CN101259426A - 制备高耐磨分子筛流化床催化剂的方法 - Google Patents
制备高耐磨分子筛流化床催化剂的方法 Download PDFInfo
- Publication number
- CN101259426A CN101259426A CNA2008100432936A CN200810043293A CN101259426A CN 101259426 A CN101259426 A CN 101259426A CN A2008100432936 A CNA2008100432936 A CN A2008100432936A CN 200810043293 A CN200810043293 A CN 200810043293A CN 101259426 A CN101259426 A CN 101259426A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- molecular sieve
- preparation
- sapo
- suspension
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种高耐磨强度的流化床催化剂的制备方法,主要解决现有技术中流化床催化剂耐磨性能偏低和制备能耗高的问题。本发明通过采用包括以下步骤:(a)将含水的分子筛、粘结剂、基体材料、催化剂细粉、液体介质均匀混合形成悬浮液,其中分子筛的含水率为1~90%;(b)高速剪切该悬浮液,直至悬浮液中的90%的颗粒尺度小于8微米;(c)干燥该悬浮液形成微球催化剂;(d)高温焙烧该微球催化剂形成成品催化剂的技术方案较好地解决了该问题,可应用于从甲醇或者二甲醚原料生产低碳烯烃的反应过程中。
Description
技术领域
本发明涉及一种制备高耐磨分子筛流化床催化剂的方法,尤其是一种应用于甲醇或者二甲醚原料生产低碳烯烃的反应过程中的分子筛流化床催化剂的制备方法。
背景技术
乙烯和丙烯可用于生产塑料和其他化工产品,是重要的有机化工原料,随着现代社会的进步和发展,其需求量越来越大。目前世界上98%以上的乙烯产量来自于蒸汽裂解技术,丙烯生产主要以蒸汽裂解生产乙烯的联产品和炼油厂催化裂化的副产品两种形式获得。由于石油需求的持续增长、产能增长有限以及石油资源的不可再生性,近年来原油价格上升趋势,使乙烯、丙烯的生产成本随之上升,并且已探明石油资源按现有生产水平仅可开采将近50年,开发非常规石油资源利用技术已迫在眉睫。
甲醇是一种常见的大宗化工原料,可由煤炭、天然气、生物质、固体废物等作为原料来生产,原料来源非常广泛。天然气等原料通过部分氧化法或蒸汽转化法得到合成气(CO+H2),然后在合成甲醇催化剂(如铜/锌氧化物催化剂)的作用下,在合成反应器中转化得到甲醇。天然气或煤经合成气生产甲醇已实现工业化,规模不断扩大、技术日臻完善。非石油资源如天然气资源相对丰富,尽管以很高的消费速度增长,但世界范围内的天然气供应仍可保证100多年。因此,在未来几十年里,世界范围内的能源结构将发生重大变化。从能源结构的多元化和可持续供应能力考虑,天然气等非常规石油资源利用正越来越受到重视。
甲醇制烯烃(Methanol-To-Olefin,简称MTO)是指利用通常由天然气或煤生产的甲醇,在催化剂作用下生成聚合级乙烯、丙烯等低碳烯烃的工艺技术。MTO技术开拓了从非常规石油资源出发制取化工产品的一条新工艺路线,已成为新能源资源技术研究开发热点之
