CN101792908B - 一种环保除锈剂及其制造方法 - Google Patents
一种环保除锈剂及其制造方法 Download PDFInfo
- Publication number
- CN101792908B CN101792908B CN2009102153532A CN200910215353A CN101792908B CN 101792908 B CN101792908 B CN 101792908B CN 2009102153532 A CN2009102153532 A CN 2009102153532A CN 200910215353 A CN200910215353 A CN 200910215353A CN 101792908 B CN101792908 B CN 101792908B
- Authority
- CN
- China
- Prior art keywords
- acid
- parts
- environment
- rust remover
- glycerine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种环保除锈剂,其中,按照下述重量份数比配置原料,有机酸15~30份,甘油5~15份,糊精0.1~2份,钼酸钠0.5~10份,磷酸0.5~2份,水45~70份,SI-1添加剂0.05~0.1份。本发明中使用的有机酸为柠檬酸,酒石酸,苹果酸、绿原酸、草酸、苯甲酸、水杨酸、咖啡酸中的任意一种。本发明改进了传统配方,其制造工艺先进,制作方法简单快捷高效。解决了目前除锈剂具有污染环境的弊端,并且,本发明不仅具有良好除锈功能外,还具有优异的防锈功能。
Description
技术领域
本发明涉及一种除去金属锈蚀的化学制剂,特别涉及一种环保除锈剂及其制造方法。
背景技术
任何金属暴露于空气中都会与氧气迅速反应,在其表面形成一层薄薄的氧化膜,这层氧化膜实际上阻碍了其继续氧化,变成了保护膜。金属与氧会否继续反应取决于其氧化膜的性质。如果氧化膜稳定,金属内部就不再生锈(如铝)。但这层氧化膜往往容易被置换或不稳定,从而空气和水会渗透氧化层保护膜,使得氧化和腐蚀继续发生。金属持续暴露于导致锈蚀的因素中,例如大部分铁和铁合金形成一层不稳定的氧化膜,很容易脱落或被其它金属置换,氧化反应在其表面继续反应,导致金属表面凹凸不平和脱落,就是我们一般认为的锈蚀。金属锈蚀的主要原因有化学腐蚀和电化学腐蚀:化学腐蚀主要是因为金属与氧气、水等接触,金属被氧化,以及其他有腐蚀性的化学物质对金属的腐蚀,如酸雨等;电化学腐蚀是因为原电池原理的腐蚀,这比上一个原因引起的危害更大,原理是水在金属物表面形成水膜,溶解氧气,二氧化碳等物质,这时就会形成金属为负电位的原电池,会使金属被较快地腐蚀。
金属的除锈,常见的有化学除锈,电动抛丸除锈,喷砂除锈,高压水磨除锈等。以化学除锈为例,其主要是利用酸与金属氧化物发生化学反应,从而除掉金属表面的锈蚀产物的一种除锈方法,即通常所说的酸洗除锈,其只能在车间内操作使用稀盐酸除锈,但不能把有锈的金属泡在里面太久,否则除完表层锈后会把里面的物质也顺便反应掉,例如除完铁锈后,酸还会跟铁反应,造成内部铁材的浪费。因此,金属的防锈使用的化学制剂大部分都是盐酸,磺酸,硝酸或其混合液,是属于强酸类产品,使用时对人体有危险性,操作时具有很高的危险系数,并且易引起各种环境污染,特别是废弃时导致水质污染,因此为了防止各种环境污染,需支付巨资清除所产生的污染物质是不可避免的现状。
金属的防锈,就必须提供一个保护屏障以防止导致锈蚀的物质与金属接触。如果氧化层结构稳定,会为金属提供一个天然的保护屏障。如果氧化层不稳定,则须人为地提供一个保护层。例如涂抹防锈油。金属防锈的化学药品,如铬、磷等是污染环境的化学药品;胺、硝酸盐等是对人体有致癌性能的有害药品。
鉴于上述种种缺点,迫切需要出现一种除锈剂,这种除锈剂应该既可除去金属产品的锈蚀,同时还具有防锈性能,并且是环保、对人体无害的安全产品,可防止各种环境污染,维持生态系的稳定性。
发明内容
本发明所要解决的技术问题在于,提供一种环保除锈剂及其制造方法,这种除锈剂使用可降解的植物性原料,其完全溶于水,保障了生物降解性能,同时具有铁及非铁金属的防腐蚀性能以及除锈性能。在任何恶劣条件下使其均具有一定期间的防腐性能,同时在废弃时采用烧毁或填埋手段,避免了污染环境。
为了达到上述目的,本发明提供了一种环保除锈剂,其中,按照下述重量份数比配置原料:
有机酸 15~30份,
甘油 5~15份,
糊精 0.1~2份,
钼酸钠 0.5~10份,
磷酸 0.5~2份,
水 45~70份,
SI-1添加剂 0.05~0.1份。
或按照下述重量份数比配置原料:
有机酸 15~22份,
甘油 5~10份,
糊精 0.1~1份,
钼酸钠 0.5~5份,
