CN101613125A - 一种锐钛矿TiO2纳米线的制备方法 - Google Patents

一种锐钛矿TiO2纳米线的制备方法 Download PDF

Info

Publication number
CN101613125A
CN101613125A CN200910089093A CN200910089093A CN101613125A CN 101613125 A CN101613125 A CN 101613125A CN 200910089093 A CN200910089093 A CN 200910089093A CN 200910089093 A CN200910089093 A CN 200910089093A CN 101613125 A CN101613125 A CN 101613125A
Authority
CN
China
Prior art keywords
nano wire
anatase octahedrite
octahedrite tio
titanium valve
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910089093A
Other languages
English (en)
Other versions
CN101613125B (zh
Inventor
刘敏
王文静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Institute of Electrical Engineering of CAS
Original Assignee
Institute of Electrical Engineering of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Institute of Electrical Engineering of CAS filed Critical Institute of Electrical Engineering of CAS
Priority to CN2009100890939A priority Critical patent/CN101613125B/zh
Publication of CN101613125A publication Critical patent/CN101613125A/zh
Application granted granted Critical
Publication of CN101613125B publication Critical patent/CN101613125B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种锐钛矿TiO2纳米线的制备方法，其特征为以钛粉为原料，先将钛粉溶解在氢氟酸中；然后与氢氧化钠或者氢氧化钾溶液混合，在一定120－200℃下进行水热反应；反应结束后洗涤至PH值达到7左右；然后在烘箱中烘干。

