CN101812203A - 高耐制动液三元乙丙橡胶配方 - Google Patents

高耐制动液三元乙丙橡胶配方 Download PDF

Info

Publication number
CN101812203A
CN101812203A CN200910311022A CN200910311022A CN101812203A CN 101812203 A CN101812203 A CN 101812203A CN 200910311022 A CN200910311022 A CN 200910311022A CN 200910311022 A CN200910311022 A CN 200910311022A CN 101812203 A CN101812203 A CN 101812203A
Authority
CN
China
Prior art keywords
formula
ethylene propylene
braking fluid
propylene terpolymer
accelerant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910311022A
Other languages
English (en)
Other versions
CN101812203B (zh
Inventor
张洪起
胡金明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Peng Ling group Limited by Share Ltd
Original Assignee
Tianjin Pengling Rubber Hose Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Pengling Rubber Hose Co Ltd filed Critical Tianjin Pengling Rubber Hose Co Ltd
Priority to CN2009103110229A priority Critical patent/CN101812203B/zh
Publication of CN101812203A publication Critical patent/CN101812203A/zh
Application granted granted Critical
Publication of CN101812203B publication Critical patent/CN101812203B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高耐制动液三元乙丙橡胶配方，其特征是配方组分和质量百分比含量为：三元乙丙橡胶：29～40，N330：5～9，N550：19～24，硅粉：24～32，聚异丁烯：5～8，氧化锌：0.5～1.5，硬脂酸：0.2～0.4，聚乙二醇：0.5～1，防老剂RD：0.2～0.4，促进剂TMTD：0.25～0.3，促进剂DTDM：0.25～0.4，促进剂DM：0.25～0.4，促进剂CZ：0.25～0.4，硫磺：0.2～0.4。对于在新配方中使用了硅粉以及聚异丁烯，改善原有配方的耐DOT制动液体积变化高于5％的问题，高分子聚异丁烯为了更好的与三元乙丙橡胶结合而不会被制动液类溶剂抽出。本发明开发的配方从性能上，明确看到能够弥补现有技术的缺陷，使胶管在长期使用后仍能保持原有性能不会有太大变化，保证制动效果。

Description

高耐制动液三元乙丙橡胶配方
技术领域
本发明涉及橡胶配方技术，特别涉及一种高耐制动液三元乙丙橡胶配方。
背景技术
随着高等级公路的增多，汽车平均速度的提高，如何让高速行驶的汽车在最短的距离内，安全、稳定的进行制动减速或停车，已成为人们所关注的主要问题之一。制动系统在其中起到至关重要的作用，而经过了由机械式向液压制动式转变，制动液胶管在液压制动系统中又占有重要的作用。现在的耐制动液性能要求为：热老化温度125摄氏度，在DOT类型制动液中浸泡72小时后胶料体积变化为±5％，而对于老配方在进行耐制动液体积变化时超出5％要求的问题(实测结果见后附性能对照表)，因此就必须有一种新产品来满足该性能要求。
老的耐制动液三元乙丙橡胶配方：
  序号   原材料名称   配方(％)
  1   三元乙丙橡胶   30.2
  2   N330   5.4
  3   N550   34.8
  4   N774   6.1
  5   石蜡油3118   19.4
  6   氧化锌   1.2
  7   硬脂酸   0.5
  8   聚乙二醇   0.8
  9   促进剂TMTD   0.3
  10   促进剂DTDM   0.4
  11   促进剂DM   0.4
  序号   原材料名称   配方(％)
  12   促进剂CZ   0.3
  13   硫磺   0.2
  合计   -   100
发明内容
本发明主要解决的是现有配方在耐制动液(DOT类)方面体积变化的不足，主要体现在，胶管在长期使用后，在制动过程中出现由于耐制动液性能不好导致体积变化增大，性能降低，从而出现制动迟缓造成事故。
新的耐制动液三元乙丙橡胶配方：
  序号   原材料组分   重量百分比含量(％)
  1   三元乙丙橡胶   29～40
  2   N330   5～9
  3   N550   19～24
  4   硅粉   24～32
  5   聚异丁烯   5～8
  6   氧化锌   0.5～1.5
  7   硬脂酸   0.2～0.4
  8   聚乙二醇   0.5～1
  9   防老剂RD   0.2～0.4
  10   促进剂TMTD   0.25～0.3
  11   促进剂DTDM   0.25～0.4
  12   促进剂DM   0.25～0.4
  13   促进剂CZ   0.25～0.4
  序号   原材料组分   重量百分比含量(％)
  14   硫磺   0.2～0.4
对于在新配方中使用了硅粉以及聚异丁烯，改善原有配方的耐DOT制动液体积变化高于5％的问题，高分子聚异丁烯为了更好的与三元乙丙橡胶结合而不会被制动液类溶剂抽出。
具体实施方式
三元乙丙配方实施方式：
含量以重量百分比计
Figure G200910311022920091207D000031
对于新、老配方硫化试片后进行的性能对比见下表：
按所列配方中原材料及用量进行混炼加工：橡胶、原材料称量-一段密炼-一段开炼-下片-二段密炼-二段开炼-下片-硫化胶片-按标准裁取式样-进行试验检测。
性能对照如下：
  序号   试验条件   技术要求   老配方实测值   新配方实测值
  1   原始性能
  1.1   硬度   75±5A   78.1   75.9
  1.2   扯断伸长   ≥300％   334   357
  1.3   扯断强力   ≥12Mpa   11.2   13
  2   耐125度72小时热老化
  2.1   硬度变化   ±7A   +6.3   +5.9
  2.2   扯断伸长变化   ±30％   -29.3   -28.9
  2.3   扯断强力变化   ±15％   +13.8   +10.8
  3   耐120度70小时DOT4老化性能
  3.1   硬度变化   ±5A   +4.5   -1.5
  3.2   扯断伸长变化   ±30％   -48.3   -28.3
  3.3   扯断强力变化   ±8％   +7.8   +3.8
  3.4   体积变化   ±5％   -7.6   1.6
本发明开发的配方从性能上尤其从耐DOT制动液老化后体积变化方面，明确看到能够弥补现有技术的缺陷，使胶管在长期使用后仍能保持原有性能不会有太大变化，保证制动效果。
本发明提出的三元乙丙橡胶配方，已通过以上进行了详细描述，相关技术人员明显能在不脱离本发明内容、精神和范围内对本文所述的配方进行改动或适当变更与组合来实现本发明技术。特别需要指出的是，所有相类似的替换和改动对本领域技术人员来说是显而易见的，他们都被视为包括在本发明精神、范围和内容中。

Claims (1)

1.一种高耐制动液三元乙丙橡胶配方，其特征是配方组份和质量百分比含量如下：
三元乙丙橡胶    29～40；
N330            5～9；
N550            19～24；
硅粉            24～32；
聚异丁烯        5～8；
氧化锌          0.5～1.5；
硬脂酸          0.2～0.4；
聚乙二醇        0.5～1；
防老剂RD        0.2～0.4；
促进剂TMTD      0.25～0.3；
促进剂DTDM      0.25～0.4；
促进剂DM        0.25～0.4；
促进剂CZ        0.25～0.4；
硫磺            0.2～0.4。
CN2009103110229A 2009-12-07 2009-12-07 高耐制动液三元乙丙橡胶配方 Active CN101812203B (zh)