WO2021193562A1 - 浸漬成形体 - Google Patents

浸漬成形体 Download PDF

Info

Publication number
WO2021193562A1
WO2021193562A1 PCT/JP2021/011779 JP2021011779W WO2021193562A1 WO 2021193562 A1 WO2021193562 A1 WO 2021193562A1 JP 2021011779 W JP2021011779 W JP 2021011779W WO 2021193562 A1 WO2021193562 A1 WO 2021193562A1
Authority
WO
WIPO (PCT)
Prior art keywords
chloroprene
polymerization
polymer block
latex
mass
Prior art date
Application number
PCT/JP2021/011779
Other languages
English (en)
French (fr)
Inventor
雄志 熊谷
渉 西野
斎藤　豊
小林　直紀
Original Assignee
デンカ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by デンカ株式会社 filed Critical デンカ株式会社
Priority to CN202180024554.3A priority Critical patent/CN115605523A/zh
Priority to US17/788,782 priority patent/US20230025987A1/en
Priority to JP2022510498A priority patent/JP7503129B2/ja
Priority to EP21776541.1A priority patent/EP4129609A4/en
Publication of WO2021193562A1 publication Critical patent/WO2021193562A1/ja

Abstract

加硫剤や加硫促進剤を使用しなくても、柔軟性、引張特性、及び耐熱老化性に優れ、また浸漬成形性良好なクロロプレン系ブロック共重合体ラテックスを用いた浸漬成形体を提供する。　単独重合時にガラス転移温度が８０℃以上の重合体が得られる単量体由来の重合体ブロック（Ａ）５～３０質量％と、クロロプレン単量体単位を含むクロロプレン系重合体ブロック（Ｂ）７０～９５質量％を含むクロロプレン系ブロック共重合体を含むラテックスを用いた浸漬成形体であり、前記浸漬成形体を１３０℃で３０分間熱処理した後にＪＩＳ　Ｋ　６２５１に準拠して測定した切断時引張強さが１７ＭＰａ以上である浸漬成形体。

Description

浸漬成形体
　本発明は、浸漬成形体に関するものである。
　ポリクロロプレンラテックスは、医療用手術手袋、検査手袋、工業手袋、風船、カテーテル、ゴム長靴などの浸漬成形品の材料として知られている。また、各種添加剤を配合することで塗料や粘着剤、接着剤として用いられている。
　浸漬成形製品用のポリクロロプレンに関する技術は種々提案されている。先行技術文献としては、クロロプレンと２，３－ジクロロ－１，３－ブタジエンとの共重合体ラテックス（例えば特許文献１参照）、クロロプレンとメタクリル酸を共重合させた変性ポリクロロプレンラテックス（例えば特許文献２参照）、加硫促進剤を含まないクロロプレン系重合体ラテックス（例えば特許文献３参照）、無機塩と酸化亜鉛を含む複合亜鉛華を含有するポリクロロプレンラテックス（例えば特許文献４参照）が知られている。
　また、クロロプレン系ブロック共重合体に関する技術としては、アゾ基を含有するポリスチレンを開始剤としてクロロプレンを重合して得られる共重合体（例えば特許文献５参照）や、ジチオカルバメート化したポリクロロプレンに芳香族ビニル単量体を重合させた共重合体（例えば特許文献６参照）、クロロプレン系ポリマーに親水性オリゴマー又は親水性ポリマーを連結させた共重合体（例えば特許文献７参照）、芳香族ビニル化合物重合体のブロックとクロロプレン系重合体のブロックを有し全体の数平均分子量とクロロプレン系重合体のブロックの数平均分子量を特定した共重合体（例えば特許文献８参照）、アクリル酸エステル重合体のブロックとクロロプレン系重合体のブロックを有する共重合体（例えば特許文献９参照）、さらに、加硫を用いずに、分子間を化学結合する方法として、特許文献１０記載の技術がある
国際公開２０１９／００９０３８号 特開２０１４－１１４３４２号公報 国際公開第２０１６／１６６９９８号 国際公開第２０１３／０１５０４３号 特開平３－２０７７１０号公報 特開平３－２１２４１４号公報 特開２００７－２９７５０２号公報 国際公開第２０１８／１８１８０１号 国際公開第２０１９／０２６９１４号 特開２０１４－２２１９０１号公報
　従来、ポリクロロプレン系ゴム組成物は目的とする機械的強度を得るために、硫黄、酸化亜鉛、酸化マグネシウム等の加硫剤、及びチウラム系、ジチオカルバミン酸塩系、チオウレア系、グアニジン系、キサントゲン酸塩系、チアゾール系等の加硫促進剤の使用が不可欠であった。加硫促進剤は皮膚炎等の皮膚疾患を発症させるＩＶ型アレルギーの原因物質であることから、加硫促進剤の削減や不使用化が重要なテーマとなっている。また、加硫促進剤の不使用化は、アレルギーの低減だけではなくコストダウンにも繋がることから、加硫促進剤を使用せずに十分な機械的強度を発現するゴム組成物が望まれている。
　そこで本発明は、加硫剤や加硫促進剤を使用しなくても、柔軟性、引張特性、及び耐熱老化性に優れ、また浸漬成形性良好なクロロプレン系ブロック共重合体ラテックスを用いた浸漬成形体を提供することを課題とする。
　本発明は、以下を要旨とするものである。
（１）単独重合時にガラス転移温度が８０℃以上の重合体が得られる単量体由来の重合体ブロック（Ａ）５～３０質量％と、クロロプレン単量体単位を含むクロロプレン系重合体ブロック（Ｂ）７０～９５質量％を含むクロロプレン系ブロック共重合体を含むラテックスを用いた浸漬成形体であり、
　前記浸漬成形体を１３０℃で３０分間熱処理した後にＪＩＳ　Ｋ　６２５１に準拠して測定した切断時引張強さが１７ＭＰａ以上である浸漬成形体。
（２）前記クロロプレン系ブロック共重合体１００質量％中に、前記重合体ブロック（Ａ）５～１５質量％と、前記クロロプレン系重合体ブロック（Ｂ）を８５～９５質量％を含むクロロプレン系ブロック共重合体を含むラテックスを用いた（１）に記載の浸漬成形体。
（３）クロロプレン系重合体ブロック（Ｂ）が、クロロプレン単量体単位及び多官能性単量体単位を有するクロロプレン系ブロック共重合体を含むラテックスを用いた（１）又は（２）に記載の浸漬成形体。
　本発明によれば、加硫剤や加硫促進剤を使用しなくても、柔軟性、引張特性、及び耐熱老化性に優れ、また浸漬成形性良好なクロロプレン系ブロック共重合体ラテックスを用いた浸漬成形体が提供される。
　以下、本発明の実施形態について詳細に説明する。なお、本明細書及び特許請求の範囲において、「Ａ～Ｂ」という記載は、Ａ以上でありＢ以下であるという意味である。
＜クロロプレン系ブロック共重合体ラテックス＞
　クロロプレン系ブロック共重合体ラテックスは、重合体ブロック（Ａ）５～３０質量％と、クロロプレン単量体単位を含むクロロプレン系重合体ブロック（Ｂ）７０～９５質量％を含むクロロプレン系ブロック共重合体を含むものである。
［重合体ブロック（Ａ）］
　重合体ブロック（Ａ）は、単独重合時にガラス転移温度が８０℃以上の重合体が得られる単量体由来の重合体ブロックである。このような単量体を用いることで、得られる浸漬成形被膜の切断時引張強さ、耐熱老化性が向上する。好ましくはガラス転移温度が８５℃以上の重合体が得られる単量体を用いるとよい。浸漬成形性の観点からは、ガラス転移温度が１５０℃以下の重合体が得られる単量体であれば好ましく、特に好ましくは１２０℃以下の重合体が得られる単量体である。ガラス転移温度は、例えば、８０、８５、９０、９５、１００、１０５、１１０、１２０、１３０、１４０、１５０℃であり、ここで例示した数値の何れか２つの間の範囲内であってもよい。なお、本明細書においてガラス転移温度とは、ＪＩＳ　Ｋ　７１２１に準拠して測定した補外ガラス転移終了温度（Ｔ　ｅｇ）である。重合体ブロック（Ａ）が、単量体（Ａ）を重合することで得られる重合体ブロックである場合、単量体（Ａ）は、単量体Ａを単独重合して、数平均分子量１００００～３００００のホモポリマー（Ａ）としたとき、該ホモポリマー（Ａ）が、上記ガラス転移温度を有する単量体であることが好ましい。
　重合体ブロック（Ａ）を構成する単量体単位としては、芳香族ビニル単量体単位、メタクリル酸メチル単量体単位、アクリロニトリル単量体単位が挙げられる。好ましくは芳香族ビニル単量体に由来する単位が用いられ、スチレン単位が好適に用いられる。重合体ブロック（Ａ）は、本発明の目的を損なわない範囲において、これら単量体同士の共重合により得られる重合体ブロック、またはこれら単量体と共重合可能な単量体に由来する単位からなる重合体ブロックであっても構わない。
