WO2020066779A1 - 磁性部材用粉末 - Google Patents
磁性部材用粉末 Download PDFInfo
- Publication number
- WO2020066779A1 WO2020066779A1 PCT/JP2019/036505 JP2019036505W WO2020066779A1 WO 2020066779 A1 WO2020066779 A1 WO 2020066779A1 JP 2019036505 W JP2019036505 W JP 2019036505W WO 2020066779 A1 WO2020066779 A1 WO 2020066779A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- powder
- alloy
- mass
- magnetic
- particles
- Prior art date
Abstract
周波数が100kHzから20MHzの領域においてノイズを抑制できる磁性部材に適した粉末が提供される。この磁性部材用粉末は、多数の粒子2からなる。この粒子2の主部は、合金製である。この合金は、Bを含む。この合金におけるBの含有率は、5.0質量%以上8.0質量%以下である。この合金はさらに、Cr、Mn、Co及びNiからなる群から選択された1種又は2種以上の元素を含みうる。これらの元素の含有率は、0質量%以上25質量%以下である。この合金の残部は、Fe及び不可避的不純物である。この合金は、Fe2B相を含む。合金におけるFe2B相の面積率は、20%以上80%以下である。
Description
本発明は磁性部材用粉末に関する。詳細には、磁性シート、磁性リング等の部材中に分散される粉末に関する。
携帯電話機、ノート型パーソナルコンピュータ、タブレット型パーソナルコンピュータ等の携帯用電子機器が、近年普及している。最近では、これらの機器の小型化及び高性能化が進んでいる。機器の小型化に伴い、機器内の回路部品にも、小型化及び高性能化の要求が高まっている。小型化及び高性能化された機器では、回路に装着される電子部品の密度が高い。従って、この電子部品から放射される電波ノイズに起因して、電子部品同士間の電波干渉、及び電子回路同士間の電波干渉が生じやすい。電波干渉は、電子機器の誤動作を招来する。
電波干渉の抑制の目的で、電子機器にノイズ抑制シートが挿入されることがある。このノイズ抑制シートは、放出された放射電波(ノイズ)を磁力に変換し、電子回路外への電波放出を防ぐ。ノイズ抑制シートの加工は容易であり、かつこのシートの形状自由度は高い。
典型的な従来のノイズ抑制シートには、フェライトと呼ばれる酸化物が、磁性材料として用いられている。このフェライトの透磁率は、高周波域において小さい。具体的には、周波数が100kHzから20Mzである領域において、透磁率が小さい。従って、この周波数域における電波から磁力への変換効率は、不十分である。
フェライトを含まず、透磁率の高い軟磁性金属粉末を含む磁性シート及び磁性リングが、提案されている。特許文献1(特開2017-208416号公報)には、FeMn合金粉末が用いられたノイズ抑制シートが開示されている。特許文献2(特開2011-108775号公報)には、Fe-Si-Al系の扁平粉末が用いられたノイズ抑制シートが開示されている。
特許文献1に開示された粉末では、反磁界係数低減の目的で、粒子が扁平化されている。この粒子の合金は、球状での使用には適していない。さらにこの粒子は、樹脂との混合による使用には適していない。
特許文献2に記載されたノイズ抑制シートでは、粉末が扁平化されているので、比較的高い周波数域でも、高い透磁率が達成されうる。しかし、Fe-Si-Al系の組成を有する粉末では、20MHzに近い高周波数域でのノイズ抑制は、十分ではない。
