WO2024070183A1 - 樹脂成形体および樹脂成形体の製造方法 - Google Patents
樹脂成形体および樹脂成形体の製造方法 Download PDFInfo
- Publication number
- WO2024070183A1 WO2024070183A1 PCT/JP2023/027611 JP2023027611W WO2024070183A1 WO 2024070183 A1 WO2024070183 A1 WO 2024070183A1 JP 2023027611 W JP2023027611 W JP 2023027611W WO 2024070183 A1 WO2024070183 A1 WO 2024070183A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mold
- coating layer
- coating
- resin molded
- molded body
- Prior art date
Abstract
樹脂を含む基材と、前記基材の表面に形成される厚さが100マイクロメートル以上1000マイクロメートル以下の第1塗膜層と、前記第1塗膜層の表面に形成される厚さが100マイクロメートル以上1000マイクロメートル以下の第2塗膜層と、を備える。
Description
本開示は、樹脂成形体およびこの樹脂成形体の製造方法に関する。
従来から、樹脂成形体を成形する金型内において樹脂成形体の塗膜層を形成する塗装方法が知られている(例えば、特許文献1参照)。このような塗装方法は、インモールドコーティング方法と称され、揮発性有機化合物の使用を削減でき、環境によい塗装方法として知られている。
また、コアバック式の射出成形装置を用いて、二種類の樹脂材料を一体化する樹脂成形方法も知られている(例えば、特許文献2参照)。
特許文献1のインモールドコーティング方法による塗装方法は、2つの塗膜層を形成する点を開示していない。さらに、特許文献2は、2つの樹脂層を一体化する方法を開示しているが、塗膜層の形成方法については開示していない。
本開示は、インモールドコーティング方法を用いて複数の塗膜層が形成された樹脂成形体およびこの樹脂成形体の製造方法を提供することにある。
本開示に係る樹脂成形体は、樹脂を含む基材と、前記基材の表面に形成される厚さが100マイクロメートル以上1000マイクロメートル以下の第1塗膜層と、前記第1塗膜層の表面に形成される厚さが100マイクロメートル以上1000マイクロメートル以下の第2塗膜層と、を備える。
また、本開示に係る樹脂成形体の製造方法は、第1型と第2型とにより形成されるキャビティに樹脂材料を注入し、基材を形成する工程と、前記第1型と前記第2型とを開き、前記基材と前記第1型との間に第1塗膜形成用材料を注入し、前記基材の表面に第1塗膜層を形成する第1塗膜工程と、前記第1型と前記第2型とを再度開き、前記第1塗膜層と前記第1型との間に第2塗膜形成用材料を注入し、前記第1塗膜層の表面に第2塗膜層を形成する第2塗膜工程と、を備える。
この樹脂成形体は、第1塗膜層はインモールドコーティング方法によって形成された塗膜層の厚さを有するものであり、第2塗膜層もインモールドコーティング方法によって形成された塗膜層の厚さを有するものである。
また、このような樹脂成形体の製造方法によれば、インモールドコーティング方法によって第1塗膜層と第2塗膜層とを形成することができる。
以下、本開示の実施形態について、図面を参照しながら説明する。
図1および図2に示すように、樹脂成形体1は、基材2と、第1塗膜層4と、第2塗膜層6と、を備える。本実施形態では、樹脂成形体1は、自動車の内装に用いる加飾パネルや、バンパーなどとして用いる樹脂部材である。樹脂成形体1は、表面1aと裏面1bとを有する。樹脂成形体1が自動車の内装部材である場合、樹脂成形体1の表面1aは、自動車のユーザに向けて組付けられる。また、樹脂成形体1が自動車の外装部材である場合、樹脂成形体1の表面1aは、自動車の外に向けて配置される。