　重合体ブロック（Ａ）の数平均分子量は、得られる浸漬成形被膜の引張特性、耐熱老化性、成形性の観点から、１０，０００以上であることが好ましい。重合体ブロック（Ａ）の数平均分子量は、例えば、１００００、１５０００、２００００、２５０００、３００００とすることができ、ここで例示した数値の何れか２つの間の範囲内であってもよい。なお、本明細書において、数平均分子量及び重量平均分子量とは、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）にて測定されるポリスチレン換算の値であり、以下記載の測定条件における測定値である。
　　装置名：ＨＬＣ－８３２０（東ソー社製）
　　カラム：ＴＳＫｇｅｌ　ＧＭＨＨＲ－Ｈを３本直列　　温度：４０℃
　　検出：示差屈折率
　　溶媒：テトラヒドロフラン
　　検量線：標準ポリスチレン（ＰＳ）を用いて作製した。
　重合体ブロック（Ａ）の分子量分布は、成形性の観点から、２．０以下であることが好ましい。重合体ブロック（Ａ）の分子量分布は、例えば、１．０、１．１、１．２、１．３、１．４、１．５、１．６、１．７、１．８、１．９、２．０とすることができ、ここで例示した数値の何れか２つの間の範囲内であってもよい。
［クロロプレン系重合体ブロック（Ｂ）］
　クロロプレン系重合体ブロック（Ｂ）は、クロロプレン単量体（２－クロロ－１，３－ブタジエン）単位を含み、クロロプレン単量体単位を主体とする。クロロプレン系重合体ブロック（Ｂ）は多官能性単量体単位を含んでいても構わない。なお、本発明の目的を損なわない範囲において、クロロプレン系重合体ブロック（Ｂ）は、クロロプレン単量体単位と、多官能性単量体単位と、これらと共重合可能な単量体に由来する単位からなる重合体ブロックであっても構わない。クロロプレン系重合体ブロック（Ｂ）は、クロロプレン系重合体ブロック（Ｂ）を１００質量％としたとき、クロロプレン単量体由来の構造単位を９０質量％以上含むことが好ましい。
　クロロプレン系重合体ブロック（Ｂ）中の各構造単位の含有量は、特に限定するものではないが、好ましくはクロロプレン単量体単位９０～９９．９５質量％、多官能性単量体単位０．０５～１０質量％である。クロロプレン系重合体ブロック（Ｂ）中の多官能性単量体単位の含有量は、例えば、０．０５、０．５０、１．００、２．００、３．００、４．００、５．００、６．００、７．００、８．００、９．００、１０．００質量％であり、ここで例示した数値の何れか２つの間の範囲内であってもよい。
［多官能性単量体］
　多官能性単量体は、得られる浸漬成形被膜の引張特性や耐熱老化性を向上させるために用いるものである。多官能性単量体は、分子中にラジカル性重合基を２個以上有する化合物である。得られる浸漬成形被膜の柔軟性、及び切断時引張強さ、及び浸漬成形性の観点から、化学式（１）で表される単量体、芳香族ポリエン単量体が好適に用いられる。化学式（１）で表される単量体としては、１．９－ノナンジオールジメタクリレート、１．９－ノナンジオールジアクリレート、ネオペンチルグリコールジメタクリレート、ネオペンチルグリコールジアクリレート、１．６－ヘキサンジオールジメタクリレート、１．６－ヘキサンジオールジアクリレート、エチレングリコールジメタクリレート、ジエチレングリコールジメタクリレート、トリエチレングリコールジメタクリレート、トリエチレングリコールジアクリレート、ポリエチレングリコールジメタクリレート、ポリエチレングリコールジアクリレートが特に好適に用いられる。芳香族ポリエン単量体としては、１０以上３０以下の炭素数を持ち、複数の二重結合（ビニル基）と単数又は複数の芳香族基を有した芳香族ポリエンであり、例えば、ｏ－ジビニルベンゼン、ｐ－ジビニルベンゼン、ｍ－ジビニルベンゼン、１，４－ジビニルナフタレン、３，４－ジビニルナフタレン、２，６－ジビニルナフタレン、１，２－ジビニル－３，４－ジメチルベンゼン、１，３－ジビニル－４，５，８－トリブチルナフタレン等、芳香族ポリエン単量体に由来する単位が挙げられ、好ましくはオルトジビニルベンゼン単位、パラジビニルベンゼン単位及びメタジビニルベンゼン単位のいずれか１種又は２種以上の混合物が好適に用いられる。
Figure JPOXMLDOC01-appb-C000001
 （式中、Ｒ１及びＲ２は水素、塩素、置換もしくは無置換のアルキル基、置換もしくは無置換のアルケニル基、置換もしくは無置換のアリール基、メルカプト基又は置換もしくは無置換のヘテロシクリル基を表す。Ｗ１は飽和もしくは不飽和炭化水素基、又は飽和もしくは不飽和環状炭化水素基、又はヘテロ原子を含む飽和もしくは不飽和炭化水素基、又はヘテロ原子を含む飽和、もしくは不飽和炭化水素基、をそれぞれ１つ以上含む構造を表す。Ｚ１は酸素、窒素、硫黄を表す。）
　クロロプレン系ブロック共重合体の各構造単位の含有量は、重合体ブロック（Ａ）５～３０質量％、クロロプレン系重合体ブロック（Ｂ）７０～９５質量％であり、好ましくは重合体ブロック（Ａ）５～１５質量％、クロロプレン系重合体ブロック（Ｂ）８５～９５質量％である。重合体ブロック（Ａ）が５質量％以上である場合に、得られる浸漬成形被膜の切断時引張強さ、耐熱老化性、及び浸漬成形性が向上する。重合体ブロック（Ａ）が３０質量％以下である場合に、得られる浸漬成形被膜の柔軟性が向上する。重合体ブロック（Ａ）は好ましくは１５質量％以下である。クロロプレン系重合体ブロック（Ｂ）が７０質量％以上である場合に、得られる浸漬成形被膜の柔軟性が向上する。クロロプレン系重合体ブロック（Ｂ）は、好ましくは８５質量％以上である。クロロプレン系重合体ブロック（Ｂ）が９５質量％以下である場合に、得られる浸漬成形被膜の切断時引張強さ、及び浸漬成形性が向上する。クロロプレン系ブロック共重合体を１００質量％としたとき、クロロプレン系ブロック共重合体に含まれる重合体ブロック（Ａ）の含有率は、例えば、５、１０、１５、２０、２５、３０質量％であり、ここで例示した数値の何れか２つの間の範囲内であってもよい。
　本発明の一実施形態に係るクロロプレン系ブロック共重合体は、重合体ブロック（Ａ）及び重合体ブロック（Ｂ）からなるものとすることができ、他の重合体ブロックを含まないものとすることができる。クロロプレン系ブロック共重合体は、重合体ブロック（Ａ）－重合体ブロック（Ｂ）のジブロック共重合体とすることができる。
　クロロプレン系ブロック共重合体の重量平均分子量は、特に制限はないが、浸漬成形性の観点から、好ましくは５～６０万であり、特に好ましくは１０～５０万である。
［浸漬成形体］
　本実施形態の浸漬成形体は、前述したクロロプレン系ブロック共重合体ラテックスを浸漬成形したものであり、モジュラスが低く柔軟でかつ切断時引張強さや切断時伸びなどの機械的特性に優れ、また耐熱老化性や浸漬成形性にも優れている。当該浸漬成形体としては、手袋、風船、及びカテーテルが好適である。本発明の一実施形態に係る浸漬成形体は、上記したクロロプレン系ブロック共重合体ラテックスを含む、クロロプレン系ブロック共重合体ラテックス組成物を成形することによって得ることもできる。なお、本発明の一実施形態に係る浸漬成形体は、一例として、実施例に記載の方法で得ることができる。
　本実施形態の浸漬成形体を製造する際の成型方法としては、例えば凝固液浸漬法が挙げられるが、これに限定されるものではなく、常法に従って成形すれば良い。
　本実施形態の浸漬成形体は、１３０℃で３０分間熱処理した後にＪＩＳ　Ｋ　６２５１に準拠して測定した切断時引張強さが１７ＭＰａ以上であり、加硫剤及び加硫促進剤を含まない未加硫浸漬成形体を与えうる。当該未加硫浸漬成形体は、柔軟性を備え、加硫剤及び加硫促進剤を含まずとも十分な機械的強度を発揮する。切断時引張強さは、１８ＭＰａ以上であることがより好ましく、１９ＭＰａ以上であることがさらにより好ましく、２０ＭＰａ以上であることがさらにより好ましい。上限は特に制限されないが、例えば、３０ＭＰａ以下である。本実施形態の浸漬成形体は、３０℃で３０分間熱処理した後、さらに、１００℃、２２時間の条件で熱老化試験を行った後にＪＩＳ　Ｋ　６２５１に準拠して測定した切断時引張強さが、１７ＭＰａ以上であることが好ましく、１８ＭＰａ以上であることがより好ましく、１９ＭＰａ以上であることがさらにより好ましく、２０ＭＰａ以上であることがさらにより好ましい。上限は特に制限されないが、例えば、３０ＭＰａ以下である。
　また、本実施形態の浸漬成形体は、１３０℃で３０分間熱処理した後にＪＩＳ　Ｋ　６２５１に準拠して測定した切断時伸びが９００％以上であることが好ましく、９０５％以上であることがより好ましく、９１０％以上であることがさらにより好ましい。上限は特に制限されないが、例えば、１３００％以下である。本実施形態の浸漬成形体は、３０℃で３０分間熱処理した後、さらに、１００℃、２２時間の条件で熱老化試験を行った後にＪＩＳ　Ｋ　６２５１に準拠して測定した切断時伸びが９００％以上であることが好ましく、９０５％以上であることがより好ましく、９１０％以上であることがさらにより好ましい。上限は特に制限されないが、例えば、１３００％以下である。
