WO2021066313A1 - 고흡수성 수지 조성물 및 이의 제조 방법 - Google Patents
고흡수성 수지 조성물 및 이의 제조 방법 Download PDFInfo
- Publication number
- WO2021066313A1 WO2021066313A1 PCT/KR2020/010385 KR2020010385W WO2021066313A1 WO 2021066313 A1 WO2021066313 A1 WO 2021066313A1 KR 2020010385 W KR2020010385 W KR 2020010385W WO 2021066313 A1 WO2021066313 A1 WO 2021066313A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- super absorbent
- absorbent polymer
- weight
- surface crosslinking
- crosslinking agent
- Prior art date
Abstract
Description
구분 | 표면 가교제* | 계면 활성제 | 기타 첨가제* | ||
EC | PC | GC | SDS | 1,3-PD | |
실시예 1 | 0.6 | 0.6 | 0.6 | 0.005 | - |
실시예 2 | 0.6 | 0.6 | 0.6 | 0.01 | - |
실시예 3 | 0.6 | 0.6 | 0.6 | 0.02 | - |
실시예 4 | 0.8 | 0.6 | 0.6 | 0.01 | - |
실시예 5 | 0.6 | 0.8 | 0.6 | 0.01 | - |
실시예 6 | 0.6 | 0.6 | 0.8 | 0.01 | - |
실시예 7 | 1.8 | - | - | 0.01 | - |
실시예 8 | - | - | 1.8 | 0.01 | - |
실시예 9 | 0.9 | 0.9 | - | 0.01 | - |
실시예 10 | - | 0.9 | 0.9 | 0.01 | - |
비교예 1 | 0.6 | 0.6 | 0.6 | - | - |
비교예 2 | - | - | - | 0.01 | - |
비교예 3 | - | - | - | 0.01 | 0.3 |
비교예 4 | 0.6 | 0.6 | 0.6 | - | 0.3 |
표면 가교제, 계면활성제 및 기타 첨가제의 성분은 베이스 수지 100중량부 기준임.EC: Etylene carbonatePC: Propylene carbonateGC: Glycerol carbonateSDS:Sodium dodecyl sulfate1,3-PD: 1,3-propanediol |
구분 | CRC(g/g) | Vortex time(sec) | 0.7AUP(g/g) |
실시예 1 | 32.6 | 61 | 25.2 |
실시예 2 | 32.6 | 54 | 25.3 |
실시예 3 | 32.5 | 51 | 25.1 |
실시예 4 | 31.0 | 55 | 24.0 |
실시예 5 | 31.2 | 56 | 22.0 |
실시예 6 | 32.1 | 53 | 25.5 |
실시예 7 | 32.3 | 65 | 24.2 |
실시예 8 | 33.1 | 59 | 22.0 |
실시예 9 | 32.2 | 63 | 25.5 |
실시예 10 | 32.0 | 65 | 22.9 |
비교예 1 | 32.1 | 67 | 25.6 |
비교예 2 | 40.0 | 55 | 12.2 |
비교예 3 | 32.2 | 62 | 21.1 |
비교예 4 | 29.0 | 70 | 22.6 |
Claims (8)
- 내부 가교제의 존재 하에, 적어도 일부가 중화된 산성기를 갖는 수용성 에틸렌계 불포화 단량체를 가교 중합하여 함수겔 중합체를 형성하는 단계;상기 함수겔 중합체를 건조, 분쇄, 및 분급하여, 베이스 수지 분말을 얻는 단계; 및고리형 카보네이트계 표면 가교제 및 소듐 도데실 설페이트를 포함하는 표면 가교액의 존재하에 상기 베이스 수지 분말을 표면 가교하여 고흡수성 수지 입자를 형성하는 단계;를 포함하고,고흡수성 수지 조성물의 제조 방법.
- 제1항에 있어서,상기 고리형 카보네이트계 표면 가교제는, 에틸렌 카보네이트, 프로필렌 카보네이트, 및 글리세롤 카보네이트로 이루어진 군에서 선택된 1종 이상을 포함하는,고흡수성 수지 조성물의 제조 방법.
- 제1항에 있어서,상기 고리형 카보네이트계 표면 가교제는,베이스 수지 총 100중량부에 대하여, 0.5 내지 5 중량부로 포함되는 고흡수성 수지 조성물의 제조 방법.
- 제1항에 있어서,상기 고리형 카보네이트계 표면 가교제는,표면 가교제 100중량부에 대하여, 에틸렌 카보네이트 10 내지 50 중량부, 프로필렌 카보네이트 10 내지 50 중량부, 및 글리세롤 카보네이트 10 내지 50 중량부를 포함하는,고흡수성 수지 조성물의 제조 방법.
- 제1항에 있어서,상기 소듐 도데실 설페이트는,베이스 수지 총 100중량부에 대하여, 0.001 내지 1.0 중량부로 포함되는 고흡수성 수지 조성물의 제조 방법.
- 제1항에 있어서,상기 표면 가교하여 고흡수성 수지 입자를 형성하는 단계는, 150℃ 내지 200℃에서, 40 내지 100분간 수행되는,고흡수성 수지 조성물의 제조 방법.
- 적어도 일부가 중화된 산성기를 갖는 수용성 에틸렌계 불포화 단량체의 가교 중합체를 포함하는 고흡수성 수지 입자;를 포함하고,상기 고흡수성 수지 입자의 표면 중 일부에, 고리형 카보네이트계 표면 가교제 및 소듐 도데실 설페이트를 매개로 상기 가교 중합체가 추가 가교되어 형성된 표면 가교층을 더 포함하고,고흡수성 수지 조성물.
- 제7항에 있어서,흡수 속도(vortex time)가 50초 내지 65초인,고흡수성 수지 조성물.