CN102108206A - 高性能尼龙树脂/硫酸钙晶须复合材料及其制备方法 - Google Patents

高性能尼龙树脂/硫酸钙晶须复合材料及其制备方法 Download PDF

Info

Publication number
CN102108206A
CN102108206A CN 200910200857 CN200910200857A CN102108206A CN 102108206 A CN102108206 A CN 102108206A CN 200910200857 CN200910200857 CN 200910200857 CN 200910200857 A CN200910200857 A CN 200910200857A CN 102108206 A CN102108206 A CN 102108206A
Authority
CN
China
Prior art keywords
calcium sulfate
parts
sulfate crystal
crystal whiskers
nylon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200910200857
Other languages
English (en)
Other versions
CN102108206B (zh
Inventor
查敏
张祥福
周文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Printer Material Technology Co Ltd
Shanghai Pret Composites Co Ltd
Zhejiang Pret New Materials Co Ltd
Shanghai Pret Material Technology Co Ltd
Chongqing Pret New Materials Co Ltd
Shanghai Pret Chemical New Materials Co Ltd
Original Assignee
Shanghai Pret Composites Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Pret Composites Co Ltd filed Critical Shanghai Pret Composites Co Ltd
Priority to CN 200910200857 priority Critical patent/CN102108206B/zh
Publication of CN102108206A publication Critical patent/CN102108206A/zh
Application granted granted Critical
Publication of CN102108206B publication Critical patent/CN102108206B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了高性能尼龙树脂/硫酸钙晶须复合材料，按以下重量百分比的原料组成：尼龙6树脂45～80份，玻璃纤维10～30份，硫酸钙晶须10～25份，其他添加剂0.2～10份。本发明首先配方中采用玻璃纤维和硫酸钙晶须复合增强尼龙材料。通过玻璃纤维和晶须的协同作用，表现出十分显著的增强效果。在一定的添加量和添加比例下，两者复合增强效果可超过纯玻纤。不仅提升了复合材料的强度、模量、耐高温性、表面光洁度，而且由于硫酸钙晶须自身的价格优势，可进一步降低生产成本。其次，对生产工艺进行了调整，以侧向喂料方式添加硫酸钙晶须，减少了硫酸钙晶须在加工过程中的断裂和磨损，提高了复合材料的强度和尺寸的稳定性。

