JPS62228421A - 溶融鋳鉄の後処理方法 - Google Patents
溶融鋳鉄の後処理方法Info
- Publication number
- JPS62228421A JPS62228421A JP61305576A JP30557686A JPS62228421A JP S62228421 A JPS62228421 A JP S62228421A JP 61305576 A JP61305576 A JP 61305576A JP 30557686 A JP30557686 A JP 30557686A JP S62228421 A JPS62228421 A JP S62228421A
- Authority
- JP
- Japan
- Prior art keywords
- cast iron
- molten cast
- post
- treatment
- molten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明はノジュラー鋳鉄を製造するために脱硫し、Ｍｇ
合金とした溶融鋳鉄を後処理する方法に関するものであ
る。
合金とした溶融鋳鉄を後処理する方法に関するものであ
る。
従来脱硫し、）、１８合金とした溶融鋳鉄の後処理は、
ＦｅＳ ｉを主成分とする接種剤を添加して接種を行う
ことのみからなる。分散した非金属介在物の除去は溶融
鋳鉄を比較的長時間キリング処理することによってのみ
達成される。しかし、この結果として温度の低下および
マグネシウムの損失が起る。
ＦｅＳ ｉを主成分とする接種剤を添加して接種を行う
ことのみからなる。分散した非金属介在物の除去は溶融
鋳鉄を比較的長時間キリング処理することによってのみ
達成される。しかし、この結果として温度の低下および
マグネシウムの損失が起る。
温度の低下およびマグネシウムの損失を小さくするには
、非金属介在物を溶融物から比較的迅速に除去するのが
望ましい。また、同伴元素、例えば、０゜キャリヤであ
るＳｉを添加せずに、溶融鋳鉄の核の状態を適当に制御
することは従来不可能であった。
、非金属介在物を溶融物から比較的迅速に除去するのが
望ましい。また、同伴元素、例えば、０゜キャリヤであ
るＳｉを添加せずに、溶融鋳鉄の核の状態を適当に制御
することは従来不可能であった。
本発明の目的は上述の欠点を消滅することができる方法
を提供することにある。
を提供することにある。
本発明はノジュラー鋳鉄を製造するために脱硫し、Ｍｇ
合金とした溶融鋳鉄を後処理するに当り、前記溶融鋳鉄
をガスまたはガス状混合物で後処理することを特徴とす
る溶融鋳鉄の後処理方法により、この目的を達成する。
合金とした溶融鋳鉄を後処理するに当り、前記溶融鋳鉄
をガスまたはガス状混合物で後処理することを特徴とす
る溶融鋳鉄の後処理方法により、この目的を達成する。
本発明方法の基本的技術思想は、脱硫し、Ｍｇ合金にし
た溶融鋳鉄中にガスおよび／またはガス状混合物を吹込
むことにある。
た溶融鋳鉄中にガスおよび／またはガス状混合物を吹込
むことにある。
本発明方法の好適例では、脱硫し、Ｍｇ合金にした溶融
鋳鉄をＡｒ、 Ｎ、およびＣ０２からなる群から選定し
た１種以上のガスで処理することにより前記溶融鋳鉄か
ら非金属介在物を除去する。
鋳鉄をＡｒ、 Ｎ、およびＣ０２からなる群から選定し
た１種以上のガスで処理することにより前記溶融鋳鉄か
ら非金属介在物を除去する。
本発明方法においては、例えば、脱硫し、Ｍｇ合金にし
た溶融鋳鉄中に、第１段階でガス状炭化水素を、第２段
階で水素除去のためにＡｒを吹込むことにより前記溶融
鋳鉄に加炭することができる。
た溶融鋳鉄中に、第１段階でガス状炭化水素を、第２段
階で水素除去のためにＡｒを吹込むことにより前記溶融