近年の電子機器に用いられる磁性部材には、高周波数域でのノイズ抑制の要請がある。本発明の目的は、周波数が100kHzから20MHzの領域においてノイズを抑制できる磁性部材に適した粉末の提供にある。
本発明に係る磁性部材用粉末は、複数の粒子からなる。これらの粒子の各々の主部は、
B:5.0質量%以上8.0質量%以下、並びに
残部:Fe及び不可避的不純物
からなる合金製である。この合金は、Fe2B相を含む。
B:5.0質量%以上8.0質量%以下、並びに
残部:Fe及び不可避的不純物
からなる合金製である。この合金は、Fe2B相を含む。
他の観点によれば、本発明に係る磁性部材用粉末は、複数の粒子からなる。これらの粒子の各々の主部は、
B:5.0質量%以上8.0質量%以下
Cr、Mn、Co及びNiからなる群から選択された1種又は2種以上:0質量%以上25質量%以下、並びに
残部:Fe及び不可避的不純物
からなる合金製である。この合金は、Fe2B相を含む。
B:5.0質量%以上8.0質量%以下
Cr、Mn、Co及びNiからなる群から選択された1種又は2種以上:0質量%以上25質量%以下、並びに
残部:Fe及び不可避的不純物
からなる合金製である。この合金は、Fe2B相を含む。
好ましくは、合金におけるFe2B相の面積率PSは、20%以上80%以下である。
好ましくは、合金における、各元素の有する電子の数の加重平均Nに対する、bHcの比(bHc/N)は、500A/(m・個)以上700A/(m・個)以下である。
粒子が、主部の表面に位置する絶縁被覆を有してもよい。
好ましくは、粒子が、球形状を有する。
本発明に係る粉末が用いられた磁性部材では、周波数が100kHzから20MHzの領域にて、ノイズが抑制されうる。
以下、適宜図面が参照されつつ、好ましい実施形態に基づいて本発明が詳細に説明される。
[第一実施形態]
本発明に係る磁性部材用粉末は、多数の粒子の集合体である。それぞれの粒子は、球形状を有するのが好ましい。図1は、この粒子2の断面図である。図2は、この粉末が分散した磁性部材(磁性シート4)が示された断面図である。
本発明に係る磁性部材用粉末は、多数の粒子の集合体である。それぞれの粒子は、球形状を有するのが好ましい。図1は、この粒子2の断面図である。図2は、この粉末が分散した磁性部材(磁性シート4)が示された断面図である。
この磁性シート4が得られるには、まず粉末が、樹脂及びゴムのような基材ポリマーに、各種薬品と共に混練されてポリマー組成物が得られる。混練には、既知の方法が採用されうる。例えば、密閉式混練機、オープンロール等により、混練がなされうる。薬品として、潤滑材及びバインダーのような加工助剤が例示される。
次に、このポリマー組成物から、磁性シート4が成形される。成形には、既知の方法が採用されうる。圧縮成形法、射出成形法、押出成形法、圧延法等により、成形がなされうる。
磁性部材の形状は、シート状には限られない。リング状、立方体状、直方体状、円筒状等の形状が、採用されうる。加工が容易との観点から、組成物に、潤滑材、バインダー等の加工助剤が配合されてもよい。
磁性部材の性能を表す指標として、透磁率μ、実部透磁率μ’及び虚部透磁率μ”がある。実部透磁率μ’は、電磁波遮蔽特性の優劣を表す。虚部透磁率μ”は、電磁波吸収特性の優劣を表す。透磁率μは、下記数式:
μ=μ’+jμ”
によって算出されうる。この数式において、「j」は虚数単位を表す。換言すれば、「j」の二乗は-1である。なお、本願において、透磁率μ、実部透磁率μ’及び虚部透磁率μ”のそれぞれは、真空透磁率との比である比透磁率で表される。高周波での磁気損失tanδは、この虚部透磁率μ”と実部透磁率μ’との比で表される。換言すれば、磁気損失tanδは下記数式:
