CN102181144A - 喷涂硬泡聚氨酯保温防水一体化材料 - Google Patents

喷涂硬泡聚氨酯保温防水一体化材料 Download PDF

Info

Publication number
CN102181144A
CN102181144A CN 201110033170 CN201110033170A CN102181144A CN 102181144 A CN102181144 A CN 102181144A CN 201110033170 CN201110033170 CN 201110033170 CN 201110033170 A CN201110033170 A CN 201110033170A CN 102181144 A CN102181144 A CN 102181144A
Authority
CN
China
Prior art keywords
weight parts
component
integrated material
waterproof integrated
insulating waterproof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110033170
Other languages
English (en)
Inventor
田凤兰
段文锋
孙莉
刘子康
杜鸿志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Oriental Yuhong Waterproof Technology Co., Ltd.
Xuzhou Woniushan New Waterproof Material Co., Ltd.
Beijing Oriental Yuhong Waterproof Technology Co Ltd
Original Assignee
Beijing Oriental Yuhong Waterproof Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Oriental Yuhong Waterproof Technology Co Ltd filed Critical Beijing Oriental Yuhong Waterproof Technology Co Ltd
Priority to CN 201110033170 priority Critical patent/CN102181144A/zh
Publication of CN102181144A publication Critical patent/CN102181144A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种喷涂硬泡聚氨酯保温防水材料，其为现场喷涂成型的等体积比的A组分和B组分构成的双组分泡沫塑料，所述A组分由0～30重量份甲苯二异氰酸酯、0～30重量份二苯基甲烷二异氰酸酯和70～100多苯基多亚甲基多异氰酸酯组成；所述B组分由30～50重量份多元醇、10～20重量份催化剂、5～10重量份匀泡剂、10～30重量份发泡剂和10～30重量份阻燃剂组成；该材料具有阻燃性、高强度、高密度、防水、保温、隔热、防腐和耐溶剂等功能的泡沫塑料层。主要应用于工业与民用建筑的各种屋面、墙体、大跨度的轻型金属、网架结构屋面的防水、保温、隔热；高层建筑、上人屋面或屋顶花园的防水、保温、绝热等。

