WO2021060139A1 - 透明導電性フィルムおよびその製造方法 - Google Patents

透明導電性フィルムおよびその製造方法 Download PDF

Info

Publication number
WO2021060139A1
WO2021060139A1 PCT/JP2020/035264 JP2020035264W WO2021060139A1 WO 2021060139 A1 WO2021060139 A1 WO 2021060139A1 JP 2020035264 W JP2020035264 W JP 2020035264W WO 2021060139 A1 WO2021060139 A1 WO 2021060139A1
Authority
WO
WIPO (PCT)
Prior art keywords
transparent conductive
conductive layer
layer
transparent
less
Prior art date
Application number
PCT/JP2020/035264
Other languages
English (en)
French (fr)
Inventor
正憲 松本
浩史 別府
智宏 竹安
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Priority to KR1020227008630A priority Critical patent/KR20220064963A/ko
Priority to US17/763,896 priority patent/US20220351878A1/en
Priority to CN202080067103.3A priority patent/CN114467150A/zh
Publication of WO2021060139A1 publication Critical patent/WO2021060139A1/ja

Abstract

透明導電性フィルムは、透明基材と、硬化樹脂層と、透明導電層とを順に備える。透明導電層の膜密度は、６．８５ｇ／ｃｍ３未満である。

Description

透明導電性フィルムおよびその製造方法
　本発明は、透明導電性フィルムおよびその製造方法に関し、詳しくは、詳しくは、光学用途に好適に用いられる透明導電性フィルム、および、その透明導電性フィルムの製造方法に関する。
　従来から、インジウムスズ複合酸化物（ＩＴＯ）からなる透明導電層を所望の電極パターンに形成した透明導電性フィルムが、タッチパネルなどの光学用途に用いられる。
　透明導電性フィルムとしては、例えば、可撓性基材フィルムとハードコート層と透明導電層とを順に備えるが提案されている（例えば、特許文献１参照。）。
　そして、特許文献１の透明導電性フィルムでは、１５０℃で加熱処理をすることによって、透明導電層（ＩＴＯ膜）を結晶化させている。
特開２０１８－０１２２９０公報
　しかるに、特許文献１の透明導電性フィルムでは、高温（１５０℃）で、透明導電層（ＩＴＯ膜）を結晶化させているため、結晶化中（加熱中）には、熱によって、ハードコート層および透明導電層が膨張する。そして、結晶化後（加熱停止後）には、膨張したハードコート層および透明導電層は、収縮する。
　そして、このような透明導電性フィルムは、常温条件下（例えば、２０℃程度）では、視認性に問題が生じることはないが、この透明導電性フィルムを加湿条件下（例えば、６５℃、相対湿度９５％）に置くと、ハードコート層だけが大きく収縮する。そのため、加湿条件下に置いた後のフィルム表面にはマイクロメートルオーダーの微細なうねりのような模様が生じる。これにより、フィルムの表面に不規則な光沢が生じ、視認性が低下するという不具合がある。
　本発明の目的は、加湿信頼性に優れる透明導電性フィルム、および、その透明導電性フィルムの製造方法を提供することにある。
　本発明［１］は、透明基材と、硬化樹脂層と、透明導電層とを順に備え、前記透明導電層の膜密度が、６．８５ｇ／ｃｍ３未満である、透明導電性フィルムである。
　本発明［２］は、前記透明基材の厚みが、５０μｍ未満である、上記［１］に記載の透明導電性フィルムを含んでいる。
　本発明［３］は、前記透明導電層が、結晶質であることを特徴とする、請求項［１］または［２］に記載の透明導電性フィルムを含んでいる。
　本発明［４］は、透明基材を準備する第１工程と、前記透明基材の上面に、硬化樹脂層を積層する第２工程と、前記硬化樹脂層の上面に、透明導電層を積層する第３工程とを備え、前記第３工程では、前記透明導電層を２０℃以上３０℃以下で静置、または、前記透明導電層を６０℃未満で加熱することにより、前記透明導電層を結晶化させ、前記透明導電層の膜密度が、６．８５ｇ／ｃｍ３未満である、透明導電性フィルムの製造方法である。
