CN1044245A - 铸造用改性聚乙烯醇粘结剂制法及用途 - Google Patents
铸造用改性聚乙烯醇粘结剂制法及用途 Download PDFInfo
- Publication number
- CN1044245A CN1044245A CN 89100437 CN89100437A CN1044245A CN 1044245 A CN1044245 A CN 1044245A CN 89100437 CN89100437 CN 89100437 CN 89100437 A CN89100437 A CN 89100437A CN 1044245 A CN1044245 A CN 1044245A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl alcohol
- preparation
- core
- binding agent
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种铸造用改性聚乙烯醇粘结剂制取方法及用途,其组分中主要有聚乙烯醇水溶液,醛类物质和氨基物质,可用于型(芯)砂,涂料及粘结膏的配制。用其配制的型(芯)砂具有成本低,渍散性好,湿强度高,无蠕变,无污染,发气量小,烘干温度低,时间短等特点;用其配制的造型(芯)涂料和粘结膏溶质悬浮性好,均匀,用量少。实为一种成本低廉、综合性能优良的较理想的铸造用粘结剂。
Description
本发明属于铸造用有机化学粘结剂。
目前铸造生产使用合脂油粘结剂配制型(芯)砂,其流动性好,干强度高,溃散性好,但是其湿强度较低,蠕变量大,影响铸件质量,再者成本高,烘干温度高,时间长,可散发出大量有毒气体,污染环境。
本发明的目的是针对上述缺点,提供一种综合性能优良,无蠕变,强度高,成本低,发气量少,无污染,烘干温度低,时间短,溃散性很好,制取方便的粘结剂。
本发明是这样实现的:该粘结剂具有以下组分:a、聚合度≥1700,醇解度>88%摩尔的聚乙烯醇水溶液,溶液浓度为2-25%;b、占上述溶液重量3-20%的醛类物质,如甲醛、苯甲醛、乙醛等;c、占上述溶液重量确1-10%的氨基物质,如尿素、甲胺、氨水、苯胺、苯甲酰胺等。
为提高其性能,上述聚乙烯醇最好为牌号PVA-1799;醛类最好为甲醛,甲醛占水溶液重量的5-15%;氨基物质最好为尿素。
该粘结剂的制取方法是:在≥70℃的温度下,先将聚合度为≥1700、醇解度>88%摩尔的聚乙烯醇溶解干中,然后加入酸,使PH≤5,再加入醛类物质,搅拌均匀,在10-80℃条件下加入碱,使PH≥7,最后加入氨基物质。上述聚乙烯醇最好加入牌号PVA-1799。醛类最好用甲醛,氨基物质最好用尿素,酸用盐酸、硫酸等,碱用KOH、NaOH等。上述的酸和碱作为缩聚反应的催化剂。
该粘结剂可用于配制型(芯)砂,其组分含有:造型(芯)用砂和占砂重0.5-15%的改性聚乙烯醇粘结剂。也可用于造型(芯)涂料和粘结膏,组分具有:耐火骨料(如石英粉、石墨粉、钴英粉等,其中一种或几种)和占总重量50-90%的改性聚乙烯醇粘结剂。在上述基础上,在≥80℃时,可再加水稀释。
该粘结剂与合脂油粘结剂相比,配制的型(芯)砂,流动性相当,高温强度也足够,溃散性更好,同时成本低,无蠕变,湿强度高,发气量少,烘干温度低,时间短,无烟无味无污染,制取方法简便易行,材料来源充足,用其配制的造型涂料和粘结膏,溶悬浮性好,涂刷性好,均匀,用量少。故是一种成本低,综合性优良的理想期铸造用粘结剂。
实施例1:
组分为:片号为PVA-1799聚乙烯醇水溶液,浓度为10%;甲醛占溶液重量的10%,尿醛占溶液重量的5%,可用于造型(芯)占砂重的3%,其余为型(芯)砂。
实施例2:
组分为牌号为PVA-1799聚乙烯醇水溶液,浓度为5%,甲醛占溶液重量的10%,尿素占溶液重量的5%。可用于制涂料,占总重量的70%,其余为耐火材料。
实施例3:
在80℃,1大气压下,将PVA-1799溶于水中,浓度为10%,溶解后,加入盐酸,使该PH=4,加入甲醛占水溶液的10%,搅拌30分钟,降温至50℃,加入KOH,使PH=8,最后加入尿素占水溶液重量的5%。
Claims (10)
1、一种铸造用改性聚乙烯醇粘结剂,其特征是具有如下组分:
a、聚合度为≥1700,醇解度>88%摩尔的聚乙烯醇水溶液,溶液浓度为2%-25%,
b、占上述溶液重量3-20%的醛类物质,
c、占上述溶液重量1-10%的氨基物质。
2、根据权利要求1所述的粘结剂,其特征在于聚乙烯醇为PVA-1799。
3、根据权利要求1所述的粘结剂,其特征在于醛类物质为甲醛,甲醛占水溶液重量的5-15%。
4、根据权利要求1所述的粘结剂,其特征在于氨基物质为尿素。
5、一种权利要求1、2、3或4所述的粘结剂的制取方法,其特征是在≥70℃温度下,先将聚乙烯醇溶解于水中,然后加入酸,使PH≤5,再加入醛类物质,搅拌均匀,在10-80℃温度下加入碱,使PH≥7,最后加入氨基物质。
6、根据权利要求5所述的粘结剂的制取方法,其特征是聚乙烯醇用PVA-1799。
7、根据权利要求5所述的粘结剂的制取方法,其特征是醛类为甲醛。
8、根据权利要求7所述的制取方法,其特征在于氨基物质用尿素。
9、一种权利要求1-6所述的粘结剂在造型造芯中的用途,其特征是型(芯)砂组分具有造型(芯)用砂和占砂重0.5-15%的改性聚乙烯醇粘结剂。
10、一种根据权利要求1-6所述的粘结剂在造型(芯)涂料和粘结膏中的用途,其特征是组分中具有:耐火材料和占总重量50-90%的改性聚乙烯醇粘结剂。