基材2は、第1塗膜層4を形成するための土台となる樹脂部材である。基材2は、熱可塑性の樹脂材料によって形成される。樹脂材料は、例えば、ポリプロピレン、ポリエチレン、ABS樹脂(アクリロニトリル-ブタジエン-スチレン共重合体)、PC樹脂(ポリカーボネート樹脂)、などである。
第1塗膜層4は、基材2の表面1a側に形成される塗膜層である。より具体的には、第1塗膜層4は、インモールドコーティング方法によって基材2の表面に付着される第1塗膜形成用材料により形成される。第1塗膜形成用材料は、例えば、特開平6-107750号公報、および特開平8-113761号公報等に記載されたインモールドコーティング方法に適した塗料を含んでもよい。また、本実施形態では、第1塗膜層4は、着色剤を含む塗料で形成されたカラー層である。なお、第1塗膜層4は、金属片、マイカ片、およびガラスビーズなどからなる、いわゆる光輝材を含んでいてもよい。インモールドコーティング方法により形成される第1塗膜層4の厚さは、100マイクロメートル以上1000マイクロメートル以下である。
また、第1塗膜層4は、離型剤を含む、および/又は、離型剤が表面に付着した塗膜層である。すなわち、第1塗膜層4用の塗料では、離型剤が内在する場合がある。また、第1塗膜層4用の塗料は、離型剤成分を含まず、金型に噴霧した離型剤が塗膜表面に積層している場合もある。離型剤は、後述する第1金型22(図3を参照)に第1塗膜層4が付着することを抑制する薬剤である。離型剤は、成形品が金型から離れることを容易にする。本実施形態では、離型剤は、例えば、軽質ナフサやワックスを含む薬剤である。ワックスは、例えば、パラフィンワックス、およびマイクロワックスなどである。このほか、離型剤は、ポリジメチルシロキサンを含んでもよい。インモールドコーティング方法によって形成される第1塗膜層4の表面に離型剤が付着した状態で、後述する第2塗膜層6が形成される。
第2塗膜層6は、第1塗膜層4の表面に形成される塗膜層である。第2塗膜層6は、2つの異なる第2塗膜形成用材料が混合し硬化した塗料を含む。本実施形態では、第2塗膜層6を形成する塗料は、ポリオール(第1材料の一例)と、イソシアネート(第2材料の一例)と、が混合され反応し硬化したウレタン塗料である。しかし、第2塗膜層6は、異なる二つ以上の材料が混合され硬化した塗料を含めば、ウレタン塗料以外の塗料であってもよい。硬化は、異なる材料が混合された反応による硬化、および、二つの異なる材料が混合されたのち、温度が低下することによる硬化を含む。
本実施形態では、第2塗膜層6は、透明な塗膜で第1塗膜層4を覆うクリア層である。クリア層は、第1塗膜層4の色に対して光沢を加える機能を有する。また、クリア層は、第1塗膜層4を保護する機能を有する。このため、本実施形態では、第2塗膜層6は、着色剤を含まない塗料、または着色剤を含む半透明の塗料によって形成される。しかし、第2塗膜層6は、2つの異なる材料が混合され硬化する塗料であれば、どのような塗料であってもよい。
第2塗膜層6の厚さは、100マイクロメートル以上1000マイクロメートル以下である。本実施形態では、第2塗膜層6であるクリア層の厚さは、第1塗膜層4であるカラー層の厚さと同等か、カラー層の厚さよりも薄く設定されている。
次に、図3、図4および図5を用いて樹脂成形体1の製造方法について説明する。図3に示すように、本実施形態では、インモールドコーティング方法に用いる金型装置20は、第1金型(第1型の一例)22と、第2金型(第2型の一例)24と、樹脂インジェクタ26と、塗料インジェクタ28と、を含む樹脂射出成形用装置である。第1金型22と、第2金型24は、型閉じすることによってキャビティ30を形成する。しかし、金型装置20は、インモールドコーティング方法が可能であればどのような金型であってもよい。