Description

高性能尼龙树脂/硫酸钙晶须复合材料及其制备方法
技术领域
本发明涉及一种高分子材料，具体为一种高性能尼龙树脂/硫酸钙晶须复合材料及其制备方法。
背景技术
尼龙6(PA6)工程塑料具有高韧性、耐磨性、自润滑、自熄性、耐油和耐腐蚀等良好的综合性能，产量居五大工程塑料之首，被广泛应用于汽车、电子电气、机械、铁路、兵器和建筑等领域。
对于填充增强尼龙材料，已有人作了相关研究并进行了报道。中国专利CN1970629A，该发明专利申请的名称为“高性能树脂/云母复合材料及生产方法”。该材料主要由树脂、云母粉、短玻璃纤维、偶联剂、抗氧剂、润滑剂等组成，其中树脂是尼龙或聚对苯二甲酸丁二醇酯。该发明方法具有操作简单、成本低、生产效率高等优点，制备的树脂/云母复合材料，具有良好的尺寸稳定性，和较高的强度、模量及耐热性等特点，同时也改善了冲击性能。该发明专利也公开了其产品的制作方法，将云母粉加入偶联剂进行活化处理、将双螺杆挤出机螺纹块组件进行组合，采用三段捏合方式进行螺纹块配置，将各组分混合或分别输送到双螺杆挤出机，进行挤出造粒等步骤。
又如专利CN101440213A，专利名称为“一种用于汽车后视镜支架的尼龙6组合物”。该材料的组成为尼龙6切片40-80％，玻璃纤维5-30％，无机矿物5-30％，相容剂1-10％，抗氧剂0.1-0.5％，偶联剂0.1-0.5％。该发明具有高流动性，极高的冲击性能，优良的尺寸稳定性，耐化学性好，制品表面光洁等特点，可用于注塑成型汽车后视镜支架，也可用于加工其他性能要求较高的汽车零部件和机电产品。
本发明采用硫酸钙晶须与玻璃纤维复合增强体系改性PA6，增强效果显著。此外本发明还对生产工艺进行了调整，以侧向喂料方式添加硫酸钙晶须，进一步提高了复合材料的强度和尺寸的稳定性。由本法制得的复合材料并加工成型的制件不仅性能优异，外表美观，生产成本也得到了有效降低，有很大的实用性和商业价值。
发明内容
本发明的目的旨在提供一种高性能尼龙树脂/硫酸钙晶须复合材料的制备方法。
本发明的目的可以通过以下技术方案来实现：
高性能尼龙树脂/硫酸钙晶须复合材料，按以下重量百分比的原料组成：
尼龙6树脂     45～80份
玻璃纤维      10～30份
硫酸钙晶须    10～25份
其他添加剂    0.2～10份。
所述的尼龙6树脂的数均分子量在5000～30000。
所述的玻璃纤维为无碱、中碱和高强度玻纤中的一种或几种，玻纤直径为5～20μm。
所述的硫酸钙晶须平均直径为0.2～8μm，平均长度为10～200μm。
所述的其他添加剂包括相容剂、增韧剂、抗氧剂、耐光照助剂、阻燃剂、各种颜色添加剂、各种酯类或脂肪酸类润滑剂等；
上述高性能尼龙树脂/硫酸钙晶须复合材料的制备方法，其具体步骤为：
(1)按上述重量配比称取原料。
(2)将尼龙6、其它添加剂均匀混和后进入双螺杆挤出机，在专用玻璃纤维口处添加玻璃纤维，在第四区侧向喂料口处添加硫酸钙晶须，加工工艺如下：一区温度190～210℃，二区温度220～240℃，三区温度220～240℃，四区温度220～240℃，五区温度220～250℃，主机转速250～440转/分钟，侧喂料转速30～60转/分钟。
(3)挤出后冷却、干燥、切粒即得高性能填充增强尼龙材料。
本发明首先配方中采用玻璃纤维和硫酸钙晶须复合增强尼龙材料。通过玻璃纤维和晶须的协同作用，表现出十分显著的增强效果。在一定的添加量和添加比例下，两者复合增强效果可超过纯玻纤。不仅提升了复合材料的强度、模量、耐高温性、表面光洁度，而且由于硫酸钙晶须自身的价格优势，可进一步降低生产成本。
其次，对生产工艺进行了调整，以侧向喂料方式添加硫酸钙晶须，减少了硫酸钙晶须在加工过程中的断裂和磨损，进一步提高了复合材料的强度和尺寸的稳定性。
具体实施方式
下面结合实施例，对本发明作进一步详细说明。
在实施例及对比例合金材料配方中，尼龙6牌号为PA6-YH800，岳阳石化生产。
所述的玻纤牌号为ER13-2000-988A，巨石集团生产。
所述的硫酸钙晶须平均直径为1～4μm，平均长度为50～200μm，洛阳亮东非金属材料科技开发有限公司生产。
所述的其他添加剂为抗氧剂1098和168(1∶1)。其中抗氧剂1098牌号为Irganox 1098，化学名称为N，N-双-[3-(3，5-二叔丁基-4-羟基苯基)丙酰基]己二胺，Ciba公司生产。抗氧剂168牌号为Irgafos 168，化学名称为三(2，4-二叔丁基苯基)亚磷酸酯，Ciba公司生产。
首先将硫酸钙晶须在80～100℃条件下干燥4～6小时。将尼龙6、其它添加剂在高速混合器中干混3～5分钟后进入双螺杆挤出机。在专用玻璃纤维口处添加玻璃纤维，在第四区侧向喂料口处添加干燥后的硫酸钙晶须。加工工艺如下：一区温度190～210℃，二区温度220～240℃，三区温度220～240℃，四区温度220～240℃，五区温度220～250℃，主机转速250～440转/分钟，侧喂料转速30～60转/分钟。
产品性能测试方法：
拉伸性能，按ISO527方法，拉伸速度为50mm/min，样条尺寸为150*10*4mm。
弯曲性能，按ISO178方法，试验速度为2mm/min，样条尺寸为80*10*4mm，跨距64mm。
缺口Charpy冲击强度，按ISO179方法，样条尺寸为80*10*4mm，缺口深度为试样厚度的五分之一。
下面介绍本发明的实施例：
实施例1
将尼龙6 70份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维15份，在第四区侧向喂料口处添加干燥过的硫酸钙晶须15份，造粒制成复合材料。
实施例2
将尼龙6 60份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维20份，在第四区侧向喂料口处添加干燥过的硫酸钙晶须20份，造粒制成复合材料。
实施例3
将尼龙6 70份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维20份，在第四区侧向喂料口处添加干燥过的硫酸钙晶须10份，造粒制成复合材料。
实施例4
将尼龙6 60份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维25份，在第四区侧向喂料口处添加干燥过的硫酸钙晶须15份，造粒制成复合材料。
对比例1
将尼龙6 70份，干燥过的硫酸钙晶须15份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维15份，造粒制成复合材料。
对比例2
将尼龙6 60份，干燥过的硫酸钙晶须20份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维20份，造粒制成复合材料。
对比例3
将尼龙6 70份，干燥过的硫酸钙晶须10份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维20份，造粒制成复合材料。
对比例4
将尼龙6 60份，干燥过的硫酸钙晶须15份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维25份，造粒制成复合材料。
对比例5
将尼龙6 70份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维30份，造粒制成复合材料。
对比例6
将尼龙6 60份，抗氧剂1098 0.1份，抗氧剂168 0.2份混合后置于双螺杆挤出机中经220～240℃熔融挤出，并在专用玻璃纤维口处添加玻璃纤维40份，造粒制成复合材料。
表1尼龙6/硫酸钙晶须复合材料性能
Figure G2009102008577D00071
由对比例1～对比例4与对比例子5～对比例6的性能对比可以看出，硫酸钙晶须与玻璃纤维的复合增强效果显著。当硫酸钙晶须与玻璃纤维添加比例相等时增强效果更为明显，特别是当填充量为30份左右，硫酸钙晶须与玻纤对基体树脂的复合增强效果可优于纯玻纤。可能是由于晶须的强度大，在加工过程中磨损较少，对树脂具有较好的增强效果，且与玻纤产生协同效应，使得增强效果更加突出。此外，从材料注塑成样件的表面可以看出复合增强的PA6材料比纯玻纤增强PA6材料具有更好的表面光洁度。
其次，实施例1～实施例4与对比例1～对比例4的性能对比可以看出，以侧向喂料方式添加硫酸钙晶须可进一步提高复合材料的性能。侧向添加硫酸钙晶须可有效的减少晶须在加工过程中的断裂和磨损，增强效果更加显著。

