CN110330842A - A kind of water dyeing mortar and preparation method thereof - Google Patents
A kind of water dyeing mortar and preparation method thereof Download PDFInfo
- Publication number
- CN110330842A CN110330842A CN201910532784.5A CN201910532784A CN110330842A CN 110330842 A CN110330842 A CN 110330842A CN 201910532784 A CN201910532784 A CN 201910532784A CN 110330842 A CN110330842 A CN 110330842A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- stirring
- mortar
- dispersed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water dyeing mortars of technical field of paint preparation and preparation method thereof, component including following parts by weight: 60-80 parts of lotion, 0.2-0.5 parts of dispersion moisture agent, 5-10 parts of coalescing agent, 2-5 parts of other auxiliary agents, 1-1.5 parts of PH regulator, 1-1.5 parts of toner, 10-20 parts of deionized water, there is excellent color fastness, mechanical strength, the performances such as water-fast, resistance to boiling water, acid and alkali-resistance, solvent resistant, resistance to natural aging, artificial ageing resistance are prominent；Environmentally protective, Diamond Search does not generate three industrial wastes, is not limited, can arbitrarily be mixed colours by color, facilitates production, toning process simple, not high to equipment requirement, and low cost takes water as a solvent, raw material cost is low, and naturally dry does not consume energy；It can be used for building inside and outside wall coating, water-permeable brick, artificial stone, integrated board, artifacts production.
Description
Technical field
The present invention relates to technical field of paint preparation, specially a kind of water dyeing mortar and preparation method thereof.
Background technique
Currently, external wall largely uses lacquer as ornament materials, the main raw material(s) of exterior wall true stone paint first is that
Natural colour sand.And natural colour sand belongs to non-renewable mineral resources, under environment-protecting high-pressure situation in recent years, more and more mines are prohibited
It only exploits, the color sand of part colours is caused often to run out of goods.There are two types of existing dye sand technologies: high temperature sintering and oiliness contaminate sand: high temperature
Sand burning energy consumption is high, and product batches are unstable；Oiliness contaminates sand and largely uses oil-based solvent in process of production, generates a large amount of
Energy-saving requirement is not achieved in VOCs, both the above method.
Based on this, the present invention devises a kind of water dyeing mortar and preparation method thereof, to solve mentioned above ask
Topic.
Summary of the invention
The purpose of the present invention is to provide a kind of water dyeing mortars and preparation method thereof, to solve above-mentioned background technique
The problem of middle proposition.
To achieve the above object, the invention provides the following technical scheme: a kind of water dyeing mortar, including following weight
The component of number: 60-80 parts of lotion, 0.2-0.5 parts of dispersion moisture agent, 5-10 parts of coalescing agent, 2-5 parts of other auxiliary agents, PH tune
Agent 1-1.5 parts, 1-1.5 parts of toner, 10-20 parts of deionized water of section.
Preferably, other described auxiliary agents include the component of following parts by weight: 0.6-2.5 parts of thickener, defoaming agent 1-1.5
Part, 0.3-0.4 parts of antifreeze, 0.1-0.4 parts of fungicide.
Preferably, the lotion uses pure-acrylic emulsion.
Preferably, the dispersion moisture agent is selected from Sodium Polyacrylate, tertiary sodium phosphate, silicate, alkyl phenol polyoxyethylene ether
One or more of with sodium alklyarylsulfonate.
Preferably, the coalescing agent is selected from one or both of polyesterols, polyvinyl alcohol, sodium alginate and xanthan gum
More than.
A kind of preparation method of water dyeing mortar, comprising the following steps:
S1: first by the deionized water in formula, dispersion moisture agent, thickener, defoaming agent, antifreeze and fungicide are in 2000-
It is dispersed with stirring 5-30min under the conditions of 4000r/min and obtains mixed liquor, for use；
S2: coalescing agent is dispersed with stirring 5-20min under the conditions of 1000- 2500r/min, the step S1 is added thereto
In mixed liquor, continue to be dispersed with stirring 5-20min under the conditions of 1000-2500r/ min, continuously add PH regulator stirring 5-
10min is ground to no particle, obtains aqueous slurry；
S3: 2-10 part aqueous slurry in selecting step S2 in parts by weight puts into lotion and mill base into the slurry of selection,
It is dispersed with stirring 10-15min under the conditions of 500-600r/ min, obtains the water dyeing mortar of required color after mixing evenly.
Preferably, the device being dispersed with stirring in described step S1, S2, S3 uses high speed disperser.
Compared with prior art, the beneficial effects of the present invention are: (1) have excellent color fastness, mechanical strength, it is water-fast,
The performances such as resistance to boiling water, acid and alkali-resistance, solvent resistant, resistance to natural aging, artificial ageing resistance are prominent；(2) environmentally protective, Diamond Search does not generate
Three industrial wastes are not limited by color, can arbitrarily be mixed colours, facilitate production, toning process simple, not high to equipment requirement, low cost,
It takes water as a solvent, at low cost, naturally dry does not consume energy；(3) it can be used for building inside and outside wall coating, water-permeable brick, artificial stone, one
Body plate, artifacts production.