　本発明の透明導電性フィルムは、透明基材と、硬化樹脂層と、透明導電層とを順に備え、透明導電層の膜密度が、６．８５ｇ／ｃｍ３未満である。
　これにより、加湿条件下における硬化樹脂層の収縮を抑制することができ、視認性の低下を抑制できる。その結果、加湿信頼性に優れる。
　本発明の透明導電性フィルムの製造方法は、透明導電層を、２０℃以上３０℃以下で静置、または、透明導電層を６０℃未満で加熱することにより、膜密度が小さくなるように、透明導電層を結晶化させる。
　これにより、加湿条件下における硬化樹脂層の収縮を抑制することができ、視認性の低下を抑制できる。その結果、加湿信頼性に優れる。
図１は、本発明の透明導電性フィルムの断面図を示す。
　図１を参照して、本発明の透明導電性フィルムの一実施形態を説明する。
　図１において、紙面上下方向は、上下方向（厚み方向）であって、紙面上側が、上側（厚み方向一方側）、紙面下側が、下側（厚み方向他方側）である。また、紙面左右方向および奥行き方向は、上下方向に直交する面方向である。具体的には、各図の方向矢印に準拠する。
　１．透明導電性フィルム
　透明導電性フィルム１は、所定の厚みを有するフィルム形状（シート形状を含む）を有し、厚み方向と直交する所定方向（面方向）に延び、平坦な上面および平坦な下面を有する。透明導電性フィルム１は、例えば、画像表示装置に備えられるタッチパネル用基材や電磁波シールドなどの一部品であり、つまり、画像表示装置ではない。すなわち、透明導電性フィルム１は、画像表示装置などを作製するための部品であり、ＯＬＥＤモジュールなどの画像表示素子を含まず、透明基材２と硬化樹脂層３と透明導電層４とを含み、部品単独で流通し、産業上利用可能なデバイスである。
　具体的には、図１に示すように、透明導電性フィルム１は、透明基材２と、透明基材２の上面（厚み方向一方面）に配置される硬化樹脂層３と、硬化樹脂層３の上面に配置される透明導電層４とを備える。より具体的には、透明導電性フィルム１は、透明基材２と、硬化樹脂層３と、透明導電層４とをこの順に備える。透明導電性フィルム１は、好ましくは、透明基材２と硬化樹脂層３と透明導電層４とからなる。
　２．透明基材
　透明基材２は、透明導電性フィルム１の機械強度を確保するための透明な基材である。
すなわち、透明基材２は、透明導電層４を、硬化樹脂層３とともに支持している。
　透明基材２は、透明導電性フィルム１の最下層であって、フィルム形状を有する。透明基材２は、硬化樹脂層３の下面に接触するように、硬化樹脂層３の下面全面に、配置されている。
　透明基材２は、例えば、透明性を有する高分子フィルムである。透明基材２の材料としては、例えば、ポリエチレン、ポリプロピレン、シクロオレフィンポリマーなどのオレフィン樹脂、例えば、ポリエチレンテレフタレート（ＰＥＴ）、ポリブチレンテレフタレート、ポリエチレンナフタレートなどのポリエステル樹脂、例えば、ポリメタクリレートなどの（メタ）アクリル樹脂（アクリル樹脂および／またはメタクリル樹脂）、例えば、ポリカーボネート樹脂、ポリエーテルスルフォン樹脂、ポリアリレート樹脂、メラミン樹脂、ポリアミド樹脂、ポリイミド樹脂、セルロース樹脂、ポリスチレン樹脂などが挙げられる。透明基材２は、単独使用または２種以上併用することができる。
　好ましくは、非結晶性の熱可塑性樹脂が挙げられる。これにより、所望の偏光軸を有することができる。また、透明性も優れる。
　このような非結晶性の熱可塑性樹脂としては、好ましくは、シクロオレフィンポリマーが挙げられる。すなわち、透明基材２は、好ましくは、シクロオレフィンポリマーから形成されるシクロオレフィン系フィルムである。
　シクロオレフィン系ポリマーは、シクロオレフィンモノマーを重合して得られ、主鎖の繰り返し単位中に脂環構造を有する高分子である。シクロオレフィン系樹脂は、好ましくは、非晶質シクロオレフィン系樹脂である。
　シクロオレフィン系ポリマーとしては、例えば、シクロオレフィンモノマーからなるシクロオレフィンホモポリマー、例えば、シクロオレフィンモノマーと、エチレンなどのオレフィンなどとの共重合体からなるシクロオレフィンコポリマーなどが挙げられる。
　シクロオレフィンモノマーとしては、例えば、ノルボルネン、メチルノルボルネン、ジメチルノルボルネン、エチリデンノルボルネン、ブチルノルボルネン、ジシクロペンタジエン、ジヒドロジシクロペンタジエン、テトラシクロドデセン、トリシクロペンタジエンなどの多環式オレフィン、例えば、シクロブテン、シクロペンテン、シシクロオクタジエン、シクロオクタトリエンなどの単環式オレフィンなどが挙げられる。好ましくは、多乾式オレフィンが挙げられる。これらシクロオレフィンは、単独使用または２種以上併用することができる。
