BR112016014238A2 - Método para a produção de uma lâmina e lâmina - Google Patents
Método para a produção de uma lâmina e lâminaInfo
- Publication number
- BR112016014238A2 BR112016014238A2 BR112016014238A BR112016014238A BR112016014238A2 BR 112016014238 A2 BR112016014238 A2 BR 112016014238A2 BR 112016014238 A BR112016014238 A BR 112016014238A BR 112016014238 A BR112016014238 A BR 112016014238A BR 112016014238 A2 BR112016014238 A2 BR 112016014238A2
- Authority
- BR
- Brazil
- Prior art keywords
- blade
- nozzle
- expressed
- production
- extension
- Prior art date
Abstract
MÉTODO PARA A PRODUÇÃO DE UMA LÂMINA E LÂMINA. A presente invenção refere - se a um método para a produção de uma lâmina que compreende um substrato produzido a partir de aço em que pelo menos uma superfície é revestida. Neste processo (I) em que: Z é a distância entre a lâmina metálica (1) e o bocal (17) ao longo da direção de ejeção principal (E), Z é expressado em m, f o2 é a fração de volume de oxigênio na zona confinada (24). d é a altura média da saída (25) do bocal (17) ao longo da direção de extensão (S) da lâmina metálica (1) na frente do bocal (17), em que dé expressado em m, V é a velocidade de extensão da lâmina metálica (1) na frente do bocal (17), V é expressado em m.s - 1 , P é a sobrepressão de gás de enxugo no bocal (17) em relação à pressão atmosférica, sendo que P é expressado em N.m - 2.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/IB2013/061222 WO2015092493A1 (fr) | 2013-12-20 | 2013-12-20 | Procédé de réalisation d'une tôle à revêtement znalmg avec un essorage optimisé et tôle correspondante |
Publications (2)
Publication Number | Publication Date |
---|---|
BR112016014238A2 true BR112016014238A2 (pt) | 2017-08-08 |
BR112016014238B1 BR112016014238B1 (pt) | 2021-06-08 |
Family
ID=50030381
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112016014238-1A BR112016014238B1 (pt) | 2013-12-20 | 2013-12-20 | método para a produção de uma lâmina e lâmina |
Country Status (16)
Country | Link |
---|---|
US (1) | US10138538B2 (pt) |
EP (1) | EP3084031B2 (pt) |
JP (1) | JP6411514B2 (pt) |
KR (1) | KR102202740B1 (pt) |
CN (1) | CN106029933B (pt) |
BR (1) | BR112016014238B1 (pt) |
CA (1) | CA2935047C (pt) |
ES (1) | ES2676045T5 (pt) |
HU (1) | HUE038070T2 (pt) |
MX (1) | MX2016007995A (pt) |
PL (1) | PL3084031T5 (pt) |
RU (1) | RU2647967C2 (pt) |
TR (1) | TR201808782T4 (pt) |
UA (1) | UA114578C2 (pt) |
WO (1) | WO2015092493A1 (pt) |
ZA (1) | ZA201604073B (pt) |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN108018514B (zh) * | 2016-10-28 | 2020-07-28 | 宝山钢铁股份有限公司 | 一种控制Zn-Al-Mg合金镀层板材表面缺陷的方法及Zn-Al-Mg合金镀层板材 |
KR102031466B1 (ko) | 2017-12-26 | 2019-10-11 | 주식회사 포스코 | 표면품질 및 내식성이 우수한 아연합금도금강재 및 그 제조방법 |
CN108913949A (zh) * | 2018-07-11 | 2018-11-30 | 江苏麟龙新材料股份有限公司 | 一种用于预镀合金钢板的无硅多元合金镀覆材料及其制造方法 |
CN108977695B (zh) * | 2018-09-30 | 2020-12-01 | 济南大学 | 一种含钛和锑的热浸镀锌铝镁合金及其制备方法 |
WO2022101667A1 (en) * | 2020-11-16 | 2022-05-19 | Arcelormittal | A method for manufacturing a steel sheet with a znalmg coating, corresponding coated steel sheet, part and vehicle |
Family Cites Families (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE1796324A1 (de) | 1967-09-01 | 1972-10-19 | Hitachi Ltd | Verfahren und Vorrichtung zur kontinuierlichen Herstellung eines metallischen UEberzuges im Tauchverfahren |
JPS58177447A (ja) * | 1982-04-08 | 1983-10-18 | Nisshin Steel Co Ltd | 耐食性、塗装性に優れた溶融亜鉛めつき鋼板の製造法 |