Description

喷涂硬泡聚氨酯保温防水一体化材料
技术领域：
本发明提供一种喷涂硬泡聚氨酯保温防水一体化材料及其施工方法。
背景技术：
喷涂硬泡聚氨酯保温材料(以下简称SPF)是一种新型的高分子合成材料，在几十年的发展过程中，其优异的特性在不同的建筑业领域中，用作屋面保温、隔热、隔音材料性能优越。SPF硬泡体屋面在欧、美、日等工业发达国家和我国香港地区及大陆地区均已获得广泛应用，市场增长率保持3-5％，美国2005年增长率为5.6％。在喷涂SPF与叠层油毡屋面的竟争中以其保温隔热、耐水、轻质、耐风揭占据着越来越明显的优势。
作为一种优异的保温节能材料，聚氨酯硬泡在建筑节能方面具有巨大的发展潜力，其导热系数低，仅0.018-0.024(w/m*k)，相当于EPS的一半，是目前所有保温材料中导热系数最低的，且热工性能好，还具有耐老化、化学稳定性好、防潮防水性优良、耐温不熔化，与建筑物基面粘结性能好等优点。但是现有的喷涂硬泡聚氨酯材料仅具有保温隔热的功能，在进行屋面施工时，除要做保温层外还需要额外做防水层。
发明内容：
本发明的一种喷涂硬泡聚氨酯保温防水材料，其为现场喷涂成型的A组分和B组分构成的双组分泡沫塑料，其中所述A组分由0～30重量份甲苯二异氰酸酯、0～30重量份二苯基甲烷二异氰酸酯和70～100多苯基多亚甲基多异氰酸酯组成；所述B组分由30～50重量份多元醇、10～20重量份催化剂、5～10重量份匀泡剂、10～30重量份发泡剂和10～30重量份阻燃剂组成。
所述的聚醚多元醇是选自聚醚多元醇，聚酯多元醇，聚合物多元醇或其混合物。
所述的聚醚多元醇选自蔗糖系、山梨醇系、乙二胺系的聚醚多元醇或其混合物，且羟值在240～550mgKOH/g，优选300～450mgKOH/g之间。
所述的聚酯多元醇是选自苯酐系、松香系的聚酯多元醇或其混合物，且羟值在240～550mgKOH/g之间，优选300～450mgKOH/g之间。
所述的催化剂选自胺类催化剂和有机锡类催化剂，选自二甲基甲酰胺、三乙醇胺、五甲基苄胺、二月桂酸二丁基锡或其混合物。
所述的发泡剂选自HCFC-141b、环戊烷、异戊烷、HFC-134a、HFC-245fa、HFC-365fmc或其混合物。
述阻燃剂选自甲基磷酸二甲酯、二溴苯基多元醇、三氯乙基磷酸酯或其混合物的卤素阻燃剂。
所述B组分中还含有抗氧剂、紫外线吸收剂、颜填料和/或增强材料。
A组分中多异氰酸酯和二异氰酸酯的端氨基聚醚的比例是可以调整的，这主要取决于所需的最终产品的性能，要想得到强度高的泡沫塑料，应增加多异氰酸酯的用量，要想得到密度低的泡沫塑料应增加二异氰酸酯的用量。
本发明的喷涂硬泡聚氨酯保温防水一体化材料的施工时喷涂设备可使用美国Graco⑧公司的A-20、E-20或H-25主机和Fusion AP喷枪，Glas-Craft公司的A5-6000主机和Probler喷枪等。
本发明的喷涂硬泡聚氨酯保温防水一体化材料显著优点是固化速度快，一般在低于20秒的时间内迅速固化，层间施工间隔只需几分钟，如施工100m2/5cm厚的泡沫塑料层，仅需4小时即可完成施工，1～2小时即可投入使用。
本发明另一个显著特点就是100％固含量，只要正确使用本技术，无论是施工期间，还是材料投入使用后，泡沫塑料层均不产生有害物质和刺激性气味。
本发明的喷涂硬泡聚氨酯保温防水一体化材料固化后表现出优异的综合性能，例如阻燃性、高强度、高密度、防水、保温、隔热、防腐和耐溶剂等。性能指标见实施例。
喷涂硬泡聚氨酯保温防水一体化材料应用最大的领域之一是工业与民用建筑的各种屋面、墙体、大跨度的轻型金属、网架结构屋面的防水、保温、隔热。
喷涂硬泡聚氨酯保温防水一体化材料可用作高层建筑、上人屋面或屋顶花园的防水、保温、绝热。
喷涂硬泡聚氨酯保温防水一体化材料可用于旧建筑的维修与改造。
喷涂硬泡聚氨酯保温防水一体化材料可用于水池、游泳池等各类建筑物的防水保温工程。
本发明提供的喷涂硬泡聚氨酯保温防水一体化材料除具有传统材料的保温隔热性能外，还具有防水性能，一层保温防水一体化材料层可以顶传统的保温层与防水层两层材料的作用，在进行施工时，阻燃型喷涂硬泡聚氨酯保温防水一体化材料的施工和传统的喷涂硬泡聚氨酯材料是一样的，这样就省去了传统材料施工时的防水层的施工工作。
具体实施方式
以下结合实施例对本发明作进一步详细描述。
其中：44V20多苯基多亚甲基多异氰酸酯为德国Bayer公司产品
TCEP三(2-氯乙基)磷酸酯为浙江淳安助剂厂产品
HCFC-141b二氯一氟乙烷为浙江三爱富化工公司产品
实施例1：
将羟值为400的聚醚多元醇50重量份加入充氮的反应釜中，在搅拌下加入硅油5重量份，二甲基甲酰胺10重量份，三乙醇胺10重量份，阻燃剂TCEP 15重量份，HCFC-141b 10重量份搅拌均匀出料包装即为B组分。A组分选用多苯基多亚甲基多异氰酸酯44V20 100重量份。A、B组分通过美国Graco公司的A-20主机和Fusion AP喷枪按1∶1(体积比)喷涂形成聚氨酯泡沫塑料。该体系适合于高层建筑、上人屋面或屋顶花园的防水、保温、绝热。
该聚氨酯泡沫塑料的主要物理性能见表1
表1聚氨酯泡沫塑料的主要物理性能
  项目   指标
  起发时间   4秒
  抗压强度   400KPa
  密度   70kg/m3
  导热系数   0.022
  氧指数   26
实施例2：
将羟值为450的聚醚多元醇30重量份加入充氮的反应釜中，在搅拌下加入硅油10重量份，二甲基甲酰胺10重量份，三乙醇胺10重量份，阻燃剂TCEP 10重量份，HCFC-141b 30重量份搅拌均匀出料包装即为B组分。A组分选用多苯基多亚甲基多异氰酸酯44V20 70重量份和甲苯二异氰酸酯30重量份。A、B组分通过美国Graco公司的A-20主机和Fusion AP喷枪按1∶1(体积比)喷涂形成聚氨酯泡沫塑料。该体系适合于高层建筑、上人屋面或屋顶花园的防水、保温、绝热。
该聚氨酯泡沫塑料的主要物理性能见表2
表2聚氨酯泡沫塑料的主要物理性能
  项目   指标
  起发时间   4秒
  抗压强度   240KPa
  密度   40kg/m3
  导热系数   0.022
  氧指数   26
实施例3：
将羟值为420的聚醚多元醇40重量份加入充氮的反应釜中，在搅拌下加入硅油7重量份，二甲基甲酰胺3重量份，三乙醇胺7重量份，阻燃剂TCEP 30重量份，HCFC-141b 20重量份搅拌均匀出料包装即为B组分。A组分选用多苯基多亚甲基多异氰酸酯44V20 70重量份和二苯基甲烷二异氰酸酯30重量份。A、B组分通过美国Graco公司的A-20主机和Fusion AP喷枪按1∶1(体积比)喷涂形成聚氨酯泡沫塑料。该体系适合于高层建筑、上人屋面或屋顶花园的防水、保温、绝热。
该聚氨酯泡沫塑料的主要物理性能见表3
表3聚氨酯泡沫塑料的主要物理性能
  项目   指标
  起发时间   6秒
  抗压强度   320KPa
  密度   50kg/m3
  导热系数   0.022
  氧指数   26
实施例4：
将羟值为400的聚醚多元醇30重量份加入充氮的反应釜中，在搅拌下加入硅油10重量份，二甲基甲酰胺8重量份，三乙醇胺7重量份，阻燃剂TCEP 22重量份，HCFC-141b 23重量份搅拌均匀出料包装即为B组分。A组分选用多苯基多亚甲基多异氰酸酯44V20 80重量份、甲苯二异氰酸酯12重量份和甲苯二异氰酸酯8重量份。A、B组分通过美国Graco公司的A-20主机和Fusion AP喷枪按1∶1(体积比)喷涂形成聚氨酯泡沫塑料。该体系适合于高层建筑、上人屋面或屋顶花园的防水、保温、绝热。
该聚氨酯泡沫塑料的主要物理性能见表4
表4聚氨酯泡沫塑料的主要物理性能
  项目   指标
  起发时间   5秒
  抗压强度   280KPa
  密度   47kg/m3
  导热系数   0.022
  氧指数   26
对比例1：
将羟值为400的聚醚多元醇40重量份加入充氮的反应釜中，在搅拌下加入硅油10重量份，二甲基甲酰胺10重量份，三乙醇胺10重量份，HCFC-141b 30重量份搅拌均匀出料包装即为B组分。A组分选用多苯基多亚甲基多异氰酸酯44V20 70重量份和甲苯二异氰酸酯30重量份。A、B组分通过美国Graco公司的A-20主机和Fusion AP喷枪按1∶1(体积比)喷涂形成聚氨酯泡沫塑料。该体系适合于高层建筑、上人屋面或屋顶花园的防水、保温、绝热。
该聚氨酯泡沫塑料的主要物理性能见表5
表5聚氨酯泡沫塑料的主要物理性能
  项目   指标
  起发时间   4.5秒
  抗压强度   260KPa
  密度   40kg/m3
  导热系数   0.026
  氧指数   19