tanδ = μ” / μ’
によって算出される。この数式から明らかな通り、渦電流損失、磁気共鳴等に起因してμ’が低下しμ”が上昇すると、損失tanδが上昇する。
μ=μ’+jμ”
によって算出されうる。この数式において、「j」は虚数単位を表す。換言すれば、「j」の二乗は-1である。なお、本願において、透磁率μ、実部透磁率μ’及び虚部透磁率μ”のそれぞれは、真空透磁率との比である比透磁率で表される。高周波での磁気損失tanδは、この虚部透磁率μ”と実部透磁率μ’との比で表される。換言すれば、磁気損失tanδは下記数式:
tanδ = μ” / μ’
によって算出される。この数式から明らかな通り、渦電流損失、磁気共鳴等に起因してμ’が低下しμ”が上昇すると、損失tanδが上昇する。
金属からなる磁性粉末の飽和磁束密度は、フェライトのそれよりも高い。これは、金属粉末の長所である。一方、従来の金属粉末では、フェライトに比べ、磁気共鳴による損失が低周波域で発生する。従ってこの金属粉末は、高周波域(周波数が100kHzから20MHzの範囲)での損失低減には、適していない。
粉末の扁平化は、高透磁率確保には有用である。しかし、扁平化された粉末は、ポリマーとの混練性に劣る。
発明者らは検討を進めた結果、所定の組成及び組織を有する金属粉末が、磁性部材に適していることを見出した。本発明に係る粉末では、高周波域において損失が抑制されうる。
この粒子2の主部は、合金製である。ここで主部とは、粒子2がその表面に絶縁性皮膜を有する場合、この被膜を除いた部分のことである。この合金は、Bを含む。この合金におけるBの含有率は、5.0質量%以上8.0質量%以下である。この合金はさらに、Cr、Mn、Co及びNiからなる群から選択された1種又は2種以上の元素を含みうる。これらの元素の含有率は、0質量%以上25質量%以下である。この合金の残部は、Fe及び不可避的不純物である。以下、各元素の役割が詳説される。
[ホウ素(B)]
Bは、Feと結合し、金属間化合物を生成する。金属間化合物が生成した合金は、Fe2B相を含む。この合金からなる粒子を含む磁性シート4では、周波数が100kHzから20MHzの領域における損失が小さい。この磁性シート4では、周波数が100kHzから20MHzの領域において、ノイズが抑制されうる。ノイズ抑制の観点から、Bの含有率は5.0質量%以上が好ましく、5.5質量%以上が特に好ましい。過剰のFe2B相は、飽和磁束密度を低下させる。飽和磁束密度の観点から、Bの含有率は8.0質量%以下が好ましく、7.5質量%以下が特に好ましい。
Bは、Feと結合し、金属間化合物を生成する。金属間化合物が生成した合金は、Fe2B相を含む。この合金からなる粒子を含む磁性シート4では、周波数が100kHzから20MHzの領域における損失が小さい。この磁性シート4では、周波数が100kHzから20MHzの領域において、ノイズが抑制されうる。ノイズ抑制の観点から、Bの含有率は5.0質量%以上が好ましく、5.5質量%以上が特に好ましい。過剰のFe2B相は、飽和磁束密度を低下させる。飽和磁束密度の観点から、Bの含有率は8.0質量%以下が好ましく、7.5質量%以下が特に好ましい。
[クロム(Cr)]
Crは、Fe中に固溶し、保磁力の向上に寄与する。保磁力は、磁気共鳴周波数と相関する。保磁力が大きい合金では、磁気共鳴周波数が高い。Crはさらに、粉末の耐食性にも寄与しうる。これらの観点から、Crの含有率は1.0質量%以上が好ましく、2.0質量%以上が特に好ましい。保磁力は、透磁率とは負の相関関係にある。Crの過剰の添加は、透磁率向上に悪影響を及ぼす。この観点から、Crの含有率は15.0質量%以下が好ましく、10.0質量%以下が特に好ましい。Crの含有率は、「JIS G 1256」の規定に準拠して測定される。
