JP6063323B2 - 粘着テープ - Google Patents
粘着テープ Download PDFInfo
- Publication number
- JP6063323B2 JP6063323B2 JP2013068300A JP2013068300A JP6063323B2 JP 6063323 B2 JP6063323 B2 JP 6063323B2 JP 2013068300 A JP2013068300 A JP 2013068300A JP 2013068300 A JP2013068300 A JP 2013068300A JP 6063323 B2 JP6063323 B2 JP 6063323B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- adhesive tape
- pressure
- sensitive adhesive
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
項1.基材と前記基材の少なくとも片面に形成された粘着剤層とからなる粘着テープであって、
前記粘着剤層は、(A)(a)アルキル基の炭素数が5〜12の(メタ)アクリル酸アルキルエステル65〜99.8重量%、(b)カルボキシル基含有単量体0.1〜8重量%、(c)下記一般式(1)
R1−(C=O)−O−R2 (1)
[式中、R1及びR2の一方は、一般式(2)
で表わされる置換基を示す。
R1及びR2のもう一方は、炭素数1〜4のアルキル基を示す。]
で表わされるエステル化合物2〜20重量%、及び(d)その他重合可能な単量体0〜15重量%を含有する単量体混合物を重合することにより得られる(メタ)アクリル系共重合体100重量部、(B)粘着付与樹脂として重合ロジン系樹脂0.5〜15重量部、並びに、(C)硬化剤としてカルボジイミド系化合物0.05〜4.0重量部を含有する粘着剤組成物を塗工してなる粘着テープ。
O=C=N−(R4−N=C=N)n−N=C=O (3)
(式中、R4は、炭素数1〜4のアルキル基を示す)
で表され、かつ数平均分子量1000〜4000である項1又は2記載の粘着テープ。
R1−(C=O)−O−R2 (1)
[式中、R1及びR2の一方は、一般式(2)
で表わされる置換基を示す。
R1及びR2のもう一方は、炭素数1〜3のアルキル基を示す。]
で表わされるエステル化合物を含有する単量体混合物を重合することにより得られるものである。
R1−(C=O)−O−R2 (1)
[式中、R1及びR2の一方は、一般式(2)
で表わされる置換基を示す。
R1及びR2のもう一方は、炭素数1〜4のアルキル基を示す。]
で表わされるエステル化合物は特に限定されず、メチル(メタ)アクリレート、エチル(メタ)アクリレート、プロピル(メタ)アクリレート、ブチル(メタ)アクリレート、酢酸ビニル、プロピオン酸ビニル、酪酸ビニル、吉草酸ビニル、酢酸イソプロペニル、プロピオン酸イソプロペニル、酪酸イソプロペニル、及び吉草酸イソプロペニルが挙げられる。これらのエステル化合物は単独で用いてもよく、2種以上を併用してもよい。なかでも、メチル(メタ)アクリレート、酢酸ビニル等が好ましい。
O=C=N−(R4−N=C=N)n−N=C=O (3)
(式中、R4は、炭素数1〜4のアルキル基を示す)
で表され、かつ数平均分子量1000〜4000である化合物等が挙げられる。かかるカルボジイミド系化合物の市販品としては、日清紡ケミカル社製のカルボジライトV−05(分子量1200)、カルボジライトV−07(分子量3000)等を挙げることができる。
炭化水素系オイルとしては、例えば、プロセスオイル、ひまし油、トール油等が挙げられる。より具体的には、ハートールFA−1(ハリマ化成)、JCT oilB等の商品名で販売されているものを用いることができる。
(1)(メタ)アクリル系共重合体の調製
2−エチルヘキシルアクリレート(2−EHA)87.5重量部、アクリル酸0.5重量部、メチルアクリレート10重量部、アクリルアミド2重量部、及び重合開始剤としてAIBN(アゾビスイソブチロニトリル)0.2重量部を添加し、フラスコ中で60℃、6時間溶液重合することにより(メタ)アクリル系共重合体を得た。
上記(1)で得られた(メタ)アクリル系共重合体100重量部に対して、重合ロジン系樹脂として重合ロシ゛ンエステルA(荒川化学工業社製、ペンセルD−125、軟化点125℃)10重量部と、硬化剤としてカルホ゛シ゛イミト゛系A硬化剤(日清紡ケミカル社製、カルボジライトV−05、数平均分子量1200)2.0重量部を加え、スパチュラを用いて常温で攪拌することにより混合して粘着剤組成物を調製した。一方、基材として厚さ100μmであるPETクロス基材を準備した。
成分(A)〜(D)の組成を表1のようにした以外は実施例1と同様にして実施例2〜12、及び比較例1〜6の粘着テープを得た。 尚、表1における(B)粘着付与樹脂、(C)硬化剤及び(D)離型剤の表示は以下の通り:
重合ロシ゛ンエステルA:ペンセルD−125(荒川化学工業社製、軟化点125℃)
重合ロシ゛ンエステルB:ペンセルD−160(荒川化学工業社製、軟化点160℃)
テルヘ゜ンフェノール:YSポリスターT160(ヤスハラケミカル社製、軟化点160℃)
