WO2021065616A1 - 合わせガラス - Google Patents

合わせガラス Download PDF

Info

Publication number
WO2021065616A1
WO2021065616A1 PCT/JP2020/035779 JP2020035779W WO2021065616A1 WO 2021065616 A1 WO2021065616 A1 WO 2021065616A1 JP 2020035779 W JP2020035779 W JP 2020035779W WO 2021065616 A1 WO2021065616 A1 WO 2021065616A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass plate
glass
light emitting
interlayer film
vehicle
Prior art date
Application number
PCT/JP2020/035779
Other languages
English (en)
French (fr)
Inventor
陽 ▲高▼橋
孝典 松島
壮志 木村
Original Assignee
Ａｇｃ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ａｇｃ株式会社 filed Critical Ａｇｃ株式会社
Priority to DE112020004771.7T priority Critical patent/DE112020004771T5/de
Priority to CN202080065841.4A priority patent/CN114423604A/zh
Publication of WO2021065616A1 publication Critical patent/WO2021065616A1/ja

Abstract

本合わせガラスは、車内側ガラス板と、車外側ガラス板と、前記車内側ガラス板と前記車外側ガラス板を接合する中間膜と、前記中間膜に封入された発光装置と、を有する車両用の合わせガラスであって、前記発光装置は、前記車内側ガラス板を介して前記車両の内部に光を出射する装置であり、前記中間膜は、前記車内側ガラス板と接合する第１の中間膜と、前記車外側ガラス板と接合する第２の中間膜と、を有し、前記発光装置よりも車内側に位置する部材の合計の可視光線透過率が５０％以下である。

Description

合わせガラス
　本発明は、合わせガラスに関する。
　従来、発光素子を有する発光装置を封入した合わせガラスが、建材用途で使用されている。又、発光素子を有する発光装置を封入した合わせガラスを、自動車の窓ガラスとして使用する技術が検討されている。
　例えば、透明なガラスの支持体上に配置された１組の発光ダイオードを、合わせガラスである自動車用のルーフに封入し、照明手段として用いる技術が挙げられる（例えば、特許文献１参照）。
特許第６３６０８２８号
　車両用の合わせガラスに発光素子を封入すると、発光素子の非発光時に発光素子に接続される配線が車内から視認されデザイン性が低下する問題があった。
　本発明は、上記の点に鑑みてなされたものであり、発光装置を封入した合わせガラスにおいて、発光素子に接続される配線を車内から目立ち難くすることを目的とする。
　本合わせガラスは、車内側ガラス板と、車外側ガラス板と、前記車内側ガラス板と前記車外側ガラス板を接合する中間膜と、前記中間膜に封入された発光装置と、を有する車両用の合わせガラスであって、前記発光装置は、前記車内側ガラス板を介して前記車両の内部に光を出射する装置であり、前記中間膜は、前記車内側ガラス板と接合する第１の中間膜と、前記車外側ガラス板と接合する第２の中間膜と、を有し、前記発光装置よりも車内側に位置する部材の合計の可視光線透過率が５０％以下である。
　開示の一実施態様によれば、発光装置を封入した合わせガラスにおいて、発光素子に接続される配線を車内から目立ち難くできる。
本実施形態に係る合わせガラスを例示する図である。 本実施形態に係る合わせガラスの湾曲形状を例示する斜視図である。 合わせガラスの取付角度について説明する図である。 図１（ａ）の領域Ｂの部分拡大平面図である。 本実施形態に係る合わせガラスの変形例１を示す平面図である。 本実施形態に係る合わせガラスの変形例２を示す平面図である。 本実施形態に係る合わせガラスの変形例３を示す平面図である。 本実施形態に係る合わせガラスの変形例４を示す平面図である。 実施例について説明する図（その１）である。 実施例について説明する図（その２）である。
　以下、図面を参照して発明を実施するための形態について説明する。各図面において、同一構成部分には同一符号を付し、重複した説明を省略する場合がある。又、各図面において、本発明の内容を理解しやすいように、大きさや形状を一部誇張している場合がある。
　なお、車両とは、代表的には自動車であるが、電車、船舶、航空機等を含む、合わせガラスを有する移動体を指すものとする。
　又、平面視とは合わせガラスの所定領域を合わせガラスの車内側の面の法線方向から視ることを指し、平面形状とは合わせガラスの所定領域を合わせガラスの車内側の面の法線方向から視た形状を指すものとする。
　図１は、本実施形態に係る合わせガラスを例示する図であり、図１（ａ）は合わせガラスを車両に取り付けて車室内から車室外に視認した様子を模式的に示している。図１（ｂ）は、図１（ａ）のＡ－Ａ線に沿う断面図である。
　図１に示すように、合わせガラス１０は、ガラス板１１と、ガラス板１２と、中間膜１３と、遮蔽層１４と、発光装置１５とを有する車両用の合わせガラスである。Ｂは、発光装置１５が配置されている領域を示している。すなわち、合わせガラス１０では、左辺及び右辺近傍の２つの領域に発光装置１５が配置されている。但し、発光装置１５は、合わせガラス１０の１つの領域に配置されてもよいし、３つ以上の領域に配置されてもよい。又、発光装置１５は、平面視において、遮蔽層１４の内側領域全体に配置されていてもよい。
　なお、図１では、合わせガラス１０を平板形状に示しているが、図２に示すように、合わせガラス１０は長手方向及び短手方向の両方に湾曲した複曲形状であってもよい。或いは、合わせガラス１０は、長手方向のみに湾曲した単曲形状や、短手方向のみに湾曲した単曲形状であってもよい。合わせガラス１０が湾曲している場合、車外側に向けて凸となるように湾曲していることが好ましい。
　又、図１及び図２では、合わせガラス１０を矩形状としているが、合わせガラス１０の平面形状は矩形状には限定されず、台形状等を含む任意の形状として構わない。
