CN101429330A - 树脂组合物 - Google Patents
树脂组合物 Download PDFInfo
- Publication number
- CN101429330A CN101429330A CNA2008101744795A CN200810174479A CN101429330A CN 101429330 A CN101429330 A CN 101429330A CN A2008101744795 A CNA2008101744795 A CN A2008101744795A CN 200810174479 A CN200810174479 A CN 200810174479A CN 101429330 A CN101429330 A CN 101429330A
- Authority
- CN
- China
- Prior art keywords
- resin combination
- weight
- composition
- resin
- phenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明的目的是提供一种废气光盘的再利用方法。本发明的另一目的是提供一种阻燃性及耐热性优异的树脂组合物。本发明的树脂组合物是相对于100重量份的由0～99重量％的芳香族聚碳酸酯树脂(A－1成分)和1～100重量％的基板为聚碳酸酯树脂的光盘粉碎物(A－2成分)组成的树脂成分(A成分)，含有0.001～8重量份的不含磷及溴的阻燃剂(B成分)和0.01～3重量份的含氟防滴落剂(C成分)的树脂组合物。
Description
技术领域
本发明涉及一种基板为芳香族聚碳酸酯树脂的废弃光盘粉碎物的再利用。更具体地说，涉及一种包括光盘粉碎物、芳香族聚碳酸酯树脂、不含磷及氟的阻燃剂及含氟防滴落剂，并且其阻燃性及耐热性优越的树脂组合物。
背景技术
由于芳香族聚碳酸酯树脂不仅具有透明性，而且还具有优异的阻燃性、耐热性，因而，其被广泛应用于各个领域。但是，相对于近年来电子、电器机器部件等的尺寸稳定化及高刚性化，不能说芳香族聚碳酸酯树脂的阻燃性也很充分。而且，最近在很多情况下要求具有符合UL规格(美国保险业者安全试验所规格(Underwriters Laboratories Inc))—94中V—0的高阻燃性，因此，其用途受到限制。
以往，作为向芳香族聚碳酸酯树脂赋予阻燃性的方法，已知有添加溴类化合物或磷类化合物的方法。这种方法使用在阻燃化要求较高的OA机器、家电产品等上。但是，因为近年来的环境问题，对该阻燃剂的脱溴要求越来越高，使用量也越来越减少。并且，磷类化合物中也存在着注射成型时产生气体、降低树脂组合物的耐热性等问题，无法满足电子、电器部件用途等所要求的耐热性要求。为此，提出了在芳香族聚碳酸酯树脂中添加有机金属盐来谋求阻燃化的方法(专利文献1及2)。
另一方面，在近年来的资源再利用、环境保护的观点下，对回收再利用废弃产品的所谓的再循环的研究非常活跃。其中，光盘被很多使用者所使用，生产量也逐年递增。从而，无法使用的光盘、从销售店退回的光盘、或者在生产过程中产生的不良品等需要再使用的光盘增多，对其再利用方法也进行了各种各样的研究。
例如，作为再利用光盘粉碎物的技术，提出了在光盘粉碎物中配合芳香族聚碳酸酯树脂和无机填充剂的组合物(专利文献3)。该提案虽然在有关光盘粉碎物的有效利用方面具有很深的意义，但是在脱溴、脱磷方面尚且需要研究。
并且，还公开有在光盘粉碎物中配合芳香族聚碳酸酯树脂和橡胶质的热塑性接枝共聚合物的组合物(专利文献4及5)。这些组合物具有合适的流动性及良好的外观等。并且，专利文献5中公开了当再利用湿热保持率优异的成型品的粉碎物时，能够获得机械强度及再循环效率优异的再生树脂的内容。但是，这些组合物无法满足电子、电器部件用途等所要求的耐热性。
专利文献1：JP特公昭54—32456号公报
专利文献2：JP特公昭60—19335号公报
专利文献3：JP专利第3257951号公报
专利文献4：JP特开平8-311326号公报
专利文献5：JP特开平9-316316号公报
发明内容
本发明的目的在于提供一种废弃光盘的再利用方法。本发明的又一个目的于提供一种阻燃性、耐热性优越的树脂组合物。本发明的另一个目的在于提供一种再利用光盘得到的阻燃性、耐热性优越的成型品。进一步，本发明的目的在于提供该树脂组合物的制造方法。
为了解决上述技术问题，本发明人等进行了悉心研究，结果发现，相对于100重量份的包括0～99重量％的芳香族聚碳酸酯树脂(A-1成分)和1～100重量％的基板为聚碳酸酯树脂的光盘粉碎物(A-2成分)的树脂成分(A成分)，含有0.001～8重量份的不含磷及溴的阻燃剂(B成分)和0.01～3重量份的含氟防滴落剂(C成分)的树脂组合物，是能够解决上述技术问题的树脂材料，从而完成了本发明。
本发明提供一种树脂组合物，该树脂组合物是相对于100重量份的树脂成分(A成分)，含有0.001～8重量份的不含磷及溴的阻燃剂(B成分)和0.01～3重量份的含氟防滴落剂(C成分)的树脂组合物，其中，所述树脂成分(A成分)包括0～99重量％的芳香族聚碳酸酯树脂(A-1成分)和1～100重量％的基板为聚碳酸酯树脂的光盘粉碎物(A-2成分)。
并且，本发明提供由上述树脂组合物而成的成型品。
进一步，本发明还提供一种树脂组合物的制造方法，该方法是相对于100重量份的树脂成分(A成分)，混合0.001～8重量份的不含磷及溴的阻燃剂(B成分)和0.01～3重量份的含氟防滴落剂(C成分)的树脂组合物的制造方法，其中，所述树脂成分(A成分)包括0～99重量％的芳香族聚碳酸酯树脂(A-1成分)和1～100重量％的基板为聚碳酸酯树脂的光盘粉碎物(A-2成分)。
具体实施方式
(A-1成分：芳香族聚碳酸酯树脂)
在本发明中作为A-1成分使用的芳香族聚碳酸酯树脂，是将二元苯酚和碳酸酯前驱体加以反应而得到的树脂。作为反应方法的例子，可以举出界面聚合法、熔融酯交换法、碳酸酯预聚物的固相酯交换法以及环状碳酸酯化合物的开环聚合法等。
作为在此使用的二元苯酚的代表性例子，可以举出氢醌、间苯二酚、4，4’—双酚、1，1—双(4—羟基苯基)乙烷、2，2—双(4—羟基苯基)丙烷(通常称之为双酚A)、2，2—双(4—羟基—3—甲基苯基)丙烷、2，2—双(4—羟基苯基)丁烷、1，1—双(4—羟基苯基)—1—苯基乙烷、1，1—双(4—羟基苯基)环己烷、1，1—双(4—羟基苯基)—3，3，5—三甲基环己烷、2，2—双(4—羟基苯基)戊烷、4，4’—(对亚苯基二异亚丙基)二酚、4，4’—(间亚苯基二异亚丙基)二酚、1，1—双(4—羟基苯基)—4—异丙基环己烷、双(4—羟基苯基)氧化物、双(4—羟基苯基)硫化物、双(4—羟基苯基)亚砜、双(4—羟基苯基)砜、双(4—羟基苯基)酮、双(4—羟基苯基)酯、双(4—羟基—3—甲基苯基)硫化物、9，9—双(4—羟基苯基)芴以及9，9—双(4—羟基—3—甲基苯基)芴等。优选的二元苯酚为双(4—羟基苯基)链烷烃，其中，从耐冲击性方面考虑，特别优选双酚A(以下有时简称为“BPA”)，已被广泛应用。
在本发明中，除了作为通用聚碳酸酯的双酚A类聚碳酸酯以外，作为A-1成分还可以使用通过其他的二元苯酚类而制造的特殊的聚碳酸酯。
例如，作为二元苯酚成分的一部分或全部，使用4，4’—(间亚苯基二异亚丙基)二酚(以下有时简称为“BPM”)、1，1—双(4—羟基苯基)环己烷、1，1—双(4—羟基苯基)—3，3，5—三甲基环己烷(以下有时简称为“Bis—TMC”)、9，9—双(4—羟基苯基)芴以及9，9—双(4—羟基—3—甲基苯基)芴(以下有时简称为“BCF”)的聚碳酸酯(均聚物或共聚物)，适合用于对吸水引起的尺寸变化或形状稳定性要求特别严格的用途上。这些除了BPA以外的二元苯酚，优选使用构成该聚碳酸酯的二元苯酚成分总量的5摩尔％以上，特别优选为10摩尔％以上。
尤其是，当要求具有高刚性且更良好的耐水解性的情况下，特别优选构成树脂组合物的A-1成分为下述(1)～(3)的聚碳酸酯共聚物。
(1)在100摩尔％的构成该聚碳酸酯的二元苯酚成分中，BPM为20～80摩尔％(更优选为40～75摩尔％，进一步优选为45～65摩尔％)、且BCF为20～80摩尔％(更优选为25～60摩尔％，进一步优选为35～55摩尔％)的聚碳酸酯共聚物；
