CH667466A5 - Verfahren zum nachbehandeln einer eisenguss-schmelze. - Google Patents
Verfahren zum nachbehandeln einer eisenguss-schmelze. Download PDFInfo
- Publication number
- CH667466A5 CH667466A5 CH5509/85A CH550985A CH667466A5 CH 667466 A5 CH667466 A5 CH 667466A5 CH 5509/85 A CH5509/85 A CH 5509/85A CH 550985 A CH550985 A CH 550985A CH 667466 A5 CH667466 A5 CH 667466A5
- Authority
- CH
- Switzerland
- Prior art keywords
- cast iron
- melt
- iron melt
- post
- alloyed
- Prior art date
Description
667 466
2
Claims (4)
1. Verfahren zum Nachbehandeln einer entschwefelten und mit Mg legierten, zur Erzeugung von Sphäroguss bestimmten Eisen-Schmelze, dadurch gekennzeichnet, dass die Eisenguss-Schmelze mit Gasen bzw. mit Gasgemischen nachbehandelt wird.
2. Verfahren nach Anspruch 1, zwecks Entfernen von nichtmetallischen Einschlüssen aus der Eisenguss-Schmelze, dadurch gekennzeichnet, dass die Eisenguss-Schmelze mit Ar bzw. Nî bzw. CO2 gespült wird.
3. Verfahren nach Anspruch 1, zwecks Aufkohlen der Eisenguss-Schmelze, dadurch gekennzeichnet, dass in erster Phase ein gasförmiger Kohlenwasserstoff und in der zweiten Phase Ar in die Eisenguss-Schmelze eingeblasen wird.
4. Verfahren nach Anspruch 1, zwecks Steuern des Keimzustandes der Eisenguss-Schmelze, dadurch gekennzeichnet, dass Luft bzw. ein Gasgemisch aus Ar + O2 bzw. N2 + O2 mit einem Anteil an O2 von 1 bis 30 Vol% in die Eisenguss-Schmelze eingeblasen wird.
BESCHREIBUNG Die Erfindung betrifft ein Verfahren zum Nachbehandeln einer entschwefelten, mit Mg legierten, zur Erzeugung von Sphäroguss bestimmten Eisenguss-Schmelze.
Das bisherige Nachbehandeln einer entschwefelten, mit Mg legierten Schmelze, besteht lediglich im Impfen unter Zugabe von Impfmitteln, die grösstenteils auf FeSi basieren. Das Entfernen von dispergierten, nichtmetallischen Einschlüssen wird nur durch ein längeres Abstehen der Eisenguss-Schmelze erreicht. Dieses ist jedoch mit Temperaturverlust und Magnesiumabklingen verbunden. Es wäre wünschenswert, die nichtmetallischen Einschlüsse aus der Schmelze schneller zu entfernen, um den Mg-Abbrand und
Temperaturverlust zu senken. Weiter vermisst man bis jetzt eine bessere Kontrolle über den Keimzustand der Eisenguss-Schmelze, ohne dass Begleitelemente, zum Beispiel Si als O2 Träger, zugegeben werden.
5 Aufgabe dieser Erfindung ist ein solches Verfahren vorzuschlagen, mit welchem die erwähnten Nachteile eliminiert werden können.
Diese Aufgabe wird durch die Lehre des ersten Anspruches gelöst.
10 Weitere vorteilhafte Varianten des Verfahrens gehen aus den abhängigen Ansprüchen hervor.
Die Grundidee des Verfahrens zum Nachbehandeln einer entschwefelten und mit Mg legierten Eisenguss-Schmelze nach dieser Erfindung besteht im Einblasen von Gasen bzw.
15 von Gasgemischen in die Schmelze.
Es werden nach diesem Verfahren die nichtmetallischen Einschlüsse aus einer entschwefelten und mit Mg legierten Eisenguss-Schmelze durch das Spülen der Schmelze mit Ar bzw. N2 bzw. CO2 entfernt.
20 Es wird nach diesem Verfahren, zum Beispiel das Aufkohlen, einer entschwefelten und mit Mg legierten Eisenguss-Schmelze dadurch erreicht, dass in der ersten Phase ein gasförmiger Kohlenwasserstoff und in der zweiten Phase Ar zur Wasserstoff-Entfernung in die Schmelze eingeblasen wird.
25 Es wird nach diesem Verfahren, zum Beispiel der Keimzustand, der Schmelze durch gezielte Oxydation gesteuert,
wobei Luft bzw. ein Gemisch aus Ar + O2 bzw. N2 + O2 mit einem Anteil an O2 von 1 - 30 Vol% in die Schmelze eingeblasen wird.
30 Die Vorteile des Verfahrens nach dieser Erfindung liegen in der Möglichkeit der gezielten Nachbehandlung von ent-schwefelter und mit Mg legierten Eisenguss-Schmelze, um eine bessere Qualität der Sphärogussteile zu erreichen. Das Einblasen von Gasen bzw. von Gasgemischen wird auf
35 bekannte Weise mittels Blasenlanzen oder poröser Stopfen vorgenommen.
G