CN101508450B - 一种钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法 - Google Patents
一种钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法 Download PDFInfo
- Publication number
- CN101508450B CN101508450B CN2009100428831A CN200910042883A CN101508450B CN 101508450 B CN101508450 B CN 101508450B CN 2009100428831 A CN2009100428831 A CN 2009100428831A CN 200910042883 A CN200910042883 A CN 200910042883A CN 101508450 B CN101508450 B CN 101508450B
- Authority
- CN
- China
- Prior art keywords
- lithium
- calcium
- solid phase
- magnesium
- phase conversion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，以低镁锂比盐湖卤水为原料，采用卤水浓缩、石灰乳脱镁脱硫、碳酸锂分离钙、碳酸钠提锂、碳酸钙热分解、生石灰水化成乳等工艺流程来提取碳酸锂产品。主要技术要点是基于阴离子(OH -、CO 3 2-)的固相转化原理，通过Ca(OH) 2→Mg(OH) 2、Li 2CO 3→Ca(OH) 2及CaCO 3→CaO→Ca(OH) 2的固相转化，实现卤水的脱镁、除钙净化锂盐以及钙闭路循环。本发明综合利用盐湖镁、锂资源，具有脱镁效率高、锂盐净化效果好、锂镁回收率高、能耗少、成本低、钙闭路循环以及项目工程投资少等特点。整个工艺简单、清洁，对环境友好。本发明尤其适应大规模工业生产。
Description
技术领域
本发明属于有色金属冶金领域，具体涉及一种从盐湖卤水中提取锂盐的工艺方法，尤其是一种从低镁锂比盐湖卤水中提取锂盐的方法。
背景技术
锂是重要的有色金属，被誉为“21世纪的能源金属”，在能源、航空般天等许多高新技术领域广泛应用，在全球经济中占有极其重要的地位。全球锂资源可分为五种类型，即伟晶岩锂、卤水锂、海水锂、温泉锂和堆积锂矿等，目前开采利用的锂资源主要是伟晶岩锂矿和卤水锂矿。当前全球大部分锂消耗来源于卤水锂矿。
目前从盐湖卤水提锂的技术关键为镁锂分离，采用的主要方法有：
(1)沉淀法。包括碳酸盐沉淀法、铝酸盐沉淀法、硼镁和硼锂共沉淀法，其中，实现工业生产的是碳酸盐沉淀法。
(2)碳化法。碳化法的主要依据碳酸锂和二氧化碳、水反应生成溶解度较大的碳酸氢锂从而将卤水中锂与其它元素分离。
(3)煅烧浸取法。镁锂氯化物在高温下煅烧，氯化镁水解为氧化镁而不溶于水；煅烧产物中可溶氯化锂经水浸出，与镁分离。
(4)吸附法。利用对锂离子有选择性吸附的吸附剂来吸附锂离子，再将锂离子洗下来，达到锂离子与其它杂质离子分离的目的。研究较多的吸附剂有：层状复合氧化物吸附剂、锑酸盐吸附剂、无定型氢氧化物吸附剂、离子筛型氧化物吸附剂和铝盐吸附剂。
(5)有机溶剂萃取法。利用卤水中不同离子在有机溶剂和水溶液中的不同分配，优先将锂萃入有机相中，再反萃得到锂盐。目前使用有机溶剂有TBP(磷酸三丁脂)等。
尽管使用的方法众多，但存在不同程度的不足。如沉淀法中产物粒度细、过滤难、锂损失大；碳化法不易于控制、锂收率低；煅烧法除镁率低、能耗高；吸附法由于吸附剂容量低而引起生产效率低；有机溶剂萃取法由于有机物的水溶性造成对盐湖区的环境污染。因此，研究者们一直在努力研究开发效率高、能耗低、便于操作、不污染环境的盐湖卤水提锂技术。
