WO2021065662A1 - ホットメルト粘着剤組成物、粘着テープ、及び粘着テープの製造方法 - Google Patents

ホットメルト粘着剤組成物、粘着テープ、及び粘着テープの製造方法 Download PDF

Info

Publication number
WO2021065662A1
WO2021065662A1 PCT/JP2020/035980 JP2020035980W WO2021065662A1 WO 2021065662 A1 WO2021065662 A1 WO 2021065662A1 JP 2020035980 W JP2020035980 W JP 2020035980W WO 2021065662 A1 WO2021065662 A1 WO 2021065662A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive
styrene
hot melt
block copolymer
adhesive composition
Prior art date
Application number
PCT/JP2020/035980
Other languages
English (en)
French (fr)
Inventor
佳明 山本
晃純 木村
洋亮 楯
光永　敏勝
Original Assignee
デンカ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by デンカ株式会社 filed Critical デンカ株式会社
Priority to JP2021551147A priority Critical patent/JPWO2021065662A1/ja
Priority to EP20872041.7A priority patent/EP4039378B1/en
Priority to US17/637,268 priority patent/US20220306904A1/en
Priority to KR1020227014222A priority patent/KR20220075364A/ko
Priority to CA3152486A priority patent/CA3152486A1/en
Priority to MX2022002943A priority patent/MX2022002943A/es
Priority to CN202080069104.1A priority patent/CN114555747A/zh
Publication of WO2021065662A1 publication Critical patent/WO2021065662A1/ja

Abstract

多孔質基材を用いた場合に、被着体に対する適度な粘着力を発現するホットメルト粘着剤組成物を提供する。　本発明によれば、スチレン系ブロック共重合体と、粘着付与剤と、可塑剤を含有し、前記スチレン系ブロック共重合体は、スチレン－ブタジエンブロック共重合体であり、ブタジエン部分が部分的に水素添加されており、前記スチレン系ブロック共重合体１００質量部に対し、前記粘着付与剤を、６５～１９０質量部含み、前記可塑剤を、０．１～２４質量部含む、ホットメルト粘着剤組成物が提供される。