カルホ゛シ゛イミト゛系A:カルボジライトV−05(日清紡ケミカル社製、数平均分子量1200)
カルホ゛シ゛イミト゛系B:カルボジライトV−07(日清紡ケミカル社製、数平均分子量3000)
アシ゛リシ゛ン系:HDU(相互薬工社製、数平均分子量254)
離型剤A:ピーロイル1050(一方社製、軟化点70℃)
離型剤B:ピーロイル1070(一方社製、軟化点80℃)。
(1)対サッシ粘着力
住宅部材用のアルミサッシ板を80×150mmにカットし、表面に25mm幅のテープサンプルを貼り付け180°剥離強度を測定した。
上記と同様なアルミサッシ板を80×150mmにカットし、表面に25mm幅のテープサンプルを25×100mmにカットし貼り付け70℃で100hr放置後の、糊残りの有無を5点満点で評価した。
5点:糊残りなし
4点:点状糊残りあり
3点:2〜3割糊残りあり
2点:3〜7割糊残りあり
1点:8割〜全面糊残りあり
上記と同様なアルミサッシ板をサンシャインウェザーメーターに1000時間照射させて劣化させ、80×150mmにカットし、表面に25mm幅のテープサンプルを25×100mmにカットし貼り付け70℃で100hr放置後の、糊残りの有無を5点満点で評価した。
5点:糊残りなし
4点:点状糊残りあり
3点:2〜3割糊残りあり
2点:3〜7割糊残りあり
1点:8割〜全面糊残りあり
上記と同様なアルミサッシ板を80×150mmにカットし、表面に25mm幅のテープサンプルを貼り付け40℃条件下で2時間後の対サッシ定荷重90°保持力を測定した。
JIS Z 0237に準じる方法により、傾斜式ボールタックの値を測定した。
結果を下記表1に示す。
糸密度(タテ糸)54本、(ヨコ糸)17本のPET基布に背面側に成膜温度330℃にてPE樹脂A(厚み40μm)を押出ラミネートした後、同様に糊面側もPE樹脂A(厚み30μm)同条件で押出ラミネートをし、基材を作製した(基材サンプル)。また、当該基材サンプルに実施例1の粘着剤組成物を前述の(2)に従い塗工、乾燥後及び養生して、粘着テープを得た(テープサンプル)。
糸密度、PE樹脂の種類及びラミネートの厚みを表2のようにした以外は実施例13と同様にして実施例14〜21の基材及び粘着テープを得た。 尚、表2におけるPE樹脂の詳細は以下の通り:
PE樹脂A:サンテックL2270(旭化成社製、密度0.922、MFR7)
PE樹脂B:サンテックL2340(旭化成社製、密度0.923、MFR3.8)。
(6)端裂抵抗評価
テープサンプルを25×240mmにカットし、引張試験機上部のチャック側に三角金具を取り付け、サンプルをその三角金具に通してつかみ間隔240mm、引張速度300±30mm/minで引張切断時の荷重を測定した。
背面側のみラミネートした基材サンプルを100×100mmにカットし、ボンドテスターにてラミ強度を測定した。
テープサンプルを25×300mmにカットし、室外機に貼付し、12時間後に剥離した時の基材切れ及びラミ抜けの有無を確認した。
基材サンプルを100×100mmにカットし、サンプルの長さ方向のほぼ中心付近に25mm幅テープを基材サンプルに対して垂直になるように基材幅方向の左端から右端に向かって貼付し、基材サンプルから約70mmくらい出るように貼付する。
結果を表2に示す。
Claims (6)
- 基材と前記基材の少なくとも片面に形成された粘着剤層とからなる粘着テープであって、
前記粘着剤層は、(A)(a)アルキル基の炭素数が5〜12の(メタ)アクリル酸アルキルエステル65〜99.8重量%、(b)カルボキシル基含有単量体0.1〜8重量%、(c)下記一般式(1)
R1−(C=O)−O−R2 (1)
[式中、R1及びR2の一方は、一般式(2)
で表わされる置換基を示す。
R1及びR2のもう一方は、炭素数1〜4のアルキル基を示す。]
で表わされるエステル化合物2〜20重量%、及び(d)その他重合可能な単量体0〜15重量%を含有する単量体混合物を重合することにより得られる(メタ)アクリル系共重合体100重量部、(B)粘着付与樹脂として重合ロジン系樹脂0.5〜15重量部、(C)硬化剤としてカルボジイミド系化合物0.05〜4.0重量部、並びに(D)離型剤としてN−長鎖アルキルマレイミドの単独重合体、もしくはN−長鎖アルキルマレイミドと共重合しうる単量体との共重合体1-20重量部を含有する粘着剤組成物を塗工してなる粘着テープ。 - 上記硬化剤カルボジイミド系化合物が下記一般式(3)
O=C=N−(R4−N=C=N)n−N=C=O (3)
(式中、R4は、炭素数1〜4のアルキル基を示す)
で表され、かつ数平均分子量1000〜4000である請求項1記載の粘着テープ。 - 重合ロジン系樹脂の軟化点は、120〜130℃である請求項1または2記載の粘着テープ。
- 基材が、ポリエステル糸をタテ糸、ヨコ糸に使用した基布の少なくとも片方の面をポリエチレンでラミネートした基材である請求項1〜3のいずれか1項に記載の粘着テープ。
- その他重合可能な単量体が、酢酸ビニル及び/又はアミド基含有単量体である請求項1〜4のいずれか1項に記載の粘着テープ。
- 上記単量体混合物における該(c)一般式(1)で表わされるエステル化合物の配合割合が、該(a)アルキル基の炭素数が5〜12の(メタ)アクリル酸アルキルエステル1重量部に対して、0.15重量部未満である請求項1〜5のいずれか1項に記載の粘着テープ。