WO2021066550A1 - 하이드록시기 함유 화합물을 이용한 폴리알킬알루미녹산 함유 용액의 정제방법 및 이를 이용한 촉매 조성물 - Google Patents

하이드록시기 함유 화합물을 이용한 폴리알킬알루미녹산 함유 용액의 정제방법 및 이를 이용한 촉매 조성물 Download PDF

Info

Publication number
WO2021066550A1
WO2021066550A1 PCT/KR2020/013380 KR2020013380W WO2021066550A1 WO 2021066550 A1 WO2021066550 A1 WO 2021066550A1 KR 2020013380 W KR2020013380 W KR 2020013380W WO 2021066550 A1 WO2021066550 A1 WO 2021066550A1
Authority
WO
WIPO (PCT)
Prior art keywords
aluminum
polyalkylaluminoxane
catalyst composition
compound
hydroxy group
Prior art date
Application number
PCT/KR2020/013380
Other languages
English (en)
French (fr)
Inventor
조윤희
서의령
김승효
정승환
김아림
한기원
한효정
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to CN202080058203.XA priority Critical patent/CN114269795B/zh
Priority to US17/634,721 priority patent/US20220275113A1/en
Priority to EP20871977.3A priority patent/EP4001314A4/en
Publication of WO2021066550A1 publication Critical patent/WO2021066550A1/ko

Abstract

본 발명은 하이드록시기 함유 화합물을 이용한 폴리알킬알루미녹산 함유 용액의 정제방법 및 이를 이용한 촉매 조성물의 제조방법, 상기 제조방법으로 제조된 촉매 조성물, 및 이를 이용한 올레핀 중합체의 제조방법에 관한 것이다.

Description

하이드록시기 함유 화합물을 이용한 폴리알킬알루미녹산 함유 용액의 정제방법 및 이를 이용한 촉매 조성물
관련 출원과의 상호 인용
본 출원은 2019년 9월 30일자 한국 특허 출원 2019-0121157에 기초한 우선권의 이익을 주장하며, 해당 한국 특허 출원들의 문헌에 개시된 모든 내용은 본 명세서의 일부로서 포함된다.
기술분야
본 발명은 하이드록시기 함유 화합물을 이용한 폴리알킬알루미녹산 함유 용액의 정제방법 및 이를 이용한 촉매 조성물의 제조방법, 상기 제조방법으로 제조된 촉매 조성물, 및 이를 이용한 올레핀 중합체의 제조방법에 관한 것이다.
알킬알루미늄의 부분 가수분해물인 폴리알킬알루미녹산 조성물은 올레핀 중합체의 제조 시 주촉매를 활성화하는 조촉매 또는 스캐빈저로 작용함이 널리 알려져 있다. 스캐빈저는 중합 반응기, 용매, 단량체 공급물 등에 존재하는 불순물과 반응하도록 촉매 시스템에 첨가되는 물질로서, 상기 불순물과의 반응을 통해 올레핀계 단량체의 중합 공정이 일어나는 동안 촉매의 피독을 방지하는 역할을 한다. 구체적으로, 스캐빈저는 트리알킬알루미늄, 알킬알루미녹산, 디알킬아연, 디알킬마그네슘 등 다양한 종류의 화합물이 사용되고 있으며, 상술한 바와 같이 폴리메틸알루미녹산, 폴리이소부틸알루미녹산 등을 예시로 들 수 있다.
스캐빈저의 일 예시 중 하나인 폴리알킬알루미녹산은 톨루엔 등의 탄화수소 용매에 용해한 용액 상태로서 시판되고 있으며, 필요 시 이를 구입하여 중합 반응에 사용하게 된다. 이 때, 시판되는 폴리알킬알루미녹산 용액에는 주성분인 폴리알킬알루미녹산 외에도 트리메틸아민(trimethylamine; TMA), 트리이소부틸알루미늄(triisobutylaluminum; Tibal) 등이 함께 포함되어 있게 되는데, 이를 그대로 중합 반응에 사용할 경우 TMA, Tibal 등은 주촉매로 작용하는 전이금속 화합물과 반응을 일으켜 전이금속 화합물의 촉매 활성을 저하시킴으로써 올레핀 중합체의 생성을 방해하거나, 중합 반응에 참여하여 사슬 이동제로 작용함으로써 고분자량의 올레핀 중합체를 제조할 수 없도록 한다.
시판되는 폴리알킬알루미녹산 용액 중 Tibal 등 불순물을 제거하는 종래의 방법으로서, 구입한 조성물 용액을 2,6-디-tert-부틸-4-메틸페놀(2,6-di-tert-butyl-4-methylphenol; BHT)과 반응시켜 Tibal의 알루미늄 원소에 상기 BHT를 결합시킴으로써, Tibal의 추가적인 반응을 방지하는 방법이 공지되어 있다.
그러나, 상기 반응을 통해 용액 중에 자유롭게 부유하는 Tibal 자체를 제거할 수는 있어도, Tibal과 BHT가 결합한 생성물 또한 폴리알킬알루미녹산 조성물을 이루는 탄화수소 용매에 가용성이기 때문에, 별도로 제거되지 않고 그 상태로서 중합 반응에 함께 참여하게 되므로, 이로 인한 또 다른 문제점이 발생할 수 있음이 예상된다.
이에, 극성 불순물을 스캐빈지하거나 촉매를 활성화하는 폴리알킬알루미녹산의 능력을 방해하지 않으면서도, 시판되는 폴리알킬알루미녹산 용액 내 존재하는 Tibal을 최대로 제거하여 올레핀계 단량체의 중합 반응시 전이금속 화합물의 촉매 활성을 개선하고, 또한 Tibal을 영구적으로 용액 내에서 제거함으로써 Tibal이 역반응으로 다시금 용액 내에 부유하는 문제점을 방지하는 방법의 개발이 필요한 실정이다.
[선행기술문헌]
[특허문헌]
KR 1996-0005169 B1
본 발명의 목적은 폴리알킬알루미녹산 함유 용액을 하이드록시기 함유 화합물과 반응시킨 후 여과하여 정제하고, 이를 전이금속 화합물과 혼합하여 촉매 조성물을 제조하는 방법을 제공하는 것이다.
본 발명의 다른 목적은 트리알킬알루미늄이 소량 함유된 폴리알킬알루미녹산 함유 용액을 이용한 촉매 조성물을 제공하는 것이다.
