WO2020213491A1 - 接合構造 - Google Patents

接合構造 Download PDF

Info

Publication number
WO2020213491A1
WO2020213491A1 PCT/JP2020/015775 JP2020015775W WO2020213491A1 WO 2020213491 A1 WO2020213491 A1 WO 2020213491A1 JP 2020015775 W JP2020015775 W JP 2020015775W WO 2020213491 A1 WO2020213491 A1 WO 2020213491A1
Authority
WO
WIPO (PCT)
Prior art keywords
penetrating portion
penetrating
flange
flange portion
welded
Prior art date
Application number
PCT/JP2020/015775
Other languages
English (en)
French (fr)
Inventor
潤司 藤原
中川　龍幸
Original Assignee
パナソニックＩｐマネジメント株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by パナソニックＩｐマネジメント株式会社 filed Critical パナソニックＩｐマネジメント株式会社
Priority to JP2021514904A priority Critical patent/JPWO2020213491A1/ja
Priority to EP20791590.1A priority patent/EP3957425A4/en
Priority to CN202080029247.XA priority patent/CN113692328B/zh
Publication of WO2020213491A1 publication Critical patent/WO2020213491A1/ja
Priority to US17/483,634 priority patent/US20220023966A1/en

Abstract

第２の部材（２０）は、第１の部材（１０）に対して溶接が困難な材料で構成されている。第１の部材（１０）には、厚み方向に貫通する第１貫通部（１１）が形成されている。第３の部材（３０）は、第２の部材（２０）の第２貫通部（２１）を介して第１貫通部（１１）の内周面および第１の部材（１０）の開口面（１０ａ）にアーク溶接される。第３の部材（３０）の凝固収縮によって第２の部材（２０）がフランジ部（３１）と第１の部材（１０）とで圧縮されることにより、第３の部材（３０）のフランジ部（３１）と第１の部材（１０）との間に第２の部材（２０）が固定される。

Description

接合構造
　本発明は、接合構造に関するものである。
　特許文献１には、第１の金属材と、第１の金属材に対して溶接が困難な異種材とを重ね合わせた状態にし、異種材の貫通部を介して溶加材（溶接ワイヤ）をアーク溶接するようにした接合構造が開示されている。
　このとき、溶融した溶加材によって、異種材の貫通部の上面側の外周部に覆い被さるようにつば部分を形成する。これにより、第１の金属材に対する溶加材の凝固収縮によるつば部分と第１の金属材との圧縮固定力によって、異種材と第１の金属材とを固定するようにしている。
国際公開第２０１８／０３０２７２号
　ところで、特許文献１の発明では、例えば、貫通部の孔径が小さい場合には、第１の金属材における溶加材の溶着面積も小さくなってしまい、接合強度が不足するおそれがある。
　本発明は、かかる点に鑑みてなされたものであり、その目的は、溶加材の溶着面積を増やして接合強度を確保できるようにすることにある。
　本発明は、金属材で構成された第１の部材と、該第１の部材に対して溶接が困難な材料で構成された第２の部材と、該第１の部材に溶接された溶加材で構成された第３の部材とが互いに接合された接合構造を対象とし、次のような解決手段を講じた。
　すなわち、第１の発明は、前記第１の部材は、厚み方向に貫通する第１貫通部を有する。前記第２の部材は、前記第１貫通部に対応する位置に開口する第２貫通部を有する。前記第３の部材は、前記第２貫通部の周縁部を押さえるフランジ部を有する。前記第３の部材は、該第２貫通部を介して前記第１の部材の前記第１貫通部の内周面および前記第２の部材の前記第２貫通部により開口される前記第１の部材の開口面にアーク溶接されている。前記第３の部材の凝固収縮によって前記第２の部材が前記フランジ部と前記第１の部材とで圧縮されることにより、前記フランジ部と該第１の部材との間に前記第２の部材が固定されている。
　第１の発明では、第２の部材は、第１の部材に対して溶接が困難な材料で構成されている。第１の部材には、厚み方向に貫通する第１貫通部が形成されている。第３の部材は、第２の部材の第２貫通部を介して第１貫通部の内周面および第２の部材の第２貫通部により開口される第１の部材の開口面にアーク溶接される。第３の部材の凝固収縮によって第２の部材がフランジ部と第１の部材とで圧縮されることにより、第３の部材のフランジ部と第１の部材との間に第２の部材が固定される。
　このように、第１の部材に第１貫通部を設け、第３の部材を第１貫通部の内周面および第２の部材の第２貫通部により開口される第１の部材の開口面にアーク溶接することで、第３の部材の溶着面積を増やすことができる。これにより、第１の部材、第２の部材、及び第３の部材の接合強度を確保することができる。
　第２の発明は、第１の発明において、前記フランジ部は、前記第２の部材における前記第１の部材とは反対側の面において、該第２貫通部よりも径方向外方に張り出している。
　第２の発明では、フランジ部によって、第２の部材における第１の部材とは反対側の面を押さえ付けることで、フランジ部と第１の部材との間に第２の部材を固定することができる。
　第３の発明は、第１の発明において、前記第２貫通部は、前記周縁部により画定されている。前記周縁部は、前記第１の部材に向かって先細りとなるテーパー部を有する。前記フランジ部は、前記テーパー部を押さえている。
　第３の発明では、周縁部にテーパー部を設けることで、溶融した溶加材が第１貫通部に向かって流れ易くなる。また、テーパー部に沿った形状にフランジ部を形成することで、第２の部材から飛び出すフランジ部の厚みを抑えることができる。
