CN101981219B - 生产具有改善外观的涂覆金属带材的方法 - Google Patents

生产具有改善外观的涂覆金属带材的方法 Download PDF

Info

Publication number
CN101981219B
CN101981219B CN2009801070225A CN200980107022A CN101981219B CN 101981219 B CN101981219 B CN 101981219B CN 2009801070225 A CN2009801070225 A CN 2009801070225A CN 200980107022 A CN200980107022 A CN 200980107022A CN 101981219 B CN101981219 B CN 101981219B
Authority
CN
China
Prior art keywords
coating
metal strip
metal
strip
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2009801070225A
Other languages
English (en)
Chinese (zh)
Other versions
CN101981219A (zh
Inventor
L·迪兹
J-M·马泰格纳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ArcelorMittal Investigacion y Desarrollo SL
Original Assignee
ArcelorMittal Investigacion y Desarrollo SL
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=39810192&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN101981219(B) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by ArcelorMittal Investigacion y Desarrollo SL filed Critical ArcelorMittal Investigacion y Desarrollo SL
Publication of CN101981219A publication Critical patent/CN101981219A/zh
Application granted granted Critical
Publication of CN101981219B publication Critical patent/CN101981219B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/18—Layered products comprising a layer of metal comprising iron or steel
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/20—Layered products comprising a layer of metal comprising aluminium or copper
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/14—Removing excess of molten coatings; Controlling or regulating the coating thickness
    • C23C2/16—Removing excess of molten coatings; Controlling or regulating the coating thickness using fluids under pressure, e.g. air knives
    • C23C2/18—Removing excess of molten coatings from elongated material
    • C23C2/20—Strips; Plates
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C26/00—Coating not provided for in groups C23C2/00 - C23C24/00
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C23C30/005—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process on hard metal substrates
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12229—Intermediate article [e.g., blank, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/1241—Nonplanar uniform thickness or nonlinear uniform diameter [e.g., L-shape]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y10T428/12979—Containing more than 10% nonferrous elements [e.g., high alloy, stainless]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12993—Surface feature [e.g., rough, mirror]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Thermal Sciences (AREA)
  • Coating With Molten Metal (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Extrusion Moulding Of Plastics Or The Like (AREA)
CN2009801070225A 2008-05-14 2009-05-14 生产具有改善外观的涂覆金属带材的方法 Active CN101981219B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP08290450.9 2008-05-14
EP08290450A EP2119804A1 (fr) 2008-05-14 2008-05-14 Procédé de fabrication d'une bande métallique revêtue présentant un aspect amélioré
PCT/FR2009/000560 WO2009147309A1 (fr) 2008-05-14 2009-05-14 Procede de fabrication d'une bande metallique revetue presentant un aspect ameliore

Publications (2)

Publication Number Publication Date
CN101981219A CN101981219A (zh) 2011-02-23
CN101981219B true CN101981219B (zh) 2012-09-12

Family

ID=39810192

Family Applications (1)

Application Number Title Priority Date Filing Date
CN2009801070225A Active CN101981219B (zh) 2008-05-14 2009-05-14 生产具有改善外观的涂覆金属带材的方法

Country Status (16)

Country Link
US (2) US9914992B2 (enExample)
EP (2) EP2119804A1 (enExample)
JP (2) JP5677289B2 (enExample)
KR (1) KR101259595B1 (enExample)
CN (1) CN101981219B (enExample)
AT (1) ATE551436T1 (enExample)
BR (1) BRPI0910310B1 (enExample)
CA (1) CA2714220C (enExample)
ES (1) ES2385287T3 (enExample)
MA (1) MA32143B1 (enExample)
MX (1) MX2010008776A (enExample)
PL (1) PL2297372T3 (enExample)
RU (1) RU2457275C2 (enExample)
UA (1) UA107326C2 (enExample)
WO (1) WO2009147309A1 (enExample)
ZA (1) ZA201005488B (enExample)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102994927A (zh) * 2012-12-20 2013-03-27 常熟市保得利电力通讯设备有限公司 一种热镀锌的配方