Specific embodiment
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on this
Embodiment in invention, all other reality obtained by those of ordinary skill in the art without making creative efforts
Example is applied, shall fall within the protection scope of the present invention.
Embodiment one
A kind of water dyeing mortar, the component including following parts by weight: 60 parts of lotion, 0.2 part of dispersion moisture agent, film forming helps
5 parts of agent, 0.6 part of thickener, 1 part of defoaming agent, 0.3 part of antifreeze, 0.1 part of fungicide, 1 part of PH regulator, 1 part of toner, go from
10 parts of sub- water.
A kind of preparation method of water dyeing mortar, comprising the following steps:
S1: first by the deionized water in formula, dispersion moisture agent, thickener, defoaming agent, antifreeze and fungicide are in 2000r/
It is dispersed with stirring 5min under the conditions of min and obtains mixed liquor, for use；
S2: being dispersed with stirring 5min for coalescing agent under the conditions of 1000r/min, and the mixing in the step S1 is added thereto
Liquid continues to be dispersed with stirring 5min under the conditions of 1000r/ min, continuously adds PH regulator stirring 5min, is ground to no particle,
Obtain aqueous slurry；
S3: 2 parts of aqueous slurries in selecting step S2 in parts by weight put into lotion and mill base into the slurry of selection,
It is dispersed with stirring 10min under the conditions of 500r/ min, obtains water dyeing mortar after mixing evenly.
Embodiment two
A kind of water dyeing mortar, the component including following parts by weight: 65 parts of lotion, 0.3 part of dispersion moisture agent, film forming helps
6 parts of agent, 0.6 part of thickener, 1 part of defoaming agent, 0.3 part of antifreeze, 0.1 part of fungicide, 1 part of PH regulator, 1 part of toner, go from
13 parts of sub- water.
A kind of preparation method of water dyeing mortar, comprising the following steps:
S1: first by the deionized water in formula, dispersion moisture agent, thickener, defoaming agent, antifreeze and fungicide are in 2500r/
It is dispersed with stirring 10min under the conditions of min and obtains mixed liquor, for use；
S2: being dispersed with stirring 10min for coalescing agent under the conditions of 1500r/min, and the mixing in the step S1 is added thereto
Liquid continues to be dispersed with stirring 10min under the conditions of 1500r/ min, continuously adds PH regulator stirring 5min, is ground to no particle,
Obtain aqueous slurry；
S3: 4 parts of aqueous slurries in selecting step S2 in parts by weight put into lotion and mill base into the slurry of selection,
It is dispersed with stirring 10min under the conditions of 500r/ min, obtains water dyeing mortar after mixing evenly.
Embodiment three
A kind of water dyeing mortar, the component including following parts by weight: 70 parts of lotion, 0.3 part of dispersion moisture agent, film forming helps
It 8 parts of agent, 1.5 parts of thickener, 1.2 parts of defoaming agent, 0.3 part of antifreeze, 0.1 part of fungicide, 1 part of PH regulator, 1 part of toner, goes
15 parts of ionized water.
A kind of preparation method of water dyeing mortar, comprising the following steps:
S1: first by the deionized water in formula, dispersion moisture agent, thickener, defoaming agent, antifreeze and fungicide are in 3000r/
It is dispersed with stirring 15min under the conditions of min and obtains mixed liquor, for use；
S2: being dispersed with stirring 15min for coalescing agent under the conditions of 1800r/min, and the mixing in the step S1 is added thereto
Liquid continues to be dispersed with stirring 15min under the conditions of 1800r/ min, continuously adds PH regulator stirring 7min, is ground to no particle,
Obtain aqueous slurry；
S3: 6 parts of aqueous slurries in selecting step S2 in parts by weight put into lotion and mill base into the slurry of selection,
It is dispersed with stirring 12min under the conditions of 550r/ min, obtains water dyeing mortar after mixing evenly.
Example IV
A kind of water dyeing mortar, the component including following parts by weight: 75 parts of lotion, 0.4 part of dispersion moisture agent, film forming helps
9 parts of agent, 2 parts of thickener, 1.3 parts of defoaming agent, 0.4 part of antifreeze, 0.4 part of fungicide, 1.5 parts of PH regulator, 1.5 parts of toner,
18 parts of deionized water.
S1: first the deionized water in formula, dispersion moisture agent, thickener, defoaming agent, antifreeze and fungicide are existed
It is dispersed with stirring 25min under the conditions of 3500r/min and obtains mixed liquor, for use；
S2: being dispersed with stirring 15min for coalescing agent under the conditions of 2000r/min, and the mixing in the step S1 is added thereto
Liquid continues to be dispersed with stirring 15min under the conditions of 2000r/ min, continuously adds PH regulator stirring 8min, is ground to no particle,
Obtain aqueous slurry；
S3: 8 parts of aqueous slurries in selecting step S2 in parts by weight put into lotion and mill base into the slurry of selection,
It is dispersed with stirring 14min under the conditions of 580r/ min, obtains water dyeing mortar after mixing evenly.