　第４の発明は、第１乃至第３の発明のうち何れか１つにおいて、前記第１貫通部は、テーパー形状を有する。前記第１貫通部は、前記厚み方向に前記第２の部材に近い端と前記第２の部材から遠い端とを有する。前記遠い端は、前記近い端よりも小さなサイズを有する。
　第４の発明では、第１貫通部を、先細りとなるテーパー状に形成することで、溶融した溶加材が第１貫通部内を近い端から遠い端に向かって流れ易くなる。
　第５の発明は、第１乃至第３の発明のうち何れか１つにおいて、前記第１貫通部は、テーパー形状を有する。前記第１貫通部は、前記厚み方向に前記第２の部材に近い端と前記第２の部材から遠い端とを有する。前記遠い端は、前記近い端よりも大きなサイズを有する。
　第５の発明では、第１貫通部を、幅広となるテーパー状に形成するようにしている。これにより、溶融した溶加材が第１貫通部の幅広部分で凝固すると、第３の部材が第１貫通部に食い込んだ状態となり、接合強度を高めることができる。
　第６の発明は、第１乃至第５の発明のうち何れか１つにおいて、前記第１貫通部は、前記第1貫通部よりも小さな複数の第１小貫通部を含む。
　第６の発明では、第１小貫通部を複数設けることで、溶融した溶加材を複数の第１小貫通部に分散させながら溶接することができる。また、複数の第１小貫通部に第３の部材が食い込んだ状態とすることで、複数の第１小貫通部においてくさび効果を得ることができ、接合安定性が向上する。
　第７の発明は、第１乃至第６の発明のうち何れか１つにおいて、前記第1の部材は、前記第1貫通部を画定する周縁部を有する。前記第３の部材は、前記第１の部材における前記第２の部材とは反対側の面において前記第１の部材の前記周縁部に係止する係止部を有する。
　第７の発明では、係止部によって、第３の部材が第１貫通部から抜けるのを抑えることができる。また、フランジ部と係止部との間に第１の部材及び第２の部材が固定されるので、接合強度を高めることができる。
　第８の発明は、第１乃至第７の発明のうち何れか１つにおいて、前記第２の部材における前記第１の部材とは反対側の面に重ね合わされた固定部材を備える。前記固定部材は、前記第２貫通部及び前記第１貫通部に対応する位置に開口する固定孔を有する。前記第３の部材は、前記固定孔及び前記第２貫通部を介して前記第１貫通部の内周面および前記第２の部材の前記第２貫通部により開口される前記第１の部材の開口面にアーク溶接される。前記フランジ部は、前記固定部材を介して前記第２の部材の前記周縁部を押さえている。前記第３の部材の凝固収縮によって前記固定部材および前記第２の部材が前記フランジ部と前記第１の部材とで圧縮されることにより、前記フランジ部と該第１の部材との間に、前記固定部材及び前記第２の部材が固定されている。
　第８の発明では、第２の部材に固定部材が重ね合わされている。第３の部材は、固定部材の固定孔及び第２の部材の第２貫通部を介して第１貫通部の内周面および前記第２の部材の前記第２貫通部により開口される前記第１の部材の開口面にアーク溶接される。第３の部材の凝固収縮によって、第３の部材のフランジ部と第１の部材との間に固定部材および第２の部材がフランジ部と第１の部材とで圧縮されることにより、固定部材及び第２の部材が固定される。
　これにより、第３の部材を第１の部材の第１貫通部の内周面および前記第２の部材の前記第２貫通部により開口される前記第１の部材の開口面にアーク溶接する際に、固定部材によって第２の部材への入熱量を抑えながら、フランジ部を形成することができる。そして、異種材である第２の部材を、第１の部材と固定部材との間に挟み込んで固定することができる。
　第９の発明は、第１乃至第８の発明のうち何れか１つにおいて、前記第２の部材は、前記第１の部材とは反対側の面に開口する段差部をさらに有し、前記第２貫通部は、該段差部の底面に形成されている。
　第９の発明では、第２の部材の段差部の底面に第２貫通部が形成されている。これにより、第３の部材のフランジ部を段差部内に配置して、第２の部材からフランジ部が飛び出すのを抑えることができる。
　第１０の発明は、第９の発明において、前記段差部の底面は、前記第２貫通部に向かって傾斜している。
　第１０の発明では、段差部の底面を第２貫通部に向かって傾斜させることで、溶融した溶加材が第２貫通部に向かって流れ易くなる。
　第１１の発明は、第１乃至第１０の発明のうち何れか１つにおいて、前記第３の部材は、前記第１の部材に溶接された第１接合部と、該第１接合部に溶接されて前記フランジ部を構成する第２接合部とを有する。
　第１１の発明では、第３の部材を、第１接合部と第２接合部とに分けて形成することで、第２の部材の材料特性を考慮した溶接法又は溶接条件の使い分けをすることができる。
　例えば、溶融した溶加材を、第２貫通部を介して第１の部材に溶接する際には、溶け込みに必要な入熱で、アークの広がりが小さい短絡溶接を行い、第１接合部を形成すればよい。その後、第２の部材を溶融しない程度の低入熱で、アークの広がりが大きい正極性や交流によるパルス溶接を行い、第２接合部を形成すればよい。これにより、第２の部材への入熱量を抑えながら、フランジ部を形成することができる。
　第１２の発明では、第１乃至第１１のうち何れか１つにおいて、第１貫通部は、第２貫通部よりも小さなサイズを有する。開口面は、第１の部材の上面のうち第２貫通部内にある領域である。
　このように、第１貫通部の径は、第２の部材の第２貫通部の径（第２の部材の第２貫通部により開口される第１の部材の開口面の径）よりも小さい。これにより、第１の部材および第２の部材に対する入熱を抑制しながら溶接を行うことが出来る。また、第１貫通部の内周面と開口面とで第３の部材の凸部形状が形成される。凸部形状は、接合される表面積を拡大する。凸部形状は、楔のようなアンカー効果を発揮して接合強度及び信頼性をより向上させる。
　第１３の発明は、第１の部材、第２の部材および第３の部材を含む接合構造に関する。第１の部材は、上面と、前記上面の反対の下面とを有する。第１の部材は、前記上面から前記下面まで延びた第１貫通部を有する。第１の部材は、金属材で構成されている。第２の部材は、第１の貫通部に対応する位置に開口しており第１の貫通部よりも大きな第２貫通部と、第２貫通部を画定する周縁部とを有する。第２の部材は、第１の部材に対して溶接が困難な材料で構成されている。第２の部材は、第１の部材の上面に配されている。第３の部材は、溶接部と、第２貫通部を介して溶接部につながるフランジ部とを有する。溶接部は、第１貫通部の内周面および第１の部材の上面における第１貫通部の周囲にアーク溶接されている。フランジ部は、周縁部を覆う。第３の部材は、第１の部材に溶接された溶加材で構成されている。第２の部材が、第３の部材の凝固収縮によってフランジ部と第１の部材とで圧縮されることにより、フランジ部と第１の部材との間に固定されている。
