CN102108016A - 一种液态复合型水泥助磨剂的制备方法 - Google Patents

一种液态复合型水泥助磨剂的制备方法 Download PDF

Info

Publication number
CN102108016A
CN102108016A CN2011100640269A CN201110064026A CN102108016A CN 102108016 A CN102108016 A CN 102108016A CN 2011100640269 A CN2011100640269 A CN 2011100640269A CN 201110064026 A CN201110064026 A CN 201110064026A CN 102108016 A CN102108016 A CN 102108016A
Authority
CN
China
Prior art keywords
cement grinding
liquid composite
grinding aid
preparation
liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011100640269A
Other languages
English (en)
Inventor
张祯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011100640269A priority Critical patent/CN102108016A/zh
Publication of CN102108016A publication Critical patent/CN102108016A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种液态复合型水泥助磨剂的制备方法，主要工艺过程是将乙二醇、羧甲基纤维素、羧甲基淀粉、六偏磷酸钠、三乙丙醇胺、纯净水以上各组份依次加入反应器中，加热混合搅拌制备成液态复合型水泥助磨剂；液态复合型水泥助磨剂的使用，使得水泥粉磨工段的磨机台时产量提高了10％～15％，吨水泥电耗降低了3～6度；液态复合型水泥助磨剂还具有计量准确，贮存和使用方便的优点。

Description

一种液态复合型水泥助磨剂的制备方法
技术领域
本发明涉及一种液态复合型水泥助磨剂的制备方法；特别指新型干法水泥生产过程中，用于水泥粉磨工段的液态复合型助磨剂的制备方法。
背景技术
目前国内新型干法水泥生产过程中，水泥粉磨工段的电耗较之国外先进水平，仍有一定的差距，在选用新型磨机的同时，通过添加专用助磨剂来提高磨机的研磨效率，降低电耗，是一个重要的研发方向。
发明内容
本发明要解决的技术问题是提供一种用于水泥粉磨工段的液态复合型水泥助磨剂的制备方法，这种液态复合型助磨剂有乙二醇、羧甲基纤维素、羧甲基淀粉、六偏磷酸钠、三乙丙醇胺、纯净水复合制备而成，使用时的添加量为研磨粉状物料量的0.01％～0.03％。
本发明要解决的技术问题由如下方案来实现：一种液态复合型水泥助磨剂的制备方法，其特征是：组成液态助磨剂的各组份按重量百分比为：乙二醇10％～15％、羧甲基纤维素2％～6％、羧甲基淀粉1％～3％、六偏磷酸钠0.5％～1.5％、三乙丙醇胺1％～3％、纯净水71.5％～85.5％。制备过程如下：按比例定量移取各组份加入反应器中，加热升温至35℃～45℃，搅拌30分钟～50分钟后，降温至室温出料包装即为液态复合型水泥助磨剂。
本发明的优点是：液态复合型水泥助磨剂的使用，使得水泥粉磨工段的磨机台时产量提高了10％～15％，吨水泥电耗降低了3～6度；液态复合型水泥助磨剂还具有计量准确，贮存和使用方便的优点。
附图说明
图1是液态复合型水泥助磨剂制备工艺流程示意图
具体实施方式
实施例1：以制备100kg液态复合型水泥助磨剂为例，称取乙二醇10kg、羧甲基纤维素2kg、羧甲基淀粉1kg、六偏磷酸钠0.5kg、三乙丙醇胺1kg、纯净水85.5kg，依次加入反应器中，开动搅拌，加热升温至35℃，搅拌30分钟后降温至室温后出料包装。
实施例2：以制备100kg液态复合型水泥助磨剂为例，称取乙二醇12.5kg、羧甲基纤维素4kg、羧甲基淀粉2kg、六偏磷酸钠1kg、三乙丙醇胺2kg、纯净水78.5kg，依次加入反应器中，开动搅拌，加热升温至40℃，搅拌40分钟后降温至室温后出料包装。
实施例3：以制备100kg液态复合型水泥助磨剂为例，称取乙二醇15kg、羧甲基纤维素6kg、羧甲基淀粉3kg、六偏磷酸钠1.5kg、三乙丙醇胺3kg、纯净水71.5kg，依次加入反应器中，开动搅拌，加热升温至45℃，搅拌50分钟后降温至室温后出料包装。

Claims (1)

1.一种液态复合水泥助磨剂的制备方法，其特征是：液态水泥助磨剂的各组份按重量百分比为，乙二醇10％～15％，羧甲基纤维素2％～6％，羧甲基淀粉1％～3％，六偏磷酸钠0.5％～1.5％，三乙丙醇胺1％～3％，纯净水71.5％～85.5％，以上各组份依次加入反应器中，加热升温至35℃～45℃，搅拌混合30分钟～50分钟，降温至室温后出料包装即为液态复合型水泥助磨剂。
CN2011100640269A 2011-03-10 2011-03-10 一种液态复合型水泥助磨剂的制备方法 Pending CN102108016A (zh)