Families Citing this family (36)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2119804A1 (fr) 2008-05-14 2009-11-18 ArcelorMittal France Procédé de fabrication d'une bande métallique revêtue présentant un aspect amélioré
WO2010130884A1 (fr) 2009-05-14 2010-11-18 Arcelormittal Investigacion Y Desarrollo Sl Procédé de fabrication d'une bande métallique revêtue présentant un aspect amélioré
WO2010130883A1 (fr) 2009-05-14 2010-11-18 Arcelormittal Investigacion Y Desarrollo Sl Procede de fabrication d'une bande metallique revetue presentant un aspect ameliore
JP5341270B1 (ja) * 2012-04-25 2013-11-13 日新製鋼株式会社 黒色めっき鋼板の製造方法および黒色めっき鋼板の成形体の製造方法
JP5335159B1 (ja) * 2012-04-25 2013-11-06 日新製鋼株式会社 黒色めっき鋼板の製造方法および黒色めっき鋼板の成形体の製造方法
CN102703846B (zh) * 2012-06-12 2015-06-24 常州大学 热浸镀Zn-Al-Zr合金镀层及其热浸镀方法
EP2703515A1 (de) 2012-09-03 2014-03-05 voestalpine Stahl GmbH Verfahren zum Aufbringen eines Schutzüberzugs auf ein Stahlflachprodukt und Stahlflachprodukt mit einem entsprechenden Schutzüberzug
PT2954086T (pt) 2013-02-06 2017-04-11 Arcelormittal Chapa com revestimento de znalmg com uma microestrutura particular e correspondente processo de produção
WO2014135753A1 (fr) 2013-03-06 2014-09-12 Arcelormittal Investigacion Y Desarrollo, S.L. Procédé de réalisation d'une tôle à revêtement znal avec un essorage optimisé, tôle, pièce et véhicule correspondants
UA116262C2 (uk) 2013-08-01 2018-02-26 Арселорміттал Сталевий лист з цинковим покриттям
UA117592C2 (uk) * 2013-08-01 2018-08-27 Арселорміттал Пофарбований оцинкований сталевий лист та спосіб його виготовлення
WO2015052546A1 (fr) 2013-10-09 2015-04-16 ArcelorMittal Investigación y Desarrollo, S.L. Tôle à revêtement znaimg à flexibilité améliorée et procédé de réalisation correspondant
US9816168B2 (en) 2013-12-20 2017-11-14 Arcelormittal Method for producing a sheet having a ZnAlMg coating with optimized wiping
CA2935047C (fr) * 2013-12-20 2021-01-05 Arcelormittal Procede de realisation d'une tole a revetement znalmg avec un essorage optimise et tole correspondante
BR112016017434B1 (pt) 2014-01-30 2022-12-27 Arcelormittal Método para fabricar partes feitas de uma lâmina de metal e parte
JP6072952B1 (ja) * 2016-03-01 2017-02-01 日新製鋼株式会社 黒色めっき鋼板を製造する方法、黒色めっき鋼板を製造する装置および黒色めっき鋼板を製造するシステム
CN108018514B (zh) * 2016-10-28 2020-07-28 宝山钢铁股份有限公司 一种控制Zn-Al-Mg合金镀层板材表面缺陷的方法及Zn-Al-Mg合金镀层板材
KR101830549B1 (ko) 2016-12-14 2018-02-20 주식회사 포스코 프레스 성형성 및 도장 선영성이 우수한 용융아연도금강판의 제조방법 및 이에 의해 제조된 용융아연도금강판
JP6438562B1 (ja) * 2017-06-13 2018-12-12 東洋鋼鈑株式会社 圧延接合体及びその製造方法
CN122522152A (zh) * 2017-05-25 2026-08-07 塔塔钢铁艾默伊登有限责任公司 制造连续热浸涂覆钢带材和热浸涂覆钢片材的方法
CN107177809A (zh) * 2017-07-05 2017-09-19 国网山东省电力公司电力科学研究院 一种热浸镀锌铝钙合金镀层及其热浸镀方法
CN108220855B (zh) * 2018-02-08 2020-04-24 鞍山发蓝股份公司 一种高强度包装用镀锌钢带的制备方法
CN108441796B (zh) * 2018-04-18 2020-01-10 江苏克罗德科技有限公司 一种热镀锌铝镁合金钢板及其生产工艺
US11013340B2 (en) 2018-05-23 2021-05-25 L&P Property Management Company Pocketed spring assembly having dimensionally stabilizing substrate
US12369722B2 (en) 2018-05-23 2025-07-29 L&P Property Management Company Method of disassembling pocketed spring assembly with dimensionally stabilizing substrate
EP3861146A1 (en) * 2018-10-02 2021-08-11 Tata Steel IJmuiden B.V. Coated metal sheet, method to provide such a coated metal sheet, and hot dip galvanizing device to manufacture such a coated metal sheet
DE102019214135A1 (de) * 2019-09-17 2021-03-18 Thyssenkrupp Steel Europe Ag Stahlblech mit einer deterministischen Oberflächenstruktur
DE102019215051B4 (de) * 2019-09-30 2024-11-21 Thyssenkrupp Steel Europe Ag Stahlblech mit einer deterministischen Oberflächenstruktur und Verfahren zur Herstellung des Stahlblechs mit einer deterministischen Oberflächenstruktur
US11905579B1 (en) 2019-09-30 2024-02-20 Thyssenkrupp Steel Europe Ag Sheet steel having a deterministic surface structure
CN110923603A (zh) * 2019-12-09 2020-03-27 晋江安能建材制造有限公司 一种高耐热性的热浸镀铝锌钢板及其生产方法
CN110777316B (zh) * 2019-12-09 2021-11-23 福建安能新材料股份有限公司 一种稀土合金热浸镀层钢板及其生产方法
CN110923600B (zh) * 2019-12-09 2021-12-14 福建安能新材料股份有限公司 一种具有锌锰镁硅合金热浸镀层的钢板及其生产方法
JP7050739B2 (ja) * 2019-12-19 2022-04-08 アルセロールミタル 電気亜鉛めっき金属シートからうねりの少ない部品を製造するための方法、対応する部品および車両
DE102020208991A1 (de) 2020-07-17 2022-01-20 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines schmelztauchbeschichteten Stahlblechs und schmelztauchbeschichtetes Stahlblech
WO2022101667A1 (en) 2020-11-16 2022-05-19 Arcelormittal A method for manufacturing a steel sheet with a znalmg coating, corresponding coated steel sheet, part and vehicle
WO2025177022A1 (en) * 2024-02-21 2025-08-28 Arcelormittal A method to produce a znalmg coated steel sheet and said steel sheet