　このように、第１の部材に第１貫通部を設け、第３の部材を第１貫通部の内周面および第２の部材の第２貫通部により開口される第１の部材の開口面にアーク溶接することで、第３の部材の溶着面積を増やすことができる。これにより、第１の部材、第２の部材、及び第３の部材の接合強度を確保することができる。
　第１４の発明は、第１の部材の準備、第２の部材の準備および第３の部材の形成を含む接合方法に関する。第１の部材は、上面と上面の反対の下面とを有する。第１の部材は、上面から下面まで延びた第１貫通部を有する。第１の部材は、金属材で構成されている。第２の部材は、第２貫通部と第２貫通部を画定する周縁部とを有する。第２の部材は、第１の部材に対して溶接が困難な材料で構成されている。第２の部材は、第２貫通部が第１貫通部に対応して位置し、かつ、第２の部材の第２貫通部により開口される第１の部材の開口面が形成されるように、第１の部材の上面に配置される。第３の部材は、第２貫通部を介して第１の部材の第１貫通部の内周面および第１の部材の開口面にアーク溶接することにより形成される。第３の部材は、第１の部材に溶接された溶加材で構成されている。第３の部材は、周縁部を押さえるフランジ部を有する。第３の部材の凝固収縮によって第２の部材がフランジ部と第１の部材とで圧縮されることにより、フランジ部と第１の部材との間に第２の部材が固定される。
　第１４の発明では、第２の部材は、第１の部材に対して溶接が困難な材料で構成されている。第１の部材には、厚み方向に貫通する第１貫通部が形成されている。第３の部材は、第２の部材の第２貫通部を介して第１貫通部の内周面および第２の部材の第２貫通部により開口される第１の部材の開口面にアーク溶接される。第３の部材の凝固収縮によって第２の部材がフランジ部と第１の部材とで圧縮されることにより、第３の部材のフランジ部と第１の部材との間に第２の部材が固定される。
　このように、第１の部材に第１貫通部を設け、第３の部材を第１貫通部の内周面および第２の部材の第２貫通部により開口される第１の部材の開口面にアーク溶接することで、第３の部材の溶着面積を増やすことができる。これにより、第１の部材、第２の部材、及び第３の部材の接合強度を確保することができる。
　本発明によれば、溶加材の溶着面積を増やして接合強度を確保することができる。
本実施形態１に係る接合構造を説明するための側面断面図である。 本実施形態２に係る接合構造を説明するための側面断面図である。 本実施形態３に係る接合構造を説明するための側面断面図である。 本実施形態４に係る接合構造を説明するための側面断面図である。 本実施形態５に係る接合構造を説明するための側面断面図である。 本実施形態６に係る接合構造を説明するための側面断面図である。 本実施形態７に係る接合構造を説明するための側面断面図である。 本実施形態８に係る接合構造を説明するための側面断面図である。 本実施形態９に係る接合構造を説明するための側面断面図である。 本実施形態１０に係る接合構造を説明するための側面断面図である。 本実施形態１１に係る接合構造を説明するための側面断面図である。 本実施形態１２に係る接合構造を説明するための側面断面図である。 本実施形態１３に係る接合構造を説明するための側面断面図である。
　以下、本発明の実施形態を図面に基づいて説明する。なお、以下の好ましい実施形態の説明は、本質的に例示に過ぎず、本発明、その適用物或いはその用途を制限することを意図するものではない。
　《実施形態１》
　図１は、金属材で構成された第１の部材１０と、第１の部材１０に対して溶接が困難な材料で構成された第２の部材２０と、溶加材で構成された第３の部材３０とを互いに接合するための接合構造を示している。
　第１の部材１０は、金属材で構成された板状の部材である。第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。図１に示す例では、第１貫通部１１は、円形状の貫通孔で形成されている。第１貫通部１１は、例えば、フライス盤加工、旋盤加工、ボール盤加工等やレーザ加工によって貫通孔として形成される。第１の部材１０は、上面１０ｂと、上面１０ｂとは反対の下面１０ｃとを有する。上面１０ｂは、第２の部材２０に面している。第１貫通部１１は、上面１０ｂから下面１０ｃまで延びている。
　第２の部材２０は、第１の部材１０に対して溶接が困難な材料で構成された板状の部材である。第２の部材２０は、第１の部材１０の上側に重ね合わされている。第２の部材２０は、厚み方向に貫通する第２貫通部２１を有する。第２貫通部２１は、第１の部材１０の第１貫通部１１に対応する位置に開口している。また、第１の部材１０に重ねられる第２部材２０の第２貫通部２１によって開口される第１の部材１０の上面は開口面１０ａとする。この開口面１０ａは第１貫通部１１の上面に相当する。第２の部材２０は、さらに、第２貫通部２１を画定する周縁部２３を有する。
　なお、本実施形態では、第２貫通部２１を円形状の貫通孔として説明するが、楕円状や長孔状の貫通孔であってもよい。貫通部２１は、貫通溝であってもよい。貫通溝は、第２の部材２０の厚み方向には上面から下面まで貫通する。貫通溝は、さらに、貫通溝の長さ方向の両端または一端では開放されている。この点で、貫通溝は、長孔状の貫通孔とは異なる。長孔状の貫通孔は、貫通孔の長さ方向の両端では閉じられている。例えば、貫通溝の長さ方向の両端で開放されている場合、第２の部材２０は、第１の部材１０上に配置された少なくとも２つの独立した板を含む。この２つの板は、互いに細長い隙間をあけて並べられている。この隙間が第２貫通部としての貫通溝を形成する。第２の部材２０が複数の独立した板を含んで複数の貫通溝を形成している場合、溶融した溶加材としての第３の部材３０を複数の貫通溝を介して第１の部材１０に溶接することで、第２の部材２０を第３の部材３０と第１の部材１０とで挟み込んで、第２の部材２０を第１の部材１０に固定する。
