WO2023153180A1 - 帯電防止フィルム - Google Patents
帯電防止フィルム Download PDFInfo
- Publication number
- WO2023153180A1 WO2023153180A1 PCT/JP2023/001766 JP2023001766W WO2023153180A1 WO 2023153180 A1 WO2023153180 A1 WO 2023153180A1 JP 2023001766 W JP2023001766 W JP 2023001766W WO 2023153180 A1 WO2023153180 A1 WO 2023153180A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- antistatic layer
- antistatic
- less
- polyester film
- Prior art date
Abstract
【課題】帯電防止層の膜厚が薄くても、加熱乾燥工程後でもヘイズの上昇を抑え、かつ表面抵抗率の低い帯電防止フィルムおよび保護フィルムを提供する。
【解決手段】 基材の少なくとも片面に帯電防止層を有する積層ポリエステルフィルムであって、帯電防止層は少なくとも、導電性高分子とメラミン系架橋剤を含み、メラミン系架橋剤が、イミノ型メチル化メラミン樹脂、メチロール型メチル化メラミン樹脂、フルエーテル型メチル化メラミン樹脂、またはイミノ・メチロール型メチル化メラミン樹脂のうち1つからなることを特徴とする積層ポリエステルフィルム:
Description
本発明は、帯電防止フィルムおよび帯電防止フィルムに粘着層を積層した保護フィルムに関するものであり、特に光学部材(例えば、有機ELや液晶ディスプレイの構成部材)などの保護フィルムに関するものである。
基材フィルムに粘着層を積層したフィルムは光学部材などの製造工程で各部材の保護フィルムとして使用されている。保護フィルムは、粘着層と介して被着体である各部材と貼り合わされ各部材の加工や搬送時にキズや汚れの付着を抑制する働きをしている。これら保護フィルムに用いられる基材フィルムには、少なくとも片面に帯電防止層を積層した帯電防止フィルムが用いられる。帯電防止層を積層する目的は、保護フィルムにゴミや埃などの異物の付着を防止することや保護フィルムを被着体から剥離するときに発生する静電気を抑制することにある。(特許文献1参照)
帯電防止フィルムとしては、帯電防止剤としてPEDOT:PSSを含む帯電防止フィルムが提案されている。(特許文献2参照)
帯電防止層を有する保護フィルムは、光学部材などの保護フィルムとして使用されるが、特にディスプレイの構成部材の加工工程で使用されている。近年は、有機ELディスプレイ(特にOLEDディスプレイ)の部材の加工工程でも使われることが多くなってきている。保護フィルムを光学部材に貼り合わせるために、保護フィルムの少なくとも片面には粘着層が設けられており、この粘着層を積層する工程には、加熱乾燥工程が含まれている。
例えば、このように保護フィルムに粘着層を積層する場合、加熱乾燥工程によりオリゴマーが析出、ヘイズが上昇しフィルム外観が悪化する場合があった。保護フィルムのヘイズ上昇に伴い、視認性が低下してしまうと、保護フィルムを被着体と貼り合わせた状態での外観検査が困難であり、課題となっていた。
本発明では上記、保護フィルムの課題に対し、帯電防止層の膜厚が薄くても、加熱乾燥工程後でもヘイズの上昇を抑え、かつ表面抵抗率の低い帯電防止フィルムおよび保護フィルムを提供する。
即ち、本発明は、以下の構成よりなる。
[1]基材の少なくとも片面に帯電防止層を有する積層ポリエステルフィルムであって、 前記帯電防止層は、導電性高分子とメラミン系架橋剤を少なくとも含み、前記メラミン系架橋剤が、イミノ型メチル化メラミン樹脂、メチロール型メチル化メラミン樹脂、フルエーテル型メチル化メラミン樹脂またはイミノ・メチロール型メチル化メラミン樹脂から選択される少なくとも1つを含む、積層ポリエステルフィルム。
[2]一態様において、前記メラミン系架橋剤の重量平均重合度が2.5以下である。
[3]一態様において、前記積層ポリエステルフィルムの140℃、10分加熱後のヘイズが、3%以下である。
[4]一態様において、前記帯電防止層の表面抵抗率が2~7[logΩ/□]である。
[5]一態様において、前記帯電防止層中にアセチレン系界面活性剤を含む。
[5]一態様において、ポリエステルフィルムの少なくとも片面に粘着層を積層した保護フィルム。
[1]基材の少なくとも片面に帯電防止層を有する積層ポリエステルフィルムであって、 前記帯電防止層は、導電性高分子とメラミン系架橋剤を少なくとも含み、前記メラミン系架橋剤が、イミノ型メチル化メラミン樹脂、メチロール型メチル化メラミン樹脂、フルエーテル型メチル化メラミン樹脂またはイミノ・メチロール型メチル化メラミン樹脂から選択される少なくとも1つを含む、積層ポリエステルフィルム。
[2]一態様において、前記メラミン系架橋剤の重量平均重合度が2.5以下である。
[3]一態様において、前記積層ポリエステルフィルムの140℃、10分加熱後のヘイズが、3%以下である。
[4]一態様において、前記帯電防止層の表面抵抗率が2~7[logΩ/□]である。
[5]一態様において、前記帯電防止層中にアセチレン系界面活性剤を含む。
[5]一態様において、ポリエステルフィルムの少なくとも片面に粘着層を積層した保護フィルム。
本発明によれば、ポリエステルフィルムの少なくとも片面にオリゴマーブロック性のある帯電防止層を積層した帯電防止フィルムを提供することで、本帯電防止フィルムに粘着層を積層した保護フィルムを被着体と貼り合わせた場合にも、外観検査が可能であり、剥離時に剥離帯電や異物付着を抑制した保護フィルムを提供することができる。