　本実施形態の浸漬成形体は、１３０℃で３０分間熱処理した後にＪＩＳ　Ｋ　６２５１に準拠して測定した５００％伸長時モジュラスが、３．０ＭＰａ以下であることが好ましく、２．９ＭＰａ以下であることがより好ましく、２．８ＭＰａ以下であることがさらにより好ましい。下限は特に制限されないが、例えば、１．０ＭＰａ以上である。本実施形態の浸漬成形体は、３０℃で３０分間熱処理した後、さらに、１００℃、２２時間の条件で熱老化試験を行った後に、ＪＩＳ　Ｋ　６２５１に準拠して測定した５００％伸長時モジュラスが３．０ＭＰａ以下であることが好ましく、２．９ＭＰａ以下であることがより好ましく、２．８ＭＰａ以下であることがさらにより好ましい。下限は特に制限されないが、例えば、１．０ＭＰａ以上である。
　なお、上記浸漬成形体は、実施例に記載の方法で得ることができ、浸漬成形体は、成形に際し、加硫剤及び加硫促進剤を用いないものとできる。
　浸漬成形体の切断時引張強さ、切断時伸び、５００％伸長時モジュラスを調整するには、クロロプレン系重合体ブロック（Ｂ）に含める多官能性単量体単位の含有量を調整したり、クロロプレン系ブロック共重合体中の当該クロロプレン系重合体ブロック（Ｂ）の含有量を調整したり、後述のＲＡＦＴ剤の存在下で重合することにより導入される官能基の種類や量を調整したりすればよい。
　本実施形態の浸漬成形体は、加硫剤又は加硫促進剤を含んでもよい。本発明の一実施形態に係る浸漬成形体が加硫剤及び／又は加硫促進剤を含む場合、該浸漬成形体を１００質量％としたとき、加硫剤及び加硫促進剤の合計含有率を５質量％以下とすることができ、１質量％以下とすることがより好ましく、０．１質量％とすることがより好ましい。しかしながら、上記未加硫浸漬成形体は、加硫剤及び加硫促進剤を含まずとも、十分な機械的強度を有しているため、アレルギーの低減及びコストダウンの観点から、加硫剤及び加硫促進剤を含まないものが好ましい。
　加硫剤としては、例えば、硫黄、酸化亜鉛、酸化マグネシウム等が挙げられる。
　加硫促進剤は、原料ゴムの加硫に際して、加硫剤と作用して加硫速度を増大させ加硫時間の短縮、加硫温度の低下、加硫剤の減量、加硫ゴムの物性向上を目的として添加する薬剤であり、通常は硫黄加硫反応を促進する薬剤を指す。
　クロロプレン系共重合体ラテックスの加硫に一般的に用いられる加硫促進剤としては、チウラム系、ジチオカルバミン酸塩系、チオウレア系、グアニジン系、キサントゲン酸塩系、チアゾール系等が挙げられ、これらは単独で又は必要に応じ２種以上組み合わせて用いられる。
　本実施形態の浸漬成形体は、加硫剤及び加硫促進剤の有無を問わず優れた機械的特性を発揮するが、アレルギー低減及びコストダウンの観点からは、加硫剤及び加硫促進剤を含まないものが好ましい。
　本実施形態の浸漬成形体に添加する老化防止剤として、通常のゴム用途に使用されている、ラジカルを捕捉して自動酸化を防止する一次老化防止剤と、ハイドロパーオキサイドを無害化する二次老化防止剤を添加することができる。それらの老化防止剤はラテックス組成物中のゴム成分１００質量部に対して、それぞれ０．１質量部以上１０質量部以下の割合で添加することができ、好ましくは２質量部以上５質量部以下の範囲である。これらの老化防止剤は単独使用のみならず２種以上を併用することも可能である。なお、一次老化防止剤の例としては、フェノール系老化防止剤、アミン系老化防止剤、アクリレート系老化防止剤、イミダゾール系老化防止剤、カルバミン酸金属塩、ワックスを挙げることができる。また、二次老化防止剤として、リン系老化防止剤、硫黄系老化防止剤、イミダゾール系老化防止剤などを挙げることができる。老化防止剤の例として特に限定するものではないが、Ｎ－フェニル－１－ナフチルアミン、アルキル化ジフェニルアミン、オクチル化ジフェニルアミン、４，４'－ビス（α，α－ジメチルベンジル）ジフェニルアミン、ｐ－（ｐ－トルエンスルホニルアミド）ジフェニルアミン、Ｎ，Ｎ'－ジ－２－ナフチル－ｐ－フェニレンジアミン、Ｎ，Ｎ'－ジフェニル－ｐ－フェニレンジアミン、Ｎ－フェニル－Ｎ'－イソプロピル－ｐ－フェニレンジアミン、Ｎ－フェニル－Ｎ'－（１，３－ジメチルブチル）－ｐ－フェニレンジアミン、Ｎ－フェニル－Ｎ'－（３－メタクリロイルオキシ－２－ヒドロキシプロピル）－ｐ－フェニレンジアミン、１，１，３－トリス－（２－メチル－４－ヒドロキシ－５－ｔ－ブチルフェニル）ブタン、４，４'－ブチリデンビス－（３－メチル－６－ｔ－ブチルフェノール）、２，２－チオビス（４－メチル－６－ｔ－ブチルフェノール）、７－オクタデシル－３－（４'－ヒドロキシ－３'，５'－ジ－ｔ－ブチルフェニル）プロピオネート、テトラキス－［メチレン－３－（３'，５'－ジ－ｔ－ブチル－４'－ヒドロキシフェニル）プロピオネート］メタン、ペンタエリスリトール－テトラキス［３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、トリエチレングリコール－ビス［３－（３－ｔ－ブチル－５－メチル－４－ヒドロキシフェニル）プロピオネート］、１，６－ヘキサンジオール－ビス［３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、２，４－ビス（ｎ－オクチルチオ）－６－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルアニリノ）－１，３，５－トリアジン、トリス－（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）－イソシアヌレート、２，２－チオ－ジエチレンビス［３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、Ｎ，Ｎ'－ヘキサメチレンビス（３，５－ジ－ｔ－ブチル－４－ヒドロキシ）－ヒドロシンナアミド、２，４－ビス［（オクチルチオ）メチル］－ｏ－クレゾール、３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル－ホスホネート－ジエチルエステル、テトラキス［メチレン（３，５－ジ－ｔ－ブチル－４－ヒドロキシヒドロシンナメイト）］メタン、オクタデシル－３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオン酸エステル及び３，９－ビス［２－｛３－（３－ｔ－ブチル－４－ヒドロキシ－５－メチルフェニル）プロピオニルオキシ｝－１，１－ジメチルエチル］－２，４，８，１０－テトラオキサスピロ［５．５］ウンデカン、トリス（ノニル・フェニル）フォスファイト、トリス（混合モノ－及びジ－ノニルフェニル）フォスファイト、ジフェニル・モノ（２－エチルヘキシル）フォスファイト、ジフェニル・モノトリデシル・フォスファイト、ジフェニル・イソデシル・フォスファイト、ジフェニル・イソオクチル・フォスファイト、ジフェニル・ノニルフェニル・フォスファイト、トリフェニルフォスファイト、トリス（トリデシル）フォスファイト、トリイソデシルフォスファイト、トリス（２－エチルヘキシル）フォスファイト、トリス（２，４－ジ－ｔ－ブチルフェニル）フォスファイト、テトラフェニルジプロピレングリコール・ジフォスファイト、テトラフェニルテトラ（トリデシル）ペンタエリスリトールテトラフォスファイト、１，１，３－トリス（２－メチル－４－ジ－トリデシルフォスファイト－５－ｔ－ブチルフェニル）ブタン、４，４'－ブチリデンビス－（３－メチル－６－ｔ－ブチル－ジ－トリデシルフォスファイト）、２，２'－エチリデンビス（４，６－ジ－ｔ－ブチルフェノール）フルオロフォスファイト、４，４'－イソプロピリデン－ジフェノールアルキル（Ｃ１２～Ｃ１５）フォスファイト、環状ネオペンタンテトライルビス（２，４－ジ－ｔ－ブチルフェニルフォスファイト）、環状ネオペンタンテトライルビス（２，６－ジ－ｔ－ブチル－４－フェニルフォスファイト）、環状ネオペンタンテトライルビス（ノニルフェニルフォスファイト）、ビス（ノニルフェニル）ペンタエリスリトールジフォスファイト、ジブチルハイドロゲンフォスファイト、ジステアリルペンタエリスリトール・ジフォスファイト及び水添ビスフェノールＡペンタエリスリトールフォスファイトポリマー、２－メルカプトベンゾイミダゾール、ｐ－クレソールとジシクロペンタジエンのブチル化反応生成物などが挙げられる。
［クロロプレン系ブロック共重合体ラテックスの製造方法］
　本発明に係るクロロプレン系ブロック共重合体ラテックスの製造方法について説明する。製造方法は、所望のクロロプレン系ブロック共重合体ラテックスが得られれば特に限定されないが、重合体ブロック（Ａ）を合成する重合工程１の後に、クロロプレン系重合体ブロック（Ｂ）を合成する重合工程２からなる二段階の重合工程を経てクロロプレン系ブロック共重合体ラテックスを得る製造方法により得ることが可能である。
（重合工程１）
