WO2021027368A1 - Revêtement de polyurée agissant contre la corrosion du génie océanique et son procédé de préparation - Google Patents

Revêtement de polyurée agissant contre la corrosion du génie océanique et son procédé de préparation Download PDF

Info

Publication number
WO2021027368A1
WO2021027368A1 PCT/CN2020/093647 CN2020093647W WO2021027368A1 WO 2021027368 A1 WO2021027368 A1 WO 2021027368A1 CN 2020093647 W CN2020093647 W CN 2020093647W WO 2021027368 A1 WO2021027368 A1 WO 2021027368A1
Authority
WO
WIPO (PCT)
Prior art keywords
parts
titanium dioxide
component
polyurea coating
nano
Prior art date
Application number
PCT/CN2020/093647
Other languages
English (en)
Chinese (zh)
Inventor
王道前
肖国亮
连联益
Original Assignee
顺缔高新材料江苏有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 顺缔高新材料江苏有限公司 filed Critical 顺缔高新材料江苏有限公司
Publication of WO2021027368A1 publication Critical patent/WO2021027368A1/fr

Abstract

L'invention concerne un revêtement de polyurée agissant contre la corrosion du génie océanique. Le revêtement de polyurée comprend un constituant A et un constituant B, le constituant A comprenant un polyisocyanate et un polycarbonate polyol, et le constituant B comprenant un polyéther à terminaison amine, un allongeur de chaîne amino, un dioxyde de titane nanométrique modifié, un oxyde de zinc nanométrique, un composé acide hydroxyaminocarboxylique, un agent antisalissures, un pigment antirouille et un agent anti-sédimentation. Les matières premières permettant de préparer le dioxyde de titane nanométrique modifié comprennent du dioxyde de titane nanométrique, un tensioactif, un agent de couplage silane, du nitrate d'argent et du sulfate de cuivre. Le revêtement de polyurée présente une forte résistance à l'eau de mer et au brouillard salin, peut résister à une adhérence microbienne et est approprié pour agir contre la corrosion du génie marin.
PCT/CN2020/093647 2019-08-12 2020-05-31 Revêtement de polyurée agissant contre la corrosion du génie océanique et son procédé de préparation WO2021027368A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201910740164.0 2019-08-12
CN201910740164.0A CN110564279B (zh) 2019-08-12 2019-08-12 一种海洋工程防腐聚脲涂料及其制备方法

Publications (1)

Publication Number Publication Date
WO2021027368A1 true WO2021027368A1 (fr) 2021-02-18

Family

ID=68775146

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2020/093647 WO2021027368A1 (fr) 2019-08-12 2020-05-31 Revêtement de polyurée agissant contre la corrosion du génie océanique et son procédé de préparation

Country Status (2)

Country Link
CN (1) CN110564279B (fr)
WO (1) WO2021027368A1 (fr)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110564279B (zh) * 2019-08-12 2021-03-12 顺缔高新材料江苏有限公司 一种海洋工程防腐聚脲涂料及其制备方法
CN112011076B (zh) * 2020-08-10 2022-09-30 江门市玛斯特包装有限公司 一种表面粗糙的包装袋及其制备方法
CN112322162A (zh) * 2020-11-11 2021-02-05 惠州市惠阳区嘉泰涂料有限公司 一种聚脲涂料及其制备方法
CN112760020A (zh) * 2021-03-01 2021-05-07 青岛爱尔家佳新材料股份有限公司 一种抗菌防腐聚脲涂料及其制备方法
CN113355010B (zh) * 2021-06-02 2022-05-31 山东丰普环保科技有限公司 一种用于水泵的超滑节能涂层材料及其制备方法
CN114369221B (zh) * 2022-01-18 2023-11-24 山东崇舜新材料科技有限公司 一种两液型聚脲及其制备方法
CN117625027B (zh) * 2023-12-18 2024-07-19 浙江上青元电力科技有限公司 一种高强度海洋运输用化工桶防腐缓蚀剂及其制备方法
CN117586690B (zh) * 2024-01-19 2024-03-19 潍坊市兴源防水材料股份有限公司 一种双组份喷涂聚脲防水涂料

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1831068A (zh) * 2006-02-21 2006-09-13 上海瑞鹏化工材料科技有限公司 一种用于发泡体保护的聚脲涂料及其制造工艺
US20100256296A1 (en) * 2004-05-24 2010-10-07 Hontek Corporation Abrasion resistant coatings
CN102311700A (zh) * 2010-06-29 2012-01-11 拜耳材料科技(中国)有限公司 脂肪族聚脲涂料、制备方法及其应用
CN102492357A (zh) * 2011-12-22 2012-06-13 湖南湘江涂料集团有限公司 一种抗粘耐磨聚脲涂料及其制备方法
CN102531460A (zh) * 2011-05-26 2012-07-04 百安力钢结构应用科技有限公司 一种具有长效杀菌功能的涂料及其制备方法
CN105368274A (zh) * 2015-11-25 2016-03-02 安徽圣德建材科技有限公司 一种耐磨防水抗菌性粉末涂料
CN107513118A (zh) * 2017-08-17 2017-12-26 蚌埠学院 一种二氧化钛/聚丙烯酰胺纳米复合材料的制备方法
CN107523205A (zh) * 2017-08-24 2017-12-29 成都托展新材料股份有限公司 一种快速固化的水下抗冲击涂料
CN110564279A (zh) * 2019-08-12 2019-12-13 顺缔高新材料江苏有限公司 一种海洋工程防腐聚脲涂料及其制备方法