樹脂インジェクタ26は、基材2(図2を参照)を形成する樹脂材料を射出するためのノズルである。本実施形態では、樹脂インジェクタ26は、キャビティ30の第2金型24側に配置される。樹脂インジェクタ26は、供給通路30aに向けて配置されてもよい。供給通路30aは、キャビティ30に接続される。塗料インジェクタ28は、第1塗膜形成用材料および第2塗膜形成用材料を注入するためのノズルである。本実施形態では、塗料インジェクタ28は、キャビティ30の第1金型22側に配置される。
まず、図4(a)に示すように、樹脂インジェクタ26からキャビティ30に樹脂材料が注入され、基材2が形成される。その後、金型装置20が型開きされて第2金型24が第1金型22から引き離され、これにより第1金型22が基材2から離間する。さらに、離型剤が第1金型22のキャビティ30に向けた面に塗布され、離型剤の層が形成される。なお、第1塗膜形成用材料に離型剤が含まれる場合は、離型剤の塗布工程を省略してもよい。また、第1塗膜形成用材料に離型剤が含まれない場合、基材2が形成される前に、離型剤が第1金型22および/又は第2金型24のキャビティ30に向けた面に塗布されてもよい。
図4(b)に示すように、第1塗膜層4を形成する場合には、第1金型22と基材2の間の距離が100マイクロメートル以上1000マイクロメートル以下となるように、第2金型24が第1金型22から引き離される。第1塗膜形成用材料は、第1金型22と基材2の間にできた隙間に、塗料インジェクタ28を介して注入される(第1塗膜工程)。このとき、第1塗膜形成用材料が流れやすくなるように、第1金型22および/又は第2金型24が加熱されてもよい。
図4(c)に示すように、第1塗膜層4が形成されると、第1金型22が第2金型24に向けて移動され、第1塗膜層4が圧縮される(図4(c)の白矢印を参照)(第1圧縮工程)。これによって、第1塗膜層4を基材2に密着させることができる。さらに、第1塗膜層4に第1金型22の表面転写をすることができる。また、第1塗膜層4が圧縮されることで、第1塗膜層4が硬化する際の収縮に起因して第1塗膜層4の表面にヒケが発生することを防止できる。このとき、第1金型22を第2金型24に向けて移動させる第1距離は、第1塗膜層4の厚さによって変更されることが好ましい。第1距離は、第1塗膜層4の厚さが厚いほど大きいことが好ましい。これによって、第1塗膜層4の厚さが厚い場合でも、第1塗膜層4を基材2に接着しやすくすることができる。後述する第2塗膜層6についても同様である。
次に、図5(a)に示すように、第1金型22が、第1塗膜層4の表面から100マイクロメートル以上1000マイクロメートル以下の距離をとった状態となるように、金型装置20が再度型開きされる(図5(a)の白矢印を参照)。その後、図5(b)に示すように、第2塗膜層6を形成するための二つの異なる材料を含む第2塗膜形成用材料がキャビティ30に注入される(第2塗膜工程)。このとき、異なる二つの材料は、塗料インジェクタ28の先端で混合されて注入される。注入された2つの材料は、塗料として第1塗膜層4の表面を流れながら反応し、硬化する。
図5(c)に示すように、塗料が硬化すると、第1金型22が第2金型24に向けて移動され、第2塗膜層6が圧縮される(図5(c)の白矢印を参照)(第2圧縮工程)。なお、本実施形態では、第2塗膜層6の厚さが、第1塗膜層4の厚さと同等か、それよりも厚く設定されている。このため、第2塗膜層6が圧縮される場合に、第1金型22を移動させる第2距離は、第1塗膜層4が圧縮される場合に第1金型22を移動させる第1距離と同等か、それよりも長い。
最後に、金型装置20が型開きされて第1金型22が第2金型24から引き離され、樹脂成形体1が取り出される。
以上説明した通り、このような樹脂成形体1によれば、第1塗膜層4と第2塗膜層6とをインモールドコーティング方法によって形成できる。これによって、塗布により塗膜層を形成する場合に比べて、揮発性有機化合物の使用を低減することができる。さらに、第2塗膜層6は、インモールドコーティング方法によって第1塗膜層4に形成される。これよって、塗布では垂下により形成できない厚い塗膜層(例えば、100マイクロメートル以上の厚さの塗膜層)を形成することができる。この結果、樹脂成形体1の耐久性が向上する。