　重合工程１について具体的に説明する。重合工程１では、重合体ブロック（Ａ）を構成する単量体をリビングラジカル重合して重合体ブロック（Ａ）を合成する。上記したように、ここで得られる重合体ブロック（Ａ）は、上記したガラス転移温度を有することが好ましい。重合で用いる乳化剤としては、特に限定されるものではないが、安定性の観点からアニオン系又はノニオン系の乳化剤が好ましい。特に得られるクロロプレン系ブロック共重合体ラテックスを用いた浸漬成形体に適当な強度を持たせて過度の収縮及び破損を防ぐことができるという理由から、ロジン酸アルカリ金属塩を使用することが好ましい。乳化剤の濃度は、重合反応を効率的に行う観点から、重合体ブロック（Ａ）を構成する単量体１００質量％に対して、５～５０質量％であることが好ましい。ラジカル重合開始剤としては、公知のラジカル重合開始剤を用いることができ、例えば過硫酸カリウム、過酸化ベンゾイル、過酸化水素、アゾ系化合物などを用いることができる。純水の添加量は、重合体ブロック（Ａ）を構成する単量体１００質量％に対して、１００～３００質量％が好ましい。純水の添加量が３００質量％以下である場合に、得られる浸漬成形被膜の切断時引張強さが向上する。重合温度は、単量体の種類に応じて適宜決定すればよいが、１０～１００℃が好ましく、２０～８０℃が特に好ましい。
（重合工程２）
　重合工程２では、上記重合工程１のリビングラジカル重合で得られた重合体ブロック（Ａ）を含むラテックスに対して、純水、乳化剤、クロロプレン単量体、及び多官能性単量体を添加して重合することでクロロプレン系ブロック共重合体ラテックスを得る。クロロプレン単量体は、一括添加でも分添でも構わない。重合工程２の重合温度は、重合制御のしやすさの観点から１０～５０℃であることが好ましい。重合反応は重合停止剤を加えることにより停止させる。重合停止剤としては、例えばチオジフェニルアミン、４－第３ブチルカテコール、２，２'－メチレンビス－４－メチル－６－第３－ブチルフェノール等がある。重合終了後の未反応単量体は、常法の減圧蒸留等の方法で除去することができる。
　重合工程２で得られたクロロプレン系ブロック共重合体ラテックスには、本発明の目的を損なわない範囲で、重合後に凍結安定剤、乳化安定剤、粘度調整剤、酸化防止剤、防腐剤などを任意に添加することができる。
　クロロプレン系ブロック共重合体は、下記化学式（２）又は化学式（３）で表される構造の官能基を有することが好ましい。
Figure JPOXMLDOC01-appb-C000002
 （化学式（２）中、Ｒ３は水素、塩素、置換もしくは無置換のアルキル基、置換もしくは無置換のアルケニル基、置換もしくは無置換のアリール基、メルカプト基又は置換もしくは無置換のヘテロシクリル基を表す。）
Figure JPOXMLDOC01-appb-C000003
　上記化学式（２）、又は化学式（３）で表される末端構造は、公知のＲＡＦＴ剤の存在下で重合を行うことで、ブロック共重合体に導入される。上記化学式（２）で表される構造を導く化合物は特に限定されるものではなく一般的な化合物を使用することができ、例えばジチオカルバメート類、ジチオエステル類が挙げられる。具体的にはベンジル１－ピロールカルボジチオエート（慣用名：ベンジル１－ピロールジチオカルバメート）、ベンジルフェニルカルボジチオエート、１－ベンジル－Ｎ，Ｎジメチル－４－アミノジチオベンゾエート、１－ベンジル－４－メトキシジチオベンゾエート、１－フェニルエチルイミダゾールカルボジチオエート（慣用名：１－フェニルエチルイミダゾールジチオカルバメート）、ベンジル－１－（２－ピロリジノン）カルボジチオエート）（慣用名：ベンジル－１－（２－ピロリジノン）ジチオカルバメート）、ベンジルフタルイミジルカルボジチオエート、（慣用名：ベンジルフタルイミジルジチオカルバメート）、２－シアノプロプ－２－イル－１－ピロールカルボジチオエート、（慣用名：２－シアノプロプ－２－イル－１－ピロールジチオカルバメート）、２－シアノブト－２－イル－１－ピロールカルボジチオエート、（慣用名：２－シアノブト－２－イル－１－ピロールジチオカルバメート）、ベンジル－１－イミダゾールカルボジチオエート、（慣用名ベンジル－１－イミダゾールジチオカルバメート）、２－シアノプロプ－２－イル－Ｎ，Ｎ－ジメチルジチオカルバメート、ベンジル－Ｎ，Ｎ－ジエチルジチオカルバメート、シアノメチル－１－（２－ピロリドン）ジチオカルバメート、２－(エトキシカルボニルベンジル)プロプ－２－イル－Ｎ，Ｎ－ジエチルジチオカルバメート、１－フェニルエチルジチオベンゾエート、２－フェニルプロプ－２－イルジチオベンゾエート、１－酢酸－１－イル－エチルジチオベンゾエート、１－（４－メトキシフェニル）エチルジチオベンゾエート、ベンジルジチオアセテート、エトキシカルボニルメチルジチオアセタート、２－（エトキシカルボニル）プロプ－２－イルジチオベンゾエート、２－シアノプロプ－２－イルジチオベンゾエート、ｔｅｒｔ－ブチルジチオベンゾエート、２，４，４－トリメチルペンタ－２－イルジチオベンゾエート、２－（４－クロロフェニル）－プロプ－２－イルジチオベンゾエート、３－ビニルベンジルジチオベンゾエート、４－ビニルベンジルジチオベンゾエート、ベンジルジエトキシホスフィニルジチオフォルマート、ｔｅｒｔ－ブチルトリチオペルベンゾエート、２－フェニルプロプ－２－イル－４－クロロジチオベンゾエート、ナフタレン－１－カルボン酸－１－メチル－１－フェニル－エチルエステル、４－シアノ－４－メチル－４－チオベンジルスルファニル酪酸、ジベンジルテトラチオテレフタラート、カルボキシメチルジチオベンゾエート、ジチオベンゾエート末端基を持つポリ（酸化エチレン）、４－シアノ－４－メチル－４－チオベンジルスルファニル酪酸末端基を持つポリ（酸化エチレン）、２－［（２－フェニルエタンチオイル）スルファニル］プロパン酸、２－［（２－フェニルエタンチオイル）スルファニル］コハク酸、３，５－ジメチル－１Ｈ－ピラゾール－１－カルボジチオエートカリウム、シアノメチル－３，５－ジメチル－１Ｈ－ピラゾール－１－カルボジチオエート、シアノメチルメチル－（フェニル）ジチオカルバメート、ベンジル－４－クロロジチオベンゾエート、フェニルメチル－４－クロロジチオベンゾエート、４－ニトロベンジル－４－クロロジチオベンゾエート、フェニルプロプ－２－イル－４－クロロジチオベンゾエート、１－シアノ－１－メチルエチル－４－クロロジチオベンゾエート、３－クロロ－２－ブテニル－４－クロロジチオベンゾエート、２－クロロ－２－ブテニルジチオベンゾエート、ベンジルジチオアセテート、３－クロロ－２－ブテニル－１Ｈ－ピロール－１－ジチオカルボン酸、２－シアノブタン－２－イル４－クロロ－３,５－ジメチル－１Ｈ－ピラゾール－１－カルボジチオエート、シアノメチルメチル（フェニル）カルバモジチオエートが挙げられる。これらのなかでも特に好ましくは、ベンジル１－ピロールカルボジチオエート、ベンジルフェニルカルボジチオエートが用いられる。上記化学式（３）で表される構造を導く化合物は、特に限定されるものではなく一般的な化合物を使用することができ、例えば、２－シアノ－２－プロピルドデシルトリチオカルボナート、ジベンジルトリチオカルボナート、ブチルベンジルトリチオカルボナート、２－［［（ブチルチオ）チオキソメチル］チオ］プロピオン酸、２－［［（ドデシルチオ）チオキソメチル］チオ］プロピオン酸、２－［［（ブチルチオ）チオキソメチル］チオ］コハク酸、２－［［（ドデシルチオ）チオキソメチル］チオ］コハク酸、２－［［（ドデシルチオ）チオキソメチル］チオ］－２－メチルプロピオン酸、２，２′－［カルボノチオイルビス（チオ）］ビス［２－メチルプロピオン酸］、２－アミノ－１－メチル－２－オキソエチルブチルトリチオカルボナート、ベンジル２－［（２－ヒドロキシエチル）アミノ］－１－メチル－２－オキソエチルトリチオカルボナート、３－［［［（ｔｅｒｔ－ブチル）チオ］チオキソメチル］チオ］プロピオン酸、シアノメチルドデシルトリチオカルボナート、ジエチルアミノベンジルトリチオカルボナート、ジブチルアミノベンジルトリチオカルボナートなどのトリチオカルボナート類が挙げられる。これらのなかでも特に好ましくは、ジベンジルトリチオカルボナート、ブチルベンジルトリチオカルボナートが用いられる。
　以下、実施例及び比較例をあげて本発明を説明するが、これらは何れも例示的なものであって本発明の内容を限定するものではない。
（実施例１）
（重合工程１）重合体ブロック（Ａ－１）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、スチレン単量体３５０ｇ、ブチルベンジルトリチオカルボナート６．０７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．８２ｇを添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。
　サンプリングしたラテックスは、多量のメタノールに混合することで樹脂分を析出させ、濾過、乾燥して重合体ブロック（Ａ－１）のサンプルを得た。得られたサンプルより重合体ブロック（Ａ）の数平均分子量、分子量分布、及びガラス転移温度を分析により求めた。分析結果を表１に示す。なお、「数平均分子量」、「分子量分布」、「ガラス転移温度」の測定方法については後述する。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４４８０ｇ、及び１．９－ノナンジオールジメタクリレート９１．４ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。