甲醇制烯烃过程,需要在分子筛的择形催化的作用下进行。分子筛是一类天然的或人工合成的沸石型结晶硅铝酸盐。其化学通式为Mx/n〔(AlO2)x·(SiO2)y〕·mH2O,式中M为化合价为n的金属离子,通常是Na+、K+、Ca2+等。分子筛具有多孔的骨架结构,在结构中有许多孔径均匀的通道和排列整齐、内表面相当大的空穴。这些晶体只能允许直径比空穴孔径小的分子进入孔穴,从而可使大小不同的分子分开,起到筛选分子的作用,故而得名。根据硅铝酸根中SiO2/Al2O3的比值不同,分子筛可分为A型、X型、Y型和丝光沸石等。
分子筛被广泛用于分离技术和催化技术,例如用于蛋白质、多糖和合成高分子等物质的分离,也可用作气体和液体的干燥剂。以分子筛为活性组分制得的催化剂通常用作固体酸催化剂。近年来,分子筛催化的非酸式反应(包括氧化、还原、烃类低聚、羰基化等反应)日益引起注意。还发现以其他杂原子(如镓、锗、铁、硼、磷等)取代铝和硅,所形成的杂原子沸石分子筛,具有某些特殊的催化性能。
很多分子筛均可用于甲醇制烯烃的催化剂活性组分,比如广为人们所知的ZSM-5分子筛、SAPO分子筛等。其他可应用于甲醇制烯烃反应的分子筛有T沸石、ZK-5、毛沸石和菱沸石等,US4062905对此进行了描述。专利US4079095描述了采用ZSM-34分子筛催化甲醇制烯烃的过程;专利US4310440描述了AlPO4分子筛催化甲醇制烯烃的过程。截至至目前,应用于MTO反应过程的分子筛以SAPO-34分子筛的性能为最佳。SAPO-34分子筛是一种磷酸硅铝微孔晶体,结构类似于菱沸石,属于三方晶系,具有三维孔道结构,其孔口直径约为0.43nm,比Y、ZSM-5、丝光、Beta等广泛工业应用的分子筛孔径小,具有强择形性,因而用于甲醇制烯烃反应时表现的性能良好,低碳烯烃的选择性较高。
分子筛应用于工业催化时,一般不能采用100%的分子筛制备成催化剂应用于工业过程。分子筛的自身粘结性比较差,自身粒度过于细小,难于成型为直接应用于工业过程的催化剂。分子筛的制造成本一般比较高,如果采用100%的分子筛作为工业催化剂,将使得工业过程的运作成本增加。工业过程一般要求催化剂具备一定的形状和强度以适应于工业反应器。对于固定床反应器,催化剂在安装之后无需移动,但催化剂需具备一定的抗压碎强度,以防止在装剂过程中催化剂受冲击而破损,并防止安装在下层的催化剂由于承受压力而破损。催化剂的破损粉化可能导致装置压力降的上升,反应行为可能会出现异常,产品组成发生变化,不利于目标反应过程。对于流化床反应器,由于催化剂本身在反应器中不断循环流动或者湍动,催化剂颗粒与颗粒、催化剂与反应器器壁、催化剂与再生器器壁、催化剂与取热器器壁、催化剂与输送管道壁之间的摩擦和碰撞均会使催化剂磨细和破损,最终以细粉的形式逸出反应系统。这些细粉会污染环境,并使催化剂的使用成本上升。因此,无论是将分子筛应用于固定床反应器,还是应用于流化床反应器,均需将分子筛和载体材料通过粘结剂的作用形成分子筛催化剂组合物;这种分子筛组合物同时可兼具催化活性、选择性、稳定性、形状和强度,从而满足工业过程对催化剂的要求。
US6509290专利公开了一种制备分子筛催化剂的方法,该催化剂中含有分子筛磨碎颗粒和原始分子筛。该磨碎颗粒主要来自催化剂生产工艺和反应系统再循环的碎颗粒。该方法包括将分子筛、原始粘结剂和填料、喷雾干燥的磨碎颗粒或团块和来自反应装置的非原始磨碎颗粒一起混合。将该混合物干燥,形成成品催化剂颗粒。为了增加催化剂颗粒的强度,该磨碎颗粒基本上不含焦炭。
US6153552专利研究了一种制备分子筛催化剂的方法,该方法包括将分子筛与氧化铝溶胶一起混合,该氧化铝溶胶在溶液中制备并保持在2-10的PH值下,喷雾干燥并高温焙烧该混合物,制得耐磨催化剂。
CN1791463专利公开了一种制备分子筛催化剂的方法,该方法包括将分子筛、液体和有效硬化量大干燥的分子筛催化剂一起混合形成淤浆,干燥该淤浆后焙烧,形成耐磨催化剂。
CN1533302专利公开了一种分子筛催化剂组合物的方法,该方法将含水0%至80%的分子筛与液体介质、粘结剂、基体材料、分子筛混合后干燥制备催化剂。