本発明の積層ポリエステルフィルム(単に、帯電防止フィルムと称する場合もある)は、ポリエステルフィルムの少なくとも片面に帯電防止層が積層されたものである。また、帯電防止フィルムの片面に粘着層を積層することもでき保護フィルムとして使用することができる。
例えば、本発明の積層ポリエステルフィルムは、粘着層積層工程で加熱乾燥する場合、保護フィルムのヘイズが上昇することを抑制でき、保護フィルムを被着体に貼り合わせ場合にも外観検査を行うことを可能にした。
例えば、本発明の積層ポリエステルフィルムは、粘着層積層工程で加熱乾燥する場合、保護フィルムのヘイズが上昇することを抑制でき、保護フィルムを被着体に貼り合わせ場合にも外観検査を行うことを可能にした。
以下、本発明について詳細に説明する。
(ポリエステルフィルム)
本発明で基材として用いるポリエステルフィルムは、主としてポリエステル樹脂より構成されるフィルムである。ここで、「主としてポリエステル樹脂より構成されるフィルム」とは、ポリエステル樹脂を50質量%以上含有する樹脂組成物から形成されるフィルムであり、他のポリマーとブレンドする場合は、ポリエステル樹脂が50質量%以上含有していることを意味し、他のモノマーが共重合されている場合は、ポリエステルの繰り返し構造単位を50モル%以上含有することを意味する。好ましくは、ポリエステルフィルムは、フィルムを構成する樹脂組成物中において、ポリエステル樹脂を90質量%以上、より好ましくは95質量%以上、更に好ましくは100質量%含有する。
本発明で基材として用いるポリエステルフィルムは、主としてポリエステル樹脂より構成されるフィルムである。ここで、「主としてポリエステル樹脂より構成されるフィルム」とは、ポリエステル樹脂を50質量%以上含有する樹脂組成物から形成されるフィルムであり、他のポリマーとブレンドする場合は、ポリエステル樹脂が50質量%以上含有していることを意味し、他のモノマーが共重合されている場合は、ポリエステルの繰り返し構造単位を50モル%以上含有することを意味する。好ましくは、ポリエステルフィルムは、フィルムを構成する樹脂組成物中において、ポリエステル樹脂を90質量%以上、より好ましくは95質量%以上、更に好ましくは100質量%含有する。
ポリエステル樹脂としては、材料は特に限定されないが、ジカルボン酸成分とジオール成分とが重縮合して形成される共重合体、又は、そのブレンド樹脂を用いることができる。ジカルボン酸成分としては、例えば、テレフタル酸、イソフタル酸、オルトフタル酸、2,5-ナフタレンジカルボン酸、2,6-ナフタレンジカルボン酸、1,4-ナフタレンジカルボン酸、1,5-ナフタレンジカルボン酸、ジフェニルカルボン酸、ジフェノキシエタンジカルボン酸、ジフェニルスルホンカルボン酸、アントラセンジカルボン酸、1,3-シクロペンタンジカルボン酸、1,3-シクロヘキサンジカルボン酸、1,4-シクロヘキサンジカルボン酸、ヘキサヒドロテレフタル酸、ヘキサヒドロイソフタル酸、マロン酸、ジメチルマロン酸、コハク酸、3,3-ジエチルコハク酸、グルタル酸、2,2-ジメチルグルタル酸、アジピン酸、2-メチルアジピン酸、トリメチルアジピン酸、ピメリン酸、アゼライン酸、ダイマー酸、セバシン酸、スベリン酸、ドデカジカルボン酸等が挙げられる。
ポリエステル樹脂を構成するジオール成分としては、例えば、エチレングリコール、プロピレングリコール、ヘキサメチレングリコール、ネオペンチルグリコール、1,2-シクロヘキサンジメタノール、1,4-シクロヘキサンジメタノール、デカメチレングリコール、1,3-プロパンジオール、1,4-ブタンジオール、1,5-ペンタンジオール、1,6-ヘキサジオール、2,2-ビス(4-ヒドロキシフェニル)プロパン、ビス(4-ヒドロキシフェニル)スルホン等が挙げられる。
ポリエステル樹脂を構成するジカルボン酸成分とジオール成分はそれぞれ1種又は2種以上を用いても良い。また、トリメリット酸などのその他の酸成分やトリメチロールプロパンなどのその他の水酸基成分を適宜添加しても良い。
ポリエステル樹脂としては、具体的には、ポリエチレンテレフタレート、ポリプロピレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレートなどが挙げられ、これらの中でも物性とコストのバランスからポリエチレンテレフタレートが好ましい。
ポリエステルフィルムの滑り性、巻き性などのハンドリング性を改善するために、フィルム中に不活性粒子を含有させてもよいが、光学用途などに用いる場合、ポリエステルフィルム中には、実質的に粒子を含まないことが好ましい。ポリエステルフィルムに粒子を含まない場合は、インラインコートで設けるコート層中に粒子を含有することが好ましい。ポリエステルフィルムに粒子を含まず、コート層に粒子を含むことで透明性が向上し外観検査などを行いやすくなるため好ましい。
本発明に用いるポリエステルフィルムのヘイズは、3%以下であることが好ましい。より好ましくは2.5%以下であり、さらに好ましくは2.0%以下である。1.5%以下であれば、極めて好ましい。3%以下であれば、保護フィルムを被着体と貼り合わせた状態で外観検査などが可能なため好ましく、光学用途の部材が被着体の場合に特に好ましい。
本発明に用いるポリエステルフィルムの表面の領域表面平均粗さ(Sa)は、1~40nmの範囲にあることが好ましく、より好ましくは1~30nmである。さらに好ましくは1~10nmである。本発明に用いるポリエステルフィルムの表面の最大突起高さ(P)は、2μm以下であることが好ましく、より好ましくは1.5μm以下である。さらに好ましくは0.8μm以下である。Saが40nm以下であり、Pが2μm以下であれば、粘着層を積層しロール状に巻き取った際に粘着性の表面を荒らす恐れがなく好ましい。
