WO2021006265A1 - マレイミド系共重合体、その製造方法、樹脂組成物及び射出成形体 - Google Patents
マレイミド系共重合体、その製造方法、樹脂組成物及び射出成形体 Download PDFInfo
- Publication number
- WO2021006265A1 WO2021006265A1 PCT/JP2020/026539 JP2020026539W WO2021006265A1 WO 2021006265 A1 WO2021006265 A1 WO 2021006265A1 JP 2020026539 W JP2020026539 W JP 2020026539W WO 2021006265 A1 WO2021006265 A1 WO 2021006265A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mass
- maleimide
- parts
- based copolymer
- monomer unit
- Prior art date
Abstract
Description
(1)芳香族ビニル単量体単位、シアン化ビニル単量体単位、及びマレイミド単量体単位から構成されるマレイミド系共重合体であり、ガラス転移温度が165℃~200℃で、JIS K 7210に記載された方法で測定された、265℃、98N荷重の条件下でのメルトマスフローレートが25~80g/10分であるマレイミド系共重合体。
(2)芳香族ビニル単量体単位40~59.5質量%、シアン化ビニル単量体単位5~20質量%、マレイミド単量体単位35~50質量%を有する(1)に記載のマレイミド系共重合体
(3)マレイミド系共重合体中に、さらに、ジカルボン酸無水物単量体単位0.5~10質量%を有する(1)又は(2)に記載のマレイミド系共重合体。
(4)残存マレイミド単量体の含有量が300ppm未満である(1)~(3)のいずれかに記載のマレイミド系共重合体。
(5)シアン化ビニル単量体の仕込み量の全量、芳香族ビニル単量体の仕込み量の10~90質量%、不飽和ジカルボン酸無水物単量体の仕込み量の0~30質量%を混合して共重合を開始させる初期重合工程と、芳香族ビニル単量体の残りの50~90質量%、不飽和ジカルボン酸無水物単量体の残り全量を、それぞれ分割又は連続的に添加させながら共重合を続ける中期重合工程と、芳香族ビニル単量体の残り全量を添加して芳香族ビニル単量体単位、シアン化ビニル単量体単位及びジカルボン酸無水物単量体単位を有する共重合体を得る終期重合工程と、得られた共重合体のジカルボン酸無水物単量体単位をアンモニア又は第1級アミンを用いてマレイミド単量体単位にイミド化するイミド化工程を有する、(1)~(4)のいずれかに記載のマレイミド系共重合体の製造方法。
(6)(1)~(4)のいずれかに記載のマレイミド系共重合体5~40質量%と、ABS樹脂、ASA樹脂、AES樹脂又はSAN樹脂、から選ばれた1種又は2種以上の樹脂60~95質量%を有する樹脂組成物。
(7)(6)に記載の樹脂組成物を用いた射出成形体。
(8)自動車の内装部材又は外装部材として使用される(7)に記載の射出成形体。
本願明細書において、例えば、「A~B」なる記載は、A以上でありB以下であることを意味する。
残存マレイミド単量体量は、以下記載の条件で測定した値である。
装置名:ガスクロマトグラフ GC-2010(株式会社島津製作所製)
カラム:キャピラリーカラム DB-5ms(アジレント・テクノロジー株式会社製)
温度 :注入口280℃、検出器280℃
カラム温度80℃(初期)で昇温分析を行う。
(昇温分析条件) 80℃:ホールド12分
80~280℃:20℃/分で昇温10分
280℃:ホールド10分
検出器:FID
手順:試料0.5gをウンデカン(内部標準物質)入り1,2-ジクロロエタン溶液(0.014g/L)5mlに溶解させる。その後、n-ヘキサン5mlを加えて振とう器で10~15分間振とうし、析出させる。ポリマーを析出・沈殿させた状態で上澄み液のみをガスクロマトグラフに注入する。得られたマレイミド単量体のピーク面積から、内部標準物質より求めた係数を用いて、定量値を算出する。
装置名:示差走査熱量計 Robot DSC6200(セイコーインスツル株式会社製)
昇温速度:10℃/分
マレイミド系共重合体の重量平均分子量は、5万~30万であり、好ましくは5万~20万である。具体的には例えば、5、6、7、8、9、10、11、12、13、14、15、16、17、18、19、20、25、30万であり、ここで例示した数値の何れか2つの間の範囲内であってもよい。重量平均分子量が5万以下であれば耐衝撃性が低下し、30万を超えると流動性が低下する。
初期重合工程:シアン化ビニル単量体の仕込み量の全量、芳香族ビニル単量体の仕込み量の10~90質量%、不飽和ジカルボン酸無水物単量体の仕込み量の0~30質量%を混合して重合初期に仕込み共重合を開始させる
中期重合工程:芳香族ビニル単量体の仕込み量の残りと、不飽和ジカルボン酸無水物単量体の仕込み量の残りを、それぞれ分割又は連続的に添加させながら共重合を続ける
終期重合工程:芳香族ビニル単量体の分割又は連続的に添加する量の1/10以上を不飽和ジカルボン酸無水物単量体の全量を仕込み終えた後に添加して重合させる
イミド化工程:得られた芳香族ビニル単量体単位、シアン化ビニル単量体単位及びジカルボン酸無水物単量体単位を有する共重合体をアンモニア又は第1級アミンでイミド化してマレイミド系共重合体を得る