　第３の部材３０は、第１の部材１０と同種系の金属材である溶加材で構成されている。ここで、同種系の金属材とは、互いに溶接可能な金属であり、同じ材質同士だけではなく、鉄系金属材同士、非鉄系金属材同士などの溶接接合性がよい金属材のことである。言い換えると、同種系の金属材とは、溶接の相性がよい同種系の材料のことである。
　具体的には、溶接時における第１の部材１０と第３の部材３０との組み合わせとしては、以下のものが挙げられる。例えば、鉄系金属材の組合せとしては、軟鋼と軟鋼、ステンレスとステンレス、軟鋼とハイテン（高張力鋼）、ハイテンとハイテン等がある。また、非鉄系金属材としては、アルミとアルミ、アルミとアルミ合金、アルミ合金とアルミ合金等がある。
　また、異種材としての第２の部材２０は、同種系の金属材としての第１の部材１０及び第３の部材３０とは、異なる材質の材料であり、第１の部材１０及び第３の部材３０に対して溶接が困難な材質である。
　例えば、同種系の金属材としての第１の部材１０及び第３の部材３０を鉄系金属材にした場合、異種材としての第２の部材２０は、銅材やアルミ材等の非鉄系金属材である。また、例えばＣＦＲＰ（Carbon Fiber Reinforced Plastics，炭素繊維強化プラスチック）、ＰＥＴ（PolyEthlen Terephthalate，ポリエチレンテレフタレート）等といった樹脂材も金属材に対する異種材として挙げられる。
　なお、以下の説明では、第１の部材１０として軟鋼材、第２の部材２０としてアルミ材、溶加材である第３の部材３０として軟鋼材を用いた場合について説明する。
　アーク溶接機１は、ノズル２と、チップ３とを備えている。ノズル２は、溶接対象物の溶接箇所にシールドガス等を供給する。チップ３は、第３の部材３０に対して溶接電流を供給する。
　アーク溶接機１は、第２貫通部２１を介して第１貫通部１１に第３の部材３０を送給しながら溶接電流を供給することで、アーク５を発生させる。アーク５は、第１の部材１０における、第１貫通部１１の内周面と、第１の部材１０の上面である開口面１０ａとに照射される。このアーク５により溶融した第３の部材３０は、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。このとき、第３の部材３０の溶融量は、第１貫通部１１の下方から流れ落ちない程度に調整されている。さらに第３の部材３０の溶融量は、第１貫通部１１の下方から一部が突出可能な量に調整されても良い。これにより、第１貫通部１１にアーク溶接により溶融接合された第３の部材３０は、第１の部材１０に対して楔のようなアンカー効果で接合強度及び信頼性がより向上する。
　そして、溶融した第３の部材３０は、第１の部材１０の上面側の開口面１０ａと第２の部材の第２貫通部２１内に積層されていき、第２貫通部２１内を埋め尽くした後、第２貫通部２１の上面側の周縁部２３に流れ出し、フランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、第２貫通部２１の周縁部２３を押さえるフランジ部３１が設けられる。フランジ部３１は、第２の部材２０における第１の部材１０とは反対側の面（図１では上面）において、第２貫通部２１よりも径方向外方に張り出している。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、第１の部材１０に第１貫通部１１を設け、第３の部材３０を第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶接することで、第３の部材３０の溶着面積を増やすことができる。これにより、第１の部材１０、第２の部材２０、及び第３の部材３０の接合強度を確保することができる。
　また、第１貫通部１１の内周面と開口面１０ａとで第３の部材３０の凸部形状が形成される。凸部形状は、接合される表面積を拡大する。凸部形状は、楔のようなアンカー効果を発揮して接合強度及び信頼性をより向上させる。なお、第１貫通部１１の径は、第２の部材２０の第２貫通部２１の径（第２の部材２０の第２貫通部２１により開口される第１の部材１０の開口面１０ａの径）よりも小さい。これにより、第１の部材１０および第２の部材２０に対する入熱を抑制しながら溶接を行うことが出来る。
　《実施形態２》
　以下、前記実施形態１と同じ部分については同じ符号を付し、相違点についてのみ説明する。
　図２に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０の第１貫通部１１に対応する位置に開口する第２貫通部２１を有する。第２貫通部２１は、周縁部２３により画定されている。周縁部２３は、第１の部材１０に向かって先細りとなるテーパー部２２を有する。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、第２貫通部２１のテーパー部２２に沿って第１貫通部１１に向かって流れ、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。このとき、第３の部材３０の溶融量は、第１貫通部１１の下方から流れ落ちない程度に調整されている。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くすことで、テーパー部２２の上面にフランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、テーパー部２２を押さえるフランジ部３１が設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、周縁部２３にテーパー部２２を設けることで、溶融した第３の部材３０が第１貫通部１１に向かって流れ易くなる。また、テーパー部２２に沿った形状にフランジ部３１を形成することで、第２の部材２０から飛び出すフランジ部３１の厚みを抑えることができる。
　《実施形態３》
　図３に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、下面１０ｃに向かって先細りとなるテーパー状に形成されている。すなわち、第１貫通部１１は、テーパー形状を有する。第１貫通部１１は、厚み方向に第２の部材２０に近い端１０ｄと第２の部材２０から遠い端１０ｅとを有する。遠い端１０ｅは、近い端１０ｄよりも小さなサイズを有する。