　合わせガラス１０は、例えば、車両用のフロントサイドガラス、リアサイドガラス、リアクォーターガラス、リアガラス、ルーフガラス、エクストラウインドウ等に適用できる。
　例えばリアガラスが前方に向け傾斜して車両に取り付けられていると、リアガラスだけでは車両の運転者の後方における視野が狭くなるため、後方の視認性が悪い。エクストラウインドウは、このような場合に、車両の運転者の後方視認性を向上させるために、車両のリアガラスの下方に取り付けられる。
　なお、エクストラウインドウの取付角度θＥは、リアガラスの取付角度θＲとは異なっていてもよい。エクストラウインドウの取付角度θＥは、地面に対し５０°以上であってもよい。好ましくは、７０°以上である。ここで、取付角度θとは、図３（ａ）及び図３（ｂ）に示すように、合わせガラス１０の水平方向の幅の中心点を、底辺から上辺まで順次結んだ線を中心線Ｌとし、該中心線Ｌと水平面Ｈ（地面と平行な平面）とがなす角度を指す。なお、図３（ａ）は合わせガラスを車両に取り付けて車室内から車室外に視認した様子を模式的に示しており、図３（ｂ）は、図３（ａ）の中心線Ｌを通る縦断面を示している。
　上述した通り、リアガラスが前方に向け傾斜して車両に取り付けられている場合、すなわち、リアガラスの取付角度θＲが、地面に対し１０°以上４０°以下である場合、リアガラスの下方に更にエクストラウインドウが配置され、かつ、エクストラウインドウの取付角度θＥが地面に対し５０°以上であれば、車両の運転者の後方における視野をより広くできる。
　なお、合わせガラス１０はエクストラウインドウに限定されない。合わせガラス１０の取付角度θが地面に対し５０°以上であれば、合わせガラス１０はリアガラスでもよいし、フロントサイドガラス、リアサイドガラス、リアクォーターガラスでもよい。すなわち、合わせガラス１０の地面に対する取付角度θは５０°以上が好ましい。より好ましくは７０°以上である。
　一方、合わせガラス１０の取付角度θが１０°以下、すなわち地面とほぼ平行になるように取り付けられていてもよい。すなわち、合わせガラス１０はルーフガラスでもよい。
　ガラス板１１は、合わせガラス１０を車両に取り付けたときに車内側となる車内側ガラス板である。又、ガラス板１２は、合わせガラス１０を車両に取り付けたときに車外側となる車外側ガラス板である。
　合わせガラス１０が湾曲している場合、曲率半径は１０００ｍｍ以上１０００００ｍｍ以下であることが好ましい。ガラス板１１とガラス板１２の曲率半径は同じでもよいし、異なっていてもよい。ガラス板１１とガラス板１２の曲率半径が異なっている場合は、ガラス板１１の曲率半径の方がガラス板１２の曲率半径よりも大きい。
　ガラス板１１とガラス板１２は互いに対向する一対のガラス板であり、中間膜１３及び発光装置１５は一対のガラス板の間に位置している。ガラス板１１とガラス板１２とは、中間膜１３及び発光装置１５を挟持した状態で固着されている。
　中間膜１３は、ガラス板１１とガラス板１２を接合する膜である。中間膜１３は、例えば、ガラス板１１と接合する中間膜１３１と、ガラス板１２と接合する中間膜１３２とを有する。中間膜１３１及び中間膜１３２とは別に、中間膜１３１と中間膜１３２の間に位置して発光装置１５の外周を包囲する額縁状の中間膜を有してもよい。中間膜１３１及び中間膜１３２を特に区別する必要がない場合には、単に中間膜１３と称する。
　なお、中間膜１３の外周はエッジ処理されていることが好ましい。すなわち、中間膜１３の端部（エッジ）は、ガラス板１１及びガラス板１２の端部（エッジ）から大きく飛び出さないように処理されていることが好ましい。中間膜１３の端部のガラス板１１及びガラス板１２の端部からの飛びだし量が１５０μｍ以下であると、外観を損なわない点で好適である。但し、合わせガラス１０がサイドガラスである場合には、下辺はドアパネルにより隠蔽されるため、中間膜１３の下辺のエッジ処理は必須ではない。ガラス板１１、ガラス板１２、及び中間膜１３の詳細については後述する。
　遮蔽層１４は、不透明な層であり、例えば、合わせガラス１０の周縁部に沿って帯状に設けることができる。ただし、遮光層１４は、スリット、格子または柄等を有してもよい。遮蔽層１４は、例えば、不透明な（例えば、黒色の）着色セラミック層である。遮蔽層１４は、遮光性を持つ着色中間膜や着色フィルム、着色中間膜と着色セラミック層の組み合わせであってもよい。着色フィルムは赤外線反射フィルム等と一体化されていてもよい。合わせガラス１０に不透明な遮蔽層１４が存在することで、合わせガラス１０の周縁部を車体に保持するウレタン等の樹脂の紫外線による劣化を抑制できる。
　遮蔽層１４は、例えば、黒色顔料を含有する溶融性ガラスフリットを含むセラミックカラーペーストをガラス板上にスクリーン印刷等により塗布し、焼成することで形成できるが、これには限定されない。遮蔽層１４は、例えば、白色、黒色又は濃色顔料を含有する有機インクをガラス板上にスクリーン印刷等により塗布し、乾燥させて形成してもよい。
　図１及び図２の例では、遮蔽層１４は、ガラス板１１の車内側の面の周縁部に設けられている。但し、遮蔽層１４は、必要に応じ、ガラス板１１の車内側の面の周縁部及びガラス板１２の車内側の面の周縁部の両方に設けられてもよい。
　図４は、図１（ａ）の領域Ｂの部分拡大平面図である。但し、図４では、発光装置１５の配線１５３の図示は省略されている。
　図１及び図４を参照すると、発光装置１５は、基材１５１と、基材１５１に実装された複数の発光素子１５２と、各々の発光素子１５２に接続された配線１５３とを有する。ただし、発光装置１５は、導光部材（不図示）であってもよい。この場合、導光部材は、中間膜１３１及び中間膜１３２に挟持される。そして、導光部材は、ガラス板１１及びガラス板１２の、内部又は外部に設けられた発光素子から出射された光を導光し、発光する。発光装置１５は、平面視において、例えば、周縁部の少なくとも一部が遮蔽層１４と重複し、周縁部の少なくとも一部が遮蔽層１４よりも内側に位置している。
　発光装置１５は、必要に応じて、基材１５１や発光素子１５２や配線１５３以外の構成要素（発光素子１５２や配線１５３を被覆する保護層等）を有してもよい。発光装置１５は、複数の発光素子１５２へ電力を供給するための不図示のバスバーを有してもよい。さらに、合わせガラス１０は、合わせガラス１０の外部から給電するために、バスバーに接続されるハーネスを有してもよい。なお、図１では配線１５３が簡略化して描かれているが、実際には配線１５３は基材１５１上に複雑にレイアウトされる。