发明内容
本发明的目的旨在提出一种短流程、低成本、少投入，降低能耗，操作方便、不污染环境的从低镁锂比盐湖卤水中提取锂的湿法冶金方法。
本发明通过下列技术方案实现的，包括以下工艺步骤；
(1)卤水浓缩：将低镁锂比盐湖卤水蒸发，浓缩；
(2)石灰乳脱镁：将浓缩后母液与石灰乳混合，进行固相转化反应，通过氢氧化钙向氢氧化镁的固相转化，卤水中镁形成氢氧化镁，通过过滤进行固液分离，将卤水中镁以氢氧化镁形态脱除；同时，固相氢氧化钙中的钙以离子形态转入溶液中；
(3)碳酸锂分离钙：将脱镁后的钙锂液与固体碳酸锂混合，进行固相转化反应，通过碳酸锂向碳酸钙的固相转化，过滤分离，将溶液中钙以碳酸钙形态分离除去，得到净化锂盐溶液；
(4)锂盐浓缩—沉淀结晶碳酸锂及碳酸钙热分解—水化：将(3)步得到的净化锂盐溶液蒸发浓缩，加入碳酸钠与锂盐反应，沉淀结晶碳酸锂；将(3)步得到的得到的碳酸钙进行热分解得到生石灰，再经水化得石灰乳，返至(2)步中脱镁。
本发明用钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，低镁锂比盐湖卤水是指经过提取钾、硼等、或经初步脱镁后的镁锂(Mg/Li)质量比不大于3.0的高盐浓度卤水；采用盐田晒蒸或加热蒸发的方式减除水分，使溶液锂含量达到7～12g/L。
本发明用钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，工艺步骤(2)步，固相转化反应在20～90℃下进行，优选50～70℃；石灰乳的加入量根据浓缩卤水母液中含镁量，以CaO/Mg(质量比)为2.5～2.8计；固液分离得到的固体物为含有少量氢氧化钙的氢氧化镁，经洗涤，固体物可用于生产镁产品的原料，洗涤液返步骤(1)回收锂；固液分离得到的溶液为钙锂溶液。
所述的步骤(3)中，溶液中钙通过与碳酸锂固体的固相转化反应形成固体碳酸钙；固相转化反应在20～90℃下进行，优选40～60℃；固体碳酸锂的加入量按溶液中含钙量计为Li2CO3/Ca(质量比)2.0～2.2；固液分离得到的固体物为含有少量碳酸锂的碳酸钙，经干燥、热解为氧化钙，再水化为石灰乳，返步骤(2)用于脱镁，同时回收锂；固液分离得到的溶液为富锂溶液。
所述的步骤(4)中将净化锂盐溶液蒸发，浓缩至锂含量达不少于20g/L；浓缩液经过滤去除沉淀物，不经降温，加入碳酸钠进行碳酸锂的沉淀结晶。
所述的步骤(5)中产生的石灰乳用于步骤(2)中脱镁；步骤(3)中分离钙所用的碳酸锂为步骤(4)中生产。
所述(2)步中石灰乳脱镁时，可直接利用浓缩卤水的热能，不进行加热；所述(3)步中碳酸锂除钙时，可直接利用脱镁后的钙锂液的热能，也不加热；所述(4)中，可直接利用溶液浓缩时的热能，不加热进行碳酸锂的沉淀结晶；工艺中，只需浓缩工序使用外供能量，固相转化过程和沉淀结晶过程可不需加热。
本发明的优点和积极效果充分体现在：
1、采用固相转化法脱镁和除钙，沉淀结晶形态好，易于过滤和洗涤，锂损失少。
本发明以沉淀法为原型、固相转化法为基础，使溶液中镁与固体氢氧化钙反应转化为固体氢氧化镁、溶液中钙与固体碳酸锂反应转化为固体碳酸钙。由于是固相转化反应，反应具有小的过饱和度，且有足够的晶种，使沉淀结晶产物晶型好、颗粒大、易于过滤和洗涤，沉淀载带的锂损失少。
采用固相转化反应进行溶液中离子的沉淀结晶，易于控制、方便操作，使工艺具有较高的生产效率。
2、采用钙元素封闭循环，降低提锂生产成本、减少对环境的污染。
采用钙元素的封闭循环的系列沉淀反应组合进行卤水中锂镁分离，利用沉淀反应过程的沉淀结晶完全、分离干净、选择性高的特点，同时利用廉价元素进行循环使用，且原材料种类少，较大程度地降低材料成本。