Crは、Fe中に固溶し、保磁力の向上に寄与する。保磁力は、磁気共鳴周波数と相関する。保磁力が大きい合金では、磁気共鳴周波数が高い。Crはさらに、粉末の耐食性にも寄与しうる。これらの観点から、Crの含有率は1.0質量%以上が好ましく、2.0質量%以上が特に好ましい。保磁力は、透磁率とは負の相関関係にある。Crの過剰の添加は、透磁率向上に悪影響を及ぼす。この観点から、Crの含有率は15.0質量%以下が好ましく、10.0質量%以下が特に好ましい。Crの含有率は、「JIS G 1256」の規定に準拠して測定される。
[マンガン(Mn)]
Mnは、Fe中に固溶し、保磁力の向上に寄与する。保磁力は、磁気共鳴周波数と相関する。保磁力が大きい合金では、磁気共鳴周波数が高い。この観点から、Mnの含有率は1.0質量%以上が好ましく、2.0質量%以上が特に好ましい。保磁力は、透磁率とは負の相関関係にある。Mnの過剰の添加は、透磁率向上に悪影響を及ぼす。この観点から、Mnの含有率は5.0質量%以下が好ましい。Mnの含有率は、「JIS G 1256」の規定に準拠して測定される。
Mnは、Fe中に固溶し、保磁力の向上に寄与する。保磁力は、磁気共鳴周波数と相関する。保磁力が大きい合金では、磁気共鳴周波数が高い。この観点から、Mnの含有率は1.0質量%以上が好ましく、2.0質量%以上が特に好ましい。保磁力は、透磁率とは負の相関関係にある。Mnの過剰の添加は、透磁率向上に悪影響を及ぼす。この観点から、Mnの含有率は5.0質量%以下が好ましい。Mnの含有率は、「JIS G 1256」の規定に準拠して測定される。
[コバルト(Co)]
Coは、Fe中に固溶し、保磁力の向上に寄与する。保磁力は、磁気共鳴周波数と相関する。保磁力が大きい合金では、磁気共鳴周波数が高い。この観点から、Coの含有率は1.0質量%以上が好ましく、2.0質量%以上が特に好ましい。保磁力は、透磁率とは負の相関関係にある。Coの過剰の添加は、透磁率向上に悪影響を及ぼす。この観点から、Coの含有率は5.0質量%以下が好ましい。Coの含有率は、「JIS G 1256」の規定に準拠して測定される。
Coは、Fe中に固溶し、保磁力の向上に寄与する。保磁力は、磁気共鳴周波数と相関する。保磁力が大きい合金では、磁気共鳴周波数が高い。この観点から、Coの含有率は1.0質量%以上が好ましく、2.0質量%以上が特に好ましい。保磁力は、透磁率とは負の相関関係にある。Coの過剰の添加は、透磁率向上に悪影響を及ぼす。この観点から、Coの含有率は5.0質量%以下が好ましい。Coの含有率は、「JIS G 1256」の規定に準拠して測定される。
[ニッケル(Ni)]
Niは、オーステナイト形成元素である。Niは、δフェライト相の生成を抑制する。さらに、Fe中のNiリッチ相は、透磁率向上に寄与する。この観点から、Niの含有率は1.0質量%以上が好ましく、2.0質量%以上が特に好ましい。Niの過剰の添加は、マルテンサイト変態を阻害し、磁気特性に悪影響を及ぼすことがある。この観点から、Niの含有率は5.0質量%以下が好ましい。Niの含有率は、「JIS G 1256」の規定に準拠して測定される。
Niは、オーステナイト形成元素である。Niは、δフェライト相の生成を抑制する。さらに、Fe中のNiリッチ相は、透磁率向上に寄与する。この観点から、Niの含有率は1.0質量%以上が好ましく、2.0質量%以上が特に好ましい。Niの過剰の添加は、マルテンサイト変態を阻害し、磁気特性に悪影響を及ぼすことがある。この観点から、Niの含有率は5.0質量%以下が好ましい。Niの含有率は、「JIS G 1256」の規定に準拠して測定される。