尽管已有一些专利涉及到了流化床催化剂的制备方法,但流化床催化剂的耐磨强度较低,制备过程中的能耗需要进一步降低。
发明内容
本发明所要解决的技术问题是现有技术中存在的分子筛流化床催化剂的耐磨性能较差、能耗较高的问题,提供一种新的制备高耐磨分子筛流化床催化剂的方法,该方法制得的催化剂具有耐磨强度高、催化性能好的优点。
为了解决上述技术问题,本发明采用的技术方案如下:一种高耐磨强度流化床催化剂的制备方法,包括以下步骤:(a)将含水的分子筛、粘结剂、基体材料、催化剂细粉、液体介质均匀混合形成悬浮液,其中分子筛的含水率为1~90%;(b)高速剪切该悬浮液,直至悬浮液中的90%的颗粒尺度小于8微米;(c)干燥该悬浮液形成微球催化剂;(d)高温焙烧该微球催化剂形成成品催化剂。
上述技术方案中,催化剂细粉优选方案为来自于反应装置,具体而言,即催化剂磨碎之后逸出反应系统的催化剂细粉;高温焙烧温度为500~1000℃;(a)步骤悬浮液固体含量优选范围为20%~50%;分子筛优选方案选自SAPO-5、SAPO-11、SAPO-17、SAPO-18、SAPO-34、SAPO-35、SAPO-44、SAPO-47、SAPO-56或ZSM-5中的至少一种;所配制的分子筛催化剂悬浮液的PH值优选范围为2.5至5.5之间;粘结剂优选方案选自一种溶胶,更优选方案为硅溶胶或铝溶胶;基体材料是一种粘土,更优选方案选自高岭土;喷雾干燥制备的催化剂经过高温焙烧后,具有优选范围小于1.5重量%/小时的磨损指数;更优选范围为具有小于1.0重量%/小时的磨损指数;最优选范围为有小于0.5重量%/小时的磨损指数;制得的催化剂中粘结剂优选范围为2.0~50重量%,分子筛优选范围为5.0~80重量%,催化剂细粉优选范围为1.0~80重量%,基体材料优选范围为0.0~90重量%。
由于催化剂颗粒在反应-再生系统中不断循环,催化剂颗粒的破碎细粉化基本上不可避免,根据催化剂强度的不同,破碎的比例、速度会有所不同。为了将细粉回收利用,避免污染环境、降低装置的操作费用,需要将细粉重新投入催化剂的生产之中。而且细粉本身是一个个硬化的颗粒,具有较高的强度,当与分子筛、粘结剂等重新组合时会对催化剂的强度带来有利的影响。同时,在配制喷雾前的分子筛悬浮液时,将洗涤完毕的分子筛不进行干燥,直接在测定含水量后,与粘结剂、基体材料、水、催化剂细粉等混合后进行制备催化剂。本方案减少了洗涤后的分子筛干燥和粉化的步骤,降低了能耗。同时,由于含水分子筛中的固体颗粒相对离散,在配制喷雾前的悬浮液时,可搅拌节省时间,在相对较短的时间内达到较好的均匀离散度。
本专利发现,采用技术方案:(a)将含水的分子筛、粘结剂、基体材料、催化剂细粉、液体介质均匀混合形成悬浮液,其中分子筛的含水率为1~90%;(b)高速剪切该悬浮液,直至悬浮液中的90%的颗粒尺度小于8微米;(c)干燥该悬浮液形成微球催化剂;(d)高温焙烧该微球催化剂形成成品催化剂。该制备方法得到的成品催化剂具有较高的耐磨强度,其磨损指数达到了0.03重量%/小时,获得了较好的技术效果。
下面通过实施例对本发明作进一步的阐述,但不仅限于本实施例。
具体实施方式
【实施例1】
根据比例16%(重量)ZSM-5分子筛:10%(重量)高岭土:10%(重量)催化剂细粉:4%(重量)铝溶胶:60%(重量)去离子水称取原料。除水之外,此处配比的原料比例均为干基重量比。分子筛中含占湿分子筛30%的水,这部分水归入去离子水中计量。此实施例中固含量为40%。
将ZSM-5分子筛和一定的水进行混合,搅拌1个小时,予以充分搅拌,用高速剪切机高速剪切15分钟后形成均匀的分子筛悬浮液;向悬浮液之中加入铝溶胶,快速搅拌15分钟,用高速剪切机剪切15分钟;加入一定量的高岭土,搅拌30分钟,达到均匀状态后,用高速剪切机进行高速剪切混合45分钟得到喷雾干燥前的悬浮液。用激光粒度仪测定此悬浮液的颗粒度,其平均粒径为3.5微米。喷雾干燥此悬浮液后进行700度高温焙烧,测定磨损指数为0.03重量%/小时。