　透明基材２の全光線透過率（ＪＩＳ　Ｋ　７３７５－２００８）は、例えば、８０％以上、好ましくは、８５％以上である。
　透明基材２の厚みは、機械的強度などの観点から、例えば、２μｍ以上、好ましくは、２０μｍ以上であり、また、例えば、３００μｍ以下、好ましくは、１５０μｍ以下、より好ましくは、屈曲性の観点から、５０μｍ未満である。透明基材２の厚みは、例えば、マイクロゲージ式厚み計を用いて測定することができる。
　３．硬化樹脂層
　硬化樹脂層３は、透明導電性フィルム１を製造する際に、透明基材２に傷が発生することを抑制するための保護層である。また、複数の透明導電性フィルム１を積層した場合に、透明導電層４に擦り傷が発生することを抑制するための耐擦傷層である。
　硬化樹脂層３は、フィルム形状を有する。硬化樹脂層３は、透明基材２の上面全面に、透明基材２の上面に接触するように、配置されている。より具体的には、硬化樹脂層３は、透明基材２と透明導電層４との間に、透明基材２の上面および透明導電層４の下面に接触するように、配置されている。
　硬化樹脂層３は、硬化性樹脂組成物から形成されている。硬化性樹脂組成物は、硬化性樹脂を含有する。
　硬化性樹脂としては、例えば、活性エネルギー線（具体的には、紫外線、電子線など）の照射により硬化する活性エネルギー線硬化性樹脂、例えば、加熱により硬化する熱硬化性樹脂などが挙げられ、好ましくは、活性エネルギー線硬化性樹脂が挙げられる。
　活性エネルギー線硬化性樹脂は、例えば、分子中に重合性炭素－炭素二重結合を有する官能基を有するポリマーが挙げられる。そのような官能基としては、例えば、ビニル基、（メタ）アクリロイル基（メタクリロイル基および／またはアクリロイル基）などが挙げられる。
　活性エネルギー線硬化性樹脂としては、具体的には、例えば、ウレタンアクリレート、エポキシアクリレートなどの（メタ）アクリル系紫外線硬化性樹脂が挙げられる。
　また、活性エネルギー線硬化性樹脂以外の硬化性樹脂としては、例えば、ウレタン樹脂、メラミン樹脂、アルキド樹脂、シロキサン系ポリマー、有機シラン縮合物などが挙げられる。
　これら樹脂は、単独使用または２種以上併用することができる。
　硬化性樹脂組成物は、粒子を含有することもできる。これにより、硬化樹脂層３を、耐ブロッキング特性を有するアンチブロッキング層とすることができる。
　粒子としては、有機粒子、無機粒子などが挙げられる。有機粒子としては、例えば、架橋アクリル・スチレン樹脂粒子などの架橋アクリル系粒子などが挙げられる。無機粒子としては、例えば、シリカ粒子、例えば、酸化ジルコニウム、酸化チタン、酸化亜鉛、酸化スズなどからなる金属酸化物粒子、例えば、炭酸カルシウムなどの炭酸塩粒子などが挙げられる。粒子は、単独使用または２種以上併用することができる。
　好ましくは、硬化性樹脂組成物は、粒子を含まず、硬化性樹脂を含む。
　硬化性樹脂組成物には、さらに、レベリング剤、チクソトロピー剤、帯電防止剤など
の公知の添加剤を含有することができる。
　硬化樹脂層３の厚みは、耐擦傷性の観点から、例えば、０．１μｍ以上、好ましくは、０．５μｍ以上であり、また、例えば、１０μｍ以下、好ましくは、３μｍ以下である。
硬化樹脂層３の厚みは、例えば、瞬間マルチ測光システム（例えば、大塚電子社製、「ＭＣＰＤ２０００」）を用いて観測される干渉スペクトルの波長に基づいて算出することができる。
　４．透明導電層
　透明導電層４は、結晶質であり、優れた導電性を発現する透明な層である。
　透明導電層４は、透明導電性フィルム１の最上層であって、フィルム形状を有する。透明導電層４は、硬化樹脂層３の上面全面に、硬化樹脂層３の上面に接触するように、配置されている。
　透明導電層４は、Ｓｎ領域５、Ｓｎ／Ｈｆ混合領域６、および、Ｈｆ領域７を、下側から順に有する。
　透明導電層４は、Ｈｆ領域７とＳｎ領域５とを厚み方向に有するため、優れた結晶化速度および導電性の両立を達成することができる。すなわち、詳しくは後述するが、低温で透明導電層４を短時間で結晶化させることができるとともに、透明導電性フィルム１は優れた導電性を発現する。
　Ｓｎ領域５は、硬化樹脂層３の上面において面方向に延びるように形成されている下層である。Ｓｎ領域５は、スズ（Ｓｎ）を含有するインジウム系酸化物から形成され、好ましくは、インジウムスズ複合酸化物（ＩＴＯ）から形成されている。