Description

一种锐钛矿TiO2纳米线的制备方法
技术领域
本发明涉及二氧化钛纳米材料及其制备方法，特别涉及一种锐钛矿TiO2纳米线的制备方法。
背景技术
二氧化钛是一种安全无毒、化学性质稳定、低成本的半导体氧化物，在化妆品、纺织、涂料、橡胶、印刷、光催化、污水处理和太阳能电池等领域有着广泛的应用。
目前制备二氧化钛的方法主要有：磁控溅射法、化学气相沉积法、溶胶-凝胶法、水热法等。磁控溅射法、化学气相沉积法，通常需要高真空及大型设备，投入大，生产成本高。溶胶-凝胶法采用四氯化钛或者钛酸四丁酯水解来制备溶胶，由于水解较为剧烈，反应过程难以控制。。水热法设备简单，反应与外界隔绝，制备得到的二氧化钛纯净、结晶较好、形貌可控，而成为广受关注的制备二氧化钛的方法。
水热实验制备二氧化钛，往往以四氯化钛或者钛酸四丁酯作为原料，上述化学物质化学性质活泼，水解剧烈，容易产生危险。也有研究者采用二氧化钛粉末作为原料制备纳米二氧化钛。但只有较少量的报道一金属钛粉为原料制备纳米二氧化钛。
文献[Materials Letters，2008，62，1819-1822]中以钛粉为原料直接与氢氧化钠溶液混合进行水热反应，产物采用稀盐酸和去离子水清洗，再经过400℃处理，制备TiO2纳米管。我们曾经以钛粉为原料制备了诸如纳米带、纳米管球、纳米花和纳米颗粒等多种二氧化钛纳米材料[专利申请号：200810239757.0，200810239755.1，200810239754.7，200810239756.6]，但目前尚未见以钛粉为原料制备锐钛矿二氧化钛纳米线的报道。
发明内容
本发明的目的在于提供一种以金属钛粉为原料，制备锐钛矿二氧化钛纳米线的制备方法。本制备方法过程简单、可控，反应温和，充分利用反应原料，不会产生有害气体，对人体无害。
本发明的目的是通过以下技术方案实现的。
本发明方法的包括以下步骤：
(1)称量钛粉0.01～1g，溶解在分析纯的氢氟酸溶液中，所用氢氟酸体积为0.1～10ml；等钛粉溶解完毕后，加入20～80ml摩尔浓度为1～10mol/L的氢氧化钠或者氢氧化钾溶液，并搅拌5分钟，然后在120℃～200℃下水热反应1小时～10小时；
(2)反应完毕后，产物用0.01mol/L～1mol/L的硝酸或者盐酸和高纯水冲洗，直至步骤(1)所得产物的PH值达到7左右；然后置于50~100℃的烘箱中5-24小时烘干，制得TiO2纳米带。
至此本发明二氧化钛纳米材料制备完毕。
附图说明
图1：为本发明之实施例1所制得的锐钛矿TiO2纳米线的扫描电镜图；
图2：为本发明之实施例1所制得的锐钛矿TiO2纳米线的X射线衍射图谱；
图3：为本发明之实施例2所制得的锐钛矿TiO2纳米线的扫描电镜图；
图4：为本发明之实施例5所制得的锐钛矿TiO2纳米线的扫描电镜图；
具体实施方式
以下结合附图和具体实施方式对本发明作进一步说明。
实施例1
称量钛粉0.1克，溶解在1ml的氢氟酸中，之后加入40ml浓度为10mol/L的氢氧化钠溶液，搅拌五分钟后，然后在水热反应釜中180℃反应5小时；反应完毕后，产物用0.1mol/L的硝酸和高纯水冲洗多次，直至PH值达到7左右；然后在80℃的烘箱中10小时烘干。
本实施例所得到的产物为锐钛矿TiO2纳米线。
图1所示为本实施例制得的TiO2纳米线的扫描电镜图；图2所示为本实施例制得TiO2纳米线的X射线衍射图谱，表明所制得的TiO2具有良好的锐钛矿结构。
实施例2
称量钛粉0.01克，溶解在0.1ml的氢氟酸中，之后加入20ml浓度为1mol/L的氢氧化钾溶液，搅拌五分钟后，然后在水热反应釜中120℃反应10小时；反应完毕后，产物用0.5mol/L的硝酸和高纯水冲洗多次，直至PH值达到7左右；然后在100℃的烘箱中5小时烘干。
本实施例所得到的产物为锐钛矿TiO2纳米线。
实施例3
称量钛粉0.05克，溶解在0.5ml的氢氟酸中，之后加入50ml浓度为5mol/L的氢氧化钠溶液，搅拌五分钟后，然后在水热反应釜中160℃反应6小时；反应完毕后，产物用0.2mol/L的盐酸和高纯水冲洗多次，直至PH值达到7左右；然后在60℃的烘箱中20小时烘干。
本实施例所得到的产物为锐钛矿TiO2纳米线。
实施例4
称量钛粉0.5克，溶解在5ml的氢氟酸中，之后加入60ml浓度为3mol/L的氢氧化钠溶液，搅拌五分钟后，然后在水热反应釜中150℃反应3小时；反应完毕后，产物用1mol/L的硝酸和高纯水冲洗多次，直至PH值达到7左右；然后在70℃的烘箱中15小时烘干。
本实施例所得到的产物为锐钛矿TiO2纳米线。
实施例5
称量钛粉1克，溶解在10ml的氢氟酸中，之后加入80ml浓度为8mol/L的氢氧化钠溶液，搅拌五分钟后，然后在水热反应釜中200℃反应1小时；反应完毕后，产物用0.5mol/L的盐酸和高纯水冲洗多次，直至PH值达到7左右；然后在50℃的烘箱中24小时烘干。
本实施例所得到的产物为锐钛矿TiO2纳米线。

Claims (1)

1.一种锐钛矿TiO2纳米线的制备方法，其特征在于：
(1)称量钛粉0.01～1g，溶解在分析纯的氢氟酸溶液中，所用氢氟酸体积为0.1～10ml；待钛粉完全溶解后，加入20～80ml摩尔浓度为1～10mol/L的氢氧化钠或者氢氧化钾溶液，并搅拌5分钟，然后在120℃～200℃下水热反应1小时～10小时；
(2)反应完毕后，产物用0.01mol/L～1mol/L的硝酸或者盐酸和高纯水冲洗，直至步骤(1)所得产物的PH值达到7左右；然后置于50～100℃的烘箱中5-24小时烘干，制得锐钛矿TiO2纳米线。
CN2009100890939A 2009-07-28 2009-07-28 一种锐钛矿TiO2纳米线的制备方法 Expired - Fee Related CN101613125B (zh)