　基材１５１は、例えば、ポリエチレンテレフタレートである。基材１５１は、ポリエチレンナフタレート、ポリアニリン、ポリチオフェン、カーボンナノチューブ、グラフェン等であってもよい。
　発光素子１５２は、例えば、ＬＥＤ（Light Emitting Diode：発光ダイオード）である。発光素子１５２は、有機ＥＬ（Organic Electro-Luminescence）、無機ＥＬ（Inorganic Electro-Luminescence）等であってもよい。なお、ここでいうＬＥＤには、マイクロＬＥＤも含まれる。
　発光素子１５２の形状は、特に限定されないが、例えば、直方体である。発光素子１５２が直方体である場合の大きさの一例を挙げれば、長さ１．０ｍｍ×幅０．５ｍｍ×高さ０．２ｍｍ、長さ１．６ｍｍ×幅０．８ｍｍ×高さ０．３ｍｍ、長さ３．２ｍｍ×幅２．０ｍｍ×高さ１．０ｍｍ等である。
　発光素子１５２がＬＥＤである場合、発光素子１５２の形状は、長さ０．１ｍｍ以上３．２ｍｍ以下、幅０．１ｍｍ以上２．０ｍｍ以下、高さ０．１ｍｍ以上１．０ｍｍ以下であることが好ましい。発光素子１５２の形状が、長さ０．１ｍｍ以上３．２ｍｍ以下、幅０．１ｍｍ以上２．０ｍｍ以下であれば、各々の発光素子１５２の発光が車内の乗客に視認されやすく、好ましい。また、発光素子１５２の高さ０．１ｍｍ以上１．０ｍｍ以下であれば、ガラス板１１と、ガラス板１２とを接合する中間膜１３に封入でき、好ましい。
　発光素子１５２がマイクロＬＥＤである場合、発光素子１５２の形状は、長さ、幅ともに１００μｍ以下、好ましくは５０μｍ以下、より好ましくは２０μｍ以下である。マイクロＬＥＤの長さ、幅の下限値は、ともに製造上の諸条件等から、特にエッジ効果を低減するために３μｍ以上であることが好ましい。マイクロＬＥＤの高さとしては、１０μｍ以上５０μｍ以下である。
　配線１５３としては、導電材料であれば特に限定されないが、例えば、錫ドープ酸化インジウム（ＩＴＯ）、フッ素ドープ酸化錫（ＦＴＯ）、アンチモンドープ酸化錫（ＡＴＯ）、酸化亜鉛（ＺｎＯ）、金属ナノワイヤー（銀ナノワイヤー、銅ナノワイヤー等）等が挙げられる。
　バスバーとしては、銀、銅、錫、金、アルミニウム、鉄、タングステン、クロム、ニッケルからなる群から選択される少なくとも１つの金属、この群から選択される２つ以上の金属を含む合金、又は導電性有機ポリマー等を、スパッタ法等により形成してもよい。又、バスバーとして、銅リボンや平編み銅線を用いてもよいし、銀ペーストを、例えば、スクリーン印刷等の印刷方式により塗布、焼成して形成してもよい。バスバーは、発光装置１５の周縁部に形成されることが好ましい。
　ハーネスとしては、フレキシブルプリント基板（ＦＰＣ）、フレキシブルフラットケーブル（ＦＦＣ）又は導線を用いてよい。
　発光装置１５は、ガラス板１１を介して車両の内部に光を出射する装置であり、基材１５１をガラス板１２側に向けて、複数の発光素子１５２をガラス板１１側に向けて中間膜１３に封入されている。発光装置１５のガラス板１１側の面（発光素子１５２の実装面）は中間膜１３１に被覆され、発光装置１５のガラス板１２側の面は中間膜１３２に被覆されている。なお、発光装置１５の基材１５１の周縁部とガラス板１１及びガラス板１２の周縁部とは、必ずしも平行でなくてもよい。
　発光素子１５２の発光色は、特に限定されないが、例えは、赤、緑、青、黄、白等である。１つの基材１５１上に、互いに発光色の異なる複数の発光素子１５２が実装されてもよい。
　発光装置１５は、複数の発光素子１５２を発光させて、車両の内部に向けて、例えば、文字（例えば、ロゴの表示、通知、警告表示等）を表示できる。又、発光装置１５は、複数の発光素子１５２を発光させて、車両の内部に向けて、例えば、図形（例えば、矢印等）や模様を表示できる。すなわち、複数の発光素子１５２を規則的に配置してもよいし、不規則的、すなわち、個々の発光素子１５２どうしの距離が同じである場合と異なる場合とが混在するように配置してもよい。なお、発光装置１５は、ルームランプや紫外線除菌ランプ等として用いることもできる。
　発光装置１５の周縁部の少なくとも一部は、平面視において、遮蔽層１４と重複していることで、発光装置１５の周縁部の少なくとも一部を車外側及び／又は車内側から視認しにくいように隠蔽でき好ましい。すなわち、発光装置１５は、基材１５１のエッジを車外側及び／又は車内側から視認しにくいように隠蔽することで、基材１５１のエッジにより生じる透視歪を車外側及び／又は車内側から視認しにくいように隠蔽できる。また、発光装置１５は、その周縁部に形成されるバスバーを車外側及び／又は車内側から視認しにくいように隠蔽できる。なお、ガラス板１１の車内側の面の周縁部及びガラス板１２の車内側の面の周縁部の両方に遮蔽層１４が設けられた場合は、発光装置１５と電気的に接続されるバスバーを車外側及び車内側の両方から視認しにくくなる点で好適である。
　ここで、ガラス板１１、ガラス板１２、及び中間膜１３について詳述する。
　〔ガラス板〕
　ガラス板１１及びガラス板１２は、無機ガラスであっても有機ガラスであってもよい。無機ガラスとしては、例えば、ソーダライムガラス、アルミノシリケートガラス、ホウ珪酸ガラス、無アルカリガラス、石英ガラス等が特に制限なく用いられる。合わせガラス１０の外側に位置するガラス板１２は、耐傷付き性の観点から無機ガラスであることが好ましく、成形性の観点からソーダライムガラスであることが好ましい。ガラス板１１及びガラス板１２がソーダライムガラスである場合、クリアガラス、鉄成分を所定量以上含むグリーンガラス及びＵＶカットグリーンガラスが好適に使用できる。
　無機ガラスは、未強化ガラス、強化ガラスの何れでもよい。未強化ガラスは、溶融ガラスを板状に成形し、徐冷したものである。強化ガラスは、未強化ガラスの表面に圧縮応力層を形成したものである。
　強化ガラスは、例えば風冷強化ガラス等の物理強化ガラス、化学強化ガラスの何れでもよい。物理強化ガラスである場合は、例えば、曲げ成形において均一に加熱したガラス板を軟化点付近の温度から急冷させる等、徐冷以外の操作により、ガラス表面とガラス内部との温度差によってガラス表面に圧縮応力層を生じさせることで、ガラス表面を強化できる。
　化学強化ガラスである場合は、例えば、曲げ成形の後、イオン交換法等によってガラス表面に圧縮応力を生じさせることでガラス表面を強化できる。又、紫外線又は赤外線を吸収するガラスを用いてもよく、更に、透明であることが好ましいが、透明性を損なわない程度に着色されたガラス板を用いてもよい。
　一方、有機ガラスの材料としては、ポリカーボネート、例えばポリメチルメタクリレート等のアクリル樹脂、ポリ塩化ビニル、ポリスチレン等の透明樹脂が挙げられる。