　Ｓｎ領域５において、酸化スズ（ＳｎＯ２）含有量は、酸化スズおよび酸化インジウム（Ｉｎ２Ｏ３）の合計量に対して、例えば、０．５質量％以上、好ましくは、３質量％以上であり、また、例えば、１５質量％以下、好ましくは、１３質量％以下である。酸化スズの含有量が上記下限以上であれば、透明導電層４の結晶速度を良好にすることができる。酸化スズの含有量が上記上限以下であれば、透明導電層４の導電性を良好にすることができる。
　Ｓｎ領域５は、ＳｎおよびＩｎ以外の金属として、不可避的不純物を含んでもよい。
　また、Ｓｎ領域５は、Ｈｆを実質的に含有しない。すなわち、Ｓｎ領域５では、Ｘ線光電子分光法による測定において、Ｈｆ元素を検出しない。
　Ｓｎ領域５の厚みは、例えば、１ｎｍ以上、好ましくは、３ｎｍ以上、好ましくは、１０ｎｍ以上であり、また、例えば、５０ｎｍ以下、好ましくは、４０ｎｍ以下、より好ましくは、３０ｎｍ以下である。各領域の厚みは、Ｘ線光電子分光法により、透明導電層４を厚み方向に測定することにより求めることができる。
　Ｓｎ／Ｈｆ混合領域６において、Ｓｎ領域５の上側において面方向に延びるように形成されている中間層である。Ｓｎ／Ｈｆ混合領域６は、Ｓｎ領域５に含まれる元素とＨｆ領域７に含まれる元素との両方が混在する。具体的には、Ｓｎ、ＨｆおよびＩｎを含有する酸化物から形成されている。また、Ｓｎ／Ｈｆ混合領域６は、Ｔａ（タンタル）を含有していてもよく、その場合は、Ｓｎ、Ｈｆ、ＴａおよびＩｎを含有する酸化物から形成されている。
　好ましくは、Ｓｎ／Ｈｆ混合領域６は、Ｓｎ領域５から、Ｈｆ領域７に徐々に変化する領域である。すなわち、Ｓｎ／Ｈｆ混合領域６の下端から上端に向かうに従って、Ｓｎ元素の含有割合が次第に減少するとともに、Ｈｆの含有割合が次第に増加する。換言すれば、透明導電層４内の断面は、界面を有しない。すなわち、透明導電層４は、Ｓｎ領域－Ｓｎ／Ｈｆ混合領域界面（６／７界面）、および、Ｓｎ／Ｈｆ混合領域－Ｈｆ領域界面（７／８界面）の両方を有しない。
　Ｓｎ／Ｈｆ混合領域６の厚みは、例えば、１ｎｍ以上、好ましくは、２ｎｍ以上、好ましくは、３ｎｍ以上であり、また、例えば、１０ｎｍ以下、好ましくは、８ｎｍ以下、より好ましくは、６ｎｍ以下である。
　Ｈｆ領域７は、Ｓｎ／Ｈｆ混合領域６の上側において面方向に延びるように形成されている上層である。Ｈｆ領域７は、ハフニウム（Ｈｆ）を含有するインジウム系酸化物から形成され、好ましくは、Ｈｆ、Ｔａ（タンタル）およびＩｎを含有する酸化物から形成されている。
　Ｈｆの含有割合（原子比）は、Ｔａを含まない場合、Ｈｆ／（Ｈｆ＋Ｉｎ）として、例えば、０．２ａｔ％以上、好ましくは、０．５ａｔ％以上であり、また、例えば、３．０ａｔ％以下、好ましくは、２．５ａｔ％以下である。
　一方、Ｈｆの含有割合（原子比）は、Ｔａを含む場合、Ｈｆ／（Ｈｆ＋Ｔａ＋Ｉｎ）として、例えば、０．２ａｔ％以上、好ましくは、０．５ａｔ％以上であり、また、例えば、３．０ａｔ％以下、好ましくは、２．５ａｔ％以下である。
　Ｔａの含有割合（原子比）は、Ｔａ／（Ｈｆ＋Ｔａ＋Ｉｎ）として、例えば、０．０２ａｔ％以上、好ましくは、０．１ａｔ％以上であり、また、例えば、１．３ａｔ％以下、好ましくは、１．０ａｔ％以下である。
　Ｉｎの含有割合（原子比）は、Ｉｎ／（Ｈｆ＋Ｉｎ）またはＩｎ／（Ｈｆ＋Ｔａ＋Ｉｎ）として、例えば、９５．０ａｔ％以上、好ましくは、９７．０ａｔ％以上であり、また、例えば、９９．７ａｔ％以下、好ましくは、９９．０ａｔ％以下である。
　Ｈｆ領域７は、Ｈｆ、ＴａおよびＩｎ以外の金属として、不可避的不純物を含んでもよい。
　また、Ｈｆ領域７は、Ｓｎを実質的に含有しない。すなわち、Ｈｆ領域７では、Ｘ線光電子分光法による測定において、Ｓｎ元素を検出しない。
　Ｈｆ領域７の厚みは、例えば、１ｎｍ以上、好ましくは、３ｎｍ以上、好ましくは、８ｎｍ以上であり、また、例えば、５０ｎｍ以下、好ましくは、４０ｎｍ以下、より好ましくは、３０ｎｍ以下である。
　Ｈｆ領域７の厚みは、好ましくは、Ｓｎ領域５の厚みよりも厚い。これにより、低温度での結晶化速度がより一層優れる。
　透明導電層４の上面の表面抵抗率は、例えば、１００Ω／□以下、好ましくは、８０Ω／□以下であり、また、例えば、１０Ω／□以上である。表面抵抗率は、４端子法により測定することができる。
　透明導電層４の上面の比抵抗は、例えば、３．０×１０－４Ω・ｃｍ以下、好ましくは、２．５×１０－４Ω・ｃｍ以下であり、また、例えば、１．０×１０－４Ω・ｃｍ以上である。比抵抗は、４端子法により測定することができる。