본 발명의 다른 목적은 상기 촉매 조성물을 이용한 올레핀 중합체의 제조방법을 제공하는 것이다.
본 발명은 (S1) 폴리알킬알루미녹산, 트리알킬알루미늄 및 탄화수소 용매를 포함하는 폴리알킬알루미녹산 함유 용액을 준비하는 단계; (S2) 상기 폴리알킬알루미녹산 함유 용액을 하이드록시기 함유 화합물과 반응시키는 단계; (S3) 상기 단계 (S2)의 반응 생성물을 여과하는 단계; 및 (S4) 상기 단계 (S3)의 여과물과 전이금속 화합물을 혼합하는 단계;를 포함하는 촉매 조성물의 제조방법을 제공한다.
또한, 본 발명은 폴리알킬알루미녹산, 트리알킬알루미늄 및 탄화수소 용매를 포함하는 폴리알킬알루미녹산 함유 용액; 및 전이금속 화합물;을 포함하고, 상기 트리알킬알루미늄은 폴리알킬알루미녹산 함유 용액 기준 4.3 몰% 이하인 촉매 조성물을 제공한다.
또한, 본 발명은 상기 촉매 조성물 존재 하에 올레핀계 단량체를 중합하는 단계;를 포함하는 올레핀 중합체의 제조방법을 제공한다.
본 발명의 방법에 따라 시판되는 폴리알킬알루미녹산 함유 용액을 정제하여 용액 내 존재하는 트리알킬알루미늄을 제거할 수 있고, 이를 촉매 조성물로 사용할 경우 상기 트리알킬알루미늄에 의해 중합 반응이 방해받는 것을 방지하고 주촉매 화합물의 활성을 최대로 높여 효율적으로 올레핀 중합체를 제조할 수 있는 효과가 있다.
또한, 본 발명의 촉매 조성물은 생성된 불용성 고체가 물리적으로 제거되었기 때문에 역반응이 일어나는 문제점을 우려할 필요가 없다. 또한, BHT와 같은 별도의 첨가제가 필요하지 않기 때문에 용액 내 트리알킬알루미늄만을 간편히 제거하고 별도의 잔류물이 남지 않아 순도 높은 올레핀 중합체를 얻을 수 있는 이점이 있다.
이하, 본 발명에 대한 이해를 돕기 위하여 본 발명을 더욱 상세하게 설명한다.
본 발명의 설명 및 청구범위에서 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여, 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.
[촉매 조성물의 제조방법]
본 발명의 촉매 조성물의 제조방법은 (S1) 폴리알킬알루미녹산, 트리알킬알루미늄 및 탄화수소 용매를 포함하는 폴리알킬알루미녹산 함유 용액을 준비하는 단계; (S2) 상기 폴리알킬알루미녹산 함유 용액을 하이드록시기 함유 화합물과 반응시키는 단계; (S3) 상기 단계 (S2)의 반응 생성물을 여과하는 단계; 및 (S4) 상기 단계 (S3)의 여과물과 전이금속 화합물을 혼합하는 단계;를 포함하는 것을 특징으로 한다.
단계 (S1)
상기 단계 (S1)은 폴리알킬알루미녹산, 트리알킬알루미늄 및 탄화수소 용매를 포함하는 폴리알킬알루미녹산 함유 용액을 준비하는 단계이다.
상기 폴리알킬알루미녹산 함유 용액의 준비는 수득 방법이나 경로에 관계 없이 모두 본 발명에 포함될 수 있으나, 구체적으로 시판되는 폴리알킬알루미녹산 함유 용액을 수득하여 준비하는 것을 의미할 수 있다. 현재 시판되어 상용화중인 폴리알킬알루미녹산은 모두 탄화수소 용매에 용해된 용액 상태로 판매되며, 일정 함량 이상의 트리알킬알루미늄이 함유되어 있어 중합 반응에 참여시 주촉매의 촉매 활성을 저하시키는 문제점이 나타나고 있는데, 본 발명은 단계 (S1)에서 준비한 폴리알킬알루미녹산 함유 용액에 포함된 트리알킬알루미늄을 효율적으로 제거함으로써 올레핀 중합체의 제조 시 더욱 유용하게 사용될 수 있도록 정제하는 것에 목적이 있다.
상기 폴리알킬알루미녹산은 촉매 조성물에서 스캐빈저, 조촉매 또는 둘 다의 역할을 수행하는 물질로서 첨가되는 것일 수 있다.
상기 폴리알킬알루미녹산은 폴리메틸알루미녹산, 폴리에틸알루미녹산, 폴리이소부틸알루미녹산 및 폴리부틸알루미녹산으로 이루어진 군에서 선택된 1종 이상일 수 있고, 예컨대 폴리이소부틸알루미녹산일 수 있으나, 이에 제한되지 않는다.
상기 트리알킬알루미늄은 트리메틸알루미늄, 트리에틸알루미늄, 트리이소부틸알루미늄, 트리프로필알루미늄, 트리부틸알루미늄, 디메틸클로로알루미늄, 트리이소프로필알루미늄, 트리-s-부틸알루미늄, 트리사이클로펜틸알루미늄, 트리펜틸알루미늄, 트리이소펜틸알루미늄, 트리헥실알루미늄, 트리옥틸알루미늄, 에틸디메틸알루미늄, 메틸디에틸알루미늄, 트리페닐알루미늄 및 트리-p-톨릴알루미늄으로 이루어진 군에서 선택된 1종 이상일 수 있고, 바람직하게는 트리이소부틸알루미늄일 수 있으나, 이에 제한되지 않는다.
상기 탄화수소 용매는 펜탄, 헥산, 헵탄, 노난, 데칸, 시클로헥산 및 이들의 이성질체 등을 포함하는 지방족 탄화수소 용매, 톨루엔, 벤젠, 크실렌 및 이들의 이성질체 등을 포함하는 방향족 탄화수소 용매로 이루어진 군에서 선택된 1종 이상있고, 바람직하게는 헥산일 수 있으나, 이에 제한되지 않는다.
바람직하게는, 상기 단계 (S1)은 폴리이소부틸알루미녹산, 트리이소부틸알루미늄 및 헥산을 포함하는 혼합 용액을 준비하는 단계일 수 있다.