(2)在100摩尔％的构成该聚碳酸酯的二元苯酚成分中，BPA为10～95摩尔％(更优选为50～90摩尔％，进一步优选为60～85摩尔％)、且BCF为5～90摩尔％(更优选为10～50摩尔％，进一步优选为15～40摩尔％)的聚碳酸酯共聚物；
(3)在100摩尔％的构成该聚碳酸酯的二元苯酚成分中，BPM为20～80摩尔％(更优选为40～75摩尔％，进一步优选为45～65摩尔％)、且Bis—TMC为20～80摩尔％(更优选为25～60摩尔％，进一步优选为35～55摩尔％)的聚碳酸酯共聚物。
这些特殊的聚碳酸酯既可以单独使用，也可以两种以上适当地混合使用。另外，也可以将这些与通用的双酚A型聚碳酸酯混合使用。
关于这些特殊的聚碳酸酯的制造方法以及特性，例如在JP特开平6-172508号公报、JP特开平8-27370号公报、JP特开2001-55435号公报以及JP特开2002-117580号公报等中有详细的记载。
另外，在上述的各种聚碳酸酯中，通过调整共聚物组成等将吸水率以及Tg(玻璃化转变温度)调整在下述范围内的聚碳酸酯，其聚合物自身的耐水解性良好，且成型后的低弯曲性也特别优异，因此，特别适合用于要求具有形状稳定性的领域中。
(i)吸水率为0.05～0.15％、优选为0.06～0.13％，且Tg为120～180℃的聚碳酸酯；或者
(ii)Tg为160～250℃、优选为170～230℃，且吸水率为0.10～0.30％、优选为0.13～0.30％、更优选为0.14～0.27％的聚碳酸酯。
在此，聚碳酸酯的吸水率，是利用直径为45mm、厚度为3.0mm的圆板状试片，根据ISO62-1980，测定在23℃的水中浸渍24小时后的水分含量而得到的数值。另外，Tg(玻璃化转变温度)，是根据JIS K7121，用差示扫描量热仪(DSC)测定而求得的数值。
作为碳酸酯前躯体，使用酰卤(Carbonyl halide)、碳酸二酯或者卤代甲酸酯(ハロホルメ—ト)等，具体地说，可以举出光气(Phosgene)、二苯基碳酸酯或二元苯酚的二卤代甲酸酯等。
当通过界面聚合法，由上述二元苯酚和碳酸酯前躯体制造芳香族聚碳酸酯树脂时，根据需要也可以使用催化剂、末端停止剂、抗氧化剂等，其中抗氧化剂用于防止二元苯酚的氧化。芳香族聚碳酸酯树脂包括：将三官能度以上的多官能芳香族化合物加以共聚合的支链聚碳酸酯树脂；将芳香族或者脂肪族(包含脂环式)的二官能度羧酸加以共聚合的聚酯碳酸酯树脂；将二官能度醇(包含脂环式)加以共聚合的共聚聚碳酸酯树脂；以及将该二官能度羧酸和二官度醇加以共聚合的聚酯碳酸酯树脂。另外，也可以是将所得到的芳香族聚碳酸酯树脂的两种以上加以混合的混合物。
支链聚碳酸酯树脂，能够向本发明的树脂组合物赋予防滴落功能等。作为用于该支链聚碳酸酯树脂中的三官能度以上的多官能芳香族化合物，可以举出均苯三酚、根皮葡酚或者4，6-二甲基-2，4，6-三(4-羟基苯基)庚烯-2、2，4，6-三甲基-2，4，6-三(4-羟基苯基)庚烷、1，3，5-三(4-羟基苯基)苯、1，1，1-三(4-羟基苯基)乙烷、1，1，1-三(3，5-二甲基-4-羟基苯基)乙烷、2，6-双(2-羟基—5-甲基苄基)-4-甲基苯酚、4-{4-[1，1-双(4-羟基苯基)乙基]苯}-α，α-二甲基苄基苯酚等的三酚；四(4-羟基苯基)甲烷、双(2，4-二羟基苯基)酮、1，4-双(4，4-二羟基三苯基甲基)苯或者偏苯三酸、均苯四甲酸、二苯酮四甲酸(Benzophenone tetracarboxylic)以及它们的酸氯化物等。其中，优选1，1，1-三(4-羟基苯基)乙烷、1，1，1-三(3，5-二甲基-4-羟基苯基)乙烷，特别优选为1，1，1-三(4-羟基苯基)乙烷。
在100摩尔％的从二元苯酚衍生的结构单元和从该多官能度芳香族化合物衍生的结构单元的总量中，支链聚碳酸酯中的从多官能度芳香族化合物衍生的结构单元优选为0.01～1摩尔％，更优选为0.05～0.9摩尔％、特别优选为0.05～0.8摩尔％。
另外，特别是采用熔融酯交换法时，有时作为副反应产生支链结构单元，该支链结构单元的含量在100摩尔％的与从二元苯酚衍生的结构单元的总量中优选为0.001～1摩尔％、更优选为0.005～0.9摩尔％、特别优选为0.01～0.8摩尔％。另外，上述支链结构的含量可通过1H-NMR测定来算出。
优选脂肪族的二官能度羧酸为α，ω-二羧酸。作为脂肪族的二官能度羧酸，例如，优选可以举出皮脂酸(癸二酸)、十二烷二酸(Dodecandioic acid)、十四烷二酸、十八烷二酸、二十烷二酸等直连饱和脂肪族二羧酸；以及环己烷二羧酸等的脂环族二羧酸。作为二官能度醇，优选为脂环族二醇，例如可以举出环己烷二甲醇、环己烷二醇以及三环癸烷二甲醇等。
而且，还可以使用对聚有机硅氧烷单元加以共聚合的聚碳酸酯—聚有机硅氧烷共聚物。
作为聚碳酸酯树脂制造方法的界面聚合法、熔融酯交换法、碳酸酯预聚物固相酯交换法、以及环状聚碳酸酯化合物的开环聚合法等反应方式，是通过各种文献以及专利公报等已公知的方法。
芳香族聚碳酸酯树脂的粘均分子量(M)优选为1×104～5×104、更优选为1.4×104～3×104、进一步优选为1.4×104～2.4×104。
在粘均分子量低于1×104的芳香族聚碳酸酯树脂中，无法得到良好的机械特性。另一方面，由粘均分子量超过5×104的芳香族聚碳酸酯树脂得到的树脂组合物，其在注射成型时的流动性差，因此通用性差。
另外，芳香族聚碳酸酯树脂，也可以通过将粘均分子量在上述范围以外的芳香族聚碳酸酯树脂加以混合而得到。特别是，具有超过上述范围(5×104)的粘均分子量的芳香族聚碳酸酯树脂，可提高树脂的熵弹性(entropyelasticity)。其结果，在将强化树脂材料成型为结构部件时采用的气体辅助成型、以及发泡成型中，能发挥良好的成型加工性。此时成型加工性的改善比上述支链聚碳酸酯更优异。作为更优选的方式，也可以使用A-1成分由粘均分子量为7×104～3×105的芳香族聚碳酸酯树脂(a-1-1成分)、以及粘均分子量为1×104～3×104的芳香族聚碳酸酯树脂(a-1-2成分)组成，且其粘均分子量为1.6×104～3.5×104的芳香族聚碳酸酯树脂(a-1成分)(以下，有时也称作“含高分子量成分的芳香族聚碳酸酯树脂”)。
在上述含高分子量成分的芳香族聚碳酸酯树脂(a-1成分)中，优选a-1-1成分的分子量为7×104～2×105、更优选为8×104～2×105、进一步优选为1×105～2×105、特别优选为1×105～1.6×105。另外，a-1-2成分的分子量优选为1×104～2.5×104、更优选为1.1×104～2.4×104、进一步优选为1.2×104～2.4×104、特别优选为1.2×104～2.3×104。
含高分子量成分的芳香族聚碳酸酯树脂(a-1成分)，可通过将上述a-1-1成分和a-1-2成分以各种比例加以混合，并将其调整为满足规定的分子量范围而得到。在100重量％的a-1成分中，优选a-1-1成分为2～40重量％、更优选为3～30重量％，进一步优选为4～20重量％，特别优选为5～20重量％。
另外，作为a-1成分的制备方法，可以举出(1)分别独立地聚合a-1-1成分和a-1-2成分，并将它们加以混合的方法；(2)采用以JP特开平5—306336号公报所示方法为代表的、将根据GPC方法的分子量分布图中表示多个聚合物峰值的芳香族聚碳酸酯树脂在同一体系内进行制造的方法，并使该芳香族聚碳酸酯树脂制造成满足本发明的a-1成分的条件的方法：以及(3)将通过该制造方法((2)的制造方法)得到的芳香族聚碳酸酯树脂和另行制造的a-1-1成分及/或a-1-2成分加以混合的方法等。
本发明所说的粘均分子量(M)，可根据下述方法算出。首先，从在20℃下将0.7g芳香族聚碳酸酯溶解在100ml二氯甲烷而得到的溶液中，用奥斯特瓦尔特粘度计，通过下式求出比粘度(ηsp)：
比粘度(ηsp)＝(t-t0)/t0
[t0为二氯甲烷落下的秒数、t为试样溶液落下的秒数]；
根据所得到的比粘度(ηsp)，通过下式算出粘均分子量(M)：
ηsp/c＝[η]+0.45×[η]2c(其中，[η]是极限粘度)
[η]＝1.23×10-4M0.83
c＝0.7。
另外，本发明的树脂组合物中，芳香族聚碳酸酯树脂的粘均分子量的计算是按照下述方法进行。即，将该树脂组合物与其重量的20～30倍的二氯甲烷进行混合，从而溶解组合物中的可溶成分。通过硅藻土过滤得到该可溶成分。然后，去除所得溶液中的溶剂。对去除溶剂后的固体进行充分的干燥，得到溶解在二氯甲烷的成分的固体。从将0.7g该固体溶解在100ml二氯甲烷而得到的溶液中，与上述同样操作求出20℃下的比粘度，并从该比粘度，与上述同样操作求出粘均分子量(M)。