鋳鉄に加炭することができる。
本発明の他の好適例では、例えば、空気および／または
１〜３０％の０２を含有するＡｒ＋０２およびＮ２＋Ｏ
２からなる群から選定した１種以上のガス状混合物を前
記溶融鋳鉄中に吹込んで酸化を行うことにより前記溶融
鋳鉄の核の状態を制御することができる。
１〜３０％の０２を含有するＡｒ＋０２およびＮ２＋Ｏ
２からなる群から選定した１種以上のガス状混合物を前
記溶融鋳鉄中に吹込んで酸化を行うことにより前記溶融
鋳鉄の核の状態を制御することができる。
本発明の利点は、ノジュラー鋳鉄の品質を一層良好にす
るために、脱硫し、Ｍｇ合金にした溶融鋳鉄の後処理を
行うことができることにある。ガスおよび／またｉｔガ
ス状混合物の吹込みは吹込みランスまたは多孔質プラグ
を使用して既知方法で行うことができる。
るために、脱硫し、Ｍｇ合金にした溶融鋳鉄の後処理を
行うことができることにある。ガスおよび／またｉｔガ
ス状混合物の吹込みは吹込みランスまたは多孔質プラグ
を使用して既知方法で行うことができる。
次に本発明を実施例について説明する。
実施例１
５００ｋｇ取鍋内で、マグネシウム処理した溶融鋳鉄を
、直径３ｍｍのランスを使用して流堡３０β／分のアル
ゴンで３０秒間処理することにより、不純物を除去した
。この鋳造物の金属組織学的検査の結果、非金属介在物
の明確な減少が明らかになった。
、直径３ｍｍのランスを使用して流堡３０β／分のアル
ゴンで３０秒間処理することにより、不純物を除去した
。この鋳造物の金属組織学的検査の結果、非金属介在物
の明確な減少が明らかになった。
重量１２．５ｋｇの鋳造物の場合に、アルゴンで処理し
て不純物を除去した後にセラミックフィルタによる試験
を行った結果、フィルタによって留められた非金属物質
は４０％減少したことが明らかになった。
て不純物を除去した後にセラミックフィルタによる試験
を行った結果、フィルタによって留められた非金属物質
は４０％減少したことが明らかになった。
実施例２
マグネシウム処理したＭｇ＝０．０５％、硫黄０．００
８％の脱硫溶湯を、流量２２１／分のＮ２９０％と０２
１０％との混合物で１４５０℃において３０秒間処理す
ることにより、不純物を除去した。
８％の脱硫溶湯を、流量２２１／分のＮ２９０％と０２
１０％との混合物で１４５０℃において３０秒間処理す
ることにより、不純物を除去した。
重量１２．５ｋｇの鋳造物について比較した結果、超微
粒硬化物（カーバイド）の減少によって壁厚は５ｍｍか
ら３ｍｍに減少したこと、および結節状組織の数は１８
０個／ｍｍ”から２４０個／ｍｍ２ に増加したことが
明らかになった。
粒硬化物（カーバイド）の減少によって壁厚は５ｍｍか
ら３ｍｍに減少したこと、および結節状組織の数は１８
０個／ｍｍ”から２４０個／ｍｍ２ に増加したことが
明らかになった。
特許出願人 ゲオルク・フィッシャー・アクチェンゲゼ
ルシャフト
ルシャフト
Claims (1)
- 【特許請求の範囲】 １、ノジュラー鋳鉄を製造するために脱硫し、Ｍｇ合金
とした溶融鋳鉄を後処理するに当り、前記溶融鋳鉄をガ
スまたはガス状混合物で 後処理することを特徴とする溶融鋳鉄の後処理方法。 ２、前記溶融鋳鉄をＡｒ、Ｎ＿２およびＣＯ＿２からな
る群から選定した１種以上のガスで処理することにより
前記溶融鋳鉄から非金属介在物を除去する特許請求の範
囲第１項記載の方法。 ３、第１段階でガス状炭化水素を、第２段階でＡｒを前
記溶融鋳鉄中に吹込むことにより前記溶融鋳鉄に加炭す
る特許請求の範囲第１項記載の方法。 ４、空気および／または１〜３０％のＯ＿２を含有する
Ａｒ＋Ｏ＿２およびＮ＿２＋Ｏ＿２からなる群か選定し
た１種以上のガス状混合物を前記溶融鋳鉄中に吹込んで
前記溶融鋳鉄の核の状態を制御する特許請求の範囲第第
１項記載の方法。