　透明導電層４全体の厚みは、例えば、５ｎｍ以上、好ましくは、１０ｎｍ以上であり、また、例えば、８０ｎｍ以下、好ましくは、３５ｎｍ以下である。透明導電層４の厚みを上記範囲とすることにより、低温度での結晶化速度および導電性の両立をより確実に達成することができる。透明導電層４の全体の厚みは、例えば、透過型電子顕微鏡を用いて、透明導電性フィルム１の断面を観察することにより測定することができる。
　透明導電層４は、結晶質である。
　透明導電層４が、結晶質であれば、上記の表面抵抗率を低くできる。
　透明導電層４の結晶質性は、例えば、透明導電性フィルム１を塩酸（２０℃、濃度５質量％）に１５分間浸漬し、続いて、水洗および乾燥した後、透明導電層４側の表面に対して１５ｍｍ程度の間の端子間抵抗を測定することにより判断できる。上記浸漬・水洗・乾燥後の透明導電性フィルム１において、１５ｍｍ間の端子間抵抗が１０ｋΩ以下である場合、透明導電層は結晶質であり、一方、上記抵抗が１０ｋΩを超過する場合、透明導電層４は非晶質である。
　５．透明導電性フィルムの製造方法
　透明導電性フィルム１を製造する方法を説明する。透明導電性フィルムの製造方法は、透明基材２を準備する第１工程と、透明基材２の上面に、硬化樹脂層３を積層する第２工程と、硬化樹脂層３の上面に、透明導電層４を積層する第３工程とを備える。
　まず、第１工程では、公知または市販の透明基材２を用意する。好ましくは、シクロオレフィン系フィルムを用意する。
　その後、必要に応じて、透明基材２と、硬化樹脂層３との密着性の観点から、透明基材２の上面に、例えば、スパッタリング、コロナ放電、火炎、紫外線照射、電子線照射、化成、酸化などのエッチング処理や下塗り処理を実施することができる。また、溶剤洗浄、超音波洗浄などにより透明基材２を除塵、清浄化することができる。
　次いで、第２工程では、透明基材２の上面に、硬化樹脂層３を積層する。例えば、透明基材２の上面に硬化性樹脂組成物を湿式塗工することにより、透明基材２の上面に硬化樹脂層３を形成する。
　具体的には、例えば、硬化性樹脂組成物を溶媒で希釈した溶液（ワニス）を調製し、続いて、硬化性樹脂組成物溶液を透明基材２の上面に塗布して、乾燥する。
　溶媒としては、例えば、有機溶媒、水系溶媒（具体的には、水）などが挙げられ、好ましくは、有機溶媒が挙げられる。有機溶媒としては、例えば、メタノール、エタノール、イソプロピルアルコールなどのアルコール化合物、例えば、アセトン、メチルエチルケトン、メチルイソブチルケトンなどのケトン化合物、例えば、酢酸エチル、酢酸ブチルなどのエステル化合物、プロピレングリコールモノメチルエーテルなどのエーテル化合物、例えば、トルエン、キシレンなどの芳香族化合物などが挙げられる。これら溶媒は、単独使用または２種以上併用することができる。
　硬化性樹脂組成物溶液における固形分濃度は、例えば、１質量％以上、好ましくは、１０質量％以上であり、また、例えば、３０質量％以下、好ましくは、２０質量％以下である。
　塗布方法は、硬化性樹脂組成物溶液および透明基材２に応じて適宜選択することができる。塗布方法としては、例えば、ディップコート法、エアーナイフコート法、カーテンコート法、ローラーコート法、ワイヤーバーコート法、グラビアコート法、エクストルージョンコート法などが挙げられる。
　乾燥温度は、例えば、５０℃以上、好ましくは、７０℃以上であり、例えば、１５０℃以下、好ましくは、１００℃以下である。
　乾燥時間は、例えば、０．５分以上、好ましくは、１分以上であり、例えば、６０分以下、好ましくは、２０分以下である。
　その後、硬化性樹脂組成物が活性エネルギー線硬化性樹脂を含有する場合は、硬化性樹脂組成物溶液の乾燥後に、活性エネルギー線を照射することにより、活性エネルギー線硬化性樹脂を硬化させる。
　なお、硬化性樹脂組成物が熱硬化性樹脂を含有する場合は、この乾燥工程により、溶媒の乾燥とともに、熱硬化性樹脂を熱硬化することができる。
　次いで、第３工程では、硬化樹脂層３の上面に、透明導電層４を積層する。例えば、乾式方法により、硬化樹脂層３の上面に透明導電層４を形成する。
　透明導電層４の形成では、Ｓｎ領域５およびＨｆ領域７をこの順で形成する。好ましくは、Ｓｎ領域５およびＨｆ領域７を同一の乾式方法にて連続して形成する。これにより、Ｓｎ領域５とＨｆ領域７との界面にて、互いに成分が混在して、Ｓｎ／Ｈｆ混合領域６が形成される。
　乾式方法としては、例えば、真空蒸着法、スパッタリング法、イオンプレーティング法などが挙げられる。好ましくは、スパッタリング法が挙げられる。この方法によって所望の透明導電層４を形成することができる。
　スパッタリング法としては、例えば、２極スパッタリング法、ＥＣＲ（電子サイクロトロン共鳴）スパッタリング法、マグネトロンスパッタリング法、イオンビームスパッタリング法などが挙げられる。好ましくは、マグネトロンスパッタリング法が挙げられる。
