WO2022044624A1 - Élément en aluminium pour collecteurs, condensateur au lithium-ion, condensateur à double couche électrique, batterie semi-solide, batterie à semi-conducteur et batterie secondaire utilisant une solution électrolytique non aqueuse - Google Patents

Élément en aluminium pour collecteurs, condensateur au lithium-ion, condensateur à double couche électrique, batterie semi-solide, batterie à semi-conducteur et batterie secondaire utilisant une solution électrolytique non aqueuse Download PDF

Info

Publication number
WO2022044624A1
WO2022044624A1 PCT/JP2021/027114 JP2021027114W WO2022044624A1 WO 2022044624 A1 WO2022044624 A1 WO 2022044624A1 JP 2021027114 W JP2021027114 W JP 2021027114W WO 2022044624 A1 WO2022044624 A1 WO 2022044624A1
Authority
WO
WIPO (PCT)
Prior art keywords
current collector
aluminum
oxide film
aluminum member
anodic oxide
Prior art date
Application number
PCT/JP2021/027114
Other languages
English (en)
Japanese (ja)
Inventor
宏和 澤田
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to JP2022545540A priority Critical patent/JPWO2022044624A1/ja
Priority to CN202180051856.XA priority patent/CN116097478A/zh
Publication of WO2022044624A1 publication Critical patent/WO2022044624A1/fr

Abstract

La présente invention aborde le problème consistant à fournir : un élément en aluminium pour des collecteurs, ledit élément en aluminium présentant une adhérence élevée à un matériau d'électrode, tout en ayant une faible résistance de contact par rapport au matériau d'électrode ; un condensateur au lithium-ion ; un condensateur électrique à double couche ; une batterie semi-solide ; une batterie à semi-conducteur ; et une batterie secondaire qui utilise une solution électrolytique non aqueuse. L'invention concerne également un élément en aluminium pour collecteurs, ledit élément en aluminium comprenant un substrat en aluminium et un revêtement d'oxyde anodique sur le substrat en aluminium. Par rapport à cet élément en aluminium pour collecteurs, le revêtement d'oxyde anodique a une pluralité de micropores ; le revêtement d'oxyde anodique est présent sur le substrat d'aluminium sous la forme d'un îlot ; la couverture de la surface du substrat en aluminium par le revêtement d'oxyde anodique est de 1 % à 80 % ; et la densité de nombre des micropores dans le revêtement d'oxyde anodique est supérieure ou égale à 600/μm2.
PCT/JP2021/027114 2020-08-25 2021-07-20 Élément en aluminium pour collecteurs, condensateur au lithium-ion, condensateur à double couche électrique, batterie semi-solide, batterie à semi-conducteur et batterie secondaire utilisant une solution électrolytique non aqueuse WO2022044624A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2022545540A JPWO2022044624A1 (fr) 2020-08-25 2021-07-20
CN202180051856.XA CN116097478A (zh) 2020-08-25 2021-07-20 集电体用铝部件以及锂离子电容器、双电层电容器、半固态电池、固态电池及使用非水电解液的二次电池

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-141506 2020-08-25
JP2020141506 2020-08-25

Publications (1)

Publication Number Publication Date
WO2022044624A1 true WO2022044624A1 (fr) 2022-03-03

Family

ID=80355083

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/027114 WO2022044624A1 (fr) 2020-08-25 2021-07-20 Élément en aluminium pour collecteurs, condensateur au lithium-ion, condensateur à double couche électrique, batterie semi-solide, batterie à semi-conducteur et batterie secondaire utilisant une solution électrolytique non aqueuse

Country Status (3)

