CN102337095A - 一种呋喃树脂胶粘剂的制备方法 - Google Patents
一种呋喃树脂胶粘剂的制备方法 Download PDFInfo
- Publication number
- CN102337095A CN102337095A CN2010102359862A CN201010235986A CN102337095A CN 102337095 A CN102337095 A CN 102337095A CN 2010102359862 A CN2010102359862 A CN 2010102359862A CN 201010235986 A CN201010235986 A CN 201010235986A CN 102337095 A CN102337095 A CN 102337095A
- Authority
- CN
- China
- Prior art keywords
- furan resin
- resin adhesive
- reaction kettle
- chemical reaction
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种呋喃树脂胶粘剂的制备方法,该产品属于化工领域,是在呋喃树脂中添加反应性稀释剂、酸性固化剂、填料而制得,该胶粘剂是铸造业最常用的胶粘剂之一,具有砂芯精度好、强度高、气味小、抗吸湿、溃散性好及砂可回收再用等优点。生产该胶粘剂使用的原料有:呋喃树脂(选用液态糠醛苯酚树脂)、环己酮、苯磺酰氯、陶瓷粉、石墨、石棉、玻璃纤维。
Description
所属技术领域:
本发明产品属于化工领域。其特征是涉及一种呋喃树脂胶粘剂的制备方法。
背景技术:
由糠醛或糠醇进行均聚或与其它单体进行共缩聚而得到的产物习惯上称为呋喃树脂。呋喃树脂为棕红色、琥珀色粘稠液体,微溶于水,易溶于酯、酮等有机溶剂,以呋喃树脂为主要原料生产的胶粘剂是铸造业最常用的粘结剂。其特点是砂芯精度好、强度高、气味小、抗吸湿、溃散性好及砂可回收再用等优点。呋喃树脂的品种较多,主要有:1.糠醛苯酚树脂。是糠醛与苯酚在碱性催化剂的作用下缩聚生成的,糠醛苯酚树脂的主要特点是在给定的固化速度时有较长的流动时间,用糠醛苯酚树脂制备的压塑粉特别适于压制形状比较复杂或较大的制品。模压制品的耐热性比酚醛树脂好,尺寸稳定性、电性能也较好;2.糠醛丙酮树脂。糠醛与丙酮在碱性条件下进行缩合反应形成糠酮单体再与甲醛在酸性条件下进一步缩聚,使糠酮单体分子间以次甲基键连接起来,形成糠醛丙酮树脂;3.糠醇树脂。糠醇在酸性条件缩聚得到的树脂。呋喃树脂与许多热塑性和热固性树脂有很好的混容性能,可与环氧树脂或酚醛树脂混合来加以改性。呋喃树脂制备的胶粘剂具有耐强酸、强碱和有机溶剂的侵蚀,在高温下仍很稳定,是铸造业最常用的胶粘剂之一。在制备该胶粘剂时常在呋喃树脂中添加酸类固化剂和填料,使胶粘剂的性能更好。
发明内容:
本发明产品是一种铸造业最常用的胶粘剂,该产品是在呋喃树脂中添加反应性稀释剂、酸类固化剂、填料而制得,该胶粘剂的特点是砂芯精度好、强度高、气味小、抗吸湿、溃散性好及砂可回收再用等优点。生产该胶粘剂使用的原料有:呋喃树脂(选用液态糠醛苯酚树脂)60%-70%、环己酮10%-20%、苯磺酰氯8%、陶瓷粉3%、石墨4%、石棉2%、玻璃纤维3%。
本发明可以通过以下技术方案来实现:
一种工业化生产呋喃树脂胶粘剂的方法,其特征是由以下步骤构成:
1.在化学反应釜中先加入液态糠醛苯酚树脂,把温度提高到55℃,开动搅拌机搅拌,然后加入反应型稀释剂环己酮,混合后搅拌均匀,保温反应1.5小时。
2.保持温度不变,继续搅拌,在化学反应釜中加入苯磺酰氯,反应0.5小时。
3.降温至常温,继续搅拌,在化学反应釜中依次加入陶瓷粉、石墨粉、石棉粉、玻璃纤维,反应0.5小时后得到成品。
本发明产品呋喃树脂胶粘剂是一种铸造业最常用的胶粘剂,该胶粘剂的特点是砂芯精度好、强度高、气味小、抗吸湿、溃散性好及砂可回收再用等优点。
具体实施方式:
实施例1:
在化学反应釜中先加入占总量60%的液态糠醛苯酚树脂,把温度提高到55℃,开动搅拌机搅拌,然后加入占总量20%反应型稀释剂环己酮,混合后搅拌均匀,保温反应1.5小时;保持温度不变,继续搅拌,在化学反应釜中加入占总量8%苯磺酰氯,反应0.5小时;降温至常温,继续搅拌,在化学反应釜中依次加入占总量3%陶瓷粉、4%石墨粉、2%石棉粉、3%玻璃纤维,反应0.5小时后得到成品。
实施例2:
在化学反应釜中先加入占总量65%的液态糠醛苯酚树脂,把温度提高到55℃,开动搅拌机搅拌,然后加入占总量15%反应型稀释剂环己酮,混合后搅拌均匀,保温反应1.5小时;保持温度不变,继续搅拌,在化学反应釜中加入占总量8%苯磺酰氯,反应0.5小时;降温至常温,继续搅拌,在化学反应釜中依次加入占总量3%陶瓷粉、4%石墨粉、2%石棉粉、3%玻璃纤维,反应0.5小时后得到成品。
实施例3:
在化学反应釜中先加入占总量70%的液态糠醛苯酚树脂,把温度提高到55℃,开动搅拌机搅拌,然后加入占总量10%反应型稀释剂环己酮,混合后搅拌均匀,保温反应1.5小时;保持温度不变,继续搅拌,在化学反应釜中加入占总量8%苯磺酰氯,反应0.5小时;降温至常温,继续搅拌,在化学反应釜中依次加入占总量3%陶瓷粉、4%石墨粉、2%石棉粉、3%玻璃纤维,反应0.5小时后得到成品。
Claims (4)
1.一种呋喃树脂胶粘剂的制备方法,其特征是:以呋喃树脂(选用液态糠醛苯酚树脂)60%-70%、环己酮10%-20%、苯磺酰氯8%、陶瓷粉3%、石墨4%、石棉2%、玻璃纤维3%为原料,通过以下步骤来得到成品。
2.根据权利要求1所述的一种呋喃树脂胶粘剂的制备方法,其第一步的特征是:在化学反应釜中加入液态糠醛苯酚树脂,开动搅拌机,把温度提高到55℃,然后加入反应型稀释剂环己酮,混合后搅拌均匀,保温反应1.5小时。
3.根据权利要求1所述的一种呋喃树脂胶粘剂的制备方法,其第二步的特征是:保持温度不变,继续搅拌,在化学反应釜中加入苯磺酰氯,反应0.5小时。
4.根据权利要求1所述的一种呋喃树脂胶粘剂的制备方法,其第三步的特征是:降温至常温,继续搅拌,在化学反应釜中依次加入陶瓷粉、石墨粉、石棉粉、玻璃纤维,反应0.5小时后得到成品。