　ガラス板１１及びガラス板１２の形状は、特に矩形状に限定されるものではなく、種々の形状及び曲率に加工された形状であってもよい。ガラス板１１及びガラス板１２の曲げ成形には、重力成形、プレス成形、ローラー成形等が用いられる。ガラス板１１及びガラス板１２の成形法についても特に限定されないが、例えば、無機ガラスの場合はフロート法等により成形されたガラス板が好ましい。
　ガラス板１２の板厚は、最薄部が１．１ｍｍ以上３ｍｍ以下であることが好ましい。ガラス板１２の板厚が１．１ｍｍ以上であると、耐飛び石性能等の強度が十分であり、３ｍｍ以下であると、合わせガラス１０の質量が大きくなり過ぎず、車両の燃費の点で好ましい。ガラス板１２の板厚は、最薄部が１．８ｍｍ以上２．８ｍｍ以下がより好ましく、１．８ｍｍ以上２．６ｍｍ以下が更に好ましく、１．８ｍｍ以上２．２ｍｍ以下が更に好ましく、１．８ｍｍ以上２．０ｍｍ以下が更に好ましい。
　ガラス板１１の板厚は、０．３ｍｍ以上２．３ｍｍ以下であることが好ましい。ガラス板１１の板厚が０．３ｍｍ以上であることによりハンドリング性がよく、２．３ｍｍ以下であることにより質量が大きくなり過ぎない。
　又、ガラス板１１及びガラス板１２は、平板形状であっても湾曲形状であってもよい。しかし、ガラス板１１及びガラス板１２が湾曲形状であり、かつガラス板１１の板厚が適切でない場合、ガラス板１１及びガラス板１２として特に曲がりが深いガラスを２枚成形すると、２枚の形状にミスマッチが生じ、圧着後の残留応力等のガラス品質に大きく影響する。
　しかし、ガラス板１１の板厚を０．３ｍｍ以上２．３ｍｍ以下とすることで、残留応力等のガラス品質を維持できる。ガラス板１１の板厚を０．３ｍｍ以上２．３ｍｍ以下とすることは、曲がりの深いガラスにおけるガラス品質の維持に特に有効である。ガラス板１１の板厚は、０．５ｍｍ以上２．１ｍｍ以下がより好ましく、０．７ｍｍ以上１．９ｍｍ以下が更に好ましい。この範囲であれば、上記の効果が更に顕著となる。
　ガラス板１１及び／又は１２の外側に撥水、紫外線や赤外線カットの機能を有する被膜や、低反射特性、低放射特性を有する被膜を設けてもよい。又、ガラス板１１及び／又は１２の中間膜１３と接する側に、紫外線や赤外線カット、低放射特性、可視光吸収、着色等の被膜を設けてもよい。
　ガラス板１１及びガラス板１２が湾曲形状の無機ガラスである場合、ガラス板１１及びガラス板１２は、フロート法による成形の後、中間膜１３による接着前に、曲げ成形される。曲げ成形は、ガラスを加熱により軟化させて行われる。曲げ成形時のガラスの加熱温度は、大凡５５０℃～７００℃である。
　〔中間膜〕
　中間膜１３としては熱可塑性樹脂が多く用いられ、例えば、可塑化ポリビニルアセタール系樹脂、可塑化ポリ塩化ビニル系樹脂、飽和ポリエステル系樹脂、可塑化飽和ポリエステル系樹脂、ポリウレタン系樹脂、可塑化ポリウレタン系樹脂、エチレン－酢酸ビニル共重合体系樹脂、エチレン－エチルアクリレート共重合体系樹脂、シクロオレフィンポリマー樹脂、アイオノマー樹脂等の従来からこの種の用途に用いられている熱可塑性樹脂が挙げられる。又、特許第６０６５２２１号に記載されている変性ブロック共重合体水素化物を含有する樹脂組成物も好適に使用できる。
　これらの中でも、透明性、耐候性、強度、接着力、耐貫通性、衝撃エネルギー吸収性、耐湿性、遮熱性、及び遮音性等の諸性能のバランスに優れることから、可塑化ポリビニルアセタール系樹脂が好適に用いられる。これらの熱可塑性樹脂は、単独で用いてもよいし、２種類以上を併用してもよい。上記可塑化ポリビニルアセタール系樹脂における「可塑化」とは、可塑剤の添加により可塑化されていることを意味する。その他の可塑化樹脂についても同様である。
　但し、中間膜１３に発光装置１５を封入する場合、封入する物の種類によっては特定の可塑剤により劣化することがあり、その場合には、その可塑剤を実質的に含有していない樹脂を用いることが好ましい。つまり、中間膜１３が可塑剤を含まないことが好ましい場合がある。可塑剤を含有していない樹脂としては、例えば、エチレン－酢酸ビニル共重合体系樹脂等が挙げられる。
　上記ポリビニルアセタール系樹脂としては、ポリビニルアルコール（以下、必要に応じて「ＰＶＡ」と言うこともある）とホルムアルデヒドとを反応させて得られるポリビニルホルマール樹脂、ＰＶＡとアセトアルデヒドとを反応させて得られる狭義のポリビニルアセタール系樹脂、ＰＶＡとｎ－ブチルアルデヒドとを反応させて得られるポリビニルブチラール樹脂（以下、必要に応じて「ＰＶＢ」と言うこともある）等が挙げられ、特に、透明性、耐候性、強度、接着力、耐貫通性、衝撃エネルギー吸収性、耐湿性、遮熱性、及び遮音性等の諸性能のバランスに優れることから、ＰＶＢが好適なものとして挙げられる。なお、これらのポリビニルアセタール系樹脂は、単独で用いてもよいし、２種類以上を併用してもよい。
　但し、中間膜１３を形成する材料は、熱可塑性樹脂には限定されない。又、中間膜１３は、赤外線吸収剤、紫外線吸収剤、発光剤等の機能性粒子を含んでもよい。又、中間膜１３は、シェードバンドと呼ばれる着色部を有してもよい。着色部を形成するために用いられる着色顔料としては、プラスチック用として使用できるものであって、着色部の可視光線透過率が４０％以下となるものであれば良く、特に限定されるものではないが、例えば、アゾ系、フタロシアニン系、キナクリドン系、ペリレン系、ペリノン系、ジオキサジン系、アンスラキノン系、イソインドリノ系などの有機着色顔料や、酸化物、水酸化物、硫化物、クロム酸、硫酸塩、炭酸塩、珪酸塩、燐酸塩、砒酸塩、フェロシアン化物、炭素、金属粉などの無機着色顔料等が挙げられる。これらの着色顔料は、単独で用いられても良いし、２種類以上が併用されても良い。着色顔料の添加量は、着色部の可視光線透過率が４０％以下となるものであるかぎり、目的の色調に合わせて任意で良く、特に限定されるものではない。
　中間膜１３の膜厚は、最薄部で０．５ｍｍ以上であることが好ましい。なお、中間膜１３が第１の中間膜１３１及び第２の中間膜１３２からなる場合、中間膜１３の膜厚とは、第１の中間膜１３１の膜厚と第２の中間膜１３２の膜厚とを合計した膜厚である。中間膜１３の最薄部の膜厚が０．５ｍｍ以上であると合わせガラスとして必要な耐衝撃性が十分となる。又、中間膜１３の膜厚は、最厚部で３ｍｍ以下であることが好ましい。中間膜１３の膜厚の最大値が３ｍｍ以下であると、合わせガラスの質量が大きくなり過ぎない。中間膜１３の膜厚の最大値は２．８ｍｍ以下がより好ましく、２．６ｍｍ以下が更に好ましい。
