CN102092761A - 抗结块硝酸锶的制备方法 - Google Patents
抗结块硝酸锶的制备方法 Download PDFInfo
- Publication number
- CN102092761A CN102092761A CN2009101919224A CN200910191922A CN102092761A CN 102092761 A CN102092761 A CN 102092761A CN 2009101919224 A CN2009101919224 A CN 2009101919224A CN 200910191922 A CN200910191922 A CN 200910191922A CN 102092761 A CN102092761 A CN 102092761A
- Authority
- CN
- China
- Prior art keywords
- strontium nitrate
- temperature
- product
- strontium
- caking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗结块硝酸锶的制备方法，以工业硝酸和工业碳酸锶为原料，依次经反应、除杂、浓缩、结晶、离心、干燥、包装制得硝酸锶产品，所述硝酸锶的干燥工艺为：将硝酸锶放入温度120～140℃、真空度-0.06～-0.08Mpa的真空干燥箱中，干燥至产品最终含水量≤0.1％；然后将干燥后的硝酸锶取出，放入温度为40～50℃的恒温密闭环境中，并通入冷风，冷却至硝酸锶温度与环境温度相同。由本发明制备的硝酸锶不易结块，减少了客户的生产使用成本；同时，延长了硝酸锶的贮存时间。
Description
技术领域
本发明涉及一种制备硝酸锶的方法，尤其是抗结块硝酸锶的制备方法。
背景技术
硝酸锶是一种重要的无机精细化工产品，用于TFT-LCD液晶、PDP等离子彩电中。目前，硝酸锶的制备方法多以工业硝酸和工业碳酸锶为原料，经过反应、除杂、浓缩、结晶、离心、干燥、包装得产品。现有的干燥包装方式是经过脱水后，干燥水份在0.3％下进行包装，没有进行目的性的控制，造成产品出来后结块现象严重，需人工粉碎后才可使用，影响客户的使用，加大了客户的生产成本；而且，产品贮存的时间较短。
发明内容
本发明针对硝酸锶易结块的问题，提供一种硝酸锶的制备方法，通过该制备方法制备的硝酸锶不易结块。
为了解决上述问题，本发明的技术方案为：一种抗结块硝酸锶的制备方法，以工业硝酸和工业碳酸锶为原料，依次经反应、除杂、浓缩、结晶、离心、干燥、包装制得硝酸锶产品，所述硝酸锶的干燥工艺为：将硝酸锶放入温度120～140℃、真空度-0.06～-0.08Mpa的真空干燥箱中，干燥至产品最终含水量≤0.1％；然后将干燥后的硝酸锶取出，放入温度为40～50℃的恒温密闭环境中，并通入冷风，冷却至硝酸锶温度与环境温度相同。
采用上述技术方案后，通过控制干燥的真空度和干燥温度，使产品在干燥过程中，干燥充分、均匀，并在控制的条件下进行龟裂，有效去除晶体内部的晶间水份，从而控制产品水份含量在0.1％以下，在包装过程中，物料在专门的包装间，在通过冷冻设备的强制冷却下，使物料冷却到规定的温度进行包装，这样，产品的粒径均匀，性能稳定，降低了晶间重新结合的可能，从而确保产品无论外观质量，还是流散性能都非常良好，产品防结块性能大大提高，产品堆放半年不会有结块的现象。
干燥温度为120～140℃，优选为125～135℃。温度过高，干燥能耗大幅度提高；温度过低，干燥效率降低，产品干燥时间延长。
真空度为-0.06～-0.08Mpa，优选为-0.065～-0.075Mpa。在真空环境下，产品附着水及较高沸点物汽化迅速，有效去除晶体内部的晶间水份和杂质，使得产品干燥效率、纯度和防结块得到明显提高。真空度低于-0.06MPa，干燥时间延长；真空度高于-0.08MPa，能耗升高，对产品防结块性能的提高没有明显影响。
冷却的温度为40～50℃，优选为40～45℃。温度过高，产品晶体分子在外界高温下重新架桥连接，使产品防结块性能降低；温度过低，效率降低，同时对产品防结块性能没有明显提高。
本发明的有益效果是：本发明的有益效果是：由本发明制备的硝酸锶不易结块，减少了客户的生产使用成本；同时，延长了硝酸锶的贮存时间。
具体实施方式
下面结合实施例进一步对本发明加以说明。
实施例1
将工业硝酸和工业碳酸锶加入反应釜中，进行反应，反应完成后按现有工艺进行除杂、浓缩、结晶、离心操作，将得到的含水2.5％的硝酸锶湿料，将硝酸锶湿料放入温度120℃、真空度-0.06Mpa的真空干燥箱中，干燥2小时，然后将干燥后的硝酸锶取出，放入温度为40℃的恒温密闭包装间中，并通入冷风，冷却至硝酸锶温度与环境温度相同，经检测产品最终含水量为0.1％，最后包装得产品。
实施例2
前面的工艺与实施例1相同，将离心后的硝酸锶湿料放入温度125℃、真空度-0.065Mpa的真空干燥箱中，干燥1.5小时，然后将干燥后的硝酸锶取出，放入温度为40℃的恒温密闭包装间中，并通入冷风，冷却至硝酸锶温度与环境温度相同，经检测产品最终含水量为0.09％，最后包装得产品。
实施例3
前面的工艺与实施例1相同，将离心后的硝酸锶湿料放入温度140℃、真空度-0.07Mpa的真空干燥箱中，干燥1小时，然后将干燥后的硝酸锶取出，放入温度为50℃的恒温密闭包装间中，并通入冷风，冷却至硝酸锶温度与环境温度相同，经检测产品最终含水量为0.085％，最后包装得产品。
Claims (3)
1.一种抗结块硝酸锶的制备方法，以工业硝酸和工业碳酸锶为原料，依次经反应、除杂、浓缩、结晶、离心、干燥、包装制得硝酸锶产品，其特征在于：所述硝酸锶的干燥工艺为：将硝酸锶放入温度120～140℃、真空度-0.06～-0.08Mpa的真空干燥箱中，干燥至产品最终含水量≤0.1％；然后将干燥后的硝酸锶取出，放入温度为40～50℃的恒温密闭环境中，并通入冷风，冷却至硝酸锶温度与环境温度相同。
2.根据权利要求1所述的抗结块硝酸锶的制备方法，其特征在于：所述真空干燥箱的温度为125～135℃，真空度为-0.065～-0.075Mpa。
3.根据权利要求1所述的抗结块硝酸锶的制备方法，其特征在于：所述恒温密闭环境的温度为40～45℃。