　第２の部材２０は、第１の部材１０の第１貫通部１１に対応する位置に開口する第２貫通部２１を有する。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、第１貫通部１１のテーパー形状に沿って第１貫通部１１の内部に向かって流れ、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。このとき、第３の部材３０の溶融量は、溶融した第３の部材３０が第１貫通部１１の下方から流れ落ちない程度に調整されている。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くした後、第２の部材２０の上面側の周縁部２３に流れ出し、フランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、周縁部２３を押さえるフランジ部３１が設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、第１貫通部１１を、下面１０ｃに向かって先細りとなるテーパー状に形成することで、溶融した第３の部材３０が第１貫通部１１の内部に向かって流れ易くなる。
　《実施形態４》
　図４に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、下面１０ｃに向かって幅広となるテーパー状に形成されている。すなわち、第１貫通部１１は、テーパー形状を有する。第１貫通部１１は、厚み方向に第２の部材２０に近い端１０ｄと第２の部材２０から遠い端１０ｅとを有する。遠い端１０ｅは、近い端１０ｄよりも大きなサイズを有する。
　第２の部材２０は、第１の部材１０の第１貫通部１１に対応する位置に開口する第２貫通部２１を有する。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。このとき、第３の部材３０の溶融量は、溶融した第３の部材３０が第１貫通部１１の下方から流れ落ちない程度に調整されている。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くした後、第２の部材２０の上面側の周縁部２３に流れ出し、フランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、周縁部２３を押さえるフランジ部３１が設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、第１貫通部１１を、下面１０ｃに向かって幅広となるテーパー状に形成するようにしている。これにより、溶融した第３の部材３０が第１貫通部１１の幅広部分で凝固すると、第３の部材３０が第１貫通部１１に食い込んだ状態となり、接合強度を高めることができる。
　《実施形態５》
　図５に示すように、第１貫通部１１は、複数の第１小貫通部１１ａを含む。第１の部材１０は、厚み方向に貫通する複数の第１小貫通部１１ａを有する。第１小貫通部１１ａは、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０の複数の第１小貫通部１１ａに対応する位置に開口する１つの第２貫通部２１を有する。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、複数の第１小貫通部１１ａに分散して各第１小貫通部１１ａの内周面および第１の部材１０の開口面１０ａに溶融結合される。このとき、第３の部材３０の溶融量は、溶融した第３の部材３０が第１小貫通部１１ａの下方から流れ落ちない程度に調整されている。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くした後、第２の部材２０の上面側の周縁部２３に流れ出し、フランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、周縁部２３を押さえるフランジ部３１が設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、第１小貫通部１１ａを複数設けることで、溶融した第３の部材３０を複数の第１小貫通部１１ａに分散させながら溶接することができる。また、複数の第１小貫通部１１ａに第３の部材３０が食い込んだ状態とすることで、複数の第１小貫通部１１ａにおいてくさび効果を得ることができ、接合安定性が向上する。
　《実施形態６》
　図６に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０の第１貫通部１１に対応する位置に開口する第２貫通部２１を有する。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。このとき、第３の部材３０の溶融量は、溶融した第３の部材３０が第１貫通部１１の下方からはみ出して第１貫通部１１の下面側の周縁部１３に広がる程度に調整されている。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くした後、第２の部材２０の上面側の周縁部２３に流れ出し、フランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、周縁部２３を押さえるフランジ部３１と、周縁部１３に係止する係止部３２とが設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と係止部３２とで圧縮される。この圧縮により、フランジ部３１と係止部３２との間に、第１の部材１０及び第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、係止部３２によって、第３の部材３０が第１貫通部１１から抜けるのを抑えることができる。また、フランジ部３１と係止部３２との間に第１の部材１０及び第２の部材２０が固定されるので、接合強度を高めることができる。
　《実施形態７》