　なお、中間膜１３は、３層以上の層を有していてもよい。例えば、中間膜を３層以上から形成し、両側の層を除く何れかの層のせん断弾性率を可塑剤の調整等により両側の層のせん断弾性率よりも小さくすることにより、合わせガラス１０の遮音性を向上できる。この場合、両側の層のせん断弾性率は同じでもよいし、異なってもよい。
　又、中間膜１３に含まれる中間膜１３１及び中間膜１３２は、同一の材料で形成することが望ましいが、中間膜１３１及び中間膜１３２を異なる材料で形成してもよい。但し、ガラス板１１及びガラス板１２との接着性、或いは合わせガラス１０の中に入れ込む機能材料等の観点から、中間膜１３の膜厚の５０％以上は上記の材料を使うことが望ましい。
　中間膜１３を作製するには、例えば、中間膜となる上記の樹脂材料を適宜選択し、押出機を用い、加熱溶融状態で押し出し成形する。押出機の押出速度等の押出条件は均一となるように設定する。その後、押し出し成形された樹脂膜を、合わせガラスのデザインに合わせて、上辺及び下辺に曲率を持たせるために、例えば必要に応じ伸展することで、中間膜１３が完成する。
　〔合わせガラス〕
　合わせガラス１０の総厚は、２．８ｍｍ以上１０ｍｍ以下であることが好ましい。合わせガラス１０の総厚が２．８ｍｍ以上であれば、十分な剛性を確保できる。又、合わせガラス１０の総厚が１０ｍｍ以下であれば、十分な透過率が得られると共にヘイズを低減できる。
　合わせガラス１０の少なくとも１辺において、ガラス板１１とガラス板１２の板ずれが１．５ｍｍ以下であることが好ましく、１ｍｍ以下であることがより好ましい。ここで、ガラス板１１とガラス板１２の板ずれとは、すなわち、平面視におけるガラス板１１の端部とガラス板１２の端部のずれ量である。
　合わせガラス１０の少なくとも１辺において、ガラス板１１とガラス板１２の板ずれが１．５ｍｍ以下であると、外観を損なわない点で好適である。合わせガラス１０の少なくとも１辺において、ガラス板１１とガラス板１２の板ずれが１．０ｍｍ以下であると、外観を損なわない点で更に好適である。
　合わせガラス１０を製造するには、ガラス板１１とガラス板１２との間に、中間膜１３及び発光装置１５を挟んで積層体とする。そして、例えば、この積層体をゴム袋やラバーチャンバー、樹脂製の袋等の中に入れ、ゲージ圧力－６５ｋＰａ～－１００ｋＰａの真空中で温度約７０℃～１１０℃で接着する。加熱条件、温度条件、及び積層方法は、発光装置１５の性質に配慮して、例えば、積層中に劣化しないように適宜選択される。
　更に、例えば１００℃～１５０℃、絶対圧力０．６ＭＰａ～１．３ＭＰａの条件で加熱加圧する圧着処理を行うことで、より耐久性の優れた合わせガラス１０を得られる。但し、場合によっては工程の簡略化、並びに合わせガラス１０中に封入する材料の特性を考慮して、この加熱加圧工程を使用しない場合もある。
　つまり、ガラス板１１又はガラス板１２のうち、何れか一方、又は両方のガラス板が互いに弾性変形した状態で接合されている、「コールドベンド」と呼ばれる方法を使用してもよい。コールドベンドは、テープ等の仮止め手段によって固定されたガラス板１１、ガラス板１２及び中間膜１３及び発光装置１５からなる積層体と、従来公知であるニップローラー又はゴム袋、ラバーチャンバー等の予備圧着装置及びオートクレーブを用いることで達成できる。
　ガラス板１１とガラス板１２との間に、本願の効果を損なわない範囲で、中間膜１３及び発光装置１５の他に、電熱線、赤外線反射、発光、発電、調光、タッチパネル、可視光反射、散乱、加飾、吸収等の機能を持つフィルムやデバイスを有してもよい。又、合わせガラス１０の表面に防曇、撥水、遮熱、低反射等の機能を有する膜を有していてもよい。又、ガラス板１１の車外側の面やガラス板１２の車内側の面に遮熱、発熱等の機能を有する膜を有していてもよい。
　［発光素子の非発光時の配線、発光素子、基材の視認性］
　発光装置１５において、発光素子１５２の非発光時に、基材１５１のエッジ、発光素子１５２、及び配線１５３が車内から視認されないことがデザイン性向上の観点から好ましい。特に、発光素子１５２の非発光時に、不規則にレイアウトされた配線１５３が視認されると、デザイン性を大きく低下させるため、配線１５３を車内から視認され難くすることは重要である。
　車両用のフロントサイドガラス、リアサイドガラス、リアクォーターガラス、リアガラス、ルーフガラス、エクストラウインドウ等は、法規上、可視光線透過率の規定がないため、任意の可視光線透過率に設定可能である。そこで、合わせガラス１０では、発光装置１５よりも車内側に位置する部材の合計の可視光線透過率が５０％以下としている。なお、可視光線透過率は、ＪＩＳ　Ｒ　３１０６：１９９８に準拠した方法で測定できる。
　合わせガラス１０では、発光装置１５よりも車内側に位置する部材は、ガラス板１１及び中間膜１３１である。従って、合わせガラス１０では、ガラス板１１及び中間膜１３１の２層を透過する可視光線の可視光線透過率が５０％以下である。より好ましくは、４０％以下であり、さらに好ましくは２０％以下である。
　このように、発光装置１５よりも車内側に位置する部材の合計の可視光線透過率を５０％以下とすることで、発光素子１５２の非発光時に、基材１５１のエッジ、発光素子１５２、及び配線１５３を車内から視認され難くできるため、デザイン性が向上する。
　但し、発光装置１５よりも車内側に位置する部材の合計の可視光線透過率は４０％以下がより好ましく、３０％以下がより好ましく、２０％以下がより好ましく、１０％以下がより好ましく、５％以下が更に好ましい。可視光線透過率を下げるほど、基材１５１のエッジ、発光素子１５２、及び配線１５３が車内から視認され難くなる。なお、発光装置１５よりも車内側に位置する部材の合計の可視合計の光線透過率を下げた場合でも、発光素子１５２の発光時には、発光素子１５２の出射光を車内から視認可能である。
　ガラス板１１及び中間膜１３１の可視光線透過率を５０％以下とするためには、例えば、ガラス板１１をプライバシーガラスとし、中間膜１３１をクリア中間膜とすればよい。この場合、例えば、ガラス板１１の可視光線透過率が５０％以下であり、中間膜１３１の可視光線透過率が９０％以上である。
　又、ガラス板１１及び中間膜１３１の可視光線透過率を５０％以下とするためには、ガラス板１１をグリーンガラス又はクリアガラスとし、中間膜１３１を着色中間膜としてもよい。この場合、例えば、ガラス板１１の可視光線透過率が８０％以上であり、中間膜１３１の可視光線透過率が５０％以下である。
　又、ガラス板１１及び中間膜１３１の可視光線透過率を５０％以下とするためには、ガラス板１１をプライバシーガラスとし、中間膜１３１を着色中間膜としてもよい。この場合、例えば、ガラス板１１の可視光線透過率が５０％以下であり、中間膜１３１の可視光線透過率が５０％以下である。
