CN100560867C - 淀粉接枝共聚物纸张涂布粘合剂 - Google Patents
淀粉接枝共聚物纸张涂布粘合剂 Download PDFInfo
- Publication number
- CN100560867C CN100560867C CNB2007100172830A CN200710017283A CN100560867C CN 100560867 C CN100560867 C CN 100560867C CN B2007100172830 A CNB2007100172830 A CN B2007100172830A CN 200710017283 A CN200710017283 A CN 200710017283A CN 100560867 C CN100560867 C CN 100560867C
- Authority
- CN
- China
- Prior art keywords
- parts
- starch
- add
- paper
- graft copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种淀粉接枝共聚物纸张涂布粘合剂及其制备工艺。它属于纸张涂布粘合剂。它由淀粉、片碱、丙烯腈、双氧水、水、丁苯胶乳、苯丙胶乳和各种助剂组成。本发明淀粉接枝共聚物纸张涂布粘合剂具有固含量高、粘度低、流动性好、成膜均匀、粘接力强、与各种合成胶乳相溶性好、抗霉变性好、性能稳定、干燥速度快、使用方便、成本低廉。涂布纸张表面强度好、平滑度好、光泽度高、吸墨性能好，可用于配制各种轻量涂布纸、自板涂布纸、铜版纸、玻璃卡纸、静电复印纸等涂布纸的高固含量涂料。
Description
一、技术领域
本发明涉及淀粉接枝共聚物纸张涂布粘合剂及其制备工艺。它属于纸张涂布粘合剂。
二、背景技术
目前纸张涂布粘合剂主要有：丁苯胶乳，苯丙胶乳，成本高，与纸张结合力差；替代品有：氧化淀粉、羧甲基淀粉、羧甲基纤维素、聚乙烯醇可替代部分合成胶乳降低涂布成本，但由于与合成胶乳丁苯胶乳、苯丙胶乳的相溶性差，结合力差，造成涂布纸张表面强度低，容易产生掉毛掉粉现象。
三、发明内容
本发明的目的是提供一种淀粉接枝共聚物纸张涂布粘合剂，部分或全部替代合成胶乳以降低纸张涂布成本以及改善已有淀粉类粘合剂的粘接力差、与合成胶乳相溶性差、抗水性差等缺点。
本发明的目的是这样来实现的：一种淀粉接枝共聚物纸张涂布粘合剂，其组成按重量配比为：
淀粉50～250份 片碱3～50份 丙烯腈5～60份 双氧水5～20份水600～850份 羧基丁苯胶乳20～350份 苯丙胶乳20～250份各种助剂55～200份；
所述的各种助剂按按重量配比为：轻质碳酸钙5～50份 增光润滑剂10～30份 抗水剂10～30份 三聚氰胺甲醛树脂10～30份 分散松香胶10～30份 甘油10～30份；
所述的淀粉为：玉米淀粉、木薯淀粉、土豆淀粉、大米淀粉；
本发明淀粉接枝共聚物纸张涂布粘合剂的制备工艺，按其组方将一定量的水加入反应釜中，边搅拌边加入配方量的淀粉，搅拌均匀后，再加入用少量水溶解的片碱，搅拌，再加入丙烯腈，搅拌，加入双氧水，搅拌、反应1～5h后，加入羧基丁苯胶乳、苯丙胶乳，搅拌，再加入轻质碳酸钙，增光润滑剂，抗水剂，三聚氰胺甲醛树脂，分散松香胶，甘油，搅拌均匀后出料，得淀粉接枝共聚物纸张涂布粘合剂成品。
四、实现方式
本发明提供淀粉接枝共聚物纸张涂布粘合剂，其组成按重量配比为：
淀粉50～250份 片碱3～50份 丙烯腈5～60份
双氧水5～20份 水600～850份 羧基丁苯胶乳20～350份
苯丙胶乳20～250份 各种助剂55～200份；
所述的各种助剂按按重量配比为：
轻质碳酸钙5～50份 增光润滑剂10～30份 抗水剂10～30份
三聚氰胺甲醛树脂10～30份 分散松香胶10～30份 甘油10～30份
所述的淀粉为：玉米淀粉、木薯淀粉、土豆淀粉、大米淀粉；
本发明淀粉接枝共聚物纸张涂布粘合剂的制备工艺，按其组成将一定量的水加入反应釜中，边搅拌边加入配方量的淀粉，搅拌均匀后，再加入用少量水溶解的片碱，搅拌，再加入丙烯腈，搅拌，加入双氧水，搅拌、反应1～5h后，加入羧基丁苯胶乳、苯丙胶乳，搅拌，再加入轻质碳酸钙，增光润滑剂，抗水剂，三聚氰胺甲醛树脂，分散松香胶，甘油，搅拌均匀后出料，得淀粉接枝共聚物纸张涂布粘合剂成品。
本发明的最佳实施方案：
最佳实施方案一：
将1300kg水加入反应釜，再加入淀粉325kg，加入片碱39kg(加92kg水溶解)加拌均匀后，再加入丙烯腈30kg，搅拌，加入双氧水15kg，反应1～5h后，加入羧基丁苯胶乳200kg和苯丙胶乳300kg，再加入轻质碳酸钙50kg，搅拌均匀后出料。
最佳实施方案二：
将700kg水加入反应釜，再加入淀粉150kg，加入片碱5kg(加10kg水溶解)加拌均匀后，再加入丙烯腈6kg，搅拌，加入双氧水10kg，反应1～5h后，加入羧基丁苯胶乳80kg和苯丙胶乳100kg，再加入轻质碳酸钙10kg，搅拌均匀后出料。
最佳实施方案三：
将1300kg水加入反应釜，再加入淀粉325kg，加入片碱39kg(加92kg水溶解)加拌均匀后，再加入丙烯腈30kg，搅拌，加入双氧水15kg，反应1～5h后，加入羧基丁苯胶乳500kg，再加入轻质碳酸钙50kg，甘油30kg，增光润滑剂30kg，抗水剂30kg，三聚氰胺甲醛树脂30kg，分散松香胶30kg，搅拌均匀后出料。
本发明淀粉接枝共聚物纸张涂布粘合剂具有固含量高、粘度低、流动性好、成膜均匀、粘接力强、与各种合成胶乳相溶性好、抗霉变性好、性能稳定、干燥速度快、使用方便、成本低廉。涂布纸张表面强度好、平滑度好、光泽度高、吸墨性能好，可用于配制各种轻量涂布纸、白板涂布纸、铜版纸、玻璃卡纸、静电复印纸等涂布纸的高固含量涂料。
Claims (2)
1、一种淀粉接枝共聚物纸张涂布粘合剂，其特征在于：其组方按重量配比为：
淀 粉 50～250份 片 碱 3～50份 丙烯腈 5～60份
双氧水 5～20份 水 600～850份 羧基丁苯胶乳 20～350份
苯丙胶乳 20～250份 各种助剂 55～200份
所述的助剂按重量配比为：轻质碳酸钙5～50份增光润滑剂10～30份抗水剂10～30份三聚氰胺甲醛树脂10～30份分散松香胶10～30份甘油10～30份
所述的淀粉接枝共聚物纸张涂布粘合剂的制备工艺，按其组成将一定量的水加入反应釜中，边搅拌边加入配方量的淀粉，搅拌均匀后，再加入用少量水溶解的片碱，搅拌，再加入丙烯腈，搅拌，加入双氧水，搅拌、反应1～5h后，加入羧基丁苯胶乳、苯丙胶乳，搅拌，再依次加入轻质碳酸钙，增光润滑剂，抗水剂，三聚氰胺甲醛树脂、分散松香胶、甘油，搅拌均匀后出料，得淀粉接枝共聚物纸张涂布粘合剂成品。
2、如权利要求1所述的淀粉接枝共聚物纸张涂布粘合剂，其特征在于：所述的淀粉为：玉米淀粉、木薯淀粉、土豆淀粉、大米淀粉。