　Ｓｎ領域５の形成におけるターゲット材としては、Ｓｎを含有するインジウム系酸化物が挙げられる。好ましくは、ＩＴＯ（Ｉｎ－Ｓｎ含有酸化物）が挙げられる。
　Ｓｎ領域５の形成において、スパッタリングガスとしては、例えば、Ａｒなどの不活性ガスが挙げられる。また、必要に応じて、酸素ガスなどの反応性ガスを併用することができる。反応性ガスを併用する場合において、反応性ガスの流量比は、スパッタガスおよび反応性ガスの合計流量比に対して、例えば、０．１流量％以上５流量％以下である。
　スパッタリング法は、真空下で実施される。具体的には、スパッタリング時の気圧は、スパッタリングレートの低下抑制、放電安定性などの観点から、例えば、１Ｐａ以下、好ましくは、０．７Ｐａ以下である。
　スパッタリング法に用いる電源は、例えば、ＤＣ電源、ＡＣ電源、ＭＦ電源およびＲＦ電源のいずれであってもよく、また、これらの組み合わせであってもよい。
　スパッタリング装置の設定厚み（目標値）は、例えば、５ｎｍ以上、好ましくは、１０ｎｍ以上、より好ましくは、１２ｎｍ以上であり、また、例えば、５０ｎｍ以下、好ましくは、３０ｎｍ以下、よりＤＣ好ましくは、２０ｎｍ以下である。
　Ｈｆ領域７の形成において、ターゲット材としては、Ｈｆを含有するインジウム系酸化物が挙げられる。好ましくはＩｎ、ＨｆおよびＴａを含有する酸化物（Ｉｎ－Ｈｆ－Ｔａ含有酸化物）が挙げられる。このようなターゲットの具体例としては、例えば、特開平１０－２６９８４３号公報、特開２０１７－１４９６３６号公報、特開２０１８－１８８６７７号公報などに記載の酸化物焼結体が挙げられる。
　スパッタリング装置の設定厚みは、例えば、５ｎｍ以上、好ましくは、１０ｎｍ以上、より好ましくは、１５ｎｍ以上であり、また、例えば、５０ｎｍ以下、好ましくは、３０ｎｍ以下、より好ましくは、２５ｎｍ以下である。
　Ｈｆ領域７の形成において、スパッタリング法の条件は、上記以外は、Ｓｎ領域５の形成と同様の条件が挙げられる。
　なお、所望厚みの透明導電層４を形成するために、ターゲット材やスパッタリングの条件などを適宜設定して複数回スパッタリングを実施してもよい。
　これにより、透明基材２、硬化樹脂層３および非晶質の透明導電層４を順に備える非晶性透明導電性フィルムが得られる。
　次いで、第３工程では、透明導電層４を所定の温度で静置または加熱することにより、透明導電層４を結晶化させる。
　透明導電層４を静置することにより、結晶化させるには、具体的には、非晶性透明導電性フィルムを、大気中で、２０℃以上３０℃以下、例えば、２４時間以上４８０時間以下の条件の下で静置する。
　静置する際の温度が、上記上限以下であれば、透明導電層４の膜密度（後述）を低くすることができる。
　静置する際の温度が、上記下限以上であれば、透明導電層４を確実に結晶化させることができる。
　また、静置する際の時間が、上記範囲内であれば、透明導電層４を確実に結晶化させることができる。
　また、透明導電層４を加熱することにより、結晶化させるには、非晶性透明導電性フィルムを大気下で加熱する。
　加熱は、例えば、赤外線ヒーター、オーブンなどを用いて実施することができる。
　加熱温度は、６０℃未満、好ましくは、４０℃以下であり、また、例えば、２５℃以上である。
　加熱温度が、上記上限以下であれば、透明導電層４の膜密度（後述）を低くすることができる。
　加熱温度が、上記下限以上であれば、透明導電層４を確実に結晶化させることができる。
　加熱時間は、例えば、１分以上、好ましくは、１０分以上であり、また、例えば、６０分以下、好ましくは、３０分以下である。
　加熱時間が上記下限以上であれば、透明導電層４を確実に結晶化することができる。一方、加熱時間が上記上限以下であれば、生産効率に優れる。
　これにより、透明導電層４が結晶化され、図１に示すように、透明基材２、硬化樹脂層３および透明導電層４を順に備える透明導電性フィルム１が得られる。透明導電層４は、結晶質であって、Ｓｎ領域５、Ｓｎ／Ｈｆ混合領域６およびＨｆ領域７を下から順に備える。
　なお、上記製造方法では、ロールトゥロール方式にて、透明基材２を搬送させながら、その透明基材２に、硬化樹脂層３および透明導電層４を形成してもよく、また、これらの層の一部または全部をバッチ方式（枚葉方式）にて形成してもよい。生産性の観点から、好ましくは、ロールトゥロール方式にて、透明基材２を搬送させながら、透明基材２に各層を形成する。
　得られる透明導電性フィルム１の厚みは、例えば、２μｍ以上、好ましくは、２０μｍ以上であり、また、例えば、１００μｍ以下、好ましくは、５０μｍ以下である。
