CN104974623A - Environment-friendly coating having granite-imitation texture, preparation method and application thereof - Google Patents

Environment-friendly coating having granite-imitation texture, preparation method and application thereof Download PDF

Info

Publication number
CN104974623A
CN104974623A CN201410148313.1A CN201410148313A CN104974623A CN 104974623 A CN104974623 A CN 104974623A CN 201410148313 A CN201410148313 A CN 201410148313A CN 104974623 A CN104974623 A CN 104974623A
Authority
CN
China
Prior art keywords
coating
environment
artificial granite
friendly type
granite texture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410148313.1A
Other languages
Chinese (zh)
Inventor
侯进全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI BOHENG BUILDING MATERIALS TECHNOLOGY DEVELOPMENT CO LTD
Original Assignee
SHANGHAI BOHENG BUILDING MATERIALS TECHNOLOGY DEVELOPMENT CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI BOHENG BUILDING MATERIALS TECHNOLOGY DEVELOPMENT CO LTD filed Critical SHANGHAI BOHENG BUILDING MATERIALS TECHNOLOGY DEVELOPMENT CO LTD
Priority to CN201410148313.1A priority Critical patent/CN104974623A/en
Publication of CN104974623A publication Critical patent/CN104974623A/en
Pending legal-status Critical Current

Abstract

The invention relates to an environment-friendly coating having granite-imitation textures, a preparation method and an application thereof. The coating includes following raw materials, by weight, 50-90 parts of a resin synthetic emulsion and 10-50 parts of color chips. Compared with a coating in the prior art, the coating is green and environment-friendly and is simple in construction.