本発明においてポリエステルフィルムの厚みは特に限定されないが、12~188μmの範囲であることが好ましい。18~125μmがより好ましく、25~100μmがさらに好ましい。12μm以上であると保護フィルムとして被着体と貼り合わせる際にシワが入るおそれが少なく、188μm以下であるとコスト的に有利である。
基材となるポリエステルフィルムは、単層であっても、2種以上の層が積層されたものであってもよい。また、本発明の効果を奏する範囲内であれば、必要に応じて、フィルム中に各種添加剤を含有させることができる。添加剤としては、例えば、酸化防止剤、耐光剤、ゲル化防止剤、有機湿潤剤、帯電防止剤、紫外線吸収剤、界面活性剤などが挙げられる。フィルムが積層構成を有する場合は、必要に応じて各層の機能に応じて添加剤を含有させることも好ましい。
ポリエステルフィルムは、例えば上記のポリエステル樹脂をフィルム状に溶融押出、キャスティングドラムで冷却固化させてフィルムを形成させる方法等によって得られる。本発明のポリエステルフィルムとしては、無延伸フィルム、延伸フィルムのいずれも用いることができるが、機械強度や耐薬品性といった耐久性の点からは延伸フィルムであることが好ましい。ポリエステルフィルムが延伸フィルムである場合、その延伸方法は特に限定されず、縦一軸延伸法、横一軸延伸法、縦横逐次二軸延伸法、縦横同時二軸延伸法等を採用することができる。
ポリエステルフィルムの表層には、密着向上層との密着性を向上させるため、アンカーコート層、コロナ処理、プラズマ処理、火炎処理などの表面処理を行うこともできる。アンカーコート層を設ける場合は、コストなどの観点からインラインコーティングで行うことが好ましい。
(帯電防止層)
本発明の帯電防止フィルムは、ポリエステルフィルムの少なくとも片面に帯電防止層を積層することが必要である。帯電防止層は片面だけでもよいし両面に積層してもよい。帯電防止層を積層することで、粘着層を積層し保護フィルムとして用いた場合にも被着体との剥離帯電を抑えたり、異物の付着を抑えることができるため好ましい。
本発明の帯電防止フィルムは、ポリエステルフィルムの少なくとも片面に帯電防止層を積層することが必要である。帯電防止層は片面だけでもよいし両面に積層してもよい。帯電防止層を積層することで、粘着層を積層し保護フィルムとして用いた場合にも被着体との剥離帯電を抑えたり、異物の付着を抑えることができるため好ましい。
帯電防止層は、導電性高分子とメラミン系架橋剤を含み硬化されてなる層である。このような組成物を、帯電防止層形成用組成物と称する場合がある。
帯電防止層の積層する手段については特に限定されず、塗布法、真空蒸着法、貼り合せなど、既知の方法を使用することができるが、帯電防止剤を含む塗液を塗布により設けることがコストの観点より好ましい。
(導電性高分子)
本発明における導電性高分子は、帯電防止性を付与できる高分子であり、カチオン性化合物などのイオン伝導を利用した高分子、π電子共役系導電性高分子などを用いることができる。低湿度下での帯電防止性の点からπ電子共役系導電性高分子を用いることが好ましい。また、π電子共役系導電性高分子は、空気中の水分に依存することなく帯電防止性能を高水準で維持することができるため、保護フィルムの様々な使用環境で良好な帯電防止性能を有するため好ましい。
また、本発明に係る導電性高分子の奏する効果を損なわない範囲で、帯電防止剤を併用できる。帯電防止剤としては、本発明における導電性高分子以外の、カチオン性化合物などのイオン伝導を利用した高分子、π電子共役系導電性高分子であってもよく、界面活性剤、酸化ケイ素化合物、導電性の金属化合物などを用いることができる。
本発明における導電性高分子は、帯電防止性を付与できる高分子であり、カチオン性化合物などのイオン伝導を利用した高分子、π電子共役系導電性高分子などを用いることができる。低湿度下での帯電防止性の点からπ電子共役系導電性高分子を用いることが好ましい。また、π電子共役系導電性高分子は、空気中の水分に依存することなく帯電防止性能を高水準で維持することができるため、保護フィルムの様々な使用環境で良好な帯電防止性能を有するため好ましい。
また、本発明に係る導電性高分子の奏する効果を損なわない範囲で、帯電防止剤を併用できる。帯電防止剤としては、本発明における導電性高分子以外の、カチオン性化合物などのイオン伝導を利用した高分子、π電子共役系導電性高分子であってもよく、界面活性剤、酸化ケイ素化合物、導電性の金属化合物などを用いることができる。
π電子共役系導電性高分子としては、アニリンあるいはその誘導体を構成単位として含むアニリン系高分子、ピロールあるいはその誘導体を構成単位として含むピロール系高分子、アセチレンあるいはその誘導体を構成単位として含むアセチレン系高分子、チオフェンあるいはその誘導体を構成単位として含むチオフェン系高分子等が挙げられる。高い透明性を得ようとするならば、π電子共役系導電性高分子としては窒素原子を有さないものが好ましく、中でもチオフェンあるいはその誘導体を構成単位として含むチオフェン系高分子は透明性の点から好適であり、特にポリアルキレンジオキシチオフェンが好適である。ポリアルキレンジオキシチオフェンとしては、ポリエチレンジオキシチオフェン、ポリプロピレンジオキシチオフェン、ポリ(エチレン/プロピレン)ジオキシチオフェンなどが挙げられる。