상기 폴리알킬알루미녹산 함유 용액에 포함된 탄화수소 용매의 함량은 폴리알킬알루미녹산 함유 용액 기준 20 내지 99 중량%일 수 있다. 탄화수소 용매의 함량이 20 중량% 미만일 경우, 후술하는 바와 같이 폴리알킬알루미녹산 함유 용액과 하이드록시기 함유 화합물이 반응하여 생성된 불용성 고체가 서로 엉겨 붙어 교반이 잘 되지 않고, 이로 인해 폴리알킬알루미녹산 함유 용액 내 트리알킬알루미늄을 제거하려는 본 발명의 효과를 구현하기가 어려울 수 있으므로, 충분한 양의 탄화수소 용매가 필요한 것이다.
단계 (S2)
상기 단계 (S2)는 상기 폴리알킬알루미녹산 함유 용액을 하이드록시기 함유 화합물과 반응시키는 단계이다.
상기 폴리알킬알루미녹산 함유 용액과 하이드록시기 함유 화합물을 반응시키는 방법은, 단계 (S1)에서 준비한 폴리알킬알루미녹산 함유 용액에 하이드록시기 함유 화합물을 첨가하는, 예컨대 하이드록시기 함유 화합물을 슬러리 상태로 폴리알킬알루미녹산 함유 용액에 이동시키는 방법으로 이루어질 수 있다. 또한, 하이드록시기 함유 화합물에 폴리알킬알루미녹산 함유 용액을 투입하는 방식으로도 이루어질 수 있다. 폴리알킬알루미녹산 함유 용액과 하이드록시기 함유 화합물을 서로 접촉시켜 반응하게 할 수 있다면 각 물질의 혼합 순서나 속도 등에는 제한이 없으며 통상의 기술자가 적절히 조절하여 수행할 수 있다.
상기 단계 (S2)에서는, 폴리알킬알루미녹산 함유 용액과 하이드록시기 함유 화합물의 혼합 용액 내에서 트리알킬알루미늄과 하이드록시기 함유 화합물이 반응하여 고체 생성물이 제조되며, 이 고체 생성물은 상기 혼합 용액 내의 탄화수소 용매에 불용성일 수 있다.
상기 불용성 고체는 자연발화성 및 금수성 물질로 제3류 위험물로 분류되는 트리알킬알루미늄과 달리, 공기 중에서도 안정하여 연소되거나 가연성 물질을 발생시키지 않는 비위험성 물질이다. 본 발명의 제조방법에서는, 트리알킬알루미늄을 효율적으로 제거하였을 뿐만 아니라, 위험한 트리알킬알루미늄을 비위험성 물질로 변형시켰으므로, 트리알킬알루미늄 또는 알루미녹산을 그 자체로 물리적 분리하는 방법보다 더욱 바람직하다.
또한, 상기 하이드록시기 함유 화합물은 폴리알킬알루미녹산 함유 용액에 포함된 트리알킬알루미늄 1 당량 기준 100 당량 이하일 수 있다. 구체적으로, 상기 하이드록시기 함유 화합물은 폴리알킬알루미녹산 함유 용액에 포함된 트리알킬알루미늄 1 당량 기준 0.01 내지 100.00 당량일 수 있고, 0.01 당량 이상, 0.05 당량 이상, 0.10 당량 이상, 1.00 당량 이상, 100.00 당량, 50.00 당량 이하, 10.00 당량 이하로 사용할 수 있다.
상기 하이드록시기 함유 화합물이 0.01 당량 미만일 경우, 트리알킬알루미늄과의 반응이 충분히 일어나지 못하여 트리알킬알루미늄 제거 효과가 미미할 수 있고, 상기 하이드록시기 함유 화합물이 100 당량 초과일 경우, 하이드록시기 함유 화합물의 사용량만큼 트리알킬알루미늄의 제거 효율이 증가하는 것은 아니므로 경제성이 저하될 수 있고, 불용성 고체의 과도한 생성으로 인해 이들이 서로 엉겨붙어 교반 및 여과하는 것이 어려울 수 있다.
상기 하이드록시기 함유 화합물은 하이드록시기를 1개 이상 함유하는 화합물을 의미하고, 구체적으로 하이드록시기를 2개 이상 함유하는 탄소수 2 내지 60의 화합물, 바람직하게는 2개 이상의 하이드록시기를 함유하는 탄소수 2 내지 30의 화합물일 수 있다. 상기와 같이, 하이드록시기를 2개 이상 포함하는 하이드록시기 함유 화합물은 보다 효율적으로 트리알킬알루미늄과 반응할 수 있으므로 바람직하게 사용될 수 있다.
하이드록시기 함유 화합물이 헥산과 같은 유기용매에 대한 용해도가 떨어질 경우 트리알킬알루미늄과 결합한 물질이 고체화될 가능성이 높으므로, 본 발명의 효과가 더욱 우수하게 구현될 수 있다.
이 때 하이드록시기는 방향족 고리에 치환되어 있을 수 있고, 탄화수소 사슬에 결합되어 있을 수 있으며, 방향족 고리가 2개 이상일 경우 서로 다른 방향족 고리에 각각 치환되어 있거나 하나의 방향족 고리에 모두 치환되어 있을 수 있으나, 이에 제한되지 않는다.
상기 하이드록시기 함유 화합물의 구체적인 예시는 1,3,5-트리하이드록시벤젠, 네오펜틸글리콜, 나프탈렌-1,5-디올, 에틸렌글리콜, 비스페놀-A, 카테콜, 메틸하이드로퀴논 및 1,2,3-트리하이드록시벤젠으로 이루어진 군에서 선택된 1종 이상일 수 있으나, 이에 제한되지 않는다.
단계 (S3)
상기 단계 (S3)는 상기 단계 (S2)의 반응 생성물을 여과하는 단계로서, 앞선 단계 (S2)에서 트리알킬알루미늄과 하이드록시기 함유 화합물의 반응으로 생성된 불용성 고체를 여과막을 사용하여 여과함으로써 혼합 용액 내에서 제거하는 단계이다.
상기 여과는 기공 크기 0.1 내지 40.0 μm인 것을 사용할 수 있고, 구체적으로 0.10 μm 이상, 0.15 μm 이상, 0.20 μm 이상, 1.0 μm 이상, 5.0 μm 이상, 7.0 μm 이상, 40.0 μm 이하, 35.0 μm 이하, 30.0 μm 이하, 20.0 μm 이하, 15.0 μm 이하, 예컨대 10 μm의 여과막을 사용하여 수행되는 것일 수 있다.