Description

ホットメルト粘着剤組成物、粘着テープ、及び粘着テープの製造方法
　本発明は、ホットメルト粘着剤組成物、粘着テープ、及び粘着テープの製造方法に関する。
　基材に対し、スチレン系ブロック共重合体と粘着付与剤等を含む粘着剤を塗布した粘着テープが様々な用途に用いられている。
　また、基材として不織布は、多孔質体であることから消音性を示し、さらに引張り強度に代表される機械強度が優れ、安価である事からテープ基材として広く使われている。
特開２０１５－２０３０３２号公報
　一方で、不織布は多孔質のため塗布液の基材裏周りがある事から溶剤系粘着剤や、水系粘着剤は粘度が低く直接塗布は難しいとされてきた。そこで比較的高粘度なホットメルト粘着剤を使用し、基材に直接塗工する方法が考えられる。
　しかし、不織布等、凹凸の大きい多孔質基材にホットメルト粘着剤を塗布すると、粘着剤の基材裏回りはしないが粘着剤塗工面が凹凸になり、被着体に対する粘着剤の接触面積が小さくなるため、粘着力や保持力が十分発現しない問題があった。
　この問題を解決するには、例えば粘着剤の厚みを厚くすることが考えられるが、必要な粘着特性を得るには粘着剤を２倍程度以上に塗布する必要があり非効率である。さらにテープ自体の重量も重くなり取り扱いが悪くなる。この問題を解決するには、粘着剤の接触面積が小さくても必要な粘着特性を得ることができるように粘着剤自体を、強粘着、高保持力にする必要がある。
　粘着力は強いほど被着体によく貼り付いて良いが、あまり強すぎるとテープ状に巻いたときに基材を繰り出すのが困難になる。
　巻き戻し力を軽くするには、基材背面に剥離剤を塗布すればよいが、不織布のような多孔質基材に剥離剤を塗布するのは、例えばトルエン等の有機溶剤に剥離剤を溶解させた剥離剤溶液を塗布しなければならず、溶液の粘度が低いため、前記の粘着剤を塗布した場合と同様に基材の裏回りの問題がある。
　そこで、剥離剤が不要で、被着体にも良く貼り付く適度な粘着力、保持力を発現する粘着剤が必要である。
　本発明はこのような問題に鑑みてなされたものであり、多孔質基材を用いた場合に、被着体に対する適度な粘着力、保持力を発現するホットメルト粘着剤組成物を提供するものである。
　本発明によれば、スチレン系ブロック共重合体と、粘着付与剤と、可塑剤を含有し、前記スチレン系ブロック共重合体は、スチレン－ブタジエンブロック共重合体であり、ブタジエン部分が部分的に水素添加されており、前記スチレン系ブロック共重合体１００質量部に対し、前記粘着付与剤を、６５～１９０質量部含み、前記可塑剤を、０．１～２４質量部含む、ホットメルト粘着剤組成物が提供される。
　以下、本発明の種々の実施形態を例示する。以下に示す実施形態は互いに組み合わせ可能である。
　好ましくは、前記粘着付与剤は、石油樹脂である。
　好ましくは、前記石油樹脂は、Ｃ５石油樹脂、Ｃ５Ｃ９石油樹脂、及び水添Ｃ９石油樹脂からなる群から選ばれる少なくとも１つである。
　好ましくは、前記可塑剤は、ＤＩＮＡ（ジイソノニルアジペート）である。
　別の観点によれば、多孔質基材と、前記多孔質基材上に設けられた粘着剤層とを備え、前記粘着剤層は、上記ホットメルト粘着剤組成物を含む、粘着テープ、が提供される。
　好ましくは、ＪＩＳＺ０２３７　「１０．粘着力」における粘着力が１．５Ｎ／ｃｍ以上であり、ＪＩＳＺ０２３７　「１３．保持力」における保持力が１０ｍｉｎ以上である。
　別の観点によれば、上記粘着テープの製造方法であって、前記ホットメルト粘着剤組成物を前記基材上に非接触塗工方式により塗工する工程を含む、粘着テープの製造方法、が提供される。
　以下、本発明の実施形態について説明する。以下に示す実施形態中で示した各種特徴事項は、互いに組み合わせ可能である。また、各特徴事項について独立して発明が成立する。
１．ホットメルト粘着剤組成物
　本発明の一実施形態に係るホットメルト粘着剤組成物は、スチレン系ブロック共重合体と、粘着付与剤と、可塑剤を含有する。
（スチレン系ブロック共重合体）
　スチレン系ブロック共重合体は、スチレン－ブタジエンブロック共重合体であり、ブタジエン部分が部分的に水素添加されている。ブタジエン部分が部分的に水素添加されているスチレン－ブタジエンブロック共重合体としては、スチレン－ブタジエン－ブチレン－スチレンブロック共重合体（ＳＢＢＳ）が挙げられる。
　スチレン－ブタジエンブロック共重合体のブタジエン部分は、２０質量％～９０質量％が水素添加されていることが好ましく、３０質量％～８０質量％が水素添加されていることがより好ましい。
　スチレン－ブタジエンブロック共重合体の重量平均分子量は、特に限定されないが、例えば、好ましくは３万～５０万であり、より好ましくは６万～３０万である。重量平均分子量は、ゲル浸透クロマトグラフ（ＧＰＣ）法により求めることができる。
　スチレン－ブタジエンブロック共重合体のスチレンコンテントは、５～５０質量％が好ましく、１０～４０質量％がより好ましい。このような範囲にすることで、被着体に対する適度な粘着力、保持力を発現する。スチレンコンテントは、ＪＩＳ　Ｋ６３８３に記載される方法を用いて測定することができる。
　前記スチレン系ブロック共重合体は１種類を使用して粘着剤としても構わないが、スチレンコンテントや重量平均分子量が異なる２種類以上をブレンドして使用しても好ましく使用できる。すなわち、２種類以上のスチレン系ブロック共重合体を併用することで、例えば粘着剤塗工時の溶融粘度を低くすることができ、塗工時の粘度を加工しやすくコントロールできるため好ましく使用することができる。また、２種類以上のスチレン系ブロック共重合体を併用すると、粘着特性においても粘着剤の粘着力や保持力が調整できる点においても好ましい。
（粘着付与剤）
　粘着付与剤は、特に限定されないが、石油樹脂であることが好ましい。石油樹脂としては、例えば、Ｃ９石油樹脂、水添Ｃ９石油樹脂、Ｃ５石油樹脂、脂環族系石油樹脂、脂環族／芳香族系石油樹脂、テルペン系樹脂、ロジン系樹脂、ロジンエステル系樹脂、テルペン－フェノール樹脂、アルキルフェノール樹脂等が挙げられる。中でも、石油樹脂は、Ｃ５石油樹脂、Ｃ５Ｃ９石油樹脂、及び水添Ｃ９石油樹脂からなる群から選ばれる少なくとも１つであることが好ましい。また、水添Ｃ９石油樹脂が最も好ましい。その理由は、粘着テープが屋外で使用されるようなことがあっても、直射日光（紫外線）曝露による劣化が少ないからである。