Cr、Mn、Co及びNiの合計含有率が過剰であると、十分なFe2B相が生成せず、周波数が100kHzから20MHzの領域においてノイズが抑制され得ない。この観点から、この合計含有率は25質量%以下が好ましく、20質量%以下が特に好ましい。Cr、Mn、Co及びNiの合計含有率は、3.0質量%以上が好ましく、5.0質量%以上が特に好ましい。合計含有率が、ゼロであってもよい。換言すれば、Cr、Mn、Co及びNiは、必須の成分ではない。
[残部]
この合金の残部は、Fe及び不可避的不純物である。この合金において、不可避的不純物である元素の含有は、許容される。
この合金の残部は、Fe及び不可避的不純物である。この合金において、不可避的不純物である元素の含有は、許容される。
[Fe2B相の面積率PS]
合金におけるFe2B相の面積率(以下、「面積率PS」という)は、20%以上80%以下が好ましい。この面積率PSが上記範囲内である合金からなる粉末を含む磁性シート4により、周波数が100kHzから20MHzの領域において、ノイズが抑制されうる。面積率PSが増加すれば、Fe2B相によるノイズ抑制効果が増加する。この観点から、この面積率PSは30%以上がより好ましく、40%以上が特に好ましい。過大な面積率PSは、透磁率の低下を招き、ノイズ抑制を阻害する。この観点から、面積率PSは70%以下がより好ましく、60%以下が特に好ましい。面積率PSの測定では、まず粒子2の断面がSEMで観察されて、エネルギー分散型X線分析(EDS)にてFe2B相が特定される。さらにこの断面に画像解析が施されて、面積率PSが算出される。無作為に抽出された10個の粒子2において面積率が測定され、これが平均される。
合金におけるFe2B相の面積率(以下、「面積率PS」という)は、20%以上80%以下が好ましい。この面積率PSが上記範囲内である合金からなる粉末を含む磁性シート4により、周波数が100kHzから20MHzの領域において、ノイズが抑制されうる。面積率PSが増加すれば、Fe2B相によるノイズ抑制効果が増加する。この観点から、この面積率PSは30%以上がより好ましく、40%以上が特に好ましい。過大な面積率PSは、透磁率の低下を招き、ノイズ抑制を阻害する。この観点から、面積率PSは70%以下がより好ましく、60%以下が特に好ましい。面積率PSの測定では、まず粒子2の断面がSEMで観察されて、エネルギー分散型X線分析(EDS)にてFe2B相が特定される。さらにこの断面に画像解析が施されて、面積率PSが算出される。無作為に抽出された10個の粒子2において面積率が測定され、これが平均される。
[bHc/N]
合金における、各元素の有する電子の数の加重平均Nに対する、bHcの比(bHc/N)は、500A/(m・個)以上が好ましい。比(bHc/N)が500A/(m・個)以上である合金からなる粉末を含む磁性シート4により、周波数が100kHzから20MHzの領域において、ノイズが抑制されうる。この観点から、比(bHc/N)は530A/(m・個)以上がより好ましく、550A/(m・個)以上が特に好ましい。比(bHc/N)は、700A/(m・個)以下が好ましい。
合金における、各元素の有する電子の数の加重平均Nに対する、bHcの比(bHc/N)は、500A/(m・個)以上が好ましい。比(bHc/N)が500A/(m・個)以上である合金からなる粉末を含む磁性シート4により、周波数が100kHzから20MHzの領域において、ノイズが抑制されうる。この観点から、比(bHc/N)は530A/(m・個)以上がより好ましく、550A/(m・個)以上が特に好ましい。比(bHc/N)は、700A/(m・個)以下が好ましい。
例えば、Fe-3mass%Bの場合、Feの電子数は26であり、Bの電子数は5なので、加重平均Nは下記の数式によって算出される。
