CN 102234186A
- Authority
- CN
- China
- Prior art keywords
- mortar
- natural color
- color sand
- natural colour
- natural
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a wall decorative material, and concretely relates to a natural color sand decorative mortar for decorating inner walls and outer walls. The natural color sand decorative mortar comprises 15 to 30 wt% of a synthetic resin emulsion, 10 to 60 wt% of natural color sand grains, 1 to 4 wt% of a film forming assistant, 0.1 to 1 wt% of a thickening agent, 11 to 73 wt% of ceramic grains, 0.1 to 0.2 wt% of an antifoaming agent, 0.1 to 0.2 wt% of an anti-mildew bactericide, and 0.5 to 18 wt% of a pH additive. The natural color sand decorative mortar has the advantages that: various artistic effects can be generated through combination of various natural color sand grains because of strong decoration; the color of the mortar lasts longer than methods of adding toner or other pigments and never fades because of good weatherability and UV- resistance; and pollution resistance, good waterproof effect, and convenient construction are achieved because the mortar can be used with priming paints and finishing varnishes, and has good bonding force with substrates of various materials.
Description
Technical field
The present invention relates to a kind of decorative material for wall surface, relate in particular to a kind of natural colour sand texture decoration mortar that the buildings inner, external wall is played decoration function.
Background technology
Decoration mortar is a kind of novel wall surface finishing material of China from external introduction, and it is made up of inorganic coagulation material, filler and aggregate, is used for the decoration on construction wall surface.Compare with finishing materials such as traditional ceramic tile, coating, decoration mortar is with rich colors, moulding and the excellent weather resistance of coating, speed of application is fast simultaneously, and decoration mortar thickness only is 3-Smm, in light weight, can reduce the load of outer heat preservation system greatly, during as the Highrise buildings facing, can peeling phenomenon not occur, thereby guarantee the external thermal insulation system safety and reliability because of bearing the blast problem.Decoration mortar is decorated at the inner, external wall that developed country extensively replaces coating and ceramic tile to be applied to buildings.
Existing well ornamental in order to guarantee decoration mortar, have the excellent anti-accumulation of salt in the surface soil, contamination resistance and weathering resistance again, common way is to adopt three layers of external decorative mortar system, comprises prime coat, decoration mortar layer and finishing varnish layer.The external decorative mortar system construction technology is: base material is polished flat, clean out, the priming paint of an emulsion form of brushing on the exsiccant body of wall; Treat priming paint after dry 24 hours, adopt the mode of mechanically spraying or manual batch scraping that decoration mortar is coated on the prime coat; Wait to decorate mortar after dry 24 hours, brushing 1-2 is all over the finishing varnish of emulsion form on the decoration mortar layer.Three layers of external decorative mortar system, by inside and outside both sides prime coat and finishing varnish layer are set at the decoration mortar layer, decoration mortar and base material and outside atmosphere are completely cut off to come, the prime coat waterproof, eliminate accumulation of salt in the surface soil phenomenon, isolated dust of finishing varnish layer and pollutent increase glossiness, make whole decoration of exterior wall system that the good anti-accumulation of salt in the surface soil, contamination resistance and weathering resistance be arranged.
But prior art used decoration mortar in the decoration mortar layer all is painted at present, promptly adds different pigment and obtain abundant colors in raw material, and this kind painted decoration mortar UV resistant performance and color stability are excellent inadequately.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of rich texture, natural colour, will never fade natural colour sand texture decoration mortar.
In order to solve the problems of the technologies described above, technical scheme of the present invention is: a kind of natural colour sand texture decoration mortar comprises the component of following weight percent meter:
Synthetic resin emulsion 15%～30%
Natural colour sand grains 10%～60%
Film coalescence aid 1%～4%
Thickening material 0.1%～1%
Ceramic particle 11%～73%
Defoamer 0.1%～0.2%
Antimildew disinfectant 0.1%～0.2%
PH value additive 0.5%～18%
Wherein, described synthetic resin emulsion is that the blend of silicone resin emulsion, phenylpropyl alcohol, pure-acrylic emulsion or multiple emulsion or multipolymer etc. are usually used in coating class emulsion, the adding of emulsion can improve the cohesive force of mortar, improves the snappiness of mortar and the tunic performance of product; Sand grains is that nature exists variously has natural colour stone and pulverizes the sand particle that forms, and sand grains makes the mortar rich texture, and stereoscopic sensation is strong, by various combinations with sand grains of natural colour, can produce multiple artistic effect; The film coalescence aid film coalescence aid be a kind of can the temporary softening agent of evaporable, can promote the plastic flow and the recoverable deformation of latex particle, improve its cohesiveness, can be in film forming in the construction temperature scope widely, can select the alcohols of selling on the market (as phenylcarbinol) for use, alkoxide (as 12 carbon alcohol esters), pure ethers (butyl glycol ether, propylene glycol phenylate etc.), pure ether-ether class (as hexylene glycol monobutyl ether acetate etc.) etc.; Ether of cellulose is a methyl cellulose ether, and the adding of thickening material can slurry consistency, is convenient to the last wall construction of mortar; Ceramic particle is pulverized or is ground for ceramics factory's waste product and forms, and the adding of ceramic particle can increase color light brightness; Defoamer is in order to eliminate the bubble in the mortar, to increase compactness; The antimildew disinfectant effect is mildew-resistant, sterilization, and defoamer and antimildew disinfectant all have commercially available; The pH value additive is that the pH value that changes mortar makes it adapt to various environments for use.
