CN101649115B - 母乳仿真婴儿奶嘴用液体硅橡胶组合物及制备奶嘴的方法 - Google Patents
母乳仿真婴儿奶嘴用液体硅橡胶组合物及制备奶嘴的方法 Download PDFInfo
- Publication number
- CN101649115B CN101649115B CN200910042100XA CN200910042100A CN101649115B CN 101649115 B CN101649115 B CN 101649115B CN 200910042100X A CN200910042100X A CN 200910042100XA CN 200910042100 A CN200910042100 A CN 200910042100A CN 101649115 B CN101649115 B CN 101649115B
- Authority
- CN
- China
- Prior art keywords
- nipple
- component
- rubber composition
- silicon rubber
- organopolysiloxane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种母乳仿真婴儿奶嘴用液体硅橡胶组合物及制备奶嘴的方法，本发明中母乳仿真婴儿奶嘴用液体硅橡胶组合物包括以下组分：组分A：(1)每个分子上至少具有两个链烯基的聚有机硅氧烷，(2)气相白炭黑，(3)铂催化剂；组分B：(1)每个分子上至少具有两个链烯基的聚有机硅氧烷，(2)气相白炭黑，(3)具有三个或更多个与硅键接的氢原子的聚有机硅氧烷，(4)炔醇类抑制剂。制备方法，包括：a、原料配置，b、制作奶嘴。本发明的目的是提供一种用于制备与母亲乳房的质感仿真度高的婴儿奶嘴，并具有良好的抗撕裂、抗拉伸和回弹性的液体硅橡胶组合物；另一种目的是提供一种用组合物制备奶嘴的方法，本发明产品软度适宜，具有母乳仿真特点。
Description
[技术领域]
本发明涉及一种母乳仿真婴儿奶嘴用液体硅橡胶组合物，本发明还涉及一种使用该液体硅橡胶组合物制备婴儿奶嘴的方法。
[背景技术]
制作婴儿奶嘴的材料，历史上采用过天然乳胶。天然乳胶是一种极具弹性且柔软的物料，弹力非常好，容易回复原状，对环境亦无害。但天然乳胶婴儿奶嘴的缺点是容易老化，使用期限较短。
随后又出现了包括采用高温热硫化硅橡胶混炼胶和加成型液体硅橡胶的硅橡胶奶嘴。硅橡胶奶嘴具有耐高温的特性，可经反复煮沸，不易老化，使用期限得到延长。
采用高温热硫化硅橡胶混炼胶制成的奶嘴也有一些问题：混炼胶的配方调整困难，容易出现黄变，影响到奶嘴的外观和透明性；制品需二次硫化，以消除残存硫化剂高温分解产生的异味。
采用加成型液体硅橡胶(LSR)注射成型的方法制作的奶嘴较好的克服了上述缺点。但是，为了同时保证奶嘴的抗撕裂、抗拉伸和回弹性等指标满足实际使用，奶嘴制品的硬度大多在(邵氏A)40～50度，与母亲乳房的质感差别较大。
[发明内容]
本发明的目的是克服现有技术的不足，提供了一种用于制备与母亲乳房的质感仿真度高的婴儿奶嘴，并具有良好的抗撕裂、抗拉伸和回弹性的液体硅橡胶组合物；
本发明的另一种目的是提供一种使用液体硅橡胶组合物制备母乳仿真婴儿奶嘴的方法，利用该方法制备处的奶嘴软度适宜，具有母乳仿真特点。
本发明是通过如下技术方案实现的。
一种母乳仿真婴儿奶嘴用液体硅橡胶组合物，按重量份包括以下组分：
组分A
(1)每个分子上至少具有两个链烯基的聚有机硅氧烷 100份
(2)气相白炭黑 5～40份
(3)铂催化剂 1～20ppm
组分B
(1)每个分子上至少具有两个链烯基的聚有机硅氧烷 100份