Claims (6)

1.高性能尼龙树脂/硫酸钙晶须复合材料，其特征在于：按以下重量百分比的原料组成：
尼龙6树脂        45～80份
玻璃纤维         10～30份
硫酸钙晶须       10～25份
其他添加剂       0.2～10份。
2.根据权利要求1所述的高性能尼龙树脂/硫酸钙晶须复合材料，其特征在于：所述的尼龙6树脂的数均分子量在5000～30000。
3.根据权利要求1所述的高性能尼龙树脂/硫酸钙晶须复合材料，其特征在于：所述的玻璃纤维为无碱、中碱和高强度玻纤中的一种或几种，玻纤直径为5～20μm。
4.根据权利要求1所述的高性能尼龙树脂/硫酸钙晶须复合材料，其特征在于：所述的硫酸钙晶须平均直径为0.2～8μm，平均长度为10～200μm。
5.根据权利要求1所述的高性能尼龙树脂/硫酸钙晶须复合材料，其特征在于：所述的其他添加剂包括相容剂、增韧剂、抗氧剂、耐光照助剂、阻燃剂、各种颜色添加剂、各种酯类或脂肪酸类润滑剂。
6.一种制备权利要求1所述的高性能尼龙树脂/硫酸钙晶须复合材料的制备方法，其具体步骤为：
(1)按权利要求1的重量配比称取原料。
(2)将尼龙6、其它添加剂均匀混和后进入双螺杆挤出机，在专用玻璃纤维口处添加玻璃纤维，在第四区侧向喂料口处添加硫酸钙晶须，加工工艺如下：一区温度190～210℃，二区温度220～240℃，三区温度220～240℃，四区温度220～240℃，五区温度220～250℃，主机转速250～440转/分钟，侧喂料转速30～60转/分钟。
(3)挤出后冷却、干燥、切粒即得高性能填充增强尼龙材料。
CN 200910200857 2009-12-25 2009-12-25 高性能尼龙树脂/硫酸钙晶须复合材料及其制备方法 Active CN102108206B (zh)