　サンプリングしたラテックスは、多量のメタノールに混合することで樹脂分を析出させ、濾過、乾燥してクロロプレン系ブロック共重合体のサンプルを得た。得られたサンプルよりクロロプレン系ブロック共重合体の重合体ブロック（Ａ－１）とクロロプレン系重合体ブロック（Ｂ－１）の含有量（質量％）を分析により求めた。分析結果を表１に示す。なお、測定方法については後述する。
（実施例２）
（重合工程１）重合体ブロック（Ａ－２）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水３３３３ｇ、不均化ロジン酸カリウム（ハリマ化成社製）１６０ｇ、水酸化カリウム２６．０ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１３．３ｇ、スチレン単量体２５０ｇ、ブチルベンジルトリチオカルボナート４．３３ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）２．７３ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－２）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－２）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体５５８４ｇ、及び１．９－ノナンジオールジメタクリレート１１４．０ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－２）とクロロプレン系重合体ブロック（Ｂ－２）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例３）
（重合工程１）重合体ブロック（Ａ－３）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水５７３３ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２７５ｇ、水酸化カリウム４４．７ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）２２．９ｇ、スチレン単量体４３０ｇ、ブチルベンジルトリチオカルボナート７．４５ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）４．６９ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－３）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－３）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体３０９４ｇ、及び１．９－ノナンジオールジメタクリレート６３．１ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－３）とクロロプレン系重合体ブロック（Ｂ－３）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例４）
（重合工程１）重合体ブロック（Ａ－４）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、スチレン単量体３５０ｇ、ブチルベンジルトリチオカルボナート６．０７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．８２ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－４）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－４）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４４８０ｇ、及び１．９－ノナンジオールジアクリレート９１．４ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－４）とクロロプレン系重合体ブロック（Ｂ－４）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例５）
（重合工程１）重合体ブロック（Ａ－５）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、スチレン単量体３５０ｇ、ブチルベンジルトリチオカルボナート６．０７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．８２ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－５）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－５）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４４８０ｇ、及びエチレングリコールジアクリレートであるライトエステルＥＧ（共栄社化学社製）９１．４ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－５）とクロロプレン系重合体ブロック（Ｂ－５）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例６）
（重合工程１）重合体ブロック（Ａ－６）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、スチレン単量体３５０ｇ、ブチルベンジルトリチオカルボナート６．０７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．８２ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－６）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－６）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４４８０ｇ、及びジビニルベンゼン９３．３ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－６）とクロロプレン系重合体ブロック（Ｂ－６）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例７）
（重合工程１）重合体ブロック（Ａ－７）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水５４５０ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２６２ｇ、水酸化カリウム４２．５ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）２１．８ｇ、スチレン単量体２５００ｇ、ブチルベンジルトリチオカルボナート４３．３ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）２７．３ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－７）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－７）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水２７３２ｇ、不均化ロジン酸カリウム（ハリマ化成社製）１３１ｇ、水酸化カリウム２１．３ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１０．９ｇ、重合工程１で作製した重合体ブロック（Ａ－２）を含むラテックス７８３ｇを仕込み、内温４５℃にし窒素気流下にて２００ｒｐｍで攪拌した。その後クロロプレン単量体３０００ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－７）とクロロプレン系重合体ブロック（Ｂ－７）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例８）