　ここで、グリーンガラスは、透明度の高いガラスである。グリーンガラスの可視光線透過率は、例えば、板厚が１．６ｍｍ～２．０ｍｍの場合で８３％～８８％程度である。又、クリアガラスは、グリーンガラスよりも更に透明度の高いガラスであり、可視光線透過率は、例えば、板厚が１．８ｍｍ～２．０ｍｍの場合で８８％～９２％程度である。
　クリア中間膜は、透明度の高い中間膜である。クリア中間膜の可視光線透過率は、例えば、膜厚が０．７６ｍｍの場合で９０％～９５％程度である。例えば、膜厚が０．７６ｍｍで可視光線透過率が９３．７％の製品が、積水化学工業社やイーストマン社から市販されている。
　プライバシーガラスは、グリーンガラス及びクリアガラスよりも透明度の低いガラスであり、濃グレー色ガラスとも称される。プライバシーガラスは、ガラス板１１において、Ｆｅ２Ｏ３に換算した全鉄の含有量を調整することで実現できる。プライバシーガラスの可視光線透過率は、例えば、板厚が１．８ｍｍの場合で４０％～５０％程度、板厚が２．０ｍｍの場合で３０％～４５％程度に調整可能である。
　プライバシーガラスの組成の一例を挙げると、酸化物基準の質量％表示で、ガラス母組成として、ＳｉＯ２：６６％～７５％、Ｎａ２Ｏ：１０％～２０％、ＣａＯ：５％～１５％、ＭｇＯ：０％～６％、Ａｌ２Ｏ３：０％～５％、Ｋ２Ｏ：０％～５％、ＦｅＯ：０．１３％～０．９％、Ｆｅ２Ｏ３で表した全鉄：０．８％以上、２．４％未満、ＴｉＯ２：１％超、５％以下、を含有し、当該ガラス母組成の成分の合量に対して、ＣｏＯを１００質量ｐｐｍ～５００質量ｐｐｍ、Ｓｅを０質量ｐｐｍ～７０質量ｐｐｍ、及びＣｒ２Ｏ３を０質量ｐｐｍ～８００質量ｐｐｍ含有し、かつＣｏＯ、Ｓｅ及びＣｒ２Ｏ３の合量が０．１質量％未満である。
　なお、プライバシーガラスについては、例えば、国際公開第２０１５／０８８０２６号に詳細に述べられており、その内容は本明細書に参考として援用できる。
　着色中間膜は、クリア中間膜よりも透明度の低い中間膜である。着色中間膜は、〔中間膜〕の説明で例示した材料を着色することで作製できる。具体的には、主として熱可塑性樹脂を含む組成物に着色剤を含有させることで着色中間膜が得られる。着色中間膜はガラス転移点を調整するための可塑剤を含有してもよい。
　着色剤としては、可視光線透過率を低下させるものであれば特に制限されず、染料、無機顔料、有機顔料等が挙げられる。これらの中でも、長期使用による退色のおそれが少ないことから無機顔料又は有機顔料が好ましく、耐光性に優れることから無機顔料が好ましい。
　有機顔料としては、アニリンブラック等の黒色顔料、アリザリンレーキ等の赤色顔料等が挙げられる。無機顔料としては、炭素系顔料、金属酸化物系顔料が挙げられる。例えば、カーボンブラック、アイボリーブラック、マルスブラック、ピーチブラック、ランプブラック、マグネタイト型四酸化三鉄等の黒色顔料、アンバー、バートンアンバー、イエローウォーカー、ヴァンダイクブラウン、シェンナ、バートンシェンナ等の茶色顔料、ベンガラ、モリブデンレッド、カドミウムレッド等の赤色顔料、赤口黄鉛、クロムバーミリオン等の橙色顔料、群青、紺青、コバルトブルー、セルリアンブルー等の青色顔料、酸化クロム、ピリジアン、エメラルドグリーン、コバルトグリーン等の緑色顔料、黄鉛、カドミウムイエロー、黄色酸化鉄、チタンイエロー等の黄色顔料、マンガンバイオレット、ミネラルバイオレット等の紫色顔料等が挙げられる。これらの着色剤は１種又は２種以上を組合せて使用してもよい。
　着色剤の配合量は、中間膜１３１の可視光線透過率が５０％以下になる量とする。着色中間膜は、更に、赤外線吸収剤、紫外線吸収剤、蛍光剤、接着性調整剤、カップリング剤、界面活性剤、酸化防止剤、熱安定剤、光安定剤、脱水剤、消泡剤、帯電防止剤、難燃剤等の各種添加剤の１種類又は２種類以上を含有してもよい。
　着色中間膜は、着色されていない中間膜１３１の表面に暗色で印刷層を形成して着色中間膜とする方法で作製してもよい。暗色の印刷層の形成方法は、通常の、樹脂基材への有色の材料を用いた印刷方法が適用できる。有色の材料としては、上記着色剤と同様の有機顔料や無機顔料が挙げられる。なお、この場合の印刷層は、セラミックス製の遮蔽層のようにガラスの軟化点付近の温度での耐久性は必要ないため、例えば、カーボンブラックを含む有機顔料の使用が可能である。印刷層の厚さは、中間膜１３１の可視光線透過率が５０％以下になる厚さに適宜調整可能である。
　なお、着色中間膜を用いることで、中間膜１３１の可視光線透過率を大幅に低減可能である。例えば、中間膜１３１の可視光線透過率を２０％以下、１０％以下、又は５％以下とすることも可能である。例えば、膜厚が０．７６ｍｍで可視光線透過率が１．３３％の製品、及び膜厚が０．７６ｍｍで可視光線透過率が８．９６％の製品が、積水化学工業社やイーストマン社から市販されている。又、膜厚が０．７６ｍｍで可視光線透過率が１８．００％の製品が、積水化学工業社から市販されている。
　なお、ガラス板１２の可視光線透過率を８０％以上とし、ガラス板１１の可視光線透過率を５０％以下とする場合、ガラス板１１とガラス板１２で組成を同一にできないため、両者の曲げの条件も異なる。そのため、ガラス板１１及びガラス板１２が湾曲形状である場合に、ガラス板１１とガラス板１２を合わせガラス１０の作製が容易にできる程度の形状精度で曲げることが困難である。
　そのため、ガラス板１１及びガラス板１２が湾曲形状である場合には、ガラス板１１の可視光線透過率を５０％以下とするよりも、中間膜１３１の可視光線透過率を５０％以下とする方が好ましい。この場合、ガラス板１１とガラス板１２で組成を同一にでき、両者の曲げの条件も同一にできるため、合わせガラス１０の製造が容易である。なお、可視光線透過率が５０％以下のガラス板１１と同じ組成で、同様に可視光線透過率が５０％以下のガラス板１２を用いてもよい。すなわち、ガラス板１１とガラス板１２とが同一組成であることが好ましい。
　なお、合わせガラス１０では、発光装置１５よりも車内側に位置する部材はガラス板１１及び中間膜１３１であるが、合わせガラス１０は、可視光線透過率を下げるために、発光装置１５よりも車内側にガラス板１１及び中間膜１３１以外の部材を有してもよい。
　例えば、合わせガラス１０は、発光装置１５よりも車内側にガラス板１１及び中間膜１３１の他にプライバシーフィルムを有してもよい。プライバシーフィルムは、例えば、ガラス板１１の車内側の面及び／又は車外側の面に配置できる。プライバシーフィルムとしては、例えば、スモークフィルム等の樹脂フィルムが挙げられる。