(A-2成分：光盘粉碎物)
在本发明中作为A-2成分使用的光盘粉碎物，是对从光盘生产到销售后的所有的渠道中发生的所谓不良品、退还品、回收品等的废弃光盘进行粉碎而得到的粉碎物。
作为光盘，可举出CD-R、CD-RW等的CD(Compact Disc)；以MO、数字影碟、DVD-ROM、DVD-Audio、DVD-R、DVD-RAM等为代表的DVD(Digital Versatile Disc)、BD(Blu-ray Disc)、HD DVD等即存光盘、记忆容量超大的全息图存储装置、近长光存储装置等大容量光盘。
在这些光盘中，优选使用CD、DVD、BD及HD DVD的粉碎物，更优选使用CD及/或DVD的粉碎物。
光盘粉碎物优选对光盘采用以下方法而得到。即，例如CD，先将其表面上的铝膜、墨水、UV镀膜等去除，之后再将该CD粉碎而制得。另外，作为该去除铝膜、墨水、UV镀膜等的方法，包括对CD表面进行切削研磨的方法、进行振动压缩的方法等的物理方法，或者使用酸、碱等的化学方法等。
对树脂基板进行粉碎的方法没有特别的限制，可以采用通常的塑料板的粉碎方法。作为其例子，可以举出使用切断型或者锤打型粉碎机的方法，但从微粉发生量少的方面考虑，优选使用切断型粉碎机。其中，还优选采用具有旋转的旋转刀刃和固定刀刃、且下部设置有圆孔过滤网(screen)的粉碎机，通过使用这种粉碎机，可以只获得微粉少、且可通过过滤网的树脂基板细片。粉碎后的树脂基板细片的形状和大小既可以是均匀的，也可以是任意的。其大小优选是能够通过直径15mm的圆孔、而且其90重量％则不能通过直径为2mm的圆孔的大小。
光盘的基板优选主要由芳香族聚碳酸酯树脂来成型。并且，当将光盘总量作为100重量％时，光盘中的芳香族聚碳酸酯树脂的量优选为90重量％以上，更优选为95重量以上，特别优选为99重量份以上。
作为用于光盘的基板上的芳香族聚碳酸酯树脂，通常是将二元苯酚和碳酸酯前驱体通过溶液法或熔融法加以反应而获得。作为在此使用的二元苯酚，可以举出氢醌、间苯二酚、4，4’—双酚、双(4—羟基苯基)甲烷、1，1-双(4—羟基苯基)乙烷、2，2—双(4—羟基苯基)丙烷(以下称之为“双酚A”)、2，2—双(3—甲基—4—羟基苯基)丙烷、2，2—双(3，5-二甲基-4—羟基苯基)丙烷、2，2-双(4-羟基苯基)丁烷、1，1—双(4—羟基苯基)—1—苯基乙烷、1，1—双(4—羟基苯基)环己烷、1，1—双(4—羟基苯基)—3，3，5—三甲基环己烷、2，2—双(4—羟基苯基)戊烷、4，4’—(间亚苯基二异亚丙基)二酚、4，4’—(对亚苯基二异亚丙基)二酚、9，9—双(4—羟基苯基)芴、1，1—双(4—羟基苯基)—4—异丙基环己烷、双(4—羟基苯基)醚、双(4—羟基苯基)硫化物以及双(4—羟基苯基)砜等。优选的二元苯酚为2，2-双(4—羟基苯基)链烷烃，特别是优选双酚A。
作为碳酸酯前驱体，使用酰卤、碳酸酯或者卤代甲酸酯(ハロホルメ—ト)等，具体地可举出光气(Phosgene)、二苯基碳酸酯、二元苯酚的二卤代甲酸酯等。
在制造芳香族聚碳酸酯树脂时，二元苯酚可以单独使用或者同时使用两种以上，根据需要也可以使用分子量调节剂、防氧化剂、催化剂等。并且，该芳香族聚碳酸酯树脂可以是对三官能度以上的多官能性芳香族化合物加以共聚合的支链聚碳酸酯树脂，也可以是两种以上芳香族聚碳酸酯树脂的混合物。用于光盘基板上的该芳香族聚碳酸酯树脂，其粘均分子量(M)为1.0×105～3.0×105，优选为1.2×105～2.0×105，更优选为1.4×105～1.6×105。
在100重量％的A成分中，光盘粉碎物(A-2成分)的含量是1～100重量％，优选为3～50重量％，更优选为5～30重量％。
(B成分：阻燃剂)
本发明中使用的阻燃剂(B成分)，是不含磷及溴的阻燃剂。B成分可带来阻燃性的提高，除此之外，还可以基于B成分的性质，带来例如防静电性、流动性、刚性以及热稳定性的提高等。
优选B成分为选自由有机金属盐以及硅化合物组成的群中的至少一种。优选B成分并用有机金属盐和硅化合物。
相对于100重量份的作为树脂成分(A成分)，本发明的树脂组合物中B成分的含量是0.001～8重量份，优选为0.01～6重量份，更优选为0.04～4重量份。
(i)有机金属盐
有机金属盐是有机酸的金属盐。有机酸是碳原子数为1～50、优选为1～40的有机酸。作为有机酸，可以举出烷基磺酸、芳香族磺酸等有机磺酸；有机硼酸、有机锡酸等。
作为金属盐，可举出碱(碱土类)金属，即碱金属或碱土类金属。作为碱金属，可以举出锂、钠、钾、铷以及铯。作为碱土类金属，可以举出铍、镁、钙、锶以及钡。更优选的是碱金属。在该碱金属中，在透明性的要求更高的情况下优选使用离子半径更大的铷以及铯，但另一方面，由于它们不是通用的而且也难以精制，因此，有时会在成本上不利。另外，锂以及钠等离子半径更小的金属则有时对阻燃性不利。可根据上述情况区别使用碱金属。最优选特性平衡优异的磺酸钾盐。也可以将该钾盐与由其他的碱金属形成的磺酸碱金属盐并用。
有机金属盐优选为有机磺酸金属盐。有机磺酸金属盐优选碱(碱土类)金属。作为有机磺酸金属盐，可举出全氟烷基磺酸金属盐、芳香族磺酸金属盐。
优选全氟烷基磺酸金属盐是碳原子数为1～18、优选为2～8的全氟烷基磺酸的金属盐。作为全氟烷基磺酸金属盐的具体例子，可以举出三氟甲烷磺酸钾、全氟丁烷磺酸钾、全氟己烷磺酸钾、全氟辛烷磺酸钾、五氟乙烷磺酸钠、全氟丁烷磺酸钠、全氟辛烷磺酸钠、三氟甲烷磺酸锂、全氟丁烷磺酸锂、全氟庚烷磺酸锂、三氟甲烷磺酸铯、全氟丁烷磺酸铯、全氟辛烷磺酸铯、全氟己烷磺酸铯、全氟丁烷磺酸铷以及全氟己烷磺酸铷等。这些既可以单独使用一种，也可以两种以上并用。在此，全氟烷基的碳原子数优选为1～18的范围、更优选为1～10的范围、进一步优选为2～8的范围。其中，特别优选为全氟丁烷磺酸钾。
由碱金属形成的全氟烷基磺酸碱(碱土类)金属盐中，通常混入很多氟化物离子(F-)。该氟化物离子的存在有可能成为降低阻燃性的原因，因此，优选尽可能减少氟化物离子的存在。该氟化物离子的含量可通过离子色谱法来测定。优选氟化物离子的含量为100ppm以下、更优选为40ppm以下、特别优选为10ppm以下。另外，从制造效率考虑时，优选0.2ppm以上。减少了上述氟化物离子含量的全氟烷基磺酸碱(碱土类)金属盐，其制造方法采用公知的制造方法，并可通过如下方法来制得。即，减少制造含氟有机金属盐时原料中含有的氟化物离子含量的方法、用反应时产生的气体或加热来去除通过反应所得到的氟化氢等的方法、以及制造含氟有机金属盐时用重结晶以及再沉淀等的精制方法来减少氟化物离子含量的方法等。特别是，由于C成分比较容易溶解于水，因此，优选通过下述工序进行制造，该工序是，采用离子交换水，特别是采用电阻值为18MΩ·cm以上，即导电率满足约为0.55μS/cm以下的水，且在比常温高的温度下进行溶解并洗涤，然后加以冷却使之重结晶的工序。
芳香族磺酸金属盐是碳原子数为7～50、优选为7～40的芳香族磺酸的金属盐。作为芳香族磺酸金属盐的具体例子，例如，可以举出二苯基硫化物—4，4’—二磺酸二钠、二苯基硫化物—4，4’—二磺酸二钾、5—磺基异酞酸钾、5—磺基异酞酸钠、聚乙烯对苯二甲酸多磺酸多钠(ポリエチレンテレフタル酸ポリスルホン酸ポリナトリウム)、1—甲氧基萘—4—磺酸钙、4—月桂基苯基醚二磺酸二钠、聚(2，6—二甲基亚苯基氧化物)多磺酸多钠(ポリ(2，6—ジメチルフエニレンオキシド)ポリスルホン酸ポリナトリウム)、聚(1，3—亚苯基氧化物)多磺酸多钠(ポリ(1，3—フエニレンオキシド)ポリスルホン酸ポリナトリウム)、聚(1，4—亚苯基氧化物)多磺酸多钠(ポリ(1，4—フエニレンオキシド)ポリスルホン酸ポリナトリウム)、聚(2，6—二苯基亚苯基氧化物)多磺酸多钾(ポリ(2，6—ジフエニルフエニレンオキシド)ポリスルホン酸ポリカリウム)、聚(2—氟代—6—丁基亚苯基氧化物)聚磺酸锂、苯磺酸酯的磺酸钾、苯磺酸钠、苯磺酸锶、苯磺酸镁、对苯二磺酸二钾、萘—2，6—二磺酸二钾、联苯—3，3’—二磺酸钙、二苯基砜—3—磺酸钠、二苯基砜—3—磺酸钾、二苯基砜—3，3’—二磺酸二钾、二苯基砜—3，4’—二磺酸二钾、α，α，α—三氟苯乙酮—4—磺酸钠、二苯甲酮—3，3’—二磺酸二钾、噻吩—2，5—二磺酸二钠、噻吩—2，5—二磺酸二钾、噻吩—2，5—二磺酸钙、苯并噻吩磺酸钠、二苯基亚砜—4—磺酸钾、萘磺酸钠的福尔马林缩合物、以及蒽磺酸钠的福尔马林缩合物等。