Description

A kind of environment-friendly type has coating of artificial granite texture and its preparation method and application
Technical field
The present invention relates to a kind of building coating, especially relate to a kind of environment-friendly type and there is coating of artificial granite texture and its preparation method and application.
Background technology
Artificial granite multicolor finish can extensively be promoted at building materials industry exterior wall interior wall, and artificial granite paint, also known as multicolor finish, is be equipped with vinylformic acid synthetic resin emulsion the decorating inner and external walls coating that colorful auxiliary agent and high-weatherability powder are main raw material(s).The ultra-thin multicolor finish of artificial granite is after China appears at 2000 the earliest, the project of the ultra-thin multicolor finish of artificial granite is selected to get more and more every year at present now, although artificial granite ultra-thin multicolor finish stone-like coating is main, its color is imitated, also be only limited to and construct at project scene, due to reasons such as site environments (scaffolding is built, weather, basal plane), the ultra-thin multicolor finish of on-the-spot artificial granite there will be phenomenons such as growing dim.Construction trouble, construction period is normal, and maintenance process also can cause aberration.In paint spay-coating process, other also can be caused to pollute.
Summary of the invention
Object of the present invention be exactly in order to overcome above-mentioned prior art exist defect and provide a kind of environment-friendly type to have coating of artificial granite texture and its preparation method and application.
Object of the present invention can be achieved through the following technical solutions: a kind of environment-friendly type has the coating of artificial granite texture, it is characterized in that, the raw material of this coating comprises the component of following weight part content: resins synthesis emulsion 30 ~ 50 weight part and natural colour sand 50 ~ 70 weight part.
Described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity is at 200 ~ 2000Pas, and testing conditions is: 3#.30rpm, 25 DEG C.
Described resins synthesis emulsion is made by the following method: by weight percentage, silicon Acrylote acrylic emulsion is added 60%, water 33.85%, Mierocrystalline cellulose 0.2%, film coalescence aid 3%, propylene glycol 2.5%, defoamer 0.15%, thickening material 0.3% stirs into the granular cream liquid of a kind of band at normal temperatures and is resins synthesis emulsion.
Described natural colour sand is that natural stone exploits out the grains of sand forming different meshes through rubble, and grains of sand order number comprises 20 ~ 40 orders, 40 ~ 80 orders, 80 ~ 120 orders, the grains of sand color that natural colour sand comprises comprises Snow Flower White, white marble, Chrysan Yellow, golden yellow or Taihang is green.
Environment-friendly type has a preparation method for the coating of artificial granite texture, it is characterized in that, comprises the following steps:
(1) by weight percentage, silicon Acrylote acrylic emulsion is added 60%, water 33.85%, Mierocrystalline cellulose 0.2%, film coalescence aid 3%, propylene glycol 2.5%, defoamer 0.15%, thickening material 0.3% stirs into the granular cream liquid of band and resins synthesis emulsion at normal temperatures;
(2) step (1) gained resins synthesis emulsion 30 ~ 50 weight part is taken and natural colour sand 50 ~ 70 weight part mix and blend obtains coating.
Environment-friendly type has an application for the coating of artificial granite texture, it is characterized in that, the paster this coating being made artificial granite texture is used as building decoration layer; Concrete grammar is as follows:
(1) by ultra-thin for roller coating above grid cloth colorful base paint special, roller coating consumption is 0.1 ~ 0.3kg/m 2, Air drying 2 ~ 5h, forms prime coat;
(2) then on prime coat, spray by spray gun the coating that environment-friendly type has artificial granite texture, quantity for spray is 1 ~ 3kg/m 2, Air drying 2 ~ 5h, forms floating coat;
(3) be pasted onto on floating coat by paster, then at chip surface roller coating protective topcoat, roller coating consumption is 0.2 ~ 0.5kg/m 2, Air drying 2 ~ 6h, forming surface enamelled coating, obtains the artificial granite texture that can directly be pasted onto on exterior wall or interior wall and pastes material.
Described prime coat thickness is 50 ~ 150um, and described ultra-thin colorful base paint special is commercially available priming paint.
Described coating thickness is 2mm.
Described paster thickness is 2mm, and paster is commercially available paster.
Described top coat layer thickness is 50 ~ 150um, and described protective topcoat is commercially available finish paint.
Compared with prior art, the present invention has the following advantages:
1, the technology of the present invention adopts silicon Acrylote acrylic emulsion, improve weathering resistance, the natural colour sand mix and blend of different colours is formed a rifle ejection as the coating of grouan texture together adding, then coating is attached to subsides material paster being formed there is grouan texture in conjunction with priming paint and finish paint, this subsides material makes finished product well at shop, paste on the wall again, can not construct at the scene as original technology and the environmental pollution caused, solve the on-the-spot environmental pollution brought in spraying process, environmental protection.
2, silicon Acrylote acrylic emulsion particle diameter of the present invention very little, has excellent penetrating power to have good sticking power to be more suitable for repacking.
3, relative to the spraying of traditional multiple gun, present spraying together makes its more simple construction technology, and the reduction of erection time improves 3-5 doubly on original basis.
4, the combination of multiple color, it is better that the color effects of grouan and the feel as stone emulate property, decorative effect attractive in appearance.
Accompanying drawing explanation
Fig. 1 is the structural representation of product.
Embodiment
Below in conjunction with the drawings and specific embodiments, the present invention is described in detail.
Embodiment 1