(2)气相白炭黑 5～40份
(3)具有三个或更多个与硅键接的氢原子的聚有机硅氧烷 1～15份
(4)炔醇类抑制剂 10～1000ppm
其中本发明液体硅橡胶组合物中，按重量份比组分A∶组分B＝1∶1；本发明产品的硬度(邵氏A)为18～29度。
如上所述的一种母乳仿真婴儿奶嘴用液体硅橡胶组合物，其中该液体硅橡胶组合物的组分A中所述的链烯基的聚有机硅氧烷的粘度在室温下为1000～200000mPa·S；组分B中所述的具有与硅键接的氢原子的聚有机硅氧烷的粘度在室温下为1～500mPa·S。
如上所述的一种母乳仿真婴儿奶嘴用液体硅橡胶组合物，其中组分A和组分B中所述的气相白炭黑的比表面积均在200～400m2/g，其中所述的气相白炭黑经过六甲基二硅氮烷、分子中所含羟基数目大于4的低分子量羟基硅油、二甲基二甲氧基硅烷、二甲基二乙氧基硅烷中的一种或两种以上处理。
如上所述的一种母乳仿真婴儿奶嘴用液体硅橡胶组合物，其中该液体硅橡胶组合物中所述的反应抑制剂为1-乙炔基-1-环己醇。
一种使用上述组合物制备奶嘴的方法，包括以下步骤：
a、原料配置：按上述比例配制组分A和组分B，按组分A∶组分B＝1∶1的重量份比例充分混合均匀，配置出液体硅胶组合物；
b、制作奶嘴：使用步骤a中的液体硅胶组合物，采用全自动液体注射成型工艺制作奶嘴；其中硫化的工程中，硫化温度130～160℃，硫化时间为20～50秒，硫化后本发明产品的硬度(邵氏A)为18～29度。
本发明的有益效果是：
本发明液体硅橡胶组合物为双组份液体胶，其抗撕裂、抗拉伸和回弹性等性能好，适合制作婴儿奶嘴；本发明中使用液体硅橡胶组合物制作奶嘴的方法简单，且利用该组合物制作的奶嘴柔软度适宜，具有母乳仿真特点，极适合婴儿早期和断奶过渡阶段使用。
[具体实施方式]
下面结合实施例对本发明作进一步详细描述：
实施例1
本发明一种用于制备母乳仿真婴儿奶嘴的液体硅橡胶组合物，按重量份包括组分A和组分B：
其中组分A按重量份由以下组分组成：
(1)100份每个分子上具有两个链烯基的聚有机硅氧烷，其中所述的聚有机硅氧烷的粘度在室温下为1万mPa.S；
(2)35份比表面积在250m2/g的气相白炭黑，其中所述的白炭黑经过六甲基二硅氮烷处理；
(3)10ppm铂催化剂。
其中组分B按重量份由以下组分组成：
(1)100份每个分子上具有两个链烯基的聚有机硅氧烷，其中所述的聚有机硅氧烷的粘度在室温下为10000mPa·S；
(2)35份比表面积在250m2/g的气相白炭黑，其中所述的白炭黑经过六甲基二硅氮烷处理；
(3)10份具有3个与硅键接的氢原子的聚有机硅氧烷，其中所述的具有与硅键接的氢原子的聚有机硅氧烷的粘度在室温下为10mPa·S；
(4)20ppm抑制剂1-乙炔基-1-环己醇
按组分A∶组分B＝1∶1的重量份比比例将组分A和组分B混合均匀即得本发明液体硅橡胶组合物。
取该组合物采用现有的全自动液体注射成型工艺制作出奶嘴，硫化温度140℃，硫化时间为45秒。即得本发明奶嘴。
实施例2
本发明一种用于制备母乳仿真婴儿奶嘴的液体硅橡胶组合物，按重量份包括组分A和组分B：
其中组分A按重量份由以下组分组成：
(1)100份每个分子上具有两个链烯基的聚有机硅氧烷，其中所述的聚有机硅氧烷的粘度在室温下为100000mPa.S；
(2)30份比表面积在300m2/g的气相白炭黑，其中所述的白炭黑经过六甲基二硅氮烷处理；
(3)15ppm铂催化剂。
其中组分B按重量份由以下组分组成：
(1)100份每个分子上具有两个链烯基的聚有机硅氧烷，其中所述的聚有机硅氧烷的粘度在室温下为10万mPa·S；
(2)30份比表面积在300m2/g的气相白炭黑，其中所述的白炭黑经过六甲基二硅氮烷处理；