상기 여과막의 기공 크기가 0.1 μm 미만일 경우, 트리알킬알루미늄과 하이드록시기 함유 화합물이 반응하여 생성된 불용성 고체가 여과막의 기공을 막게 되어 여과 효율이 저하되며 여과 시간이 길어지는 문제점이 나타날 수 있고, 상기 여과막의 기공 크기가 40.0 μm 초과일 경우, 상기 불용성 고체가 여과막을 통과해버려 이를 분리 및 제거하지 못하는 결과를 초래할 수 있다.
본 발명에서는 단계 (S2)에서 생성된 고체를 효율적으로 제거할 수 있는 범위 내의 기공 크기를 갖는 여과막을 적절히 선택하여 사용할 수 있고, 이를 통해 트리알킬알루미늄을 효과적으로 제거한 고순도의 폴리알킬알루미녹산 함유 용액을 수득할 수 있는 것이다.
상기 단계 (S3)는 단계 (S2)의 반응 생성물을 곧바로 여과할 수도 있고, 또는 단계 (S2)의 반응 생성물을 정치시켜 불용성 고체를 침전시킨 후, 상층액만을 회수하여 이를 여과하는 것일 수 있다. 상기와 같이 상층액만을 회수하여 이를 여과함으로써 1차적으로 불용성 고체를 다량 제거할 수 있고, 이를 통해 불용성 고체를 제거하는 효율성을 높일 수 있다.
이와 같이, 본 발명의 촉매 조성물의 제조방법은 상기 단계 (S1) 내지 (S3)를 통해 폴리알킬알루미녹산 함유 용액 내에 포함된 트리알킬알루미늄을 물리적으로 제거함으로써, 용액 내 트리알킬알루미늄을 4.3 몰% 이하이도록 감소시킬 수 있고, 반응 조건, 폴리알킬알루미녹산 및 트리알킬알루미늄의 종류, 여과막의 기공 크기 등에 따라 트리알킬알루미늄의 함량을 더욱 낮출 수도 있다.
단계 (S4)
상기 단계 (S4)는 상기 단계 (S3)의 여과물과 전이금속 화합물을 혼합하는 단계이다.
상술한 바와 같이, 본 발명에서는 단계 (S1) 내지 (S3)를 통해 폴리알킬알루미녹산의 상대적 함량은 높이고 트리알킬알루미늄 등 불순물 함량은 낮춘 용액을 수득하였다. 또한, 단계 (S4)를 통해 주촉매로서 작용하는 전이금속 화합물을 혼합하여 촉매 조성물을 제조하게 된다. 이와 같이 제조된 촉매 조성물에는 폴리알킬알루미녹산이 함유되어 있으며, 이는 스캐빈저 및/또는 조촉매로 사용됨과 동시에 트리알킬알루미늄에 의한 방해를 받지 않아 전이금속 화합물의 촉매 활성이 현저히 개선될 수 있다.
[촉매 조성물]
본 발명의 촉매 조성물은 폴리알킬알루미녹산, 트리알킬알루미늄 및 탄화수소 용매를 포함하는 폴리알킬알루미녹산 함유 용액; 및 전이금속 화합물;을 포함하고, 상기 트리알킬알루미늄은 폴리알킬알루미녹산 함유 용액 기준 4.3 몰% 이하인 것을 특징으로 한다.
상기 촉매 조성물은 본 발명의 제조방법을 통해 수득한 것일 수 있다. 상기 촉매 조성물은, 본 발명에 따라 폴리알킬알루미녹산 함유 용액 내 트리알킬알루미늄을 제거한 후 이를 전이금속 화합물과 혼합함으로써 제조된 것으로서, 폴리알킬알루미녹산 함유 용액에 포함된 트리알킬알루미늄이 4.3 몰% 이하의 낮은 함량이다.
상기 촉매 조성물은 전술한 바와 같이 폴리알킬알루미녹산 및 전이금속 화합물(주촉매 화합물)을 포함하고 있으며, 1종 이상의 조촉매 화합물을 추가로 포함할 수 있다. 이 때 촉매 조성물이란 전이금속 화합물, 조촉매 화합물 및 폴리알킬알루미녹산의 3성분이 동시에 또는 임의의 순서로 혼합됨으로써, 활성이 있는 조성물로 수득될 수 있는 상태를 의미한다.
상기 전이금속 화합물은 올레핀계 단량체의 중합 반응에서 촉매로서 작용할 수 있는 것으로 공지된 모든 화합물이 사용가능하다.
상기 조촉매는 하기 화학식 1 또는 2 중에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.
[화학식 1]
D(R1)3
상기 화학식 1에서,
D는 보론이고,
R1은 각각 독립적으로 할로겐 라디칼; 탄소수 1 내지 20의 하이드로카르빌 라디칼; 또는 할로겐으로 치환된 탄소수 1 내지 20의 하이드로카르빌 라디칼이고,
[화학식 2]
[L-H]+[Z(A)4]- 또는 [L]+[Z(A)4]-
상기 화학식 2에서,
L은 중성 또는 양이온성 루이스 산이고,
H는 수소 원자이고,
Z는 13족 원소이고,
A는 각각 독립적으로 1 이상의 수소 원자가 치환기로 치환될 수 있는 탄소수 6 내지 20의 아릴기; 또는 1 이상의 수소 원자가 치환기로 치환될 수 있는 탄소수 1 내지 20의 알킬기이고,
상기 A의 치환기는 할로겐 원자, 탄소수 1 내지 20의 하이드로카빌기, 탄소수 1 내지 20의 알콕시기 또는 탄소수 6 내지 20의 아릴옥시기이다.
상기 화학식 1로 표시되는 화합물은 트리메틸보론, 트리에틸보론, 트리이소부틸보론, 트리프로필보론, 트리부틸보론 등이 포함될 수 있으나, 이에 제한되지 않는다.