　図７に示すように、第１貫通部１１は、複数の第１小貫通部１１ａを含む。第１の部材１０は、厚み方向に貫通する複数の第１小貫通部１１ａを有する。第１小貫通部１１ａは、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０の複数の第１小貫通部１１ａに対応する位置に開口する１つの第２貫通部２１を有する。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、複数の第１小貫通部１１ａに分散して各第１小貫通部１１ａの内周面および第１の部材１０の開口面１０ａに溶融結合される。このとき、第３の部材３０の溶融量は、溶融した第３の部材３０が第１小貫通部１１ａの下方からはみ出して第１の部材１０の下面側の周縁部１３に広がる程度に調整されている。図７に示す例では、複数の第１小貫通部１１ａの下方からはみ出した第３の部材３０同士がブリッジ状に連結した状態となっている。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くした後、第２の部材２０の上面側の周縁部２３に流れ出し、フランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、周縁部２３を押さえるフランジ部３１と、周縁部１３に係止する係止部３２とが設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と係止部３２との間に、第１の部材１０及び第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、複数の第１小貫通部１１ａの下方からはみ出してブリッジ状に連結された係止部３２によって、第３の部材３０が第１小貫通部１１ａから抜けるのを抑えることができる。また、複数の第１小貫通部１１ａに第３の部材３０が食い込んだ状態とすることで、複数の第１小貫通部１１ａにおいてくさび効果を得ることができ、接合安定性が向上する。
　《実施形態８》
　図８に示すように、第１貫通部１１は、複数の第１小貫通部１１ａを含む。第１の部材１０は、厚み方向に貫通する複数の第１小貫通部１１ａを有する。第１小貫通部１１ａは、円形状の貫通孔で形成されている。複数の第１小貫通部１１ａは、厚み方向に対して傾斜する方向に貫通している。
　図８に示す例では、左側の第１小貫通部１１ａは、右斜め下方に傾斜している。右側の第１小貫通部１１ａは、左斜め下方に傾斜している。これにより、左右の第１小貫通部１１ａにおける下側の開口間の距離が、上側の開口間の距離よりも短くなっている。
　第２の部材２０は、第１の部材１０の複数の第１小貫通部１１ａに対応する位置に開口する１つの第２貫通部２１を有する。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、複数の第１小貫通部１１ａに分散しながら、斜め下方に流れて各第１小貫通部１１ａの内周面および第１の部材１０の開口面１０ａに溶融結合される。このとき、第３の部材３０の溶融量は、溶融した第３の部材３０が第１小貫通部１１ａの下方からはみ出して第１の部材１０の下面側の周縁部１３に広がる程度に調整されている。図８に示す例では、複数の第１小貫通部１１ａの下方からはみ出した第３の部材３０同士がブリッジ状に連結した状態となっている。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くした後、第２の部材２０の上面側の周縁部２３に流れ出し、フランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、周縁部２３を押さえるフランジ部３１と、周縁部１３に係止する係止部３２とが設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と係止部３２とで圧縮される。この圧縮により、フランジ部３１と係止部３２との間に、第１の部材１０及び第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、複数の第１小貫通部１１ａを、下側の開口間の距離が短くなるように傾斜させているので、複数の第１小貫通部１１ａの下方からはみ出した第３の部材３０同士をブリッジ状に連結させて係止部３２を形成し易くなる。また、係止部３２によって、第３の部材３０が第１小貫通部１１ａから抜けるのを抑えることができる。
　《実施形態９》
　図９に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０の第１貫通部１１に対応する位置に開口する第２貫通部２１を有する。第２の部材２０の上面には、固定部材４０が重ね合わされている。
　固定部材４０は、例えば矩形状や円盤状の金属材で構成されている。
　固定部材４０の外形形状は、第２の部材２０の周縁部２３を押さえる形状であればどのような形であっても良い。
　固定部材４０は、第１の部材１０及び第３の部材３０と溶接可能な同種系の金属材で構成されている。なお、固定部材４０は、第１の部材１０及び第３の部材３０とは異なる材質で構成されていてもよい。
　固定部材４０の中央部には、第２の部材２０側にテーパー状に押し出されたエンボス形状の突起部４１が設けられている。突起部４１は、第２貫通部２１に挿入されている。
　固定部材４０は、第２貫通部２１及び第１貫通部１１に対応する位置に開口する固定孔４２を有する。固定孔４２は、突起部４１の底面に形成されている。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、固定孔４２及び第２貫通部２１を介して第１貫通部１１に向かって流れ、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。溶融した第３の部材３０は、固定部材４０の上面にフランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、固定部材４０の固定孔４２の周縁部を押さえるフランジ部３１が設けられる。フランジ部３１は、固定部材４０を介して第２の部材２０の周縁部２３を間接的に押さえている。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、固定部材４０及び第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、第３の部材３０を第１の部材１０の第１貫通部１１に溶接する際に、固定部材４０によって第２の部材２０への入熱量を抑えながら、フランジ部３１を形成することができる。そして、異種材である第２の部材２０を、第１の部材１０と固定部材４０との間に挟み込んで固定することができる。
　《実施形態１０》