JP2755387B2 (ja) | 1988-04-12 | 1998-05-20 | 大洋製鋼株式会社 | プレコート鋼板用溶融亜鉛アルミニウム合金めっき鋼板の製造方法およびプレコート鋼板 |
JP3357467B2 (ja) * | 1994-07-20 | 2002-12-16 | 川崎製鉄株式会社 | 耐食性と耐摩耗性に優れた溶融亜鉛めっき鋼材およびその製造方法 |
JP3580261B2 (ja) | 2001-03-23 | 2004-10-20 | 住友金属工業株式会社 | 溶融Zn−Al−Mgめっき鋼板およびその製造方法 |
ES2350921T3 (es) | 2002-07-24 | 2011-01-28 | Nisshin Steel Co., Ltd. | Chapa de acero galvanizado por inmersión en caliente basado en cinc excelente en la retención de brillo. |
US6677058B1 (en) | 2002-07-31 | 2004-01-13 | Nisshin Steel Co., Ltd. | Hot-dip Zn plated steel sheet excellent in luster-retaining property and method of producing the same |
EP2119804A1 (fr) | 2008-05-14 | 2009-11-18 | ArcelorMittal France | Procédé de fabrication d'une bande métallique revêtue présentant un aspect amélioré |
AU2009298988B2 (en) | 2008-10-01 | 2015-07-02 | Nippon Steel Corporation | Method for producing hot dip plated steel sheet and apparatus for hot dip plating |
US20100200239A1 (en) * | 2009-02-09 | 2010-08-12 | Kemira Chemicals, Inc. | Friction reducing compositions for well treatment fluids and methods of use |
WO2010130883A1 (fr) * | 2009-05-14 | 2010-11-18 | Arcelormittal Investigacion Y Desarrollo Sl | Procede de fabrication d'une bande metallique revetue presentant un aspect ameliore |
JP5221732B2 (ja) * | 2010-10-26 | 2013-06-26 | 日新製鋼株式会社 | ガスワイピング装置 |
JP5221733B2 (ja) | 2010-10-26 | 2013-06-26 | 日新製鋼株式会社 | ガスワイピング装置 |
KR20120075235A (ko) * | 2010-12-28 | 2012-07-06 | 주식회사 포스코 | 고내식 용융아연합금 도금강판과 그 제조방법 |
-
2013
- 2013-12-20 PL PL13826634T patent/PL3084031T5/pl unknown
- 2013-12-20 CA CA2935047A patent/CA2935047C/fr active Active
- 2013-12-20 RU RU2016124476A patent/RU2647967C2/ru active
- 2013-12-20 ES ES13826634T patent/ES2676045T5/es active Active
- 2013-12-20 EP EP13826634.1A patent/EP3084031B2/fr active Active
- 2013-12-20 KR KR1020167016345A patent/KR102202740B1/ko active IP Right Grant
- 2013-12-20 UA UAA201606633A patent/UA114578C2/uk unknown
- 2013-12-20 MX MX2016007995A patent/MX2016007995A/es unknown
- 2013-12-20 CN CN201380081782.XA patent/CN106029933B/zh active Active
- 2013-12-20 HU HUE13826634A patent/HUE038070T2/hu unknown
- 2013-12-20 WO PCT/IB2013/061222 patent/WO2015092493A1/fr active Application Filing
- 2013-12-20 JP JP2016541322A patent/JP6411514B2/ja active Active
- 2013-12-20 US US15/106,367 patent/US10138538B2/en active Active
- 2013-12-20 TR TR2018/08782T patent/TR201808782T4/tr unknown
- 2013-12-20 BR BR112016014238-1A patent/BR112016014238B1/pt active IP Right Grant
-
2016
- 2016-06-15 ZA ZA2016/04073A patent/ZA201604073B/en unknown
Also Published As
Publication number | Publication date |
---|---|
KR20160100974A (ko) | 2016-08-24 |
MX2016007995A (es) | 2016-10-07 |
RU2647967C2 (ru) | 2018-03-21 |
US10138538B2 (en) | 2018-11-27 |
JP2017508875A (ja) | 2017-03-30 |
ES2676045T3 (es) | 2018-07-16 |
EP3084031A1 (fr) | 2016-10-26 |
ES2676045T5 (es) | 2022-04-29 |
RU2016124476A (ru) | 2017-12-25 |
PL3084031T3 (pl) | 2018-09-28 |
JP6411514B2 (ja) | 2018-10-24 |
CN106029933A (zh) | 2016-10-12 |
WO2015092493A1 (fr) | 2015-06-25 |
CA2935047A1 (fr) | 2015-06-25 |
EP3084031B1 (fr) | 2018-04-04 |
ZA201604073B (en) | 2017-07-26 |
TR201808782T4 (tr) | 2018-07-23 |
CA2935047C (fr) | 2021-01-05 |
HUE038070T2 (hu) | 2018-09-28 |
PL3084031T5 (pl) | 2022-06-06 |
US20170029928A1 (en) | 2017-02-02 |
KR102202740B1 (ko) | 2021-01-13 |
BR112016014238B1 (pt) | 2021-06-08 |
EP3084031B2 (fr) | 2021-12-29 |