マレイミド系共重合体と各種樹脂を混練混合する方法については、特に限定されるものではないが、公知の溶融混練技術を用いることができる。好適に使用できる溶融混練装置としては、単軸押出機、完全噛合形同方向回転二軸押出機、完全噛合形異方向回転二軸押出機、非又は不完全噛合形二軸押出機などのスクリュー押出機、バンバリーミキサー、コニーダー及び混合ロールなどがある。
マレイミド系共重合体とこれらの樹脂とを混練混合する際に、さらに安定剤、紫外線吸収剤、難燃剤、可塑剤、滑剤、ガラス繊維、無機充填剤、着色剤、帯電防止剤等を添加しても差し支えない。
射出成形体としては、例えば、テレビ、複写機、電話機、時計、冷蔵庫、掃除機、エアコン、洗濯機、PC、DVD/ブルーレイプレイヤー、オーディオ、ドライヤー、キーボード、タブレット、デジタルカメラ、アタッシュケース、パチンコ台、家庭用ゲーム機、その他電化製品等の筐体/外装材、メーターケース、インストルメントパネル、レジスター、コントロールスイッチ、コンソールボックス、バンパーモール、ルーフレール、エンブレム、ダッシュボードトリム、電子エンクロージャー、ホイールキャップ、ホイールカバー、フェンダーフレアー、ドアハンドル、ドアパネル、ドアミラー、リアランプハウジング、ヘッドランプハウジング、ランプカバー、ルーフスポイラー、リアスポイラー、アンテナカバー、フロントグリル、ラジエーターグリル、センターコンソール、カーオーディオ、カーナビ、その他の自動車内外装材、カーポート部材、サッシ、ドアキャップ、ドア取手、フェンス部材、システムラック、スノコ、便座、窓枠、化粧パネル、洗面化粧台、ラチスフェンス、テラスデッキ、ベンチ等の住宅部材、食品用トレイ、おもちゃ、スポーツ用品、家具、楽器、半導体搬送用容器、プラズマ集塵ユニット、等の日用品部材、の部材が挙げられる。中でも、高耐熱性が要求される自動車内外装材に適しており、流動性に優れることから、ランプハウジングやスポイラーなど大型射出成形体に適している。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン6質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン20.3質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-1を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物25質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン2質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン17.7質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-2を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物35質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン2質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン21.3質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-3を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物24質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン13質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン17.4質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-4を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.8質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン6質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン19.8質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-5を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.11質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン6質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン20.7質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-6を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン6質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン17.2質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-7を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル15質