磷酸 0.5~1份,
水 45~60份,
SI-1添加剂 0.05~0.09份。
或按照下述重量份数比配置原料:
有机酸 22~30份,
甘油 10~15份,
糊精 1~2份,
钼酸钠 5~10份,
磷酸 1~2份,
水 60~70份,
SI-1添加剂 0.06~0.1份。
或按照下述重量份数比配置原料:
有机酸 20~25份,
甘油 8~12份,
糊精 0.8~1.5份,
钼酸钠 2~7份,
磷酸 0.8~1.5份,
水 50~65份,
SI-1添加剂 0.07~0.08份。
所述有机酸为柠檬酸,酒石酸,苹果酸、绿原酸、草酸、苯甲酸、水杨酸、咖啡酸中的任意一种。
为了更好的是实现本发明目的,本发明还提供了一种环保除锈剂的制造方法,其中,所述制造方法包括如下步骤:
a、将重量份数比的有机酸15~30份,糊精0.1~2份,钼酸钠0.5~10份,磷酸0.5~2份,水45~70份,放入搅拌机内室温下匀速搅拌25-40分钟;
b、将步骤a获得的混合溶液中放入质量份数比为5~15份的甘油,室温下匀速搅拌;
c、将步骤b获得的混合溶液中加入重量份数比为0.05~0.1份的添加剂SI-1,室温下匀速搅拌后得到环保除锈剂。
所述b步骤中匀速搅拌的时间为8~15分钟,搅拌机的转速为20-35转/分钟;所述c步骤中匀速搅拌的时间为25~35分钟,搅拌机的转速为25~30转/分钟。
所述添加剂SI-1为碘化纳。
本发明具有如下优点:
1、改进传统配方,以可食用的有机酸作为原料,减少了使用强酸制造出的现有除锈剂的繁琐操作过程和易造成污染等不好的影响;甘油为可降解材料中提炼出来的,如植物甘油,其加强了金属表面的附着性能。
2、工艺先进,制作方法简单快捷高效。
3、解决了目前除锈剂具有污染环境的弊端,并且,本发明除了除锈功能外,还具有防锈功能。
具体实施方式
本发明提供了一种环保除锈剂,这种除锈剂使用可降解的植物性原料,其完全溶于水,保障了生物降解性能,同时具有铁及非铁金属的防腐蚀性能以及除锈性能。在任何恶劣条件下使其均具有一定期间的防腐性能,同时在废弃时采用烧毁或填埋手段,避免了污染环境。
实施例1.
先将重量份数比的有机酸18份,糊精0.8份,钼酸钠3份,磷酸1.1份,水60份,放入搅拌机内室温下匀速搅拌30分钟;
然后将获得的混合溶液中放入质量份数比为8份的甘油,室温下匀速搅拌10分钟,搅拌机的转速为25转/分钟;;
接着将获得的上述混合溶液中加入重量份数比为0.06份的添加剂SI-1,室温下匀速搅拌30分钟,搅拌机的转速为25转/分钟。随后得到环保除锈剂。
本发明制造过程中添加剂SI-1为制酸剂,其主要成分为碘化纳,是天津光星化学试剂有限公司的市售产品,其主要作用为:在酸性环境中,使混合溶液产品转换为具有防锈性质的环保除锈剂。
本发明中使用的有机酸为为柠檬酸,酒石酸,苹果酸、绿原酸、草酸、苯甲酸、水杨酸、咖啡酸中的任意一种。使用的甘油是从可降解材料提炼出的,如植物甘油。
本发明的配方按照重量分数配比还可以为:
有机酸 15~30份,
甘油 5~15份,
糊精 0.1~2份,
钼酸钠 0.5~10份,
磷酸 0.5~2份,
水 45~70份,
SI-1添加剂 0.05~0.1份。
或按照下述重量份数比配置原料:
有机酸 15~22份,
甘油 5~10份,
糊精 0.1~1份,
钼酸钠 0.5~5份,
磷酸 0.5~1份,
水 45~60份,
SI-1添加剂 0.05~0.09份。
或按照下述重量份数比配置原料:
有机酸 22~30份,
甘油 10~15份,
糊精 1~2份,
钼酸钠 5~10份,
磷酸 1~2份,
水 60~70份,
SI-1添加剂 0.06~0.1份。
或按照下述重量份数比配置原料:
有机酸 20~25份,
甘油 8~12份,
糊精 0.8~1.5份,
钼酸钠 2~7份,
磷酸 0.8~1.5份,
水 50~65份,
SI-1添加剂 0.07~0.08份。
实施例2
先将重量份数比的有机酸25份,糊精1.5份,钼酸钠7份,磷酸1.3份,水70份,放入搅拌机内室温下匀速搅拌30分钟;
然后将获得的混合溶液中放入质量份数比为12份的甘油,室温下匀速搅拌15分钟,搅拌机的转速为25转/分钟;;
接着将获得的上述混合溶液中加入重量份数比为0.08份的添加剂SI-1,室温下匀速搅拌30分钟,搅拌机的转速为25转/分钟。随后得到环保除锈剂。
本发明制造过程中添加剂SI-1为制酸剂,其主要成分为碘化纳,是天津光星化学试剂有限公司的市售产品,其主要作用为:在酸性环境中,使混合溶液产品转换为具有防锈性质的环保除锈剂。本发明中使用的有机酸为为柠檬酸,酒石酸,苹果酸、绿原酸、草酸、苯甲酸、水杨酸、咖啡酸中的任意一种。使用的甘油是从可降解材料提炼出的,如植物甘油。
对实施例1或实施例2所得的环保除锈剂做防锈实验
实验内容:
接触性测试:湿度90%以上,恒温箱温度为50°,实验时间为24小时.