这些芳香族磺酸碱(碱土类)金属盐中，特别优选钾盐。在这些芳香族磺酸碱(碱土类)金属盐中，优选二苯基砜—3—磺酸钾以及二苯基砜—3，3’—二磺酸二钾，特别优选它们的混合物(前者和后者的重量比为15/85～30/70)。
作为其他有机金属盐，可以优选举出硫酸酯的碱(碱土类)金属盐以及芳香族磺酰胺的碱(碱土类)金属盐等。作为硫酸酯的碱(碱土类)金属盐，特别地可以举出一元及/或多元醇类硫酸酯的碱(碱土类)金属盐，作为该一元及/或多元醇类硫酸酯，可以举出硫酸甲酯、硫酸乙酯、硫酸月桂酯、十六烷基硫酸酯、聚羟乙烯基烷基苯基醚的硫酸酯、季戊四醇的一、二、三、四硫酸酯、月硅酸单甘油酯的硫酸酯、棕榈酸单甘油酯的硫酸酯以及硬脂酸单甘油酯的硫酸酯等。作为这些硫酸酯的碱(碱土类)金属盐，优选举出硫酸月桂酯的碱(碱土类)金属盐。
作为芳香族磺酰胺的碱(碱土类)金属盐，例如可以举出糖精、N—对甲苯磺酰基—对甲苯磺酰亚胺、N—(N’—苄基氨基羰基)磺酰亚胺以及N—(苯基羧基)磺酰亚胺的碱(碱土类)金属盐等。
相对于100重量份的A成分，有机金属盐的含量优选为0.001～1重量份、更优选为0.005～0.5重量份、进一步优选为0.01～0.3重量份，最优选为0.03～0.15重量份。
(ii)硅化合物
硅化合物是通过燃烧时的化学反应提高阻燃性的化合物。作为该硅化合物，可使用以往作为芳香族聚碳酸酯树脂的阻燃剂提出的各种化合物。
硅化合物被认为是在燃烧时，通过其自身的结合或者通过与来自树脂的成分结合形成结构(structure)，或者通过形成该结构时的还原反应，对聚碳酸酯树脂赋予阻燃效果。因此，优选含有在上述反应中活性高的基团。更具体地说，优选含有规定量的选自烷氧基以及氢基(ハイドロジエン)(即Si-H基)中的至少一种基团。优选该基团(烷氧基，Si-H基)的含量比为0.1～1.2mol/100g的范围、更优选为0.12～1mol/100g的范围、进一步优选为0.15～0.6mol/100g的范围。该含量比，可利用碱分解法，通过测定每单位重量的硅化合物产生的氢或者醇的量来求出。另外，优选烷氧基是碳原子数为1～4的烷氧基，特别优选为甲氧基。通过将Si-H量调整在0.1～1.2mol/100g范围，可使燃烧时硅的结构形成较容易。
通常，硅化合物的结构是通过任意组合下述四种硅氧烷单元而构成。即，
M单元：(CH3)3SiO1/2、H(CH3)2SiO1/2、H2(CH3)SiO1/2、(CH3)2(CH2＝CH)SiO1/2、(CH3)2(C6H5)SiO1/2、(CH3)(C6H5)(CH2＝CH)SiO1/2等的单官能度硅氧烷单元；
D单元：(CH3)2SiO、H(CH3)SiO、H2SiO、H(C6H5)SiO、(CH3)(CH2＝CH)SiO、(C6H5)2SiO等的二官能度硅氧烷单元；
T单元：(CH3)SiO3/2、(C3H7)SiO3/2、HSiO3/2、(CH2＝CH)SiO3/2、(C6H5)SiO3/2等的三官能度硅氧烷单元；
Q单元：用SiO2表示的四官能度硅氧烷单元。
用于硅类阻燃剂中的硅化合物的结构，具体地可举出用下述示意式来表示的结构，即，Dn、Tp、MmDn、MmTp、MmQq、MmDnTp、MmDnQq、MmTpQq、MmDnTpQq、DnTp、DnQq、DnTpQq。其中，优选的硅化合物结构为MmDn、MmTp、MmDnTp、MmDnQq，更优选的结构为MmDn或MmDnTp。
在此，上述示意式中的系数m、n、p、q为表示各硅氧烷单元的聚合度的1以上的整数，各示意式中系数的总和为硅化合物的平均聚合度。优选该平均聚合度在3～150的范围、更优选为3～80的范围、进一步优选为3～60的范围、特别优选为4～40的范围。该平均聚合度处于越优选的范围，其阻燃性则越优异。而且，如后述的含有规定量的芳香族基团的硅化合物，其透明性或色泽也优异。其结果，能够得到良好的反射光。
另外，当m、n、p、q中的任何一个为2以上的数值时，附有该系数的硅氧烷单元，可以是所结合的氢原子或有机残基为不同的两种以上的硅氧烷单元。
硅化合物既可以是直链结构，也可以是具有支链结构的硅化合物。另外，与硅原子结合的有机残基优选是碳原子数为1～30、更优选为1～20的有机残基。作为该有机残基，具体地可以举出甲基、乙基、丙基、丁基、己基以及癸基等的烷基；环己基等的环烷基；苯基等的芳基；甲苯基等的芳烷基等。更优选的是碳原子数为1～8的烷基、链烯基或者芳基。作为烷基，特别优选为甲基、乙基、以及丙基等的碳原子数为1～4的烷基。
而且，硅化合物优选含有芳基。另一方面，作为二氧化钛颜料的有机表面处理剂的硅烷化合物以及硅氧烷化合物，当其不含芳基时能够得到理想的效果，因此，与硅类阻燃剂在其优选的形式中能够明确地被区别开。更优选的硅类阻燃剂，是用下述通式(1)表示的芳香族基团的含量比例(芳香族基团量)为10～70重量％(更优选为15～60重量％)的硅化合物。
(式(1)中，X分别独立地表示OH基、具有或未具有含杂原子官能团的碳原子数为1～20的烃基；n表示0～5的整数。而且在式(1)中，当n为2以上时，可分别取相互不同种类的X。)
综上所述，硅化合物是分子中含有Si-H基及芳香族基的硅化合物，优选(1)Si-H基含量(Si-H量)为0.1～1.2mol/100g、(2)上述式(1)所示的芳香族基的含量(芳香族基量)为10～70重量％，且(3)平均聚合度为3～150的硅化合物。
另外，作为硅类阻燃剂，优选将用M、MH、D、DH、DΦ2、T及TΦ表示的硅氧烷单位以每分子的平均数分别具有m、mh、d、dh、dp2、t、tp，且满足下式(i)～(iv)的硅类阻燃剂。
2≤m+mh≤40 (i)
0.35≤d+dh+dp2≤148 (ii)
0≤t+tp≤38 (iii)
0.35≤mh+dh≤110 (iv)
{其中，M：(CH3)3SiO1/2、
MH：H(CH3)2SiO1/2、
D：(CH3)2SiO、
DH：H(CH3)SiO、
DΦ2：(C6H5)2SiO、
T：(CH3)SiO3/2、
TΦ：(C6H5)SiO3/2。}
当调整为上述范围时，在本发明的树脂组合物中容易同时实现良好的阻燃性、耐热性。
作为硅类阻燃剂使用的硅化合物，除了上述Si-H基以及烷氧基以外还可以含有反应基团，作为该反应基团，例如可以举出氨基、羧基、环氧基、乙烯基、巯基、以及甲基丙烯酰氧基等。
作为具有Si-H基的硅化合物，优选举出含有用下述通式(2)以及(3)表示的结构单元中的至少一种以上的硅化合物：
(在(式(2)以及式(3)中，Z1～Z3分别独立地表示氢原子、碳原子数为1～20的一价有机残基、或者用下式(4)表示的基团；α1～α3分别独立地表示0或者1；ml表示0或者1以上的整数；进一步，在式(2)中，当ml为2以上时，其重复单元可以分别取相互不同的多个重复单元。)
(在式(4)中，Z4～Z8分别独立地表示氢原子、碳原子数为1～20的一价有机残基；α4～α8分别独立地表示0或者1；m2表示0或者1以上的整数；进一步，在式(4)中，当m2为2以上时，其重复单元可以分别取相互不同的多个重复单元。)
在用于硅类阻燃剂的硅化合物中，作为具有烷氧基的硅化合物，例如可以举出选自用式(5)以及式(6)表示的化合物中的至少一种化合物：
(在式(5)中，β1表示乙烯基、碳原子数为1～6的烷基、碳原子数为3～6的环烷基、碳原子数为6～12的芳基以及芳烷基；γ1、γ2、γ3、γ4、γ5以及γ6表示碳原子数为1～6的烷基以及环烷基、和碳原子数为6～12的芳基以及芳烷基，其中至少一个基团为芳基或芳烷基；δ1、δ2、以及δ3表示碳原子数为1～4的烷氧基。)
(在式(6)中，β2以及β3表示乙烯基、碳原子数为1～6的烷基、碳原子数为3～6的环烷基、碳原子数为6～12的芳基以及芳烷基；γ7、γ8、γ9、γ10、γ11、γ12、γ13以及γ14表示碳原子数为1～6的烷基、碳原子数为3～6的环烷基、碳原子数为6～12的芳基以及芳烷基，其中至少一个基团为芳基或芳烷基；δ4、δ5、δ6、以及δ7表示碳原子数为1～4的烷氧基。)
相对于100重量份的A成分，硅类化合物的配合量优选为0.01～8重量份、更优选为0.5～6重量份、进一步优选为1～4重量份。
(C成分：含氟防滴落剂)
作为含氟防滴落剂(C成分)，可举出具有原纤维形成能力的含氟聚合物。作为该聚合物，可举出聚四氟乙烯、四氟乙烯类共聚物(例如，四氟乙烯/全氟丙烯共聚物等)、美国专利第4379910号公报中公开的由部分氟化聚合物、氟化二酚来制造的聚碳酸酯树脂等。其中，优选聚四氟乙烯(以下，有时称为“PTFE”)。