Claims (8)

1.一种喷涂硬泡聚氨酯保温防水一体化材料，其为现场喷涂成型的等体积比的A组分和B组分构成的双组分泡沫塑料，其中：
所述A组分由0～30重量份甲苯二异氰酸酯、0～30重量份二苯基甲烷二异氰酸酯和70～100多苯基多亚甲基多异氰酸酯组成；
所述B组分由30～50重量份多元醇、10～20重量份催化剂、5～10重量份匀泡剂、10～30重量份发泡剂和10～30重量份阻燃剂组成。
2.根据权利要求1所述的喷涂硬泡聚氨酯保温防水一体化材料，其特征在于所述的多元醇选自聚醚多元醇，聚酯多元醇，聚合物多元醇或其混合物。
3.根据权利要求2所述的喷涂硬泡聚氨酯保温防水一体化材料，其特征在于所述的多元醇选自蔗糖系、山梨醇系、乙二胺系的聚醚多元醇或其混合物，且羟值在240～550mgKOH/g。
4.根据权利要求2的喷涂硬泡聚氨酯保温防水一体化材料，其特征在于所述的聚酯多元醇选自苯酐系、松香系的聚酯多元醇或其混合物，且羟值在240～550mgKOH/g之间。
5.根据权利要求1的喷涂硬泡聚氨酯保温防水一体化材料，其特征在于所述催化剂选自二甲基甲酰胺、三乙醇胺、五甲基苄胺、二月桂酸二丁基锡或其混合物。
6.根据权利要求1的喷涂硬泡聚氨酯保温防水一体化材料，其特征在于所述发泡剂选自HCFC-141b、环戊烷、异戊烷、HFC-134a、HFC-245fa、HFC-365fmc或其混合物。
7.根据权利要求1的喷涂硬泡聚氨酯保温防水一体化材料，其特征在于所述阻燃剂选自甲基磷酸二甲酯、二溴苯基多元醇、三氯乙基磷酸酯或其混合物。
8.根据权利要求1的喷涂硬泡聚氨酯保温防水一体化材料，其特征在于所述B组分中还含有抗氧剂、紫外线吸收剂、颜填料和/或增强材料。
CN 201110033170 2011-01-31 2011-01-31 喷涂硬泡聚氨酯保温防水一体化材料 Pending CN102181144A (zh)