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン1質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン19.8質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-8を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.01質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン6質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン20.3質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体B-1を得た。得られたマレイミド系共重合体B-1の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.01質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物27質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン10質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン18.9質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体B-2を得た。得られたマレイミド系共重合体B-2の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物20質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン17質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン13.3質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体B-3を得た。得られたマレイミド系共重合体B-3の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン6質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン16.6質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体B-4を得た。得られたマレイミド系共重合体B-4の分析結果を表1に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.9質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン6質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン19.8質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体B-5を得た。得られたマレイミド系共重合体B-5の分析結果を表2に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート0.1質量部、α-メチルスチレンダイマーを0.9質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。昇温後92℃を保持しながら、マレイン酸無水物27質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン10質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン18.4質量部、トリエチルアミン0.3質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体B-6を得た。得られたマレイミド系共重合体B-6の分析結果を表2に示す。
攪拌機を備えた容積約120リットルのオートクレーブ中にスチレン20質量部、アクリロニトリル10質量部、マレイン酸無水物5質量部、t-ブチルパーオキシ-2-エチルヘキサノエート 0.1質量部、α-メチルスチレンダイマー を0.6質量部、メチルエチルケトン12質量部を仕込み、気相部を窒素ガスで置換した後、撹拌しながら40分かけて92℃まで昇温した。 昇温後92℃を保持しながら、マレイン酸無水物31質量部とt-ブチルパーオキシ-2-エチルヘキサノエート0.22質量部をメチルエチルケトン75質量部に溶解した溶液及びスチレン28質量部を7時間かけて連続的に添加した。更にマレイン酸無水物添加終了後、スチレン6質量部を2時間かけて連続的に添加した。スチレン添加後、120℃に昇温し、1時間反応させて重合を終了させた。その後、重合液にアニリン12.6質量部、トリエチルアミン0.2質量部を加え140℃で7時間反応させた。反応終了後のイミド化反応液をベントタイプスクリュー式押出機に投入し、揮発分を除去してペレット状のマレイミド系共重合体A-1を得た。得られたマレイミド系共重合体の分析結果を表1に示す。
重量平均分子量は、ゲルパーミエーションクロマトグラフィー(GPC)にて測定されるポリスチレン換算の値であり、次の条件で測定した。
装置名:SYSTEM-21Shodex(昭和電工株式会社製)
カラム:PLgelMIXED-Bを3本直列