Country Link
JP (1) JPWO2022044624A1 (fr)
CN (1) CN116097478A (fr)
WO (1) WO2022044624A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000243383A (ja) * 1999-02-22 2000-09-08 Toshiba Battery Co Ltd リチウム二次電池の製造方法
KR101195081B1 (ko) * 2011-04-29 2012-10-29 한국에너지기술연구원 고전기전도성, 고내구성을 갖는 탄소 코팅 알루미늄 집전체 및 그 제조방법
JP2012216513A (ja) * 2011-03-29 2012-11-08 Fujifilm Corp 集電体用アルミニウム基材、集電体、正極、負極および二次電池
JP2014211960A (ja) * 2013-04-17 2014-11-13 進和工業株式会社 集電体材料
JP2015053240A (ja) * 2013-09-09 2015-03-19 富士フイルム株式会社 集電体用アルミニウム基材、集電体、正極、負極および二次電池

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000243383A (ja) * 1999-02-22 2000-09-08 Toshiba Battery Co Ltd リチウム二次電池の製造方法
JP2012216513A (ja) * 2011-03-29 2012-11-08 Fujifilm Corp 集電体用アルミニウム基材、集電体、正極、負極および二次電池
KR101195081B1 (ko) * 2011-04-29 2012-10-29 한국에너지기술연구원 고전기전도성, 고내구성을 갖는 탄소 코팅 알루미늄 집전체 및 그 제조방법
JP2014211960A (ja) * 2013-04-17 2014-11-13 進和工業株式会社 集電体材料
JP2015053240A (ja) * 2013-09-09 2015-03-19 富士フイルム株式会社 集電体用アルミニウム基材、集電体、正極、負極および二次電池

Also Published As

Publication number Publication date
CN116097478A (zh) 2023-05-09
JPWO2022044624A1 (fr) 2022-03-03

Similar Documents

Publication Publication Date Title
JP4993258B2 (ja) リチウムイオン電池の集電体用アルミニウム箔及びそれを用いたリチウムイオン電池
JP5941210B1 (ja) リチウム電池用負極、リチウム電池、及びリチウム電池用負極の製造方法
JP3581784B2 (ja) 非水溶媒二次電池の負極集電体用銅箔
EP3202957B1 (fr) Plaque d'aluminium
JP6044546B2 (ja) 多孔アルミニウム箔の製造方法、多孔アルミニウム箔、蓄電デバイス用正極集電体、蓄電デバイス用電極、および、蓄電デバイス
JP2008103132A (ja) リチウムイオン電池の集電体用アルミニウム箔及びそれを用いたリチウムイオン電池
EP2639341A1 (fr) Procédé de production d'une feuille d'aluminium
US9514887B2 (en) Aluminum foil with carbonaceous particles dispersed and supported therein
US11527760B2 (en) Aluminum member for electrodes and method of producing aluminum member for electrodes
Nurpeissova et al. Synergistic effect of 3D current collector structure and Ni inactive matrix on the electrochemical performances of Sn-based anodes for lithium-ion batteries
JP6822629B2 (ja) 銅箔、その製造方法、それを含む電極、及びそれを含む二次電池
CN111225997B (zh) 铝箔及电极用铝部件
WO2022185778A1 (fr) Substrat d'aluminium pour collecteur, condensateur, cellule auxiliaire et procédé de fabrication de substrat d'aluminium pour collecteur
WO2022044624A1 (fr) Élément en aluminium pour collecteurs, condensateur au lithium-ion, condensateur à double couche électrique, batterie semi-solide, batterie à semi-conducteur et batterie secondaire utilisant une solution électrolytique non aqueuse
Chen et al. Tuning the structures and conductivity of nanoporous TiO2―TiO films through anodizing electrolytes as LIB anodes with ultra-high capacity and excellent cycling performance
KR102534518B1 (ko) 알루미늄박, 알루미늄박의 제조 방법, 집전체, 리튬 이온 커패시터, 및, 리튬 이온 배터리
JP4460055B2 (ja) リチウム２次電池電極用銅箔およびその製造方法、該銅箔を用いたリチウム２次電池用電極およびリチウム２次電池
JP2006228652A (ja) リチウム２次電池電極用銅箔およびその製造方法、該銅箔を用いたリチウム２次電池用電極およびリチウム２次電池
WO2021033537A1 (fr) Feuille d'aluminium

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21861053

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022545540

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21861053

Country of ref document: EP

Kind code of ref document: A1