WO2020221286A1 - MEMBRANE DE NANOFIBRES COMPOSITES DE β-FEOOH/POLYACRYLONITRILE, PROCÉDÉ DE PRÉPARATION S'Y RAPPORTANT ET SON UTILISATION - Google Patents

MEMBRANE DE NANOFIBRES COMPOSITES DE β-FEOOH/POLYACRYLONITRILE, PROCÉDÉ DE PRÉPARATION S'Y RAPPORTANT ET SON UTILISATION Download PDF

Info

Publication number
WO2020221286A1
WO2020221286A1 PCT/CN2020/087725 CN2020087725W WO2020221286A1 WO 2020221286 A1 WO2020221286 A1 WO 2020221286A1 CN 2020087725 W CN2020087725 W CN 2020087725W WO 2020221286 A1 WO2020221286 A1 WO 2020221286A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyacrylonitrile
nanofiber membrane
feooh
solution
composite nanofiber
Prior art date
Application number
PCT/CN2020/087725
Other languages
English (en)
Chinese (zh)
Inventor
何毅
张李云
范毅
马兰
石恒
李双双
钟菲
李振宇
Original Assignee
西南石油大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 西南石油大学 filed Critical 西南石油大学
Publication of WO2020221286A1 publication Critical patent/WO2020221286A1/fr

Abstract

L'invention concerne une membrane de nanofibres composites de β-FeOOH/polyacrylonitrile, un procédé de préparation s'y rapportant et son utilisation, appartenant au domaine technique des matériaux. Le procédé pour la préparation de la membrane de nanofibres composites de β-FeOOH/polyacrylonitrile comprend les étapes suivantes : la préparation d'une membrane de nanofibres de polyacrylonitrile consistant à préparer une membrane de nanofibres de polyacrylonitrile au moyen d'un filage électrostatique; un traitement de stabilisation consistant à soumettre la membrane de nanofibres de polyacrylonitrile à un traitement thermique à gradient; et un traitement de biominéralisation consistant à formuler une solution mélangée à partir d'une solution de chlorure ferrique et d'acide chlorhydrique en un rapport volumique de 2:1, placer la membrane de nanofibres de polyacrylonitrile stabilisée dans la solution mélangée et agiter celle-ci pendant 1 à 3 min, puis faire réagir celle-ci dans des conditions de 55 à 65 °C pendant 10 à 14 h, puis nettoyer et sécher celle-ci pour obtenir la membrane de nanofibres composites de β-FeOOH/polyacrylonitrile. La membrane de fibres a de meilleures stabilité et propriétés mécaniques et a également des propriétés superhydrophiles-superhydrophobes sous l'eau, l'efficacité d'adsorption de celle-ci étant élevée et la membrane étant recyclable.
PCT/CN2020/087725 2019-04-30 2020-04-29 MEMBRANE DE NANOFIBRES COMPOSITES DE β-FEOOH/POLYACRYLONITRILE, PROCÉDÉ DE PRÉPARATION S'Y RAPPORTANT ET SON UTILISATION WO2020221286A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201910362641.4A CN110205748B (zh) 2019-04-30 2019-04-30 一种β-FeOOH/聚丙烯腈的复合纳米纤维膜及其制备方法与应用
CN201910362641.4 2019-04-30

Publications (1)

Publication Number Publication Date
WO2020221286A1 true WO2020221286A1 (fr) 2020-11-05

Family

ID=67786771

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2020/087725 WO2020221286A1 (fr) 2019-04-30 2020-04-29 MEMBRANE DE NANOFIBRES COMPOSITES DE β-FEOOH/POLYACRYLONITRILE, PROCÉDÉ DE PRÉPARATION S'Y RAPPORTANT ET SON UTILISATION

Country Status (2)

Country Link
CN (1) CN110205748B (fr)
WO (1) WO2020221286A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113699693A (zh) * 2021-08-03 2021-11-26 佛山市南海区苏科大环境研究院 一种超疏水、抗粘附的纳米纤维膜及其制备方法和应用
CN113731375A (zh) * 2021-08-23 2021-12-03 辽宁大学 一种3d微纳松针状超疏水材料的制备及其应用
CN113802266A (zh) * 2021-09-26 2021-12-17 北京石油化工学院 一种聚丙烯腈复合纳米纤维膜、制备方法及其用途
CN113996118A (zh) * 2021-11-29 2022-02-01 闽江学院 一种具有梯度结构的复合过滤材料及其制备方法
CN114507941A (zh) * 2022-02-15 2022-05-17 肇庆学院 一种用于可见光催化杀菌的纤维膜及其制备方法
CN115416382A (zh) * 2022-09-02 2022-12-02 南通大学 一种层合结构中空微纳米纤维非织造材料及其制备方法与应用
CN115821400A (zh) * 2022-11-22 2023-03-21 天津工业大学 一种四元仿生雾水收集材料及其制备技术