在沉淀碳酸钙过程中混入沉淀物中的碳酸锂，通过钙循环过程进行生产体系而得到回收，提高锂的回收率。
在整个工艺中，表观上只使用了碳酸钠一种化工材料进行盐湖卤水中镁锂分离提取碳酸锂，钙质循环使用，只需少量补充；主要副产物为氢氧化镁、氯化钠，不污染环境，且可综合利用。
3、发明中合理配置工序、充分利用过程中自产物，简化物质体系。
本发明中固相转化脱镁过程中使用的石灰乳(氢氧化钙)原料，经过脱镁转入溶液，再经碳酸锂固相转化为碳酸钙，再干燥—热解—水化而恢复，自产自用、封闭循环。
固相转化除钙过程中，反应原料碳酸锂则为工艺的最终产物，也属于自产自用。
用碳酸锂除钙而不用碳酸钠除钙，只在最后碳酸锂沉淀结晶工序中使用碳酸钠，没有在工艺的物质流中过早引入钠，简化了整个工艺的物质体系。
4、合理利用热能，能量效率高，能耗低。
固相转化和沉淀结晶过程，在较高温度下进行会产生较好的结果。本发明采用合理的工艺条件，利用浓缩过程供给溶液的能量，在固相转化和沉淀结晶过程中不再外供能量加热，合理配置设备设施，减少物质在操作和转运过程中的热损耗，以满足固相转化和沉淀结晶过程的温度要求。
蒸发浓缩过程是主要的耗能步骤，本发明中采用固体反应剂进行固相转化反应，减少了物质体系的膨胀，降低了蒸发量和能耗。
工艺中只对蒸发浓缩过程外加能量，通过合理利用热能，实现了能量的高效利用，单位能耗低。
5、沉淀反应采用固体沉淀剂，工艺过程物质体系膨胀少，使工艺具有产能大、效率高。
采用固相转化脱镁和除钙，沉淀剂分别为固体物，固—液反应具有比液—液反应小得多的体积、或大得多的反应容量；工艺过程产生膨胀少、降低了蒸发量，从而使得工艺产能大、效率高。
6、流程简洁、成本低；
本发明从盐湖卤水中提取锂盐的方法，包括卤水浓缩、脱镁、除钙、沉淀结晶等4个主要单元操作，和1个钙质反应物再生的干燥—热解—水化系列操作，工艺简洁，流程短。由于在发明中合理使用单元操作、综合利用资源，钙闭路循环、利用自产石灰乳和碳酸锂，不向体系增加其他新的杂质、不使用繁杂的除杂或分离步骤，使得提锂成本低。
附图说明
附图为本发明的工艺流程图。
具体实施方式
下面结合具体实施对本发明做进一步描述。本发明可以按发明内容的任一方式实施。这些实施例的给出决不是限制本发明。
实施例使用低镁锂比(Mg/Li)盐湖卤水，是指经过提取钾、硼等的低镁锂比盐湖卤水，或高镁锂比盐湖卤水经初步脱镁后的低镁锂比卤水，要求镁锂比(质量比)不大于3.0。
实施例1
A.取低镁锂比盐湖卤水经脱水浓缩，浓缩卤水中锂、镁含量分别为7.4g/L、20.8g/L；卤水温度94℃。
B.按液固比3∶1于反应器(脱镁器)内加水，搅拌；按CaO/Mg(质量比)2.8计取生石灰(CaO)加入脱镁反应器内水中，形成石灰乳。
C.反应器不断搅拌，缓慢将热浓缩卤水加入反应器内；加料反应时间180min。
D.趁热过滤，洗涤；洗涤液返回用于配制石灰乳；过滤溶液(脱镁液)温度62℃，主要成分(g/L)为：锂6.3，镁＜0.1，钙29.5。
E.按液固比3∶1于反应器(脱钙器)内加水，搅拌；按Li2CO3/Ca(质量比)2.0计取碳酸锂加入脱钙反应器内水中，形成碳酸锂浆液。
F.将热脱镁液缓慢加入搅拌的脱钙反应器内，加料反应时间60min；
G.趁热过滤，洗涤；洗涤液返回用于配制碳酸锂浆液；过滤溶液(脱钙液)温度43℃，成分为(g/L)：锂5.3，镁＜0.01，钙＜0.01。
H.将脱钙液浓缩至含锂21.0g/L，趁热在不低于90℃下用碳酸钠沉淀结晶法得到碳酸锂。
实施例2
A.取低镁锂比盐湖卤水经脱水浓缩，浓缩卤水中锂、镁含量分别为11.5g/L、27.6g/L；卤水温度97℃。
B.按液固比3∶1于反应器(脱镁器)内加水，搅拌；按CaO/Mg(质量比)2.5计取生石灰(CaO)加入脱镁反应器内水中，形成石灰乳。
C.反应器不断搅拌，缓慢将热浓缩卤水加入反应器内；加料反应时间120min。