なお、チオフェンあるいはその誘導体を構成単位として含むチオフェン系高分子には、帯電防止性を更に良好なものとするためドーピング剤を、例えばチオフェンあるいはその誘導体を構成単位として含む高分子100質量部に対し0.1質量部以上500質量部以下配合することができる。多い場合には、電子移動が困難となるため帯電防止性能の低下の問題があり、逆に少ない場合には、溶媒に対する分散性低下の問題がある。このドーピング剤としては、LiCl、R1‐30COOLi(R1‐30:炭素数1以上30以下の飽和炭化水素基)、R1‐30SO3Li、R1‐30COONa、R1‐30SO3Na、R1‐30COOK、R1‐30SO3K、テトラエチルアンモニウム、I2、BF3Na、BF4Na、HClO4、CF3SO3H、FeCl3、テトラシアノキノリン(TCNQ)、Na2B10Cl10、フタロシアニン、ポルフィリン、グルタミン酸、アルキルスルホン酸塩、ポリスチレンスルホン酸Na(K、Li)塩、スチレン・スチレンスルホン酸Na(K、Li)塩共重合体、ポリスチレンスルホン酸アニオン、スチレンスルホン酸・スチレンスルホン酸アニオン共重合体等を挙げることができる。
本発明において帯電防止層中に含まれる導電性高分子は、帯電防止層における全固形分100質量%に対し、5質量%以上含まれることが好ましく、より好ましくは10質量%以上である。なお、帯電防止剤としてπ電子共役系導電性高分子を用いる場合において、前記ドーピング剤を用いる場合は、本願に規定するπ電子共役系導電性高分子の帯電防止層中の含有量には、導電性高分子と前記ドーピング剤の合計量のことである。
このような量で帯電防止剤を含むことで、良好な帯電防止性を付与できる。
このような量で帯電防止剤を含むことで、良好な帯電防止性を付与できる。
本発明において帯電防止層中に含まれる導電性高分子は、帯電防止層における全固形分100質量%に対し、50質量%以下であることが好ましく、より好ましくは40質量%以下である。なお、帯電防止剤としてπ電子共役系導電性高分子を用いる場合において、前記ドーピング剤を用いる場合は、本願に規定するπ電子共役系導電性高分子の帯電防止層中の含有量には、導電性高分子と前記ドーピング剤の合計量のことである。
このような量で帯電防止剤を含むことで、メラミン系架橋剤と相互作用を引き起こさず、塗液が凝集しにくく、帯電防止層の欠点が少なく高い透明性を保持できる。
このような量で帯電防止剤を含むことで、メラミン系架橋剤と相互作用を引き起こさず、塗液が凝集しにくく、帯電防止層の欠点が少なく高い透明性を保持できる。
(メラミン系架橋剤)
本発明において、帯電防止層に架橋構造を形成させるために、帯電防止層はメラミン系架橋剤が含まれて形成される。メラミン系架橋剤を含有させることにより、耐久性が向上し高温高湿度条件で処理した場合にも帯電防止性能の低下が抑制されるため好ましい。帯電防止層の架橋密度を高めるためには、メラミン系架橋剤の反応性を高めることが好ましい。反応性の高いメラミン系架橋剤について後述する。また、架橋反応を促進させるため、触媒等を必要に応じて適宜使用することができる。
本発明において、帯電防止層に架橋構造を形成させるために、帯電防止層はメラミン系架橋剤が含まれて形成される。メラミン系架橋剤を含有させることにより、耐久性が向上し高温高湿度条件で処理した場合にも帯電防止性能の低下が抑制されるため好ましい。帯電防止層の架橋密度を高めるためには、メラミン系架橋剤の反応性を高めることが好ましい。反応性の高いメラミン系架橋剤について後述する。また、架橋反応を促進させるため、触媒等を必要に応じて適宜使用することができる。
本発明における帯電防止層に用いるメラミン系架橋剤としては、一般的なものを使用でき特に限定されないが、メラミンとホルムアルデヒドを縮合して得られ、1分子中にトリアジン環、及びメチロール基及び/又はアルコキシメチル基をそれぞれ1つ以上有していることが好ましい。具体的には、メラミンとホルムアルデヒドを縮合して得られるメチロールメラミン誘導体に、低級アルコールとしてメチルアルコール、エチルアルコール、イソプロピルアルコール、ブチルアルコール等を脱水縮合反応させてエーテル化した化合物などが好ましい。メチロール化メラミン誘導体としては、例えばモノメチロールメラミン、ジメチロールメラミン、トリメチロールメラミン、テトラメチロールメラミン、ペンタメチロールメラミン、ヘキサメチロールメラミンを挙げることができる。1種類を用いても2種類以上も用いても構わない。
メラミン系架橋剤の反応性を高め、帯電防止層の架橋密度を高めるためには、1分子中により多くの架橋点をもつメチロール型メチル化メラミンやヘキサアルコキシメチルメラミンを用いることが好ましいが、反応性により優れるヘキサアルコキシメチルメラミンがより好ましく、特にヘキサメトキシメチルメラミンを用いることが好ましい。この時、ヘキサメチロールメラミンとは、下記式(a)中、Xがメチロール基(-CH2-OH)であるものである。ヘキサアルコキシメチルメラミンとは、メチロールメラミン誘導体にアルコールを用いて脱水縮合反応させたものであり、Xが(-CH2-OR、Rは炭素数1~4のアルキル基)であるものである。ヘキサメトキシメチルメラミンとは、Xが(-CH2-OMe)であるものである。
上記(a)中のXはそれぞれ同じであってもよいし、異なっていても良い。また上記Rは、それぞれ同じであっても良く、異なっていても良い。また、Xは(-H)でも良い。
本発明で用いるメラミン系架橋剤は、単一の化合物ではなく、複数の化合物の混合体であることが好ましい。メラミン系化合物中の主成分となる化合物の構造から、イミノ型(X=-H)、メチロール型(X=-CH2-OH)、フルエーテル型(X=-CH2-OR、Rは炭素数1~4のアルキル基)、イミノ・メチロール型に大別することができる。
一態様において、反応性の観点から、フルエーテル型、メチロール型を用いることが好ましく、フルエーテル型がより好ましく、フルエーテル型の中でもRがメチル基であるヘキサメトキシメチルメラミン(CAS番号3089-11-0)を用いることが最も好ましい。このヘキサメトキシメチルメラミンの含有率が高いメラミン系化合物を用いるほど、反応性が高く架橋密度の高い帯電防止層とすることができる。