また、本実施形態の樹脂成形体1の製造方法では、第1塗膜層4および第2塗膜層6が圧縮される。これによって、塗膜層をより強固に接着し、剥がれにくくすることができる。さらに、第1塗膜層4と第2塗膜層6とが同じ第1金型22と第2金型24とを用いて製造される。これにより、別々の金型を用いる場合に比べて製造コストを抑制できる。
また、本実施形態の樹脂成形体1の製造方法では、樹脂成形体1を取り出す工程まで第1金型22と第2金型24とが解放(つまり、キャビティ30が解放)されることがない。これによって、各塗膜層にゴミなどが付着することがない。この結果、このような製造方法によって製造された樹脂成形体1は、塗膜の剥がれがなく、見栄えの良さを維持しやすい。
<他の実施形態>
以上、本開示の実施形態について説明したが、本開示は上記実施形態に限定されるものではなく、発明の要旨を逸脱しない範囲で種々の変更が可能である。
以上、本開示の実施形態について説明したが、本開示は上記実施形態に限定されるものではなく、発明の要旨を逸脱しない範囲で種々の変更が可能である。
例えば、上記実施形態では、樹脂成形体1は、自動車に用いる部材を例に説明したが、本開示はこれに限定されない。樹脂成形体1は、自動車以外に用いる樹脂部材であってもよい。
また、基材2を形成する樹脂材料として、ポリプロピレン、ポリエチレン、ABS樹脂、PC樹脂などの熱可塑性樹脂を例示したが、本開示はこれに限定されない。基材2は、例えば、ポリアミド、ポリエチレンテレフタレート、変性ポリフェニレンエーテルなどの熱可塑性樹脂、あるいはこれら熱可塑性樹脂のアロイ材、さらにはこれら熱可塑性樹脂に繊維状あるいは鱗片状のフィラーを配合した樹脂材料であってもよい。いずれにせよ、基材2は、熱可塑性樹脂で形成されれば、どのような樹脂であってもよい。
上記実施形態では、基材2と第1金型22との間に第1塗膜層4および第2塗膜層6を形成したが、本開示はこれに限定されない。例えば、第1金型22側に基材2を貼り付かせて第2金型24と基材2との間に隙間を空けてから塗膜形成用材料を注入し、基材2と第2金型24との間に第1塗膜層4および第2塗膜層6を形成してもよい。
1 :樹脂成形体
1a :表面
1b :裏面
2 :基材
4 :第1塗膜層
6 :第2塗膜層
20 :金型装置
22 :第1金型
24 :第2金型
26 :樹脂インジェクタ
28 :塗料インジェクタ
30 :キャビティ
1a :表面
1b :裏面
2 :基材
4 :第1塗膜層
6 :第2塗膜層
20 :金型装置
22 :第1金型
24 :第2金型
26 :樹脂インジェクタ
28 :塗料インジェクタ
30 :キャビティ
Claims (4)
- 樹脂を含む基材と、
前記基材の表面に形成される厚さが100マイクロメートル以上1000マイクロメートル以下の第1塗膜層と、
前記第1塗膜層の表面に形成される厚さが100マイクロメートル以上1000マイクロメートル以下の第2塗膜層と、
を備える樹脂成形体。 - 前記第1塗膜層および前記第2塗膜層の少なくとも一方は、第1材料と前記第1材料と異なる第2材料とが混合して硬化した塗料を含む、
請求項1に記載の樹脂成形体。 - 前記第1材料がポリオールであり、前記第2材料がイソシアネートである、
請求項2に記載の樹脂成形体。 - 第1型と第2型とにより形成されるキャビティに樹脂材料を注入し、基材を形成する工程と、
前記第1型と前記第2型とを開き、前記基材と前記第1型との間に第1塗膜形成用材料を注入し、前記基材の表面に第1塗膜層を形成する第1塗膜工程と、
前記第1型と前記第2型とを再度開き、前記第1塗膜層と前記第1型との間に第2塗膜形成用材料を注入し、前記第1塗膜層の表面に第2塗膜層を形成する第2塗膜工程と、
を備える、樹脂成形体の製造方法。