具有原纤维形成能力的PTFE具有极高的分子量，显示出通过剪切力等的外部作用使PTFE之间结合而形成纤维状的倾向。作为其分子量，通过标准比重求出的数均分子量为100万～1000万，优选200万～900万。该PTFE除了使用固体形状以外，还可以使用水性分散液形式的PTFE。另外，为了提高在树脂中的分散性，而且为了得到更优异的阻燃性及机械特性，该具有原纤维形成能力的PTFE还可以使用与其它的树脂加以混合的混合形态的PTFE混合物。
作为该具有原纤维形成能力的PTFE的市售品，例如可举出DUPONT-MITSUI FLUOROCHEMICALS COMPANY，LTD的テフロン(注册商标)6J、DAIKIN工业(株)制造的ポリフロンMPA FA500、F—201L等。作为PTFE的水性分散液的市售品，代表性的例如可举出旭アイシ—アイフロロポリマ—ズ(株)制造的フルオンAD—1、AD—936，DAIKIN工业(株)制造的フルオンD—1、D—2，DU PONT-MITSUI FLUOROCHEMICALSCOMPANY，LTD制造的テフロン(注册商标)30J等。
作为混合形态的PTFE，可使用通过下述方法得到的混合形态的PTFE：(1)将PTFE的水性分散液与有机聚合物的水性分散液或溶液加以混合并进行共沉淀而得到共凝集混合物的方法(JP特开昭60—258263号公报、JP特开昭63—154744号公报等中记载的方法)；(2)将PTFE的水性分散液与干燥的有机聚合物粒子加以混合的方法(JP特开平4—272957号公报中记载的方法)；(3)将PTFE的水性分散液与有机聚合物粒子溶液均匀混合，从该混合物同时除去各自的介质的方法(JP特开平06—220210号公报、JP特开平08—188653号公报等中记载的方法)；(4)在PTFE的水性分散液中聚合用于形成有机聚合物的单体的方法(JP特开平9—95583号公报中记载的方法)；以及(5)将PTFE的水性分散液与有机聚合物分散液均匀混合后，进一步在该混合分散液中聚合乙烯类单体，然后得到混合物的方法(JP特开平11—29679号公报等中记载的方法)。作为这些混合形态的PTFE的市售品，可举出以Mitsubishi Rayon Co.Ltd.制造的[メタブレンA3000](商品名)、[メタブレンA3700](商品名)、[メタブレンA3800](商品名)为代表的メタブレンA系列；PIC社制造的[POLY TS AD001](商品名)；以及GEスペシヤリテイ—ケミカルズ社制造的[BLENDEXB449](商品名)等。
相对于100重量份的A成分，本发明树脂组合物中的含氟防滴落剂(C成分)的含量是0.01～3重量份，优选0.1～2重量份，更优选0.2～1重量份。
(D成分：强化填充材料)
本发明的树脂组合物中，作为强化填充材料(D成分)可以配合选自由纤维状无机填充材料(D-1成分)以及板状无机填充材料(D-2成分)组成的群中的至少一种强化填充材料。作为强化填充材料，可举出硅酸盐矿物类填充材料、玻璃类填充材料、碳纤维类填充材料等。作为该硅酸盐矿物类填充材料，可以优选举出滑石、白云母、合成氟云母等的云母、蒙脱石以及硅灰石。作为玻璃类填充材料，可以举出玻璃纤维、玻璃短纤维、玻璃片以及玻璃磨碎纤维等。硅酸盐矿物类填充材料以及玻璃类填充材料，可以采用其表面被氧化钛、氧化锌、氧化铈以及氧化硅等金属氧化物涂层的填充材料。作为碳纤维类填充材料，可以举出如镀金属碳化纤维、研磨碳纤维(カ—ボンミルドフアイバ—)、气相生长碳纤维等的碳纤维，及纳米碳管等。其中，D-1成分优选为选自由玻璃纤维、玻璃短纤维、硅灰石及碳纤维组成的群中的至少一种纤维状无机填充材料。D-2成分优选为选自由玻璃片、云母及滑石组成的群中的至少一种板状无机填充材料。
优选强化填充材料(D成分)可事先被表面处理剂实施过表面处理。作为该表面处理剂，可以举出硅烷偶合剂(包括烷基烷氧基硅烷或聚有机氢硅氧烷等)、高级脂肪酸酯、酸化合物(例如，亚磷酸、磷酸、羧酸、以及羧酸酐等)、以及蜡等的各种表面处理剂。进一步地，也可以通过烯烃类树脂、苯乙烯类树脂、丙烯酸类树脂、聚酯类树脂、环氧类树脂、以及聚氨酯类树脂等的各种树脂、高级脂肪酸酯、以及蜡等的集束剂进行造粒使之成为颗粒状。
相对于100重量份的A成分，强化填充材料(D成分)的含量优选为1～100重量份、更优选为5～70重量份、进一步优选为10～50重量份。
(其他添加剂)
除了上述A～D成分以外，本发明的树脂组合物中还可以配合通常能与聚碳酸酯树脂配合的各种添加剂。
(I)磷类稳定剂
本发明的树脂组合物中，在不会促进水解的程度范围内，优选配合磷类稳定剂。该磷类稳定剂可提高制造时或成型加工时的热稳定性，且提高机械特性、色泽以及成型稳定性。作为磷类稳定剂，可以举出亚磷酸、磷酸、亚膦酸、膦酸及这些酸的酯、和叔膦等。
作为具体的亚磷酸酯(phosphite)化合物，例如可举出，亚磷酸三苯酯、三(壬基苯基)亚磷酸酯、三癸基亚磷酸酯、三辛基亚磷酸酯、三(十八烷基)亚磷酸酯、二癸基单苯基亚磷酸酯、二辛基单苯基亚磷酸酯、二异丙基单苯基亚磷酸酯、单丁基二苯基亚磷酸酯、单癸基二苯基亚磷酸酯、单辛基二苯基亚磷酸酯、2，2—亚甲基双(4，6—二叔丁基苯基)辛基亚磷酸酯、三(二乙基苯基)亚磷酸酯、三(二异丙基苯基)亚磷酸酯、三(二正丁基苯基)亚磷酸酯、三(2，4—二叔丁基苯基)亚磷酸酯、三(2，6—二叔丁基苯基)亚磷酸酯、二硬脂酰季戊四醇二亚磷酸酯、双(2，4—二叔丁基苯基)季戊四醇二亚磷酸酯、双(2，6—二叔丁基—4—甲基苯基)季戊四醇二亚磷酸酯、双(2，6—二叔丁基—4—乙基苯基)季戊四醇二亚磷酸酯、苯基双酚A季戊四醇二亚磷酸酯、双(壬基苯基)季戊四醇二亚磷酸酯、二环己基季戊四醇二亚磷酸酯等。
进一步，作为其他的亚磷酸酯化合物，可以使用与二元苯酚类反应且具有环状结构的亚磷酸酯化合物。例如，可以举出2，2’-亚甲基双(4，6-二叔丁基苯基)(2，4-二叔丁基苯基)亚磷酸酯、2，2’-亚甲基双(4，6-二叔丁基苯基)(2-叔丁基-4-甲基苯基)亚磷酸酯、2，2’-亚甲基双(4-甲基-6-叔丁基苯基)(2-叔丁基-4-甲基苯基)亚磷酸酯、2，2’-亚乙基双(4-甲基-6-叔丁基苯基)(2-叔丁基-4-甲基苯基)亚磷酸酯等。
作为磷酸酯(phosphate)化合物，可以举出磷酸三丁酯、磷酸三甲酯、磷酸三甲苯酯、磷酸三苯酯、三氯苯基磷酸酯、磷酸三乙酯、二苯基甲苯磷酸酯、二苯基单邻联苯基磷酸酯、三丁氧基乙基磷酸酯、磷酸二丁酯、磷酸二辛酯、磷酸二异丙酯等，优选磷酸三苯酯、磷酸三甲酯。
作为亚膦酸酯化合物(phosphonite)，可以举出四(2，4—二叔丁基苯基)—4，4’—联亚苯基二亚膦酸酯、四(2，4—二叔丁基苯基)—4，3’—联亚苯基二亚膦酸酯、四(2，4—二叔丁基苯基)—3，3’—联亚苯基二亚膦酸酯、四(2，6—二叔丁基苯基)—4，4’—联亚苯基二亚膦酸酯、四(2，6—二叔丁基苯基)—4，3’—联亚苯基二亚膦酸酯、四(2，6—二叔丁基苯基)—3，3’—联亚苯基二亚膦酸酯、双(2，4—二叔丁基苯基)—4—苯基—苯基亚膦酸酯、双(2，4—二叔丁基苯基)—3—苯基—苯基亚膦酸酯、双(2，6—二正丁基苯基)—3—苯基—苯基亚膦酸酯、双(2，6—二叔丁基苯基)—4—苯基—苯基亚膦酸酯、双(2，6—二叔丁基苯基)—3—苯基—苯基亚膦酸酯等。其中，优选四(二叔丁基苯基)—联亚苯基二亚膦酸酯、双(二叔丁基苯基)—苯基—苯基亚膦酸酯，更优选四(2，4—二叔丁基苯基)—联亚苯基二亚膦酸酯、双(2，4—二叔丁基苯基)—苯基—苯基亚膦酸酯。该亚膦酸酯化合物可与上述烷基具有两个以上取代芳基的亚磷酸酯化合物并用，并优选采用这种方式。
作为膦酸酯化合物(phosphonate)，可以举出苯膦酸二甲酯、苯膦酸二乙酯以及苯膦酸二丙酯等。
作为叔膦，可以举出三乙基膦、三丙基膦、三丁基膦、三辛基膦、三戊基膦、二甲基苯基膦、二丁基苯基膦、二苯基甲基膦、二苯基辛基膦、三苯基膦、三对甲苯膦、三萘基膦以及二苯基苄基膦等。特别优选的叔膦为三苯基膦。
上述磷类稳定剂既可以只使用一种，也可以两种以上混合使用。在上述磷类稳定剂中，优选配合有以磷酸三甲酯为代表的磷酸烷基酯化合物。另外，也优选将该磷酸烷基酯化合物与亚磷酸酯化合物及/或亚膦酸酯化合物并用。
(II)受阻酚类稳定剂