상기 화학식 2으로 표시되는 화합물의 예로는 트리메틸암모늄 테트라페닐보레이트, 트리에틸암모늄 테트라페닐보레이트, 트리프로필암모늄 테트라페닐보레이트, 트리부틸암모늄 테트라페닐보레이트, 트리메틸암모늄 테트라(p-톨릴)보레이트, 트리에틸암모늄 테트라(p-톨릴)보레이트, 트리프로필암모늄 테트라(p-톨릴)보레이트, 트리부틸암모늄 테트라(p-톨릴)보레이트, 트리메틸암모늄 테트라(o,p-디메틸페닐)보레이트, 트리에틸암모늄 테트라(o,p-디메틸페닐)보레이트, 트리프로필암모늄 테트라(o,p-디메틸페닐)보레이트, 트리부틸암모늄 테트라(p-톨릴)보레이트, 트리메틸암모늄 테트라(p-트리플루오로메틸페닐)보레이트, 트리에틸암모늄 테트라(p-트리플루오로메틸페닐)보레이트, 트리프로필암모늄 테트라(p-트리플루오로메틸페닐)보레이트, 트리부틸암모늄 테트라(p-트리플루오로메틸페닐)보레이트, 트리메틸암모늄 테트라(펜타플루오로페닐)보레이트, 트리에틸암모늄 테트라(펜타플루오로페닐)보레이트, 트리프로필암모늄 테트라(펜타플루오로페닐)보레이트, 트리부틸암모늄 테트라(펜타플루오로페닐)보레이트, N,N-디에틸아닐리늄 테트라페닐보레이트, N,N-디에틸아닐리늄 테트라(펜타플루오로페닐)보레이트, 디에틸암모늄 테트라(펜타플루오로페닐)보레이트, 트리메틸포스포늄 테트라페닐보레이트, 트리페닐포스포늄 테트라페닐보레이트, 트리페닐카보늄 테트라(p-트리플루오로메틸페닐)보레이트, 트리페닐카보늄 테트라(펜타플루오로페닐)보레이트, 트리메틸암모늄 테트라페닐알루미네이트, 트리에틸암모늄 테트라페닐알루미네이트, 트리프로필암모늄 테트라페닐알루미네이트, 트리부틸암모늄 테트라페닐알루미네이트, 트리메틸암모늄 테트라(p-톨릴)알루미네이트, 트리에틸암모늄 테트라(p-톨릴)알루미네이트, 트리프로필암모늄 테트라(p-톨릴)알루미네이트, 트리부틸암모늄 테트라(p-톨릴)알루미네이트, 트리메틸암모늄 테트라(o,p-디메틸페닐)알루미네이트, 트리에틸암모늄 테트라(o,p-디메틸페닐)알루미네이트, 트리프로필암모늄 테트라(o,p-디메틸페닐)알루미네이트, 트리부틸암모늄 테트라(p-톨릴)알루미네이트, 트리메틸암모늄 테트라(p-트리플루오로메틸페닐)알루미네이트, 트리에틸암모늄 테트라(p-트리플루오로메틸페닐)알루미네이트, 트리프로필암모늄 테트라(p-트리플루오로메틸페닐)알루미네이트, 트리부틸암모늄 테트라(p-트리플루오로메틸페닐)알루미네이트, 트리메틸암모늄 테트라(펜타플루오로페닐)알루미네이트, 트리에틸암모늄 테트라(펜타플루오로페닐)알루미네이트, 트리프로필암모늄 테트라(펜타플루오로페닐)알루미네이트, 트리부틸암모늄 테트라(펜타플루오로페닐)알루미네이트, N,N-디에틸아닐리늄 테트라페닐알루미네이트, N,N-디에틸아닐리늄 테트라(펜타플루오로페닐)알루미네이트, 디에틸암모늄 테트라(펜타플루오로페닐)알루미네이트 등이 있으나, 이에 제한되지 않는다.
상기 촉매 조성물은 전이금속 화합물과 상기 화학식 1로 표시되는 화합물을 접촉시켜 혼합물을 얻는 단계; 및 상기 혼합물에 화합물 2로 표시되는 화합물을 첨가하는 단계;를 포함하는 제조방법으로 제조된 것일 수 있다.
이 때, 상기 전이금속 화합물 기준 화학식 1로 표시되는 화합물의 몰비는 1 : 2 내지 1 : 5,000일 수 있고, 바람직하게는 1 : 10 내지 1 : 1,000, 보다 바람직하게는 1 : 20 내지 1 : 500일 수 있다.
상기 전이금속 화합물 기준 상기 화학식 1로 표시되는 화합물의 몰비가 1 : 2 미만일 경우에는 알킬화제의 양이 매우 작아 금속 화합물의 알킬화가 완전히 진행되지 못하는 문제가 있고, 1 : 5,000 초과인 경우에는 금속 화합물의 알킬화는 이루어지지만 남아있는 과량의 알킬화제와 상기 화학식 2으로 표시되는 화합물인 활성화제 간의 부반응으로 인하여 알킬화된 금속 화합물의 활성화가 완전히 이루어지지 못하는 문제가 있다.
또한, 상기 촉매 조성물은 전이금속 화합물과 상기 화학식 2로 표시되는 화합물을 접촉시키는 단계;를 포함하는 제조방법으로 제조된 것일 수 있다.
이 때, 상기 전이금속 화합물 기준 상기 화학식 2로 표시되는 화합물의 몰비는 1 : 1 내지 1 : 25일 수 있고, 바람직하게는 1 : 1 내지 1 : 10, 보다 바람직하게는 1 : 1 내지 1 : 5일 수 있다.
상기 전이금속 화합물 기준 상기 화학식 2로 표시되는 화합물의 몰비가 1 : 1 미만일 경우에는 활성화제의 양이 상대적으로 적어 금속 화합물의 활성화가 완전히 이루어지지 못해 생성되는 촉매 조성물의 활성도가 떨어지는 문제가 있고, 1 : 25 초과인 경우에는 전이금속 화합물의 활성화가 완전히 이루어지지만 남아 있는 과량의 활성화제로 촉매 조성물의 단가가 경제적으로 못하거나 생성되는 고분자의 순도가 떨어지는 문제가 있다.
상기 촉매 조성물의 제조 시에 반응 용매로서 펜탄, 헥산, 헵탄 등과 같은 탄화수소계 용매나, 벤젠, 톨루엔 등과 같은 방향족계 용매가 사용될 수 있으나, 반드시 이에 한정되지는 않으며 당해 기술 분야에서 사용 가능한 모든 용매가 사용될 수 있다.
상기 촉매 조성물 내에 포함된 폴리알킬알루미녹산 함유 용액은, 트리알킬알루미늄의 함량이 낮아 올레핀 중합체의 제조 시 스캐빈저 및/또는 조촉매로서 유용하게 활용될 수 있으므로, 본 발명에서 제공하는 촉매 조성물은 중합 반응을 촉진시키는 활성이 우수하여 이를 이용함으로써 좋은 수율로 올레핀 중합체를 제조할 수 있다.