　スチレン系ブロック共重合体１００質量部に対し、粘着付与剤を、好ましくは６５～１９０質量部含み、より好ましくは８０～１５０質量部含み、さらに好ましくは１００～１５０質量部含む。このような範囲とすることで、被着体に対する適度な粘着力、保持力を発現可能である。この粘着付与剤の含有量は、具体的には例えば、６５，７０，７５，８０，８５，９０，９５，１００，１０５，１１０，１１５，１２０，１２５，１３０，１３５，１４０，１４５，１５０，１５５，１６０，１６５，１７０，１７５，１８０，１８５，１９０質量部であり、ここで例示した数値の何れか２つの間の範囲内であってもよい。
（可塑剤）
　本発明の一実施形態に係るホットメルト粘着剤組成物は、可塑剤を含有する。ホットメルト粘着剤組成物は、スチレン系ブロック共重合体１００質量部に対し、可塑剤を、０．１～２４質量部含み、１～２０質量部含むことが好ましく、５～１５質量部含むことがより好ましい。
　また、可塑剤はとしては、フタル酸エステル系の可塑剤はスチレン系ブロック共重合体と相溶性が良く、少量で可塑化効果が得られるため好ましい。フタル酸エステル系の可塑剤としては、ＤＩＮＡ(ジイソノニルアジペート)、ＤＥＨＰ（ジ－（２－エチルヘキシル）フタレート）、ＤＢＰ（ジブチルフタレート）、ＢＢＰ（ブチルベンジルフタレート）、ＤＩＮＰ（ジイソノニルフタレート）、ＤＩＤＰ（ジイソデシルフタレート）、ＤＮＯＰ(ジノルマルオクチルフタレート)（が挙げられる。しかし、ＤＩＮＡ以外のフタル酸エステルはＲＥＡＣＨ（Ｒｅｇｉｓｔｒａｔｉｏｎ，Ｅｖａｌｕａｔｉｏｎ，Ａｕｔｈｏｒｉｚａｔｉｏｎ，ａｎｄ　Ｒｅｓｔｒｉｃｔｉｏｎ　ｏｆ　Ｃｈｅｍｉｃａｌｓ）等の規制が適用される可能性があるので使用の際は注意が必要であるが、ＤＩＮＡはこれらの規制は適用されないので好ましく使用できる。
（添加剤）
　本発明の一実施形態に係るホットメルト粘着剤組成物は、必要に応じて本発明の効果を阻害しない範囲で、無機充填剤、改質剤、安定剤、酸化防止剤、紫外線吸収剤などの各種添加剤を含んでもいてもよい。
２．粘着テープ
　本発明の一実施形態に係る粘着テープは、多孔質基材と、多孔質基材上に設けられた粘着剤層とを備える。
　粘着テープは、ＪＩＳＺ０２３７　「１０．粘着力」における粘着力が、好ましくは１．５Ｎ／ｃｍ以上であり、より好ましくは２．０Ｎ／ｃｍ以上である。粘着力は、好ましくは８Ｎ／ｃｍ以下であり、より好ましくは６Ｎ／ｃｍ以下である。このような範囲にすることで、被着体によく貼り付つく一方で、テープ状に巻いたときの基材を繰り出しが容易である。
　粘着テープは、ＪＩＳＺ０２３７　「１３．保持力」における保持力が、好ましくは１０ｍｉｎ以上であり、より好ましくは２０ｍｉｎ以上である。保持力は、好ましくは１００ｍｉｎ以下であり、より好ましくは８０ｍｉｎ以下である。このような範囲にすることで、十分な保持力を有する一方で、テープ状に巻いたときの取り扱いが容易である。
（多孔質基材）
　多孔質基材は、多孔質材からなる基材であれば特に制限はないが、引張り強度に代表される機械強度が優れ、安価であることから不織布が好ましい。
（粘着剤層）
　粘着剤層は、上記ホットメルト粘着剤組成物を含む。粘着剤層の目付量は、特に限定されないが、例えば１０～１００ｇ／ｍ２である。この目付量が少なすぎると、粘着性が不十分になり、多過ぎると塗工性能が悪くなることがある。
３．粘着テープの製造方法
　本発明の一実施形態に係る粘着テープの製造方法は、上記ホットメルト粘着剤組成物を基材上に塗工する工程を含む。
　塗工方法に特に制限はないが、粘着剤の原料を加熱して溶融、混練してホットメルト方式により塗布することが好ましく、非接触塗工方式により塗工することがより好ましい。
　非接触塗工の例としては、クロスコーター（ＩＴＷダイナテック社製）が挙げられる。一般的に不織布等の基材の直接粘着剤を塗工すると、基材に対して粘着剤の染み込みが発生し、大幅に粘着特性が低下する。クロスコーターを使用すると、不織布に粘着剤塗工すると粘着剤の染み込みが抑制できるため、粘着特性低下が発生しにくいため好ましい。
　以下に実施例をあげて本発明を更に詳細に説明する。また、これらはいずれも例示的なものであって、本発明の内容を限定するものではない。
　表１及び表２に記載の基材上に、粘着剤組成物を６０ｇ／ｍ２の目付量になる様に、非接触塗工方式により塗工して粘着剤層を形成することによって評価用の粘着テープを作製した。粘着剤組成物としては、表１に示すように、スチレン系ブロック共重合体１００に対して、粘着付与剤と、可塑剤（ＤＩＮＡ、新日本理化株式会社製　サンソサイザーＤＩＮＡ）と、酸化防止剤（ＢＡＳＦ製イルガノックス１０１０）、紫外性吸収剤（ＢＡＳＦ製ＴＩＮＵＶＩＮ　Ｐ）を添加し、１５０℃で混練して溶融状態の粘着剤を得て、クロスコーターで塗工して、粘着剤層を得た。なお、ステッチボンド不織布は多孔質基材であり、ＰＥＴフィルムは非多孔質基材のものである。
　表１及び表２中の各成分は次の通りである。
ＳＢＢＳ：旭化成株式会社製　アサプレンＮ５２１
ＳＩＳ：日本ゼオン株式会社製　クインタック３４２１
Ｃ５石油樹脂：日本ゼオン株式会社製　クイントンＲ１００
Ｃ５Ｃ９石油樹脂：日本ゼオン株式会社製　クイントンＳ１９５
水添Ｃ９石油樹脂：荒川化学工業株式会社製　アルコンＰ－１００
テルペンフェノール：ヤスハラケミカル株式会社製　ＹＳポリスターＴ１００
＜粘着テープの巻き戻し＞
　粘着テープの巻き戻しについては、粘着剤を塗布した基材を直径３インチの紙管に巻き取った後、２０ｍｍ幅にカットし得られた粘着テープ捲重体から手でテープ基材を引きだせるかどうかを下記の基準にて判定した。その結果を表１及び表２に示す。
○：引き出すことが可能だった。
×：引き出す時に必要な力が大きく引き出すことができなかった。
＜ＳＵＳ粘着力＞
　ＪＩＳＺ０２３７　「１０．粘着力」に従ってＳＵＳ板に対する１８０°ピール粘着力を測定した。その結果を表１及び表２に示す。
＜保持力＞
　ＪＩＳＺ０２３７　「１３．保持力」に従って測定した。被着体はＳＵＳ板を使用し、粘着テープの貼り付け面積は２５ｍｍ×２５ｍｍとした。測定温度は６０℃、荷重は１ｋｇとして、おもりが落下するまでの時間を測定した。その結果を表１及び表２に示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002