一態様において、反応性の観点から、フルエーテル型、メチロール型を用いることが好ましく、フルエーテル型がより好ましく、フルエーテル型の中でもRがメチル基であるヘキサメトキシメチルメラミン(CAS番号3089-11-0)を用いることが最も好ましい。このヘキサメトキシメチルメラミンの含有率が高いメラミン系化合物を用いるほど、反応性が高く架橋密度の高い帯電防止層とすることができる。
本発明における帯電防止層に用いるメラミン系架橋剤において、重量平均重合度が2.5以下であることが好ましく、2.3以下であることがより好ましく、2.0以下であることが更に好ましい。重量平均重合度が2.5以下であると、導電性高分子との相溶性を良好にでき、また、塗液の凝集を抑制でき、欠点の少ないフィルムを形成できる。
更に、本発明においては、重量平均重合度が2.5以下であると、メラミン系架橋剤に含まれる単核体の含有量が多くなることで反応性に優れ、架橋密度が向上し、オリゴマーが析出しにくい帯電防止層とすることができるため好ましい。
例えば、重量平均重合度は1.1以上であってもよく、1.5を超えてもよい。
更に、本発明においては、重量平均重合度が2.5以下であると、メラミン系架橋剤に含まれる単核体の含有量が多くなることで反応性に優れ、架橋密度が向上し、オリゴマーが析出しにくい帯電防止層とすることができるため好ましい。
例えば、重量平均重合度は1.1以上であってもよく、1.5を超えてもよい。
メラミン系架橋剤はその合成過程において、イミノ基(-NH2-)を含有するものや、多核体が混入することがある。これらメラミン誘導体が混合していても、メラミン系架橋剤の重量平均重合度が上記範囲内であれば反応性に優れ、それぞれ好適に用いることができる。
本発明における帯電防止層には、メラミン系架橋剤が帯電防止層における全固形分100質量%に対して、50質量%以上95質量%以下含まれることが好ましく、より好ましくは55質量%以上95質量%以下であり、さらに好ましくは60質量%以上95質量%以下である。メラミン系化合物を50質量%以上含むことで帯電防止層がメラミン系化合物の自己架橋により、高い架橋密度を得ることができ、緻密な帯電防止層となるためオリゴマー析出を抑制でき、好ましい。このとき、帯電防止層の全固形分とは、溶媒や酸触媒は乾燥過程で相当部分蒸発してしまうため、実質的にメラミン系架橋剤と導電性高分子の固形分の合計した値とみなして差し支えない。
本発明における帯電防止層には、外観向上のために界面活性剤を用いてもかまわない。界面活性剤としては、特に限定されず、シリコーン系界面活性剤や、パーフルオロアルキル基を有するフッ素系界面活性剤、アセチレン系界面活性剤などの炭化水素系などを用いることができる。
特に、アセチレン系界面活性剤を含むことが望ましい。アセチレン系界面活性剤を含むことで、本帯電防止フィルムを保護フィルムとして用いた場合でも、保護した製品への移行を回避することができ、最終製品への悪影響を減らすことができる。
例えば、帯電防止層はバインダー樹脂を含んでもよい。バインダー樹脂は特に限定されないが、本発明の帯電防止層が有する機能を十分に発揮できるものが望ましい。
特に、アセチレン系界面活性剤を含むことが望ましい。アセチレン系界面活性剤を含むことで、本帯電防止フィルムを保護フィルムとして用いた場合でも、保護した製品への移行を回避することができ、最終製品への悪影響を減らすことができる。
例えば、帯電防止層はバインダー樹脂を含んでもよい。バインダー樹脂は特に限定されないが、本発明の帯電防止層が有する機能を十分に発揮できるものが望ましい。
本発明の帯電防止フィルムに粘着層を積層した保護フィルムは、光学部材などの製造工程で使用されるため、製造工程を汚染しないように、帯電防止層に用いても構わない界面活性剤としては、炭化水素系であるアセチレン系界面活性剤を用いることが好ましい。市販されているアセチレン系界面活性剤の例としては、サーフィノールシリーズやオルフィンシリーズ(日信化学工業社)が挙げられる。
帯電防止層には、前述のほか、本発明の目的を阻害しない範囲で必要に応じて、滑剤、色素、紫外線吸収剤、シランカップリング剤、等を混合しても良い。
帯電防止層には実質的にシリコーン化合物を含まない。
本発明において「シリコーン化合物を実質的に含有しない」とは、ケイ光X線分析でSi元素を定量した場合に50ppm以下であることにより定義され、好ましくは10ppm以下、最も好ましくは検出限界以下となる含有量である。「これは積極的に帯電防止層中にシリコーン成分を添加させなくても、外来異物由来のコンタミ成分や、原料樹脂あるいはフィルムの製造工程におけるラインや装置に付着した汚れが剥離して、帯電防止層中に混入する場合があるためである。
帯電防止層中には、実質的にシリコーン化合物を含まないことにより、本帯電防止フィルムを保護フィルムとして用いた場合でも、保護した製品へのシリコーンの移行を回避することができ、最終製品への悪影響を減らすことができる。
本発明において「シリコーン化合物を実質的に含有しない」とは、ケイ光X線分析でSi元素を定量した場合に50ppm以下であることにより定義され、好ましくは10ppm以下、最も好ましくは検出限界以下となる含有量である。「これは積極的に帯電防止層中にシリコーン成分を添加させなくても、外来異物由来のコンタミ成分や、原料樹脂あるいはフィルムの製造工程におけるラインや装置に付着した汚れが剥離して、帯電防止層中に混入する場合があるためである。
