CN104909598B - 一种氟硅酸钠水泥助磨剂及其制备方法 - Google Patents

一种氟硅酸钠水泥助磨剂及其制备方法 Download PDF

Info

Publication number
CN104909598B
CN104909598B CN201510264266.1A CN201510264266A CN104909598B CN 104909598 B CN104909598 B CN 104909598B CN 201510264266 A CN201510264266 A CN 201510264266A CN 104909598 B CN104909598 B CN 104909598B
Authority
CN
China
Prior art keywords
prodan
cement
grinding aid
water
triethanolamine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510264266.1A
Other languages
English (en)
Other versions
CN104909598A (zh
Inventor
谭纪林
华玉海
华建军
蒋兆广
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huaian Cement Factory Co ltd
Tan Jilin
Original Assignee
Huai An Chu Cheng Cement Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huai An Chu Cheng Cement Co Ltd filed Critical Huai An Chu Cheng Cement Co Ltd
Priority to CN201510264266.1A priority Critical patent/CN104909598B/zh
Publication of CN104909598A publication Critical patent/CN104909598A/zh
Application granted granted Critical
Publication of CN104909598B publication Critical patent/CN104909598B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种氟硅酸钠水泥助磨剂，由如下组分按质量百分比组成：氟硅酸钠20‑25%、三乙醇胺5‑10%和水65‑75%。制备方法是将氟硅酸钠、三乙醇胺和水按配比称重后，在常温下将氟硅酸钠加入水中进行搅拌至完全溶解，然后将三乙醇胺加入其中进行搅拌至完全溶解，即制得氟硅酸钠水泥助磨剂。本发明可以提高熟料的粉磨效率，减少熟料用量，多用混合材掺量，解决了水泥生产中的包球现象，提高了水泥比表面积，而又减少了水泥需水量，从而达到了提高产量、质量和降低成本的效果。

Description

一种氟硅酸钠水泥助磨剂及其制备方法
技术领域
本发明属于水泥生产领域，尤其涉及一种氟硅酸钠水泥助磨剂及其制备方法。
背景技术
在水泥粉磨生产过程中，助磨剂的使用是一项有利于节能降耗、减排利废的措施，当熟料、石膏和各种混合材在粉磨过种中，就会产生物料与磨机和物料与物料之间起到撞击而导致静电，从而产生水泥磨机出现严重的包球现象，影响水泥的生产效率和质量保证。目前，国内外生产的水泥助磨剂虽然可以消除这种问题，但生产成本高。
节能降耗是当前水泥行业的紧迫工作，但与水泥生产过程中其他节能减排的途径相比，用一种性能优良的水泥助磨剂可以提高磨机的台时产量降低水泥电耗，减少熟料用量，多掺混合材用量，减少水泥中的需水量，降低水泥成本，使水泥生产企业在市场中增强了竞争力。
发明内容
发明目的：本发明的目的是为了解决现有的水泥助磨剂生产成本高的问题，提供一种氟硅酸钠水泥助磨剂及其制备方法。
技术方案：本发明所述的氟硅酸钠水泥助磨剂，由如下组分按质量百分比组成：氟硅酸钠（Na2SiF6）20-25%、三乙醇胺5-10%和水65-75%。
本发明还提供一种氟硅酸钠水泥助磨剂的制备方法，将氟硅酸钠、三乙醇胺和水按配比称重后，在常温下将氟硅酸钠加入水中进行搅拌至完全溶解，然后将三乙醇胺加入其中进行搅拌至完全溶解，即制得氟硅酸钠水泥助磨剂。
有益效果：1、由于本发明中添加有氟硅酸钠，因此，可以提高熟料的粉磨效率，减少熟料用量，多用混合材掺量，解决了水泥生产中的包球现象，提高了水泥比表面积，而又减少了水泥需水量，从而达到了提高产量、质量和降低成本的效果。
2、经实际检验，用本发明的氟硅酸钠水泥助磨剂与外购助磨剂和不掺助磨剂相比较情况下，掺用本发明助磨剂可提高水泥生产粉磨效率，提高水泥磨机台时产量20-30%，减少熟料5-7%，提高水泥比表面积40-80㎡/kg，提高水泥强度3天、28天分别为3-5mpa、4-6mpa，增加混合材的添加量，又能减少水泥中的需水量10%，全国每年按15亿吨水泥计算，可节约用水量1.5亿吨左右，实现了节能降耗、减排利废的措施，同时，保证了水泥节能提产的要求。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，这些实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
实施例1
氟硅酸钠水泥助磨剂，由如下组分按质量百分比组成：氟硅钠20%，三乙醇胺5%，水75%。
实施例2
氟硅酸钠水泥助磨剂，由如下组分按质量百分比组成：氟硅钠22%、三乙醇胺7%、水71%。
实施例3
氟硅酸钠水泥助磨剂，由如下组分按质量百分比组成：氟硅钠23%、三乙醇胺8%、水69%。
实施例4
氟硅酸钠水泥助磨剂，由如下组分按质量百分比组成：氟硅钠24%、三乙醇胺9%、水67%。
实施例5
氟硅酸钠水泥助磨剂，由如下组分按质量百分比组成：氟硅钠25%，三乙醇胺10%，水65%
将上述实施例1-5各组分按配比称量后，在常温条件下将氟硅酸钠先加入水中，搅拌至完全溶解，然后再将三乙醇胺加入其中搅拌至溶解，即制得氟硅酸钠水泥助磨剂。
下表是本发明氟硅酸钠水泥助磨剂各实施例与不掺助磨剂和外购助磨剂性能相比较检验结果。各实施例制备得到的氟硅酸钠水泥助磨剂和外购助磨剂的添加量均为0.8‰。
从表格中可以看出，用本发明的氟硅酸钠水泥助磨剂与外购助磨剂和不掺助磨剂相比较情况下，掺用本发明助磨剂可提高水泥生产粉磨效率，提高水泥磨机台时产量20-30%，减少熟料5-7%，提高水泥比表面积40-80㎡/kg，提高水泥强度3天、28天分别为3-5mpa、4-6mpa，增加混合材的添加量，又能减少水泥中的需水量10%，全国每年按15亿吨水泥计算，可节约用水量1.5亿吨左右，实现了节能降耗、减排利废的措施，同时，保证了水泥节能提产的要求。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围，凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。

Claims (2)

1.一种氟硅酸钠水泥助磨剂，其特征在于，由如下组分按质量百分比组成：氟硅酸钠20-25%、三乙醇胺5-10%和水65-75%。
2.如权利要求1所述的氟硅酸钠水泥助磨剂的制备方法，其特征在于，将氟硅酸钠、三乙醇胺和水按配比称重后，在常温下将氟硅酸钠加入水中进行搅拌至完全溶解，然后将三乙醇胺加入其中进行搅拌至完全溶解，即制得氟硅酸钠水泥助磨剂。
CN201510264266.1A 2015-05-22 2015-05-22 一种氟硅酸钠水泥助磨剂及其制备方法 Expired - Fee Related CN104909598B (zh)