在本发明的树脂组合物中，还可以配合受阻酚类稳定剂。通过配合该受阻酚类稳定剂，可以发挥例如抑制成型加工时的色泽恶化或长期使用中的色泽恶化的效果。作为受阻酚类稳定剂，例如可以举出α-生育酚、丁基羟基甲苯、芥子醇、维生素E、正十八烷基—β—(4’—羟基-3’，5’-二叔丁基苯基)丙酸酯、2-叔丁基-6-(3’-叔丁基-5’-甲基2’-羟基苄基)-4-甲基苯基丙烯酸酯、2，6-二叔丁基-4-(N，N-二甲基氨基甲基)苯酚、3，5-二叔丁基-4-羟基苄基膦酸二乙基酯、2，2’-亚甲基双(4-甲基-6-叔丁基苯酚)、2，2’-亚甲基双(4-乙基-6-叔丁基苯酚)、4，4’-亚甲基双(2，6-二叔丁基苯酚)、2，2’-亚甲基双(4-甲基-6-环己基苯酚)、2，2’-亚甲基双(6-α-甲基苄基-对甲酚)、2，2’-亚乙基-双(4，6-二叔丁基苯酚)、2，2’-亚丁基-双(4-甲基-6-叔丁基苯酚)、4，4’-亚丁基-双(3-甲基-6-叔丁基苯酚)、三乙二醇-N-双-3-(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯、1，6-己二醇-双[3-(3，5-二叔丁基-4-羟基苯基)丙酸酯]、双[2-叔丁基-4-甲基-6-(3-叔丁基-5-甲基-2-羟基苄基)苯基]对苯二甲酸酯、3，9-双{2-[3-(3-叔丁基-4-羟基-5-甲基苯基)丙酰氧基]-1，1-二甲基乙基}-2，4，8，10-四氧杂螺[5，5]十一烷、4，4’-硫代双(6-叔丁基-间甲酚)、4，4’-硫代双(3-甲基-6-叔丁基苯酚)、2，2’-硫代双(4-甲基-6-叔丁基苯酚)、双(3，5-二叔丁基-4-羟基苄基)硫化物、4，4’-二硫代双(2，6-二叔丁基苯酚)、4，4’-三硫代双(2，6-二叔丁基苯酚)、2，2-硫代二乙烯基-双[3-(3，5-二叔丁基-4-羟基苯基)丙酸酯]、2，4-双(正辛基硫代)-6-(4-羟基-3’，5’-二叔丁基苯氨基)-1，3，5-三嗪、N，N’-六亚甲基双-(3，5-二叔丁基-4-羟基氢化肉桂酰胺)、N，N’-双[3-(3，5-二叔丁基-4-羟基苯基)丙酰基]肼、1，1，3-三(2-甲基-4-羟基-5-叔丁基苯基)丁烷、1，3，5-三甲基-2，4，6-三(3，5-二叔丁基-4-羟基苄基)苯、三(3，5-二叔丁基-4-羟基苯基)异氰尿酸酯、三(3，5-二叔丁基-4-羟基苄基)异氰尿酸酯、1，3，5-三(4-叔丁基-3-羟基-2，6-二甲基苄基)异氰尿酸酯、1，3，5-三2[3(3，5-二叔丁基-4-羟基苯基)丙酰氧基]乙基异氰尿酸酯、以及四[亚甲基-3-(3’，5’-二叔丁基-4-羟基苯基)丙酸酯]甲烷等。这些均很容易得到。上述受阻酚类稳定剂既可以单独使用，也可以两种以上组合使用。
相对于100重量份的芳香族聚碳酸酯树脂(A成分)，磷类稳定剂以及受阻酚类稳定剂的含量优选为0.0001～1重量份、更优选为0.001～0.5重量份、进一步优选为0.005～0.3重量份。
(III)上述以外的热稳定剂
在本发明的树脂组合物中，除了上述磷类稳定剂以及受阻酚类稳定剂以外，还可以配合其他的热稳定剂。作为该其他的热稳定剂，例如可以优选举出以3-羟基-5，7-二叔丁基-呋喃-2-酮和邻二甲苯的反应生成物为代表的内酯类稳定剂。关于该稳定剂的详细内容，在JP特开平7-233160号公报中有记载。该化合物作为Irganox HP-136(商标，CIBA SPECIALTY CHEMICALS公司制造)而市售，可利用该化合物。另外，市售的还有将该化合物与各种亚磷酸酯化合物以及受阻酚类化合物加以混合的稳定剂。例如，可以举出上述公司制造的Irganox HP-2921。相对于100重量份的A成分，优选内酯类稳定剂的含量为0.0005～0.05重量份，更优选为0.001～0.03重量份。
另外，作为其他稳定剂，可以举出季戊四醇四(3-巯基丙酸酯)、季戊四醇四(3-月桂基硫代丙酸酯)以及丙三醇-3-硬脂酰硫代丙酸酯等的含硫稳定剂。相对于100重量份的A成分，优选该含硫稳定剂的含量为0.001～0.1重量份，更优选为0.01～0.08重量份。
(IV)紫外线吸收剂
在本发明的树脂组合物中，为了赋予耐光性可以配合紫外线吸收剂。
作为紫外线吸收剂，具体地可以举出二苯甲酮类，例如可以举出2，4-二羟基二苯甲酮、2-羟基-4-甲氧基二苯甲酮、2-羟基-4-辛氧基二苯甲酮、2-羟基-4-苄氧基二苯甲酮、2-羟基-4-甲氧基-5-磺氧基二苯甲酮、2-羟基-4-甲氧基-5-磺氧基三氢化物二苯甲酮(2—ヒドロキシ—4—メトキシ—5—スルホキシトリハイドライドレイトベンゾフエノン)、2，2’-二羟基-4-甲氧基二苯甲酮、2，2’，4，4’-四羟基二苯甲酮、2，2’-二羟基-4，4’-二甲氧基二苯甲酮、2，2’-二羟基-4，4’-二甲氧基-5-磺氧酸钠二苯甲酮、双(5-苯甲酰-4-羟基-2-甲氧基苯基)甲烷、2-羟基-4-正十二烷氧基二苯甲酮以及2-羟基-4-甲氧基-2’-羧基二苯甲酮等。
作为紫外线吸收剂的苯并三唑类，具体地可以举出2-(2-羟基-5-甲基苯基)苯并三唑、2-(2-羟基-5-叔辛基苯基)苯并三唑、2-(2-羟基-3，5-二枯基苯基)苯基苯并三唑、2-(2-羟基-3-叔丁基-5-甲基苯基)-5-氯苯并三唑、2，2’-亚甲基双[4-(1，1，3，3-四甲基丁基)-6-(2H-苯并三唑-2-基)苯酚]、2-(2-羟基-3，5-二叔丁基苯基)苯并三唑、2-(2-羟基-3，5-二叔丁基苯基)-5-氯苯并三唑、2-(2-羟基-3，5-二叔戊基苯基)苯并三唑、2-(2-羟基-5-叔辛基苯基)苯并三唑、2-(2-羟基-5-叔丁基苯基)苯并三唑、2-(2-羟基-4-辛氧基苯基)苯并三唑、2，2’-亚甲基双(4-枯基-6-苯并三唑苯基)、2，2’-对亚苯基双(1，3-苯并噁嗪-4-酮)、2-[2-羟基-3-(3，4，5，6-四氢邻苯二甲酰胺甲基)-5-甲基苯基]苯并三唑、2-(2’-羟基-5-甲基丙烯酰氧乙基苯基)-2H-苯并三唑和能够与该单体共聚合的乙烯类单体的共聚物或2-(2’-羟基-5-丙烯酰氧乙基苯基)-2H-苯并三唑和能够与该单体共聚合的乙烯类单体的共聚物等的具有2-羟基苯基-2H-苯并三唑骨架的聚合物等。
作为紫外线吸收剂的羟基苯基三嗪，例如，具体地可以举出2-(4，6-二苯基-1，3，5-三嗪-2-基)-5-己基氧苯酚、2-(4，6-二苯基-1，3，5-三嗪-2-基)-5-甲基氧苯酚、2-(4，6-二苯基-1，3，5-三嗪-2-基)-5-乙基氧苯酚、2-(4，6-二苯基-1，3，5-三嗪-2-基)-5-丙基氧苯酚以及2-(4，6-二苯基-1，3，5-三嗪-2-基)-5-丁基氧苯酚等。进一步，还可以举出2-(4，6-双(2，4-二甲基苯基)-1，3，5-三嗪-2-基)-5-己基氧苯酚等上述示例化合物中的苯基成为2，4-二甲基苯基的化合物。
作为紫外线吸收剂的环状亚胺基酯，具体地例如可以举出2，2’-对亚苯基双(3，1-苯并噁嗪-4-酮)、2，2’-间亚苯基双(3，1-苯并噁嗪-4-酮)以及2，2’-p，p’-二亚苯基双(3，1-苯并噁嗪-4-酮)等。
另外，作为紫外线吸收剂的氰基丙烯酸酯类，具体地例如可以举出1，3-双-[(2’-氰基-3’，3’-二苯基丙烯酰基)氧]-2，2-双-[(2-氰基-3，3-二苯基丙烯酰基)氧]甲基丙烷以及1，3-双-[(2-氰基-3，3-二苯基丙烯酰基)氧]苯等。
进一步，上述紫外线吸收剂也可以是，通过采用可进行自由基聚合的单体化合物结构，将该紫外线吸收性单体以及/或者光稳定性单体与(甲基)丙烯酸烷基酯等的单体进行共聚合而得到的聚合型紫外线吸收剂。作为上述紫外线吸收剂单体，可优选举出(甲基)丙烯酸酯的酯取代基中含有苯并三唑骨架、二苯甲酮骨架、三嗪骨架、环状亚胺酯骨架以及氰基丙烯酸酯骨架的化合物。
上述中，在考虑紫外线吸收能力时优选采用苯并三唑类以及羟基苯基三嗪类，而在考虑耐热性以及色泽时，则优选采用环状亚胺酯类以及氰基丙烯酸酯类。上述紫外线吸收剂既可以单独使用，还可以使用两种以上的混合物。
相对于100重量份的A成分，紫外线吸收剂的含量优选为0.01～2重量份，更优选为0.03～2重量份，进一步优选为0.02～1重量份，最优选为0.05～0.5重量份。
(V)其他树脂及弹性体
在保证本发明的效果的条件下，本发明的树脂组合物中可以配合少量的其他树脂或者弹性体来代替部分A成分。在与A成分的共计100重量％中，其他树脂或弹性体的配合量优选20重量％，更优选10重量％，特别优选5重量％以下。