5×0.03+26×(1-0.03)=25.37
5×0.03+26×(1-0.03)=25.37
例えば、Fe-2mass%Cr-5mass%Bの場合、Feの電子数は26であり、Crの電子数は24であり、Bの電子数は5なので、加重平均Nは下記の数式によって算出される。
24×0.02+5×0.05+26×(1-0.02-0.05)=24.91
24×0.02+5×0.05+26×(1-0.02-0.05)=24.91
bHcは、振動試料型磁力計によって測定される。測定時の印加磁場は、120,000A/mである。磁性体のヒステリシスループを解析することにより、bHcが導出される。振動試料型磁力計の一例としては、Lake Shore社のAGM 2900が挙げられる。
[平均粒径]
この粉末の平均粒径D50は、20μm以上150μm以下が好ましい。平均粒径D50が20μm以上である粉末は、流動性に優れており、従ってバインダー等と容易に混合されうる。この観点から、平均粒径D50は25μm以上がより好ましく、30μm以上が特に好ましい。平均粒径D50が150μm以下である粉末から、厚さが小さな磁性シート4が得られうる。この磁性シート4は、小型の電子機器に適用されうる。この観点から、平均粒径D50は120μm以下がより好ましく、100μm以下が特に好ましい。
この粉末の平均粒径D50は、20μm以上150μm以下が好ましい。平均粒径D50が20μm以上である粉末は、流動性に優れており、従ってバインダー等と容易に混合されうる。この観点から、平均粒径D50は25μm以上がより好ましく、30μm以上が特に好ましい。平均粒径D50が150μm以下である粉末から、厚さが小さな磁性シート4が得られうる。この磁性シート4は、小型の電子機器に適用されうる。この観点から、平均粒径D50は120μm以下がより好ましく、100μm以下が特に好ましい。
平均粒径D50は、粉体の全体積を100%として累積カーブが求められたとき、その累積カーブが50%となる点の粒子径である。粒子径は、レーザー回折・散乱式粒子径分布測定装置により測定される。この装置のセル内に、粉末が純水と共に流し込まれ、粒子2の光散乱情報に基づいて、平均粒径が検出される。この装置の一例として、日機装社の「マイクロトラックMT3000」が挙げられる。
この粉末は、アトマイズによって製造されうる。好ましいアトマイズとして、ガスアトマイズ法及び水アトマイズ法が挙げられる。
[第二実施形態]
図3は、本発明の他の実施形態に係る磁性部材用粉末の粒子6が示された断面図である。この粒子6は、球状の主部8と絶縁性皮膜10とを有している。換言すれば、粒子6は、主部8の表面に位置する(絶縁性皮膜10で構成される)絶縁被覆を有している。主部8の材質、性状、サイズ等は、図1に示された粒子2のそれらと同じである。この粒子6は、図1に示された粒子2の表面に絶縁性皮膜10が付着することで得られうる。
図3は、本発明の他の実施形態に係る磁性部材用粉末の粒子6が示された断面図である。この粒子6は、球状の主部8と絶縁性皮膜10とを有している。換言すれば、粒子6は、主部8の表面に位置する(絶縁性皮膜10で構成される)絶縁被覆を有している。主部8の材質、性状、サイズ等は、図1に示された粒子2のそれらと同じである。この粒子6は、図1に示された粒子2の表面に絶縁性皮膜10が付着することで得られうる。
粒子6の主部8と、この粒子6に隣接する他の粒子6の主部8との直接の接触が、絶縁性皮膜10によって防止される。これにより、渦電流損失が抑制される。この観点から、皮膜10の厚みは20nm以上が好ましく、30nm以上が特に好ましい。主部8が有する磁気特性が阻害されにくいとの観点から、皮膜10の厚みは500nm以下が好ましく、100nm以下が特に好ましい。