（重合工程１）重合体ブロック（Ａ－８）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、スチレン単量体３５０ｇ、ブチルベンジルトリチオカルボナート６．０７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．８２ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－８）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－８）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４４８０ｇ、及びトリアリルイソシアヌレート９１．４ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－８）とクロロプレン系重合体ブロック（Ｂ－８）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例９）
（重合工程１）重合体ブロック（Ａ－９）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、スチレン単量体３５０ｇ、ブチルベンジルトリチオカルボナート６．０７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．８２ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－９）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－９）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４４８０ｇ、及びヒドロキシピバリン酸ネオペンチルグリコールアクリル酸付加物（共栄社化学社製）９１．４ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－９）とクロロプレン系重合体ブロック（Ｂ－９）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例１０）
（重合工程１）重合体ブロック（Ａ－１０）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、スチレン単量体３５０ｇ、ブチルベンジルトリチオカルボナート６．０７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．８２ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－１０）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１０）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４４８０ｇ、及びトリメチロールプロパントリアクリレート（共栄社化学社製）９１．４ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－１０）とクロロプレン系重合体ブロック（Ｂ－１０）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例１１）
（重合工程１）重合体ブロック（Ａ－１１）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水６６６７ｇ、不均化ロジン酸カリウム（ハリマ化成社製）３２０ｇ、水酸化カリウム５２．０ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）２６．７ｇ、スチレン単量体５００ｇ、ブチルベンジルトリチオカルボナート６．５０ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）４．０９ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－１１）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１１）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体１６０７ｇ、及び１．９－ノナンジオールジメタクリレート３２．８ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－１１）とクロロプレン系重合体ブロック（Ｂ－１１）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例１２）
（重合工程１）重合体ブロック（Ａ－１２）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水５４５０ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２６２ｇ、水酸化カリウム４２．５ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）２１．８ｇ、スチレン単量体２５００ｇ、ブチルベンジルトリチオカルボナート３２．５ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）２０．５ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－１２）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１２）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水１１８８ｇ、不均化ロジン酸カリウム（ハリマ化成社製）５７ｇ、水酸化カリウム９．３ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）４．８ｇ、重合工程１で作製した重合体ブロック（Ａ－１２）を含むラテックス３１４７ｇを仕込み、内温４５℃にし窒素気流下にて２００ｒｐｍで攪拌した。その後クロロプレン単量体３０００ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－１２）とクロロプレン系重合体ブロック（Ｂ－１２）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（実施例１３）
（重合工程１）重合体ブロック（Ａ－１３）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、メチルメタクリレート単量体３５０ｇ、ブチル－２－シアノイソプロピルトリチオカルボネート４．１４ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）２．８７ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－１３）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１３）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４４２４ｇ、及び１．９－ノナンジオールジメタクリレート９０．３ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－１３）とクロロプレン系重合体ブロック（Ｂ－１３）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（比較例１）
（重合工程１）重合体ブロック（Ａ－１４）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水３０６７ｇ、不均化ロジン酸カリウム（ハリマ化成社製）１４７ｇ、水酸化カリウム２３．９ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１２．３ｇ、スチレン単量体２３０ｇ、ブチルベンジルトリチオカルボナート３．９９ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）２．５１ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－１４）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１４）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体７２７８ｇ、及び１．９－ノナンジオールジメタクリレート１４８．５ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－１４）とクロロプレン系重合体ブロック（Ｂ－１４）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（比較例２）