뿐만 아니라, 트리알킬알루미늄을 고체 생성물로 전환하여 여과함으로써 폴리알킬알루미녹산 함유 용액으로부터 영구적으로 제거하였기 때문에, 역반응이 일어나 트리알킬알루미늄이 다시금 용액 내 존재하게 되는 등의 문제점이 전혀 발생할 우려가 없어 중합 반응의 안정성 및 예측성을 더욱 높일 수 있다.
[올레핀 중합체의 제조방법]
본 발명의 올레핀 중합체의 제조방법은 상기 촉매 조성물 존재 하에 올레핀계 단량체를 중합하는 단계;를 포함하는 것을 특징으로 한다.
상기 "중합체"란 동일 혹은 상이한 종류의 단량체들을 중합함으로써 제조된 중합체 화합물을 지칭한다. 이와 같이 해서 일반 용어 중합체는, 단지 1종의 단량체로부터 제조된 중합체를 지칭하는데 통상 이용되는 단독중합체란 용어, 및 이하에 규정된 바와 같은 혼성중합체(interpolymer)란 용어를 망라한다.
상기 올레핀계 단량체는 에틸렌, 프로필렌, 1-부텐, 1-펜텐, 4-메틸-1-펜텐, 1-헥센, 1-헵텐, 1-옥텐, 1-데센, 1-운데센, 1-도데센, 1-테트라데센, 1-헥사데센 및 1-에이코센으로 이루어진 군으로부터 선택된 1종 이상일 수 있으나, 이에 제한되지 않는다.
구체적으로, 본 발명의 올레핀 중합체는 올레핀계 단량체의 종류에 따라 올레핀 호모중합체일 수 있고, 올레핀/알파-올레핀 공중합체일 수 있으며, 바람직하게는 에틸렌/알파-올레핀 공중합체일 수 있다. 이 경우 공단량체인 알파-올레핀계 단량체의 함량은 올레핀 중합체의 용도, 목적 등에 따라 통상의 기술자가 적절히 선택할 수 있고, 약 1 내지 99 몰%일 수 있다.
상기 촉매 조성물을 이용한 가장 바람직한 중합체 제조 공정은 용액 공정이며, 또한 이러한 촉매 조성물을 실리카와 같은 무기 담체와 함께 사용하면 슬러리 또는 기상 공정에도 적용 가능하다.
상기 촉매 조성물은 올레핀계 단량체의 중합 공정에 적합한 탄소수 5 내지 12의 지방족 탄화수소 용매, 예를 들면 펜탄, 헥산, 헵탄, 노난, 데칸, 및 이들의 이성질체와 톨루엔, 벤젠과 같은 방향족 탄화수소 용매, 디클로로메탄, 클로로벤젠과 같은 염소원자로 치환된 탄화수소 용매 등에 용해하거나 희석하여 주입 가능하다. 여기에 사용되는 용매는 소량의 알킬알루미늄 처리함으로써 촉매 독으로 작용하는 소량의 물 또는 공기 등을 제거하여 사용하는 것이 바람직하며, 조촉매를 더 사용하여 실시하는 것도 가능하다.
실시예
이하, 실시예에 의하여 본 발명을 더욱 상세하게 설명하고자 한다. 그러나, 하기 실시예는 본 발명을 예시하기 위한 것으로 이들만으로 본 발명의 범위가 한정되는 것은 아니다.
[시약 준비]
폴리이소부틸알루미녹산(PBAO, Polyisobutylaluminoxane)은 Tosho社에서 구매하여 헥산(hexane)에 용해되어 있는 상태 그대로 사용하였다. Tosho社에서 구매한 폴리이소부틸알루미녹산 함유 용액은 트리이소부틸알루미늄을 4.4 몰% 포함하고 있다. 하이드록시기 함유 화합물은 각각 Aldrich社 또는 TCI社에서 구매하여 사용하였다.
[폴리이소부틸알루미녹산 함유 용액의 준비 및 정제]
실시 제조예 1
500 mL의 쉬렝크(schlenk) 플라스크에, 폴리이소부틸알루미녹산 함유 용액 내 포함되어 있는 트리이소부틸알루미늄 1 당량 기준 2.00 당량의 1,3,5-트리하이드록시벤젠을 투입하고, 3시간 동안 진공 건조하였다. 또 다른 500 mL 쉬렝크 플라스크에는, 상기 폴리이소부틸알루미녹산 함유 용액 175 g 및 헥산 175 g을 투입하여 준비하였다.
상기 폴리이소부틸알루미녹산 함유 용액 및 헥산이 담겨 있는 500 mL 쉬렝크 플라스크에, 상기에서 500 mL 쉬렝크 플라스크에 준비한 1,3,5-트리하이드록시벤젠을 30 mL 헥산을 사용하여 모두 슬러리 상태로 캐뉼라를 통해 이동시켰다.
이동 완료 후 12시간 동안 교반하고 정치시켜 고체 생성물을 형성하였으며, 이후 밤새 정치시켰다. 정치된 상태에서 상등액 부분을 조심스럽게 10.0 μm 기공 크기 필터를 이용하여 여과하였다.
실시 제조예 2 내지 11
하기 표 1과 같이 변경한 것을 제외하고는, 상기 실시 제조예 1과 동일하게 준비하였다.
비교 제조예 1
폴리알킬알루미녹산 함유 용액을 Tosho社에서 구매한 그대로 사용하였다.
하이드록시기 함유 화합물 트리이소부틸알루미늄 1 당량 기준 당량(eq) 기공 크기(μm)
실시 제조예 1 1,3,5-트리하이드록시벤젠 2.00 10.00
실시 제조예 2 1,3,5-트리하이드록시벤젠 0.05 10.00
실시 제조예 3 1,3,5-트리하이드록시벤젠 2.00 0.15
실시 제조예 4 1,3,5-트리하이드록시벤젠 3.00 35.00
실시 제조예 5 네오펜틸글리콜 4.00 10.00
실시 제조예 6 나프탈렌-1,5-디올 4.00 10.00
실시 제조예 7 에틸렌글리콜 6.60 10.00
실시 제조예 8 비스페놀-A 4.00 10.00
실시 제조예 9 카테콜 2.00 10.00
실시 제조예 10 메틸하이드로퀴논 4.00 10.00
실시 제조예 11 1,2,3-트리하이드록시벤젠 2.00 10.00
비교 제조예 1 - - 10.00
실험예 1
(1) 트리이소부틸알루미늄(mol%)
상기와 같이 여과하여 수득한 용액을 1H NMR로 THF deuterated solvent에 용해하여 잔여 트리이소부틸알루미늄의 함량을 측정하였다.