Embodiment five
A kind of water dyeing mortar, the component including following parts by weight: 80 parts of lotion, 0.5 part of dispersion moisture agent, film forming helps
10 parts of agent, 2.5 parts of thickener, 1.5 parts of defoaming agent, 0.4 part of antifreeze, 0.4 part of fungicide, 1.5 parts of PH regulator, toner 1.5
Part, 20 parts of deionized water.
S1: first the deionized water in formula, dispersion moisture agent, thickener, defoaming agent, antifreeze and fungicide are existed
It is dispersed with stirring 30min under the conditions of 4000r/min and obtains mixed liquor, for use；
S2: being dispersed with stirring 20min for coalescing agent under the conditions of 2500r/min, and the mixing in the step S1 is added thereto
Liquid continues to be dispersed with stirring 20min under the conditions of 2500r/ min, continuously adds PH regulator stirring 10min, is ground to nothing
Grain, obtains aqueous slurry；
S3: 10 parts of aqueous slurries in selecting step S2 in parts by weight put into lotion and mill base into the slurry of selection,
It is dispersed with stirring 15min under the conditions of 600r/ min, obtains water dyeing mortar after mixing evenly.
The water dyeing mortar prepared through embodiment one, embodiment two, embodiment three, example IV and embodiment five
Material experiment is it is found that the properties of finished product prepared by preparation method of the invention are significantly excellent in common production in the prior art
Product, and the preferred preparation method in the embodiment of the present invention three, obtained end properties are the most excellent.
In the description of this specification, the description of reference term " one embodiment ", " example ", " specific example " etc. means
Particular features, structures, materials, or characteristics described in conjunction with this embodiment or example are contained at least one implementation of the invention
In example or example.In the present specification, schematic expression of the above terms may not refer to the same embodiment or example.
Moreover, particular features, structures, materials, or characteristics described can be in any one or more of the embodiments or examples to close
Suitable mode combines.
Present invention disclosed above preferred embodiment is only intended to help to illustrate the present invention.There is no detailed for preferred embodiment
All details are described, are not limited the invention to the specific embodiments described.Obviously, according to the content of this specification,
It can make many modifications and variations.These embodiments are chosen and specifically described to this specification, is in order to better explain the present invention
Principle and practical application, so that skilled artisan be enable to better understand and utilize the present invention.The present invention is only
It is limited by claims and its full scope and equivalent.
Claims (7)
1. a kind of water dyeing mortar, which is characterized in that the component including following parts by weight: 60-80 parts of lotion, dispersion profit
0.2-0.5 parts of humectant, 5-10 parts of coalescing agent, 2-5 parts of other auxiliary agents, 1-1.5 parts of PH regulator, 1-1.5 parts of mill base, deionization
10-20 parts of water.
2. a kind of water dyeing mortar according to claim 1, it is characterised in that: other described auxiliary agents include following weight
The component of amount number: 0.6-2.5 parts of thickener, 1-1.5 parts of defoaming agent, 0.3-0.4 parts of antifreeze, 0.1-0.4 parts of fungicide.
3. a kind of water dyeing mortar according to claim 1, it is characterised in that: the lotion uses pure-acrylic emulsion.
4. a kind of water dyeing mortar according to claim 1, it is characterised in that: the dispersion moisture agent is selected from poly- third
One or more of olefin(e) acid sodium, tertiary sodium phosphate, silicate, alkyl phenol polyoxyethylene ether and sodium alklyarylsulfonate.
5. a kind of water dyeing mortar according to claim 1, it is characterised in that: the coalescing agent is selected from polyester
One or more of alcohol, polyvinyl alcohol, sodium alginate and xanthan gum.
6. a kind of preparation method of water dyeing mortar, it is characterised in that: the following steps are included:
S1: first by the deionized water in formula, dispersion moisture agent, thickener, defoaming agent, antifreeze and fungicide are in 2000-
It is dispersed with stirring 5-30min under the conditions of 4000r/min and obtains mixed liquor, for use；
S2: coalescing agent is dispersed with stirring 5-20min under the conditions of 1000- 2500r/min, the step S1 is added thereto
In mixed liquor, continue to be dispersed with stirring 5-20min under the conditions of 1000-2500r/ min, continuously add PH regulator stirring 5-
10min is ground to no particle, obtains aqueous slurry；
S3: 2-10 part aqueous slurry in selecting step S2 in parts by weight puts into lotion and mill base into the slurry of selection,
It is dispersed with stirring 10-15min under the conditions of 500-600r/ min, obtains the water dyeing mortar of required color after mixing evenly.
7. a kind of preparation method of water dyeing mortar according to claim 6, it is characterised in that: the step S1,
The device being dispersed with stirring in S2, S3 uses high speed disperser.