Environment-friendly type has a coating for artificial granite texture, and the raw material of this coating comprises the component of following weight part content: resins synthesis emulsion 40 weight part and natural colour sand 60 weight part.
Described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity is at 200 ~ 2000Pas, and testing conditions is: 3#.30rpm, 25 DEG C.
Described resins synthesis emulsion is made by the following method: by weight percentage, silicon Acrylote acrylic emulsion is added 60%, water 33.85%, Mierocrystalline cellulose 0.2%, film coalescence aid 3%, propylene glycol 2.5%, defoamer 0.15%, thickening material 0.3% stirs into the granular cream liquid of a kind of band at normal temperatures and is resins synthesis emulsion.
Described natural colour sand is that natural stone exploits out the grains of sand forming different meshes through rubble, and grains of sand order number comprises 20 ~ 40 orders, 40 ~ 80 orders, 80 ~ 120 orders, the grains of sand color that natural colour sand comprises comprises Snow Flower White, white marble, Chrysan Yellow, the multiple colors such as golden yellow or Taihang is green.
Resins synthesis emulsion 40 weight part and natural colour sand 60 weight part mix and blend are obtained coating, and the paster this coating being made artificial granite texture is used as building decoration layer; Concrete grammar is as follows:
(1) by ultra-thin for roller coating above grid cloth colorful base paint special, roller coating consumption is 0.2kg/m 2, Air drying 4h, forms prime coat;
(2) then on prime coat, spray by spray gun the coating that environment-friendly type has artificial granite texture, quantity for spray is 2kg/m 2, Air drying 3h, forms floating coat;
(3) be pasted onto on floating coat by paster, then at chip surface roller coating protective topcoat, roller coating consumption is 0.3kg/m 2, Air drying 5h, forming surface enamelled coating, obtains the artificial granite texture that can directly be pasted onto on exterior wall or interior wall and pastes material.
Gained artificial granite texture pastes equipment structure as shown in Figure 1, and described prime coat 1 thickness is 100um, and described ultra-thin colorful base paint special is commercially available priming paint.Described floating coat 2 thickness is 2mm.Described paster 3 thickness is 2mm, and paster is commercially available paster.Described top coat layer 4 thickness is 100um, and described protective topcoat is commercially available finish paint.
Embodiment 2
Environment-friendly type has a coating for artificial granite texture, and the raw material of this coating comprises the component of following weight part content: resins synthesis emulsion 30 weight part and natural colour sand 70 weight part.
Described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity is at 200 ~ 2000Pas, and testing conditions is: 3#.30rpm, 25 DEG C.
Described resins synthesis emulsion is made by the following method: by weight percentage, silicon Acrylote acrylic emulsion is added 60%, water 33.85%, Mierocrystalline cellulose 0.2%, film coalescence aid 3%, propylene glycol 2.5%, defoamer 0.15%, thickening material 0.3% stirs into the granular cream liquid of a kind of band at normal temperatures and is resins synthesis emulsion.
Described natural colour sand is that natural stone exploits out the grains of sand forming different meshes through rubble, and grains of sand order number comprises 20 ~ 40 orders, 40 ~ 80 orders, 80 ~ 120 orders, the grains of sand color that natural colour sand comprises comprises Snow Flower White, white marble, Chrysan Yellow, the multiple colors such as golden yellow or Taihang is green.
Resins synthesis emulsion 30 weight part and natural colour sand 70 weight part mix and blend are obtained coating, and the paster this coating being made artificial granite texture is used as building decoration layer; Concrete grammar is as follows:
(1) by ultra-thin for roller coating above grid cloth colorful base paint special, roller coating consumption is 0.1kg/m 2, Air drying 2h, forms prime coat;
(2) then on prime coat, spray by spray gun the coating that environment-friendly type has artificial granite texture, quantity for spray is 1kg/m 2, Air drying 2h, forms floating coat;
(3) be pasted onto on floating coat by paster, then at chip surface roller coating protective topcoat, roller coating consumption is 0.2kg/m 2, Air drying 2h, forming surface enamelled coating, obtains the artificial granite texture that can directly be pasted onto on exterior wall or interior wall and pastes material.
Embodiment 3
Environment-friendly type has a coating for artificial granite texture, and the raw material of this coating comprises the component of following weight part content: resins synthesis emulsion 50 weight part and natural colour sand 50 weight part.
Described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity is at 200 ~ 2000Pas, and testing conditions is: 3#.30rpm, 25 DEG C.
Described resins synthesis emulsion is made by the following method: by weight percentage, silicon Acrylote acrylic emulsion is added 60%, water 33.85%, Mierocrystalline cellulose 0.2%, film coalescence aid 3%, propylene glycol 2.5%, defoamer 0.15%, thickening material 0.3% stirs into the granular cream liquid of a kind of band at normal temperatures and is resins synthesis emulsion.
Described natural colour sand is that natural stone exploits out the grains of sand forming different meshes through rubble, and grains of sand order number comprises 20 ~ 40 orders, 40 ~ 80 orders, 80 ~ 120 orders, the grains of sand color that natural colour sand comprises comprises Snow Flower White, white marble, Chrysan Yellow, the multiple colors such as golden yellow or Taihang is green.
Resins synthesis emulsion 50 weight part and natural colour sand 50 weight part mix and blend are obtained coating, and the paster this coating being made artificial granite texture is used as building decoration layer; Concrete grammar is as follows:
(1) by ultra-thin for roller coating above grid cloth colorful base paint special, roller coating consumption is 0.3kg/m 2, Air drying 5h, forms prime coat;
(2) then on prime coat, spray by spray gun the coating that environment-friendly type has artificial granite texture, quantity for spray is 3kg/m 2, Air drying 5h, forms floating coat;
(3) be pasted onto on floating coat by paster, then at chip surface roller coating protective topcoat, roller coating consumption is 0.5kg/m 2, Air drying 6h, forming surface enamelled coating, obtains the artificial granite texture that can directly be pasted onto on exterior wall or interior wall and pastes material.