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110205748B (zh) * 2019-04-30 2022-04-01 西南石油大学 一种β-FeOOH/聚丙烯腈的复合纳米纤维膜及其制备方法与应用
CN110872741B (zh) * 2019-09-12 2023-01-13 武汉工程大学 一种同时用于乳液分离和染料吸附的复合纳米纤维膜及其制备方法
CN110616502B (zh) * 2019-10-23 2020-07-10 西南石油大学 一种ZnO/聚吡咯改性的聚丙烯腈纳米纤维膜及其制备方法
CN111871225B (zh) * 2020-07-31 2021-04-27 西华大学 一种可见光驱动自清洁氧化石墨烯油水分离膜及其制备方法和应用
CN111926458B (zh) * 2020-08-17 2021-04-09 西南石油大学 一种毛毛虫结构的纳米纤维膜及其制备方法与应用
CN112156662B (zh) * 2020-09-30 2021-09-07 东华大学 一种自清洁静电纺纳米纤维滤膜、制备方法及应用
CN113373595B (zh) * 2021-05-19 2023-02-03 济南大学 一种FeOOH/PVDF纤维支架及其制备方法和应用
CN113663533A (zh) * 2021-08-30 2021-11-19 中国石油大学(华东) 纳米纤维油水分离膜的制备方法及纳米纤维油水分离膜
CN114606653B (zh) * 2022-03-11 2022-10-11 北京师范大学珠海校区 一种高效稳定磁性纳米纤维膜、制备方法及其应用
CN114657703B (zh) * 2022-03-29 2023-06-20 中原工学院 一种TiO2/乙烯脲/聚丙烯腈除甲醛纳米纤维膜及其制备方法和应用
CN115140872A (zh) * 2022-09-07 2022-10-04 中山市中环环保废液回收有限公司 高盐高cod废水的低能耗处理方法
CN115569673A (zh) * 2022-10-19 2023-01-06 浙江理工大学 具备光催化降解有机染料功能的纳米纤维膜及其制备方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102747439A (zh) * 2011-04-21 2012-10-24 中国科学院合肥物质科学研究院 分散性纳米复合材料及其制备方法
KR101609802B1 (ko) * 2015-02-09 2016-04-06 광주과학기술원 아카가나이트 분말이 고정화된 수중 산소산 음이온 제거 및 회수용 입상 흡착제 및 그 제조방법
CN105734725A (zh) * 2016-03-02 2016-07-06 复旦大学 一种“囊泡串”结构纯碳纤维材料及其制备方法
CN106039998A (zh) * 2016-07-18 2016-10-26 浙江大学 负载β‑FeOOH纳米晶体的光催化复合纳滤膜及其制备方法
CN110205748A (zh) * 2019-04-30 2019-09-06 西南石油大学 一种β-FeOOH/聚丙烯腈的复合纳米纤维膜及其制备方法与应用

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5673408A (en) * 1979-11-21 1981-06-18 Kanto Denka Kogyo Kk Magnetic powder for magnetic recording and magnetic tape employing that magnetic powder
JP2003183960A (ja) * 2001-12-14 2003-07-03 Toho Tenax Co Ltd ポリアクリロニトリル系炭素繊維強化酸化繊維シート、及びその製造方法
US7132022B2 (en) * 2004-03-23 2006-11-07 L&P Property Management Company Bi-layer nonwoven fire resistant batt and an associated method for manufacturing the same
CN1319646C (zh) * 2004-04-02 2007-06-06 中国科学技术大学 用于一氧化碳氧化反应的催化剂三氧化二铁及其制备方法
CN101455975A (zh) * 2007-12-14 2009-06-17 北京化工大学 多孔碳纳米纤维负载纳米晶粒催化剂及其制备方法
CN102758262B (zh) * 2011-04-29 2014-08-13 中国科学院化学研究所 超疏油的水下自清洁的矿化纤维膜及其制备方法
CN106390766B (zh) * 2016-09-23 2019-03-05 天津工业大学 一种具有自清洁功能的仿鼻腔纤毛结构过滤材料
CN107984837B (zh) * 2017-12-05 2020-05-01 安徽鹰龙工业设计有限公司 一种增强型吸油棉
CN108611793B (zh) * 2018-05-18 2020-11-20 北京化工大学 一种高强度静电纺丝聚丙烯腈基纳米碳纤维毡的制备方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102747439A (zh) * 2011-04-21 2012-10-24 中国科学院合肥物质科学研究院 分散性纳米复合材料及其制备方法
KR101609802B1 (ko) * 2015-02-09 2016-04-06 광주과학기술원 아카가나이트 분말이 고정화된 수중 산소산 음이온 제거 및 회수용 입상 흡착제 및 그 제조방법
CN105734725A (zh) * 2016-03-02 2016-07-06 复旦大学 一种“囊泡串”结构纯碳纤维材料及其制备方法
CN106039998A (zh) * 2016-07-18 2016-10-26 浙江大学 负载β‑FeOOH纳米晶体的光催化复合纳滤膜及其制备方法
CN110205748A (zh) * 2019-04-30 2019-09-06 西南石油大学 一种β-FeOOH/聚丙烯腈的复合纳米纤维膜及其制备方法与应用