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1161383A (zh) * 1996-12-10 1997-10-08 马鞍山市鼎泰金属制品公司 新型稀土锌铝合金镀层材料及其热浸镀工艺
WO2002033141A1 (en) * 2000-10-19 2002-04-25 Nkk Corporation Zinc-plated steel sheet and method for preparation thereof, and method for manufacturing formed article by press working
CN1612947A (zh) * 2002-01-09 2005-05-04 新日本制铁株式会社 涂装后的耐蚀性与涂装鲜映性优异的镀锌钢板

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5573888A (en) * 1978-11-22 1980-06-03 Nippon Kokan Kk <Nkk> High corrosion resistant zinc-electroplated steel sheet with coating and non-coating
AU544400B2 (en) * 1980-03-25 1985-05-23 International Lead Zinc Research Organization Inc. Zinc-aluminum alloys and coatings
AU525668B2 (en) * 1980-04-25 1982-11-18 Nippon Steel Corporation Hot dip galvanizing steel strip with zinc based alloys
JPS5891162A (ja) * 1981-11-18 1983-05-31 Nisshin Steel Co Ltd 溶融亜鉛めつき鋼板の製造方法
JPS6158257A (ja) 1984-08-29 1986-03-25 Toshiba Corp 半導体装置の製造方法
JPH02175852A (ja) * 1988-09-07 1990-07-09 Nippon Steel Corp 表面平滑性に優れた高耐食性溶融亜鉛―アルミニウム合金めっき鋼板の製造方法
JPH0675728B2 (ja) 1988-12-27 1994-09-28 川崎製鉄株式会社 鮮映性に優れた表面処理鋼板の製造法
BE1003440A6 (fr) * 1989-12-21 1992-03-24 Centre Rech Metallurgique Procede pour augmenter la resistance a la corrosion d'un revetement de zinc-aluminium.
JP2754126B2 (ja) * 1992-11-26 1998-05-20 新日本製鐵株式会社 外観、耐経時黒変性、耐食性に優れる溶融Ｚｎ−Ａｌめっき鋼板
JP3201469B2 (ja) * 1997-11-04 2001-08-20 日新製鋼株式会社 Ｍｇ含有溶融Ｚｎ基めっき鋼板
JP2001152304A (ja) 1999-11-30 2001-06-05 Nkk Corp 表面外観が優れた溶融Ａｌ−Ｚｎ系合金めっき鋼板の製造方法
JP3503594B2 (ja) 2000-12-05 2004-03-08 住友金属工業株式会社 耐黒変性に優れた溶融Ｚｎ−Ａｌ合金めっき鋼板とその製造方法
JP4655420B2 (ja) * 2001-07-02 2011-03-23 Ｊｆｅスチール株式会社 プレス成形性に優れた溶融亜鉛めっき鋼帯の製造方法
JP3732141B2 (ja) * 2001-11-09 2006-01-05 新日本製鐵株式会社 加工後の耐食性に優れた溶融亜鉛−Ａｌ系合金めっき鋼板及びその製造方法
CN100540719C (zh) * 2002-03-08 2009-09-16 新日本制铁株式会社 表面平滑性优良的高耐蚀性热浸镀钢材
JP4601268B2 (ja) * 2003-01-21 2010-12-22 Ｊｆｅスチール株式会社 表面処理亜鉛系めっき鋼板
DE05758026T1 (de) * 2004-06-29 2009-04-30 Corus Staal B.V. Stahlblech mit durch feuerverzinkung aufgbrachter zinklegierungsbeschichtung und herstellungsverfahren dafür
RU2295584C1 (ru) * 2005-06-14 2007-03-20 Общество с ограниченной ответственностью "Полимет" Сплав на основе цинка
EP2119804A1 (fr) 2008-05-14 2009-11-18 ArcelorMittal France Procédé de fabrication d'une bande métallique revêtue présentant un aspect amélioré
WO2010130883A1 (fr) 2009-05-14 2010-11-18 Arcelormittal Investigacion Y Desarrollo Sl Procede de fabrication d'une bande metallique revetue presentant un aspect ameliore
WO2010130884A1 (fr) 2009-05-14 2010-11-18 Arcelormittal Investigacion Y Desarrollo Sl Procédé de fabrication d'une bande métallique revêtue présentant un aspect amélioré
JP6158257B2 (ja) 2015-07-17 2017-07-05 愛三工業株式会社 燃料供給装置