　例えば、３Ｍ社から、可視光線透過率が８％～７１％のフィルムが市販されている。又、リンテック社から、可視光線透過率が１１％～６５％のフィルムが市販されている。又、アイケーシー社から、可視光線透過率が７％～４４％のフィルムが市販されている。例えば、これらの中から、発光装置１５よりも車内側に位置する部材の合計の可視光線透過率が５０％以下となるフィルムを選択し、プライバシーフィルムとして用いることができる。
　合わせガラス１０が、発光装置１５よりも車内側にプライバシーフィルムを有する場合、ガラス板１１としてグリーンガラス及びクリアガラスを用い、中間膜１３１としてクリア中間膜を用いることも可能である。但し、プライバシーフィルムとプライバシーガラス及び／又は着色中間膜とを併用してもよい。
　このように、発光装置１５において、発光素子１５２の非発光時に、基材１５１のエッジ、発光素子１５２、及び配線１５３を車内から視認され難くするためには、発光装置１５よりも車内側に位置する部材の合計の可視光線透過率を５０％以下とすると好適である。具体的には、合わせガラス１０のうち、平面視で遮蔽層１４と重複しない部分においても、発光装置１５よりも車内側に位置する部材の合計の可視光線透過率を５０％以下とすると好適である。そして、合わせガラス１０のうち、遮蔽層１４と重複しない部分において、発光装置１５よりも車内側に位置する部材の合計の可視光線透過率は０％より大きいことが、車内から車外を視認する上で好適である。
　発光装置１５よりも車内側に位置する部材の合計の可視光線透過率は、５０％以下の範囲内において、部分的に可視光線透過率を変えてもよい。例えば、合わせガラス１０は、平面視において、基材１５１のエッジ、発光素子１５２、及び配線１５３のいずれとも重複しない部分は、基材１５１のエッジ、発光素子１５２、及び配線１５３の少なくとも１つと重複する部分よりも可視光線透過率が大きくてよい。このように、隠蔽が好ましい部位のみ可視光線透過率を下げることで、車内からの外部の視認性を確保しつつ、隠蔽が好ましい部位を視認されにくくできる。
　それに加え、発光装置１５の背景となる発光装置１５よりも車外側に位置するガラス板１２及び／又は中間膜１３２の可視光線透過率を下げてもよい。これにより、発光素子１５２の非発光時に、基材１５１のエッジ、発光素子１５２、及び配線１５３が車内から更に視認され難くなると共に、車外からも視認され難くなる。
　ガラス板１２及び／又は中間膜１３２の可視光線透過率を下げるためには、例えば、ガラス板１２をプライバシーガラスとし、中間膜１３２をクリア中間膜とすればよい。この場合、例えば、ガラス板１２の可視光線透過率が５０％以下であり、中間膜１３２の可視光線透過率が９０％以上である。
　又、ガラス板１２及び／又は中間膜１３２の可視光線透過率を下げるためには、ガラス板１２をグリーンガラス又はクリアガラスとし、中間膜１３２を着色中間膜としてもよい。この場合、例えば、ガラス板１２の可視光線透過率が８０％以上であり、中間膜１３２の可視光線透過率が５０％以下である。
　又、ガラス板１２及び／又は中間膜１３２の可視光線透過率を下げるためには、ガラス板１２をプライバシーガラスとし、中間膜１３２を着色中間膜としてもよい。この場合、例えば、ガラス板１２の可視光線透過率が５０％以下であり、中間膜１３２の可視光線透過率が５０％以下である。
　なお、図１では、合わせガラス１０の左辺及び右辺近傍の２つの領域に発光装置１５が配置される例を示したが、発光装置１５は、合わせガラス１０の左辺及び／又は右辺近傍の１つの領域に配置されてもよいし、３つ以上の領域に配置されてもよい。
　又、発光装置１５が配置される領域は、合わせガラスの左辺及び右辺近傍には限定されず、例えば、図５に示す合わせガラス１０Ａのように、上辺近傍の２つの領域Ｂに発光装置１５を配置してもよい。或いは、合わせガラス１０Ａの上辺近傍の１つ又は３つ以上の領域に、発光装置１５を配置してもよい。
　又、図６に示す合わせガラス１０Ｂのように、下辺近傍の１つの領域Ｂに、発光装置１５を配置してもよい。或いは、合わせガラス１０Ｂの下辺近傍の２つ以上の領域に、発光装置１５を配置してもよい。或いは、発光装置１５は、合わせガラスの左辺近傍、右辺近傍、上辺近傍、及び下辺近傍から選択された何れか２つ以上の領域に配置してもよい。
　又、図７に示す合わせガラス１０Ｃのように、右下の角部近傍の１つの領域Ｂに、発光装置１５を配置してもよい。或いは、合わせガラス１０Ｃの右下の角部近傍の２つ以上の領域に、発光装置１５を配置してもよい。或いは、合わせガラス１０Ｃの右上、左上、及び／又は左下の角部近傍の１つ以上の領域に、発光装置１５を配置してもよい。
　又、図８に示す合わせガラス１０Ｄのように、平面視において、遮蔽層１４の内側領域全体に発光装置１５を配置してもよい。すなわち、発光装置１５は、平面視において、遮蔽層１４と重複しない領域全体に配置されていてもよい。
　〈実施例〉
　以下、実施例について説明するが、本発明は、これらの例に何ら限定されるものではない。
　［例１］
　合わせガラスとした際に外板（車外側ガラス板）となるガラス板１２、内板（車内側ガラス板）となるガラス板１１、及び２枚の中間膜１３１及び中間膜１３２を図９の例１の層構成に合わせて準備した。ガラス板１１及びガラス板１２の寸法は、何れも、３００ｍｍ×３００ｍｍ×板厚２ｍｍとした。又、中間膜１３１及び中間膜１３２の寸法は、何れも、３００ｍｍ×３００ｍｍ×板厚０．７６ｍｍとした。又、ポリエチレンテレフタレート製の基材に長さ１．６ｍｍ×幅０．８ｍｍ×高さ０．３ｍｍのＬＥＤが複数個実装され、ＩＴＯで配線が形成された発光装置を準備した。
　なお、図９のガラス板１１及びガラス板１２の欄において、Ｐはプライバシーガラス、Ｃはクリアガラス、Ｇｒｅｅｎはグリーンガラスを示している。又、図９の中間膜１３１及び中間膜１３２の欄において、Ｃはクリア中間膜、Ｇは着色中間膜を示しており、Ｇの括弧内は中間膜単体での可視光線透過率である。図１０についても同様である。
　次にガラス板１１とガラス板１２との間に中間膜１３１と発光装置と中間膜１３２を挟んで積層体を作製し、積層体をゴム袋の中に入れ、ゲージ圧力－６５ｋＰａ～－１００ｋＰａの真空中で温度約７０℃～１１０℃で接着した。そして、絶対圧力０．６ＭＰａ～１．３ＭＰａ、温度約１００℃～１５０℃の条件で加圧及び加熱し、評価用合わせガラスＬＧ１を作製した。