帯電防止層中には、実質的にシリコーン化合物を含まないことにより、本帯電防止フィルムを保護フィルムとして用いた場合でも、保護した製品へのシリコーンの移行を回避することができ、最終製品への悪影響を減らすことができる。
本発明の帯電防止層の膜厚は、0.005μm以上1μm以下が好ましい。より好ましくは、0.01μm以上0.5μm以下であり、さらに好ましくは、0.01μm以上0.2μm以下である。帯電防止層の膜厚が0.005μm以上であると、帯電防止効果が得られ好ましい。一方、1μm以下であると、着色が少なく透明性が高くなるため好ましい。
ここで、本発明の積層ポリエステルフィルムは、メラミン系架橋剤が、イミノ型メチル化メラミン樹脂、メチロール型メチル化メラミン樹脂、フルエーテル型メチル化メラミン樹脂またはイミノ・メチロール型メチル化メラミン樹脂から選択される少なくとも1つを含むことを特徴とする。これらいずれかのメラミン系架橋剤を含有することにより、本帯電防止層の架橋密度が高くなり、帯電防止層の膜厚が薄くても、加熱後でもヘイズ上昇が少なく、本帯電防止フィルムに粘着層を積層した保護フィルムを被着体と貼り合わせた場合にも、外観検査が可能であり、剥離時に剥離帯電や異物付着を抑制した保護フィルムを提供することができる。
本発明の積層ポリエステルフィルムのヘイズは、3.0%以下であることが好ましい。より好ましくは2.0%以下であり、さらに好ましくは1.5%以下である。1.0%以下であれば、極めて好ましい。3.0%以下であれば、保護フィルムを被着体と貼り合わせた状態で外観検査などが可能なため好ましく、光学用途の部材が被着体の場合に特に好ましい。ヘイズは0であってもよく、例えば、0.1%以上であってもよい。
本発明の積層ポリエステルフィルムの140℃、10分加熱後のヘイズは、3.0%以下であることが好ましい。より好ましくは2.7%以下であり、さらに好ましくは2.4%以下である。3.0%以下であれば、保護フィルムを被着体と貼り合わせた状態で外観検査などが可能なため好ましく、光学用途の部材が被着体の場合に特に好ましい。140℃、10分加熱後のヘイズは、0であってもよく、例えば、0.1%以上であってもよい。特定の理論に限定して解釈すべきではないが、本発明に係る帯電防止層を有することで、反応性に優れ、架橋密度が向上し、オリゴマーが析出しにくい帯電防止層を得ることができる。その結果、140℃、10分加熱後のヘイズの大幅な上昇を抑制できるものと推測される。
例えば、積層ポリエステルフィルムの140℃、10分加熱後のヘイズから、加熱前の積層ポリエステルフィルムのヘイズを差し引いたΔヘイズ値は、-0.2以上2.5以下であってよく、例えば、-0.2以上1.6以下であってもよい。Δヘイズ値がこのような範囲内であることにより、オリゴマーが析出しにくい帯電防止層を得ることができる。
オリゴマーが析出しにくい帯電防止層を形成することで、粘着層積層工程で加熱乾燥を経ても、保護フィルムの視認性は低下しにくく、保護フィルムを被着体に貼り合わせ場合にも外観検査を行うことができる、という効果を導くことができる。
オリゴマーが析出しにくい帯電防止層を形成することで、粘着層積層工程で加熱乾燥を経ても、保護フィルムの視認性は低下しにくく、保護フィルムを被着体に貼り合わせ場合にも外観検査を行うことができる、という効果を導くことができる。
本発明の帯電防止層の表面抵抗率は、7[logΩ/□]以下である。より好ましくは、6.5[logΩ/□]以下であり、さらに好ましくは、6[logΩ/□]以下である。表面抵抗率を7[logΩ/□]以下にすることで保護フィルムへの帯電を抑制することができ、工程中の異物付着を防ぐことができ、さらには保護フィルムの帯電が保護した製品への電気的な悪影響を抑えることができる。
また、帯電防止フィルムの表面抵抗率の下限は特に定めなくてもよいが、2[logΩ/□]以上であることが好ましい。帯電防止フィルムの表面抵抗率が2[logΩ/□]未満であると、帯電防止層の加工コストが増大してしまうため好ましくない。
本発明に用いる帯電防止フィルムの全光線透過率は、80%以上であることが好ましい。より好ましくは85%以上であり、さらに好ましくは88%以上である。90%以上であれば、極めて好ましい。80%以上であれば、保護フィルムを被着体と貼り合わせた状態で外観検査などが可能なため好ましく、光学用途の部材が被着体の場合に特に好ましい。
帯電防止層は、アルコールで拭き取り後でも表面抵抗率変化が1.3倍以下であることが好ましい。より好ましくは1.2倍以下であり、さらに好ましくは1.1倍以下である。1.3倍以下であれば、粘着加工などの工程でアルコールを使用しても、保護フィルムになったときに初期の表面抵抗率を維持するため好ましい。
帯電防止層の表面の領域表面平均粗さ(Sa)は、1~40nmの範囲にあることが好ましく、より好ましくは1~30nmである。さらに好ましくは1~10nmである。本発明に用いる帯電防止フィルムの表面の最大突起高さ(P)は、2μm以下であることが好ましく、より好ましくは1.5μm以下である。さらに好ましくは0.8μm以下である。Saが40nm以下であり、Pが2μm以下であれば、粘着層を積層しロール状に巻き取った際に粘着性の表面を荒らす恐れがなく好ましい。
基材フィルム表面に帯電防止層を塗布積層する方法としては、前述の帯電防止剤やバインダー樹脂などを、溶媒に分散・溶解させた塗液をグラビアロールコーティング法、リバースロールコーティング法、ナイフコータ法、ディップコート法、バーコート法、スピンコート法などで塗布する方法があるが、導電性組成物に適したコート法は特に制限はない。また、フィルムの製造工程で塗布層を設けるインラインコート方式、フィルム製造後に塗布層を設けるオフラインコート方式により設けることができる。