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100256296A1 (en) * 2004-05-24 2010-10-07 Hontek Corporation Abrasion resistant coatings
CN1831068A (zh) * 2006-02-21 2006-09-13 上海瑞鹏化工材料科技有限公司 一种用于发泡体保护的聚脲涂料及其制造工艺
CN102311700A (zh) * 2010-06-29 2012-01-11 拜耳材料科技(中国)有限公司 脂肪族聚脲涂料、制备方法及其应用
CN102531460A (zh) * 2011-05-26 2012-07-04 百安力钢结构应用科技有限公司 一种具有长效杀菌功能的涂料及其制备方法
CN102492357A (zh) * 2011-12-22 2012-06-13 湖南湘江涂料集团有限公司 一种抗粘耐磨聚脲涂料及其制备方法
CN105368274A (zh) * 2015-11-25 2016-03-02 安徽圣德建材科技有限公司 一种耐磨防水抗菌性粉末涂料
CN107513118A (zh) * 2017-08-17 2017-12-26 蚌埠学院 一种二氧化钛/聚丙烯酰胺纳米复合材料的制备方法
CN107523205A (zh) * 2017-08-24 2017-12-29 成都托展新材料股份有限公司 一种快速固化的水下抗冲击涂料
CN110564279A (zh) * 2019-08-12 2019-12-13 顺缔高新材料江苏有限公司 一种海洋工程防腐聚脲涂料及其制备方法

Also Published As

Publication number Publication date
CN110564279B (zh) 2021-03-12
CN110564279A (zh) 2019-12-13

Similar Documents

Publication Publication Date Title
WO2021027368A1 (fr) Revêtement de polyurée agissant contre la corrosion du génie océanique et son procédé de préparation
CN109554064B (zh) 一种用于钢结构表面的耐候耐蚀防腐涂层及其制备方法
CN102676029A (zh) 深海环境钢结构喷涂聚氨酯防腐底漆
WO2021027369A1 (fr) Revêtement de polyurée résistant à l'usure, son procédé de préparation et son utilisation
CN108570273B (zh) 一种无溶剂氧化石墨烯-玻璃鳞片防腐涂料及其制备方法
CN110305580B (zh) 一种石墨烯基疏水型防腐蚀涂料及其制备方法和应用
CN100345922C (zh) 高耐盐水性红丹醇酸防锈漆及其制造方法
CN109181480B (zh) 一种包含改性二氧化钛的环氧富锌涂料及制备方法和用途
CN111647337A (zh) 一种锌烯防腐底漆及其应用
CN115286767B (zh) 一种抗菌氟改性环氧乙烯基酯树脂及其制备方法和多机制协同通用防腐涂料
CN113025185A (zh) 一种石墨烯超疏水防腐涂料及其制备方法
CN116535931A (zh) 水性环氧树脂防腐涂料及其制备方法和应用
KR101322301B1 (ko) 고내수성 및 고접착력이 필요한 철구조물 도장용 무용제 에폭시 도료 조성물 및 그 제조방법
CN108559358B (zh) 一种无溶剂石墨烯-玻璃鳞片防腐涂料及其制备方法
CN114713479A (zh) 一种通过激光固化提高液料喷涂EP+PDMS/SiO2超疏水涂层耐久性能的方法
CN114479620A (zh) 一种可水下涂装的防污防腐涂料及其制备方法
CN102898928B (zh) 湿固化环氧磷酸锌带锈底漆
CN109988493A (zh) 一种耐候性修补涂料组合物及其制备方法和用途
CN115820091B (zh) 一种制备GO-PDA-CeO2/PU耐磨超疏水长效防腐蚀涂层的方法
CN109909131B (zh) 一种石墨烯基钢材防腐涂层的制备方法
CN115160915B (zh) 一种高固体可全船使用的防腐底漆
CN106085223B (zh) 氟改性环氧聚硅氧烷涂料及其制备方法和应用
CN108546503A (zh) 耐磨防腐涂料及其制备方法
CN112760020A (zh) 一种抗菌防腐聚脲涂料及其制备方法
CN106380998A (zh) 一种聚苯胺‑短切玻纤‑酚醛树脂涂料及其制备方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20853194

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20853194

Country of ref document: EP

Kind code of ref document: A1