　図１０に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０の第１貫通部１１に対応する位置に開口する第２貫通部２１を有する。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。
　このとき、第２の部材２０の周縁部２３に沿ってアーク溶接機１のノズル２を旋回させることで、周縁部２３に対して、溶融した第３の部材３０を供給する。これにより、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くすとともに、第２の部材２０の上面側の周縁部２３にフランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、周縁部２３を押さえるフランジ部３１が設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、アーク溶接機１のノズル２を旋回させ、第２の部材２０の周縁部２３に対して、低入熱である交流溶接や短絡溶接によるスパイラル状の軌跡でアーク溶接することで、入熱を抑えながらのフランジ部３１を形成することができる。
　《実施形態１１》
　図１１に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０とは反対側の面（図１１では上面）に開口する段差部２５と、段差部２５の底面に形成された第２貫通部２１とを有する。第２貫通部２１は、第１の部材１０の第１貫通部１１に対応する位置に開口している。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くした後、第２の部材２０の上面側の周縁部２３、つまり、段差部２５の底面に流れ出し、フランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、周縁部２３を押さえるフランジ部３１が設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が圧縮固定される。
　以上のように、本実施形態に係る接合構造によれば、第３の部材３０のフランジ部３１を段差部２５内に配置して、第２の部材２０からフランジ部３１が飛び出すのを抑えることができる。
　《実施形態１２》
　図１２に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０とは反対側の面（図１２では上面）に開口する段差部２５と、段差部２５の底面に形成された第２貫通部２１とを有する。段差部２５の底面は、第２貫通部２１に向かって傾斜している。第２貫通部２１は、第１の部材１０の第１貫通部１１に対応する位置に開口している。
　第３の部材３０は、アーク５により溶融する。溶融した第３の部材３０は、段差部２５の傾斜面に沿って第２貫通部２１に向かって流れた後、第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合される。
　そして、溶融した第３の部材３０は、第２貫通部２１内を埋め尽くした後、第２の部材２０の上面側の周縁部２３、つまり、段差部２５の底面に流れ出し、段差部２５の傾斜面にフランジ状に広がる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、段差部２５の傾斜面を押さえるフランジ部３１が設けられる。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、段差部２５の底面を第２貫通部２１に向かって傾斜させることで、溶融した第３の部材３０が第２貫通部２１に向かって流れ易くなる。また、第３の部材３０のフランジ部３１を段差部２５内に配置して、第２の部材２０からフランジ部３１が飛び出すのを抑えることができる。
　《実施形態１３》
　図１３に示すように、第１の部材１０は、厚み方向に貫通する第１貫通部１１を有する。第１貫通部１１は、円形状の貫通孔で形成されている。
　第２の部材２０は、第１の部材１０の第１貫通部１１に対応する位置に開口する第２貫通部２１を有する。
　第３の部材３０は、アーク５により溶融する。第３の部材３０は、第１の部材１０に溶接された第１接合部３５と、第１接合部３５に溶接されてフランジ部３１を構成する第２接合部３６とを有する。
　具体的に、溶融した第３の部材３０を、第２貫通部２１を介して第１の部材１０に溶接する際には、溶け込みに必要な入熱で、アーク５の広がりが小さい短絡溶接を行い、上側中央部が凹んだ形状の第１接合部３５を形成する。その後、第２の部材２０を溶融しない程度の低入熱で、アーク５の広がりが大きい正極性や交流によるパルス溶接を行い、溶融した第３の部材３０が、第１接合部３５の上側中央部が凹んだ形状に沿って広がり第２接合部３６を形成する。これにより、第２の部材２０への入熱量を抑えながら、フランジ部３１を形成することができる。
　溶融した第３の部材３０がビードとなる過程で、第３の部材３０には、第１接合部３５と、第２接合部３６とが設けられる。第１接合部３５は、第１の部材１０の第１貫通部１１の内周面および第１の部材１０の開口面１０ａに溶融結合している。第２接合部３６は、第１接合部３５に溶融結合して、周縁部２３を押さえるフランジ部３１を構成している。
　そして、第３の部材３０が凝固収縮することで、第２の部材２０がフランジ部３１と第１の部材１０とで圧縮される。この圧縮により、フランジ部３１と第１の部材１０との間に、異種材である第２の部材２０が固定される。
　以上のように、本実施形態に係る接合構造によれば、第３の部材３０を、第１接合部３５と第２接合部３６とに分けて形成することで、第２の部材２０の材料特性を考慮した溶接法又は溶接条件の使い分けをすることができる。
　《その他の実施形態》
　前記実施形態については、以下のような構成としてもよい。
　本実施形態では、第１の部材１０の第１貫通部１１に対してアーク溶接を行うようにしたが、例えば、レーザフィラー溶接を行うようにしてもよい。
　また、本実施形態において説明した第１の部材１０の第１貫通部１１の形状と、第２の部材２０の第２貫通部２１の形状との組み合わせは、あくまでも一例であり、その他の組み合わせであってもよい。
　以上説明したように、本発明は、溶加材の溶着面積を増やして接合強度を確保することができるという実用性の高い効果が得られることから、きわめて有用で産業上の利用可能性は高い。
　１０　　第１の部材
　１１　　第１貫通部
　２０　　第２の部材