帯電防止層は、前記方法で帯電防止層を形成する乾燥温度としては、通常60℃以上150℃以下であり、好ましくは90℃以上140℃以下である。この温度が60℃以上であると、短時間の処理でよく、生産性向上の観点から好ましい。また、架橋剤を含む場合は架橋反応が十分進行するため好ましい。一方、この温度が150℃以下であると、フィルムの平面性が保たれるため好ましい。
本発明の積層ポリエステルフィルムには、粘着剤を塗布し硬化させることで粘着層を積層することができる。粘着剤は、特に限定されず、使用することができ、得られた積層フィルムは、保護フィルムとして使用される。粘着層を積層する面は、帯電防止フィルムのどちらの側でも構わない。片面のみに帯電防止層を有する帯電防止フィルムを用いる場合は、帯電防止フィルムの粘着層を積層した面とは反対面には、帯電防止層がある方が好ましい。
また、本発明の積層ポリエステルフィルムにおける帯電防止層に、セラミックグリーンシート、樹脂フィルム等を積層してもよい。
また、本発明の積層ポリエステルフィルムにおける帯電防止層に、セラミックグリーンシート、樹脂フィルム等を積層してもよい。
本発明を詳細に説明するために、以下に実施例を挙げて説明するが、もちろん本発明はこれらの実施例に限定されるものではない。なお、本発明に用いた評価方法は以下の通りである。
(表面抵抗率)
本発明の帯電防止フィルム表面の表面抵抗率は、温度23℃、湿度55%の条件下で24時間調湿後、帯電防止層表面の表面抵抗率を簡易型低抵抗率計(日東精工アナリテック(株)製、ロレスタAX MCP-370)を用いて測定し、下記の判定基準で評価した。表面抵抗率が6[logΩ/□]を超える場合は、表面抵抗測定器(シムコジャパン(株)製、ワークサーフェイステスター ST-3)を用いて測定した。
◎:表面抵抗率が2以上4以下[logΩ/□]
○:表面抵抗率が4超7以下[logΩ/□]
△:表面抵抗率が7超[logΩ/□]
本発明の帯電防止フィルム表面の表面抵抗率は、温度23℃、湿度55%の条件下で24時間調湿後、帯電防止層表面の表面抵抗率を簡易型低抵抗率計(日東精工アナリテック(株)製、ロレスタAX MCP-370)を用いて測定し、下記の判定基準で評価した。表面抵抗率が6[logΩ/□]を超える場合は、表面抵抗測定器(シムコジャパン(株)製、ワークサーフェイステスター ST-3)を用いて測定した。
◎:表面抵抗率が2以上4以下[logΩ/□]
○:表面抵抗率が4超7以下[logΩ/□]
△:表面抵抗率が7超[logΩ/□]
(全光線透過率、ヘイズ)
本発明のフィルムの全光線透過率およびヘイズはJIS K 7136に準拠し、濁度計(日本電色製、NDH7000II)を用いて、140℃、10分加熱処理前後のフィルムを測定した。
本発明のフィルムの全光線透過率およびヘイズはJIS K 7136に準拠し、濁度計(日本電色製、NDH7000II)を用いて、140℃、10分加熱処理前後のフィルムを測定した。
(耐アルコール性)
エタノールを染み込ませたキムワイプを用いて、本発明のフィルムを10往復拭き取る処理前後の表面抵抗値を測定した。また、上記処理後の外観変化を下記の判定基準で評価した。
◎:ほとんど変化なし
〇:少し変化有り
△:変化有り
×:帯電防止層が染み落ちるほど変化あり
エタノールを染み込ませたキムワイプを用いて、本発明のフィルムを10往復拭き取る処理前後の表面抵抗値を測定した。また、上記処理後の外観変化を下記の判定基準で評価した。
◎:ほとんど変化なし
〇:少し変化有り
△:変化有り
×:帯電防止層が染み落ちるほど変化あり
(実施例1)
表2に記載の配合量で帯電防止層塗工液を得た。
(帯電防止層塗工液)
水 23.06質量部
イソプロピルアルコール 34.59質量部
導電性ポリマー 37.5質量部
架橋剤A(日本カーバイド工業社製、イミノ型メチル化メラミン樹脂、固形分濃度80質量%) 0.86質量部
導電助剤 3.0質量部
界面活性剤(日信化学工業社製、EXP.4200、固形分濃度75質量%) 0.53質量部
表2に記載の配合量で帯電防止層塗工液を得た。
(帯電防止層塗工液)
水 23.06質量部
イソプロピルアルコール 34.59質量部
導電性ポリマー 37.5質量部
架橋剤A(日本カーバイド工業社製、イミノ型メチル化メラミン樹脂、固形分濃度80質量%) 0.86質量部
導電助剤 3.0質量部
界面活性剤(日信化学工業社製、EXP.4200、固形分濃度75質量%) 0.53質量部
(帯電防止層の形成)
得られた帯電防止層塗工液を厚み75μmのA4360(コスモシャイン(登録商標)、東洋紡社製)の片面に、wet膜厚が7.5μmになるようにグラビアコーターを用いて塗工し、熱風乾燥炉で140℃30秒乾燥・硬化させて帯電防止層付きのポリエステルフィルムを得た。
得られた帯電防止層塗工液を厚み75μmのA4360(コスモシャイン(登録商標)、東洋紡社製)の片面に、wet膜厚が7.5μmになるようにグラビアコーターを用いて塗工し、熱風乾燥炉で140℃30秒乾燥・硬化させて帯電防止層付きのポリエステルフィルムを得た。
(実施例2)
組成を表2のものに変更した以外は、実施例1と同様の手順で帯電防止層を形成した。
組成を表2のものに変更した以外は、実施例1と同様の手順で帯電防止層を形成した。
(実施例3、4)
表2のような組成で架橋剤B(日本カーバイド工業社製、メチロール型メチル化メラミン樹脂、固形分濃度70質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤B(日本カーバイド工業社製、メチロール型メチル化メラミン樹脂、固形分濃度70質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
(実施例5、6)