Claims (10)

1. environment-friendly type has a coating for artificial granite texture, it is characterized in that, the raw material of this coating comprises the component of following weight part content: resins synthesis emulsion 30 ~ 50 weight part and natural colour sand 50 ~ 70 weight part.
2. a kind of environment-friendly type according to claim 1 has the coating of artificial granite texture, it is characterized in that, described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity is at 200 ~ 2000Pas, and testing conditions is: 3#.30rpm, 25 DEG C.
3. a kind of environment-friendly type according to claim 1 and 2 has the coating of artificial granite texture, it is characterized in that, described resins synthesis emulsion is made by the following method: by weight percentage, silicon Acrylote acrylic emulsion is added 60%, water 33.85%, Mierocrystalline cellulose 0.2%, film coalescence aid 3%, propylene glycol 2.5%, defoamer 0.15%, thickening material 0.3% stirs into the granular cream liquid of a kind of band at normal temperatures and is resins synthesis emulsion.
4. a kind of environment-friendly type according to claim 1 has the coating of artificial granite texture, it is characterized in that, described natural colour sand is that natural stone exploits out the grains of sand forming different meshes through rubble, grains of sand order number comprises 20 ~ 40 orders, 40 ~ 80 orders, 80 ~ 120 orders, the grains of sand color that natural colour sand comprises comprises Snow Flower White, white marble, Chrysan Yellow, golden yellow or Taihang is green.
5. environment-friendly type as claimed in claim 1 has a preparation method for the coating of artificial granite texture, it is characterized in that, comprises the following steps:
(1) by weight percentage, silicon Acrylote acrylic emulsion is added 60%, water 33.85%, Mierocrystalline cellulose 0.2%, film coalescence aid 3%, propylene glycol 2.5%, defoamer 0.15%, thickening material 0.3% stirs into the granular cream liquid of band and resins synthesis emulsion at normal temperatures;
(2) step (1) gained resins synthesis emulsion 30 ~ 50 weight part is taken and natural colour sand 50 ~ 70 weight part mix and blend obtains coating.
6. environment-friendly type as claimed in claim 1 has an application for the coating of artificial granite texture, it is characterized in that, the paster this coating being made artificial granite texture is used as building decoration layer: concrete grammar is as follows:
(1) by ultra-thin for roller coating above grid cloth colorful base paint special, roller coating consumption is 0.1 ~ 0.3kg/m 2, Air drying 2 ~ 5h, forms prime coat;
(2) then on prime coat, spray by spray gun the coating that environment-friendly type has artificial granite texture, quantity for spray is 1 ~ 3kg/m 2, Air drying 2 ~ 5h, forms floating coat;
(3) be pasted onto on floating coat by paster, then at chip surface roller coating protective topcoat, roller coating consumption is 0.2 ~ 0.5kg/m 2, Air drying 2 ~ 6h, forming surface enamelled coating, obtains the artificial granite texture that can directly be pasted onto on exterior wall or interior wall and pastes material.
7. a kind of environment-friendly type according to claim 6 has the coating of artificial granite texture, it is characterized in that, described prime coat thickness is 50 ~ 150um, and described ultra-thin colorful base paint special is commercially available priming paint.
8. a kind of environment-friendly type according to claim 6 has the coating of artificial granite texture, it is characterized in that, described coating thickness is 2mm.
9. a kind of environment-friendly type according to claim 6 has the coating of artificial granite texture, it is characterized in that, described paster thickness is 2mm, and paster is commercially available paster.
10. a kind of environment-friendly type according to claim 6 has the coating of artificial granite texture, it is characterized in that, described top coat layer thickness is 50 ~ 150um, and described protective topcoat is commercially available finish paint.
CN201410148313.1A 2014-04-14 2014-04-14 Environment-friendly coating having granite-imitation texture, preparation method and application thereof Pending CN104974623A (en)