作为该其他树脂，可举出聚对苯二甲酸乙二醇酯、聚对苯二甲酸丁二醇酯等的聚酯树脂；聚酰胺树脂，聚酰亚胺树脂，聚醚酰亚胺树脂，聚氨酯树脂，硅树脂，聚亚苯醚树脂，聚亚苯醚硫化物树脂，聚砜树脂，聚乙烯、聚丙烯等聚烯烃树脂，聚苯乙烯树脂，丙烯腈/苯乙烯共聚物(AS树脂)、丙烯腈/丁二烯/苯乙烯共聚物(ABS树脂)，聚甲基丙烯酸酯树脂，酚醛树脂、环氧树脂等树脂。
另外，作为弹性体，例如可举出异丁烯/异戊二烯橡胶，苯乙烯/丁二烯橡胶，乙烯/丙烯橡胶，丙烯酸类弹性体、聚酯类弹性体、聚酰胺类弹性体、作为核壳型(core-shell)弹性体的MBS(甲基丙烯酸甲酯/苯乙烯/丁二烯)橡胶，MAS(甲基丙烯酸甲酯/丙烯腈/苯乙烯)橡胶等。
(VI)上述以外的其他成分
除了上述以外，为了向成型品赋予各种功能或改善特性，在本发明的树脂组合物中还可以配合少量的其自身已被公知的添加剂。这些添加剂在不损害本发明目的的范围内，可以按照通常的配合量加以配合。
作为该添加剂，可以举出滑动剂(例如PTFE粒子)、着色剂(例如碳黑、氧化钛等的颜料、染料)、光扩散剂(例如丙烯酸交联粒子、聚硅氧烷交联粒子、碳酸钙粒子)、荧光染料、荧光增白剂、光稳定剂(以受阻胺类化合物为代表)、无机类荧光体(例如以铝酸盐作为结晶母料的荧光体)、抗静电剂、结晶成核剂、无机或有机抗菌剂、光催化剂类防污剂(例如微粒子氧化钛、微粒子氧化锌)、脱模剂、流动改质剂、自由基发生剂、红外线吸收剂(热线吸收剂)以及光致变色剂等。
<关于树脂组合物的制造方法>
本发明的树脂组合物可以通过相对于100重量份的由0～99重量％的芳香族聚碳酸酯树脂(A-1成分)和1～100重量％的基板为聚碳酸酯树脂的光盘粉碎物(A-2成分)组成的树脂成分(A成分)，混合0.001～8重量份的不含磷及溴的阻燃剂(B成分)和0.01～3重量份的含氟防滴落剂(C成分)来制造。
本发明的制造方法中，为了实现含氟防滴落剂(C成分)的良好的分散，优选在混合时使用如双轴挤出机等的多轴挤出机来对各成分进行熔融混炼。
作为双轴挤出机的代表性例子，可以举出ZSK(商品名，Werner &Pfleiderer公司制造)。作为相同型号的具体例子，可以举出TEX(商品名，(株)日本制钢所制造)、TEM(商品名，东芝机械(株)制造)、KTX(商品名，(株)神户制钢所制造)等。另外，作为具体例子，还可以举出FCM(商品名，Farrel公司制造)、Ko-Kneader(商品名，Buss公司制造)以及DSM(商品名，Krauss-Maffei公司制造)等的熔融混炼机。上述中，更优选以ZSK为代表的型号。在该ZSK型号的双轴挤出机中，其螺杆为完全齿合型，螺杆由长度和间距不同的各种螺杆部分(Screw segment)以及宽度不同的各种捏合盘(kneader disc)(或与其相当的混炼用部分)组成。
在双轴挤出机中，更优选的方式为如下所述。即，螺杆形状可以采用单线螺纹、双线螺纹以及三线螺纹的螺纹式螺杆(ネジスクリユ—)，特别优选使用对熔融树脂的运送能力或剪切混炼能力的两方面适用范围都宽的双线螺纹螺杆。双轴挤出机中的螺杆长度(L)和直径(D)之比(L/D)优选为20～45，更优选为28～42。L/D值越大越容易达成均匀的分散状态，但过于大时，因热老化容易产生树脂的分解。螺杆必须具有一个以上的混炼区，优选具有1～3个，其中，所述混炼区由用于提高混炼性的捏合盘部分(或者与其相当的混炼部分)构成。
进一步，作为挤出机，优选使用具有可以对原料中的水分或由熔融混炼树脂产生的挥发性气体进行脱除的排气口的挤出机。优选设置有用于从排气口将所产生的水分或挥发气体有效地排至挤出机外部的真空泵。另外，在挤出机模具部前的区域设置有用于去除混入在挤出原料中的杂质等的过滤网，由此也可以将杂质从树脂组合物中除去。作为该过滤网，可以举出金属网、滤网更换器、烧结金属板(盘式过滤器等)等。
而且，将B成分、C成分及其他添加剂(下面例示中，仅称为“添加剂”)供给挤出机的方法没有特别的限定，但作为其代表性的例子可以举出以下方法：(i)将添加剂与聚碳酸酯树脂分别独立地供给挤出机的方法；(ii)采用超级混合机等的混合机，事先对添加剂与聚碳酸酯树脂粉末进行预混合后，再供给挤出机的方法；以及(iii)事先对添加剂与聚碳酸酯树脂进行熔融混炼，制成主颗粒(マスタ—ペレツト)的方法。
上述方法(ii)之一，为将所需要的原材料全部进行预混合后再供给挤出机的方法。其他的方法，为先制成高浓度地配合有添加剂的主剂(マスタ—
)，将该主剂单独地或与剩下的聚碳酸酯树脂进一步进行预混合后，再供给挤出机的方法。另外，该主剂可以选择粉末状以及对该粉末进行压缩造粒等的任意形状。另外，作为其他的预混合方法，例如可以举出诺塔混合器、V型混合器、亨舍尔混合器、化学动力装置以及挤出混合器等，但优选超级混合器等的高速搅拌型的混合器。进一步，其他的预混合方法，例如是将聚碳酸酯树脂和添加剂均匀分散在溶剂而配制溶液后，去除该溶剂的方法。
通过挤出机挤出的树脂，可以直接切断而进行颗粒化，或形成股线后，将该股线用造粒机加以切断而进行颗粒化。另外，当有必要减少外部的如尘埃等的影响时，优选对挤出机周围的环境气体进行洁净化。进一步，在该颗粒的制造中，可通过在光盘用聚碳酸酯树脂中已经提出的各种方法，适当地进行颗粒形状分布的狭小化、短切物(ミスカツト物)的减少、运输或输送时产生的微小粉粒的减少以及股线或颗粒内部产生的气泡(真空气泡)的减少。根据这些方法，可以进行成型的高循环化以及减少银斑(シルバ—)等的不良现象的产生比例。另外，颗粒的形状可以是圆柱形、角柱形、球形等的通常的形状，更优选为圆柱形。优选该圆柱的直径为1～5mm，更优选为1.5～4mm，进一步优选为2～3.3mm。另一方面，圆柱的长度优选为1～30mm，更优选为2～5mm，进一步优选为2.5～3.5mm。
<关于成型品>
本发明的树脂组合物，通常可通过对如上所述制造的颗粒进行注射成型而制造出各种产品。而且，也可以不经过造粒，将用挤出机加以熔融混炼的树脂直接制造成片状、薄膜状、异型挤出成型品、吹塑(direct blow)成型品以及注射成型品。
在上述注射成型中，不仅可以采用通常的成型方法，还可以根据目的，适当采用注射压缩成型、注射压力成型、气体辅助注射成型、发泡成型(包括通过超临界流体注入的成型)、插入成型、模内涂层(In-Mold Coating)成型、隔热模具成型、急速加热冷却模具成型、双色成型、夹层成型、以及超高速注射成型等的注射成型法，从而得到成型品。这些各种成形方法的优点都已经公知。另外，成型可以选择冷流道方式以及热流道方式中的任何一种。
另外，本发明的树脂组合物，也可通过挤出成型成为各种异形挤出成型品、片状、以及薄膜状等形式而加以利用。另外，在片状、薄膜状成型中，还可以使用吹塑法、压延法、铸塑法等。而且，通过实施特定的延伸操作，也可以成型为热收缩管。另外，也可以通过旋转成型或吹塑成型等，将本发明的树脂组合物制造成成型品。
如此地，可提供具有优异的阻燃型、耐热性及刚性的树脂组合物的成型品。即，根据本发明，可以得到对树脂组合物加以熔融成型而成的成型品，该树脂组合物，是相对于100重量份的由0～99重量％的芳香族聚碳酸酯树脂(A-1成分)和1～100重量％的基板为聚碳酸酯树脂的光盘粉碎物(A-2成分)组成的树脂成分(A成分)，含有0.001～8重量份的不含磷及溴的阻燃剂(B成分)和0.01～3重量份的含氟防滴落剂(C成分)而成的树脂组合物。
而且，对由本发明的树脂组合物形成的成型品，可以进行各种表面处理。在此所说的表面处理，是指蒸镀(物理蒸镀、化学蒸镀等)、镀敷(电镀、非电解电镀、熔融电镀等)、涂装、涂层、印刷等的在树脂成型品的表层形成新的涂层的处理，可以使用通常用于聚碳酸酯树脂的方法。作为表面处理，具体地可以举出硬涂层、疏水/疏油涂层、紫外线吸收涂层、红外线吸收涂层、金属涂层(蒸镀)等的各种表面处理。
实施例
下面，通过实施例详细说明本发明。另外，评价是按照下述方法进行。
(1)阻燃性
利用厚度为1.6mm及2mm的试片，实施UL规格94的垂直燃烧试验，评价其等级。
(2)耐热性
耐热性是通过负载挠曲温度来进行评价。负载挠曲温度是利用以注射成型法制作的试片，在1.80MPa的测定条件下，基于ISO 75-1及75-2来测定。
(3)夏比冲击强度
按照ISO 179进行缺口夏比冲击强度的测定。
(4)刚性
按照ISO 178测定弯曲弹性率(试片尺寸：长度80mm×宽度10mm×厚度4mm)。
实施例1～29及比较例1～16