Claims (7)

  1. スチレン系ブロック共重合体と、粘着付与剤と、可塑剤を含有し、
    前記スチレン系ブロック共重合体は、スチレン－ブタジエンブロック共重合体であり、ブタジエン部分が部分的に水素添加されており、
    前記スチレン系ブロック共重合体１００質量部に対し、
    　前記粘着付与剤を、６５～１９０質量部含み、
    　前記可塑剤を、０．１～２４質量部含む、
    ホットメルト粘着剤組成物。
  2. 前記粘着付与剤は、石油樹脂である、請求項１に記載のホットメルト粘着剤組成物。
  3. 前記石油樹脂は、Ｃ５石油樹脂、Ｃ５Ｃ９石油樹脂、及び水添Ｃ９石油樹脂からなる群から選ばれる少なくとも１つである、請求項２に記載のホットメルト粘着剤組成物。
  4. 前記可塑剤は、ＤＩＮＡ（ジイソノニルアジペート）である、請求項１～請求項３の何れか１項に記載のホットメルト粘着剤組成物。
  5. 多孔質基材と、前記多孔質基材上に設けられた粘着剤層とを備え、
    前記粘着剤層は、請求項１～請求項４の何れか１項に記載のホットメルト粘着剤組成物を含む、
    粘着テープ。
  6. ＪＩＳ　Ｚ０２３７　「１０．粘着力」における粘着力が１．５Ｎ／ｃｍ以上であり、
    ＪＩＳ　Ｚ０２３７　「１３．保持力」における保持力が１０ｍｉｎ以上である、
    請求項５に記載の粘着テープ。
  7. 請求項５又は請求項６に記載の粘着テープの製造方法であって、
    前記ホットメルト粘着剤組成物を前記基材上に非接触塗工方式により塗工する工程を含む、
    粘着テープの製造方法。
PCT/JP2020/035980 2019-10-01 2020-09-24 ホットメルト粘着剤組成物、粘着テープ、及び粘着テープの製造方法 WO2021065662A1 (ja)