盐雾试验(GB/T-10125-1977):5%NaCl溶液,温度35°,24小时.
准备试片:
把金属试片各切成2.5cm×2.5cm后,用氧化铝砂纸把试片表面均匀磨平,然后用异丙醇干净地擦拭后晾干。
实验过程:
用5%的盐水涂抹在试片上,过12小时后把生锈的试片用本发明的实施例1或2所得的环保除锈剂干净除锈,然后把除完锈的试片用普通膜热封合密封包装准备。
过一段时间后,检查试片的除锈效果如下表所示:
因此,从上述表格得出结论,本发明制造的除锈剂对各种金属在一定的期间内具有优异的防锈作用。
综上所述,本发明改进了传统配方,以可食用的有机酸作为原料,减少了使用强酸制造出的现有除锈剂的繁琐操作过程和易造成污染等不好的影响;甘油为可降解材料中提炼出来的,如植物甘油,其加强了金属表面的附着性能。另外,本发明制造工艺先进,制作方法简单快捷高效。解决了目前除锈剂具有污染环境的弊端,并且,本发明除了除锈功能外,还具有优异的防锈功能。
Claims (6)
1.一种环保除锈剂,其特征在于,按照下述重量份数比配置原料:
有机酸 15~30份,
甘油 5~15份,
糊精 0.1~2份,
钼酸钠 0.5~10份,
磷酸 0.5~2份,
水 45~70份,
碘化钠 0.05~0.1份;
所述有机酸为柠檬酸,酒石酸,苹果酸、绿原酸、草酸、苯甲酸、水杨酸、咖啡酸中的任意一种。
2.根据权利要求1所述环保除锈剂,其特征在于,按照下述重量份数比配置原料:
有机酸 15~22份,
甘油 5~10份,
糊精 0.1~1份,
钼酸钠 0.5~5份,
磷酸 0.5~1份,
水 45~60份,
碘化钠 0.05~0.09份;
所述有机酸为柠檬酸,酒石酸,苹果酸、绿原酸、草酸、苯甲酸、水杨酸、咖啡酸中的任意一种。
3.根据权利要求1所述环保除锈剂,其特征在于,按照下述重量份数比配置原料:
有机酸 22~30份,
甘油 10~15份,
糊精 1~2份,
钼酸钠 5~10份,
磷酸 1~2份,
水 60~70份,
碘化钠 0.06~0.1份;
所述有机酸为柠檬酸,酒石酸,苹果酸、绿原酸、草酸、苯甲酸、水杨酸、咖啡酸中的任意一种。
4.根据权利要求1所述环保除锈剂,其特征在于,按照下述重量份数比配置原料:
有机酸 20~25份,
甘油 8~12份,
糊精 0.8~1.5份,
钼酸钠 2~7份,
磷酸 0.8~1.5份,
水 50~65份,
碘化钠 0.07~0.08份;
所述有机酸为柠檬酸,酒石酸,苹果酸、绿原酸、草酸、苯甲酸、水杨酸、咖啡酸中的任意一种。
5.一种如权利要求1所述环保除锈剂的制造方法,其特征在于,所述制造方法包括如下步骤:
a、将重量份数比的有机酸15~30份,糊精0.1~2份,钼酸钠0.5~10份,磷酸0.5~2份,水45~70份,放入搅拌机内室温下匀速搅拌25-40分钟;
b、将步骤a获得的混合溶液中放入质量份数比为5~15份的甘油,室温下匀速搅拌;
c、将步骤b获得的混合溶液中加入重量份数比为0.05~0.1份的碘化钠,室温下匀速搅拌后得到环保除锈剂。
6.根据权利要求5所述环保除锈剂的制造方法,其特征在于,所述b步骤中匀速搅拌的时间为8~15分钟,搅拌机的转速为20-35转/分钟;所述c步骤中匀速搅拌的时间为25~35分钟,搅拌机的转速为25~30转/分钟。