【实施例2~5】
与实施例1的加料顺序完全相同,只是在进行悬浮液的配制时,剪切时间缩短,获得了不同的悬浮液颗粒尺度,并影响了催化剂的磨损指数,相关结果见表1。
表1
实施例 | 悬浮液颗粒平均尺度(微米) | 磨损指数(重量%/小时) |
实施例2 | 7.2 | 1.85 |
实施例3 | 4.6 | 0.092 |
实施例4 | 3.8 | 0.05 |
实施例5 | 2.9 | 0.03 |
比较例1 | 8.5 | 2.77 |
【比较例1】
与实施例1的加料顺序完全相同,只是在进行悬浮液的配制时,剪切时间缩短,获得了不同的悬浮液颗粒尺度,并影响了催化剂的磨损指数,相关结果见表1。
【实施例6~9】
与实施例1的操作步骤和试验条件完全相同,只是在完成悬浮液的配制后,通过加氨水调节悬浮液的PH值。相关结果见表2。
表2
实施例 | 悬浮液PH值 | 磨损指数(重量%/小时) |
实施例6 | 3.4 | 0.07 |
实施例7 | 3.8 | 0.15 |
实施例8 | 4.3 | 0.22 |
实施例9 | 4.8 | 0.98 |
【实施例10~13】
与实施例1的操作步骤和试验条件完全相同,只是在配制悬浮液时加入的分子筛含水率不同。相关结果见表3。
表3
实施例 | 分子筛含水率 | 磨损指数(重量%/小时) |
实施例10 | 10% | 0.07 |
实施例11 | 40% | 0.05 |
实施例12 | 60% | 0.12 |
实施例13 | 75% | 018 |
Claims (9)
1、一种高耐磨强度流化床催化剂的制备方法,包括以下步骤:(a)将含水的分子筛、粘结剂、基体材料、催化剂细粉、液体介质均匀混合形成悬浮液,其中分子筛的含水率为1%~90%;(b)高速剪切该悬浮液,直至悬浮液中的90%的颗粒尺度小于8微米;(c)干燥该悬浮液形成微球催化剂;(d)高温焙烧该微球催化剂形成成品催化剂。
2、根据权利要求1所述的高耐磨强度的流化床催化剂的制备方法,其特征在于催化剂细粉来自于反应装置,具体而言,即催化剂磨碎之后逸出反应系统的催化剂细粉;高温焙烧的温度为500~1000℃。
3、根据权利要求1所述的高耐磨强度的流化床催化剂的制备方法,其特征在于(a)步骤悬浮液固体含量为20~50%。
4、根据权利要求1所述的高耐磨强度的流化床催化剂的制备方法,其特征在于分子筛选自SAPO-5、SAPO-11、SAPO-17、SAPO-18、SAPO-34、SAPO-35、SAPO-44、SAPO-47、SAPO-56或ZSM-5中的至少一种;所配制的分子筛催化剂悬浮液的PH值在2.5至5.5之间。
5、根据权利要求1所述的高耐磨强度的流化床催化剂的制备方法,其特征在于粘结剂是一种溶胶,基体材料是一种粘土;喷雾干燥制备的催化剂经过高温焙烧后,具有小于1.5重量%/小时的磨损指数。
6、根据权利要求5所述的高耐磨强度的流化床催化剂的制备方法,其特征在于喷雾干燥制备的催化剂经过高温焙烧后,具有小于1.0重量%/小时的磨损指数。
7、根据权利要求6所述的高耐磨强度的流化床催化剂的制备方法,其特征在于喷雾干燥制备的催化剂经过高温焙烧后,具有小于0.5重量%/小时的磨损指数。
8、根据权利要求5所述的高耐磨强度的流化床催化剂的制备方法,其特征在于其特征在于粘结剂为硅溶胶或铝溶胶;基体材料为高岭土。
9、根据权利要求1所述的高耐磨强度的流化床催化剂的制备方法,其特征在于制得的催化剂中粘结剂占2.0~50重量%;分子筛占5.0~80重量%;催化剂细粉占1.0~80重量%;基体材料占0.0~90重量%。