絶縁性皮膜10を有さない粒子で作製したシートの体積抵抗値αに対する、絶縁性皮膜10を有する粒子6で作製したシートの体積抵抗値βの比(β/α)は、100以上である。
図3に示されるように、皮膜10は主部8の全体を覆っている。皮膜10が、主部8を部分的に覆ってもよい。
粒子6が、主部8と皮膜10との間に他の皮膜を有してもよい。粒子6が、皮膜10の外側に他の皮膜を有してもよい。
皮膜10は、チタンアルコキシド類及びケイ素アルコキシド類を含む重合体からなるのが好ましい。この重合体はチタンアルコキシド類とケイ素アルコキシド類との混合物の重合反応によって得られうる。チタンアルコキシド類は、1つの分子中にあるチタン原子に少なくとも1つのアルコキシド基が結合している化合物である。ケイ素アルコキシド類は、1つの分子中にあるケイ素原子に少なくとも1つのアルコキシド基が結合している化合物である。アルコキシド基は、有機基が負の電荷を持つ酸素と結合した化合物である。有機基は、有機化合物からなる基である。
チタンアルコキシド類には、チタンアルコキシドのモノマー、このモノマーが複数重合されて形成されたオリゴマー、及びチタンアルコキシドが生成する前の段階の化合物(前駆体とも称される。)が含まれる。ケイ素アルコキシド類には、ケイ素アルコキシドのモノマー、このモノマーが複数重合されて形成されたオリゴマー、及びケイ素アルコキシドが生成する前の段階の化合物(前駆体とも称される。)が含まれる。
チタンアルコキシドの具体例として、チタンテトラメトキシド、チタンテトラエトキシド、チタンテトライソプロポキシド、チタンテトラブトキシド、チタンテトラ-2-エチルヘキソキシド及びイソプロピルトリドデシルベンゼンスフォニルチタネートが挙げられる。
ケイ素アルコキシドの具体例として、テトラエトキシシラン、テトラメトキシシラン、メチルトリエトキシシラン、テトライソプロポキシシラン、ビニルトリメトキシシラン、γ-アミノプロピルトリエトキシシラン及びN-(β-アミノエチル)-γ-アミノプロピルメチルジメトキシシランが挙げられる。
主部8への皮膜10の付着には、種々のコーティング方法が採用されうる。コーティング方法の具体例として、混合法、ゾル・ゲル法、スプレードライヤー法及び転動流動層法が挙げられる。
チタンアルコキシド類及びケイ素アルコキシド類を含む重合体が溶剤で希釈されて、コーティングに供されてもよい。好ましい溶剤として、アセトン、メチルエチルケトン、アセトニトリル、メタノール、エタノール、イソプロピルアルコール、n-ブタノール、ベンゼン、トルエン、ヘキサン、ヘプタン、シクロヘキサン、クロロホルム、クロロベンゼン、ジクロロベンゼン、酢酸エチル、プロピオン酸エチル及びテトラヒドロフランが例示される。
皮膜10が、チタンアルコキシド類及びケイ素アルコキシド類を含む重合体と共に、他の化合物を含んでもよい。皮膜10が、チタンアルコキシド類及びケイ素アルコキシド類を含む重合体以外の化合物から形成されてもよい。
以下、実施例によって本発明の効果が明らかにされるが、この実施例の記載に基づいて本発明が限定的に解釈されるべきではない。
[実施例1]
アトマイズにより、下記の表1に示された組成を有する実施例1の粉末を製作した。この粉末における各粒子の形状は、球であった。この粉体を、小型ミキサーを用いて100℃の温度下でエポキシ樹脂と混練し、粉末が樹脂マトリクス中に均一に分散した樹脂組成物を得た。エポキシ樹脂と粉末との体積比は、5対2とされた。この樹脂組成物を、圧力が4MPaであり、温度が200℃であるの条件で5分間熱プレス処理し、厚みが0.1mmである磁性シートを得た。
