CN102491684A - Imitated ceramic decorative mortar - Google Patents
Imitated ceramic decorative mortar Download PDFInfo
- Publication number
- CN102491684A CN102491684A CN201110401584XA CN201110401584A CN102491684A CN 102491684 A CN102491684 A CN 102491684A CN 201110401584X A CN201110401584X A CN 201110401584XA CN 201110401584 A CN201110401584 A CN 201110401584A CN 102491684 A CN102491684 A CN 102491684A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic particle
- particle
- color
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses imitated ceramic decorative mortar which comprises the following components in parts by weight: 1.5-2.5 parts of hydroxyethyl cellulose ether with viscosity of 100000mpa.s, 80-100 parts of water, 140-180 parts of pure acrylic emulsion, 12-15 parts of dodecyl ester, 16-19 parts of glycol, 7-8.5 parts of sodium polyacrylate, 1.2-1.8 parts of methyl alkylol amine and 650-750 parts of ceramic particle. The weather-resistant decorative mortar provided by the invention takes a colorful ceramic particle as a filling material, can be blended to form various styles and shapes according to the size and color of the ceramic particle, has the characteristics of bright color, good weather-resistant property and same service life as that of a building and never fades, and can be widely applied to outer wall decorative finish projects of top-grade communities and luxury villas.
Description
Technical field
The present invention relates to a kind of building mortar, be specifically related to a kind of outside the building wall and play decoration function, have the decoration mortar of good contamination resistance and weathering resistance simultaneously.
Background technology
At present, decoration mortar is a kind of external wall decorative material of novel environment friendly, and development has still been met some stubborn problems rapidly in the actual process of applying.Beijing, Shanghai, some high-grade building of ground such as Guangzhou after adopting the decoration mortar facing, triennium less than, metope color and luster just occurred and has differed, phenomenons such as local color dimness make that whole exterior wall is attractive in appearance to receive very big influence, have had a strong impact on cityscape.Major cause be wall face under ultraviolet long-term irradiation, the pigment that adds in the above-mentioned decoration mortar is decomposed or is aging, loses color and luster.Also some producer also replaces pigment through the natural colour of color sand; But the color category of color sand is limited after all, and the decoration mortar that uses color sand preparation can lose the glossiness of color sand nature behind wall in the construction; The metope color is very dim, does not reach the ideal color effect.
Summary of the invention
Technical problem to be solved by this invention is to overcome above-mentioned deficiency, and a kind of imitative porcelain decoration mortar that is suitable for exterior wall finish is provided, and this mortar contamination resistance is good, and weathering resistance is strong, lovely luster, and anti-uv-ray is will never change colour by force, long service life.
Technical scheme of the present invention: a kind of imitative porcelain decoration mortar, its each component and parts by weight are:
Viscosity is 1.5～2.5 parts of the hydroxyethyl ether celluloses of 100000mpas, 80～100 parts in water, 140～180 parts of pure-acrylic emulsions; 12～15 parts of alcohol esters, 16～19 parts of terepthaloyl moietie, 7～8.5 parts of ZX-Is; 1.2～1.8 parts of methyl hydramine, 650～750 parts of ceramic particles.Above-mentioned raw material stirring except that ceramic particle is become thick shape, add ceramic particle at last and stir and get final product.
Said ceramic particle is that to adopt kaolin, feldspar, quartz and clay be main raw material, adds inorganic toner, forms through high-temperature firing, and particle diameter is less than 2mm, and tap density is less than 1000 irregular shape particle.
The present invention compared with prior art has following beneficial effect: 1, the present invention is a stopping composition through adding the ceramic particle that forms through high-temperature firing; Its look is to fuse into wherein during with mineral dye high temperature; Can not occur fading; The phenomenon that fades guarantees that imitative porcelain decoration mortar to the decoration function that building exterior wall face rose, has improved the weathering resistance and the contamination resistance of mortar.2, it is environment friendly and pollution-free, can withstand freeze thawing and ultraviolet irradiation, and grain color can be fired into red, orange, yellow, green, blue, blue, purple, palm fibre, multiple color such as white.The inside and outside color entire body of particle is consistent, uses and can not fade, fade, and can also the ceramic particle of two kinds of different colours be mixed according to different ratios, obtains more decorated style.
Concrete embodiment
Embodiment 1
A kind of imitative porcelain decoration mortar, its each component and parts by weight are: viscosity is the hydroxyethyl ether cellulose 1.5kg of 100000mpas, water 80kg; Pure-acrylic emulsion 140kg, alcohol ester 12 12kg, terepthaloyl moietie 16kg; ZX-I 7kg, methyl hydramine 1.2kg, yellow ceramic particle 650kg; The ceramic particle particle diameter is 1mm, and tap density is 850 irregular shape particle.Above-mentioned raw material stirring except that ceramic particle is become thick shape, add ceramic particle at last and stir and get final product.
Embodiment 2
A kind of imitative porcelain decoration mortar, its each component and parts by weight are: viscosity is the hydroxyethyl ether cellulose 2.5kg of 100000mpas, water 100kg; Pure-acrylic emulsion 180kg, alcohol ester 12 15kg, terepthaloyl moietie 19kg; ZX-I 8.5kg, methyl hydramine 1.8kg, whiteware particle 700kg; Black ceramic particle 50kg, whiteware particle and black ceramic grain diameter are 2mm, tap density is 1000 irregular shape particle.Above-mentioned raw material stirring except that ceramic particle is become thick shape, add ceramic particle at last and stir and get final product.
Embodiment 3
A kind of imitative porcelain decoration mortar, its each component and parts by weight are: viscosity is the hydroxyethyl ether cellulose 2kg of 100000mpas, water 90kg; Pure-acrylic emulsion 150kg, alcohol ester 12 13kg, terepthaloyl moietie 18kg; ZX-I 8kg, methyl hydramine 1.5kg, red ceramic particle 700kg; The ceramic particle particle diameter is 1.5mm, and tap density is 920 irregular shape particle.Above-mentioned raw material stirring except that ceramic particle is become thick shape, add ceramic particle at last and stir and get final product.
Claims (2)
1. imitative porcelain decoration mortar, it is characterized in that: its each component and parts by weight are:
Viscosity is 1.5～2.5 parts of the hydroxyethyl ether celluloses of 100000mpas, 80～100 parts in water, 140～180 parts of pure-acrylic emulsions; 12～15 parts of alcohol esters, 16～19 parts of terepthaloyl moietie, 7～8.5 parts of ZX-Is; 1.2～1.8 parts of methyl hydramine, 650～750 parts of ceramic particles.
2. imitative porcelain decoration mortar according to claim 1 is characterized in that: said ceramic particle be particle diameter less than 2mm, tap density is less than 1000 irregular shape particle.