D.趁热过滤，洗涤；洗涤液返回用于配制石灰乳；过滤溶液(脱镁液)温度68℃，主要成分(g/L)为：锂9.5，镁＜0.1，钙38.0。
E.按液固比2.5∶1于反应器(脱钙器)内加水，搅拌；按Li2CO3/Ca(质量比)2.2计取碳酸锂加入脱钙反应器内水中，形成碳酸锂浆液。
F.将热脱镁液缓慢加入搅拌的脱钙反应器内，加料反应时间90min；
G.趁热过滤，洗涤；洗涤液返回用于配制碳酸锂浆液；过滤溶液(脱钙液)温度52℃，成分为(g/L)：锂7.8，镁＜0.01，钙＜0.01。
H.将脱钙液浓缩至含锂24.0g/L，趁热在不低于90℃下用碳酸钠沉淀结晶法得到碳酸锂。
Claims (8)
1.钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，其特征在于，包括以下工艺步骤：
(1)卤水浓缩：将低镁锂比盐湖卤水蒸发，浓缩；
(2)石灰乳脱镁：将(1)步浓缩后母液与石灰乳混合，进行固相转化反应，通过氢氧化钙向氢氧化镁的固相转化，以氢氧化镁形态脱除母液中镁；
(3)碳酸锂分离钙：将脱镁后的钙锂液与固体碳酸锂混合，进行固相转化反应，通过碳酸锂向碳酸钙的固相转化，以碳酸钙形态分离除去溶液中钙后得到净化锂盐溶液；
(4)锂盐浓缩-沉淀结晶碳酸锂及碳酸钙热分解-水化：将(3)步得到的净化锂盐溶液蒸发浓缩；加入碳酸钠与之反应，沉淀结晶碳酸锂；将(3)步得到的碳酸钙进行热分解得到生石灰，再经水化得石灰乳，返至(2)步中脱镁；
低镁锂比盐湖卤水是指经过提取钾和硼，或是经初步脱镁后的高盐浓度卤水，镁锂Mg/Li质量比不大于3.0；
所述(2)步中，按浓缩卤水母液中含镁量计，以CaO/Mg的质量比为2.5～2.8加入石灰乳；固相转化反应在20～90℃下进行；
所述(3)步中，与脱镁后的钙锂作用的碳酸锂，按溶液中含钙量计为Li2CO3/Ca的质量比为2.0～2.2；固相转化反应在20～90℃下进行。
2.根据权利要求1所述的钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，其特征在于：所述(1)步中，蒸发减除水分采用的是盐田晒蒸或是加热蒸发；蒸发至溶液锂含量达到7～12g/L。
3.根据权利要求1所述的钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，其特征在于：所述的(2)步中固相转化反应后固液分离得到的固体物为含有少量氢氧化钙的氢氧化镁，经洗涤，固体物可用于生产镁产品的原料，洗涤液返步骤(1)回收锂。
4.根据权利要求1所述的钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，其特征在于：所述的步骤(4)中将净化锂盐溶液蒸发，浓缩至锂含量达不少于20g/L；浓缩液经过滤去除沉淀物，不经降温，加入碳酸钠进行碳酸锂的沉淀结晶。
5.根据权利要求1所述的钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，其特征在于：所述的步骤(3)中分离钙所用的碳酸锂为步骤(4)中生产。
6.根据权利要求1所述的钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，其特征在于：所述(2)步中石灰乳脱镁时，直接利用浓缩卤水的热能。
7.根据权利要求1中所述钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，其特征在于：(3)步中碳酸锂除钙时，直接利用脱镁后的钙锂液的热能。
8.根据权利要求1中所述钙循环固相转化法从低镁锂比盐湖卤水中提取锂盐的方法，其特征在于：所述(4)中，直接利用溶液浓缩时的热能，进行碳酸锂的沉淀结晶。