　２１　　第２貫通部
　２２　　テーパー部
　１３、２３　　周縁部
　２５　　段差部
　３０　　第３の部材
　３１　　フランジ部
　３２　　係止部
　３５　　第１接合部
　３６　　第２接合部
　４０　　固定部材
　４２　　固定孔

Claims (14)

  1. 　金属材で構成された第１の部材と、該第１の部材に対して溶接が困難な材料で構成された第２の部材と、該第１の部材に溶接された溶加材で構成された第３の部材とが互いに接合された接合構造であって、
    　前記第１の部材は、厚み方向に貫通する第１貫通部を有し、
    　前記第２の部材は、前記第１貫通部に対応する位置に開口する第２貫通部を有し、
    　前記第３の部材は、前記第２貫通部の周縁部を押さえるフランジ部を有するとともに、該第２貫通部を介して前記第１の部材の前記第１貫通部の内周面および前記第２の部材の前記第２貫通部により開口される前記第１の部材の開口面にアーク溶接され、
    　前記第３の部材の凝固収縮によって前記第２の部材が前記フランジ部と前記第１の部材とで圧縮されることにより、前記フランジ部と該第１の部材との間に前記第２の部材が固定されている接合構造。
  2. 　請求項１において、
    　前記フランジ部は、前記第２の部材における前記第１の部材とは反対側の面において、該第２貫通部よりも径方向外方に張り出している接合構造。
  3. 　請求項１において、
    　前記第２貫通部は、前記周縁部により画定されており、前記周縁部は、前記第１の部材に向かって先細りとなるテーパー部を有し、
    　前記フランジ部は、前記テーパー部を押さえている接合構造。
  4. 　請求項１乃至３のうち何れか１つにおいて、
    　前記第１貫通部は、テーパー形状を有し、前記第１貫通部は、前記厚み方向に前記第２の部材に近い端と前記第２の部材から遠い端とを有し、前記遠い端は、前記近い端よりも小さなサイズを有する接合構造。
  5. 　請求項１乃至３のうち何れか１つにおいて、
    　前記第１貫通部は、テーパー形状を有し、前記第１貫通部は、前記厚み方向に前記第２の部材に近い端と前記第２の部材から遠い端とを有し、前記遠い端は、前記近い端よりも大きなサイズを有する接合構造。
  6. 　請求項１乃至５のうち何れか１つにおいて、
    　前記第１貫通部は、前記第１貫通部よりも小さな複数の第１小貫通部を含む接合構造。
  7. 　請求項１乃至６のうち何れか１つにおいて、
    　前記第３の部材は、前記第１の部材における前記第２の部材とは反対側の面において前記第１貫通部の周縁部に係止する係止部を有する接合構造。
  8. 　請求項１乃至７のうち何れか１つにおいて、
    　前記第２の部材における前記第１の部材とは反対側の面に重ね合わされた固定部材を備え、
    　前記固定部材は、前記第２貫通部及び前記第１貫通部に対応する位置に開口する固定孔を有し、
    　前記第３の部材は、前記固定孔及び前記第２貫通部を介して前記第１貫通部の内周面および前記第２の部材の前記第２貫通部により開口される前記第１の部材の開口面にアーク溶接され、
    　前記フランジ部は、前記固定部材を介して前記第２貫通部の周縁部を押さえており、
    　前記第３の部材の凝固収縮によって前記固定部材および前記第２の部材が前記フランジ部と前記第１の部材とで圧縮されることにより、前記フランジ部と該第１の部材との間に、前記固定部材及び前記第２の部材が固定されている接合構造。
  9. 　請求項１乃至８のうち何れか１つにおいて、
    　前記第２の部材は、前記第１の部材とは反対側の面に開口する段差部をさらに有し、前記第２貫通部は、該段差部の底面に形成された接合構造。
  10. 　請求項９において、
    　前記段差部の底面は、前記第２貫通部に向かって傾斜している接合構造。
  11. 　請求項１乃至１０のうち何れか１つにおいて、
    　前記第３の部材は、前記第１の部材に溶接された第１接合部と、該第１接合部に溶接されて前記フランジ部を構成する第２接合部とを有する接合構造。
  12. 　請求項１乃至１１のうち何れか１つにおいて、
    　前記第１貫通部は、前記第２貫通部よりも小さなサイズを有し、前記開口面は、前記第１の部材の前記上面のうち前記第２貫通部内にある領域である接合構造。
  13. 　上面と、前記上面の反対の下面と、前記上面から前記下面まで延びた第１貫通部とを有し、金属材で構成された第１の部材と、
    　前記第１の貫通部に対応する位置に開口しており前記第１の貫通部よりも大きな第２貫通部と、前記第２貫通部を画定する周縁部とを有し、前記第１の部材に対して溶接が困難な材料で構成され、前記第１の部材の前記上面に配された第２の部材と、
    　前記第１貫通部の内周面および前記第１の部材の前記上面における前記第１貫通部の周囲にアーク溶接された溶接部と、前記第２貫通部を介して前記溶接部につながり前記周縁部を覆うフランジ部とを有し、前記第１の部材に溶接された溶加材で構成された第３の部材と、を備え、
    　前記第２の部材が、前記第３の部材の凝固収縮によって前記フランジ部と前記第１の部材とで圧縮されることにより、前記フランジ部と前記第１の部材との間に固定されている接合構造。
  14. 　上面と前記上面の反対の下面とを有し、前記上面から前記下面まで延びた第１貫通部を有する、金属材で構成された第１の部材を準備し、
    　第２貫通部と前記第２貫通部を画定する周縁部とを有し、前記第１の部材に対して溶接が困難な材料で構成された第２の部材を準備し、
    　前記第２貫通部が前記第１貫通部に対応して位置し、かつ、前記第２の部材の前記第２貫通部により開口される前記第１の部材の開口面が形成されるように、前記第２の部材を前記第１の部材の前記上面に配置し、
    　前記第２貫通部を介して前記第１の部材の前記第１貫通部の内周面および前記第１の部材の開口面にアーク溶接することにより、前記第１の部材に溶接された溶加材で構成され、前記周縁部を押さえるフランジ部を有する第３の部材を形成し、
    　前記第３の部材の凝固収縮によって前記第２の部材が前記フランジ部と前記第１の部材とで圧縮されることにより、前記フランジ部と前記第１の部材との間に前記第２の部材が固定される、接合方法。
PCT/JP2020/015775 2019-04-19 2020-04-08 接合構造 WO2020213491A1 (ja)