　そして、評価用合わせガラスＬＧ１について、評価対象（基材のエッジ、ＬＥＤ、及び配線）の視認性の評価を行った。具体的には、評価用合わせガラスＬＧ１をガラス板１２側が下になるように白色台紙上に配置し、蛍光灯下において発光装置の全てのＬＥＤを非発光状態とした。次に、観察者の視点から発光装置までの距離を０．４ｍとして、ガラス板１１側から評価対象（基材のエッジ、ＬＥＤ、及び配線）が視認できるか否かを確認した。観察者は、１．５以上の視力を有する者を任意に１０人選択し、全員が評価対象を視認できなかった場合を〇（合格）、７人以上が視認できなかった場合を△（合格）、それ以外を×（不合格）とした。
　又、評価用合わせガラスＬＧ１について、評価用合わせガラスＧ１全体の可視光線透過率Ｔｖ１（％）と、ガラス板１１及び中間膜１３１のみの可視光線透過率Ｔｖ２（％）を、ＪＩＳ　Ｒ　３１０６：１９９８に準拠した方法で測定した。
　［例２～例８］
　ガラス板１１及びガラス板１２並びに中間膜１３１及び中間膜１３２を図９の例２～例８の層構成に合わせて準備した以外は例１と同様にして、評価用合わせガラスＬＧ２～ＬＧ８を作製した。そして、評価用合わせガラスＬＧ２～ＬＧ８について、例１と同様に、可視光線透過率Ｔｖ１及び可視光線透過率Ｔｖ２の測定と、視認性の評価を行った。
　［例９～例１７］
　ガラス板１１及びガラス板１２並びに中間膜１３１及び中間膜１３２を図１０の例９～例１７の層構成に合わせて準備した以外は例１と同様にして、評価用合わせガラスＬＧ９～ＬＧ１７を作製した。そして、評価用合わせガラスＬＧ９～ＬＧ１７について、例１と同様に、可視光線透過率Ｔｖ１及び可視光線透過率Ｔｖ２の測定と、視認性の評価を行った。
　［評価結果］
　図９及び図１０に、各々の評価用合わせガラスについて、ガラス板１１及びガラス板１２並びに中間膜１３１及び中間膜１３２の層構成と共に、可視光線透過率Ｔｖ１及び可視光線透過率Ｔｖ２、評価結果をまとめた。
　図９及び図１０の評価結果より、可視光線透過率Ｔｖ２が５０％以下であれば、発光素子の非発光時に、配線が車内側ガラス板となるガラス板１１側から視認され難くなることがわかった。そして、可視光線透過率Ｔｖ２を５０％以下とするには、ガラス板１１をプライバシーガラスとするか、中間膜１３１を着色中間膜とするか、或いはその両方を行えばよいことがわかった。
　又、ガラス板１２及び／又は中間膜１３２の透過率を下げることで、発光素子の非発光時に、配線に加えて、基材のエッジ及びＬＥＤが車内側ガラス板となるガラス板１１側から視認され難くなることがわかった。
　これらから、次のような結論が得られる。すなわち、ガラス板１１をプライバシーガラスとするか、中間膜１３１を着色中間膜とするか、或いはその両方を行って可視光線透過率Ｔｖ２を５０％以下とすることで、配線が車内側ガラス板となるガラス板１１側から視認され難くなる点で好ましい。それに加えて、ガラス板１２をプライバシーガラスとするか、中間膜１３２を着色中間膜とするか、或いはその両方を行うことで、配線と共に基材のエッジ及びＬＥＤが車内側ガラス板となるガラス板１１側から視認され難くなる点で更に好ましい。
　以上、好ましい実施形態等について詳説したが、上述した実施形態等に制限されることはなく、特許請求の範囲に記載された範囲を逸脱することなく、上述した実施形態等に種々の変形及び置換を加えることができる。
　本国際出願は２０１９年１０月３日に出願した日本国特許出願２０１９－１８２６００号に基づく優先権を主張するものであり、日本国特許出願２０１９－１８２６００号の全内容を本国際出願に援用する。
１０、１０Ａ、１０Ｂ、１０Ｃ、１０Ｄ　合わせガラス
１１、１２　ガラス板
１３、１３１、１３２　中間膜
１４　遮蔽層
１５　発光装置
１５１　基材
１５２　発光素子
１５３　配線

Claims (14)

  1. 　車内側ガラス板と、車外側ガラス板と、前記車内側ガラス板と前記車外側ガラス板を接合する中間膜と、前記中間膜に封入された発光装置と、を有する車両用の合わせガラスであって、
    　前記発光装置は、前記車内側ガラス板を介して前記車両の内部に光を出射する装置であり、
    　前記中間膜は、前記車内側ガラス板と接合する第１の中間膜と、前記車外側ガラス板と接合する第２の中間膜と、を有し、
    　前記発光装置よりも車内側に位置する部材の合計の可視光線透過率が５０％以下である合わせガラス。
  2. 　前記部材は、前記車内側ガラス板及び前記第１の中間膜であり、前記車内側ガラス板の可視光線透過率が５０％以下であり、前記第１の中間膜の可視光線透過率が９０％以上である請求項１に記載の合わせガラス。
  3. 　前記部材は、前記車内側ガラス板及び前記第１の中間膜であり、前記車内側ガラス板の可視光線透過率が８０％以上であり、前記第１の中間膜の可視光線透過率が５０％以下である請求項１に記載の合わせガラス。
  4. 　前記部材は、前記車内側ガラス板及び前記第１の中間膜であり、前記車内側ガラス板の可視光線透過率が５０％以下であり、前記第１の中間膜の可視光線透過率が５０％以下である請求項１に記載の合わせガラス。
  5. 　前記車外側ガラス板の可視光線透過率が５０％以下であり、前記第２の中間膜の可視光線透過率が９０％以上である請求項１乃至４の何れ一項に記載の合わせガラス。
  6. 　前記車外側ガラス板の可視光線透過率が８０％以上であり、前記第２の中間膜の可視光線透過率が５０％以下である請求項１乃至４の何れ一項に記載の合わせガラス。
  7. 　前記車外側ガラス板の可視光線透過率が５０％以下であり、前記第２の中間膜の可視光線透過率が５０％以下である請求項１乃至４の何れ一項に記載の合わせガラス。
  8. 　前記発光装置は、発光素子を光源とする請求項１乃至７の何れ一項に記載の合わせガラス。
  9. 　前記発光素子は、発光ダイオードである請求項８に記載の合わせガラス。
  10. 　前記発光装置は、基材と、前記基材に実装された複数の前記発光素子と、複数の前記発光素子に接続された配線と、バスバーとを有する請求項８又は９に記載の合わせガラス。
  11. 　前記発光素子の形状は、長さ０．１ｍｍ以上３．２ｍｍ以下、幅０．１ｍｍ以上２．０ｍｍ以下、高さ０．１ｍｍ以上１．０ｍｍ以下である請求項８乃至１０の何れ一項に記載の合わせガラス。
  12. 　前記車内側ガラス板の車内側の面の周縁部には遮蔽層が形成されており、前記発光装置の周縁部の少なくとも一部は、平面視において、前記遮蔽層と重複している請求項１乃至１１の何れか一項に記載の合わせガラス。
  13. 　前記発光装置の周縁部の少なくとも一部は、前記遮蔽層よりも内側に位置している請求項１２に記載の合わせガラス。
  14. 　前記車内側ガラス板及び前記車外側ガラス板は湾曲形状である請求項１乃至１３の何れ一項に記載の合わせガラス。
PCT/JP2020/035779 2019-10-03 2020-09-23 合わせガラス WO2021065616A1 (ja)