（重合工程１）重合体ブロック（Ａ－１５）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水６６６７ｇ、不均化ロジン酸カリウム（ハリマ化成社製）３２０ｇ、水酸化カリウム５２．０ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）２６．７ｇ、スチレン単量体５００ｇ、ブチルベンジルトリチオカルボナート４．２７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）２．６９ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－１５）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１５）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体１６０７ｇ、及び１．９－ノナンジオールジメタクリレート３２．８ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－１５）とクロロプレン系重合体ブロック（Ｂ－１５）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（比較例３）
クロロプレン系重合体ブロック（Ｂ－１６）のみの共重合体の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水３６００ｇ、不均化ロジン酸カリウム（ハリマ化成社製）１７５ｇ、水酸化カリウム２８．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１６．０ｇ、クロロプレン単量体４０００ｇ、１．９－ノナンジオールジメタクリレート８１．６ｇ、ブチルベンジルトリチオカルボナート４．７２ｇを仕込み、内温４５℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）２．９６ｇ添加して重合を開始した。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。
（比較例４）
（重合工程１）重合体ブロック（Ａ－１７）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６１６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２０６ｇ、水酸化カリウム２．３ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）４６．２ｇ、スチレン単量体４６２ｇ、ブチルベンジルトリチオカルボナート９．２ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）６．０ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－１７）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１７）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体４１５４ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－１８）とクロロプレン系重合体ブロック（Ｂ－１７）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（比較例５）
（重合工程１）重合体ブロック（Ａ－１８）の合成
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６１６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２０６ｇ、水酸化カリウム２．３ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）４６．２ｇ、スチレン単量体６９２ｇ、ブチルベンジルトリチオカルボナート９．２ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）６．０ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは重合工程２に使用した。重合体ブロック（Ａ－１９）の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表１に示す。
（重合工程２）クロロプレン系重合体ブロック（Ｂ－１８）の合成
　重合工程１の後、内温が４５℃まで下がったところで、クロロプレン単量体３９２４ｇを２時間かけてゆっくり添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。クロロプレン系ブロック共重合体の重合体ブロック（Ａ－１８）とクロロプレン系重合体ブロック（Ｂ－１８）の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表１に示す。
（比較例６）
トリブロック共重合体の合成
（第１ブロックの合成）
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６１３ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２０４．４ｇ、水酸化カリウム２．３ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）４６．１ｇ、スチレン単量体２３０ｇ、ベンジル１－ピロールカルボジチオエート９．２ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）６．０ｇ添加して重合を開始した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスは次の重合工程に使用した。第１ブロックの数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表２に示す。
（第２ブロックの合成）
　第１ブロックの合成の後、内温が４５℃まで下がったところで、クロロプレン単量体４４２４ｇを添加し重合を行った。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。得られたラテックスを用いて次の重合工程に使用した。
（第３ブロックの合成）
　第２ブロックの合成の後、内温を８０℃まで昇温にし、スチレン単量体２３０ｇを仕込み、重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）６．０ｇ添加して重合を開始した。重合を行った後、２５℃まで冷却し重合を停止した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。合成したトリブロック共重合体の第１ブロックと第３ブロックであるスチレンブロックと、第２ブロックであるクロロプレンブロックの含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表２に示す。
（比較例７）
重合体ブロック（Ａ）の単独重合体とクロロプレン系重合体ブロック（Ｂ）の単独重合体の混合物の作製
（重合体ブロック（Ａ）の単独重合体の合成）
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水４６６６ｇ、不均化ロジン酸カリウム（ハリマ化成社製）２２４ｇ、水酸化カリウム３６．４ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１８．７ｇ、スチレン単量体３５０ｇ、ブチルベンジルトリチオカルボナート６．０７ｇを仕込み、内温８０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．８２ｇを添加して重合を開始した。スチレン単量体の重合率９５％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させた。物性測定のために、得られたラテックスを２０ｍｌサンプリングした。重合体ブロック（Ａ）の単独重合体の数平均分子量、分子量分布、及びガラス転移温度を実施例１と同様に分析により求めた。分析結果を表３に示す。
（クロロプレン系重合体ブロック（Ｂ）の単独重合体の合成）
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水３９６０ｇ、不均化ロジン酸カリウム（ハリマ化成社製）１９３ｇ、水酸化カリウム３１．２ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１７．６ｇ、クロロプレン単量体４４００ｇ、１．９－ノナンジオールジメタクリレート８９．８ｇ、ブチルベンジルトリチオカルボナート５．１９ｇを仕込み、内温４５℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として２，２'－アゾビス［２－（２－イミダゾリン－２－イル）プロパン］２塩化水素（富士フイルム和光純薬社製、商品名：ＶＡ－０４４）３．２６ｇ添加して重合を開始した。クロロプレン単量体の重合率８０％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。