(2) 여과 시간(hr)
여과 투입물이 필터를 모두 통과하기까지의 시간을 측정하였다.
(3) 회수율(%)
회수율(%) = [여과 후 회수한 폴리이소부틸알루미녹산 함유 용액(g) / 반응물 상태인 폴리이소부틸알루미녹산 함유 용액(g)] × 100
트리이소부틸알루미늄(mol%) 여과 시간(hr) 회수율(%)
실시 제조예 1 < 0.1 0.1 94
실시 제조예 2 2.900 0.1 95
실시 제조예 3 < 0.1 24.0 90
실시 제조예 4 < 0.1 0.1 95
실시 제조예 5 < 0.1 0.1 90
실시 제조예 6 1.176 0.1 90
실시 제조예 7 0.137 0.1 90
실시 제조예 8 1.470 0.1 90
실시 제조예 9 < 0.1 0.1 90
실시 제조예 10 < 0.1 0.1 90
실시 제조예 11 0.176 0.1 90
비교 제조예 1 4.400 - -
상기 표 1에 나타낸 바와 같이, 본 발명에 따라 폴리알킬알루미녹산 함유 용액에 하이드록시기 함유 화합물을 반응시킨 후 이를 여과하여 제조한 실시 제조예 1 내지 11 모두, 트리이소부틸알루미늄이 크게 제거되어 잔류 트리이소부틸알루미늄의 함량이 비교 제조예 1에 비해 매우 낮은 것을 알 수 있다.
보다 구체적으로 실시예를 살펴보면, 1,3,5-트리하이드록시벤젠을 트리이소부틸알루미늄 기준 2.00 당량 사용하면서 기공 크기가 10.0 μm인 여과막을 사용한 실시 제조예 1의 경우, 짧은 시간 동안 트리이소부틸알루미늄을 선택적으로 제거하여, 여과 시간이 단축되고 회수율도 우수하였다.
한편, 트리이소부틸알루미늄을 0.05 당량 사용한 실시 제조예 2는 상대적으로 트리이소부틸알루미늄 제거 효과가 저하되었다.
또한, 기공 크기 0.15 μm인 여과막을 사용한 실시 제조예 3는 여과 시간이 늘어났고, 기공 크기 35.0 μm인 여과막을 사용한 실시 제조예 4의 경우 불용성 고체의 일부가 함께 여과된 것을 육안으로 관찰하였다.
[올레핀 중합체의 제조]
실시예 1
한국등록특허 10-0738694에 개시된 제조방법을 이용하여 하기 화학식 A의 전이금속 화합물을 준비하였다.
[화학식 A]
Figure PCTKR2020013380-appb-I000001
2L 오토클레이브 연속 공정 반응기에 헥산 용매(900 mL)와 1-옥텐(300 mL)을 채운 후, 반응기의 온도를 150 ℃로 예열하였다. 이어서 상기 오토클레이브 반응기 속으로 에틸렌을 투입하여 반응기의 압력을 35 bar로 맞춰주고, 상기 전이금속 화합물 1 μmol, 디메틸아닐리늄 테트라키스(펜타플루오로페닐)보레이트 조촉매 10 당량, 상기 제조예 1에서 제조한 폴리이소부틸알루미늄 함유 용액 1.5 mmol을 동시에 반응기로 투입하였다. 8분을 유지하며 공중합 반응을 연속 진행하여 공중합체를 제조하였다. 다음으로, 남은 에틸렌 가스를 빼내고, 수득된 공중합체 함유 용액에 과량의 에탄올을 가하여 침전을 유도하였다. 침전된 고분자를 에탄올로 2회 내지 3회 세척한 후, 90 ℃ 진공 오븐에서 12시간 이상 건조하여 공중합체를 수득하였다.
실시예 2
한국공개특허 10-2016-0019875에 개시된 제조방법을 이용하여 하기 화학식 B의 전이금속 화합물을 준비하였다.
[화학식 B]
Figure PCTKR2020013380-appb-I000002
전이금속 화합물로서 상기 화학식 B의 화합물을 사용한 것을 제외하고는, 상기 실시예 1과 동일한 방법으로 올레핀 중합체를 제조하였다.
비교예 1
제조예 1 대신 비교 제조예 1의 폴리알킬알루미녹산 함유 용액을 사용한 것을 제외하고는, 상기 실시예 1과 동일한 방법으로 올레핀 중합체를 제조하였다.
비교예 2
제조예 1 대신 비교 제조예 1의 폴리알킬알루미녹산 함유 용액을 사용한 것을 제외하고는, 상기 실시예 2와 동일한 방법으로 올레핀 중합체를 제조하였다.
상기 실시예 1 및 2, 비교예 1 및 2에서 사용한 전이금속 화합물, 폴리알킬알루미녹산 함유 용액의 종류를 정리하면 하기 표 2과 같다.
전이금속 화합물 폴리알킬알루미녹산 함유 용액
실시예 1 화학식 A 실시 제조예 1
실시예 2 화학식 B 실시 제조예 1
비교예 1 화학식 A 비교 제조예 1
비교예 2 화학식 B 비교 제조예 1
[올레핀 중합체의 물성 분석]
실험예 1
상기 실시예 및 비교예에서 제조한 각 중합체의 물성을 비교 분석하였다. 측정 조건 및 방법은 하기와 같으며, 측정 결과를 표 3에 정리하여 나타내었다.
(1) 촉매 활성도(activity, KgPE/mmol)
수득한 중합체를 중합 반응에 사용한 전이금속 화합물의 몰수로 나누어 촉매 활성도를 계산하였다.
(2) 용융 지수(Melt Index, MI2.16)
ASTM D-1238(조건 E, 190℃, 2.16 Kg 하중)로 측정하였다.
(3) 밀도(Density, g/cc)
ASTM D-792에 따라 샘플을 180 ℃ 프레스 몰드(Press Mold)로 두께 3 mm, 반지름 2 cm 의 시트를 제작하고 10 ℃/min으로 냉각하여 메틀러(Mettler) 저울에서 측정하였다.