　また、透明導電性フィルム１において、透明導電層４の膜密度は、６．８５ｇ／ｃｍ３未満、好ましくは、６．８０ｇ／ｃｍ３以下、より好ましくは、６．７５ｇ／ｃｍ３以下、さらに好ましくは、６．７１ｇ／ｃｍ３以下である。
　透明導電層４の膜密度が、上記上限以下であれば、加湿信頼性に優れる。
　詳しくは、例えば、特許文献１のように、透明導電層４を高温（１５０℃）で結晶化させると、結晶化中（加熱中）には、熱によって、硬化樹脂層３および透明導電層４が膨張する。そして、結晶化後（加熱停止後）には、膨張した硬化樹脂層３および透明導電層４は、収縮する。
　そして、このような透明導電性フィルム１を、常温条件下（例えば、２０℃程度）に置いても、視認性に問題が生じることはないが、加湿条件下（例えば、６０℃以上７０℃以下、相対湿度８０％以上９０％以下）に置くと、硬化樹脂層３が大きく収縮する。そのため、加湿条件下に置いた後の透明導電性フィルム１の表面にはマイクロメートルオーダーの微細なうねりのような模様が生じる。これにより、透明導電性フィルム１の表面に不規則な光沢が生じ、視認性が低下するという不具合がある。
　一方、上記の透明導電性フィルム１の製造方法では、透明導電層４を、低温（２０℃以上３０℃以下）で静置するか、または、低温（６０℃未満）で加熱することで、透明導電層４の膜密度が低くなるように、具体的には、膜密度が６．８５ｇ／ｃｍ３未満になるように結晶化させる。
　これにより、上記した加湿条件下における硬化樹脂層３の収縮を抑制することができ、視認性の低下を抑制できる。つまり、加湿信頼性に優れる。
　なお、上記の膜密度は、後述する実施例の条件に従って、Ｘ線反射率法により測定することができる。
　このような透明導電性フィルム１は、例えば、光学装置に備えられる。光学装置としては、例えば、画像表示装置などが挙げられる。透明導電性フィルム１を画像表示装置（具体的には、ＯＬＥＤモジュール、ＬＣＤモジュールなどの画像表示素子を有する画像表示装置）に備える場合には、透明導電性フィルム１は、必要に応じてパターニングされて、例えば、電磁波シールド、タッチパネル用基材などとして用いられる。タッチパネル用基材として用いられる場合、タッチパネルの形式としては、例えば、光学方式、超音波方式、静電容量方式、抵抗膜方式などの各種方式が挙げられ、静電容量方式のタッチパネルに好適に用いられる。
６．変形例
　上記した説明では、透明導電層４は、Ｓｎ領域５とＨｆ領域７との間に配置されるＳｎ／Ｈｆ混合領域６を備えているが、Ｓｎ／Ｈｆ混合領域６を備えなくてもよい。
　また、上記した説明では、透明導電層４は、Ｓｎ領域５、Ｓｎ／Ｈｆ混合領域６およびＨｆ領域７を下から順に備えたが、透明導電層４は、Ｈｆ領域７、Ｓｎ／Ｈｆ混合領域６、および、Ｓｎ領域５を、下側から順に備えることもでき、また、透明導電層４は、Ｈｆ領域７、Ｓｎ／Ｈｆ混合領域６、Ｓｎ領域５、Ｓｎ／Ｈｆ混合領域６、および、Ｈｆ領域７を下側から順に備えることでもきる。
　また、上記した説明では、透明導電層４は、Ｓｎ領域５、Ｓｎ／Ｈｆ混合領域６、および、Ｈｆ領域７を備えた多層構造であるが、これに限定されず、単層構造でもよい。
　透明導電層４が単層構造である場合には、透明導電層４は、例えば、Ｉｎ、Ｓｎ、Ｚｎ、Ｇａ、Ｓｂ、Ｔｉ、Ｓｉ、Ｚｒ、Ｍｇ、Ａｌ、Ａｕ、Ａｇ、Ｃｕ、Ｐｄ、Ｗからなる群より選択される少なくとも１種の金属を含む金属酸化物などの材料から形成される。
　透明導電層４は、好ましくは、インジウムスズ複合酸化物（ＩＴＯ）などのインジウム含有酸化物から形成される。
　以下に実施例および比較例を示し、本発明をさらに具体的に説明する。なお、本発明は、何ら実施例および比較例に限定されない。また、以下の記載において用いられる配合割合（含有割合）、物性値、パラメータなどの具体的数値は、上記の「発明を実施するための形態」において記載されている、それらに対応する配合割合（含有割合）、物性値、パラメータなど該当記載の上限値（「以下」、「未満」として定義されている数値）または下限値（「以上」、「超過」として定義されている数値）に代替することができる。
１．透明導電性フィルムの製造
　　実施例１
　透明基材として、シクロオレフィン系フィルム（厚み２２μｍ、日本ゼオン社製、「ゼオノアフィルム」）を用意した。
　透明基材の上面に、紫外線硬化性アクリル樹脂を含有する硬化性樹脂組成物溶液を塗布および乾燥した。その後、紫外線照射により硬化性樹脂組成物を硬化させた。これにより、厚み１．０μｍの硬化樹脂層を形成した。
　次いで、硬化樹脂層の上面に、透明導電層を形成した。