（重合体ブロック（Ａ）の単独重合体ラテックスとクロロプレン系重合体ブロック（Ｂ）の単独重合体ラテックスの混合）
　得られた重合体ブロック（Ａ）の単独重合体ラテックス４０００ｇとクロロプレン系重合体ブロック（Ｂ）の単独重合体のラテックス４０００ｇを容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブに仕込み、内温４５℃にして２００ｒｐｍで攪拌した。物性測定のために、得られたラテックスを２０ｍｌサンプリングし、残りのラテックスを用いて評価用のフィルム作製を行った。混合して得られるポリマー中の重合体ブロック（Ａ）の単独重合体とクロロプレン系重合体ブロック（Ｂ）の単独重合体の含有量（質量％）を実施例１と同様に分析により求めた。分析結果を表３に示す。
（比較例８）
　容量１０Ｌ、攪拌機及び加熱冷却用ジャケット付のオートクレーブを用いて重合を行った。純水３１５０ｇ、トール生ロジン（ハリマ化成社製）１６８ｇ、水酸化カリウム５２．５ｇ、β－ナフタレンスルホン酸ホルマリン縮合物のナトリウム塩（花王社製、商品名：デモールＮ）１７．５ｇ、クロロプレン単量体３３２５ｇ、２，３－ジクロロ－１，３－ブタジエン単量体１７５g、ドデシルメルカプタン１．０５gを仕込み、内温１０℃にし窒素気流下にて２００ｒｐｍで攪拌した。重合開始剤として過硫酸カリウム３．５ｇを添加して重合を開始した。重合転化率８９％となった時点で重合停止剤であるＮ，Ｎ－ジエチルヒドロキシルアミンの１０重量％水溶液を添加することで重合を停止させ、減圧蒸留により未反応のクロロプレン単量体を除去した。得られたラテックスを用いて評価用のフィルム作製を行った。
［分析］
（重合体ブロック（Ａ）の数平均分子量及び分子量分布測定）
　数平均分子量及び分子量分布は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）にて測定されるポリスチレン換算の値であり、下記記載の測定条件における測定値である。
　　装置名：ＨＬＣ－８３２０（東ソー社製）
　　カラム：ＴＳＫｇｅｌ　ＧＭＨＨＲ－Ｈを３本直列
　　温度：４０℃
　　検出：示差屈折率
　　溶媒：テトラヒドロフラン
　　検量線：標準ポリスチレン（ＰＳ）を用いて作製した。
（重合体ブロック（Ａ）のガラス転移温度）
　ガラス転移温度は、ＪＩＳ　Ｋ　７１２１に準拠して示差走査熱量計を用い、以下の方法で測定した。
　　装置名：ＤＳＣ１（Ｍｅｔｔｌｅｒ　Ｔｏｌｅｄｏ社製）
　　手順：５０ｍｌ／ｍｉｎの窒素気流下で、昇温速度１０℃／ｍｉｎで１２０℃まで昇温して、１０分間１２０℃に保った後、－６０℃まで冷却し、昇温速度１０℃／ｍｉｎで１２０℃まで昇温して得られたＤＳＣ曲線から、高温側のペースラインを低温側に延長した直線と、ピークの高温側の曲線にこう配が最大になるような点で引いた接線との交点の温度をガラス転移温度とした。
（クロロプレン系ブロック共重合体の重合体ブロック（Ａ）とクロロプレン系重合体ブロック（Ｂ）の含有量測定）
　熱分解ガスクロマトグラムと１Ｈ－ＮＭＲを用い、以下の方法で測定した。
　熱分解ガスクロマトグラム 装置名：ＨＰ５８９０－II
　カラム：ＤＢ－５　０．２５ｍｍφ×３０ｍ（膜厚１．０μｍ）
　カラム温度：５０℃（５ｍｉｎ）→１０℃／ｍｉｎ→１５０℃→２５℃／ｍｉｎ→３００℃
　注入口温度：２５０℃
　検出器温度：２８０℃
　検出器：ＦＩＤ
　１Ｈ－ＮＭＲ 装置名：ＪＮＭ－ＥＣＸ－４００（日本電子社製）
　手順：重合体ブロック（Ａ）と多官能性単量体単位を含まないクロロプレン系重合体ブロック（Ｂ）からなるクロロプレン系ブロック共重合体を熱分解ガスクロマトグラムで測定し、重合体ブロック（Ａ）由来のピークとクロロプレン系重合体ブロック（Ｂ）由来のピークの面積比と、１Ｈ－ＮＭＲを測定して得られたクロロプレン系ブロック共重合体中の重合体ブロック（Ａ）とクロロプレン系重合体ブロック（Ｂ）の含有量から検量線を作成した。サンプリングしたラテックスをメタノールに混合して析出したクロロプレン系ブロック共重合体のサンプルを熱分解ガスクロマトグラムで測定し、重合体ブロック（Ａ）由来のピークとクロロプレン系重合体ブロック（Ｂ）由来のピークの面積比から、上記で作成した検量線を用いてクロロプレン系ブロック共重合体中の重合体ブロック（Ａ）とクロロプレン系重合体ブロック（Ｂ）の含有量を求めた。
［引張試験用サンプルの作製］
（クロロプレン系ブロック共重合体を含むラテックスの調製）
　重合工程２で得られたラテックス中のクロロプレン系ブロック共重合体１００質量部（固形分換算）に対して、老化防止剤としてｐ－クレソールとジシクロペンタジエンのブチル化反応生成物（商品名「ノクラックＰＢＫ」、大内新興化学工業株式会社製）２質量部、ラウリル硫酸ナトリウム（商品名「エマール１０」、花王株式会社製）０．３質量部、及び水を加えて配合物の固形分濃度が３０質量％になるように調製し、陶器製ボールミルを用いて、２０℃で１６時間混合し、調製した。
（フィルムの作製）
　外径５０ｍｍの陶器製の筒を、水６２質量部、硝酸カリウム四水和物３５質量部、及び炭酸カルシウム３質量部を混合した凝固液に１秒間浸して取り出した。４分間乾燥させた後、上記で調製したラテックスに２分間浸した。その後４５℃の流水で１分間洗浄し、１３０℃で３０分間加熱して水分を除去し、引張試験用のフィルム（１４０×１５０ｍｍ、厚み：０．２ｍｍ）を作製した。
［引張特性の評価］
　作製したフィルムを、１３０℃で３０分間熱処理した後にＪＩＳ　Ｋ　６２５１に準拠して５００％伸長時モジュラス、切断時引張強さ破断強度及び切断時伸びを測定した。なお、５００％伸長時モジュラスは３．０ＭＰａ以下、切断時引張強さは１７ＭＰａ以上、切断時伸びは９００％以上を合格レベルとした。
［熱老化特性の評価］
　作製した浸漬成形被膜を強制循環型熱老化試験機内で１００℃、２２時間の条件で熱老化試験を行った後、ＪＩＳ　Ｋ　６２５１に準拠して５００％伸長時モジュラス、切断時引張強さ及び切断時伸びを測定した。５００％伸長時モジュラスは３．０ＭＰａ以下、切断時引張強さは１７ＭＰａ以上、切断時伸びは９００％以上を合格とした。
［浸漬成形性の評価］
　上記フィルムの作製と同様の方法でフィルムを作製し、外径５０ｍｍの陶器製の筒からフィルムを剥がす際の、剥がしやすさと剥がしたフィルムの外観から、以下の基準で浸漬成形性を評価した。
　３：陶器製の筒からフィルムを剥がしやすく、またフィルムの外観が良好である。
　２：陶器製の筒からフィルムを剥がしやすく、フィルムにやや皺がある。
　１：陶器製の筒からフィルムを剥がしにくく、フィルムにやや皺がある。
なお、２以上を合格レベルとした。
Figure JPOXMLDOC01-appb-T000004
Figure JPOXMLDOC01-appb-I000005
Figure JPOXMLDOC01-appb-T000006
Figure JPOXMLDOC01-appb-T000007
Figure JPOXMLDOC01-appb-T000008
　実施例１～１３については、いずれも加硫剤や加硫促進剤を使用しなくても、５００％伸長時モジュラス３．０ＭＰａ以下で柔軟性に優れ、切断時引張強さ１７ＭＰａ以上、切断時伸び９００％以上であり、引張特性に優れていた。また、熱老化試験後の５００％伸長時モジュラス３．０ＭＰａ以下で柔軟性に優れ、切断時引張強さ１７ＭＰａ以上、切断時伸び９００％以上であり、耐熱老化性にも優れ、また浸漬成形性にも優れていた。一方、比較例１～８については、柔軟性、引張特性、耐熱老化性、及び浸漬成形性のうちいずれかの物性において劣るものであった。
　本発明のクロロプレン系ブロック共重合体ラテックスから得られる浸漬成形体は、柔軟性、引張特性、耐熱老化性、浸漬成形性に優れており、手術用手袋、手袋、風船、カテーテルなどに好適に用いることができる。

Claims (3)

  1. 　単独重合時にガラス転移温度が８０℃以上の重合体が得られる単量体由来の重合体ブロック（Ａ）５～３０質量％と、クロロプレン単量体単位を含むクロロプレン系重合体ブロック（Ｂ）７０～９５質量％を含むクロロプレン系ブロック共重合体を含むラテックスを用いた浸漬成形体であり、
    　前記浸漬成形体を１３０℃で３０分間熱処理した後にＪＩＳ　Ｋ　６２５１に準拠して測定した切断時引張強さが１７ＭＰａ以上である浸漬成形体。
  2. 　前記クロロプレン系ブロック共重合体１００質量％中に、前記重合体ブロック（Ａ）５～１５質量％と、前記クロロプレン系重合体ブロック（Ｂ）を８５～９５質量％を含むクロロプレン系ブロック共重合体を含むラテックスを用いた請求項１に記載の浸漬成形体。
  3. 　クロロプレン系重合体ブロック（Ｂ）が、クロロプレン単量体単位及び多官能性単量体単位を有するクロロプレン系ブロック共重合体を含むラテックスを用いた請求項１又は２に記載の浸漬成形体。
PCT/JP2021/011779 2020-03-26 2021-03-22 浸漬成形体 WO2021193562A1 (ja)