温度:40℃
検出:示差屈折率
溶媒:テトラヒドロフラン
濃度:2質量%
検量線:標準ポリスチレン(PS)(PL製)を用いて作成した。
メルトマスフローレートは、JIS K 7210に準拠して、265℃、98N荷重にて測定した。
ガラス転移温度は、JIS K-7121に準拠して、以下の装置及び測定条件によりマレイミド系共重合体の中間点ガラス転移温度(Tmg)を測定した。
装置名:Robot DSC6200(セイコーインスツル株式会社製)
昇温速度:10℃/分
試料0.5gをウンデカン(内部標準物質)入り1,2-ジクロロエタン溶液(0.014g/L)5mlに溶解させる。その後、n-ヘキサン5mlを加えて振とう器で10~15分間振とうし、析出させる。ポリマーを析出・沈殿させた状態で上澄み液のみをガスクロマトグラフに注入する。得られたマレイミド単量体のピーク面積から、内部標準物質より求めた係数を用いて、定量値を算出した。
装置名:ガスクロマトグラフ GC-2010(株式会社島津製作所製)
カラム:キャピラリーカラム DB-5ms(アジレント・テクノロジー株式会社製)
温度 :注入口280℃、検出器280℃
カラム温度80℃(初期)で昇温分析を行う。
(昇温分析条件) 80℃:ホールド12分
80~280℃:20℃/分で昇温10分
280℃:ホールド10分
検出器:FID
実施例1~8、比較例1~6(マレイミド系共重合体とABS樹脂との混練混合)
マレイミド系共重合体A-1~A-8、及びB-1~B-6、一般に市販されているシアン化ビニル単量体単位を有しないマレイミド系共重合体である「MS-NIP」(デンカ株式会社製)と、ABS樹脂「GR-3000」(デンカ株式会社製)もしくはASA樹脂「Luran S 757G」(INEOS Styrolution株式会社製)とを表3及び表4に示した配合割合でブレンドした後、二軸押出機(東芝機械株式会社製 TEM-35B)を用いて押出しペレット化した。このペレットを使用し、射出成形機により試験片を作成して、各物性値の測定を行った。結果を表3及び表4に示す。
JIS K-7111に準拠して、ノッチあり試験片を用い、打撃方向はエッジワイズを採用して相対湿度50%、雰囲気温度23℃で測定した。なお、測定機は株式会社東洋精機製作所製デジタル衝撃試験機を使用した。
JIS K7206に準拠して、50法(荷重50N、昇温速度50℃/時間)で試験片は10mm×10mm、厚さ4mmのものを用いて測定した。なお、測定機は株式会社東洋精機製作所製HDT&VSPT試験装置を使用した。
JIS K 7210に準拠して、220℃、98N荷重にて測定した。
試験片形状316×20×2mm、長半径250mm、短半径150mmの1/4楕円法により、23℃、48時間後のクラックを観察した。試験片は成形ひずみの影響を排除するため、260℃にてペレットをプレス成形して、切り出して製造した。薬品はトルエンを用いて行った。
なお、臨界ひずみは下記式にて求めた。
ε=b/2a2{1-(a2-b2)X2/a4}1.5×t×100
臨界ひずみ:ε、長半径:a、短半径:b、試験厚み:t、クラック発生点:X
臨界ひずみから下記基準にて耐薬品性を評価した。
◎:0.8以上、○:0.6~0.7、△:0.3~0.5、×:0.2以下
Claims (8)
- 芳香族ビニル単量体単位、シアン化ビニル単量体単位、及びマレイミド単量体単位から構成されるマレイミド系共重合体であり、ガラス転移温度が165℃~200℃で、JIS K 7210に記載された方法で測定された、265℃、98N荷重の条件下でのメルトマスフローレートが25~80g/10分であるマレイミド系共重合体。
- 芳香族ビニル単量体単位40~59.5質量%、シアン化ビニル単量体単位5~20質量%、マレイミド単量体単位35~50質量%を有する請求項1に記載のマレイミド系共重合体。
- マレイミド系共重合体中に、さらに、ジカルボン酸無水物単量体単位0.5~10質量%を有する請求項1又は請求項2に記載のマレイミド系共重合体。
- 残存マレイミド単量体の含有量が300ppm未満である請求項1~請求項3いずれか一項に記載のマレイミド系共重合体。
- シアン化ビニル単量体の仕込み量の全量、芳香族ビニル単量体の仕込み量の10~90質量%、不飽和ジカルボン酸無水物単量体の仕込み量の0~30質量%を混合して共重合を開始させる初期重合工程と、芳香族ビニル単量体の残りの50~90質量%、不飽和ジカルボン酸無水物単量体の残り全量を、それぞれ分割又は連続的に添加させながら共重合を続ける中期重合工程と、芳香族ビニル単量体の残り全量を添加して芳香族ビニル単量体単位、シアン化ビニル単量体単位及びジカルボン酸無水物単量体単位を有する共重合体を得る終期重合工程と、得られた共重合体のジカルボン酸無水物単量体単位をアンモニア又は第1級アミンを用いてマレイミド単量体単位にイミド化するイミド化工程を有する、請求項1~請求項4いずれか一項に記載のマレイミド系共重合体の製造方法。
- 請求項1~請求項4いずれか一項に記載のマレイミド系共重合体5~40質量%と、アクリロニトリル-ブタジエン-スチレン共重合樹脂、アクリロニトリル-スチレン-アクリル系ゴム共重合樹脂、アクリロニトリル-エチレン・プロピレン系ゴム-スチレン共重合樹脂又はスチレン-アクリロニトリル共重合樹脂、から選ばれた1種又は2種以上の樹脂60~95質量%を有する樹脂組成物。
- 請求項6に記載の樹脂組成物を用いた射出成形体。
- 自動車の内装部材又は外装部材として使用される請求項7に記載の射出成形体。