　具体的には、ＤＣスパッタリング法によって、スパッタ出力の設定厚みを２１ｎｍに調整して、ＩＴＯ焼結体（９０ｗｔ％酸化インジウムおよび１０ｗｔ％酸化スズ含有）をスパッタリングした。真空条件は、アルゴンガス９８％および酸素ガス２％を導入し、気圧を０．４Ｐａとした。これにより、厚み２４μｍの非晶質のＩＴＯ層を形成した。
　次いで、このＩＴＯ層の上面にスパッタ出力の設定厚みを５ｎｍに調整して、ＩＴＯ焼結体（９６．７ｗｔ％酸化インジウムおよび３．３ｗｔ％酸化スズ含有）をスパッタリングした。真空条件は、アルゴンガス９８％および酸素ガス２％を導入し、気圧を０．４Ｐａとした。これにより、厚み５ｎｍの非晶質のＩＴＯ層を形成した。
　その後、ＩＴＯ層の上面に、ＤＣスパッタリング法によって、スパッタ出力の設定厚みを１０ｎｍに調整して、Ｉｎ－Ｈｆ－Ｔａ含有酸化物焼結体（東ソー社製、商品名「ＵＳＲ」）をスパッタリングした。真空条件は、アルゴンガス９８％および酸素ガス２％を導入し、気圧を０．４Ｐａとした。これにより、厚み５μｍの非晶質のＩｎ－Ｈｆ－Ｔａ含有酸化物層を形成した。
　これにより、硬化樹脂層の上面に、非晶性の透明導電層を形成し、非晶性透明導電性フィルムを得た。
　次いで、この非晶性透明導電性フィルムを、大気下で、２５℃４８０時間放置し、透明導電層を結晶化させた。
　これにより、透明導電性フィルムを得た。
　実施例２
　非晶性透明導電性フィルムを、大気下で、４０℃２４時間で加熱し、透明導電層を結晶化させた以外は、実施例１と同様にして、透明導電性フィルムを得た。
　比較例１
　非晶性透明導電性フィルムを、大気下で、６０℃１２時間で加熱し、透明導電層を結晶化させた以外は、実施例１と同様にして、透明導電性フィルムを得た。
　比較例２
　非晶性透明導電性フィルムを、大気下で、９５℃１時間で加熱し、透明導電層を結晶化させた以外は、実施例１と同様にして、透明導電性フィルムを得た。
２．評価
（膜密度）
　各実施例および各比較例の透明導電性フィルムについて、Ｘ線反射率法によって、膜密度を測定した。
　なお、Ｘ線反射率の測定条件を以下に示す。
測定条件：
　装置：Ｒｉｇａｋｕ社製、「ＳｍａｒｔＬａｂ」
　測定時間：２５分
　入射スリット：０．０５０ｍｍ
　受光スリット１：０．０５０ｍｍ
　受光スリット２：０．１００ｍｍ
　測定範囲：０～２．５°
　ステップ：０．００８°
　スピード：０．１００°／ｍｉｎ
（ヘイズ（視認性））
　各実施例および各比較例の透明導電性フィルムについて、ヘイズ（ヘイズ（初期）と称する。）を測定した。
　次いで、各実施例および各比較例の透明導電性フィルムを、加湿条件下（６５℃、相対湿度９０％）に静置した後、再度、ヘイズ（ヘイズ（加湿）と称する。）を測定した。
　その結果を表１に示す。
　また、ヘイズの変化率（（ヘイズ（加湿）－ヘイズ（初期）／ヘイズ（加湿））×１００）によって、視認性を評価した。
〇：視認性あり（ヘイズの変化率が、２５％未満）
×：視認性なし（ヘイズの変化率が、２５％以上）
　なお、ヘイズ測定の測定条件を以下に示す。
　装置：直読ヘーズメーターＨＧＭ－２ＤＰ（Ｃ光源用）（スガ試験機社製）
光源：ハロゲンランプ１２Ｖ、５０Ｗ
受光特性：３９５～７４５ｎｍ
Figure JPOXMLDOC01-appb-T000001
　なお、上記発明は、本発明の例示の実施形態として提供したが、これは単なる例示にすぎず、限定的に解釈してはならない。当該技術分野の当業者によって明らかな本発明の変形例は、後記請求の範囲に含まれるものである。
　本発明の透明導電性フィルムおよび透明導電性フィルムの製造方法は、光学用途おいて好適に用いられる。

Claims (4)

  1. 　透明基材と、硬化樹脂層と、透明導電層とを順に備え、
    　前記透明導電層の膜密度が、６．８５ｇ／ｃｍ３未満であることを特徴とする、透明導電性フィルム。
  2. 　前記透明基材の厚みが、５０μｍ未満であることを特徴とする、請求項１に記載の透明導電性フィルム。
  3. 　前記透明導電層が、結晶質であることを特徴とする、請求項１に記載の透明導電性フィルム。
  4. 　透明基材を準備する第１工程と、
    　前記透明基材の上面に、硬化樹脂層を積層する第２工程と、
    　前記硬化樹脂層の上面に、透明導電層を積層する第３工程とを備え、
    　前記第３工程では、前記透明導電層を２０℃以上３０℃以下で静置、または、前記透明導電層を６０℃未満で加熱することにより、前記透明導電層を結晶化させ、
    　前記透明導電層の膜密度が、６．８５ｇ／ｃｍ３未満であることを特徴とする、透明導電性フィルムの製造方法。
PCT/JP2020/035264 2019-09-25 2020-09-17 透明導電性フィルムおよびその製造方法 WO2021060139A1 (ja)