Natural colour sand texture decoration mortar of the present invention, adopt the advantage of above technical scheme to be:
1. ornamental strong: sand shape texture is arranged, and stereoscopic sensation is strong, and color is natural, by various combinations with sand grains of natural colour, can produce multiple artistic effect.
2. weathering resistance, good ultraviolet resistance: because color comes from sand grains itself, the look soundness is more lasting, will never fade than the method for interpolation toner or other pigments.
3. be used with priming paint, finishing varnish, good bonding force all arranged with the ground of various materials, anti-pollution, good water-proof effect, it is more convenient to construct.
Embodiment
Below in conjunction with drawings and Examples technical solution of the present invention is further specified:
Each Example formulations is as follows: (weight percent)
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | |
| Synthetic resin emulsion | 15％ | 25％ | 15％ | 20％ |
| The natural colour sand grains | 60％ | 10％ | 10％ | 50％ |
| Film coalescence aid | 1％ | 4％ | 1％ | 3％ |
| Thickening material | 0.1％ | 0.5％ | 0.1％ | 0.3％ |
| Ceramic particle | 11％ | 45％ | 73％ | 16％ |
| Defoamer | 0.1％ | 0.2％ | 0.1％ | 0.1％ |
| Antimildew disinfectant | 0.1％ | 0.2％ | 0.1％ | 0.1％ |
| The pH value additive | 12.7％ | 15.1％ | 0.7％ | 10.5％ |
| Embodiment 5 | Embodiment 6 | Embodiment 7 | Embodiment 8 | |
| Synthetic resin emulsion | 18％ | 28％ | 22％ | 20％ |
| The natural colour sand grains | 50％ | 16％ | 45％ | 55％ |
| Film coalescence aid | 2％ | 2.5％ | 2.8％ | 3.5％ |
| Thickening material | 0.8％ | 1％ | 0.6％ | 0.8％ |
| Ceramic particle | 25％ | 35％ | 15％ | 20％ |
| Defoamer | 0.15％ | 0.2％ | 0.1％ | 0.1％ |
| Antimildew disinfectant | 0.15％ | 0.2％ | 0.1％ | 0.1％ |
| The pH value additive | 3.9％ | 17.1％ | 14.4％ | 0.5％ |
Detected result:
Decoration mortar with embodiment 4 obtains detects according to JC/T 24-2000 SAND SLURRY SYNTHETIC EMULSION ARCHITECTURAL COATINGS standard, and it is as follows to record the result:
The using method of natural colour sand texture decoration mortar of the present invention: be ready to decoration mortar by Example formulations, add water and stir, be used with priming paint, finishing varnish.Base material polishes flat, and cleans out the priming paint of an emulsion form of brushing on the exsiccant body of wall; Treat that priming paint is after dry 24 hours, adopt the mode of mechanically spraying or manual batch scraping that decoration mortar is coated on the prime coat, when adopting spraying, can regulate gun slot and the air pressure sky is little, obtain various different stereo effects moulding such as sand shape, point-like, criticize by hand when scraping, decoration mortar is criticized scraping on the prime coat earlier, available spatula or rubber mold suppress various textures behind about 5-10min, reach decorative effect preferably; Wait to decorate mortar after dry 24 hours, brushing 1-2 is all over the finishing varnish of emulsion form on the decoration mortar layer.
Above-described only is preferred implementation of the present invention; should be understood that; for a person skilled in the art; under the prerequisite that does not break away from principle of the present invention; can also make some improvement; these also should be considered as protection scope of the present invention, and these can not influence effect of the invention process and practical applicability.
Claims (2)
1. natural colour sand texture decoration mortar is characterized in that: the component that comprises following weight percent meter:
Synthetic resin emulsion 15%～30%
Natural colour sand grains 10%～60%
Film coalescence aid 1%～4%
Thickening material 0.1%～1%
Ceramic particle 11%～73%
Defoamer 0.1%～0.2%
Antimildew disinfectant 0.1%～0.2%
PH value additive 0.5%～18%
Described synthetic resin emulsion is the blend or the multipolymer of silicone resin emulsion, phenylpropyl alcohol, pure-acrylic emulsion or multiple emulsion.
2. a kind of natural colour sand texture decoration mortar according to claim 1 is characterized in that: the natural colour sand grains is the sand grains that natural band colored stone head is pulverized back classification gained.