CN1015344B - 铸造用改性聚乙烯醇粘结剂制法及用途 - Google Patents
铸造用改性聚乙烯醇粘结剂制法及用途Info
- Publication number
- CN1015344B CN1015344B CN 89100437 CN89100437A CN1015344B CN 1015344 B CN1015344 B CN 1015344B CN 89100437 CN89100437 CN 89100437 CN 89100437 A CN89100437 A CN 89100437A CN 1015344 B CN1015344 B CN 1015344B
- Authority
- CN
- China
- Prior art keywords
- polyvinyl alcohol
- binding agent
- modified polyvinyl
- casting
- alcohol adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
本发明涉及一种铸造用改性聚乙烯醇粘结剂制法及用途,由聚乙烯醇水溶液或能和聚乙烯醇反应的醛类物质,能同上述醛类物质发生缩聚反应的氨基物质,在一定条件下混合制成。该粘结剂的特点是:成本低,用量少,制取方便,用其配制的型(芯)砂,铸造涂料及粘结膏具有优良的铸造性能。
Description
本发明属于铸造用有机化学粘结剂、制法及应用。
中国专利CN87101061A公开了一种聚乙烯醇缩甲醛铸造胶粘剂,由聚乙烯醇缩甲醛单质结构同羟基纤维单质结构混合而成,同传统的合脂粘结剂相比,该粘结剂具有无毒、无味、节省能源,提高铸件质量,减少环境污染等优点。但尚存在成本高,合成工艺复杂,在型(芯)砂中的加入量较多,抗拉强度低,适用范围小等缺点,从而影响其推广应用。
本发明的目的是提供一种保留上述胶粘剂的优点,同时独具成本低、用量少,强度高,合成温度低,生产方法简便,不仅用于造型制芯,还可用于配制铸造用涂料、粘结膏等的新型铸造用粘结剂。
本发明是这样实现的:该粘结剂具有如下组分:a、聚合度≥1700,醇解度>88%摩尔的聚乙烯醇水溶液,溶液浓度为2-25%;b、占上述溶液重量3-20%的醛类物质,如甲醛、苯甲醛、乙醛等,能和聚乙烯醇发生缩聚反应的醛类物质均可。c、占上述溶液重量1-10%的氨基物质,如尿素、甲胺、氨水、苯胺、苯甲酰胺等,能同上述醛类物发生缩聚反应的氨基物质均可。
为了提高其性能,上述聚乙烯醇最好为牌号PVA-1799,醛类最好为甲醛,甲醛占水溶液重量的5-15%,氨基物质最好为尿素。
该粘结剂的制取方法是:在≥70℃的温度下,先将聚合度为≥1700,醇解度>88%摩尔的聚乙烯醇溶解于水中,然后加入酸,使PH≤5,再加入醛类物质,搅拌均匀,在10-80℃条件下加入碱,使PH≥7。最后加入氨基物质。上述聚乙烯醇最好加入牌号PVA-1799。醛类最好用甲醛,氨基物质最好用尿素,酸用盐酸、硫酸等,碱用KOH、NaOH等。上述的酸和碱作为缩聚反应的催化剂。
该粘结剂可用于配制型(芯)砂,其组份含有:造型(芯)用砂和占砂重0.5-15%的改性聚乙烯醇粘结剂。也可用于造型(芯)涂料或粘结膏,组份具有:耐火骨料(如石英粉、石墨粉、钴黄粉等,其中一种或几种)和占总重量50-90%的改性聚乙烯醇粘结剂,在≥80℃时,可加水稀释。
本发明成功地达到了上述发明目的。
实施例1:
在80℃,将PVA-1799聚乙烯醇溶于水中,重量百分比浓度为10%,溶解后,加入盐酸,使该PH=4,加入甲醛占水溶液的10%,搅拌降温至50℃,加入KOH,使PH=8,最后加入尿素,占聚乙烯醇水溶液重量的5%。制得的粘结剂可用于造型(芯)。
实施例2:
在90℃制得PVA-1799水溶液,浓度为5%,加入盐酸,使该PH=3,加入甲醛占水溶液的10%,充分反应,再加入NaOH,使PH=7,加入尿素5%,制得的粘结剂可用于制备多种涂料。
Claims (9)
1、一种铸造用改性聚乙烯醇粘结剂,其特征是具有如下组分:
a、聚合度为≥1700、醇解度>88%摩尔的聚乙烯醇水溶液,溶液浓度为2-25%,
b、占上述溶液重量3-20%能和聚乙烯醇发生缩聚反应的醛类物质,
c、占上述溶液重量1-10%能同上述醛类物质发生缩聚反应的氨基物质。
2、根据权利要求1所述的粘结剂,其特征在于聚乙烯醇为PVA-1799。
3、根据权利要求1所述的粘结剂,其特征在于醛类物质为甲醛,甲醛占水溶液重量的5-15%。
4、根据权利要求1所述的粘结剂,其特征在于氨基物质为尿素。
5、一种根据权利要求1、2、3或4所述的粘结剂的制取方法,其特征是在≥70℃的高温下,先将聚乙烯醇溶解于水中,然后加入酸、使PH≤5,再加入能和聚乙烯醇发生缩聚反应的醛类物质,搅拌均匀,在10-80℃的温度下加入碱,使PH≥7,最后加入能同上述醛类物质发生缩聚反应的氨基物质。
6、根据权利要求5所述的粘结剂的制取方法,其特征是聚乙烯醇用PVA-1799。
7、根据权利要求5所述的粘结剂的制取方法,其特征是醛类物质为甲醛。
8、根据权利要求7所述的制取方法,其特征在于氨基物质为尿素。
9、一种根据权利要求1-4所述的粘结剂的用途,其特征是作为配制铸造用造型、造芯材料、涂料或粘结膏的粘结剂使用。