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
(実施例7)
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)、界面活性剤をダイノール604(日信化学工業社製、固形分濃度100質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)、界面活性剤をダイノール604(日信化学工業社製、固形分濃度100質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
(実施例8)
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)、界面活性剤をサーフィノールSE-F(日信化学工業社製、固形分濃度81質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)、界面活性剤をサーフィノールSE-F(日信化学工業社製、固形分濃度81質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
(実施例9)
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)、界面活性剤を67additive(ダウ・東レ社製、固形分濃度100質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)、界面活性剤を67additive(ダウ・東レ社製、固形分濃度100質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
(実施例10、11)
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)、バインダー樹脂としてMD1200(東洋紡社製、固形分濃度35質量%)、界面活性剤をダイノール604にした以外は、実施例1と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤C(日本カーバイド工業社製、フルエーテル型メチル化メラミン樹脂、固形分濃度70質量%)、バインダー樹脂としてMD1200(東洋紡社製、固形分濃度35質量%)、界面活性剤をダイノール604にした以外は、実施例1と同様の手順で帯電防止層を形成した。
(実施例12)
表2のような組成で架橋剤D(日本カーバイド工業社製、イミノ・メチロール型メチル化メラミン樹脂、固形分濃度70質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤D(日本カーバイド工業社製、イミノ・メチロール型メチル化メラミン樹脂、固形分濃度70質量%)にした以外は、実施例1と同様の手順で帯電防止層を形成した。
(比較例2)
表2のような組成で架橋剤E(日清紡ケミカル社製、カルボジイミド、固形分濃度40質量%)にした以外は、実施例10と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤E(日清紡ケミカル社製、カルボジイミド、固形分濃度40質量%)にした以外は、実施例10と同様の手順で帯電防止層を形成した。
(比較例3)
表2のような組成で架橋剤F(Baxenden社製、ブロックイソシアネート、固形分濃度40質量%)にした以外は、実施例10と同様の手順で帯電防止層を形成した。
表2のような組成で架橋剤F(Baxenden社製、ブロックイソシアネート、固形分濃度40質量%)にした以外は、実施例10と同様の手順で帯電防止層を形成した。
今回開示された実施の形態および実施例はすべての点で例示であって、制限的なものではないと考えられるべきである。本発明の範囲は上記した実施の形態ではなく請求の範囲によって示され、請求の範囲と均等の意味、および範囲内でのすべての変更が含まれることが意図される。
実施例で得られた本発明の積層ポリエステルフィルムは、ポリエステルフィルムの少なくとも片面に加熱後もヘイズが低い帯電防止層を積層した帯電防止フィルムを提供することで、本帯電防止フィルムに粘着層を積層し保護フィルムとして用いた場合にも、外観検査が可能であり、剥離時に剥離帯電や異物付着を抑制した保護フィルムを提供することができる。
比較例1、2は、メラミン系架橋剤を含まないため、加熱後ヘイズが本発明の範囲から外れ、帯電防止層の反対面に粘着層を加工するときの加熱乾燥工程でオリゴマーがより析出するフィルムが得られた。
本発明は、帯電防止フィルムおよび帯電防止フィルムに粘着層を積層した粘着フィルムに関するものであり、特に光学部材(例えば、有機ELや液晶ディスプレイの構成部材)などの保護フィルム関する。
Claims (6)
- 基材の少なくとも片面に帯電防止層を有する積層ポリエステルフィルムであって、
前記帯電防止層は、導電性高分子とメラミン系架橋剤を含み、
前記メラミン系架橋剤が、イミノ型メチル化メラミン樹脂、メチロール型メチル化メラミン樹脂、フルエーテル型メチル化メラミン樹脂、またはイミノ・メチロール型メチル化メラミン樹脂から選択される少なくとも1つを含む、
積層ポリエステルフィルム。 - 前記メラミン系架橋剤の重量平均重合度が2.5以下である請求項1記載のポリエステルフィルム。
- 前記積層ポリエステルフィルムの140℃、10分加熱後のヘイズが3%以下である請求項1に記載のポリエステルフィルム。
- 帯電防止層の表面抵抗率が2~7[logΩ/□]である請求項1に記載のポリエステルフィルム。
- 帯電防止層中にアセチレン系界面活性剤を含む請求項1に記載のポリエステルフィルム。
- 請求項1~5の何れかに記載のポリエステルフィルムの少なくとも片面に粘着層を積層した保護フィルム。