アトマイズにより、下記の表1に示された組成を有する実施例1の粉末を製作した。この粉末における各粒子の形状は、球であった。この粉体を、小型ミキサーを用いて100℃の温度下でエポキシ樹脂と混練し、粉末が樹脂マトリクス中に均一に分散した樹脂組成物を得た。エポキシ樹脂と粉末との体積比は、5対2とされた。この樹脂組成物を、圧力が4MPaであり、温度が200℃であるの条件で5分間熱プレス処理し、厚みが0.1mmである磁性シートを得た。
[実施例2~30及び比較例1~16]
組成を下記の表1~3に示される通りとした他は実施例1と同様にして、実施例2~30及び比較例1~16の粉末を製作した。これら粉末から、実施例1と同様にして、磁性シートを得た。
組成を下記の表1~3に示される通りとした他は実施例1と同様にして、実施例2~30及び比較例1~16の粉末を製作した。これら粉末から、実施例1と同様にして、磁性シートを得た。
[磁性シートの評価]
温度が25℃である条件下で周波数を変動させて、磁性シートの透磁率及びtanδを、測定した。測定は、アジレント・テクノロジー(Agilent Technologies)社製の商品名「ベクトル・ネットワーク・アナライザーN5245A」によって行った。この10MHzにおける実部透磁率μ’及びtanδが0.02を超える周波数域の下限値FLを、求めた。さらに、この実部透磁率μ’及び下限値FLに基づき、下記の基準に従って、各粉末をランク付けした。
A:μ’が4.0以上かつ、FLが100MHz以上
B:μ’が4.0以上かつ、FLが40MHzを超え100MHz未満
C:μ’が4.0以上かつ、FLが10MHz以上40MHz以下
F:μ’が4.0未満または、FLが10MHz未満
これらの結果が、下記の表1~3に示されている。
温度が25℃である条件下で周波数を変動させて、磁性シートの透磁率及びtanδを、測定した。測定は、アジレント・テクノロジー(Agilent Technologies)社製の商品名「ベクトル・ネットワーク・アナライザーN5245A」によって行った。この10MHzにおける実部透磁率μ’及びtanδが0.02を超える周波数域の下限値FLを、求めた。さらに、この実部透磁率μ’及び下限値FLに基づき、下記の基準に従って、各粉末をランク付けした。
A:μ’が4.0以上かつ、FLが100MHz以上
B:μ’が4.0以上かつ、FLが40MHzを超え100MHz未満
C:μ’が4.0以上かつ、FLが10MHz以上40MHz以下
F:μ’が4.0未満または、FLが10MHz未満
これらの結果が、下記の表1~3に示されている。
表1~3に示された評価結果から、本発明の優位性は明らかである。
本発明に係る粉末は、種々の磁性部材に適している。
Claims (6)
- 複数の粒子からなる磁性部材用粉末であって、
前記粒子の各々の主部が、
B:5.0質量%以上8.0質量%以下、並びに
残部:Fe及び不可避的不純物
からなる合金製であり、前記合金がFe2B相を含む、磁性部材用粉末。 - 複数の粒子からなる磁性部材用粉末であって、
前記粒子の各々の主部が、
B:5.0質量%以上8.0質量%以下
Cr、Mn、Co及びNiからなる群から選択された1種又は2種以上:0質量%以上25質量%以下、並びに
残部:Fe及び不可避的不純物
からなる合金製であり、前記合金がFe2B相を含む、磁性部材用粉末。 - 前記合金におけるFe2B相の面積率PSが、20%以上80%以下である、請求項1又は2に記載の磁性部材用粉末。
- 前記合金における、各元素の有する電子の数の加重平均Nに対する、bHcの比(bHc/N)が、500A/(m・個)以上700A/(m・個)以下である、請求項1~3のいずれか一項に記載の磁性部材用粉末。
- 前記粒子が、前記主部の表面に位置する絶縁被覆を有する、請求項1~4のいずれか一項に記載の磁性部材用粉末。
- 上記粒子が、球形状を有する、請求項1~5のいずれか一項に記載の磁性部材用粉末。