UA114578C2 (uk) | 2017-06-26 |
CN106029933B (zh) | 2018-09-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112016014238A2 (pt) | Método para a produção de uma lâmina e lâmina | |
UA114936C2 (uk) | СПОСІБ ВИРОБНИЦТВА СТАЛЕВОГО ЛИСТА З Zn-Al ПОКРИТТЯМ І З ОПТИМІЗОВАНОЮ ЧИСТОВОЮ ОБРОБКОЮ, ВІДПОВІДНИЙ СТАЛЕВИЙ ЛИСТ, ДЕТАЛЬ І АВТОТРАНСПОРТНИЙ ЗАСІБ | |
BR112019008710A2 (pt) | método e aparelho para produzir um componente de um artigo gerador de aerossol | |
GB2555303A (en) | Carton and carton blank | |
UY36313A (es) | Composición que comprende un carbonato de calcio reaccionado en la superficie como agente antiaglomerante, y método para producirla | |
MX2016017267A (es) | Procedimiento y herramienta de conformacion para el conformado en caliente asi como correspondiente pieza de trabajo. | |
BR112017011929A2 (pt) | processo de rompimento de uma forma interior em uma folha de vidro | |
WO2017103123A3 (de) | Herstellung von quarzglaskörpern mit taupunktkontrolle im schmelzofen | |
MX2016007442A (es) | Procedimiento y aparato para producir discos de rueda termoconformados. | |
BR112017017574A2 (pt) | processo para a produção de um produto de ureia estabilizado por formaldeído. | |
MY178267A (en) | Establishing a registered score, slit or slot in corrugated board, and articles produced therefrom | |
PH12019501804A1 (en) | Method for producing corrugated cardboard blanks, and device | |
AR106815A1 (es) | Proceso para la epoxidación de propeno | |
BR112014027951A2 (pt) | método aprimorado de aplicação de um revestimento de extremidade a frio integrado ao processo de fabricação de recipiente de vidro | |
BR112018012056A2 (pt) | ?processo e sistema de reação para produção de óxido de etileno, carbonato de etileno e/ou etilenoglicol a partir de etileno? | |
PE20180956A1 (es) | Metodo de doblado de vidrio soportado por presion positiva y dispositivo adecuado para el mismo | |
MX2018000760A (es) | Metodo de flexion por gravedad auxiliado por presion elevada y dispositivo adecuado para el mismo. | |
BR112018011440A2 (pt) | método de produção de produto moldado e produto moldado | |
MX2018001884A (es) | Metodo de flexion por gravedad auxiliado por presion elevada y dispositivo adecuado para el mismo. | |
BR112015026390A2 (pt) | dispositivo de processamento de grafagem por rolete e método de processamento de grafagem por rolete | |
WO2014121914A3 (de) | VERFAHREN ZUR FORMFREIEN HERSTELLUNG EINES GEFORMTEN GLASARTIKELS MIT VORBESTIMMTER GEOMETRIE, VERWENDUNG EINES VERFAHRENSGEMÄß HERGESTELLTEN GLASARTIKELS UND GEFORMTER GLASARTIKEL | |
MX2017007895A (es) | Aleación de aluminio adecuada para la producción a alta velocidad de botellas de aluminio y su proceso de fabricación. | |
BR112018076667A2 (pt) | método e dispositivo para a produção de microesferas de vidro ocas | |
PH12016502366B1 (en) | Formed material manufacturing method and formed material | |
PH12016501466B1 (en) | Die for ironing process, and shaped material production method |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B06U | Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette] | ||
B06A | Patent application procedure suspended [chapter 6.1 patent gazette] | ||
B09A | Decision: intention to grant [chapter 9.1 patent gazette] | ||
B16A | Patent or certificate of addition of invention granted [chapter 16.1 patent gazette] |
Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 20/12/2013, OBSERVADAS AS CONDICOES LEGAIS. |