在通过界面缩聚法由双酚A和光气制造的聚碳酸酯树脂粉末中，按表1～5中记载的各配合量配合各种添加剂，用混合机加以混合后，用排气式双轴挤出机(TEX30α(完全齿合，同方向旋转，双线螺纹螺杆)，日本制钢所株式会社制造)进行熔融混炼，从而得到颗粒。添加剂分别以配合量的10倍的浓度，预先用亨舍尔混合机制作与聚碳酸酯树脂粉末的预混合物后，用混合机进行全体混合。挤出条件为，挤出量：20kg/h；螺杆旋转数：150rpm；排气部真空度：3KPa；挤出温度：从第一供给口到挤压模为270℃。
在120℃条件下，利用热风循环式干燥机将获得的上述颗粒干燥6小时后，利用注射成型机，在料筒(cylinder)温度290℃、模具温度80℃及注射速度50mm/sec条件下，同时成型负载挠曲温度测定用试片及弯曲弹性率测定用试片。使用了注射成型机(SG-150U，住友重机械工业(株)制造)。
另外，表1～5中的符号表示的各成分的内容为如下所示。
(A-1成份)
PC-1：通过界面缩聚法，由双酚A、作为末端停止剂的对叔丁基苯酚、以及光气合成的直链芳香族聚碳酸酯树脂粉末(パンライトL-1225WP(商品名)，粘均分子量为22400，帝人化成株式会社制造)
PC-2：通过界面缩聚法，由双酚A、作为末端停止剂的对叔丁基苯酚、以及光气合成的直链芳香族聚碳酸酯树脂粉末(L-1225WX(商品名)，粘均分子量为20900，帝人化成株式会社制造)
PC-3：通过熔融酯交换反应，由双酚A与二苯基碳酸酯合成的支链键成分在重复单元总量中约占0.1摩尔％的聚碳酸酯树脂颗粒(粘均分子量为22500，该支链键成分的比例是通过1H—NMR的测定算出，用同样方式测定的PC-1聚碳酸酯树脂中为0摩尔％(没有相应的峰))
PC-4：通过界面缩聚法，由双酚A、作为末端停止剂的对叔丁基苯酚、以及光气合成的直链芳香族聚碳酸酯树脂粉末(CM-1000(商品名)，粘均分子量为16000，帝人化成株式会社制造)
(A-2成分)
PC-5：利用粉碎机将直径为120mm、并去除了铝膜等的CD粉碎成平均粒径为6mm的粉碎物的光盘粉碎物(基板是利用由粘均分子量为15000的双酚A获得的芳香族聚碳酸酯树脂形成，在CD总量中，其占99.6重量％)。
PC-5：利用粉碎机将直径为120mm、并去除了金属膜等的DVD粉碎成平均粒径为6mm的粉碎物的光盘粉碎物(基板是利用由粘均分子量为15000的双酚A获得的芳香族聚碳酸酯树脂形成，在DVD总量中，其占92重量％)。
(B成分)
B-1：全氟丁烷磺酸钾金属盐(メガフアツクF—114P(商品名)，大日本油墨化学株式会社制造)
B-2：含有Si—H基以及苯基的直链状硅化合物
(B-2的制造)
往带有搅拌器、冷却装置、温度计的1L烧瓶中加入301.9g水以及150g甲苯，并将内温冷却至5℃。在滴液漏斗中投入21.7g三甲基氯硅烷、23.0g甲基二氯硅烷、12.9g二甲基二氯硅烷以及76.0g二苯基二氯硅烷的混合物，并在搅拌的同时用2小时向烧瓶内滴下。在这期间，持续进行冷却，以使内温维持在20℃以下。滴下结束后，继续在内温20℃下搅拌4小时进行熟化，然后，静置除去分离的盐酸水层，添加10％碳酸钠水溶液搅拌5分钟后，静置除去分离的水层。然后，进一步用离子交换水清洗3次，确认甲苯层变为中性。将该甲苯溶液在减压下加热至内温120℃，从而除去甲苯与低沸点物后，通过过滤除去不溶物，得到硅化合物B-2。该硅化合物B-1中，Si—H量为0.21mol/100g、芳香族基量为49重量％、平均聚合度为8.0。
(B成分比较用)
B-3：以双酚A双(磷酸二苯酯)为主成分的磷酸酯(CR-741(商品名)，大八化学工业(株)制造)
B-4：四溴双酚A的碳酸酯低聚体(フアイヤガ—ドFG-7000，帝人化成(株)制造)
(C成分)
C-1：ポリフロンMPA FA500(商品名)(聚四氟乙烯，DAIKININDUSTRIES，1td.制造)
C-2：POLY TS AD001(商品名)(PIC社制造，该聚四氟乙烯类混合物为由聚四氟乙烯粒子与苯乙烯—丙烯腈共聚物粒子构成的混合物(聚四氟乙烯含量为50重量％))
(D成分)
D-1：ECS—03T—511(商品名)(玻璃纤维，直径13μm、切断长度3mm，日本电气硝子(株)制造)
D-2：PEF—301S(商品名)(玻璃磨碎纤维，直径9μm、数均纤维长度30μm，日东纺(株)制造)
D-3：Upn HS-T0.8(商品名)(林化成工业(株)制造的滑石，板状，平均粒子径为2μm)
(其他)
SL：リケマ—ルSL900(商品名)(饱和脂肪酸酯类脱模剂，RIKENVITAMIN CO.，LTD制造)
TMP：TMP(商品名)(磷类稳定剂，大八化学工业(株)制造)
从上述表1至5明确可知，本发明树脂组合物的阻燃性、耐热性优异。
发明效果
根据本发明，可再利用废弃的光盘。由于本发明的树脂组合物未含有溴类化合物，因此对环境的影响少。另外，由于本发明的树脂组合物未含有磷类化合物，因此，在不降低耐热性的情况下，实现优异的阻燃性。
根据本发明的制造方法，能够再利用光盘，能够制造出阻燃性、耐热性优异的树脂组合物。另外，本发明成型品的阻燃性、耐热性优异。
工业实用性
本发明的树脂组合物，由于其具有优异的阻燃性、耐热性，因此可适用于各种电子/电器、OA机器、车辆部件、机械部件、其它的农业材料、运输容器、游戏机以及杂货等的各种用途中。
Claims (12)
1.一种树脂组合物，其特征在于，所述树脂组合物包括树脂成分、不含磷及溴的阻燃剂和含氟防滴落剂，其中，所述树脂成分含有0～99重量％的芳香族聚碳酸酯树脂以及1～100重量％的基板为聚碳酸酯树脂的光盘粉碎物，且相对于100重量份的所述树脂成分，所述不含磷及溴的阻燃剂为0.001～8重量份、所述含氟防滴落剂为0.01～3重量份。
2.如权利要求1所述的树脂组合物，其特征在于，所述不含磷及溴的阻燃剂为选自由有机金属盐及硅化合物组成的群中选择的至少一种阻燃剂。
3.如权利要求2所述的树脂组合物，其特征在于，所述有机金属盐是有机磺酸金属盐。
4.如权利要求3所述的树脂组合物，其特征在于，所述有机磺酸金属盐是全氟烷基磺酸金属盐。
5.如权利要求2所述的树脂组合物，其特征在于，所述硅化合物为分子中含有Si-H基及芳香族基的硅化合物，该硅化合物的Si-H基含量为0.1～1.2mol/100g、以下式(1)表示的芳香族基含量为10～70重量％、且平均聚合度为3～150；
式(1)中，X分别独立地表示OH基、具有或未具有含杂原子官能团的碳原子数为1～20的烃基，n表示0～5的整数，而且，在式(1)中，若n为2以上时，可以分别取相互不同种类的X。
6.如权利要求5所述的树脂组合物，其特征在于，所述硅化合物将用M、MH、D、DH、DΦ2、T及TΦ表示的硅氧烷单元，以每分子的平均数分别具有m、mh、d、dh、dp2、t、tp，且满足下式(i)～(iv)，
2≤m+mh≤40 (i)
35≤d+dh+dp2≤148 (ii)
0≤t+tp≤38 (iii)
35≤mh+dh≤110 (iv)
其中，M表示：(CH3)3SiO1/2、
MH表示：H(CH3)2SiO1/2、
D表示：(CH3)2SiO、
DH表示：H(CH3)SiO、
DΦ2表示：(C6H5)2SiO、
T表示：(CH3)SiO3/2、
TΦ表示：(C6H5)SiO3/2。
7.如权利要求1～6中任意一项所述的树脂组合物，其特征在于，相对于100重量份的所述树脂成分，含有1～100重量份的强化填充材料，该强化填充材料为选自由纤维状无机填充材料以及板状无机填充材料组成的群中的至少一种以上的强化填充材料。
8.如权利要求7所述的树脂组合物，其特征在于，所述纤维状无机填充材料为选自由玻璃纤维、玻璃短纤维、硅灰石以及碳纤维组成的群中的至少一种纤维状无机填充材料。
9.如权利要求7所述的树脂组合物，其特征在于，所述板状无机填充材料为选自由玻璃片、云母及滑石组成的群中的至少一种板状无机填充材料。
10.如权利要求1～9中任意一项所述的树脂组合物，其特征在于，所述光盘为CD及/或DVD。
11.一种成型品，其是由权利要求1～10中任意一项所述的树脂组合物形成的成型品。
12.一种树脂组合物的制造方法，其特征在于，相对于100重量份的树脂成分，混合0.001～8重量份的不含磷及溴的阻燃剂和0.01～3重量份的含氟防滴落剂，其中，所述树脂成分含有0～99重量％的芳香族聚碳酸酯树脂以及1～100重量％的基板为聚碳酸酯树脂的光盘粉碎物。