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
LEE, JONG HWA ET AL.: "Partially oxidized polyacrylonitrile nanofibrous membrane as a thermally stable separator for lithium ion batteries", POLYMER, vol. 68, 25 April 2015 (2015-04-25), pages 335 - 343, XP029177300, ISSN: 0032-3861 *

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113699693A (zh) * 2021-08-03 2021-11-26 佛山市南海区苏科大环境研究院 一种超疏水、抗粘附的纳米纤维膜及其制备方法和应用
CN113699693B (zh) * 2021-08-03 2023-03-31 佛山市南海区苏科大环境研究院 一种超疏水、抗粘附的纳米纤维膜及其制备方法和应用
CN113731375A (zh) * 2021-08-23 2021-12-03 辽宁大学 一种3d微纳松针状超疏水材料的制备及其应用
CN113802266A (zh) * 2021-09-26 2021-12-17 北京石油化工学院 一种聚丙烯腈复合纳米纤维膜、制备方法及其用途
CN113996118A (zh) * 2021-11-29 2022-02-01 闽江学院 一种具有梯度结构的复合过滤材料及其制备方法
CN114507941A (zh) * 2022-02-15 2022-05-17 肇庆学院 一种用于可见光催化杀菌的纤维膜及其制备方法
CN114507941B (zh) * 2022-02-15 2023-07-07 肇庆学院 一种用于可见光催化杀菌的纤维膜及其制备方法
CN115416382A (zh) * 2022-09-02 2022-12-02 南通大学 一种层合结构中空微纳米纤维非织造材料及其制备方法与应用
CN115416382B (zh) * 2022-09-02 2024-03-29 南通大学 一种层合结构中空微纳米纤维非织造材料及其制备方法与应用
CN115821400A (zh) * 2022-11-22 2023-03-21 天津工业大学 一种四元仿生雾水收集材料及其制备技术

Also Published As

Publication number Publication date
CN110205748A (zh) 2019-09-06
CN110205748B (zh) 2022-04-01

Similar Documents

Publication Publication Date Title
WO2020221286A1 (fr) MEMBRANE DE NANOFIBRES COMPOSITES DE β-FEOOH/POLYACRYLONITRILE, PROCÉDÉ DE PRÉPARATION S'Y RAPPORTANT ET SON UTILISATION
Tan et al. Controllable exfoliation of natural silk fibers into nanofibrils by protein denaturant deep eutectic solvent: nanofibrous strategy for multifunctional membranes
Zhao et al. Superhydrophobic and superoleophilic PH-CNT membrane for emulsified oil-water separation
EP2817448A1 (fr) Régénération de cellulose
CN112999895B (zh) 一种聚偏氟乙烯亲水拉伸膜的制备方法
CN105544093A (zh) 一种功能性aopan-rc复合纳米纤维膜的制备方法及其应用
CN101967279A (zh) 一种聚苯胺复合纳米纤维可逆变色膜的制备方法
CN109943920A (zh) 一种静电混纺聚丙烯腈/木质素制备碳纳米纤维的方法
CN109289542A (zh) 具有光Fenton催化性能的抗污染超滤膜制备方法
JP6025669B2 (ja) 耐炎性ポリマー、ポリマー溶液、耐炎繊維および炭素繊維の製造方法
CN112619622A (zh) 可高效清除水中离子型染料及重金属离子的纳米复合纤维膜及其制备方法与应用
CN103061046A (zh) 一种pa6多孔纳米纤维复合膜的制备方法
KR101420084B1 (ko) 전도성 장섬유의 제조방법 및 이를 통해 제조된 전도성 장섬유
Shen et al. Hydrophilic SPE/MPTES-PAN electrospun membrane prepared via click chemistry for high efficiency oil–water separation
Lv et al. Preparation of superhydrophilic poly (acrylonitrile/acrylic acid) electrospun membrane and its application in oil/water separation
JP4773902B2 (ja) ナノファイバー不織布及びその製造方法
CN108479432A (zh) 一种亲水性酚酞聚醚砜复合纳米纤维超滤膜的制备方法
CN111468072A (zh) 一种负载zif-8的无纺布复合材料在染料吸附处理中的应用
CN108057423B (zh) 一种具有吸附特性的磁性壳聚糖复合材料的制备方法
CN105714411A (zh) 一种聚吡咙/聚醚砜/碳纳米管三元复合材料的制备方法
CN114797484B (zh) 一种具有吸附性能的多孔分离膜及其制备方法和应用
CN108149339A (zh) 一种回收涤纶纳米纤维静电纺丝液
CN107151833B (zh) 一种聚酰亚胺微细旦纤维及其制备方法
KR101468380B1 (ko) 은도금 전도성 장섬유의 제조방법 및 이를 통해 제조된 은도금 전도성 장섬유
CN109295615B (zh) 一种耐久性石墨烯导电丝素蛋白纳米纤维膜的制备方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20798393

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20798393

Country of ref document: EP

Kind code of ref document: A1