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1161383A (zh) * 1996-12-10 1997-10-08 马鞍山市鼎泰金属制品公司 新型稀土锌铝合金镀层材料及其热浸镀工艺
WO2002033141A1 (en) * 2000-10-19 2002-04-25 Nkk Corporation Zinc-plated steel sheet and method for preparation thereof, and method for manufacturing formed article by press working
CN1612947A (zh) * 2002-01-09 2005-05-04 新日本制铁株式会社 涂装后的耐蚀性与涂装鲜映性优异的镀锌钢板

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102994927A (zh) * 2012-12-20 2013-03-27 常熟市保得利电力通讯设备有限公司 一种热镀锌的配方

Also Published As

Publication number Publication date
CA2714220A1 (fr) 2009-12-10
KR20100118129A (ko) 2010-11-04
EP2297372A1 (fr) 2011-03-23
ES2385287T3 (es) 2012-07-20
ZA201005488B (en) 2011-09-28
PL2297372T3 (pl) 2012-09-28
JP5986185B2 (ja) 2016-09-06
US10550458B2 (en) 2020-02-04
CN101981219A (zh) 2011-02-23
US9914992B2 (en) 2018-03-13
RU2010136313A (ru) 2012-03-10
UA107326C2 (en) 2014-12-25
MX2010008776A (es) 2010-08-30
US20110111255A1 (en) 2011-05-12
EP2119804A1 (fr) 2009-11-18
KR101259595B1 (ko) 2013-04-30
BRPI0910310A2 (pt) 2016-04-26
US20180002798A1 (en) 2018-01-04
MA32143B1 (fr) 2011-03-01
ATE551436T1 (de) 2012-04-15
JP2015083721A (ja) 2015-04-30
RU2457275C2 (ru) 2012-07-27
BRPI0910310B1 (pt) 2019-07-02
CA2714220C (fr) 2012-12-18
EP2297372B1 (fr) 2012-03-28
WO2009147309A1 (fr) 2009-12-10
JP2011521103A (ja) 2011-07-21
JP5677289B2 (ja) 2015-02-25

Similar Documents

Publication Publication Date Title
JP5986185B2 (ja) 外観が改善された被覆金属ストリップを製造する方法
JP5669824B2 (ja) 改善された外観を有する被覆金属バンドを製造する方法
JP6009100B2 (ja) ＺｎＡｌコーティングおよび最適化された拭きつけを用いて金属シートを製造するための方法、対応する金属シート、部品および車両
EP3396004B1 (en) Method for preparing a plated steel material having excellent friction resistance and white rust resistance
KR101528116B1 (ko) 개선된 외형을 갖는 코팅된 금속 스트립의 제조 방법
CN106029933B (zh) 用于生产具有最佳擦拭的ZnAlMg涂覆的金属板材的方法和相应的金属板材
CN111108226A (zh) 具有改善的表面外观的热浸涂覆的钢带及其制造方法
JP2026009969A (ja) ＺｎＡｌＭｇ被膜を有する鋼板の製造方法、対応する被覆鋼板、部品及び車両
US9816168B2 (en) Method for producing a sheet having a ZnAlMg coating with optimized wiping
BR112023006093B1 (pt) Método para fabricar uma chapa de aço fornecida com um revestimento, chapa de aço revestida e peça

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant