CN101008164A - 淀粉接枝共聚物纸张涂布粘合剂 - Google Patents

淀粉接枝共聚物纸张涂布粘合剂 Download PDF

Info

Publication number
CN101008164A
CN101008164A CN 200710017283 CN200710017283A CN101008164A CN 101008164 A CN101008164 A CN 101008164A CN 200710017283 CN200710017283 CN 200710017283 CN 200710017283 A CN200710017283 A CN 200710017283A CN 101008164 A CN101008164 A CN 101008164A
Authority
CN
China
Prior art keywords
add
starch
graft copolymer
latex
copolymer adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200710017283
Other languages
English (en)
Other versions
CN100560867C (zh
Inventor
张光华
程建华
陈均志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2007100172830A priority Critical patent/CN100560867C/zh
Publication of CN101008164A publication Critical patent/CN101008164A/zh
Application granted granted Critical
Publication of CN100560867C publication Critical patent/CN100560867C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种淀粉接枝共聚物纸张涂布粘合剂及其制备工艺。它属于纸张涂布粘合剂。它由淀粉、片碱、丙烯腈、双氧水、水、丁苯胶乳、苯丙胶乳和各种助剂组成。本发明淀粉接枝共聚物纸张涂布粘合剂具有固含量高、粘度低、流动性好、成膜均匀、粘接力强、与各种合成胶乳相溶性好、抗霉变性好、性能稳定、干燥速度快、使用方便、成本低廉。涂布纸张表面强度好、平滑度好、光泽度高、吸墨性能好，可用于配制各种轻量涂布纸、白板涂布纸、铜版纸、玻璃卡纸、静电复印纸等涂布纸的高固含量涂料。

Description

淀粉接枝共聚物纸张涂布粘合剂
一、技术领域
本发明涉及淀粉接枝共聚物纸张涂布粘合剂及其制备工艺。它属于纸张涂布粘合剂。
二、背景技术
目前纸张涂布粘合剂主要有：丁苯胶乳，苯丙胶乳，成本高，与纸张结合力差；替代品有：氧化淀粉、羧甲基淀粉、羧甲基纤维素、聚乙烯醇可替代部分合成胶乳降低涂布成本，但由于与合成胶乳丁苯胶乳、苯丙胶乳的相溶性差，结合力差，造成涂布纸张表面强度低，容易产生掉毛掉粉现象。
三、发明的目的
本发明的目的是提供一种淀粉接枝共聚物纸张涂布粘合剂，部分或全部替代合成胶乳以降低纸张涂布成本以及改善已有淀粉类粘合剂的粘接力差、与合成胶乳相溶性差、抗水性差等缺点。
本发明的目的是这样来实现的：一种淀粉接枝共聚物纸张涂布粘合剂，其组成按重量配比(份)为：
淀粉50～250      片碱3～50       丙烯腈5～60
双氧水5～20      水600～850      羧基丁苯胶乳20～350
苯丙胶乳20～250  各种助剂55～200
所述的各种助剂按按重量配比(份)为：
轻质碳酸钙5～50            增光润滑剂10～30    抗水剂10～30
三聚氰胺甲醛树脂10～30     分散松香胶10～30    甘油10～30
所述的淀粉为：玉米淀粉、木薯淀粉、土豆淀粉、大米淀粉；所述的合成胶乳为：苯丙胶乳、羧基丁苯胶乳
本发明淀粉接枝共聚物纸张涂布粘合剂的制备工艺，按其组方将一定量的水加入反应釜中，边搅拌边加入配方量的淀粉，搅拌均匀后，再加入用少量水溶解的片碱，搅拌，再加入丙烯腈，搅拌，加入双氧水，搅拌、反应1～5h后，加入合成胶乳，搅拌，再加入轻质碳酸钙，增光润滑剂，抗水剂，三聚氰胺甲醛树脂，分散松香胶，甘油等生产配方所述的各种助剂，搅拌均匀后出料，得淀粉接枝共聚物纸张涂布粘合剂成品。
四、实现方式
本发明提供淀粉接枝共聚物纸张涂布粘合剂，其组成按重量配比(份)为：
淀粉50～250      片碱3～50       丙烯腈5～60
双氧水5～20      水600～850      羧基丁苯胶乳20～350
苯丙胶乳20～250  各种助剂55～200
所述的各种助剂按按重量配比(份)为：
轻质碳酸钙5～50         增光润滑剂10～30     抗水剂10～30
三聚氰胺甲醛树脂10～30  分散松香胶10～30     甘油10～30
所述的淀粉为：玉米淀粉、木薯淀粉、土豆淀粉、大米淀粉；所述的合成胶乳为：苯丙胶乳、羧基丁苯胶乳
本发明淀粉接枝共聚物纸张涂布粘合剂的制备工艺，按其组成将一定量的水加入反应釜中，边搅拌边加入配方量的淀粉，搅拌均匀后，再加入用少量水溶解的片碱，搅拌，再加入丙烯腈，搅拌，加入双氧水，搅拌、反应1～5h后，加入合成胶乳，搅拌，再加入轻质碳酸钙，增光润滑剂，抗水剂，三聚氰胺甲醛树脂，分散松香胶，甘油等生产配方所述的各种助剂，搅拌均匀后出料，得淀粉接枝共聚物纸张涂布粘合剂成品。
本发明的最佳实施方案：
最佳实施方案一：
将1300kg水加入反应釜，再加入淀粉325kg，加入片碱39kg(加92kg水溶解)加拌均匀后，再加入丙烯腈30kg，搅拌，加入双氧水15kg，反应1～5h后，加入丁苯胶乳200kg和苯丁胶乳300kg，再加入轻质碳酸钙50kg，搅拌均匀后出料。
最佳实施方案二：
将700kg水加入反应釜，再加入淀粉150kg，加入片碱5kg(加10kg水溶解)加拌均匀后，再加入丙烯腈6kg，搅拌，加入双氧水10kg，反应1～5h后，加入丁苯胶乳80kg和苯丁胶乳100kg，再加入轻质碳酸钙10kg，搅拌均匀后出料。
最佳实施方案三：
将1300kg水加入反应釜，再加入淀粉325kg，加入片碱39kg(加92kg水溶解)加拌均匀后，再加入丙烯腈30kg，搅拌，加入双氧水15kg，反应1～5h后，加入羧基丁苯胶乳500kg，再加入轻质碳酸钙50kg，甘油30kg，增光润滑剂30kg，抗水剂30kg，三聚氰胺甲醛树脂30kg，分散松香胶30kg，搅拌均匀后出料。
本发明淀粉接枝共聚物纸张涂布粘合剂具有固含量高、粘度低、流动性好、成膜均匀、粘接力强、与各种合成胶乳相溶性好、抗霉变性好、性能稳定、干燥速度快、使用方便、成本低廉。涂布纸张表面强度好、平滑度好、光泽度高、吸墨性能好，可用于配制各种轻量涂布纸、白板涂布纸、铜版纸、玻璃卡纸、静电复印纸等涂布纸的高固含量涂料。

Claims (4)

1、一种淀粉接枝共聚物纸张涂布粘合剂，其组成按重量配比(份)为：
淀粉50～250      片碱3～50          丙烯腈5～60
双氧水5～20      水600～850         羧基丁苯胶乳20～350
苯丙胶乳20～250  各种助剂55～200。
2、如权利要求1所述的淀粉接枝共聚物纸张涂布粘合剂，其特征在于：所述的助剂按按重量配比(份)为：
轻质碳酸钙5～50         增光润滑剂10～30          抗水剂10～30
三聚氰胺甲醛树脂10～30  分散松香胶10～30          甘油10～30。
3、如权利要求1所述的淀粉接枝共聚物纸张涂布粘合剂，其特征在于：所述的淀粉为：玉米淀粉、木薯淀粉、土豆淀粉、大米淀粉；所述的合成胶乳为：苯丙胶乳、羧基丁苯胶乳。
4、如权利要求1所述的淀粉接枝共聚物纸张涂布粘合剂的制备工艺，其特征在于：按其组方将一定量的水加入反应釜中，边搅拌边加入配方量的淀粉，搅拌均匀后，再加入用少量水溶解的片碱，搅拌，再加入丙烯腈，搅拌，加入双氧水，搅拌、反应1～5h后，加入合成胶乳，搅拌，再加入轻质碳酸钙，增光润滑剂，抗水剂，三聚氰胺甲醛树脂，分散松香胶，甘油等生产配方所述的各种助剂，搅拌均匀后出料，得淀粉接枝共聚物纸张涂布粘合剂成品。
CNB2007100172830A 2007-01-24 2007-01-24 淀粉接枝共聚物纸张涂布粘合剂 Expired - Fee Related CN100560867C (zh)