(4) 용융 온도(Tm, ℃)
시차주사열량계(Differential Scanning Calorimeter, DSC, 장치명: DSC 2920, 제조사: TA instrument)를 이용하여 중합체의 용융 온도를 측정하였다. 구체적으로는 중합체를 150 ℃까지 가열한 후 5분 동안 유지하고, -100 ℃까지 온도를 내린 후 다시 온도를 증가시켰다. 이때 온도의 상승 속도와 하강속도는 각각 10 ℃/min으로 조절하였다. 용융 온도는 두 번째 온도가 상승하는 구간에서 측정한 흡열 피크의 최대 지점으로 하였다.
(5) 결정화 온도(Tc, ℃)
DSC를 이용하여 용융 온도 측정시와 동일한 방법으로 수행하고, 온도를 감소시키면서 나타나는 곡선으로부터 발열 피크의 최대 지점을 결정화 온도로 하였다.
촉매 활성도 (KgPE/mmol) MI2.16 밀도(g/cc) Tm(℃) Tc(℃)
실시예 1 70.5 0.23 0.895 93.3 76.9
실시예 2 123.0 0.67 0.860 42.9 23.7
비교예 1 20.35 0.009 0.893 92.4 74.6
비교예 2 32.0 0.57 0.856 40.5 20.3/40.4
상기 표 3의 결과에서 알 수 있는 바와 같이, 본 발명에 따라 제조한 촉매 조성물을 사용한 실시예 1 및 2의 경우, 전반적으로 비교예에 비해 촉매 활성도가 현저히 상승된 것을 알 수 있었다.
구체적으로, 전이금속 화합물의 종류가 동일한 실시예 1과 비교예 1, 실시예 2와 비교예 2을 각각 비교해보면, 전이금속 화합물은 동일하지만 폴리이소부틸알루미녹산 함유 용액을 하이드록시기 함유 화합물과 반응시켜 트리이소부틸알루미늄을 제거하여 사용한 실시예 1 및 2에서, 각각 비교예 1 및 2보다 3배 이상 높은 촉매 활성도를 나타나는 것으로 나타났다.
이와 같이, 본 발명의 제조방법으로 제조된 촉매 조성물은 전이금속 화합물의 촉매 활성을 높이고 효율적으로 올레핀 중합체를 제조할 수 있으며, 이는 전이금속 화합물의 종류에 관계 없이 다양한 종류의 전이금속 화합물에서 구현되는 효과임을 확인하였다.

Claims (12)

  1. (S1) 폴리알킬알루미녹산, 트리알킬알루미늄 및 탄화수소 용매를 포함하는 폴리알킬알루미녹산 함유 용액을 준비하는 단계;
    (S2) 상기 폴리알킬알루미녹산 함유 용액을 하이드록시기 함유 화합물과 반응시키는 단계;
    (S3) 상기 단계 (S2)의 반응 생성물을 여과하는 단계; 및
    (S4) 상기 단계 (S3)의 여과물과 전이금속 화합물을 혼합하는 단계;를 포함하는 촉매 조성물의 제조방법.
  2. 청구항 1에 있어서,
    상기 폴리알킬알루미녹산은 폴리메틸알루미녹산, 폴리에틸알루미녹산, 폴리이소부틸알루미녹산 및 폴리부틸알루미녹산으로 이루어진 군에서 선택된 1종 이상인 촉매 조성물의 제조방법.
  3. 청구항 1에 있어서,
    상기 트리알킬알루미늄은 트리메틸알루미늄, 트리에틸알루미늄, 트리이소부틸알루미늄, 트리프로필알루미늄, 트리부틸알루미늄, 디메틸클로로알루미늄, 트리이소프로필알루미늄, 트리-s-부틸알루미늄, 트리사이클로펜틸알루미늄, 트리펜틸알루미늄, 트리이소펜틸알루미늄, 트리헥실알루미늄, 트리옥틸알루미늄, 에틸디메틸알루미늄, 메틸디에틸알루미늄, 트리페닐알루미늄 및 트리-p-톨릴알루미늄으로 이루어진 군에서 선택된 1종 이상인 촉매 조성물의 제조방법.
  4. 청구항 1에 있어서,
    상기 하이드록시기 함유 화합물은 하이드록시기를 2개 이상 함유하는 탄소수 2 내지 60의 화합물인 촉매 조성물의 제조방법.
  5. 청구항 1에 있어서,
    상기 탄화수소 용매는 폴리알킬알루미녹산 함유 용액 기준 20 내지 99 중량%인 촉매 조성물의 제조방법.
  6. 청구항 1에 있어서,
    상기 하이드록시기 함유 화합물은 폴리알킬알루미녹산 함유 용액에 포함된 트리알킬알루미늄 1 당량 기준 0.01 내지 100.00 당량인 촉매 조성물의 제조방법.
  7. 청구항 1에 있어서,
    상기 단계 (S2)에서,
    폴리알킬알루미녹산 및 하이드록시기 함유 화합물의 반응으로 상기 탄화수소 용매에 불용성인 고체가 생성되는 촉매 조성물의 제조방법.
  8. 청구항 1에 있어서,
    상기 단계 (S3)의 여과는 기공 크기 0.1 내지 40.0 μm의 여과막을 사용하여 수행되는 것인 촉매 조성물의 제조방법.
  9. 청구항 1에 있어서,
    상기 단계 (S3)는 단계 (S2)의 반응 생성물을 정치시킨 후 상층액을 회수하여 여과하는 것인 촉매 조성물의 제조방법.
  10. 폴리알킬알루미녹산, 트리알킬알루미늄 및 탄화수소 용매를 포함하는 폴리알킬알루미녹산 함유 용액; 및 전이금속 화합물;을 포함하고,
    상기 트리알킬알루미늄은 폴리알킬알루미녹산 함유 용액 기준 4.3 몰% 이하인 촉매 조성물.
  11. 청구항 10에 있어서,
    상기 촉매 조성물은 청구항 1 내지 9 중 어느 한 항의 제조방법으로 제조된 것인 촉매 조성물.
  12. 청구항 10의 촉매 조성물 존재 하에 올레핀계 단량체를 중합하는 단계;를 포함하는 올레핀 중합체의 제조방법.
PCT/KR2020/013380 2019-09-30 2020-09-29 하이드록시기 함유 화합물을 이용한 폴리알킬알루미녹산 함유 용액의 정제방법 및 이를 이용한 촉매 조성물 WO2021066550A1 (ko)