(3)8份具有4个与硅键接的氢原子的聚有机硅氧烷，其中所述的具有与硅键接的氢原子的聚有机硅氧烷的粘度在室温下为100mPa·S；
(4)50ppm抑制剂1-乙炔基-1-环己醇
按组分A∶组分B＝1∶1的重量份比比例将组分A和组分B混合均匀即得本发明液体硅橡胶组合物。
取该组合物采用现有的全自动液体注射成型工艺制作出奶嘴，硫化温度150℃，硫化时间为38秒。即得本发明奶嘴。
实施例3
本发明一种用于制备母乳仿真婴儿奶嘴的液体硅橡胶组合物，按重量份包括组分A和组分B：
其中组分A按重量份由以下组分组成：
(1)100份每个分子上具有两个链烯基的聚有机硅氧烷，其中所述的聚有机硅氧烷的粘度在室温下为200000mPa.S；
(2)30份比表面积在400m2/g的气相白炭黑，其中所述的气相白炭黑经过小分子羟基硅油处理；
(3)20ppm铂催化剂。
其中组分B按重量份由以下组分组成：
(1)100份每个分子上具有两个链烯基的聚有机硅氧烷，其中所述的聚有机硅氧烷的粘度在室温下为200000mPa·S；
(2)30份比表面积在400m2/g的气相白炭黑，其中所述的气相白炭黑经过小分子羟基硅油处理；
(3)15份具有4个与硅键接的氢原子的聚有机硅氧烷，其中所述的具有与硅键接的氢原子的聚有机硅氧烷的粘度在室温下为500mPa·S；
(4)100ppm抑制剂1-乙炔基-1-环己醇
按组分A∶组分B＝1∶1的重量份比比例将组分A和组分B混合均匀即得本发明液体硅橡胶组合物。
取该组合物采用现有的全自动液体注射成型工艺制作出奶嘴，硫化温度170℃，硫化时间为20秒。即得本发明奶嘴。
将上述3个实施例中的液体硅橡胶组合物，按A、B组分以1∶1的比例混合，于130℃×5min条件下制成标准试片，分别用哑铃和直角裁刀截取。测试物理机械性能指标，拉伸强度、伸长率：按GB/T 528-1998测试；撕裂强度：按GB/T 528-1999测试；硬度：按GB/T 531-1999测试，测试结果见表1：
表1性能测试结果
| 性能测试项目 | 实施例1 | 实施例2 | 实施例3 |
| 硬度(邵氏A) | 20 | 23 | 27 |
| 拉伸强度(MPa) | 8.5 | 9.1 | 9.7 |
| 断裂伸长率(％) | 1120 | 980 | 930 |
| 撕裂强度(kN/m) | 23 | 26 | 29 |
| 透明度 | 透明 | 透明 | 高度透明 |
Claims (2)
1.一种母乳仿真婴儿奶嘴用液体硅橡胶组合物，其特征在于：
按重量份包括以下组分：
组分A
(1)每个分子上具有两个链烯基的聚有机硅氧烷 100份
(2)气相白炭黑 30份
(3)铂催化剂 20ppm
组分B
(1)每个分子上具有两个链烯基的聚有机硅氧烷 100份
(2)气相白炭黑 30份
(3)具有四个与硅键接的氢原子的聚有机硅氧烷 15份
(4)炔醇类抑制剂 100ppm
其中所述的聚有机硅氧烷的粘度在室温下为200000mPa·S；所述的气相白炭黑的比表面积为400m2/g，所述的气相白炭黑经过小分子羟基硅油处理；所述的具有与硅键接的氢原子的聚有机硅氧烷的粘度在室温下为500mPa·S；所述的炔醇类抑制剂为1-乙炔基-1-环己醇；所得液体硅橡胶组合物中，按重量份比组分A∶组分B＝1∶1；所得产品的硬度邵氏A为27度。
2.一种使用权利要求1所述组合物制备奶嘴的方法，包括以下步骤：
a、原料配置：按上述比例配制组分A和组分B，按组分A∶组分B＝1∶1的重量份比例充分混合均匀，配置出液体硅胶组合物；
b、制作奶嘴：使用步骤a中的液体硅胶组合物，采用全自动液体注射成型工艺制作奶嘴；其中硫化的工程中，硫化温度170℃，硫化时间为20秒，硫化后所得产品的硬度邵氏A为27度。